EPOTUF Product Code: Epoxy Resin Solution

Transcription

1 April 2001 EPOTUF Product Code: Epoxy Resin Solution DESCRIPTION EPOTUF is a solvent cut of EPOTUF at 75% solids in xylene. APPLICATIONS High performance two-package systems for coatings Industrial maintenance coatings Marine coatings Flooring Tank linings Structural steel primers Concrete sealers and surfacers FEATURES Fast dry Good flexibility and impact resistance Good corrosion and chemical resistance Low color PROPERTIES Percent Solids, Weight 75 Percent Solids, Volume 68 Viscosity at 25 C, cps 10,000 Color, Gardner-Holdt 3 max. Pounds per Gallon, Solution 9.00 Specific Gravity, 25/25 C 1.08 Solvent Xylene Epoxide Equivalent Weight, Solids 525 STORAGE Store in a cool, dry place, preferably under 80 F to ensure a useful shelf life of at least one year. Read the EPOTUF Material Safety Data Sheet before handling, storing, or using this product.

2 S Red Floor Enamel EB-38505A EPOTUF Mapico 516 Red Iron Oxide (1) Bentone SD-2 (2) Aromatic 150 Type Propylene Glycol Monomethyl Ether High-speed disperse to 5 N.S.: EPOTUF Aromatic 150 Type TOTAL EPOTUF Propylene Glycol Monomethyl Ether Aromatic 150 Type TOTAL TOTAL COMPONENTS A + B 8.34 Pigment Volume Concentration, Percent 0.35 Pigment/Binder Ratio 821 Spread at 1 Mil, Ft 2 per Gallon Percent Solids, Weight Percent Solids, Volume 9.38 Pounds per Gallon 431 VOC, Grams per Liter 3.60 VOC, Pounds per Gallon 70 Viscosity, Initial, Krebs Units >24 Pot Life, Hours 2 Dry Time, Tack-Free, Hours, 1.5 Wet Mils 98 Gloss 60, 3 Mils, 48 Hours Cure (1) Columbian Chemical (2) Elementis White Spraying Enamel EB-38505B EPOTUF Methyl Isobutyl Ketone Tronox CR-800 (1) High-speed disperse to 7 N.S.: EPOTUF Methyl Isobutyl Ketone Diisobutyl Ketone BYK TOTAL EPOTUF n-butanol Xylene TOTAL TOTAL COMPONENTS A + B Pigment Volume Concentration, Percent Pigment/Binder Ratio 662 Spread at 1 Mil, Ft 2 per Gallon Percent Solids, Weight Percent Solids, Volume 9.47 Pounds per Gallon 483 VOC, Grams per Liter 4.03 VOC, Pounds per Gallon 35 Viscosity, #2 Zahn Cup, Seconds >24 Pot Life, Hours 4-5 Dry Time, Tack-Free, Hours (1) Kerr McGee (2) BYK Chemie 2

3 Gloss White Epoxy Enamel Using EPOTUF and EPOTUF AntiTerra U (1) Xylene Tronox CR-800 (2) Bentone SD-2 (3) High-speed disperse to at least 7 NS.: Xylene Methyl Isobutyl Ketone PM Acetate n-butanol TOTAL 58.9 Percent Solids, Weight 44.3 Percent Solids, Volume 9.8 Weight/Gallon, Pounds 0.63/1 Pigment to Binder, Weight Ratio 14.9 Pigment Volume Concentration, Percent 4.0 VOC, Pounds per Gallon 480 VOC, Grams per Liter (1) BYK-Chemie (3) Elementis (2) Kerr McGee EPOTUF Xylene TOTAL TOTAL COMPONENTS A + B Thoroughly mix components A and B 1:1 by volume approximately 30 minutes prior to use. Viscosity, Seconds, #2 Zahn Cup 39 Dry Time, 3 Mils Wet Film, Hours Set Dry 0.5 Through Dry 8.0 Hard Dry 12.0 Corrosion Resistance Salt Fog, 2 MDFT on CRS Field Blisters Field Rust Scribe Blisters 4D Scribe Rust 5 Creepage 1/8 Tape Adhesion 0% Durability Xenon Arc Weatherometer, 84 Hours Gloss Based on 7-Day Ambient Cure Gloss HB Impact Resistance Direct 140 Reverse 120 Solvent Resistance, MEK Double Rubs >100 Chemical Resistance, 3-Hour Spot Test, Covered 10% Acetic Acid 5 2% Nitric Acid 5 10% Sulfuric Acid 5 10% Sodium Hydroxide 5 10% Hydrochloric Acid 5 Acetone 4 Xylene 5 Isopropanol 5 Gasoline 4 Ethanol 5 1:1 Ethanol/Water 5 3

4 Anticorrosive Epoxy Primer Using EPOTUF and EPOTUF Methyl Isobutyl Ketone Cyclohexanone Red Oxide R5098 (1) Wollastocoat 10ES (2) Halox CW-2230 (3) Bentone SD-2 (1) High-speed disperse to at least 4 NS EPOTUF Methyl Isobutyl Ketone Xylene TOTAL 58.8 Percent Solids, Weight 40.9 Percent Solids, Volume Weight/Gallon, Pounds 1.24/1 Pigment to Binder Weight Ratio 30.0 Pigment Volume Concentration, Percent 4.1 VOC, Pounds per Gallon 492 VOC, Grams per Liter (1) Elementis (3) Halox Pigments (2) NYCO EPOTUF n-butanol Xylene TOTAL TOTAL COMPONENTS A + B Thoroughly mix components A and B (2:1 by volume) approximately one hour prior to use. Viscosity, Seconds, #2 Zahn Cup 37 Pot Life, Hours >24 Dry Time, 8 MWFT, Set, Hours ½ Tack Free, Hours 4 Dry Hard Overnight Salt Fog Resistance Scribe Creepage 1/16 Scribe Blistering 8M Field Rust Field Blistering 8M Based on 7-day ambient cure 3.5 mil films on polished cold-rolled steel 2H Impact Resistance Forward 52 Reverse 10 1/8 Conical Mandrel Bend Pass Adhesion, Cross-Hatch Polished CRS 100% Unpolished CRS 95% Aluminum 75% Chemical Resistance, 8-Hour Spot Test 10% Acetic Acid Poor 10% Sulfuric Acid Good 10% Sodium Hydroxide Excellent Xylene Fair Methanol Fair Humidity Resistance, QCT Cabinet Blistering 4

5 High Build Epoxy Mastic Using EPOTUF , and EPOTUF EPOTUF Methyl Isobutyl Ketone MPA 60X (1) Bentone SD-2 (1) Cab-O-Sil M-5 (2) Imsil A-10 (3) High-speed disperse to at least 5 N.S Methyl Isobutyl Ketone TOTAL EPOTUF Xylene Ti-Pure R-960 (4) High-speed disperse to at least 7 N.S Nevoxy EPX-L (5) MPA 60X (1) Nytal 400 (6) Minex 4 (7) High-speed disperse to at least 5 N.S Nevoxy EPX-L Xylene TOTAL 86.1 Percent Solids, Weight 74.7 Percent Solids, Volume 12.8 Weight/Gallon, Pounds 1.75/1 Pigment to Binder, Weight Ratio 39.2 Pigment Volume Concentration, Percent 1.8 VOC, Pounds per Gallon 213 VOC, Grams per Liter (1) Elementis (5) Neville (2) Cabot (6) R. T. Vanderbilt (3) Unimin (7) Indusmin (4) DuPont Combine and B (1:1 by volume) and allow a 30 minute induction time prior to use. Thin with a50:50 blend of isopropanol and xylene. Mix Ratio, Weight 53.3 / 46.7 VOC, Pounds per Gallon, After Thinning 2.16 Viscosity, Seconds, #4 Zahn Cup 26 Pot Life, Hours Dry Time, 15 MWFT, Set-to-Touch, Hours 10 Through Dry, Hours 13 Based on 7-Day Ambient Cure 2 Coats of 6 Mils Each on Polished CRS B, after 100 MEK DR 4B Impact Resistance, Forward 60 Chemical Resistance, 24 hour spots, 8 MDFT 10% Acetic Acid 4 10% Sulfuric Acid 3 10% Hydrochloric Acid 3 10% Sodium Hydroxide 5 Xylene 4 Methanol 4 Water 5 Acetone 3 Corrosion Resistance, Salt Fog, 9 Mil Film on CRS 2000 Scribe Blisters Scribe Corrosion Creep 1/32 1/8 Field Blistering Field Rusting Corrosion Resistance, Salt Fog, 9 Mil Film on Hot Rolled Blasted Steel 2000 Scribe Blisters 2 (one) 0 (two) Scribe Corrosion Creep 1/32 1/32 Field Blistering Field Rusting Corrosion Resistance, Salt Fog, 11.5 Mil Film on Hot Rolled Blasted Steel 2000 Scribe Blisters 2 (one) 2 (one) Scribe Corrosion Creep 1/16 1/8 Field Blistering Field Rusting 5