CrystalTM Tapis Coton

Transcription

1 CrystalTM Tapis Coton #10 black/white #30 brown #70 anthracite Les tapis coton CrystalTM empêchent la poussière et l humidité de se disperser dans des bâtiments. Ces tapis en coton absorbent la poussière et l humidité entièrement. Le caoutchouc 100% Nitrile empêche le tapis d onduler et de fissurer dans tous les conditions de temps. Tailles standards Spécifications 60 x x x 200 Fil : 100% Coton 75 x x x 240 Poids de fil: 1050 gr/m2 85 x x x 250 Caoutchouc : Nitrile (Bord 2,5mm / Centre 1,5mm) 85 x x x 300 Poids total: 3050 gr/m2 85 x x 300 Taille maximale :150 x 550 cm / Variation de taille: +/- 2% Options de dorsal : lisse, picots Également disponible en caoutchouc de 3mm

2 Crystal Cotton Mat Specifications Carpet Specifications Yarn Weight Pile Thickness 50% Polyester / 50% Cotton 1050 gr/m² 10mm Total Weight Primary Backing Rubber Backing Border Width 3050 gr/m² Freudenberg LUTRADUR Polyester Spun bound Non-woven Fabric 130 gr/m² 100% Nitrile rubber for maximum oil resistance, weight reduction and flexibility. Compression molded with reinforced borders on all four side Border Thickness: Body Thickness: 2 cm 2.5mm 1.5mm Size Variance +/-2%

3 Cotton Washing Instructions Recommended for Crystal Cotton Mats No. Process Comments Time Water Level Temperature 1. Flush 2-3 Min. Medium 49 C 2. Flush Optional 2-3 Min. Medium 27 C 3. Break 5-10 Min. High 49 C 4. Rinse 2 Min. High Cold 5. Rinse 2 Min. High Cold 6. Extract Low Speed 1-2 Min. 7. Shake Out Drum Turning 1 Min. 8. Extract Max. 250G 3-5 Min. 9. Dry Optional 5-30 Min. 82 C (Basket Temp.) 10. Cool Down 5 Min Additional Recommendations 1. For Heavy Soiled Mats, increase temperature up to max. 60 C. Frequent washing at this temperature can lead to color-loss 2. Break should not exceed ph of 9,5; use low ph non-ionic detergents 3. To prevent pilling on other mats, Crystal mats should not be washed with mats made of Nylon or other synthetic carpet yarns 4. Do not over-dry mats; Basket-temperature of dryer should not exceed 82 C 5. Insure that cotton mats are thoroughly dried to prevent mildew from forming in the cotton yarn 6. Lay Mats flat following removal from washer; allow mats to cool before rolling

4 Prestige Carpets bvba Dhr. Dirk Santens Klein Frankrijk RONSE Your notice of Your reference Date Analysis Report Required tests : EN (2007) + A1 (2009) Identification number T Information given by the client Crystal Date of receipt Petra Wittevrongel Order responsible This report runs to 7 pages and may be reproduced, as long as it is presented in its entire form, without written permission of Centexbel. The results of the analysis cover the received samples. Centexbel is not responsible for the representativeness of the samples. In assessing compliance with the specifications, we did not take into account the uncertainty on the test results. VAT BE CENTEXBEL-GENT Technologiepark 7 BE-9052 Zwijnaarde Tel Fax gent@centexbel.be Fin. Acc IBAN BE CENTEXBEL-BRUSSELS Montoyerstraat 24 B2 BE-1000 Brussels Tel Fax

5 Analysis Report Page 2/7 Reference: T Crystal Information given by the client Product standard Quality FR treated FR-surface treatment Use-surface Substrate, support Backing layer Total mass Pile thickness Total thickness Surface structure EN (2007) + A1 (2009) Crystal no no Cotton PES Nitrile rubber 3050 g/m² 10.0 mm 11.5 mm Cut pile Notified body No: 0493

6 Analysis Report Page 3/7 Reference: T Crystal Reaction to fire tests Ignitability of building products subjected to direct impingement of flame - Single-flame source test Date of ending the test Standard used Product standard Floor covering Deviation from the standard Conditioning EN ISO (2010) EN (2007) + A1 (2009) - 23 C, relative humidity 50% Minimum 14 days or until constant mass is achieved The test results relate to the behaviour of the test specimens of a product under the particular conditions of the test: they are not intended to be the sole criterion for assessing the potential fire hazard of the product in use. Substrate Mounting Cleaning Fibre cement board - density (1800 ± 200) kg/m³ Loose-laid Specimens have not been cleaned

7 Analysis Report Page 4/7 Flame application time (s) Flame application 15 Surface Time to reach 150 mm mark (s) 1 Length Width 5 6 = mark not reached within 20 s after application of the flame Criteria Floorcoverings time to reach the mark: Classification - 20 s : Class Efl - < 20 s : Class Ffl Class Efl Limitations This classification document does not represent type approval or certification of the product. Performed under accreditation in the fire lab under the responsibility of Pros Van Hoeyland

8 Analysis Report Page 5/7 Reference: T Crystal Reaction to fire tests for floorings - Determination of the burning behaviour using a radiant heat source Date of ending the test Standard used Product standard Deviation from the standard Conditioning EN ISO (2010) EN (2007) + A1 (2009) - 23 C, relative humidity 50% Minimum 14 days or until constant mass is achieved The test results relate to the behaviour of the test specimens of a product under the particular conditions of the test: they are not intended to be the sole criterion for assessing the potential fire hazard of the product in use. Substrate Mounting Cleaning Fibre cement board - density (1800 ± 200) kg/m³ Loose-laid Specimens have not been cleaned

9 Radiant heat flux Flame spread distance (cm) Length #1 Width #1 #2 #3 Average 10 min min min Flame time 28 min 05 s 30 min 00 s 28 min 20 s 30 min 00 s Analysis Report Page 6/7 Heat flux kw/m² Heat flux at the time of flame extinguishment or after a test duration of 30 minutes. Fire classification in accordance with EN (2007) + A1 (2009) Class EN ISO or CWFT EN ISO (test duration = 30 min) Bfl Efl heat flux 8,0 kw/m² Cfl Efl heat flux 4,5 kw/m² Dfl Efl heat flux 3,0 kw/m² Smoke production: Light attenuation Maximum (%) Length #1 56 Width #1 28 #2 50 #3 65 Average Total (%.min) Additional classification in accordance with EN (2007) + A1 (2009) smoke production 750%.min s1 smoke production > 750%.min s2

10 Analysis Report Page 7/7 Reaction to fire classification : Efl / s1 loose-laid on a non-combustible substrate End use substrates of classes A1or A2-s1,d0 (ISO 13238: ) Limitations This classification document does not represent type approval or certification of the product. The classification assigned to the product in this report is appropriate to a declaration of conformity by the manufacturer within the context of system 3 attestation of conformity and CE marking under the Construction Products Directive. The manufacturer has made a declaration, which is held on file. This confirms that the products design requires no specific processes, procedures or stages (e.g. no addition of flame -retardants, limitation of organic content, or addition of fillers) that are aimed at enhancing the fire performance in order to obtain the classification achieved. As a consequence the manufacturer has concluded that system 3 attestation is appropriate. The test laboratory has, therefore, played no part in sampling the product for the test, although it holds appropriate references, supplied by the manufacturer, to provide for traceability of the samples tested. Performed under accreditation in the fire lab under the responsibility of Pros Van Hoeyland