Somaloy 3P. Material Data

Transcription

1 Somaloy 3P Material Data

2 What is the most important property for your application? Somaloy is an isotropic, high resistive Soft Magnetic Composite (SMC) material for electromagnetic applications. Somaloy makes it possible to esign innovative, compact an powerful components that match your specific application an future emans. The secret is the unique 3D flux properties an net-shaping opportunity. Höganäs evelop an provie the Somaloy prouct range which comprises press-reay power mixes. Each Somaloy prouct has properties that can be carefully tailore to ensure optimum performance in your specific component an application. We will help you with material selection that suits your specific nees in your evelopment process. The Somaloy prouct family The Somaloy prouct family inclues 3 groups; 1P, 3P an 5P with ifferent performance levels (P): Somaloy 1P Baseline Somaloy 3P Mechanical strength, permeability Somaloy 5P Lowest losses Mechanical strength 3P 5P 1P Cost-efficient Compact esign High performance Comparing SMC ata to electric steel-sheets SMC ata is measure on single ring components (OD55/ ID45/H5 mm) via square cross-section. The measure SMC sample is a full magnetic core component that can be compare to a punche an stacke electric steelsheet pack representing the same geometry. Data for electric steel-sheets are normally given for a single sheet, teste with an Epstein frame test. SMC is not teste by this metho an thereby ata is not irectly comparable. Aitional esign factors aime for electric steel-sheet stacks oes not apply for SMC. Magnetic losses Fin out more Contact your local sales representative or visit

3 List of content Overview Page Somaloy 3P Prouct Portfolio...4 Typical ata of all proucts with the compaction pressure of 800 MPa Detaile material ata Large particles #40 Somaloy 700HR 3P 800 MPa...5 Somaloy 700HR 3P 600 MPa...6 Somaloy 700 3P 800 MPa...7 Somaloy 700 3P 600 MPa...8 Somaloy P 800 MPa...9 Somaloy P 600 MPa...10 Somaloy power particle Höganäs AB (publ.), June HOG

4 Somaloy Prouct portfolio Somaloy material Large particles #40 Density [g/cm 3 ] Resistivity [µohm m] TRS ambient [MPa] B@ A/m [ T ] 1T µ max Cross-section 5x5 mm 15x15 mm 100 Hz 400 Hz 1000 Hz 2000 Hz 1000 Hz Somaloy 700HR 5P Somaloy P Somaloy 700HR 1P Somaloy 700 1P Somaloy 700HR 3P Somaloy 700 3P Somaloy P Somaloy material Meium particles #100 Density [g/cm 3 ] Resistivity [µohm m] TRS ambient [MPa] B@ A/m [ T ] µ max 100 Hz 1 T es Cross-section 5x5 mm 1 khz 1 T 5 khz T 10 khz 0.1 T Somaloy 130i 5P x15 mm Somaloy 130i 1P Somaloy 500 1P Fine particles #200 Somaloy 110i 1P Somaloy 110i 5P Typical prouct ata 800 MPa compaction pressure, magnetic ata measure accoring to CEI/IEC khz 1 T For more information, please contact your local sales representative.

5 Somaloy 700HR 3P Somaloy 700HR 3P Pressure: 800 MPa 800 MPa Transverse rupture strength/150 o C [MPa] 120/120 SS-ISO 3325 Density [g/cm 3 ] 7.52 SS-ISO 2738 Tensile strength/yiel strength [MPa] 65/65 SS-EN , ISO 2740 Thermal expansion [K -1 ] 11 e-06 ASTM E 228/MPIF 35 Compressive Strength/Yiel [MPa] 600/290 ASTM E9-89a Thermal conuctivity [W/m*K] 25 ISO Young s moulus [GPa] 170 ASTM E Resistivity [μωm] 600 Impact Energy [J] 1.8 SS-EN 10045, SS-EN Power properties Stanars Apparent ensity [g/cm 3 ] 3.16 ISO 3923/1 Flow [s/50g] 35 ISO 4490 Magnetic properties Stanars Green ensity [g/cm 3 ] 7.54 ISO 3927 B@4000A/m [T] 1.31 IEC Green strength [MPa] 28 ISO 3995 B@10000A/m [T] 7 IEC Springback [%] 0.10 ISO 4492, ISO 2740 [A/m] 225 IEC Heat treate im. change [%] ISO 4492, ISO max IEC Total im. change [%] 0.09 ISO 4492, ISO 2740 B [ T ] /60 Hz 100 Hz 200 Hz 300 Hz 400 Hz 500 Hz 600 Hz 700 Hz 800 Hz 900 Hz 1000 Hz 2000 Hz 0,5T / ,0T 5.1/ ,5T 9.5/ Measure accoring to CEI/IEC :2003 on ring sample (OD55 ID45 H5 mm). Loss moel µ 0 M B = * f * B * f 2 * B 2 + Moel is verifie up to T an 5000Hz. B 2 * f 2 * 2 Hysterisis loss B Fiel strength [T] Höganäs AB (publ.). February HOG

6 Somaloy 700HR 3P Somaloy 700HR 3P Pressure: 600 MPa 600 MPa Transverse rupture strength/150 o C [MPa] 130/130 SS-ISO 3325 Density [g/cm 3 ] 7.40 SS-ISO 2738 Tensile strength/yiel strength [MPa] 55/55 SS-EN , ISO 2740 Thermal expansion [K -1 ] 11 e-06 ASTM E 228/MPIF 35 Compressive Strength/Yiel [MPa] 330/240 ASTM E9-89a Thermal conuctivity [W/m*K] 30 ISO Young s moulus [GPa] 170 ASTM E Resistivity [μωm] 300 Impact Energy [J] 1.9 SS-EN 10045, SS-EN Power properties Stanars Apparent ensity [g/cm 3 ] 3.16 ISO 3923/1 Flow [s/50g] 35 ISO 4490 Magnetic properties Stanars Green ensity [g/cm 3 ] 7.43 ISO 3927 B@4000A/m [T] 1.30 IEC Green strength [MPa] 25 ISO 3995 B@10000A/m [T] 3 IEC Springback [%] 0.11 ISO 4492, ISO 2740 [A/m] 230 IEC Heat treate im. change [%] 0 ISO 4492, ISO max IEC Total im. change [%] 0.11 ISO 4492, ISO 2740 B [ T ] /60 Hz 100 Hz 200 Hz 300 Hz 400 Hz 500 Hz 600 Hz 700 Hz 800 Hz 900 Hz 1000 Hz 2000 Hz T 1.6/ T 5.3/ T 11/ Measure accoring to CEI/IEC :2003 on ring sample (OD55 ID45 H5 mm). Loss moel = * f * B * f 2 * B 2 + Moel is verifie up to T an 5000Hz. 0.0 µ 0 M B B 2 * f 2 * 2 Hysterisis loss B Fiel strength [T] Höganäs AB (publ.). February HOG

7 Somaloy 700 3P Somaloy 700 3P Pressure: 800 MPa 800 MPa Transverse rupture strength/150 o C [MPa] 125/125 SS-ISO 3325 Density [g/cm 3 ] 7.57 SS-ISO 2738 Tensile strength/yiel strength [MPa] 65/65 SS-EN , ISO 2740 Thermal expansion [K -1 ] 11 e-06 ASTM E 228/MPIF 35 Compressive Strength/Yiel [MPa] 550/280 ASTM E9-89a Thermal conuctivity [W/m*K] 25 ISO Young s moulus [GPa] 190 ASTM E Resistivity [μωm] 200 Impact Energy [J] 2 SS-EN 10045, SS-EN Power properties Stanars Apparent ensity [g/cm 3 ] 3.32 ISO 3923/1 Flow [s/50g] 34 ISO 4490 Magnetic properties Stanars Green ensity [g/cm 3 ] 7.59 ISO 3927 B@4000A/m [T] 1.37 IEC Green strength [MPa] 24 ISO 3995 B@10000A/m [T] 1.61 IEC Springback [%] 0.10 ISO 4492, ISO 2740 [A/m] 217 IEC Heat treate im. change [%] ISO 4492, ISO max IEC Total im. change [%] 0.09 ISO 4492, ISO 2740 B [T] 0 µ 0 M B /60 Hz 100 Hz 200 Hz 300 Hz 400 Hz 500 Hz 600 Hz 700 Hz 800 Hz 900 Hz 1000 Hz 2000 Hz T / T 5.0/ T 10/ Measure accoring to CEI/IEC :2003 on ring sample (OD55 ID45 H5 mm). Loss moel = * f * B * f 2 * B 2 + Moel is verifie up to T an 5000Hz. B 2 * f 2 * 2 Hysterisis loss B Fiel strength [T] Höganäs AB (publ.). February HOG

8 Somaloy 700 3P Somaloy 700 3P Pressure: 600 MPa 600 MPa Transverse rupture strength/150 o C [MPa] 130/130 SS-ISO 3325 Density [g/cm 3 ] 7.40 SS-ISO 2738 Tensile strength/yiel strength [MPa] 65/65 SS-EN , ISO 2740 Thermal expansion [K -1 ] 11 e-06 ASTM E 228/MPIF 35 Compressive Strength/Yiel [MPa] 350/260 ASTM E9-89a Thermal conuctivity [W/m*K] 30 ISO Young s moulus [GPa] 190 ASTM E Resistivity [μωm] 150 Impact Energy [J] 1.8 SS-EN 10045, SS-EN Power properties Stanars Apparent ensity [g/cm 3 ] 3.32 ISO 3923/1 Flow [s/50g] 34 ISO 4490 Magnetic properties Stanars Green ensity [g/cm 3 ] 7.43 ISO 3927 B@4000A/m [T] 1.34 IEC Green strength [MPa] 21 ISO 3995 B@10000A/m [T] 5 IEC Springback [%] 0.11 ISO 4492, ISO 2740 [A/m] 220 IEC Heat treate im. change [%] ISO 4492, ISO max IEC Total im. change [%] 0.10 ISO 4492, ISO 2740 B [ T ] /60 Hz 100 Hz 200 Hz 300 Hz 400 Hz 500 Hz 600 Hz 700 Hz 800 Hz 900 Hz 1000 Hz 2000 Hz T / T 5.2/ T 11/ Measure accoring to CEI/IEC :2003 on ring sample (OD55 ID45 H5 mm). Loss moel µ 0 M B = * f * B * f 2 * B 2 + Moel is verifie up to T an 5000Hz. B 2 * f 2 * 2 Hysterisis loss B Fiel strength [T] Höganäs AB (publ.). August HOG

9 Somaloy P Somaloy P Pressure: 800 MPa 800 MPa Transverse rupture strength/150 o C [MPa] 140/140 SS-ISO 3325 Density [g/cm 3 ] 7.56 SS-ISO 2738 Tensile strength/yiel strength [MPa] 70/70 SS-EN , ISO 2740 Thermal expansion [K -1 ] 11 e-06 ASTM E 228/MPIF 35 Compressive Strength/Yiel [MPa] 470/290 ASTM E9-89a Thermal conuctivity [W/m*K] 25 ISO Young s moulus [GPa] 170 ASTM E Resistivity [μωm] 70 Impact Energy [J] 1.9 SS-EN 10045, SS-EN Power properties Stanars Apparent ensity [g/cm 3 ] 3.19 ISO 3923/1 Flow [s/50g] 36 ISO 4490 Magnetic properties Stanars Green ensity [g/cm 3 ] 7.54 ISO 3927 B@4000A/m [T] 1.42 IEC Green strength [MPa] 24 ISO 3995 B@10000A/m [T] 1.63 IEC Springback [%] 0.12 ISO 4492, ISO 2740 [A/m] 217 IEC Heat treate im. change [%] ISO 4492, ISO max IEC Total im. change [%] 0.11 ISO 4492, ISO 2740 B [ T ] /60 Hz 100 Hz 200 Hz 300 Hz 400 Hz 500 Hz 600 Hz T / T 5.0/ T 10/ Measure accoring to CEI/IEC :2003 on ring sample (OD55 ID45 H5 mm). Loss moel µ 0 M B = * f * B * f 2 * B 2 + Moel is verifie up to T an 2000Hz. B 2 * f 2 * 2 Hysterisis loss B Fiel strength [T] Höganäs AB (publ.). February HOG

10 Somaloy P Somaloy P Pressure: 600 MPa 600 MPa Transverse rupture strength/150 o C [MPa] 140/140 SS-ISO 3325 Density [g/cm 3 ] 7.42 SS-ISO 2738 Tensile strength/yiel strength [MPa] 60/60 SS-EN , ISO 2740 Thermal expansion [K -1 ] 11 e-06 ASTM E 228/MPIF 35 Compressive Strength/Yiel [MPa] 370/260 ASTM E9-89a Thermal conuctivity [W/m*K] 30 ISO Young s moulus [GPa] 170 ASTM E Resistivity [μωm] 55 Impact Energy [J] 1.9 SS-EN 10045, SS-EN Power properties Stanars Apparent ensity [g/cm 3 ] 3.19 ISO 3923/1 Flow [s/50g] 36 ISO 4490 Magnetic properties Stanars Green ensity [g/cm 3 ] 7.42 ISO 3927 B@4000A/m [T] 1.38 IEC Green strength [MPa] 21 ISO 3995 B@10000A/m [T] 7 IEC Springback [%] 0.11 ISO 4492, ISO 2740 [A/m] 220 IEC Heat treate im. change [%] 0 ISO 4492, ISO max IEC Total im. change [%] 0.11 ISO 4492, ISO 2740 B [ T ] /60 Hz 100 Hz 200 Hz 300 Hz 400 Hz 500 Hz 600 Hz T / T 5.2/ T 11/ Measure accoring to CEI/IEC :2003 on ring sample (OD55 ID45 H5 mm). Loss moel 0.0 µ 0 M = * f * B * f 2 * B 2 + Moel is verifie up to T an 2000Hz. B B 2 * f 2 * 2 Hysterisis loss B Fiel strength [T] Höganäs AB (publ.). February HOG

11 Sween Höganäs AB Höganäs Phone Power of Power Metal power technology has the power to open up a worl of opportunities. The inherent properties of metal powers provie unique possibilities to tailor solutions to match your exact requirements. Our ambition is to constantly wien an grow the range of metal power applications. That s what we call Power of Power. With our leaing position in metal power technology, Höganäs is perfectly place to Brazil China France Germany Höganäs Brasil Lta Mogi as Cruzes Phone brazil@hoganas.com Höganäs (China) Co. Lt Shanghai Phone china@hoganas.com Höganäs France S.A.S. Limas Phone france@hoganas.com Höganäs GmbH Düsselorf Phone germany@hoganas.com help you explore these opportunities. To fin out how you can benefit from the Power of Power, please Inia Höganäs Inia Pvt Lt Pune Phone inia@hoganas.com contact your nearest Höganäs office. Italy Höganäs Italia S.r.l. Rapallo (Genoa) Phone italy@hoganas.com Japan Höganäs Japan K.K. Tokyo Phone japan@hoganas.com Rep. of Korea Höganäs Korea Lt Seoul Phone korea@hoganas.com Russia Höganäs East Europe LLC Saint Petersburg Phone russia@hoganas.com Heaquarter Prouction ArcX tech centres Sales (incl. agents an istributors) PoP centres Spain Taiwan Unite Kingom Unite States Höganäs Ibérica S.A. Mari Phone spain@hoganas.com Höganäs Taiwan Lt Taipei Phone taiwan@hoganas.com Höganäs (Great Britain) Lt Tonbrige, Kent Phone uk@hoganas.com North American Höganäs Co. Hollsopple: PA Phone info@nah.com Höganäs AB (publ.), June HOG