PAVESEAL 1 POLYSULPHIDE SEALANT POURING GRADE

Transcription

1 IMPERIALSEALS PRODUCT DATA EJS /89/1 PAVESEAL 1 POLYSULPHIDE SEALANT POURING GRADE PAVESEAL 1 AG2 pouring grade is a two part Polysulphide Sealant which cures once the two components are mixed together to form a flexible rubber seal. It has good adhesion to concrete, metals and many common building materials APPLICATION Paveseal 1 AG 2 is recommended for the sealing of horizontal structural floor joints in factory floors, road joints, joints in aircraft runways, aircraft parking aprons and hangers. SPECIFICATION COMPLIANCES BS TYPE FB (Includes N & F) JOINT SIZE SUITABILITY Minimum joint width : 6 mm Maximum joint width : 30 mm Minimum joint depth : 12 mm Maximum joint depth : 25 mm WIDTH & DEPTH RATIO 1:1 ratio for floor joints up to 25 mm width. 30 mm width requires a depth of 25 mm. TECHNICAL DATA Working 20 C : Approximately 1hr 30 minutes. Application Temperature : +5 C to +40 C Service Temperature : - 40 C to 80 C Shore A Hardness : 15 to 20 Cure C & 65% RH : 7 Days full cure Chemical Resistance : Resistance to : Most dilute acids and Alkalis Petrol Diesel Jet Fuel Many Solvents UV Resistance : Good Service Life : 20 years Movement Accommodation : In tension and Compression : 25% PACKAGING In dual pack of Base & Hardener : 5 liter pack Priming The walls of concrete joints surfaces and most other substrates need to be primed prior to the application of Paveseal 1 AG 2. Primers Paveseal 1 AG2 primer Coverage Equipment : 500 ml tins : 125 meters per tin Manual Barrel Gun Spiral Mixer Follow Base plate. Quantity Estimator Joint Size Meters Per Liter 6 mm x 6 mm mm x 6 mm mm x 9 mm mm x 18 mm 3 25 mm x 25 mm 1.6 APPLICATION INSTRUCTIONS. 1. Prime the walls of joint with primer and allow primer to dry. 2. Mix Paveseal 1 in accordance to instruction. 3. Fill barrel gun with the mixed sealant. 4. Cap the barrel gun and insert nozzle mechanism to fill the joint with sealant. 5. Use a flat spatula to level the sealants into the joint. 6. Remove masking tape by pulling it outwards from the face of the joint. 7. Clean walls of joint from all Contaminations and insure joint is dry. 8. Mask the edge of joints with masking tape. 9. Insert Migurod into joint to determine the depth of sealant and also to prevent adhesion to the base of joint. 10. Prime the walls of joint with primer and allow primer to dry. 11. Mix Paveseal 1 in accordance to instruction. 12. Fill barrel gun with the mixed sealant.

2 PAVESEAL 1 IMPERIALSEALS (UK) PTE LTD TEL: FAX: info@imperialseals.com.sg IMPERIALSEALS 13. Cap the barrel gun and insert nozzle into joint before gently pressing the trigger mechanism to fill the joint with sealant. 14. Use a flat spatula to level the sealants into the joint. 15. Remove masking tape by pulling it outwards from the face of the joint. COUNTRY OF ORIGIN Product is manufactured in the United Kingdom. PRUDENT FORTHOUGHTS TO MINIMISE THE RISK OF SELECTING SEALANTS WITH POOR PERFORMING CHARACHERTICS AFTER APPLICATION. CONSIDERATION SHOULD BE GIVEN TO: Country of manufacture: It is an acceptable fact that very few countries produce quality two part polysulphide sealants with sufficient base polymers. Leading UK manufacturers abide to standards in production and have less possibilities of defaulting in standards. Manufacturing Experience: At least 20 years. Hardness: Horizontal joints min 20 degree (hardness to prevent dirt gathering onto cured sealants.) Modified Sealants: Modified Blends of sealants manufactured from Polysulphide and Bitumen are questionable. It pays to use the state of the art Polysulphide sealants. Single part or Single component Sealants: Not recommended for horizontal expansion joints. Standards: Polysulphide sealants should conform to prevalent standards or higher.

3 IMPERIALSEALS PRODUCT DATA EJS/89/2 PAVESEAL 2 POLYSULPHIDE SEALANT GUN GRADE PAVESEAL AG 2 gun grade is a two part Polysulphide Sealant which cures once the two components are mixed together to form a flexible rubber seal. It has good adhesion to concrete, metals and many common building materials. It is designed for joints in horizontal and vertical surfaces. APPLICATION Paveseal 2 AG 2 is recommended for the sealing of vertical and horizontal expansion joints in factory walls and floors, road, aircraft runways, aircraft parking aprons and hangers. It is suitable for use in precast metal and precast concrete panel joints SPECIFICATION COMPLIANCES BS 4254 : 1983 BS EN ISO F 25 LM JOINT SIZE SUTIABILITY Minimum joint width : 6 mm Maximum joint width : 25 mm single application 50 mm multiple application JOINT DEPTH Minimum joint depth Minimum joint depth Maximum joint depth WIDTH & DEPTH RATIO Butt Joints : 2:1 ratio Floor Joints : 1:1 ratio : 10 mm on porous substrate : 6 mm on non-porous substrate : 25 mm TECHNICAL DATA Working 20 C : Approximately 1hr 30 minutes. Application Temperature : +5 C to +40 C0 Service Temperature : - 40 C to 80 C Shore A Hardness : 25 Cure C & 65% RH : 7 Days full cure Chemical Resistance : Resistance to : Most dilute acids and Alkalis Petrol Diesel Chemical Resistance : Jet Fuel Many Solvents Vegetable oils UV Resistance : Good Service Life : 20 years Movement Accommodation Butt Joints (movement in Tension and Compression) : 30% Lap Joints: ( movement in Shear) : 50% PACKAGING In dual pack of Base & Hardener COLOUR : 2.5 liter pack : Grey PRIMING The wall of concrete surfaces and most other substrate need to be primed prior to the application of Paveseal 2. Primers Paveseal 2 AG2 primer : 500 ml tins Coverage Equipment : 125 meters per tin : Manual Barrel Gun Spiral Mixer Follow Base plate. Quantity Estimator Joint Size Meters Per Liter 6 mm x 6 mm mm x 6 mm mm x 9 mm mm x 18 mm mm x 25 mm 1.6

4 PAVESEAL 2 IMPERIALSEALS (UK) PTE LTD TEL: FAX: info@imperialseals.com.sg IMPERIALSEALS APPLICATION INSTRUCTIONS. 1. Clean walls of joint from all contamination and insure joint is dry. 2. Mask the edge of joints with masking tape 3. Insert Migurod into joint to determine the depth of sealant and also to prevent adhesion to the base of joint. 4. Prime the walls of joint with primer and allow primer to dry. 5. Mix Paveseal 2 in accordance to instruction. 6. Fill barrel gun with the mixed sealant. 7. Cap the barrel gun and insert nozzle into joint before gently pressing the trigger mechanism to fill the joint with sealant. 8. Use a flat spatula to level the sealants into the joint. 9. Remove masking tape by pulling it outwards from the face of the joint. COUNTRY OF ORIGIN This Product is manufactured in the United Kingdom. PRUDENT FORTHOUGHTS TO MINIMISE THE RISK OF SELECTING SEALANTS WITH POOR PERFORMING CHARACHERTICS AFTER APPLICATION. CONSIDERATION SHOULD BE GIVEN TO: Country of manufacture: It is an acceptable fact that very few countries produce quality two part polysulphide sealants with sufficient base polymers. Leading UK manufacturers abide to standards in production and have less possibilities of defaulting in standards. Manufacturing Experience: At least 20 years. Hardness: Horizontal joints min 20 degree (hardness to prevent dirt gathering onto cured sealants.) Modified Sealants: Modified Blends of sealants manufactured from Polysulphide and Bitumen are questionable. It pays to use the state of the art Polysulphide sealants. Single Part or Single component Sealants: Not recommended for horizontal expansion joints. Standards: Polysulphide sealants should conform to prevalent standards or higher.

5 IMPERIALSEALS PRODUCT DATA EJS/89/3 PAVESEAL 3 POLYSULPHIDE SEALANT GUN GRADE PAVESEAL 3 ARBO 2150 is a Polysulphide sealant manufactured with higher polymer content. It s specifications exceeds the existing British Standard and Euro Standards for Polysulphide sealants. ARBO 2150 is designed for expansion joints on floors which will be exposed to heavy foot trafficking and industrial wheel trafficking. It will resist high levels of compression. APPLICATION Paveseal 3 Arbo 2150 is recommended for the sealing of expansion, construction and contraction joints in building structues. Paveseal 3 is suitable for both vertical and horizontal joints on factory floors, distribution centres, warehouses, vehicle parking aprons, roads, aircraft runways, aircraft parking aprons and hangers. It is suitable for use in compartmentalization joints on large open tiled floors where joints are formed in squares of 6 meters x 6 meters to allow for the expansion and contraction of cement screed, tile bedding mortar and tiles or granite finishes. This requirement is mandatory due to the differing coefficient of expansion of the different materials used to build up floor finishes. Paveseal 3 is technically more suited than using rigid stainless steel blades with neoprene inserts or the use of plastic strips to fill compartmentalization joints. Joints are formed to allow for expansion and contraction of substrates to take place. As such, materials of high rigidity should never be used to fill compartmentalization joints. Sealants and preformed profiles should be well designed to accommodate anticipated minute moments from compartmentalisation joints. Rigid profile in fills does not serve any functional purpose. Paveseal 3 is recommended in sewage treatment works where biodegradation resistance is required for aggressive environment. SPECIFICATION COMPLIANCES Exceeds BS : 1983 Exceeds BS EN ISO F 25 LM JOINT SIZE SUTIABILITY Minimum joint width : 6 mm Maximum joint width : 25 mm single application 50 mm multiple application JOINT DEPTH Minimum joint depth : 12 mm on porous substrate Minimum joint depth : 6 mm on non-porous substrate Maximum joint depth : 25 mm Chemical Resistance : Resistance to : Most dilute acids and Alkalis Petrol Diesel, UV Resistance : Good Service Life : 20 years Movement Accommodation: Butt Joints (movement in Tension and Compression) 20% Lap Joints: ( movement in Shear) 40% PACKAGING In dual pack of Base & Hardener COLOUR STORAGE LIFE : 2 litre pack : Black & Grey : 12 Months PRIMING The wall of concrete surfaces and most other substrate need to be primed prior to the application of Paveseal 3. Primers Paveseal AG2 primer Coverage Equipment 500 ml tins : 125 meters per tin : Manual Barrel Gun Spiral Mixer Follow Base plate. WIDTH & DEPTH RATIO Butt Joints : 2:1 ratio Floor Joints : 1:1 ratio TECHNICAL DATA Working 20 C : Approximately 1hr 30 minutes. Application Temperature : +5 C to +40 C Service Temperature : - 40 C to 80 C

6 PAVESEAL 3 IMPERIALSEALS (UK) PTE LTD TEL: FAX: info@imperialseals.com.sg IMPERIALSEALS Shore A Hardness : 50 Cure C & 65% RH : 7 Days full cure Quantity Estimator Joint Size Meters Per Liter 6 mm x 6 mm mm x 6 mm mm x 9 mm mm x 18 mm mm x 25 mm 1.6 APPLICATIONS. 1. Clean walls of joint from all contamination and insure joint is dry. 2. Mask the edge of joints with masking tape 3. Insert Migurod into joint to determine the depth of sealant and also to prevent adhesion to the base of joint. 4. Prime the walls of joint with primer and allow primer to dry. 5. Mix Paveseal 3 in accordance to instruction and install sealant. COUNTRY OF ORIGIN This Product is manufactured in the United Kingdom. PRUDENT FORTHOUGHTS TO MINIMISE THE RISK OF SELECTING SEALANTS WITH POOR PERFORMING CHARACHERTICS AFTER APPLICATION. CONSIDERATION SHOULD BE GIVEN TO: Country of manufacture: It is an acceptable fact that very few countries produce quality two part polysulphide sealants with sufficient base polymers. Leading UK manufacturers abide to standards in production and have less possibilities of defaulting in standards. Manufacturing Experience: At least 20 years. Hardness: Horizontal joints min 35 degree (hardness to prevent dirt gathering onto cured sealants.) Modified Sealants: Modified Blends of sealants manufactured from Polysulphide and Bitumen are questionable. It pays to use the state of the art Polysulphide sealants. Standards: Polysulphide sealants should conform to prevalent standards or higher.

7 IMPERIALSEALS PRODUCT DATA EJS /89/4 PAVESEAL 4 GUN GRADE EPOXY SEALANT PAVESEAL is a unique two part Epoxy sealant which cures to form a hard wearing seal in construction and compartmentalisation joints. Paveseal 4 is designed to accommodate small movements in extension and compression. Recommended for use in a variety of internal stress relief joint Systems such as: compartmentalisation joints for floor finishes swimming pool control joints chemical resistant flooring joints on factory floors kitchen floor tile pointing other arrears which will experience continual water resistance and a high degree of chemical resistance (especially to common cleaning substances) are required. Applications Paveseal 4 is recommended for joints in swimming pools, tile to tile points on floors of special treatment rooms, compartmentalization joints on large floor surfaces, shower rooms and water retaining structures. NB: Not recommended for structural expansion joints. Packaging 1.2 Litre Set, with separate tins for Base and Curing Agent Follower plate Colours Off White, Grey Application Instructions Joint Preparation The joint surfaces must be clean and free from all contamination. Surfaces should be degreased using the appropriate surface cleaner (contact Technical Service Department for further information). Mixing The ratio of base to curing agent controls the performance properties of 1025 and tins are filled to an exact mixing ratio. It is vital therefore that the whole contents of the curing agent tin are added to the base tin. The 2 components must be thoroughly mixed to ensure complete homogeneity (Spiral pig tail mixing equipment is recommended). Application The usual application method once mixed is to fill the sealant into empty cartridge dispensers using the follower tin supplied with the pack. The cartridge is placed over the hole in the centre of the plate and filled by applying steady downward pressure. Insert the plunger into the cartridge and the mixed sealant is then ready for application using a Caulking Gun. The sealant should be extruded firmly into the joint by maintaining an even pressure on the trigger of the gun. Joint Backing Where applicable, appropriate joint filler, e.g. closed cell polyethylene foam should be used to provide the correct joint depth. All joint preparation and sealant application should be carried out in accordance with BS8000 Part 16 (British standard for the sealing of joints in buildings) Joint Size Suitability Joint Width Minimum 6mm Maximum 20mm (single application) Joint Depth Minimum 10mm on porous substrates Minimum 6mm on non-porous substrates Maximum 10mm Width: Depth Ratio 1:1, 1-2 Health and Safety Base component is Polyamide based and curing agent contains Epoxy resin. Both components require careful handling. Application Temperature Service Temperature Cure Rate (at 20º C) : +10º C to + 40º C : -20º C to +90º C : 48 hours. At lower temperatures cure rate will be extended. Technical Data Typical Shore D Hardness (cured at 20º C) : Work Life (Typical at 20º C) : 45 minutes Chemical Resistance: Resistant to most alkalis and dilute acids, petrol, diesel, jet fuel. Resistant to most cleaning chemicals used in swimming pool situations (neat Hypochlorite crystals should not be applied to 1025 SP).

8 PAVESEAL 4 IMPERIALSEALS (UK) PTE LTD TEL: FAX: info@imperialseals.com.sg IMPERIALSEALS Service Life: 20 years + in non-critical applications. Use in swimming pools will lower this figure (depending upon application performance required). Movement Accommodation: Tension 5% Compression 50 % Accessories Cleaners Cleaner 17-1 litre Tin (Xylene based not suitable for use with plastics or delicate finishes) Cleaner 16 1 Litre Tin (Alcohol Based) Equipment Bulk Loading Guns Heavy Duty Follower Plates Quantity Estimator Joint Size (mm) Metres/ 1.2 litre set 6 x x x x 10 6 Important: The information in this leaflet is given in good faith and based on results gained from experience and tests. However, all recommendations or suggestions are made without guarantee since the conditions of use are beyond our control. Goods are supplied subject to the Company s terms and conditions of sales, a copy of which is available on request.