WELD PROCEDURE DATA. Carrier Pipe Thickness (WT): 6.4 mm < WT = 31.8 mm (Design and CSA Z662 Cl )
|
|
- Malcolm Clarke
- 6 years ago
- Views:
Transcription
1 WELD PROCEDURE DATA WPS: WEI-30-1 Rev. 0 Application: Branch and Lap (Sleeve) Connections on non-flowing, gas lines which are either pressured or non-pressured. Supporting PQR: WEI (Branch) Qualification Limits: Carrier Pipe Diameter (D): 25.4 mm < D = 1067 mm (Design) Carrier Pipe Thickness (WT): 6.4 mm < WT = 31.8 mm (Design and CSA Z662 Cl ) Branch Diameter: < 60.3 mm (CSA Z662 Table 10.2 and SP OM) Branch Thickness: 4.8 mm < WT = 25.4 mm (ASME Sec. IX QW 450) Sleeve Thickness : As per design requirements Material Grade: < Grade 483 (ASME Sec. IX QW-153). CE: 0.45 (Lab Test & CSA Z662 Cl ). Electrodes: Classification: E Size: 3/32, 1/8 and 5/32 Service: Sweet and sour Special Requirements: Qualification Code: Welding limited to non flowing condition CSA Z662, Cl. 10.9, and ASME Sec. IX. 1
2 QW-482 WELDING PROCEDURE SPECIFICATIONS (WPS) (Section IX, ASME Boiler and Pressure Vessel Code) WPS-WEI-30-1 REV 0 Company Name: Westcoast Energy Inc By: H. M. Yamauchi Welding Procedure Specification: WEI-30-1 Date: Feb. 20, 2004 Supporting: PQR , 48.3 mm Branch Welding Process(es): SMAW JOINTS (QW-402) Joint Design Groove, Fillet Backing: Nil Backing Material (Type): Nil BASE MATERIALS (QW-403) S-1 Group 1 to S-1 Group 1. Typical Materials: API 5L X52, ASTM A333 Gr. 6 Qualification: Carrier Pipe Thickness Limitation > 6.4 mm Branch Thickness: 4.8 mm < WT < 17.4 mm Sleeve Thickness: As per design requirement. FILLER METALS (QW-404) Spec. No. (SFA): 5.1 AWS No. (Class): E F-No: 4 A-No: 1 Size of Filler Metals 3/32,1/8 Deposited Weld Metal Groove: 5.1 mm Fillet: min. 6.0 mm, max branch WT 2
3 QW-482 WELDING PROCEDURE SPECIFICATIONS (WPS) (Section IX, ASME Boiler and Pressure Vessel Code) WPS-WEI-30-1 REV 0 POSITIONS (QW-405) Position(s) of Weld Joint: Welding Progression: Position(s) of Fillet: Branch 6G. Header Horizontal 5G Slightly uphill for branch. All PREHEAT (QW-406) Preheat Temp. Min: 120 C Inter-pass Temp. Max: 120 C C Instructions: POSTWELD HEAT TREATMENT (QW-407) Temperature Range: N/A Time Range: -- TECHNIQUE (QW-410) Number of welders: One, or two for branch, two for sleeves. Type of line-up clamps: Mechanical Length of time line-up clamps to be held: Until weldment is tacked String or Weave Bead: String, weave up to 3X electrode diameter. Initial and inter-pass cleaning: Brush and grind weld metal to clean metal. Filler Metal Weld Layers Class Dia. Type Polar. Current Amp. Range Volt Range Travel Speed Range cm/min Heat Input KJ/mm 1 E /32 DCEN/EP E /8 DCEN/EP , 3, 4. E /8 DCEP E /32 DCEP The minimum heat input shall not be less than that outlined above. The weld beads should be deposited in near sequential order as indicated on sketch. The temper bead, where employed, shall be deposited on top of last pass on the header wall, as close as possible to the extremity, without impinging on the header wall. After temper bead has cooled to room temperature temper bead shall be ground to acceptable weld profile. 3
4 QW-483 Procedure Qualification Record (PQR) QW-201.2, Section IX, ASME Boiler and Pressure Code PQR WEI Company: Westcoast Energy Inc Procedure Qualification Record: WEI , Branch Weld Date: Feb. 16, 2004 WPS WEI-30-1 Welding Process(es): SMAW Types (Manual, Automatic, Semi-Auto) Manual Joints Base Metals Postweld Heat Treatment (QW-407) Material: Header 762 mm OD x 9.5 mm API 5L X52 CE Temperature: N/A Time Branch 48.3 mm OD x 5.1 mm WT ASTM A333 Gr.6 CE S-1 Grp. 1 to S-1 Grp 1 Gas (QW-408) Shielding Trailing Backing Percent Composition Gas(es) (Mixture) Flow Rate N/A Filler Materials (QW-404) Electrical Characteristics (QW-409) SFA Specification: 5.1 Electrode Polarity Amps Volts cm/min kj/mm AWS Classification: E /32 DCEN Filler Metal F-No 4 1/8 DCEP Weld Metal Analysis A-No 1. Size of Filler Metal: 3/32, 1/8 Technique (QW-410) Deposited Weld Metal: 8.6 mm groove + fillet Travel Speed: cm / min. String or Weave Bead: String with slight wave (3 X electrode) Position (QW-405) Oscillation: -- Position: Header Horizontal, Branch 6G Multi-pass or Single Pass (per side): Multi-pass Weld Progression: Essentially uphill Single or multiple electrodes: N/A Preheat (QW-406) Preheat Temp: Min 120 C Interpass Temp: Max 300 C 4
5 QW-483 Procedure Qualification Record (PQR) QW-201.2, Section IX, ASME Boiler and Pressure Code PQR WEI Tensile Test (QW-150) Specimen No. Width Thickness Area Ultimate Total Load (lb) N/A Ultimate Unit Stress (psi) Type of Failure and Location Guided-Bend Tests (QW-160) CSA Z662, Clause Type and Figure No. Result Passed -see attached Bacon Donaldson File# A March 05, 2004 Report #4 Rev. 1 Hardness Tests and Macroexamination Fillet-Weld Test (QW-180) CSA Z662 clause Hardness Passed, see attached Bacon Donaldson File #A , May 3, 2004 Report #1 Rev. 1 Macro- Passed, see attached Bacon Donaldson File #A March 5, 2004 Report #4 Rev. 1 Tests Chemistry : (Header 0.45): 0.43 See attached file # A Report 12 Rev. 1 Welder s name: Mike Doll Clock No. Stamp No. Tests conducted by: Canspec (Bacon Donaldson) Laboratory Test No. We certify that the statements in this record are correct and that the test welds were prepared, welded, and tested in accordance with the requirements of CSA Z-662 Code Date Mar Approved By: Henry Yamauchi 5
6 Bacon Donaldson Phone: (604) Horseshoe Way Fax: (604) Richmond, BC, Canada V7A 4V4 Consulting Engineers A Rockwood Company FILLET WELD HARDNESS TEST REPORT DUKE ENERGY 1333 West Georgia Street Vancouver, BC V6E 3K9 Attention: HENRY YAMAUCHI Date: May 3, 2004 File No: A P.O. No: Report No: 1 Description: 1½" Ø Branch on Ambient Header (WPS #30-1) WPS #: 30-1, PQR # Name of Welder: Randall Roberts Reg. #: Hardness Test Method: ASTM E Test Specification: CSA Z662-03, Clause Scale: Vickers Hardness Number (1 Kg Load) HARDNESS READING (HV) Sample ID WPS# Location Average (of 1 to 5) MM2 HAZ on Pipe MM2 HAZ on Attachment MM3 HAZ on Pipe MM3 HAZ on Attachment Province of British Columbia authorized testing agency for boiler, pressure vessel and pressure piping: No. TA-15. Test machine calibrated to ASTM E4 and CSA A23.2-9C specifications. Specimens will be disposed of after 30 days unless alternate provisions are made. Reported by: Reviewed by: Wesley Narciso, E.I.T. David Kwong, C.Tech SCOPE OF SERVICES: The agreement of Bacon Donaldson to perform services extends only to those services provided for in writing. Under no circumstances shall such services extend beyond the performance of the requested services. It is expressly understood that all descriptions, comments and expressions of opinion reflect the opinions or observations of Bacon Donaldson based on information and assumptions supplied by the owner/operator and are not intended nor can they be construed as representations or warranties. Bacon Donaldson is not assuming any responsibilities of the owner/operator and the owner/operator retains complete responsibility for the engineering, manufacture, repair and use decisions as a result of the data or other information provided by Bacon Donaldson. In no event shall Bacon Donaldson's liability in respect of the services referred to herein exceed the amount paid for such services. STANDARD OF CARE: In performing the services provided, Bacon Donaldson uses the degree, care, and skill ordinarily exercised under similar circumstances by others performing such services in the same or similar locality. No other warranty, expressed or implied, is made or intended by Bacon Donaldson. 6
7 Bacon Donaldson Phone: (604) Horseshoe Way Fax: (604) Richmond, BC, Canada V7A 4V4 Consulting Engineers A Rockwood Company WELDER QUALIFICATION TEST DUKE ENERGY P.O. Box 1150 Hope, BC V0X 1L0 Attention: BARRY WESTGATE Date: March 5, 2004 File No: A P.O. No: Report No: 4, Revision 1 Sample Description: 1½" Branch onto ambient header Lab Sample ID: K Procedure No: WPS # 30-1, PQR # Welding Process: Base Material: Carbon Steel Filler Material: Test Sample Size: 1½" Pipe Welder ID: Randall Roberts Reg. # Test Specification: CSA Z Specimen Identification Type of Bend Results *BEND TEST Specimen Identification Type of Bend Results KF1 Face Acceptable KF2 Face Acceptable * As per CSA Z662 - Clause **MACROSECTION TEST MACRO EXAM AND HARDNESS TEST Specimen Identification Results Specimen Identification Results KM2 KM3 Acceptable Acceptable ** As per CSA Z662 - Clause Province of British Columbia authorized testing agency for boiler, pressure vessel and pressure piping: No. TA-15. Test machine calibrated to ASTM E4 and CSA A23.2-9C specifications. Specimens will be disposed of after 30 days unless alternate provisions are made. Reported by: Reviewed by: David Kwong, CTech Murray Swayze, P.Eng. SCOPE OF SERVICES: The agreement of Bacon Donaldson to perform services extends only to those services provided for in writing. Under no circumstances shall such services extend beyond the performance of the requested services. It is expressly understood that all descriptions, comments and expressions of opinion reflect the opinions or observations of Bacon Donaldson based on information and assumptions supplied by the owner/operator and are not intended nor can they be construed as representations or warranties. Bacon Donaldson is not assuming any responsibilities of the owner/operator and the owner/operator retains complete responsibility for the engineering, manufacture, repair and use decisions as a result of the data or other information provided by Bacon Donaldson. In no event shall Bacon Donaldson's liability in respect of the services referred to herein exceed the amount paid for such services. STANDARD OF CARE: In performing the services provided, Bacon Donaldson uses the degree, care, and skill ordinarily exercised under similar circumstances by others performing such services in the same or similar locality. No other warranty, expressed or implied, is made or intended by Bacon Donaldson. 7
8 Bacon Donaldson Phone: (604) Horseshoe Way Fax: (604) Richmond, BC, Canada V7A 4V4 Consulting Engineers A Rockwood Company CHEMICAL ANALYSIS REPORT DUKE ENERGY 1333 West Georgia Street Vancouver, BC V6E 3K9 Attention: HENRY YAMAUCHI Date: February 20, 2004 File No: A P.O. No: Report No: 12, Revision 1 Description: 1.5", 4", Header with CE 0.45 and Header Sample for WPS # 16-1, 30-1 Sample ID: Test Method: Spectrographic Analysis TEST RESULTS Element Chemical Composition (%) 1.5" 4" Header (.45) Header Carbon Manganese Phosphorous Sulphur Silicon Nickel Copper Chromium Molybdenum Niobium Vanadium Aluminum Boron < < < < Caron Equivalent (CE) Reported by: David Kwong, CTech Reviewed by: SCOPE OF SERVICES: The agreement of Bacon Donaldson to perform services extends only to those services provided for in writing. Under no circumstances shall such services extend beyond the performance of the requested services. It is expressly understood that all descriptions, comments and expressions of opinion reflect the opinions or observations of Bacon Donaldson based on information and assumptions supplied by the owner/operator and are not intended nor can they be construed as representations or warranties. Bacon Donaldson is not assuming any responsibilities of the owner/operator and the owner/operator retains complete responsibility for the engineering, manufacture, repair and use decisions as a result of the data or other information provided by Bacon Donaldson. In no event shall Bacon Donaldson's liability in respect of the services referred to herein exceed the amount paid for such services. STANDARD OF CARE: In performing the services provided, Bacon Donaldson uses the degree, care, and skill ordinarily exercised under similar circumstances by others performing such services in the same or similar locality. No other warranty, expressed or implied, is made or intended by Bacon Donaldson. Attach 4 - WPS 30-1 Rev0.doc
QW-482 WELDING PROCEDURE SPECIFICATION (WPS)
QW-482 WELDING PROCEDURE SPECIFICATION (WPS) Company Name: J.T. Thorpe & Son, Inc. By: J. Jacob Dupree, Q.C. Manager Welding Procedure Specification No.: JTT-03 Date: 9/20/2016 rev. 3 Supporting PQR No.(s)
More informationQW-482 WELDING PROCEDURE SPECIFICATION (WPS)
QW-482 WELDING PROCEDURE SPECIFICATION (WPS) Company Name: J.T. Thorpe & Son, Inc. By: J. Jacob Dupree, P.E., Q.C. Manager Welding Procedure Specification No.: JTT-24-CVN Revision No. 0 November 5, 2010
More informationQW-482 WELDING PROCEDURE SPECIFICATION (WPS)
QW-482 WELDING PROCEDURE SPECIFICATION (WPS) Company Name: J.T. Thorpe & Son, Inc. By: J. Jacob Dupree, P.E., Q.C. Manager Welding Procedure Specification No.: JTT-22-STUD Revision No. 0 Date: 4/15/2009
More informationWELDING PROCEDURE SPECIFICATION NO
NATIONAL CERTIFIED PIPE WELDING BUREAU WELDING PROCEDURE SPECIFICATION NO. 1-7-1 FOR GAS METAL ARC WELDING WITH FLUXCORE WIRE (GMAW-FC) SEMI-AUTOMATIC OR MACHINE OF CARBON STEEL PIPE, VALVES, FITTINGS
More informationWELDING PROCEDURE SPECIFICATION NO
NATIONAL CERTIFIED PIPE WELDING BUREAU WELDING PROCEDURE SPECIFICATION NO. 45-32-1 FOR GAS TUNGSTEN ARC WELDING (GTAW) AND SHIELDED METAL ARC WELDING (SMAW) OF NICKEL ALLOY 20 (UNS N08020) PIPE, VALVES,
More informationENBRIDGE PIPELINES INC. WELDING PROCEDURE DATA SHEET
APPLICATION: Branch, Weld-O-Let, Fillet Weld New Construction & Non-Product Filled Pipelines CODE: CSA Z662-11 PROJECT: BPP (CA) MATERIAL GRADE: Run: 414 MPa (X-60) SMYS Carbon Equivalent 0.28 Maximum
More informationPIPELINE WELDING PROCEDURE SPECIFICATION
PIPELINE WELDING PROCEDURE SPECIFICATION Davco Welding Ltd. 1219 3 Avenue Wainwright, Alberta T9W 1K9 WPS No: Scope: DAV-16 This welding procedure specification details the procedure to be followed for
More informationAmerican Welding Society Nashville Section. Welding Procedure Development
American Welding Society Nashville Section Welding Procedure Development AWS & ASME Welding Procedures Welding Procedure Specification (WPS) Written document that provides direction to the welder for making
More information1. Poor attitude toward any of the other students, instructors, or judges. 2. Failure to use personal protective equipment (PPE).
Welding Contest Rules and Score Sheet 2016 4G Rules: 1. Be Safe & Have Fun 2. Can tack in any position but groove welding must be in accordance with your WPS. 3. Can use wire brush, chipping hammer, and
More informationDesign Upgradation and Three Dimensional Finite Element Fatigue Analysis on Composite Pressure Vessel
Design Upgradation and Three Dimensional Finite Element Fatigue Analysis on Composite Pressure Vessel S. Kamalakannan PG Scholar, Department of Mechanical Engineering Knowledge Institute of Technology,
More informationACHIEVING TOUGHNESS IN P91 WELDS FROM ROOT TO CAP USING SEMIAUTOMATIC HIGH DEPOSITION METAL TRANSFER (HDMT) GTAW WELDING PROCESS
ACHIEVING TOUGHNESS IN P91 WELDS FROM ROOT TO CAP USING SEMIAUTOMATIC HIGH DEPOSITION METAL TRANSFER (HDMT) GTAW WELDING PROCESS Charles W. Pat Patrick Scott Witkowski Brad Berglan Ramon Solo Jose Leza
More informationJohn C. Stennis Space Center Standard WELD PROCEDURE FOR WELDING COPPER TUBE
Revision February 2010 National eronautics and Space dministration John C. Space Center Space Center, MS 39529-6000 John C. Space Center WELD PROCEDURE FOR WELDING COPPER TUBE Original signed by: Michael
More informationOIL TECH SERVICES, INC.
OIL TECH SERVICES, INC. 800 Wilcrest, Suite 100 Houston, TX 77042-1359 (310)-527-2695 (713) 789-5144 E Mail: mlombard@itmreps.com Website: www.itmreps.com WELDING Weld Procedure Specifications (WPS): Welding
More informationSECTION IX. Subject Interpretation File No. QW-182, Fracture Tests... IX QW-200.4(b)... IX QW
SECTION IX Subject Interpretation File No. QW-182, Fracture Tests... IX-10-32 11-939 QW-200.4(b)... IX-10-34 10-1966 QW-250... IX-10-28 09-558 QW-300.3, Simultaneous Performance Qualifications... IX-10-29
More information49 CFR Part 192. Not applicable to welding during manufacture of pipe and components
49 CFR Part 192 Not applicable to welding during manufacture of pipe and components --- and other strange nomenclature A joining process that produces a coalescence of metals (or non-metals) by heating
More informationAPI-582. a practical approach for industrial welding practices. All rights reserved to thepetrostreet team
Recommended Welding Guidelines API-582 a practical approach for industrial welding practices By The PetroStreet Team CONTENTS Key Sections: Θ Section 6 WELDING CONSUMABLES Θ Section 7 SHIELDING AND PURGING
More informationPipeline Systems PLSC0017 Requirements for Welder Qualifications in Accordance with ASME Section IX
June 2018 Pipeline Systems PLSC0017 Requirements for Welder Qualifications in Accordance with ASME Section IX PURPOSE AND USE OF PROCESS INDUSTRY PRACTICES In an effort to minimize the cost of process
More informationThe Impact Testing Enigma A Review of ASME Section VIII, Division 1, Subsection C, Part UCS, Impact Testing Requirements
the pressure equipment safety authority The Impact Testing Enigma A Review of ASME Section VIII, Division 1, Subsection C, Part UCS, Impact Testing Requirements AB-511 Edition 2, Revision 1 Issued 2017-05-03
More informationSummary of Changes in. ASME Section IX, 2001 Addenda
Summary of Changes in ASME Section IX, 2001 Addenda Prepared by Walter J. Sperko, P.E. Sperko Engineering Services, Inc 4803 Archwood Drive Greensboro, NC 27406 USA Voice: 336-674-0600 FAX: 336-674-0600
More informationWLD 152 Wire Welding Certification Practice
WLD 152 Wire Welding Certification Practice Index Course Information Accessing ebook and coursemate info. 3 4 Science on Steel 6-10 Craftsmanship Expectations 11 Welding Projects with Information Sheets
More informationREMOVAL OF CAST LIP STEP 1 STEP 2. Layout cut lines, based on existing welds and verify with dimension taken from new lip. STEP 3
REMOVAL OF CAST LIP STEP 1 fig. 1-1 Brace clam from cheek plate to cheek plate (A). Brace clam from bucket floor, (just behind back of lip joint), to upper cheek plate on both sides (B). The purpose of
More informationApproved 07/26/2017 NR Key Features. Conformances. Typical Applications. Welding Positions
Procedures Structural Code Seismic Supplement FLUXCORED SELFSHIELDED (S) WIRE Innershield Mild Steel, All Position AWS E71T8 NR 232 Key Features High deposition rates for outofposition welding Penetrating
More informationAWS Amendment Notice
AWS Amendment Notice The following Amendments have been made and incorporated into the current edition of this document. 2 nd Printing: Subject: List of Tables 12.3 M 270M (A709M) Gr. 250, 345, 345S Minimum
More informationSection 14. Welding Field Welding 1. Welding Processes 6. Stud Welding 9. Welding Positions 11
Section 14 Welding 14.1 Field Welding 1 Welding Processes 6 Stud Welding 9 Welding Positions 11 Field Welding Section 14.1 Field Welding Bridge Structures AWS D1.5 (00560.26(a)) Reinforcement AWS D1.4
More informationSection 13. Welding Field Welding 1. Welding Processes 6. Stud Welding 9. Welding Positions 15
Section 13 Welding 13.1 Field Welding 1 Welding Processes 6 Stud Welding 9 Welding Positions 15 Field Welding Section 13 Field Welding Bridge Structures AWS D1.5 (00560.26(a)) Reinforcement AWS D1.4 (00530.42(d))
More informationSummary of Changes in. ASME Section IX, 2005 Addenda. As Published in the Welding Journal October, Prepared by
Summary of Changes in ASME Section IX, 2005 Addenda As Published in the Welding Journal October, 2005 Prepared by Walter J. Sperko, P.E. Sperko Engineering Services, Inc 4803 Archwood Drive Greensboro,
More informationNS Plus -102 AWS ER80S-D2, ER90S-D2
NS Plus -102 AWS ER80S-D2, ER90S-D2 DESCRIPTION NS Plus 102 is a premium copper-coated low alloy, high-strength solid filler metal containing 0.5% molybdenum to maintain hardness and strength following
More informationWELDING PROCEDURE SPECIFICATION. Shielded Metal Arc Welding-SMAW
WELDING PROCEDURE SPECIFICATION Shielded Metal Arc Welding-SMAW WPS Number: WPS-SMAW-CS Revision: 0 Company Name & Address ABC WELDING & FABRICATING 123 WeldProc Boulevard Toronto, ON A1B 2C3 CWB Approval
More informationwelder certification welder performance qualification
Chapter 29 Welder Certification OBJECTIVES After completing this chapter, the student should be able : Explain welder qualification and certification. Outline the steps required certify a welder. Make
More informationREFERENCE SYLLABUS. for WELDING EXAMINER & WELDING EXAMINER IN TRAINING CERTIFICATES OF COMPETENCY EXAMINATIONS
WELDING EXAMINER & CERTIFICATES OF COMPETENCY S AB-94 Edition 2, Revision 0, 2016-05-01 GENERAL INFORMATION INTRODUCTION: This Syllabus is intended to assist candidates in preparing the Welding Examiner
More informationWELDING PROCEDURE QUALIFICATION RECORD
WELDING PROCEDURE QUALIFICATION RECORD N QP-ITA-18-00692-rev.0 LEVEL 2 Manufacturer s WPS no CO 03/18 REV.0 Manufacturer COMERI COSTRUZIONI MECCANICHE SRL Address VIA FRIULI, 8 29017 FIORENZUOLA D ARDA
More informationGuide for AWS Visual Weld Inspection
Guide for Visual Weld Overview & Contents Scope This guide is intended to assist Owner/Operators, Contractors, Authority Having Jurisdiction (AHJ) personnel, Inspectors, Manufacturers and Contractors/Fabricators
More informationCompatibility Testing of Postle Duraband NC over Arnco 100XT TM
Postle Industries, Inc. Cleveland, OH Compatibility Testing of Postle Duraband NC over Arnco 100XT TM THHA E4-19994 July 31, 2014 Srinivasa R. Koneti, BSME & MSMSE Materials Engineering Manager Disclaimer
More informationAN OVERVIEW ON SHIELDED METAL ARC WELDING (SMAW) OF STAINLESS STEEL (SS)
Suggested Spec. for SMAW-SS - 1 - AN OVERVIEW ON SHIELDED METAL ARC WELDING (SMAW) OF STAINLESS STEEL (SS) Scope This document provides information on welding and related operations of stainless steel
More informationWelding of Large Diameter Pipelines: Design, Processes, Procedures Specifications for Welding Steel Water Pipe
Welding of Large Diameter Pipelines: Design, Processes, Procedures Specifications for Welding Steel Water Pipe Field Welding of Steel Pipe Joints Nash Williams, Owner National Welding Corporation 2 Steel
More informationTEACH YOUR TRADE. WE LL DO THE REST.
TEACH YOUR TRADE. WE LL DO THE REST. ENROLLMENT IN SKILLED TRADE PROGRAMS IS UP 70%. IS YOUR WORKFORCE DEVELOPMENT CURRICULUM READY? Credit: Texas State Technical College Welding Program The Wall Street
More informationLincoln Electric External Evaluation Evaluation of EXX45-P2 Welding Electrodes
Lincoln Electric External Evaluation Evaluation of EXX45-P2 Welding Electrodes Evaluation of EXX45-P2 Welding Electrodes Final Report for Lincoln Electric Company Report No.: 82674761 April 22, 2008 Evaluation
More informationM. F. Sullivan. 9/27/2016 Dr. Sandor Somogyi
The Code is a large document and it is sometimes very difficult to understand. Even for many of us who work with it every day. In my opinion there is no one person who could be termed as a Code Expert.
More informationTECH TIPS. Booms/Scissors. Service Call: Platform repair instructions of steel guard rails on Terex/Genie Aerial Work Platforms and Scissors
TECH TIPS Service Call: Platform repair instructions of steel guard rails on Terex/Genie Aerial Work Platforms and Scissors Tools Needed: See attached document for required tools Model: Booms/Scissors
More informationThe following points should be considered when selecting the proper coated electrode. 1. Match the mechanical properties of the base metal.
HQ Aluminum Elect The following points should be considered when selecting the proper coated electrode. 1. Match the mechanical properties of the base metal. 2. Match the chemical composition of the base
More informationNATURAL GAS COMPRESSOR STATION PIPELINE WELDING AND RELATED FACILITIES. Engr. Md. Saidur Rahman 1,*
Proceedings of the International Conference on Mechanical Engineering and Renewable Energy 2015 (ICMERE2015) 26 29 November, 2015, Chittagong, Bangladesh ICMERE2015-PI-243 NATURAL GAS COMPRESSOR STATION
More informationExcellent for rusty, scaly, oily plate and pipes. Excellent for open root pass welding
Quantum Arc D2 AWS ER80S-D2, ER90S-G WELDING POSITIONS: FEATURES: BENEFITS: Higher tensile and yield strength weldments than ER70S-X wires High in deoxidizers Excellent wetting characteristics Low silicon
More information7018 MR. Conformances
STICK (SMAW) ELECTRODE Excalibur 7018 MR Mild Steel, Low Hydrogen AWS Improved coating integrity Extreme bendability 60% less moisture pickup vs. competition Reduction of arc starting porosity Clear puddle
More informationNS Plus -115 AWS ER70S-6
NS Plus -115 AWS ER70S-6 DESCRIPTION NS Plus 115 is a premium copper-coated mild steel solid filler metal containing a high combined total of manganese and silicon. The wire produces a smooth, uniform
More informationRepair Ability of Incoloy 800 in Vent Gas Wash Tower Pipe System
AIJSTPME (2012) 5(2): 39-44 Repair Ability of Incoloy 800 in Vent Gas Wash Tower Pipe System Poopat B. Department of Production Engineering, Faculty of Engineering, KMUTT, Bangkok, Thailand Warinsiriruk
More informationStandard Specification for Carbon Steel Forgings for Piping Applications 1
Addr: 29, 227 Changle Rd., Shanghai, 2000. Tel: 86-2-6470807 Designation: A 0/A 0M 0 Endorsed by Manufacturers Standardization Society of the Valve and Fittings Industry Used in USDOE-NE Standards Standard
More informationChapter 11 of EPI Part 10 Construction Specification 11. WELDING. a) Scope
Chapter 11 of EPI Part 10 Construction Specification 11. WELDING a) Scope These welding Specifications for Mainline Construction detail the requirements for mainline welding, repair welding, tie-in welding
More informationWELDING PROCEDURE QUALIFICATION RECORD
WELDING PROCEDURE QUALIFICATION RECORD N QP-ITA-18-00690-rev.0 LEVEL 2 Manufacturer s WPS no CO 01/18 REV.0 Manufacturer COMERI COSTRUZIONI MECCANICHE SRL Address VIA FRIULI, 8 29017 FIORENZUOLA D ARDA
More informationStandard Specification for Forged Carbon and Alloy Steel. Flanges for Low-Temperature Service¹ ASTM A707/707M Scope :-
Standard Specification for Forged Carbon and Alloy Steel Flanges for Low-Temperature Service¹ 1. Scope :- 1.1 This specification covers forged carbon and alloy steel flanges intended primarily for petroleum
More information1¼Cr-½Mo CREEP RESISTING STEEL
DATA SHEET A-12 1¼Cr-½Mo CREEP RESISTING STEEL METRODE PRODUCTS LTD HANWORTH LANE, CHERTSEY SURREY, KT16 9LL Tel: +44(0)1932 566721 Fax: +44(0)1932 565168 Sales Fax: +44(0)1932 569449 Technical Fax: +44(0)1932
More informationSMAW THEORY. Course # WELD1110
Course # WELD1110 SMAW THEORY OBJECTIVES: At the completion of this course the student will be able to recall from lectures, demonstrations and audio visual aids the theory and applications of the (SMAW)
More informationSpecification for Welding Earthmoving, Construction, and Agricultural Equipment
Key Words Structural welds, field repair, welding, earthmoving equipment, construction equipment, agricultural equipment AWS D14.3/D14.3M:2005 An American National Standard Approved by American National
More informationStandard Specification for Carbon and Alloy Steel Forgings for Thin-Walled Pressure Vessels 1
Designation: A 372/A 372M 03 An American National Standard Standard Specification for Carbon and Alloy Steel Forgings for Thin-Walled Pressure Vessels 1 This standard is issued under the fixed designation
More informationHandbook. Gas Tungsten Arc Welding. Sixth Edition. William H. Minnick Mark A. Prosser. Welding/Fabrication Instructor. Janesville, Wisconsin
Gas Tungsten Arc Welding Handbook Sixth Edition William H. Minnick Mark A. Prosser Welding/Fabrication Instructor Black hawk Technical College Janesville, Wisconsin 6 Gas Tungsten Arc Welding Handbook
More informationImproving API 1104 for the Twenty-second Edition
Improving API 1104 for the Twenty-second Edition Something to consider during your subcommittee meetings 1 SAFER, SMARTER, GREENER Introduction API 1104 contains quite a bit of ambiguity For welding procedure
More informationMETAL-CORED GMAW-C CONSUMABLES WELDING CONSUMABLES CATALOG
METAL-CORED GMAW-C CONSUMABLES WELDING CONSUMABLES CATALOG [129] Selection Guide INTRODUCTION STICK MIG & TIG METAL-CORED Product Name & AWS Class Mild Steel MC-6 (E70C-6M H4) MC-706 (E70C-6M H4) MC-710XL
More informationASTM A105/A105M-10. Standard Specification for Carbon Steel Forgings for. Piping Applications ¹
Standard Specification for Carbon Steel Forgings for Piping Applications ¹ 1. Scope :- 1.1 This specification covers forged carbon steel piping components for ambient and higher temperature service in
More informationHeat Input & Interpass temperature during welding
Heat Input & Interpass temperature during welding By Leif Andersen, One definition of welding goes like this: Welding is control of heat. In the previous article The need for Pre-Heating when Welding we
More informationSTAINLESS STEEL SHEETS
STAINLESS & NICKEL ALLOY CHATHAM STEEL CORPORATION 59 STAINLESS STEEL SHEETS TYPE 04, 04L, 6, 6L No. 2B Finish Cold Rolled, Annealed *No. 2D Finish No. Finish Polished One Side No. 4 Finish Polished One
More informationpdfmachine trial version
EFFECT OF WELDING TECHNIQUES (GTAW & SMAW) ON THE MICROSTRUCTURE & MECHANICAL PROPERTIES OF MILD STEEL SA 516 Gr. 70 By Dr. Muhammad Taqi Zahid Butt, S. Ahmed, S. Rasool, U. Ali and S. U. Rehman* ABSTRACT
More informationAtlas Evaluation & Inspection Services
Atlas Evaluation & Inspection Services 943 East Hazelwood Ave, Rahway, NJ 07065 Ph: 732 388 7711 Fax: 732 388 7767 Website: www.aeisndt.com AWS CERTIFIED WELDER TEST (VERTICAL AND OVERHEAD) FOR NYC LICENSE
More informationCREEP RESISTING STEEL
Data Sheet A-13 2¼Cr-1Mo CREEP RESISTING STEEL METRODE PRODUCTS LTD HANWORTH LANE, CHERTSEY SURREY, KT16 9LL, UK Tel: +44(0)1932 566721 Fax: +44(0)1932 565168 Email: info@metrode.com Website: www.metrode.com
More informationREFERENCE SYLLABUS. for WELDING EXAMINER & WELDING EXAMINER IN TRAINING CERTIFICATES OF COMPETENCY EXAMINATIONS
WELDING EXAMINER & CERTIFICATES OF COMPETENCY S AB-94 Edition 1, Revision 6, 2016-05-01 This syllabus is being phased out and will be discontinued on April 30, 2018. GENERAL INFORMATION INTRODUCTION: This
More information"Welder Certification"
"Welder Certification" The purpose of this presentation is to introduce you to the various aspects of welder certification. This is not intended to cover all of the requirements for certification but only
More informationPART UF REQUIREMENTS FOR PRESSURE VESSELS FABRICATED BY FORGINGS
p 1 of 6 UF-1 UF-12 PART UF REQUIREMENTS FOR PRESSURE VESSELS FABRICATED BY FORGING the test temperature be higher than 20 F ( 29 C). Certification is required. An ultrasonic examination shall be made
More information4 Shielded Metal Arc Welding*
4 Shielded Metal Arc Welding* * Abbreviated MMA (Manual metal arc welding). American designation: shielded metal arc welding (SMAW). Shielded metal arc welding (SMAW) is an AW process that uses a consumable
More informationStructural Welding Code Reinforcing Steel
Key Words Allowable stress, inspection, qualification, reinforcing steel, structural details, welded joint details AWS D1.4/D1.4M:2005 An American National Standard Approved by the American National Standards
More informationMETRODE WELDING CONSUMABLES
A28 2¼Cr-1Mo CREEP RESISTING STEEL Alloy type 2¼Cr-1Mo alloyed steel consumables for elevated temperature service. ASTM Materials to be welded BS EN & DIN A387 Gr 21 & 22 11CrMo9-10 (1.7383) A182 F22 10CrMo
More informationDIVISION: METALS SECTION: STRUCTURAL STEEL FRAMING REPORT HOLDER: CAST CONNEX CORPORATION
0 Most Widely Accepted and Trusted ICC ES Evaluation Report ICC ES 000 (800) 423 6587 (562) 699 0543 www.icc es.org ESR 3031 Reissued 12/2017 This report is subject to renewal 12/2019. DIVISION: 05 00
More informationMolybdenum. Standard Specification for Pressure Vessel Plates, Alloy Steel, Chromium- Designation: A 387/A 387M 03
Designation: A 387/A 387M 03 Used in USDOE-NE Standards Standard Specification for Pressure Vessel Plates, Alloy Steel, Chromium- Molybdenum 1 This standard is issued under the fixed designation A 387/A
More informationStandard Specification for Piping Fittings of Wrought Carbon Steel and Alloy Steel for Moderate and High Temperature Service 1
Designation: A 234/A 234M 02 Used in USDOE-NE Standards An American National Standard Standard Specification for Piping Fittings of Wrought Carbon Steel and Alloy Steel for Moderate and High Temperature
More informationSO YOU RE THE NEW WELDING ENGINEER
SO YOU RE THE NEW WELDING ENGINEER The Importance of Pre and Post-Weld Operations Fabtech 2014 Mike Rice Sr. Corporate Welding Engineer The Importance of Pre and Post-Weld Operations Pre-Weld Operations
More informationChapter 3 Shielded. Metal Arc Welding
Chapter 3 Shielded Metal Arc 1. SMAW Electrode 2 Filler metals for shielded metal arc welding are composed of a metal alloy core, covered by a flux coating. The core wire carries the current for welding
More informationLicensed Copy: EnCana (U.K.) Ltd (EnCana (U.K.) Limited, Encana UK Ltd, 27 July 2004, Uncontrolled Copy, (c) BSI
BRITISH STANDARD BS 4515-2:1999 ICS 23.040.10; 25.160.01 NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW Specification for Welding of steel pipelines on land and offshore Ð Part
More informationINSPECTION AND TEST. PROCEDURE Total Page 13
PROCEDURE Total Page 13 Client : Project Name: P/O No. : Item No. : 3 2 1 0 FOR APPROVAL Rev Description Date Prepared By Checked By Approved By PROCEDURE Page 1 of 8 1. General 1.1 Scope This specification
More informationNorth Atlantic ENGINEERING STANDARD SPECIFICATION 1/7 REV. QUALITY SLAG BOWL WELDING AND QUALITY REQUIREMENTS. Approved by.
1/7 Rev Description Revision by Approved by Issue Date YYYY/MM/DD 1 Update from Job 497-01 KLR 015/04/01 Updated 1.0 and 4.3 PB 016/03/09 KLR 015/04/01 PB 016/03/09 015/04/01 016/03/09 Sud = Sudbury, Ontario,
More informationWELDING CONSUMABLES FOR DUPLEX AND SUPERDUPLEX STAINLESS STEELS OPTIMISING PROPERTIES AFTER HEAT TREATMENT
WELDING CONSUMABLES FOR DUPLEX AND SUPERDUPLEX STAINLESS STEELS OPTIMISING PROPERTIES AFTER HEAT TREATMENT by G B Holloway & J C M Farrar Metrode Products Limited ABSTRACT The first 50 years of duplex
More informationStandard Specification for Forged Carbon and Alloy Steel Flanges for Low- Temperature Service 1
Designation: A 707/A 707M 02 (Reapproved 2007) Standard Specification for Forged Carbon and Alloy Steel Flanges for Low- Temperature Service 1 This standard is issued under the fixed designation A 707/A
More informationPED Certified OHSAS 18001:2007 ISO 9001 : 2008 ISO 14001:2004 Govt. Recognized Export House.
PED Certified OHSAS 800:2007 ISO 900 : 2008 ISO 400:2004 Govt. Recognized Export House. SPECIALIST IN: - STAINLESS STEEL, ALLOY STEEL, CARON STEEL SEAMLESS & WELDED PIPES PED APRPOVED FITTINGS & FLANGES
More informationAASHTO/AWS D1.5M/D1.5:2008. Table of Contents
Table of Contents Personnel...v Foreword...ix List of Tables... xviii List of Figures...xix List of Forms...xxi 1. General Provisions...1 1.1 Application...1 1.2 Base Metal...1 1.3 Welding Processes...1
More informationWelding of Pipelines and Related Facilities API STANDARD 1104 TWENTY-FIRST EDITION, SEPTEMBER 2013
Welding of Pipelines and Related Facilities API STANDARD 1104 TWENTY-FIRST EDITION, SEPTEMBER 2013 Special Notes API publications necessarily address problems of a general nature. With respect to particular
More informationTable of Contents Page No.
Table of Contents Personnel... iii Foreword...v List of Tables... xiii List of Figures...xiv List of Forms...xvi 1. General Provisions...1 1.1 Application...1 1.2 Base Metal...1 1.3 Welding Processes...2
More informationMETALLIC MATERIAL SPECIFICATION
1. Scope: Page: 1 of 5 1.1. This specification shall be utilized in procurement of AISI 8630 modified steel (UNS G86300) in quenched and tempered condition to 22 HRc maximum hardness. 1.2. These materials
More informationSubject: WPS America.com Software Upgrades-AWS and ASME Codes Updates
Subject: WPS America.com Software Upgrades-AWS and ASME Codes Updates Dear Users of WPS America.com: WPS America.com welding software for the AWS and ASME codes has been successfully upgraded. As part
More informationPILE WELDING QUALITY CONTROL PLAN
Michigan Department Of Transportation 5627 (10/14) PILE WELDING QUALITY CONTROL PLAN CONTRACTOR LOCATION PREPARED BY CONTROL SECTION JOB NO. DATE Bridge Field Services Approval Block CHECKED BY DATE SPECIFICATIONS
More informationStandard Specification for Carbon Steel Forgings for Piping Applications 1
Designation: A0/A0M 4 Endorsed by Manufacturers Standardization Society of the Valve and Fittings Industry Used in USDOE-NE Standards Standard Specification for Carbon Steel Forgings for Piping Applications
More informationDissimilar Steel Welding of Super Heater Coils for Power Boiler Applications
American Journal of Materials Research 2015; 2(5): 44-49 Published online August 30, 2015 (http://www.aascit.org/journal/ajmr) ISSN: 2375-3919 Dissimilar Steel Welding of Super Heater Coils for Power Boiler
More informationProcess Review Checklist
Process Review Checklist DISCLAIMER. Due to time constraints, the student process review exercise is only a few minutes long. A through, complete process review checklist is not expected as a result but
More informationSPECIFICATION FOR LOW-ALLOY STEEL ELECTRODES AND FLUXES FOR SUBMERGED ARC WELDING
SPECIFICATION FOR LOW-ALLOY STEEL ELECTRODES AND FLUXES FOR SUBMERGED ARC WELDING A99 SFA-5.23 (Identical with AWS Specification A5.23/A5.23M-97.) 1. Scope This specification prescribes requirements for
More informationTable of Contents Page No.
Table of Contents Page No. Personnel... iii Foreword...v List of Tables...xii List of Figures... xiii 1. General Requirements...1 1.1 Scope...1 1.2 Approval...1 1.3 Definitions...1 1.4 Welding Symbols...1
More informationCanadian Welding Bureau Welding Procedure Qualification AWS D1.1 vs CSA W47.1
Welding Procedure Qualification Canadian Welding Bureau Welding Procedure Qualification Comparison of Key Concepts and Requirements This document provides a general comparison of key concepts and requirements
More information71T1 - Gas Shielded Flux Cored Welding Wire Provides excellent performance in all position welding. Weld Metal - Chemistry
Flux Cored Wire 71T1 - Gas Shielded Flux Cored Welding Wire Provides excellent performance in all position welding Description: Provides a stable arc, low spatter, easy to remove slag, and neat weld metal.
More informationSPECIFICATION FOR CONSUMABLE INSERTS
SPECIFICATION FOR CONSUMABLE INSERTS A99 (Identical with AWS Specification A5.30-79R) Scope: This specification prescribes requirements for classification of consumable inserts. 1 Note: The values stated
More information25%Cr SUPERDUPLEX
DATA SHEET B-62 25%Cr SUPERDUPLEX - 2507 METRODE PRODUCTS LTD HANWORTH LANE, CHERTSEY SURREY, KT16 9LL Tel: +44(0)1932 566721 Fax: +44(0)1932 565168 Sales Fax: +44(0)1932 569449 Technical Fax: +44(0)1932
More informationStandard Specification for Centrifugally Cast Ferritic Alloy Steel Pipe for High- Temperature Service 1
Designation: Standard Specification for Centrifugally Cast Ferritic Alloy Steel Pipe for High- Temperature Service 1 This standard is issued under the fixed designation A 426/A 426M; the number immediately
More informationWelding. What is Welding?
Welding Welding What is Welding? Welding is a joining process in which metals are heated, melted and mixed to produce a joint with properties similar to those of the materials being joined. Parent Metal
More informationQUALITY CONTROL FORM SAMPLE
QUALITY CONTROL FORM Document Name: Inspection & Test Plan (ITP) Project Name: Subject : Document No.: FO No. : Offer No.: Material Code: Rev.:00 INSPECTION AND TEST PLAN FOR Rev. Date Description Contractor
More information"Welder Certification"
"Welder Certification" The purpose of this presentation is to introduce you to the various aspects of welder certification. This is not intended to cover all of the requirements for certification but only
More information