Regular Hi-Dense Hi-Temp. Viscosity (Approx.) time to deliver psi thru a.104" orifice (seconds)

Transcription

1 3 Scotch-Weld TM 2214 Regular 2214 Hi-Dense 2214 Hi-Temp 2214 Hi-Temp New Formula 2214 Non-Metallic Filled Technical Data November, 2010 Product Description One part 250 F (121 C) curing 100% solids, 3M Scotch-Weld Epoxy Adhesive 2214 is a paste consistency epoxy adhesive designed for bonding metals and many high temperature plastics such as fiberglass reinforced plastic, polyester, and phenolics. 3M Scotch-Weld Adhesive 2214 Regular is an aluminum filled general purpose product for use in applications where high strength bonds are needed in a temperature range of -67 F to 250 F (-53 C to 121 C). 3M Scotch-Weld Adhesive 2214 Hi-Dense is a deaerated version of Scotch- Weld adhesive 2214 regular for use where a very dense, void free bondline is required. 3M Scotch-Weld Adhesive 2214 Hi-Temp and Hi-Temp New Formula are aluminum filled, deaerated products for use where higher strengths are required between 180 F to 350 F (82 C to 177 C). 3M Scotch-Weld Adhesive 2214 Non-Metallic Filled is a non-metal filled version of Scotch-Weld adhesive 2214 regular. Typical Uncured Physical Properties Hi-Temp New Formula Non-Metallic Filled Viscosity (Approx.) time to deliver psi thru a.104" orifice (seconds) Viscosity (Brookfield) Because of Thixotropic paste nature of these products Brookfield viscosity will be over 1,000,000 cps. Color Gray Gray Gray Gray Cream Base Modified Modified Modified Modified Modified Epoxy Epoxy Epoxy Epoxy Epoxy Net Weight (lbs/gal)

2 Typical Cured Physical Properties Hi-Temp New Formula Non-Metallic Filled Color Gray Gray Gray Gray Brown Cream to Tan Shore D Hardness (Approx.) Elongation (Approx. %) <2 <2 1 1 <2 Ultimate Tensile 10,000 10,000 8,000 9,000 (Approx. psi) Modulus Elasticity 750, , , ,000 (Approx. psi) Typical Thermal Properties (Cured) Thermal Conductivity Coefficient of Thermal Expanse (BTU/HR/FT2/ F/FT) (in./in./ C) 3M Scotch-Weld Adhesive 2214 Regular x 10-6 (between 0-80 C) 3M Scotch-Weld Adhesive 2214 Hi-Dense x 10-6 (between 0-80 C) 3M Scotch-Weld Adhesive 2214 Hi-Temp x 10-6 (between 0-80 C) 3M Scotch-Weld Adhesive 2214 Hi-Temp New Formula x 10-6 (between C) 3M Scotch-Weld Adhesive 2214 Non-Metallic Filled x 10-6 (between C) Typical Electrical Properties (Cured) Dielectric Constant (1) ASTM-D-150 Dissipation Factor (2) ASTM-D-150 Power Range 1.00 KC Test Temperature 73 F (23 C) 140 F (60 C) 194 F (90 C) 219 F (104 C) Scotch-Weld adhesive 2214 Regular (1) (2) Scotch-Weld adhesive 2214 Hi-Dense (1) (2) Scotch-Weld adhesive 2214 Hi-Temp (1) (2) Scotch-Weld adhesive 2214 Non-Metallic (1) Filled (2) Scotch-Weld adhesive 2214 Hi-Temp (1) New Formula (2) Arc Resistance ASTM-D Surface Resistivity ASTM-D-257 Dielectric Strength ASTM-D-149 Volume Resistivity ASTM-D

3 Typical Electrical Properties (Cured) [continued] ARC Resistance Dielectric Strength Surface Volume (Seconds) (Volts Per Mil Thickness) Resistivity Resistivity (500 Volts-DC) (500 Volts-DC) Sample 3M Scotch-Weld Epoxy Thickness Ohms/Square Ohms-CM Adhesive 2214 Volts/Mil Inches 73 F (23 C) 73 F (23 C) Regular x x Hi-Dense x x Hi-Temp x x Non-Metallic Filled x Handling/Curing Information Directions for Use 1. Warm products to room temperature before opening containers to restore proper application consistency and to prevent moisture condensation on adhesive surface. Containers may be stored at room temperature for 1-2 days to thaw. Do not warm at temperatures above 80 F (27 C). 2. For high strength structural bonds, paint, oxide films, oils, dust, mold release agents and all other surface contaminants must be completely removed. However, the amount of surface preparation directly depends on the substrates, the required bond strength, environmental aging resistance, and requirements determined by the user in light of the user s particular purpose and method of application. For specific surface preparations on common substrates, see the section on surface preparation. 3. Use gloves to minimize skin contact and do not use solvents for cleaning hands. 4. For maximum bond strength, apply product evenly to both surfaces to be joined. 5. Join the adhesive coated surfaces and heat cure using the following bondline temperature and time for the specific product being used. Any of the following cure cycles will result in a full cure. 3M Scotch-Weld Adhesive 2214 Regular } F (121 C) 3M Scotch-Weld Adhesive 2214 Hi-Dense F (149 C) 3M Scotch-Weld Adhesive 2214 Hi-Temp F (177 C) 3M Scotch-Weld Adhesive 2214 Non-Metallic Filled 3M Scotch-Weld Adhesive 2214 Hi-Temp F (121 C) New Formula F (149 C) 6. Keep parts from moving during cure as contact pressure is necessary. 7. Cleanup can be accomplished with solvent such as 3M Scotch-Grip Solvent No. 3 or Methyl Ethyl Ketone.* *Note: Prior to use of these solvents, extinguish or eliminate any ignition sources and read and follow supplier s environmental, health, and safety recommendations listed on the MSDS and product label

4 Surface Preparation The following cleaning methods are suggested for common surfaces: Steel: 1. Wipe free of dust with oil-free solvent such as Methyl Ethyl Ketone.* 2. Sandblast or abrade using clean fine grit abrasives. 3. Wipe again with solvent to remove loose particles. Aluminum: 1. Vapor Degrease Perchloroethylene* condensing vapors for 5-10 minutes. 2. Alkaline Degrease Oakite 164 solution (9-11 oz./gallon water) at 190 F ± 10 F (87 C ± 5 C) for minutes. Rinse immediately in large quantities of cold running water. 3. Acid (FPL) Etch Place panels in their following solution for 10 minutes at 150 F ± 5 F (66 C ± 2 C). Sodium Dichromate oz./gallon Sulfuric Acid, 66 Be oz./gallon 2024-T3 aluminum (dissolved) 0.2 oz./gallon minimum Tap water as needed to balance 4. Rinse Rinse panels in clear running tap water. 5. Dry Air dry 15 minutes; force dry 10 minutes at 150 F ± 10 F (66 C ± 5 C). 6. If primer is to be used, it should be applied within 4 hours after surface preparation. Plastics: 1. Solvent wipe with Isopropyl Alcohol.* 2. Abrade using clean fine grit abrasives. 3. Solvent wipe with Isopropyl Alcohol.* Rubbers: 1. Solvent wipe with Methyl Ethyl Ketone.* 2. Abrade using clean fine grit abrasives. 3. Solvent wipe with Methyl Ethyl Ketone.* Glass: 1. Solvent wipe with acetone or Methyl Ethyl Ketone.* Note: For glass applications which will be subjected to high moisture/humidity conditions, 3M Scotch-Weld Primer EC-3901 should be used to prime the glass. *Note: Prior to use of these solvents, extinguish or eliminate any ignition sources and read and follow supplier s environmental, health, and safety recommendations listed on the MSDS and product label. Application/Equipment Information These products may be applied by spatula, trowel, or flow equipment. Dispensing equipment is available for intermittent or production line use. These systems are ideal because of their variable shot size and flow rate characteristics and are adaptable to most applications. For more information, contact your local 3M sales representative

5 Equipment Suggestions Note: Minimum pumping temperature is 65 F (18 C) for all products. Regular Production Extrusion Equipment Ratio 55:1 with a chopping check Pneumatic type Super high High valve and priming piston, capacity-12 psi on pressure with pressure 8 in. air motor. 3.7 cu. in./cycle material surface standard lining type Output based on 1/4" tip flow gun (material temperature 65 F [18 C]) (minimum pumping temperature is 65 F [18 C]) Length-20', I.D.-1/2" 4800*.36 Length-20', I.D.-3/4" 4800* 1.0 Non-Metallic Filled Production Extrusion Equipment Ratio 38:1 with a chopping check Pneumatic type Super high High valve and priming piston capacity-10 psi on pressure with pressure material surface standard lining type Output based on 3/8" tip flow gun-8" diameter air motor (minimum pumping temperature is 65 F [18 C]) Length-10', I.D.-3/4" Length-20', I.D.-3/4" Length-20', I.D.-3/4" +10, I.D.-1/2" Length-20', I.D.-1/2" Hi-Temp Production Extrusion Equipment Ratio 40:1 with a chopping check Pneumatic type Super high High valve and priming piston, capacity-12 psi on pressure with pressure 6 in. air motor. 2 cu. in./cycle material surface standard lining type Output based on 1/4" tip flow gun (material temperature 65 F [18 C]) Length-20', I.D.-1/2" Length-20', I.D.-3/4"

6 Equipment Suggestions (continued) Note: Minimum pumping temperature is 65 F (18 C) for all products. Hi-Dense Production Extrusion Equipment Ratio 55:1 with a chopping check Pneumatic type Super high High valve and priming piston, capacity-12 psi on pressure with pressure 8 in. air motor. 3.7 cu. in./cycle material surface standard lining type Output based on 1/4" tip flow gun (material temperature 65 F [18 C]) (minimum pumping temperature is 65 F [18 C]) Length-20', I.D.-1/2" 4500*.45 Length-20', I.D.-3/4" 4500*.9 Hi-Temp New Formula Production Extrusion Equipment Ratio 55:1 with a chopping check Pneumatic type Super high High valve and priming piston, capacity-12 psi on pressure with pressure 8 in. air motor. 3.7 cu. in./cycle material surface standard lining type Output based on 1/4" tip flow gun (material temperature 65 F [18 C]) (minimum pumping temperature is 65 F [18 C]) Length-20', I.D.-1/2" 4800*.36 Length-20', I.D.-3/4" 4800* 1.0 *These pressures will require a special consideration during hose selection. They are actual working pressures. Typical Adhesive Performance Characteristics Test Temperature Note: All of the following data was developed using a cure cycle of F (121 C) under 25 psi pressure except Scotch-Weld adhesive 2214 Hi-Temp New Formula which was 60 minutes at 250 F (121 C). A. Aluminum Overlap Shear Overlap shear strength was measured on FPL etched 1" wide by 1/2" overlap specimens. The bonds were made from 2 panels of 4" x 7" x.063", 2024 T3 clad aluminum bonded together and cut into 1" wide specimens. The separation rate of the testing jaws was.1"/minute. Tests similar to ASTM D (All data in psi). or typical only and should not be used for specification purposes. Hi-Temp New Formula Non-Metallic Filled -67 F (-53 C) F (24 C) F (82 C) F (121 C) F (149 C) F (177 C)

7 Typical Adhesive Performance Characteristics (continued) B. Aluminum T-Peel T-Peel bonds were measured on 1" wide specimens cut from two FPL etched 8" x 8" x.032" 2024 T3 clad aluminum panels bonded together. The separation note of the testing jaws was 20"/minute. Tests similar to ASTM D (All data in lbs./in. of width.) or typical only and should not be used for specification purposes. Hi-Temp Non-Metallic Test Temperature New Formula Filled 75 F (24 C) C. Steel Overlap Shear Overlap shear strength was measured on 1" wide by 1/2" overlap specimens. These bonds were made on 1" x 4" x.035" thick cold rolled steel which was MEK solvent wiped prior to bonding. The separation rate of the testing jaws was.1"/min. Tests similar to ASTM D (All data in psi.) or typical only and should not be used for specification purposes. Hi-Temp Non-Metallic Test Temperature New Formula Filled -67 F (-53 C) F (24 C) F (82 C) F (121 C) F (149 C) F (177 C) D. Steel T-Peel T-Peel bonds were measured on two 1" wide x 8" long specimens bonded together. These bonds were made on MEK wiped.035" steel. After bonding they were then pulled apart in 180 Peel at a jaw separation rate of 20"/minute rate. Tests similar to ASTM D (All data in lbs./in. of width.) or typical only and should not be used for specification purposes. Hi-Temp Non-Metallic Test Temperature New Formula Filled 75 F (24 C)

8 Environmental Resistance Note: The following data is overlap shear after aging for 365 days in the specified environment. Tests were run on FPL etched aluminum and solvent degreased, sandblasted.035" thick cold rolled steel. Bonds and tests similar to ASTM D (All data in psi.) Aluminum Steel Aluminum Steel Tap 75 F (24 C) % relative 120 F (49 C) Ethyl F (24 C) Storage Store products at 40 F (4 C) or below for maximum storage life. Higher temperatures reduce normal storage life. Rotate stock on a first-in-first-out basis. CAUTION: Products are heat sensitive. Storage above 130 F (54 C) may cause an exothermic reaction resulting in evolution of excessive heat, noxious fumes, and possibly fire. Shelf Life All of these products have a shelf life of 8 months when stored in their unopened 40 F (4 C) and 12 0 F (-18 C). Precautionary Information Refer to Product Label and Material Safety Data Sheet for health and safety information before using this product. For additional health and safety information, call or (651) Technical Information The technical information, recommendations and other statements contained in this document are based upon tests or experience that 3M believes are reliable, but the accuracy or completeness of such information is not guaranteed. Product Use Many factors beyond 3M s control and uniquely within user s knowledge and control can affect the use and performance of a 3M product in a particular application. Given the variety of factors that can affect the use and performance of a 3M product, user is solely responsible for evaluating the 3M product and determining whether it is fit for a particular purpose and suitable for user s method of application. Warranty, Limited Remedy, and Disclaimer Unless an additional warranty is specifically stated on the applicable 3M product packaging or product literature, 3M warrants that each 3M product meets the applicable 3M product specification at the time 3M ships the product. 3M MAKES NO OTHER WARRANTIES OR CONDITIONS, EXPRESS OR IMPLIED, INCLUDING, BUT NOT LIMITED TO, ANY IMPLIED WARRANTY OR CONDITION OF MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE OR ANY IMPLIED WARRANTY OR CONDITION ARISING OUT OF A COURSE OF DEALING, CUSTOM OR USAGE OF TRADE. If the 3M product does not conform to this warranty, then the sole and exclusive remedy is, at 3M s option, replacement of the 3M product or refund of the purchase price. Limitation of Liability Except where prohibited by law, 3M will not be liable for any loss or damage arising from the 3M product, whether direct, indirect, special, incidental or consequential, regardless of the legal theory asserted, including warranty, contract, negligence or strict liability. ISO 9001: This Industrial Adhesives and Tapes Division product was manufactured under a 3M quality system registered to ISO 9001:2008 standards. Industrial Adhesives and Tapes Division 3M Center, Building 225-3S-06 St. Paul, MN (Fax) Recycled Paper 40% pre-consumer 10% post-consumer 3M and Scotch-Weld are trademarks of 3M Company. Printed in U.S.A. 3M (11/10)