PERFORMANCE OF TUNGSTEN CARBIDE TIPPED DETACHABLE WEAR PADS FOR SHREDDER HAMMERS
|
|
- Amberlynn Hawkins
- 6 years ago
- Views:
Transcription
1 FORTY-FIRST CONFERENCE PERFORMANCE OF TUNGSTEN CARBIDE TIPPED DETACHABLE WEAR PADS FOR SHREDDER HAMMERS BY E. L. HORNIBLOW and F. JOHNSON Cattle Creek Co-operative Sugar Milling Association Limited Introduction Original development in providing wear protection to shredder hammers started in In 1966, Shawn and McWhinney reported hammer tests including some results on tungsten carbide inserts. Experimentation was confined to small hammers up to mm wide, and protection was provided by thin sections of cemented carbide some 3.2 mm thick. The incidence of failure was high, due to shattering of the tips through impact with stones. While some minor success was achieved, the manufacturer terminated experiments in face of overwhelming evidence reported by Jacklin (1972). This report supported the use of electro casting chromium carbide onto hammers contained in a water cooled mould. Between the years 1965 and 1971, a considerable improvement had been made in the methods of harvesting cane. The level of entrained tramp material had significantly decreased in most areas. This improvement provided a climate wherein the re-introduction of tungsten carbide-faced hammer experimentation appeared to be justified. Reasons for Using Replaceable Wear Pads The project was revised in the light of experience gained during original tests and from field information supplied by engineers in the Mackay district. Merit was seen in providing a replaceable/disposable head, faced with tungsten carbide, and proto-types were placed in service at Pleystowe mill. The reasons for the change from solid hammer to replaceable wear pads are: It was seen that by brazing (silver soldering) carbide pieces to hammer bodies, operational difficulties were bound to occur even where the best re'suits were obtained. The hammers would need to be reconditioned by the manufacturer. This would entail transportation over 620 to 650 kilometres each season. Where odd failures occurred, the hammer face would wear and require major reconditioning to accommodate further pieces of carbide or, alternatively, be sent to scrap. Original tests used thin sections of carbide, which were not shock. resistant. This method was obviously used to minimize the mass of carbide employed, with a view to reducing initial cost. The result was a wear piece most likely to shatter under adverse conditions.
2 152 FORTY-FIRST CONFERENCE Benefits to be Obtained from Using Wear Pads Unlike hardface welding, which is dependant upon the skill of the welder, carbide plate protection is reproducible. Replacement of worn pads can be made with minimum loss of mill crushing time. Continuous crushing can be obtained with no loss of shredding efficiency. Cane shredding is freer, particularly under wet cane conditions. Hammers require balancing no more than once per season. First installation requires only one set of hammers plus a few spares, as against two sets of hammers where weld hardfacing is employed. Hammer life is related to wear in the "boss" of the hammer only. Shredder maintenance costs are reduced approximately 50 per cent. Replaceable Wear Pads-Original Design The design of the wear pads seated in 1972 was changed. A solid piece of carbide 12.7 mm thick was silver soldered to the top of the wear pad. Studs of carbide were silver-soldered into holes drilled below the main wear piece. Two styles were tested, a single row and double row pattern of wear studs were used. By using studs, the carbide was presented to the work fully supported by the steel body of the pad, i.e., in the strongest presentation to resist shatter due to impact against tramp material. Hammer bodies were machined to accept a wear pad held in position by high tensile socket headed "un brako" bolts. Additional security was provided by introducing a spigot fastening on the wear pad top. To provide a wear resistant surface, the steel body was oil-quenched in the post-braze period. Figure 1 shows the wear pads tested on a Pleystowe hammer. Fig.-l Pleystowe trial 1972
3 Fig. 2-Pleystowe trial Results of Tests The results of the limited tests were sufficiently encouraging to warrant wider tests during Precise records of all wear pad performance were not obtained because, where minor chipping of carbides occurred, the pads were removed from the mill and returned to the manufacturer for examination. Several pads from the limited number supplied crushed some tonnes of cane before the season terminated. Significant Findings The stud pattern was successful in that no losses were encountered due to failure from impact with tramp materials. Towards the end of the season, the wear area became apparent, and was seen to extend from the outer edge of the hammer extending down about 38 mm. This indicated the total area requiring protection. Carbide wear was excellent, but the steel backing eroded away between the studs, indicating the need to use a more wearresistant steel or different wear pattern protection The steel in the hardened condition proved to be on the brittle side and, where carbide failure occurred, the steel si~nllarly failed against major impact, i.e., when weld hardfaced hammer heads become detached. On the Pleystowe hammer (Figure 2), the wear pad was not fully supported by the hammer backing. The wear pads protruded beyond the narrow section hammer body. When this style of hammer was used, it became apparent that a tougher wear pad steel was necessary. The prototype was over-designed, and modifications were seen to be necessary. Difficulties were anticipated in providing the spigot at mills where machine stop facilities were limited. Experience showed that chamfers on the pad sides were not necessary and tended to weaken the wear pad.
4 154 FORTY-FIRST CONFERENCE The carbide grade used showed good wear properties. However, under adverse conditions where steel tramp metal was included with the cane or resulted from detached hammer heads, failure occurred. The tungsten carbide used was of medium wear resistance in relation to other carbides available, i.e., composition 16.0 per cent Cobalt binder with a 2 micrometer Tungsten Carbide base. Modifications Made for and During 1972 Season Changes to Wear Pad Style The hammer wear pad was modified to include a keyway instead.. of a spigot. All necessarv chamfers were deleted. These changes vrovided easier machining of the wear pad and hammer head,~he keyway allowed engineers the choice of using a fixed key milled into the hammer or using a loose key. To prevent erosion of the steel backing, a wedge-shaped carbdie tip was introduced. This was incorporated on advice received from Cattle Creek mill. Provision was made to accommodate a 5 degree positive rake through neutral to a 5 degree negative rake according to engineers' preference in relation to carbide tip location (refer to Figure 2.) Steel Backing To provide better wear resistance in the steel body, a change was made to a special air hardening steel, Comsteel Orbit grade. This steel has a through hardness capability rather than the skin hardening properties obtainable from the previously used steel. A typical analysis of this steel is C0.7%, S.15%, Mn2.0%, Cr 1.0%, Si0.30%, MO 1.35% Carbide Grades To determine optimum carbide performance, three grades of tungsten carbide were placed under test. a. YO grade. This is a tough grade of carbide commonly used in a fully supported steel casing in cold heading operations for making steel bolts. b. PO grade. A wear and impact resistant grade commonly used for lamination die punches and dies. c. DO grade. A wear resistant grade commonly used in rotary percussion drills in hard rock mining. TABLE I-Composition of test carbides Grade Tantalum carbide Cobalt binder Base carbide size YO 2.0% 25.0% 2-3 micrometer PO 16.0% 2-1 micrometer DO II.Ox 6.0 micrometer Photo micro graphs of the various grades are shown in Figure 3. Photo micro graphs of the various grades are shown in Figure 3.
5 1974 FORTY-FIRST CONFERENCE 155 TABLE Il-Typical physical properties of test carbides Grade S.G. Hardness Abrasion Transverse Coercive V.P.N. index rupture strength force YO min. 70 PO min. 95 DO l l min. 100 Tests were carried out at various mills in the Mackay area, with the most comprehensive test being conducted at Cattle Creek. Cattle Creek mill has a high incidence of stones in the cane supply, and any success recorded at this mill could be related to the rest of the industry. Modifications Resulting from Field Tests 1. In view of the incidence of steel cracking when using "Orbit" steel, the manufacturer has altered the post-braze heat treatment cycle and the steel pads are tempered for two hours at 200 C. 2. Radii in keyways and tip recesses have been increased to eliminate "stress raisers" and to provide additional insurance against any further crack problems. 3. North Eton used a 5 degree positive rake on their hammer and achieved improved results and a better wear pattern. 4. North Eton also used a red lead paste to seal the wear pad, preventing any possibility of cane intrusion under the pad, and to provide easy removal of the worn wear pad at the end of the season. Wear Pattern The wear pattern shows that the highest incidence of wear is in the top of the wear padltip. In the mm-long wedge-shaped tip provided, the most severe wear is from the thick end working in the area nearest the strike bar, diminishing progressively to the thin end of the wedge. By inclining the tip forward, a more even weat is experienced over the life of the carbide. However, some initial loss in impact resistance could be expected and inclination should not exceed 5 degrees. This is shown in Figure 4. Results of Insert Trial--Cattle Creek Initially, 110 tips were acquired for trial purpose, consisting of 50 hard inserts (DO) designated type A; 40 medium inserts (PO), type B and 20 soft inserts (YO), type C. An extra 20 type A inserts were acquired later when it became apparent that type C insert was unsatisfactory (they were too soft). In all, 84 insert hammers-32 type A, 32 type B and 20 Type C-were randomly arranged in four complete rows, 21 hammers per row, the remaining tips being held for replacements. The first two rows were installed on 11 August 1973 and the two remaining rows were installed on 18 August. A total of 52 inserts-22 type A, 27 type B and 3 type C-completed the season without replacement. In many instances, replacement of the remaining insert hammers was due to breakage of the tungsten carbide tip rather than to wear. Table 3 lists the average hammer life for each type in terms of the average tonnes crushed per hammer and the percentage of original
6 1 56 FORTY-FIRST CONFERENCE 1974 YO grade. Impact-resistant grade. PO grade. Tough, wear-resistant grade (fine grain).
7 1974 FORTY-FIRST CONFERENCE 157 DO grade. Tougher grade, with increased wear resistance (course grain). Fig. 3-Micro photographs of cemented tungsten carbide used at Cattle Creek Mill magnification : 1 SOOX. inserts to complete the season. The average life has been defined as throughput (in tonnes) divided by number of hammers. These values suggest that type B insert was the best, because the hard type A tip failed more from breakage caused by foreign material, such as rocks. Figure 5 shows the hammers in various stages of wear. Item A is a new insert; B is a typical worn insert after treating tonnes; Item C shows the tip breakage due to foreign material, and D shows the wasting of the hammer head that can occur below the insert. Wasting of the hammer head highlights the need for hard-facing the head of the hammer if large through-puts tonnages are to be expected from the hammer. Maintenance Costs During the 1973 season, the shredder was run with a total of 168 hammers and 8 rows, 4 rows of the conventional hard-faced hammers and four rows of the trial insert hammers. Maintenance costs, based on material and labour costs, for each group of hammers were $1.10 cents per tonne cane for conventional hammers and 78 cents per tonne cane for the insert type. TABLE Ill-Average life of inserts TypeA TypeB TypeC Average hammer life (tonnes cane hammer) Per cent original hammers to complete remainder of season (approx tonnes)
8 158 FORTY-FIRST CONFERENCE 1974 Fig. 4-Wear pattern. Results of Insert Trial-North Eton The inserts were placed under test during the second week of the season and were in service at the end of the season. Inspection shows that two to three weeks of service life remains in worn hammers. The grade of tungsten carbide in service was Type B (PO Grade). Eficiency The cost per tonne cane crushed (based on 120 tonnes per hour average) for conventional hard-facing is $ per tonne canefor tungsten carbide hard-facing. $ per tonne cane. Breakage rate of carbide inserts was 10 per cent over the season. The total crop crushed was tonnes. The wear pad cost is based on original installation cost plus 10 per cent replacement, divided into tonnes of cane crushed. No adjustment in costs have been made for further wear life available in Results of Insert Trials-Pleystowe Mill Based on the results of limited tests conducted with tungsten carbide wear pads in 1972, an expanded list was arranged for the 1973 season. Because of errors in manufacture related to the number of bolts, holes, and the necessity for re-supply, the test was delayed until the end of the season. In 1972, one tip returned tonnes crushed before the hammer was lost through a failure in the hammer eye. Tests for the 1973 season indicate that this throughput life repeatable in that about tonnes were crushed with no significant wear (see figure 6). The cost per tonne of cane crushed was not precisely determined for wear pads. However, an estimated 50 per cent reduction was obtained in shredder maintenance costs. Eficiency Based on the first tonnes of cane crushed, the cost of hammer maintenance (arc hard-facing) was $ per tonne while estimated
9 FORTY-FIRST CONFERENcE Fig. 5-Hammer wear comparison. A-A Fig. 6--Shows wear comparison. new wear pad on a Cattle Creek 51 mm hammer. B-Pleystowe style hammer and 70 mm wear pad after crushing approximately 10 tonnes of.cane. C-North Eton hammer and wear pad which crushed tonnes approximat
10 160 FORTY-FIRST CONFERENCE 1970 cost for tungsten carbide-faced pads was 1.06 cents per tonne. The cost for arc hard-facing does not include the requirements to purchase a duplicate set of hammers or the removal and replacement costs involved in routine maintenance. These costs are: duplicate hammers, approximately $7 000, hammers $6 000, and removal and replacement $1 000). Comments The cost information supplied is only approximate, having been based on the limited information available from three mills. More definite information will not be obtained until several mills have completed a season with a full complement of tungsten carbide wear pads. Acknowledgements Thanks are accorded to the Chief Engineers of Pleystowe and North Eton for their interest and assistance in providing details of their tests and the management of Cattle Creek mill for permission to publish this paper. REFERENCES Jacklii, G. D. The electro-casting of shredder hammer tips. Proc. Qd. Soc. Sug. Cane Technol. Thirty-ninth conf. 95. Shann, D. S. and McWhiuney W. (1966). Cane shredder hammer performance. Proc. Qd. Soc. Sugar Cane Technol. Thirty-third conf. 151.
SINTERED ALLOY POWDER CARBIDE AND TUNGSTEN CARBIDE MATERIALS FOR SHREDDER HAMMER TIPS
REFEREED PAPER SINTERED ALLOY POWDER CARBIDE AND TUNGSTEN CARBIDE MATERIALS FOR SHREDDER HAMMER TIPS DUTTAGUPTA J IMCO Alloys Pvt Ltd, India jdgupta@imcoalloys.com imco@vsnl.com Abstract This abstract
More information> RX12UF. Cobalt content w/w. Grade. Properties and recommendations. HARTMETALL ESTECH AG 6285 Hitzkirch
pli > Ultra-fine grain carbides are characterized by a very high hardness and wear resistance. They are used for milling tools and drills for processing abrasive, soft and tough materials, in nozzles and
More informationAISI D2 Cold work tool steel
T OOL STEEL FACTS AISI D2 Cold work tool steel Great Tooling Starts Here! This information is based on our present state of knowledge and is intended to provide general notes on our products and their
More informationORVAR SUPREME. Hot work tool steel
Hot work tool steel This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty
More informationHardfacing Electrodes. Special tubular construction requiring low operating currents. Hardness : 650/700 HB.
Hardfacing Electrodes Special tubular construction requiring low operating currents. Hardness : 650/700 HB. These electrodes have been engineered to provide extended service life at ambiant and elevated
More informationMATERIALIZING VISIONS. Bohler-Uddeholm H13 TOOL STEEL
MATERIALIZING VISIONS Bohler-Uddeholm H13 TOOL STEEL Bohler-Uddeholm H13 General Bohler-Uddeholm H13 is a chromium-molybdenumvanadium alloyed steel which is characterized by: Good resistance to abrasion
More informationHOTVAR Hot work tool steel
T OOL STEEL FACTS HOTVAR Hot work tool steel Wherever tools are made Wherever tools are used General HOTVAR is a high performance molybdenumvanadium alloyed hot-work tool steel which is characterized by:
More informationHOTVAR. Hot work tool steel
Hot work tool steel General HOTVAR is a high performance molybdenumvanadium alloyed hot-work tool steel which is characterized by: High hot wear resistance Very good high temperature properties High resistance
More informationIMPACT. Chemical composition For the chemical composition of the ladle analysis the following limits are applicable (in %):
IMPACT Wear resistant steel Material data sheet, edition April 2016 1 DILLIDUR IMPACT is a wear resistant steel with a nominal hardness of 340 HBW in delivery condition. DILLIDUR IMPACT is not a constructional
More informationQRO 90 SUPREME Hot work tool steel
T O O L S T E E L F A C T S QRO 90 Hot work tool steel Great Tooling Starts Here! Cover photo: Bo Dahlgren This information is based on our present state of knowledge and is intended to provide general
More informationThe Convenience Stores For Metal
TOOL STEEL SELECTOR GUIDE Application Suggested Grades Arbors... O1, A2, A6 Battering Tools... S5, S1, S7 Blacksmith Tools... S5, S1 Boiler-Shop Tools... S5, S1, S7 Bolt Clippers... S5, S1 Boring Tools...
More informationSANDVIK FINEMAC FREE- CUTTING WIRE WIRE
SANDVIK FINEMAC FREE- CUTTING WIRE WIRE DATASHEET Sandvik Finemac is a lead-free, hardenable, free-cutting carbon steel characterized by excellent machinability and high hardness, high wear resistance
More informationUltra-met. carbide metalworking technologies (800) (866)
CEMENTED CARBIDE GRAIN STRUCTURES January 2006 720 North Main Street P.O. Box 313 Urbana, OH 43078 800.543.9952 866.543.9952 937.653.7133 Fax: 937.653.4754 CEMENTED CARBIDE GRAIN STRUCTURES January 2006
More informationTungsten Carbide Wear Experts
GOOD EARTH TOOLS Tungsten Carbide Wear Experts Tungsten Carbide Pioneers Good Earth Tools, Inc. (GET) is a manufacturing company that specializes in wear-proofing industrial products. We are pioneers in
More informationOverview. Tool Steel Failures. Define Tool Steel Properties. Determine Modes of Failures. Identify Probable Failure Causes. Recommend Solutions.
Overview Tool Steel Failures Define Tool Steel Properties. Determine Modes of Failures. Identify Probable Failure Causes. Recommend Solutions. Important Properties of Tool Steel Harden Ability Ability
More informationMSE-226 Engineering Materials
MSE-226 Engineering Materials Lecture-7 ALLOY STEELS Tool Steels TYPES of FERROUS ALLOYS FERROUS ALLOYS Plain Carbon Steels Alloy Steels Cast Irons - Low carbon Steel - Medium carbon steel - High carbon
More informationIndusteel Industeel, the right steel Creusabro at the right place Unique, Best, Proven
Industeel Industeel, Creusabro the right steel at Unique, the right Best, place Proven A complete range to meet any situation Creusabro is a complete range of advanced abrasion resistant steel plates bringing
More informationZZ HARDMETAL. Successful Cooperation Commences Here. Zhuzhou ZZ Import and Export Co., Ltd
Successful Cooperation Commences Here Zhuzhou ZZ Import and Export Co., Ltd Brief Introduction Zhuzhou ZZ Hardmetal R&D Center was established in the hometown of hard metal of China --- Zhuzhou city in
More informationIMPAX SUPREME. IMPAX Prehardened mould steel
IMPAX SUPREME IMPAX Prehardened mould steel 1 Edition: 4, 11.2003 No. 031101 This information is based on our present state of knowledge and is intended to provide general notes on our products and their
More informationSelection of Tool & Die Steels
Selection of Tool & Die Steels Introduction The success of a metal forming tool depends on optimizing all the factors affecting its performance. Usually, operating conditions (applied loads, abrasive environments,
More informationQRO 90 SUPREME. Hot work tool steel
QRO 90 SUPREME Hot work tool steel This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed
More informationAISI A2 Cold work tool steel
T OOL STEEL FACTS AISI A2 Cold work tool steel Great Tooling Starts Here! General AISI A2 is an air- or oil hardening chromiummolybdenum-vanadium alloyed tool steel characterized by: Good machinability
More information2890 Ligonier St. Latrobe, PA Phone Fax Toll Free
Your Best Choice For Carbide Components 2890 Ligonier St. Latrobe, PA 15650 Phone 724.532.3041 Fax 724.532.3043 Toll Free 800.862.7066 www.extramet.net OUR HISTORY OUR MISSION Extramet s Primary Objective
More informationALUMEC. High strength aluminium
High strength aluminium This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty
More informationThe raw materials. Clay (or fly ash, slate, sand**) *) Limestone is sometimes exchanged with shells or chalk **) Fly ash, shiffer, sand
Cement Industry This presentation contains general suggestions. SSAB hereby expressly disclaims any liability for their suitability for individual applications. It is the responsibility of the user of
More informationIMPAX SUPREME Prehardened mould steel
T OOL STEEL FACTS IMPAX Prehardened mould steel Wherever tools are made Wherever tools are used This information is based on our present state of knowledge and is intended to provide general notes on our
More informationWELDING,FABRICATION AND REPAIRS
WELDING,FABRICATION AND REPAIRS FABRICATION Flat profiles and formed sections can be fabricated into larger items or finished structures using conventional welding procedures. Liners may be fixed to existing
More informationDOZER EDGES & END BITS
CUTTING EDGES DOZER EDGES & END BITS EXTREME PERFORMANCE MAXIMIZE YOUR PRODUCTION Hensley offers an extensive line of blades and end bits for all makes and models of dozers. Blades and end bits are fabricated
More informationEdition 3, The latest revised edition of this brochure is the English version, which is always published on our web site
This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty of specific properties
More informationSteel yourself - A good blade is a must in the world of recycling
Steel yourself - A good blade is a must in the world of recycling Effective shredding of certain waste streams is an essential precursor to effective recycling, and steel blades are an important part of
More informationPLASTIC MOULD STEEL M340 BÖHLER. voestalpine BÖHLER Edelstahl GmbH & Co KG BÖHLER KUNSTSTOFFFORMENSTAHL
PLASTIC MOULD STEEL BÖHLER M340 voestalpine BÖHLER Edelstahl GmbH & Co KG www.voestalpine.com/bohler-edelstahl BÖHLER KUNSTSTOFFFORMENSTAHL EXACTLY TO YOUR LIKING An increase in productivity in high-tech
More informationEndurance performance of conical picks with hardfacing for improving wear resistance
Underground Mining Technology 2017 M Hudyma & Y Potvin (eds) 2017 Australian Centre for Geomechanics, Perth, ISBN 978-0-9924810-7-0 https://papers.acg.uwa.edu.au/p/1710_52_choi/ Endurance performance of
More informationHOLDAX Prehardened holder steel
Prehardened holder steel This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty
More informationFar-reaching efficiency.
Steel Far-reaching efficiency. The new XABO 1300. Achieving new heights in lightweight heavy-duty construction for special vehicles. With a minimum yield strength of 1,300 megapascals, the quenched and
More informationUDDEHOLM VIDAR 1 ESR
UDDEHOLM VIDAR 1 ESR This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty
More informationHEAT TREAT BULLETIN BULLETIN REVIEW
Bulletin No. 7 ISO 9001 Registered HEAT TREAT BULLETIN BULLETIN REVIEW BULLETIN REVIEW In an effort to improve our product and service, East-Lind Heat Treat has issued six bulletins over the past three
More informationUddeholm Formax. Formax is a trademark registered in Sweden
Uddeholm Formax Formax is a trademark registered in Sweden UDDEHOLMS AB No part of this publication may be reproduced or transmitted for commercial purposes without permission of the copyright holder.
More informationCemented carbide composite roll solutions for intermediate and finishing stands. ENGINEERED SOLUTIONS Smart Rolling Solutions
Cemented carbide composite roll solutions for intermediate and finishing stands ENGINEERED SOLUTIONS Smart Rolling Solutions TABLE OF CONTENTS DESIGNED TO CUSTOMER SPECIFICATION CEMENTED CARBIDE CEMENTED
More informationCALMAX. Plastic mould and cold work steel
Plastic mould and cold work steel General CALMAX is a chromium-molybdenum-vanadium alloyed steel characterized by: High toughness Good wear resistance Good through hardening properties Good dimensional
More informationUDDEHOLM VIDAR 1 ESR
UDDEHOLM VIDAR 1 ESR This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty
More informationLonger Wearlife Parts For Asphalt Plants
Longer Wearlife Parts For Asphalt Plants Still proudly made in the USA Kenco Engineering, Inc. Roseville, CA 800-363-9859 www.kencoengineering.com helps keep your plant working at day one productivity
More informationEXPERIENCES WITH A HEAVY DUTY SHREDDER
THIRTY-SEVENTH CONFERENCE EXPERIENCES WITH A HEAVY DUTY SHREDDER By C. D. CAMERON Pioneer Sugar Mills Limited, Ayr Introduction Examination of shredded preparation at Inkerman last season prompted an attempt
More informationHX900 cast-in-carbide
HX900 cast-in-carbide Cast-in-carbide for the toughest conditions HX900 is a unique wear material combining the wear resistance of cemented carbide with the shock resistance, ductility and forming capability
More informationVANADIS 6 SuperClean
T O O L S T E E L F A C T S SuperClean High performance powder metallurgical cold work tool steel Great Tooling Starts Here! Cover photo: Powder pressing punch of. Excellent results have been obtained
More informationSUPERIOR MACHINABILITY
Uddeholm Balder Uddeholm Balder Reliable and efficient steel is essential for good results. The same goes for achieving high productivity and high availability. When choosing the right steel many parameters
More informationลวดเช อมพ เศษ. Weld Mold / USA. Tool and Die Alloy Welding Materials
ลวดเช อมพ เศษ Weld Mold / USA Tool and Die Alloy Welding Materials High-strength alloys for bearing surfaces and tools that must work-harden, for the joining of cracked die sections and for applications
More informationCASE STUDY #1 Zinc Recovery Plant No.2 SHAL Tank Agitator Blade Failure Report & Recommendations
CASE STUDY #1 Zinc Recovery Plant No.2 SHAL Tank Agitator Blade Failure Report & Recommendations By: Justin Taylor Photo 1 Report Summary The purpose of this document was to put forward an initial recommendation
More informationUDDEHOLM TOOL HOLDER CONCEPT
Uddeholm Idun Uddeholm Idun Reliable and efficient steel is essential for good results. The same goes for achieving high productivity and high availability. When choosing the right steel many parameters
More informationWORLD'S TOOLS, SHARP TOOLS FOR WEALTH.
WORLD'S TOOLS, SHARP TOOLS FOR WEALTH http://www.chinacarbide.com Profile Key Philosophy: Good Faith Creating Value Enterprise Spirit: Pursuing a Perfect Mastery Making Limitless Progress Zhuzhou Cemented
More informationPlate HARDWEAR Plate: Premium abrasion-resistant steels Introducing HARDWEAR 550F
ArcelorMittal USA Plate HARDWEAR Plate: Premium abrasion-resistant steels Introducing HARDWEAR 55F Introduction HARDWEAR, a line of premium abrasion-resistant plate steels, is available in four grades
More informationBulletin No. 4. ISO 9001 Registered HEAT TREAT BULLETIN. Case Hardening Of Steel Components And Straightening
Bulletin No. 4 ISO 9001 Registered HEAT TREAT BULLETIN Case Hardening Of Steel Components And Straightening The topics of discussion for this bulletin are: 1. Case hardening of steel components, and 2.
More informationSelecting the Right Tool Steel for Your Metalforming Application.
Selecting the Right Tool Steel for Your Metalforming Application. Patricia Miller, Senior Technical Manager What parameters drive your tooling material choice? Application Work materials Failure mechanism
More informationWhy Hardox? Juha Erkkilä
Why Hardox? Juha Erkkilä 50 mm Hardox 450 Hardox Wearparts Hardox Plate Product Program Steel Grade Hardness Nominal [HBW] Impact toughness LCVN typical (20 mm) TCVN minimum Bending properties Transverse
More informationUddeholm Sverker 3. Classified according to EU Directive 1999/45/EC For further information see our Material Safety Data Sheets. Edition 8, 06.
Uddeholm Sverker 3 UDDEHOLMS AB No part of this publication may be reproduced or transmitted for commercial purposes without permission of the copyright holder. This information is based on our present
More informationUddeholm Holdax. Classified according to EU Directive 1999/45/EC For further information see our Material Safety Data Sheets.
Uddeholm Holdax UDDEHOLMS AB No part of this publication may be reproduced or transmitted for commercial purposes without permission of the copyright holder. This information is based on our present state
More informationCUTTING TOOL TECHNOLOGY
CUTTING TOOL TECHNOLOGY Tool Life Tool Materials Tool Geometry Cutting Fluids Cutting Tool Technology Two principal aspects: 1. Tool material 2. Tool geometry Three Modes of Tool Failure Fracture failure
More informationCutting Tool Materials and Cutting Fluids. Dr. Mohammad Abuhaiba
Cutting Tool Materials and Cutting Fluids HomeWork #2 22.37 obtain data on the thermal properties of various commonly used cutting fluids. Identify those which are basically effective coolants and those
More informationESCO Universal Wear Solutions. Mining, Construction, Aggregate & Industrial Applications
ESCO Universal Wear Solutions Mining, Construction, Aggregate & Industrial Applications ESCO Corporation With a history of proprietary products and a reputation for engineering and metallurgical expertise,
More informationCARBIDE TOOLS & DIES MORE THAN 65 YEARS OF EXPERTISE IN CEMENTED CARBIDE AND WEAR RESISTANT PARTS
CARBIDE TOOLS & DIES MORE THAN 65 YEARS OF EXPERTISE IN CEMENTED CARBIDE AND WEAR RESISTANT PARTS PARTNERS IN HARD PRECISION MORE THAN 65 YEARS OF EXPERTISE IN CEMENTED CARBIDE AND WEAR RESISTANT PARTS
More informationFOR MACHINABLE AND FLAME HARDENABLE SURFACING. RECOMMENDED CURRENT RANGE & PACKING DETAILS Size (mm) Amps
H-MACH-1 FOR MACHINABLE AND FLAME HARDENABLE SURFACING Fe Cr Mn EURO-TECH H-MACH-1 is an all position basic coated electrode which can be successfully used in thick surfacing and intermediate layers can
More informationVALLIAMMAI ENGINEERING COLLEGE DEPARTMENT OF MECHANICAL ENGINEERING ME 6302 MANUFACTURING TECHNOLOGY 1 (QUESTION BANK) I-METAL CASTING PROCESSES PART-A (2 MARKS) 1.Name any four types of commonly used
More informationTOOL STEEL. Tool Steel VJ-04/2015. Copyright 2015 by Vojay LLP, United Kingdom.
www.vojaygroup.com VJ04/2015. Copyright 2015 by Vojay LLP, United Kingdom. Heat treatment requirements High Speed & Die General description Tool steel refers to a variety of carbon and alloy steels that
More informationHigh strength fine grained structural steel. Quenched and tempered. Product description. 890 a product brand of Dillinger 1/6
890 High strength fine grained structural steel Quenched and tempered Material data sheet, edition April 2016 1 DILLIMAX 890 is a high strength quenched and tempered, fine grained structural steel with
More informationHigh strength fine grained structural steel. Quenched and tempered. Product description. 965 a product brand of Dillinger 1/6
965 High strength fine grained structural steel Quenched and tempered Material data sheet, edition April 2016 1 DILLIMAX 965 is a high strength quenched and tempered, fine grained structural steel with
More informationWear-resistant steels. Technical terms of delivery for heavy plates. voestalpine Grobblech GmbH
Wear-resistant steels Technical terms of delivery for heavy plates voestalpine Grobblech GmbH www.voestalpine.com/grobblech Wear-resistant steels durostat durostat 400 durostat 450 durostat 500 durostat
More informationNordberg NP series impact crushers. Wear parts application guide
Nordberg NP series impact crushers Wear parts application guide Breaker plates Side liners Blow bars Wear parts application guide - Nordberg NP series impact crusher NP impactor and basic concepts There
More informationUDDEHOLM RAMAX LH. Uddeholm Ramax LH is a part of the Uddeholm Stainless Concept.
UDDEHOLM RAMAX LH TAKING STANDARDS TO A NEW LEVEL Setting standards is important in the tooling industry. Uddeholm Ramax LH is no exception. It is a first class tool steel for mould bases, with excellent
More informationA NEW COLD WORK PM-GRADE COMBINING HIGH WEAR RESISTANCE WITH HIGH DUCTILITY
A NEW COLD WORK PM-GRADE COMBINING HIGH WEAR RESISTANCE WITH HIGH DUCTILITY By Magnus Tidesten, Anna Medvedeva, Fredrik Carlsson and Annica Engström-Svensson UDDEHOLMS AB Uddeholm Vanadis 8 SuperClean
More informationWear-resistant steels. Technical terms of delivery for heavy plates. voestalpine Grobblech GmbH
Wear-resistant steels Technical terms of delivery for heavy plates voestalpine Grobblech GmbH www.voestalpine.com/grobblech Wear-resistant steels durostat durostat 400 durostat 450 durostat 500 durostat
More informationBy combining Uddeholm Ramax HH with one of our other products within the Stainless Concept, you can create a completely stainless mould.
UDDEHOLM RAMAX HH Uddeholm Ramax HH provides several benefits: The product offers uniform hardness in all dimensions combined with excellent indentation resistance. It is a corrosion resistant grade which
More informationUddeholm Formvar. FORMVAR is a trade mark registered in the European Union
Uddeholm Formvar FORMVAR is a trade mark registered in the European Union UDDEHOLMS AB No part of this publication may be reproduced or transmitted for commercial purposes without permission of the copyright
More informationEdition 5, The latest revised edition of this brochure is the English version, which is always published on our web site
UDDEHOLM HOLDAX This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty of
More informationQuend 700. Extra High Strength Structural Steel. Dimensions. 1 Steel description and applications. 4 Flatness, tolerances & surface properties
Extra High Strength Structural Steel Quend 700 1 Steel description and applications Quend 700 is extra high strength structural steel produced as quenched and tempered with a minimum yield strength of
More informationOPTIMIZATION OF PROPERTIES AND STRUCTURE WITH ADDITION OF TITANIUM IN HADFIELD STEELS Mohammad Bagher Limooei (1), Shabnam Hosseini (1)
Abstract OPTIMIZATION OF PROPERTIES AND STRUCTURE WITH ADDITION OF TITANIUM IN HADFIELD STEELS Mohammad Bagher Limooei (1), Shabnam Hosseini (1) 1- Islamic Azad University, Ayatollah Amoli Branch sh_hosseini@yahoo.com,
More informationUDDEHOLM TOOL HOLDER CONCEPT
Uddeholm Idun Uddeholm Idun Reliable and efficient steel is essential for good results. The same goes for achieving high productivity and high availability. When choosing the right steel many parameters
More informationSteel. Relia Quality Wear Resistant Plates PROPERTIES
is a range of high hardness, conventional low-alloyed martensitic steels, which obtain their hardness through intense water quenching during plate manufacturing. steel plates offer outstanding resistance
More informationCLADDING AND HARDFACING POWDERS
CLADDING AND HARDFACING POWDERS GTV consumables for Laser Cladding Version 1.1 Ni: NICKEL BASED POWDERS GTV No. Description Particle size Hardness C Ni Cr B Si Fe Mo Others 31.25.10 Inconel 625-160 +53
More informationEdition 5, The latest revised edition of this brochure is the English version, which is always published on our web site
UDDEHOLM SVERKER 3 This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty
More informationStandard Flux cored wires
Issued 11/12/2005 VERSCHLEISS-SCHUTZ GMBH THALE Standard Flux cored wires regarding application and properties content Standard Flux cored wires: CAST IRON WELDING...1 TOOL STEELS...2 TUNGSTEN CARBIDE
More informationCHAPTER 5 WORKPIECE MATERIALS AND PARAMETERS FOR EXPERIMENT
71 CHAPTER 5 WORKPIECE MATERIALS AND PARAMETERS FOR EXPERIMENT 5.1 INTRODUCTION The workpiece materials for the experimental study are selected on the basis such that mathematical equations arrived at
More informationYour Partner for Toolmaker Solutions
Your Partner for Toolmaker Solutions 2017.V1 US CERATIZIT is a high-tech engineering group specialized in tooling and hard material technologies. Tooling the Future 2 CATALOGUE RODS & PREFORMS 2017 HARD
More informationCHAPTER 21. Cutting-Tool Materials and Cutting Fluids. Kalpakjian Schmid Manufacturing Engineering and Technology 2001 Prentice-Hall Page 21-1
CHAPTER 21 Cutting-Tool Materials and Cutting Fluids Manufacturing Engineering and Technology 2001 Prentice-Hall Page 21-1 Cutting Tool Material Hardnesses Figure 21.1 The hardness of various cutting-tool
More informationATI 418 SPL alloy is readily forgeable and has fair machinability and cold formability in the annealed condition.
ATI 418 SPL Stainless Steel (UNS S41800) GENERAL PROPERTIES ATI 418 SPL alloy (Greek Ascoloy) is a corrosion and heat resistant stainless steel similar in many respects to Type 410 but exhibiting improved
More informationScanaVIPTOOL Steels VIP. It is the steel solution. Scana Steel USA (Steel Service center) What is VIP? Why VIP? Who needs VIP?
STEELUSA Scana USA ( Service center) What is VIP? VIP is the registered trademark for our products that are VIP treated for our VIP customers. VIP stands for Value added, Isotropy, Performance that are
More informationHot rolled Steel Plates, Sheets and Coils
Hot rolled Steel Plates, Sheets and Coils Steels resistant to wear and surface pressure AR Hardened steel resistant to abrasive wear cause by rolling contact and high surface pressure can be used to signiþ
More informationWelding Alloys Group STELLOY. Cobalt Products. Cobalt Base Welding Consumables for Cladding and Hardfacing
Welding Alloys Group STELLOY Cobalt Products Cobalt Base Welding Consumables for Cladding and Hardfacing Welding Alloys Group Since its foundation in 1966, the Welding Alloys Group,an independent group,
More informationSS-EN ISO 9001 SS-EN ISO 14001
UDDEHOLM FORMAXTM This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty
More information1 Cutting Tool Materials of common use
1 Cutting Tool Materials of common use Instructional Objectives At the end of this lesson, the students will be able to (i) Identify the needs and cite the chronological development of cutting tool materials.
More informationFailure Investigation of Cast Diesel Electric Loco Wheel +
Failure Investigation of Cast Diesel Electric Loco Wheel + M. K. Mukhopadhyay Former Dy. Chief Chemist & Metallurgist in Indian Railways E-mail : monoj48@gmail.com Introduction To meet the demand for Indian
More informationPRELIMINARY BROCHURE. Uddeholm Vanadis 8 SuperClean
PRELIMINARY BROCHURE Uddeholm Vanadis 8 SuperClean UDDEHOLMS AB No part of this publication may be reproduced or transmitted for commercial purposes without permission of the copyright holder. This information
More informationRAMAX 2. Prehardened stainless holder steel
RAMAX 2 Prehardened stainless holder steel This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be
More informationSTABILIZER HARDFACING PRODUCTS OIL &GAS DOWN HOLE DRILLING APPLICATION
STABILIZER HARDFACING PRODUCTS OIL &GAS DOWN HOLE DRILLING APPLICATION 1 HF 3000 PROCESS PRODUCTS/SOLUTIONS FOR HARDFACING ON STABILIZERS Welder brazing TUNGSTEN CARBIDE INSERTS TCI 70 to STABILIZER using
More informationINTRODUCTION. Think HSS
INTRODUCTION Think HSS SUMMARY METALLURGY 2 Excellent strength 3 A super sharp edge 4 Safe and reliable tools Alloy elements 6 The influence of alloy elements 7 Standard compositions of HSS 8 The HSS-PM
More informationTool Service. Welding consumables for toolmaking
Tool Service for toolmaking Since its foundation in 1966, the Welding Alloys Group has become the global specialist in the development of low and high alloyed cored wires. Individual developments and new
More informationHARDFACING ELECTRODES
HARDFACING ELECTRODES UTOP 38.. K1 UTOP 43.. K2 UTOP 45.. K3 UTOP 52.. K4 UTOP 55.. K5 TOOLDUR... K6 E DUR 250... K7 E DUR 300 K8 E DUR 400... K9 E DUR 500 K10 E DUR 600 K11 E DUR 60R. K12 E DUR 600Si..
More informationFabrication Guide. sole manufacturer of T200X HARDFACED PLATE. Wear Resistant Hardfaced Plate
Fabrication Guide Wear Resistant Hardfaced Plate HARDFACED PLATE sole manufacturer of T200X TM Wear Resistant Hardfaced Plate Fabrication Guide T his guide provides practical information on how to cut,
More informationChemical composition For the ladle analysis, the following limiting values in % are applicable: C Si Mn P S
500 Wear resistant steel Material data sheet, edition April 2016 1 DILLIDUR 500 is a wear resistant steel with a nominal hardness of 500 HBW in delivery condition ex works. DILLIDUR 500 is preferentially
More informationTHERMACLAD. A New Generation of Build-Up and Overlay Alloys. Engineered for the Toughest Roll Rebuilding Applications
THERMACLAD A New Generation of Build-Up and Overlay Alloys Engineered for the Toughest Roll Rebuilding Applications THERMACLAD BUILD-UP AND OVERLAY SUBMERGED ARC WELDING WIRES Stoody Company has a long
More informationREGIN 3. Cold work tool steel
Cold work tool steel This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty
More information