Technical Data Sheet StoLevell Duo plus

Transcription

1 Mineral bonding and reinforcing mortar Characteristics Areas of application Properties Exterior and interior For all mineral substrates For bonding insulation boards onto mineral substrates For producing thin-layer reinforcing coats As bonding and reinforcing compound for StoTherm Vario and Mineral High adhesive strength Weather-resistant Highly water-repellent Highly water vapour permeable Good adhesion to substrate Suited for machine application Technical Data Criterion Minimum layer thickness Maximum layer thickness Norm / Test prescript Value/ Units 3 mm 5 mm Mortar class EN CS III Mortar class DIN V P II Apparent density of cured mortar EN ,4 g/cm³ Flexural strength (28 days) EN ,1 N/mm² Compressive strength (28 days) EN Modulus of elasticity dynamic (28 days) Coefficient of water vapour diffusion resistance µ TP BE-PCC 4,8 N/mm² N/mm² 25 Water absorption ETAG 004 0,5 kg/m² Water absorption (class) EN Thermal conductivity (Table value) Thermal conductivity (Table value) EN 1745 EN 1745 W 2 = c 0,20 kg/m²*min 0,5 0,83 W/(m*k) for P=50 % 0,93 W/(m*k) for P=90 % Information Table value Table value Fire behaviour (class) EN A1 Non-combustible Coverage 770 L/t Rev.-Nr.: 1 / EN / / 1/6

2 The characteristic values stated are average values or approx. values. We use natural raw materials in our products, which means that the stated values can vary slightly in the same delivery batch; this does not affect the suitability of the product for its intended purpose. Substrate Requirement Preparation The substrate must be firm, level, dry, load bearing and free from grease and dust. The suitability of the fixing method with the substrate must be assessed individually on site where necessary. Damp or not fully cured substrates can lead to defects in subsequent coats, such as blistering or cracking. Check existing coatings for their suitability and load bearing capacity. Remove any loose or structurally weak finishes. The substrate must be cleaned where necessary. Application Application temperature Minimum substrate and air temperature: +5 C Maximum substrate and air temperature: +30 C Processing time Mixing ratio At +20 C: approx. 60 minutes 5.8 l water per 25 kg Preparing the material Pour water into a container and then add the dry mortar material. Stir for approx. 2 minutes, allow to mature for approx. 3 minutes and then stir again for approx. 30 seconds. Consumption Type of application Consumption approx. Reinforcement 4,50-6,00 kg/m² Bonding of EPS boards 4,50-5,50 kg/m² Bonding of mineral wool boards 6,50-7,50 kg/m² Adhesive application onto the wall for Sto-EPS Boards and Sto-Speed Lamellas Additional bonding of insulation boards with rail attachment 5,00-6,00 kg/m² 2,50-3,00 kg/m² Bonding of Resol insulation boards 4,50 kg/m² per mm of layer thickness 1,30 kg/m² The consumption depends on the application method, substrate and consistency, amongst other factors. The stated consumption values are guide values only. Where required, precise consumption values can be established on site. Application Manually or by machine Bonding: Coat the product manually with a stainless steel trowel, or by machine. The insulation boards must be immediately pushed into or floated on the fresh bonding mortar bed and pressed against it. Rev.-Nr.: 1 / EN / / 2/6

3 Amount of bonding for adhesive application onto the wall: With Sto PS rigid foam boards, at least 60 % of the board must be covered with adhesive. With Sto Speed lamellas, at least 50 % of the board must be covered with adhesive. Amount of bonding for adhesive application on the board: At least 40 % of the board must be covered with adhesive. For EWI systems with ceramic cladding, basically an adhesive surface of 60 % of the board must be covered with adhesive. Reinforcing: Apply the product manually with a stainless steel trowel or by machine. Fully embed the mesh in the upper third of the reinforcement in the still damp reinforcing compound. Mesh joints must overlap by min. 10 cm. Diagonal reinforcement must be used on building openings (such as windows, door reveals, etc.). Recommended average reinforcement layer thickness 3-5 mm. The specified value is a reference value. Depending on the application (corners, reveals, etc.), therefore, the layer thickness can vary greatly. Machine application (mixing and/or pumping) must be aimed for. The material can also be applied with commonly available render spray machines for fine textured render. Drying, curing, over-coating The drying time depends on the temperature, wind and relative humidity. During unfavourable weather conditions it is imperative that suitable protective measures (e.g. protection against rain) be applied to the work in progress and freshly completed facades. Depending on the weather, curing takes approx. 1 day/mm of layer thickness. At +20 C temperature (air and substrate) and 65% relative humidity, the next coat can be applied after approx hours. Cleaning tools Indications, recommendations, general information, miscellaneous Delivery Colour shade Tintable Packaging Clean tools with water immediately after use. Further details of the application can be found in the system-related application guideline. The use of QS products is recommended for reinforcing work during the cold and damp time of year. light grey Not tintable. Sack Rev.-Nr.: 1 / EN / / 3/6

4 Storage Storage conditions Storage life Store in dry conditions. This product is low in chromate content. The quality of the material in its original container is guaranteed for the maximum stated storage life. The storage life information is included in the batch number on the container. Explanation of batch number: Digit 1 = last digit of the year, digits = calendar week Example: storage life ends at the end of week 45 in 2011 Certificates / Approvals ETA-09/0058 ETA-07/0023 ETA-09/0267 Z Z Z Z Z Z Z Z StoTherm Classic 5 (EPS and StoArmat Classic plus) European technical approval StoTherm Mineral 6 (MW/MW-L and StoLevell Duo) European technical approval StoTherm Resol European technical approval StoTherm Classic / Vario, bonded on solid substrates StoTherm Classic / Vario / Mineral, rail attachment StoTherm Classic / Vario / Mineral, bonded and dowelled StoTherm Resol, bonded and dowelled StoTherm Mineral L / Classic L EWI systems with ceramic- and natural stone cladding StoTherm Classic / Vario / Classic L, bonded, in timber frame construction Doubled-up EWIS on existing EWIS Identification Product group Composition GISCODE Safety and reliability Bonding and reinforcing mortar White cement, Lime hydrate, Polymer powder, sands, additives ZP1 cement-containing products, low in chromate (chromate content <= 2 ppm) This product is a hazardous material. For further information on handling, storage and disposal of the product, please refer to the current Material Safety Data Sheet, available on request for professional users. Rev.-Nr.: 1 / EN / / 4/6

5 Special information Irritant The information and data in this technical data sheet is intended for common applications and the product's suitability for these, and is based on our findings and experience. Nevertheless, users are responsible for establishing the suitability of the product for its intended use. Applications other than those mentioned explicitly in this technical data sheet may not be carried out unless they have been discussed with Sto AG. Where no approval is given, such applications are at the risk of the user. This applies in particular when the product is used in combination with other products. When a new technical data sheet is published, all previous technical data sheets are no longer valid. Rev.-Nr.: 1 / EN / / 5/6

6 Sto AG Ehrenbachstr. 1 D Stühlingen Phone Fax infoservice.export@stoeu.com CE Rev.-Nr.: 1 / EN / / 6/6