Supporting Information Benchmarking Cellulose Nanocrystals: From the Laboratory to Industrial Production

Size: px
Start display at page:

Download "Supporting Information Benchmarking Cellulose Nanocrystals: From the Laboratory to Industrial Production"

Transcription

1 Benchmarking Cellulose Nanocrystals: From the Laboratory to Industrial Production Michael S. Reid 1, Marco Villalobos 2 and Emily D. Cranston 1* 1 Department of Chemical Engineering, McMaster University Hamilton, Ontario, Canada, LS 4L 2 Cabot Corporation, Billerica, MA, US, 121 *Corresponding author: ecranst@mcmaster.ca 1

2 Crystallinity X-ray Diffraction. XRD measurements, to obtain the degree of crystallinity, were performed on freeze dried CNCs samples using a Bruker D DAVINCI diffractometer (Bruker USA) with a cobalt sealed tube source (λ avg = Å), 35 kv, 45 ma with a parallel focus Goebel Mirror, Vantec 5 area detector, and.5 mm micro-slit and.5 mm short collimator over a 2θ range of -45. Si wafer blanks were subtracted from all sample measurements. Two dimensional area detector frames were integrated to produce diffraction patterns, which then underwent Rietveld refinement. Percent crystallinity was determined by deconvolution using the cellulose I single crystal information file (CIF) to define peak position and a fixed amorphous peak at A pseudo-voigt function with linear background was used to fit peak shape and the CIF file with a March Dollase preferred orientation function model was used to fit peak intensity. For samples that contained both cellulose I and cellulose II structures the percentage of each crystal phase is presented. It is important to note that there are a number of methods described in the literature used to determine the crystallinity of cellulose and is not only limited to XRD.[1] [4] Furthermore, the validity and limitations of these methods and data fitting routines is a hotly debated topic and is beyond the scope of this work. Largely XRD is reported and the Rietveld refinement commonly considered to be the most accurate method.[5] [7] In a recent publication however, Ahvenainen et al. found good correlation with the five most common XRD fitting methods and the two dimensional Rietveld method.[] Moreover, within their work it is emphasized that comparison between samples and laboratories is extremely challenging. As such the crystallinity values presented here should be taken as relative (and comparable within this study) not absolute. Using the deconvolution method presented above the error in these measurements is taken to be 3-5%. 2

3 a)' 3, 2,5 1,5 5 b)' 1,4 1, Green-R-Si.raw_ alpha cellulose 1. % alpha cellulose 1. % Figure S1: XRD spectra of AITF CNCs a) as received and b) Soxhlet extracted in ethanol for 24 h. 2 Green-E-Si.raw_1 a)' Counts Yellow-R-Si.raw_ alpha cellulose 1. % 3 4 b)' 5, Yellow-E-Si.raw_1 1alpha cellulose 1. % 4, 3, Figure S2: XRD spectra of Lab-Made CNCs a) as received and b) Soxhlet extracted in ethanol for 24 h. 3

4 a)' 3, Supporting Information Orange-R2-Si.raw_1 1alpha cellulose 1. % 2,5 1, b)' 2,5 Orange-E2-Si.raw_1 1alpha cellulose 1. % 1, Figure S3: XRD spectra of CelluForce CNCs a) as received and b) Soxhlet extracted in ethanol for 24 h. a)' 2,5 Pink-R-Si.raw_1 1alpha cellulose 53.9 % Cellulose II % Counts 1,5 5 b)' 3, Pink-E-Si.raw_ alpha cellulose % Cellulose II 25.1 % 2,5 1, Figure S4: XRD spectra of FPL CNCs a) as received and b) Soxhlet extracted in ethanol for 24 h. 4

5 Thermal Stability Thermal Gravimetric Analysis. Thermal gravimetric analysis (TGA) was performed using TA Instruments Q5 thermal analyzer under a constant 1 ml/min argon flow. A minimum of 1 mg of freeze-dried as received and Soxhlet extracted CNCs were heated to 6 C at heating rate of 1 C/min. 1" Lab-Made"as"Received" Lab-Made"Soxhlet"Extracted" " Percent'Mass' 6" 4" 2" " 1" 15" 2" 25" 3" 35" 4" 45" 5" Temperature'( C)' Figure S5: TGA curves of as received and Soxhlet extracted Lab-Made CNCs. 1" CelluForce"as"Received" CelluForce"Soxhlet"Extracted" " Percent'Mass' 6" 4" 2" " 1" 15" 2" 25" 3" 35" 4" 45" 5" Temperature'( C)' Figure S6: TGA curves of as received and Soxhlet extracted CelluForce CNCs. 5

6 1" FPL"as"Received" FPL"Soxhlet"Extracted" " Percent'Mass' 6" 4" 2" " 1" 15" 2" 25" 3" 35" 4" 45" 5" Temperature'( C)' Figure S7: TGA curves of as received and Soxhlet extracted FPL CNCs. 1" " AITF"as"Received" AITF"Soxhlet"Extracted" So>wood"AITF" Percent'Mass' 6" 4" 2" " 1" 15" 2" 25" 3" 35" 4" 45" 5" Temperature'( C)' Figure S: TGA curves of as received and Soxhlet extracted cotton AITF CNCs and as received softwood AITF CNCs. 6

7 Changing Source and Production Scale 3, 2,5 AITF-RAW-SiBlank.raw_1 1beta cellulose 1. % 1, Figure S9: XRD spectra of as received AITF CNCS extracted from bleached softwood pulp. Other Nanocellulose Producers 2, 2,6 2,4 2,2 1, 1,6 1,4 1, AR-C-RAW-SiBlank.raw_1 1beta cellulose 1. % Figure S1: XRD spectra of as received API s BioPlus Crystals 3 4 3, BLUEGOOSE-RAW-SiBlank.raw_1 1beta cellulose 1. % 2,5 1, Figure S11: XRD spectra of as received Blue Goose Biorefineries BGB Natural nanocellulose 7

8 14" 12" 1" Mean%Intensity%(%)% " 6" 4" 2" " 1" 1" 1" 1" Apparent%Par2cle%Size%(nm)% Figure S12: Apparent particle size distribution of Blue Goose Biorefineries BGB Natural as measured by DLS References [1] U. P. Agarwal, S. a. Ralph, R. S. Reiner, and C. Baez, Probing crystallinity of never-dried wood cellulose with Raman spectroscopy, Cellulose, vol. 23, no. 1, pp , Feb [2] Y. Nishiyama, P. Langan, and H. Chanzy, Crystal structure and hydrogen-bonding system in cellulose Ibeta from synchrotron X-ray and neutron fiber diffraction., J. Am. Chem. Soc., vol. 124, no. 31, pp , Aug. 22. [3] S. Park, J. O. Baker, M. E. Himmel, P. a Parilla, and D. K. Johnson, Cellulose crystallinity index: measurement techniques and their impact on interpreting cellulase performance, Biotechnol. Biofuels, vol. 3, no. 1, p. 1, 21. [4] A. D. French and M. Santiago Cintrón, Cellulose polymorphy, crystallite size, and the Segal Crystallinity Index, Cellulose, vol. 2, no. 1, pp. 53 5, 213. [5] C. Driemeier and G. a. Calligaris, Theoretical and experimental developments for accurate determination of crystallinity of cellulose i materials, J. Appl. Crystallogr., vol., no. 1, pp , 211. [6] R. P. Oliveira and C. Driemeier, CRAFS: A model to analyze two-dimensional X-ray diffraction patterns of plant cellulose, J. Appl. Crystallogr., vol. 46, no. 4, pp , 213. [7] C. Driemeier, Two-dimensional Rietveld analysis of celluloses from higher plants, Cellulose, vol. 21, no. 2, pp , Apr [] P. Ahvenainen, I. Kontro, and K. Svedström, Comparison of sample crystallinity determination methods by X-ray diffraction for challenging cellulose I materials, Cellulose, vol. 23, no. 2, pp , Apr. 216.

Characterization of amorphous pharmaceuticals what can you do in the home lab? Michael Evans, Christina Drathen Bruker AXS GmbH, Karlsruhe, Germany

Characterization of amorphous pharmaceuticals what can you do in the home lab? Michael Evans, Christina Drathen Bruker AXS GmbH, Karlsruhe, Germany Characterization of amorphous pharmaceuticals what can you do in the home lab? Michael Evans, Christina Drathen Bruker AXS GmbH, Karlsruhe, Germany This document was presented at PPXRD - Pharmaceutical

More information

Supplementary Information

Supplementary Information Supplementary Information Design, synthesis and characterization of a Pt-Gd metal-organic framework containing potentially catalytically active sites Kai C. Szeto, Kjell Ove Kongshaug,, Søren Jakobsen,

More information

Lesson 1 Rietveld Refinement and Profex / BGMN

Lesson 1 Rietveld Refinement and Profex / BGMN Lesson 1 Rietveld Refinement and Profex / BGMN Nicola Döbelin RMS Foundation, Bettlach, Switzerland June 13 15, 2018, Bettlach, CH Diffraction Pattern 1000 Diffraction Angle 800 Absolute Intensity Intensity

More information

Supporting Information. Top-down fabrication of crystalline metal-organic framework nanosheets. Experimental section

Supporting Information. Top-down fabrication of crystalline metal-organic framework nanosheets. Experimental section Supporting Information Top-down fabrication of crystalline metal-organic framework nanosheets Pei-Zhou Li, a,b Yasushi Maeda a and Qiang Xu* a,b a National Institute of Advanced Industrial Science and

More information

X-ray diffraction

X-ray diffraction 2.2.3.- X-ray diffraction 2.2.3.1.- Origins and fundamentals of the technique The first experimental evidence concerning x-ray diffraction was given by Max von Laue who in 1912 demonstrated that x-rays

More information

ENZYME-ASSISTED ISOLATION OF MICRO FIBRILLATED CELLULOSE (MFC) FROM SACCHARUM MUNJA FIBRE AND ITS CHARACTERIZATION

ENZYME-ASSISTED ISOLATION OF MICRO FIBRILLATED CELLULOSE (MFC) FROM SACCHARUM MUNJA FIBRE AND ITS CHARACTERIZATION ISSN: 2250-0138 (Online) ENZYME-ASSISTED ISOLATION OF MICRO FIBRILLATED CELLULOSE (MFC) FROM SACCHARUM MUNJA FIBRE AND ITS CHARACTERIZATION GIRENDRA PAL SINGH a1, PALLAVI VISHWAS MADIWALE b AND R.V. ADIVAREKAR

More information

X-ray Diffraction Analysis of Polymers Expanding Materials Characterization Capabilities Using the ICDD Powder Diffraction File TM

X-ray Diffraction Analysis of Polymers Expanding Materials Characterization Capabilities Using the ICDD Powder Diffraction File TM X-ray Diffraction Analysis of Polymers Expanding Materials Characterization Capabilities Using the ICDD Powder Diffraction File TM Tom Blanton Stacy Gates, Soorya Kabekkodu, Justin Blanton, Cyrus Crowder

More information

Introduction to Powder Diffraction/Practical Data Collection

Introduction to Powder Diffraction/Practical Data Collection Durham University Chemistry Department Introduction to Powder Diffraction/Practical Data Collection Dr Ivana Evans Durham, January 2007 Durham Outline Information in a powder pattern What is diffraction

More information

ENZYME-ASSISTED ISOLATION OF MICRO FIBRILLATED CELLULOSE (MFC) FROM SACCHARUM MUNJA FIBRE AND ITS CHARACTERIZATION

ENZYME-ASSISTED ISOLATION OF MICRO FIBRILLATED CELLULOSE (MFC) FROM SACCHARUM MUNJA FIBRE AND ITS CHARACTERIZATION ISSN: 2250-0138 (Online) ENZYME-ASSISTED ISOLATION OF MICRO FIBRILLATED CELLULOSE (MFC) FROM SACCHARUM MUNJA FIBRE AND ITS CHARACTERIZATION GIRENDRA PAL SINGH a1, PALLAVI VISHWAS MADIWALE b AND R.V. ADIVAREKAR

More information

Effect of sample moisture content on XRD-estimated cellulose crystallinity index and crystallite size

Effect of sample moisture content on XRD-estimated cellulose crystallinity index and crystallite size Cellulose (2017) 24:1971 1984 DOI 10.1007/s10570-017-1259-0 ORIGINAL PAPER Effect of sample moisture content on XRD-estimated cellulose crystallinity index and crystallite size Umesh P. Agarwal. Sally

More information

Supplementary Information. A New Precipitation Pathway for Calcium Sulfate Dihydrate (Gypsum) via Amorphous and Hemihydrate Intermediates

Supplementary Information. A New Precipitation Pathway for Calcium Sulfate Dihydrate (Gypsum) via Amorphous and Hemihydrate Intermediates A New Precipitation Pathway for Calcium Sulfate Dihydrate (Gypsum) via Amorphous and Hemihydrate Intermediates Yun-Wei Wang, Yi-Yeoun Kim, Hugo K. Christenson and Fiona C. Meldrum Precipitation and Analysis

More information

Department of Chemistry and the Macromolecular Science and Engineering Program,

Department of Chemistry and the Macromolecular Science and Engineering Program, Supporting Information for the Design and Synthesis of a Series of Nitrogen-rich Energetic Cocrystals of 5,5 -dinitro-2h,2h -3,3 -bi-1,2,4- triazole (DNBT) Jonathan C. Bennion, Andrew McBain, Steven F.

More information

Novel biorefinery: A residue from wood bioethanol production converted into cellulose nanocrystals

Novel biorefinery: A residue from wood bioethanol production converted into cellulose nanocrystals Novel biorefinery: A residue from wood bioethanol production converted into cellulose nanocrystals ABSTRACT Martha Herrera, Jackson A. Etang, Aji P. Mathew and Kristiina Oksman, Department of Applied Physics

More information

Polydopamine tethered enzyme/metal-organic framework composites with high stability and reusability

Polydopamine tethered enzyme/metal-organic framework composites with high stability and reusability Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2015 Supporting information for Polydopamine tethered enzyme/metal-organic framework composites with

More information

AGING OF EXPLOSIVE CRYSTALS (RDX) INVESTIGATED BY X-RAY DIFFRACTION

AGING OF EXPLOSIVE CRYSTALS (RDX) INVESTIGATED BY X-RAY DIFFRACTION 1 AGING OF EXPLOSIVE CRYSTALS (RDX) INVESTIGATED BY X-RAY DIFFRACTION Michael Herrmann, Manfred A. Bohn Fraunhofer Institut für Chemische Technologie ICT, Pfinztal, Germany ABSTRACT Coarse and fine particles

More information

Electronic Supplementary Information Motorized. Janus Metal Organic Framework Crystals

Electronic Supplementary Information Motorized. Janus Metal Organic Framework Crystals Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2014 Electronic Supplementary Information Motorized Janus Metal Organic Framework Crystals Tristan T.

More information

Lesson 1 Good Diffraction Data

Lesson 1 Good Diffraction Data Lesson 1 Good Diffraction Data Nicola Döbelin RMS Foundation, Bettlach, Switzerland Digital Diffractometers Transmission Geometry Debye-Scherrer Geometry Reflective Geometry Bragg-Brentano Geometry Glass

More information

Structure of crystallographically challenged hydrogen storage materials using the atomic pair distribution function analysis

Structure of crystallographically challenged hydrogen storage materials using the atomic pair distribution function analysis Structure of crystallographically challenged hydrogen storage materials using the atomic pair distribution function analysis H. Kim, 1 K. Sakaki, 1 K. Asano, 1 M. Yamauchi, 2 A. Machida, 3 T. Watanuki,

More information

Metal Insertion in a Microporous Metal-Organic Framework Lined with 2,2 -Bipyridine

Metal Insertion in a Microporous Metal-Organic Framework Lined with 2,2 -Bipyridine Supporting Information for: Metal Insertion in a Microporous Metal-Organic Framework Lined with 2,2 -Bipyridine Eric D. Bloch, David Britt, Chain Lee, Christian J. Doonan, Fernando Javier Uribe-Romo, Hiroyasu

More information

Water-Enhanced Oxidation of Graphite to Graphene Oxide with Controlled Species of Oxygenated Groups

Water-Enhanced Oxidation of Graphite to Graphene Oxide with Controlled Species of Oxygenated Groups Electronic Supplementary Material (ESI) for Chemical Science. This journal is The Royal Society of Chemistry 2015 Electronic Supporting Information Water-Enhanced Oxidation of Graphite to Graphene Oxide

More information

PREPARATION AND PROPERTIES OF COTTON STALK BARK FIBER

PREPARATION AND PROPERTIES OF COTTON STALK BARK FIBER Journal of Materials Science and Engineering with Advanced Technology Volume 4, Number 1, 2011, Pages 57-68 PREPARATION AND PROPERTIES OF COTTON STALK BARK FIBER LONG LI, GUANZHONG SHENG, SHENGJING ZHANG

More information

Department of Fibres & Textile Processing Technology, Institute of Chemical Technology, Mumbai

Department of Fibres & Textile Processing Technology, Institute of Chemical Technology, Mumbai Enzyme-Assisted Isolation of Micro fibrillated Cellulose (MFC) from Saccharum Munja Fibre and its Characterization Girendra Pal Singh, Pallavi Vishwas Madiwale and R.V. Adivarekar Department of Fibres

More information

Drying Cellulose Nanocrystal Suspensions

Drying Cellulose Nanocrystal Suspensions Drying Cellulose Nanocrystal Suspensions Abstract. Drying cellulose nanocrystals (CNCs) while maintaining their nanoscale dimensions is a major challenge for uses which require a dry form of the material.

More information

Identification of Crystal Structure and Lattice Parameter. for Metal Powders Using X-ray Diffraction. Eman Mousa Alhajji

Identification of Crystal Structure and Lattice Parameter. for Metal Powders Using X-ray Diffraction. Eman Mousa Alhajji Identification of Crystal Structure and Lattice Parameter for Metal Powders Using X-ray Diffraction Eman Mousa Alhajji North Carolina State University Department of Materials Science and Engineering MSE

More information

Supplimentary Information. Large-Scale Synthesis and Functionalization of Hexagonal Boron Nitride. Nanosheets

Supplimentary Information. Large-Scale Synthesis and Functionalization of Hexagonal Boron Nitride. Nanosheets Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2014 Supplimentary Information Large-Scale Synthesis and Functionalization of Hexagonal Boron Nitride

More information

Travaux Pratiques de Matériaux de Construction

Travaux Pratiques de Matériaux de Construction Travaux Pratiques de Matériaux de Construction Section Matériaux 6 ème semestre 2009 Etude de Matériaux Cimentaire Par Diffraction des Rayons X Responsable: Silke Ruffing E-Mail: silke.ruffing@epfl.ch

More information

Smithsonian Museum Conservation Institute

Smithsonian Museum Conservation Institute Smithsonian Museum Conservation Institute XRD Analysis of the Corrosion Products from a Tlingit Copper Rattle MCI#6241 Object: Tlingit Stikine Rattle Owner/Custodian: National Museum of the American Indian

More information

A. KISHI AND H. TORAYA

A. KISHI AND H. TORAYA THE RIGAKU JOURNAL VOL. 21 / NO. 1 / 2004, 25 30 SIMULTANEOUS MEASUREMENTS OF X-RAY DIFFRACTION (XRD) AND DIFFERENTIAL SCANNING CALORIMETRY (DSC) DATA UNDER CONTROLLED HUMIDITY CONDITION: INSTRUMENTATION

More information

Supporting information

Supporting information Supporting information Surface area measurements 200-300 mg of each sample was degassed at 300 C for 2h under N 2 flow followed by a six point N 2 adsorption carried out at p/p 0 of 1 to 5 using a Nova

More information

Practical X-Ray Diffraction

Practical X-Ray Diffraction Typical Example Practical X-Ray Diffraction White powder sample of NaCl,KCl,KNO 3 (trace of H 2 O) Département de chimie Université Laval Prof. Josée BRISSON Dr. Wenhua BI 2014-03-20 Powder X-Ray Diffraction

More information

Supplementary Figure S1 A comparison between the indium trimer in ITC-n and nickel trimer in ITC-n-Ni.

Supplementary Figure S1 A comparison between the indium trimer in ITC-n and nickel trimer in ITC-n-Ni. Supplementary Figure S1 A comparison between the indium trimer in ITC-n and nickel trimer in ITC-n-Ni. Supplementary Figure S2 Powder XRD and the simulation pattern of (a) ITC-1, (b) ITC-2, ITC-2NH 2 and

More information

AN IN SITU HIGH-TEMPERATURE X-RAY DIFFRACTION STUDY OF PHASE TRANSFORMATIONS IN SILVER BEHENATE

AN IN SITU HIGH-TEMPERATURE X-RAY DIFFRACTION STUDY OF PHASE TRANSFORMATIONS IN SILVER BEHENATE Copyright JCPDS - International Centre for Diffraction Data 2005, Advances in X-ray Analysis, Volume 48. 27 AN IN SITU HIGH-TEMPERATURE X-RAY DIFFRACTION STUDY OF PHASE TRANSFORMATIONS IN SILVER BEHENATE

More information

QUANTITATIVE IN-SITU X-RAY DIFFRACTION ANALYSIS OF EARLY HYDRATION OF PORTLAND CEMENT AT DEFINED TEMPERATURES

QUANTITATIVE IN-SITU X-RAY DIFFRACTION ANALYSIS OF EARLY HYDRATION OF PORTLAND CEMENT AT DEFINED TEMPERATURES Copyright JCPDS-International Centre for Diffraction Data 9 ISSN 197- QUANTITATIVE IN-SITU X-RAY DIFFRACTION ANALYSIS OF EARLY HYDRATION OF PORTLAND CEMENT AT DEFINED TEMPERATURES C. Hesse (1), F. Goetz-Neunhoeffer

More information

How Many Parameters Can Affect the Solid Form of Cocrystallization Products in Mechanochemical Reactions? A Case Study

How Many Parameters Can Affect the Solid Form of Cocrystallization Products in Mechanochemical Reactions? A Case Study Supporting Information How Many Parameters Can Affect the Solid Form of Cocrystallization Products in Mechanochemical Reactions? A Case Study Yue Yuan, a,b Lin Wang, a Duanxiu Li, a Zongwu Deng, a Hailu

More information

A Designed 3D Porous Hydrogen-Bonding Network Based on a Metal-Organic Polyhedron

A Designed 3D Porous Hydrogen-Bonding Network Based on a Metal-Organic Polyhedron Supporting Information A Designed 3D Porous Hydrogen-Bonding Network Based on a Metal-Organic Polyhedron Wei Wei,*, Wanlong Li, Xingzhu Wang, Jieya He Department of Chemistry, Capital Normal University,

More information

Fundamentals of X-ray diffraction and scattering

Fundamentals of X-ray diffraction and scattering Fundamentals of X-ray diffraction and scattering Don Savage dsavage@wisc.edu 1231 Engineering Research Building (608) 263-0831 X-ray diffraction and X-ray scattering Involves the elastic scattering of

More information

Lesson 3 Sample Preparation

Lesson 3 Sample Preparation Lesson 3 Sample Preparation Nicola Döbelin RMS Foundation, Bettlach, Switzerland January 14 16, 2015, Bern, Switzerland Repetition: Bragg-Brentano Diffractometer Typical Configuration (with Kβ filter)

More information

Electronic Supplementary Information. Effect of Lattice Strain in Electrocatalytic Activity of IrO 2 for Water Splitting

Electronic Supplementary Information. Effect of Lattice Strain in Electrocatalytic Activity of IrO 2 for Water Splitting Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2018 Electronic Supplementary Information Effect of Lattice Strain in Electrocatalytic Activity of IrO

More information

Technical articles Micro-area X-ray diffraction measurement by SmartLab μ

Technical articles Micro-area X-ray diffraction measurement by SmartLab μ Technical articles Micro-area X-ray diffraction measurement by SmartLab μhr diffractometer system with ultra-high brilliance microfocus X-ray optics and two-dimensional detector HyPix-3000 Yuji Shiramata*

More information

Amorphous Quantitation Strategy for Crystalline Drug Substance a GSK Perspective. Peter Varlashkin GSK, Durham, NC, USA PPXRD 11

Amorphous Quantitation Strategy for Crystalline Drug Substance a GSK Perspective. Peter Varlashkin GSK, Durham, NC, USA PPXRD 11 Amorphous Quantitation Strategy for Crystalline Drug Substance a GSK Perspective Peter Varlashkin GSK, Durham, NC, USA PPXRD 11 This document was presented at PPXRD - Pharmaceutical Powder X-ray Diffraction

More information

FAYALITE SLAG MODIFIED STAINLESS STEEL AOD SLAG

FAYALITE SLAG MODIFIED STAINLESS STEEL AOD SLAG FAYALITE SLAG MODIFIED STAINLESS STEEL AOD SLAG Shuigen HUANG, Muxing GUO, Peter Tom JONES, Bart BLANPAIN Department of Metallurgy and Materials Engineering, KU Leuven, 3001 Heverlee, Belgium shuigen.huang@mtm.kuleuven.be,

More information

X-ray Powder Diffraction in Catalysis

X-ray Powder Diffraction in Catalysis X-ray Powder Diffraction in Catalysis 0/63 Introduction Introduction: scope of this lecture This lecture is designed as a practically oriented guide to powder XRD in catalysis, not as an introduction into

More information

Supporting Information. for. Advanced Materials, adma Wiley-VCH 2007

Supporting Information. for. Advanced Materials, adma Wiley-VCH 2007 Supporting Information for Advanced Materials, adma.200701772 Wiley-VCH 2007 69451 Weinheim, Germany Supporting Information Oligo(p-phenylene vinylene)s as a New Class of Piezochromic Fluorophores Jill

More information

Diffraction: Real Samples Powder Method

Diffraction: Real Samples Powder Method Diffraction: Real Samples Powder Method Diffraction: Real Samples Up to this point we have been considering diffraction arising from infinitely large crystals that are strain free and behave like ideally

More information

Instrument Configuration for Powder Diffraction

Instrument Configuration for Powder Diffraction Instrument Configuration for Powder Diffraction Advanced X-ray Workshop S.N. Bose National Centre for Basic Sciences, 14-15/12/2011 Innovation with Integrity Overview What is the application? What are

More information

for direct conversion of syngas to lower olefins

for direct conversion of syngas to lower olefins Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2015 Supporting Information Hierarchical structured α-al 2 O 3 supported S-promoted Fe catalysts for

More information

Reversible Hydrogen Storage

Reversible Hydrogen Storage Hydrogenation of Magnesium Nickel Boride for Reversible Hydrogen Storage Wen Li a, John J. Vajo a, Robert W. Cumberland a, Ping Liu a, Son-Jong Hwang b, Chul Kim b#, and Robert C. Bowman, Jr. c a HRL Laboratories,

More information

MICROSTRUCTURE OF THE PLASTIC BONDED EXPLOSIVE KS32

MICROSTRUCTURE OF THE PLASTIC BONDED EXPLOSIVE KS32 Copyright JCPDS-International Centre for Diffraction Data 2012 ISSN 1097-0002 65 MICROSTRUCTURE OF THE PLASTIC BONDED EXPLOSIVE KS32 M. Herrmann 1, P. B. Kempa 1, U. Förter-Barth 1, W. Arnold 2 1 Fraunhofer

More information

Electronic Supplementary Information (ESI) Eutectic melting of LiBH 4 KBH 4

Electronic Supplementary Information (ESI) Eutectic melting of LiBH 4 KBH 4 Electronic Supplementary Material (ESI) for Physical Chemistry Chemical Physics. This journal is the Owner Societies 2014 Electronic Supplementary Information (ESI) Eutectic melting of LiBH 4 KBH 4 Morten

More information

Electronic Supplementary Information. Jian-Rong Wang, Junjie Bao, Xiaowu Fan, Wenjuan Dai and Xuefeng Mei *

Electronic Supplementary Information. Jian-Rong Wang, Junjie Bao, Xiaowu Fan, Wenjuan Dai and Xuefeng Mei * Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2016 Electronic Supplementary Information ph-switchable vitamin B 9 gels for stoichiometry-controlled

More information

EDO UNIVERSITY IYAMHO FACULTY OF SCIENCE SEMINAR SERIES

EDO UNIVERSITY IYAMHO FACULTY OF SCIENCE SEMINAR SERIES EDO UNIVERSITY IYAMHO FACULTY OF SCIENCE SEMINAR SERIES STRUCTURAL CHARACTERIZATION OF CELLULOSE OF DIFFERENCE SIZE CLASSIFICATIONS M. A. ADEKOYA B.ED (IBADAN), PGD, M.TECH (AKURE) Department of Physics

More information

X-ray Diffraction and Vibrational Spectroscopy of Catalysts for Exhaust Aftertreatment

X-ray Diffraction and Vibrational Spectroscopy of Catalysts for Exhaust Aftertreatment Copyright (c)jcpds-international Centre for Diffraction Data 2002, Advances in X-ray Analysis, Volume 45. 139 X-ray Diffraction and Vibrational Spectroscopy of Catalysts for Exhaust Aftertreatment Roger

More information

AN INNOVATED LABORATORY XAFS APPARATUS

AN INNOVATED LABORATORY XAFS APPARATUS Copyright (c)jcpds-international Centre for Diffraction Data 2002, Advances in X-ray Analysis, Volume 45. 397 AN INNOVATED LABORATORY XAFS APPARATUS TAGUCHI Takeyoshi XRD Division, Rigaku Corporation HARADA

More information

Studying Amorphous Pharmaceutical Materials by Powder X-Ray Diffraction and other Solid-State Techniques

Studying Amorphous Pharmaceutical Materials by Powder X-Ray Diffraction and other Solid-State Techniques Studying Amorphous Pharmaceutical Materials by Powder X-Ray Diffraction and other Solid-State Techniques Shawn Yin, George Crull, Martha Davidovich, Denette Murphy, Anisha Patel, Beth Sarsfield, Ray Scaringe,

More information

Materials Lab 1(MT344) X-ray Diffractometer Operation and Data Analysis. Instructor: Dr. Xueyan Wu ( 吴雪艳 )

Materials Lab 1(MT344) X-ray Diffractometer Operation and Data Analysis. Instructor: Dr. Xueyan Wu ( 吴雪艳 ) Materials Lab 1(MT344) X-ray Diffractometer Operation and Data Analysis Instructor: Dr. Xueyan Wu ( 吴雪艳 ) Goals To give students a practical introduction into the use of X-ray diffractometer and data collection.

More information

A pcu-type Metal-Organic Framework with Spindle [Zn 7 (OH) 8 ] 6+ Cluster as Secondary Building Units

A pcu-type Metal-Organic Framework with Spindle [Zn 7 (OH) 8 ] 6+ Cluster as Secondary Building Units A pcu-type Metal-Organic Framework with Spindle [Zn 7 (OH) 8 ] 6+ Cluster as Secondary Building Units Jian-Rong Li, Ying Tao, Qun Yu and Xian-He Bu* Materials, methods and synthesis All the reagents for

More information

Effects of Different Purification Methods on Chicken Feather Keratin

Effects of Different Purification Methods on Chicken Feather Keratin Advanced Materials Research Online: 2014-06-06 ISSN: 1662-8985, Vols. 941-944, pp 1184-1187 doi:10.4028/www.scientific.net/amr.941-944.1184 2014 Trans Tech Publications, Switzerland Effects of Different

More information

SYSTEMATIC ERRORS IN LINEAR PSD BASED HTXRD SYSTEMS

SYSTEMATIC ERRORS IN LINEAR PSD BASED HTXRD SYSTEMS Copyright(c)JCPDS-International Centre for Diffraction Data 2,Advances in X-ray Analysis,Vol.43 267 SYSTEMATIC ERRORS IN LINEAR PSD BASED HTXRD SYSTEMS E.A. Payzant and W.S. Harrison, III * Metals and

More information

J GHOSH, *,#, S K CHATTOPADHYAY, A K MEIKAP and S K CHATTERJEE. The results were compared with earlier observations on pure zirconium. 1.

J GHOSH, *,#, S K CHATTOPADHYAY, A K MEIKAP and S K CHATTERJEE. The results were compared with earlier observations on pure zirconium. 1. Bull. Mater. Sci., Vol. 9, No. 4, August 006, pp. 385 390. Indian Academy of Sciences. Microstructural studies on variation of defect parameters in Zr Sn alloys and their transition with interchange of

More information

Supplementary Information. Federico A. Rabuffetti and Richard L. Brutchey

Supplementary Information. Federico A. Rabuffetti and Richard L. Brutchey Supplementary Information Local Structural Distortion of BaZr x Ti 1 x O 3 Nanocrystals Synthesized at Room Temperature Federico A. Rabuffetti and Richard L. Brutchey Department of Chemistry, University

More information

In Situ Powder X-ray Diffraction Study of Magnetic CoFe 2 O 4 Nanocrystallite Synthesis

In Situ Powder X-ray Diffraction Study of Magnetic CoFe 2 O 4 Nanocrystallite Synthesis Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2015 Supporting Information for: In Situ Powder Xray Diffraction Study of Magnetic CoFe 2 O 4 Nanocrystallite

More information

Effect of templates on catalytic activity of ordered mesoporous ceria for CO oxidation

Effect of templates on catalytic activity of ordered mesoporous ceria for CO oxidation Advanced Materials Research Submitted: 2014-06-13 ISSN: 1662-8985, Vols. 1033-1034, pp 95-98 Accepted: 2014-07-02 doi:10.4028/www.scientific.net/amr.1033-1034.95 Online: 2014-10-01 2014 Trans Tech Publications,

More information

Technical Specification for Laboratory X-ray diffraction system for measurements of Crystallographic Texture and Residual Stress

Technical Specification for Laboratory X-ray diffraction system for measurements of Crystallographic Texture and Residual Stress INDIAN INSTITUTE OF TECHNOLOGY BOMBAY MATERIALS MANAGEMENT DIVISION Direct : (+91-22) 2576 8800 (DR) / 8803 (Local) / 8804 (Import) / 8805 (Enquiry & Bill tracking), 8802(Progress) Email : drmm@iitb.ac.in,

More information

Fundamentals of Crystalline State and Crystal Lattice p. 1 Crystalline State p. 2 Crystal Lattice and Unit Cell p. 4 Shape of the Unit Cell p.

Fundamentals of Crystalline State and Crystal Lattice p. 1 Crystalline State p. 2 Crystal Lattice and Unit Cell p. 4 Shape of the Unit Cell p. Fundamentals of Crystalline State and Crystal Lattice p. 1 Crystalline State p. 2 Crystal Lattice and Unit Cell p. 4 Shape of the Unit Cell p. 7 Crystallographic Planes, Directions, and Indices p. 8 Crystallographic

More information

X ray diffraction in materials science

X ray diffraction in materials science X ray diffraction in materials science Goals: Use XRD spectra to determine the orientation of single crystals and preferred orientations in a thin film. Understand how grain size and strain affect the

More information

Supporting Information

Supporting Information S1 Supporting Information Metallocenes@COF-102: Organometallic Host-Guest Chemistry of Porous Crystalline Organic Frameworks Suresh Babu Kalidindi, [a] Kirill Yusenko, [a] and Roland A. Fischer* a Inorganic

More information

NanoTrees: Making Paper Stronger than Steel. Robert Moon, PhD and Greg Schueneman, PhD Forest Biopolymer Science & Engineering

NanoTrees: Making Paper Stronger than Steel. Robert Moon, PhD and Greg Schueneman, PhD Forest Biopolymer Science & Engineering NanoTrees: Making Paper Stronger than Steel Robert Moon, PhD and Greg Schueneman, PhD Forest Biopolymer Science & Engineering What do they do? Parks & Forests Recreation Camping Forest Fires Wildlife &

More information

Performance Improvement of Nano-Catalysts by Promoter-Induced Defects in the Support Material: Methanol Synthesis over Cu/ZnO:Al

Performance Improvement of Nano-Catalysts by Promoter-Induced Defects in the Support Material: Methanol Synthesis over Cu/ZnO:Al Supporting information for Performance Improvement of Nano-Catalysts by Promoter-Induced Defects in the Support Material: Methanol Synthesis over Cu/ZnO:Al By Malte Behrens, Stefan Zander, Patrick Kurr,

More information

Study of discrimination between natural graphite and artificial graphite

Study of discrimination between natural graphite and artificial graphite 65 * * * Study of discrimination between natural graphite and artificial graphite Kenji KIMURA*, Masanori KODA*, Naoki KURASHIMA* *Central Customs Laboratory, Ministry of Finance 6-3-5, Kashiwanoha, Kashiwa,

More information

A Low-Cost High-Energy Potassium Cathode

A Low-Cost High-Energy Potassium Cathode Supporting information A Low-Cost High-Energy Potassium Cathode Leigang Xue, Yutao Li, Hongcai Gao, Weidong Zhou, Xujie Lü, Watchareeya Kaveevivitchai, Arumugam Manthiram, and John B. Goodenough * Materials

More information

Supporting Information. Low temperature synthesis of silicon carbide nanomaterials using

Supporting Information. Low temperature synthesis of silicon carbide nanomaterials using Supporting Information Low temperature synthesis of silicon carbide nanomaterials using solid-state method Mita Dasog, Larissa F. Smith, Tapas K. Purkait and Jonathan G. C. Veinot * Department of Chemistry,

More information

Tailoring the Oxygen Content of Graphite and Reduced Graphene Oxide for Specific Applications

Tailoring the Oxygen Content of Graphite and Reduced Graphene Oxide for Specific Applications Supporting Information Tailoring the Oxygen Content of Graphite and Reduced Graphene Oxide for Specific Applications Naoki Morimoto, Takuya Kubo and Yuta Nishina 1. Materials. Graphite (SP-1) was purchased

More information

This lecture is part of the Basic XRD Course.

This lecture is part of the Basic XRD Course. This lecture is part of the Basic XRD Course. Basic XRD Course 1 A perfect polycrystalline sample should contain a large number of crystallites. Ideally, we should always be able to find a set of crystallites

More information

What if your diffractometer aligned itself?

What if your diffractometer aligned itself? Ultima IV Perhaps the greatest challenge facing X-ray diffractometer users today is how to minimize time and effort spent on reconfiguring of the system for different applications. Wade Adams, Ph.D., Director,

More information

Bright Thermal (Blackbody) Emission of Visible Light From LnO2 (Ln = Pr, Tb), Photoinduced by NIR 980 nm Laser

Bright Thermal (Blackbody) Emission of Visible Light From LnO2 (Ln = Pr, Tb), Photoinduced by NIR 980 nm Laser Electronic Supplementary Material (ESI) for Dalton Transactions. This journal is The Royal Society of Chemistry Electronic Supplementary Material (ESI) for Dalton Transactions This journal is The Royal

More information

Supporting Information

Supporting Information Supporting Information Interconversion between Metal-Organic Polyhedra and Metal-Organic Frameworks Jian-Rong Li, Daren J. Timmons, and Hong-Cai Zhou Department of Chemistry, Texas A&M University, College

More information

Basics of XRD part IV

Basics of XRD part IV Basics of XRD part IV Dr. Peter G. Weidler Institute of Functional Interfaces IFG 1 10/31/17 KIT The Research University in the Helmholtz Association Name of Institute, Faculty, Department www.kit.edu

More information

Copyright JCPDS - International Centre for Diffraction Data 2004, Advances in X-ray Analysis, Volume

Copyright JCPDS - International Centre for Diffraction Data 2004, Advances in X-ray Analysis, Volume Copyright JCPDS - International Centre for Diffraction Data 2004, Advances in X-ray Analysis, Volume 47. 240 SIMULTANEOUS MEASUREMENTS OF X-RAY DIFFRACTION (XRD) AND DIFFERENTIAL SCANNING CALORIMETRY (DSC)

More information

Quantitative phase analysis using the Rietveld method for samples in the Ti-Cr binary systems

Quantitative phase analysis using the Rietveld method for samples in the Ti-Cr binary systems 586 Quantitative phase analysis using the Rietveld method for samples in the Ti-Cr binary systems Ofer Beeri and Giora Kimmel Nuclear Research Center Negev, P.O.Box 9001, Beer-Sheva, 84190 Israel Abstract

More information

Nanoconfinement Crystallization of Frustrated Alkyl Groups: Crossover of Mesophase to Crystalline Structure

Nanoconfinement Crystallization of Frustrated Alkyl Groups: Crossover of Mesophase to Crystalline Structure Nanoconfinement Crystallization of Frustrated Alkyl Groups: Crossover of Mesophase to Crystalline Structure Haifeng Shi,,,* Haixia Wang, John H. Xin, Xingxiang Zhang, and Dujin Wang, * State Key Laboratory

More information

Layered TiS 2 Positive Electrode for Mg Batteries

Layered TiS 2 Positive Electrode for Mg Batteries Supporting Information: Layered TiS 2 Positive Electrode for Mg Batteries Xiaoqi Sun, Patrick Bonnick and Linda F. Nazar* Department of Chemistry and the Waterloo Institute of Nanotechnology, University

More information

Formation of and Light Emission from Si nanocrystals Embedded in Amorphous Silicon Oxides

Formation of and Light Emission from Si nanocrystals Embedded in Amorphous Silicon Oxides 10.1149/1.2392914, copyright The Electrochemical Society Formation of and Light Emission from Si nanocrystals Embedded in Amorphous Silicon Oxides D. Comedi a, O. H. Y. Zalloum b, D. E. Blakie b, J. Wojcik

More information

A Stable Super-Supertetrahedron with Infinite Order via. Assembly of Supertetrahedral T4 Zinc-Indium Sulfide Clusters

A Stable Super-Supertetrahedron with Infinite Order via. Assembly of Supertetrahedral T4 Zinc-Indium Sulfide Clusters Supporting Information for A Stable Super-Supertetrahedron with Infinite Order via Assembly of Supertetrahedral T4 Zinc-Indium Sulfide Clusters Li Zhang, Chaozhuang Xue, Wei Wang, Dandan Hu, Jing Lv, Dongsheng

More information

ATTACHMENT D3 University of British Columbia X-Ray Diffraction Report and Scanning Electron Microscopy Images

ATTACHMENT D3 University of British Columbia X-Ray Diffraction Report and Scanning Electron Microscopy Images Appendix D Laboratory Geotechnical Data and Interpretation ATTACHMENT D3 University of British Columbia X-Ray Diffraction Report and QUANTITATIVE PHASE ANALYSIS OF ONE POWDER SAMPLE USING THE RIETVELD

More information

A new polymorph of 1-hydroxy-2-naphthoic acid obtained

A new polymorph of 1-hydroxy-2-naphthoic acid obtained Supporting information Volume 71 (2015) Supporting information for article: A new polymorph of 1-hydroxy-2-naphthoic acid obtained during failed co-crystallization experiments Qi Zhang, Meiqi Li and Xuefeng

More information

CHAPTER 4 SYNTHESIS, CHARACTERIZATION AND MICROENCAPSULATION PROCESS OF THE NANO SILICA

CHAPTER 4 SYNTHESIS, CHARACTERIZATION AND MICROENCAPSULATION PROCESS OF THE NANO SILICA 70 CHAPTER 4 SYNTHESIS, CHARACTERIZATION AND MICROENCAPSULATION PROCESS OF THE NANO SILICA 4.1 INTRODUCTION This chapter is concerned with the synthesis of nano silica particles from the natural resources

More information

Electronic Supplemental Information

Electronic Supplemental Information Electronic Supplemental Information Laser wavelength- and power-dependent plasmon-driven chemical reactions by single particle surface enhanced Raman spectroscopy Leilei Kang, a Ping Xu* a,b Bin Zhang,

More information

Supplementary Information

Supplementary Information Supplementary Information Disperse fine equiaxed alpha alumina nanoparticles with narrow size distribution synthesised by selective corrosion and coagulation separation Sanxu Pu, Lu Li, Ji Ma, Fuliang

More information

Europe. Benchtop X-Ray Diffractometer.

Europe. Benchtop X-Ray Diffractometer. Europe Benchtop X-Ray Diffractometer www.gnr.it benchtop x-ray diffractometer Europe, High Performance in a compact configuration GNR is a worldwide market leader supplying advanced X-Ray (XRD, XRF) and

More information

Comparative kinetic study of the thermal decomposition of nanocellulose produced by H 2 SO 4 hydrolysis, Tempo, and AVAP processes

Comparative kinetic study of the thermal decomposition of nanocellulose produced by H 2 SO 4 hydrolysis, Tempo, and AVAP processes Atlanta University Center DigitalCommons@Robert W. Woodruff Library, Atlanta University Center ETD Collection for AUC Robert W. Woodruff Library 7-1-2015 Comparative kinetic study of the thermal decomposition

More information

Synthesis and Characterization of Cadmium Sulfide Nanoparticles

Synthesis and Characterization of Cadmium Sulfide Nanoparticles Synthesis and Characterization of Cadmium Sulfide Nanoparticles R.Hepzi Pramila Devamani 1*, R.Kiruthika, P.Mahadevi and S.Sagithapriya 2 1 1. Assistant Professor, Department of Physics, V.V.Vanniaperumal

More information

Methane oxidation over A-site ordered and disordered Sr 0.8 Gd 0.2 CoO 3- perovskites

Methane oxidation over A-site ordered and disordered Sr 0.8 Gd 0.2 CoO 3- perovskites Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2014 Methane oxidation over A-site ordered and disordered Sr 0.8 Gd 0.2 CoO 3- perovskites Sergei N.

More information

Travaux Pratiques de Matériaux de Construction. Etude de Matériaux Cimentaires par Diffraction des Rayons X sur Poudre

Travaux Pratiques de Matériaux de Construction. Etude de Matériaux Cimentaires par Diffraction des Rayons X sur Poudre Travaux Pratiques de Matériaux de Construction Section Matériaux 6 ème semestre 2015 Etude de Matériaux Cimentaires par Diffraction des Rayons X sur Poudre Study Cementitious Materials by X-ray diffraction

More information

Supporting Information for Sub-1 nm Nanowire Based Superlattice Showing High Strength and Low Modulus Huiling Liu,, Qihua Gong, Yonghai Yue,*,

Supporting Information for Sub-1 nm Nanowire Based Superlattice Showing High Strength and Low Modulus Huiling Liu,, Qihua Gong, Yonghai Yue,*, Supporting Information for Sub-1 nm Nanowire Based Superlattice Showing High Strength and Low Modulus Huiling Liu,, Qihua Gong, Yonghai Yue,*, Lin Guo*, and Xun Wang*, *To whom correspondence should be

More information

Application Note. Introduction. Analysis of crystal polymorphism by Raman Spectroscopy for Medicine Development

Application Note. Introduction. Analysis of crystal polymorphism by Raman Spectroscopy for Medicine Development Application Note Analysis of crystal polymorphism by Raman Spectroscopy for Medicine Introduction Crystal polymorphism is a phenomenon where Raman applications in the pharmaceutical Industry compounds

More information

Preparation of Large-area, Crack-free Polysilazane-based Photonic. Crystals

Preparation of Large-area, Crack-free Polysilazane-based Photonic. Crystals Supporting Information Preparation of Large-area, Crack-free Polysilazane-based Photonic Crystals Zongbo Zhang a,c, Weizhi Shen a,c, Changqing Ye a,c, Yongming Luo a, Shuhong Li b, Mingzhu Li a,*, Caihong

More information

XPS STUDY OF DIAMOND-LIKE CARBON-BASED NANOCOMPOSITE FILMS

XPS STUDY OF DIAMOND-LIKE CARBON-BASED NANOCOMPOSITE FILMS International Journal of Nanoscience Vol. 3, No. 6 (2004) 797 802 c World Scientific Publishing Company XPS STUDY OF DIAMOND-LIKE CARBON-BASED NANOCOMPOSITE FILMS S. ZHANG,Y.Q.FU,X.L.BUIandH.J.DU School

More information

STRUCTURAL INFORMATION FROM THE RAMAN SPECTRA OF ACTIVATED CARBON MATERIALS

STRUCTURAL INFORMATION FROM THE RAMAN SPECTRA OF ACTIVATED CARBON MATERIALS STRUCTURAL INFORMATION FROM THE RAMAN SPECTRA OF ACTIVATED CARBON MATERIALS N. Shimodaira, A.Masui, A.Takada, YShinozaki, and N. Tomita Research Center, Asahi Glass Co. Ltd. 1150 Hazawa-cho, Kanagawa-ku,

More information

Application Note. Raman Spectroscopy Analysis of Crystalline Polymorphs for Pharmaceutical Development

Application Note. Raman Spectroscopy Analysis of Crystalline Polymorphs for Pharmaceutical Development Raman Applications in the Pharmaceutical Industry Impurity Analysis (Identification of micro impurities - sizes less than 1 µm) Evaluation of Synthetized Compounds (Structural analysis in combination with

More information

DIFFRACTION METHODS IN MATERIAL SCIENCE. PD Dr. Nikolay Zotov Lecture 6

DIFFRACTION METHODS IN MATERIAL SCIENCE. PD Dr. Nikolay Zotov   Lecture 6 DIFFRACTION METHODS IN MATERIAL SCIENCE PD Dr. Nikolay Zotov Email: zotov@imw.uni-stuttgart.de Lecture 6 OUTLINE OF THE COURSE 0. Introduction 1. Classification of Materials 2. Defects in Solids 3+4. Basics

More information