RHODORSIL RTV 141 A and B

Size: px

Start display at page:

Download "RHODORSIL RTV 141 A and B"

Louise Leonard
6 years ago
Views:

1 Cancels and replaces SIL Description RHODORSIL RTV 141 A and B is a two component, polyaddition reaction, room temperature curing silicone elastomer. Curing can be accelerated by heating. After mixing the two components RHODORSIL RTV 141 A and B forms a relatively low viscosity, colorless liquid which transforms into an elastic and transparent material once cured. The reaction does not give off any heat. Advantages TRANSPARENCY, good optical transmission. GOOD POURABILITY, for easy filling. Possibility of adding fillers. Good reversion resistance in confined spaces Applications Characteristics Coating or potting protection of electronic components and electrotechnical equipment. Opto-electronic links. Insulation of light sensitive cells. Sheathing of step index optic fibers. 1. Components of RHODORSIL RTV 141 A and B Properties Physical state... Appearance (1)... Color... Specific gravity at 25 C, approx. Viscosity at 25 C, mpa.s, approx... 2 Mixing the two components RHODORSIL RTV 141 A Slightly viscous liquid Clear or slightly cloudy Colorless RHODORSIL RTV 141 B Slightly viscous liquid Clear or slightly cloudy Colorless RHODORSIL RTV 141 A parts RHODORSIL RTV 141 B parts Viscosity of RTV 141A and B mixture 25 C, mpa.s, ap px Pot life of the catalysed mixture at 25 C, approx h Gellnorm at 50 C, approx min 1/5

2 RTV 141 Change in viscosity Viscosity Pa.s Mini * Maxi Time (h) Time after which the elastomer (or the object) can be handled at 25 C, approx...24 to 4 8 h 3. Cured compound 3.1 Mechanical properties Measured after curing 1 hour at 150 C On 6 mm thick specimen Shore A hardness, points, approx (Standard ASTM D 2240) On 2 mm thick film Tensile strength, MPa, approx (Standard AFNOR NF T 46002) Elongation at break, %, approx (Standard AFNOR NF T ) 3.2 Physical properties Linear shrinkage, %, approx Refractive index, n 25 approx Volume expansion coefficient, K -1, approx Thermal conductivity, W(m.K), approx ,16 Brittle point, C, approx (Standard ASTM D 746) Peak thermal withstand, C, approx Comment : Curing at room temperature gives low linear shrinkage (0.4%), however it stops the cured compound from reaching its optimum mechanical properties. 2/5

3 3.3 Dielectric properties Dielectric strength, kv/mm, approx (Standards AFNOR NF C et CEI 243) Dielectric constant at 1 khz, approx (Standards AFNOR C et CEI 250) Dielectric dissipation factor at 1 khz, approx (Standards AFNOR NF C et CEI 250) Volume resistivity, Ω.cm, approx (Standards AFNOR NF C et CEI 93) Comment: the above values cannot be used for specifications. To write such a document please consult us. Processing Remix each of the two components (base + catalyst) before each use. 1. Mixing the two components Add 10 parts of RHODORSIL RTV 141 B to 100 parts of RHODORSIL RTV 141 A. The two components are thoroughly mixed using an electrical or pneumatic mixer, on a low speed setting so as to limit the inclusion of air in the mixture. A dispensing machine can also be used. 2. Degasing After mixing parts A and B, it is preferable to degas the products to eliminate the air bubbles that would be visible in the finished part and which would reduce the mechanical and dielectrical properties. Degasing is generally carried out with a vacuum of 30 to 50 mbar releasing the vacuum several times during the operation. This product is particularly long to degas. A recipient with a high diameter/height ratio is better suited to quick degasing; however the height must be sufficient to contain the swelling of the elastomer under vacuum conditions. 3. Pouring the mixture RHODORSIL RTV 141 is poured slowly and regularly. In the case of a high thickness coating operation, the casting must be made at the lowest point in the volume to be filled; this avoids forming and including air bubbles in the volume. It should not be filled totally to allow expansion of the RTV at service temperatures. 4. Curing At 23 C, demoulding of RHODORSIL RTV 141 A and B is possible after approximately 24 to 48 hours at room temperature. Heat helps to accelerate curing. Recommended curing temperature : 4 hours at 60 C or 2 hours at 100 C or 1 hour at 150 C Comment : Certain materials that the RTV may be in contact with when curing could inhibit the reaction: Sulphur-containing cured natural and synthetic rubber compounds RTV's catalysed with metal salts PVC stabilized with tin salts Epoxydes catalysed with amines 3/5

4 If in doubt, it is recommended to carry out a test beforehand. It is also recommended to keep special degasing equipment for this type of RTV. Indeed, degasing of other products in the same container could pollute the latter and be detrimental to the curing of RHODORSIL RTV 141 A and B. 5. Adhesion Adhesion is achieved on most materials using PRIMER PMB 821 (after degreasing beforehand with a solvent), applied by immersion or with a brush, then dried for 30 minutes at approx. 25 C. For optimum adhesion, the RTV must be poured within the following four hours. Excess primer deteriorates the adhesion level. When PRIMER PMB 821 does not give sufficient results, another primer can be recommended, please consult us. Specific case of repair work : An object coated in RHODORSIL RTV 141 can be repaired: after cutting, simply make up the volume of elastomer with more, new RHODORSIL RTV 141 which has strong self adhesion without the need for a primer. Repair of RHODORSIL RTV 141 is invisible in the transparent bulk; however, the incision should be made at the last minute to avoid any soiling of the surfaces before the new product is poured in. Make sure that packaging is hermetically closed again each time it is used. Packaging RHODORSIL RTV 141 A and B are delivered in kits of : - 1 kg of part A kg of part B - 5 kg of part A kg of part B RHODORSIL RTV 141 A is also available in 25 and 200 kg packs and the corresponding 2.5 and 20 kg packs of RHODORSIL RTV 141 B. Storage and shelf life When stored in its original unopened packaging, at a temperature of between -5 C and + 30 C, RHODORSIL RTV 141 A and B may be stored for up to 24 months, from the date of manufacture clearly marked on the packaging. Beyond this date, Bluestar Silicones no longer guarantees the conformity of the products with the sales specifications. Safety Consult the Safety Data Sheet for RHODORSIL RTV 141 A and B. 4/5

5 Visit our website EUROPE NORTH AMERICA LATIN AMERICA ASIA PACIFIC Bluestar Silicones France 21 Avenue Georges Pompidou F69486 Lyon Cedex 03 FRANCE Tel. (33) Fax (33) Bluestar Silicones USA Two Tower Center Boulevard Suite 1601 East Brunswick, NJ United States Tel. (1) Fax (1) Bluestar Silicones Brasil Ltda. Av. Maria Coelho Aguiar, 215, Bloco G -1º Andar São Paulo - SP - Brasil Tel. (55) Bluestar Silicones Hong Kong Trading Co., Ltd. 29/ F, 88 Hing Fat Street Causeway Bay - Hong Kong Tel. (852) Fax (852) Warning to the users The information contained in this document is given in good faith based on our current knowledge. It is only an indication and is in no way binding, particularly as regards infringement of or prejudice to third party rights through the use of our products. BLUESTAR SILICONES guarantees that its products comply with its sales specifications. This information must on no account be used as a substitute for necessary prior tests which alone can ensure that a product is suitable for given use. Users are responsible for ensuring compliance with local legislation and for obtaining the necessary certifications and authorisations. Users are requested to check that they are in possession of the latest version of this document and BLUESTAR SILICONES is at their disposal to supply any additional information. 5/5

BLUESIL V-340. Addition Cure Silicone Elastomer. Moldmaking February Description. Applications. Typical Properties

BLUESIL V-340. Addition Cure Silicone Elastomer. Moldmaking February Description. Applications. Typical Properties Moldmaking February 2012 BLUESIL V-340 Description Applications Typical Properties Addition Cure Silicone Elastomer BLUESIL V-340 is a two component, addition reaction, room temperature or heat accelerated