An Investigation of Adhesion Wear Behavior of Tool Steel on Blanking Die
|
|
- Barbara Beasley
- 6 years ago
- Views:
Transcription
1 2011 International Conference on Advanced Materials Engineering IPCSIT vol.15 (2011) (2011) IACSIT Press, Singapore An Investigation of Adhesion Wear Behavior of Tool Steel on Blanking Die Komgrit Lawanwong 1+, Natthasak Pornputsiri and Ghit Luangsopapun 2 1 Department of Tool&Die engineering, Faculty of Industrial and Technology, Rajamangala University of Technology Rattanakosin, Wang Klai Kang Wong Campus Prachubkirikhan 77110, THAILAND. 2 Thailand Institute of Scientific and Technological Research, Pathum Thani 12120, THAILAND. Abstract. This research work aims to exploration wear phenomenon on punch for blanking stainless steel. Three punch materials: JIS SKD11, and were studied. Those punches were hardened to fixed hardness 59 HRC. Stainless steel JIS SUS 430 having the same thickness of 2 mm were employed as workpiece material for the experiments. Clearance between punch and die of blanking tool was five percent of workpiece thickness. The strip was blanked into circular shapes of 25 mm. in diameter. Direct measurement of wear on blanking punch was carried out using optical microscope. Each punch was used for blanking 2,000 stroke/conditions. It was found that had shown lower wear than SK D 11 and respectively. The higher tungsten, molybdenum and vanadium content of increase the amount of carbide compound caused hard and durable of cutting edge. Beside, punch had shown highest adhesive because high chromium content has compatibility of elements. The compatibility of metal element caused of high adhesion, friction and wear rate. Punch material had shown high wear rate because of low chemical composition. Moreover punch had shown highest corrosion on cutting edge. Keywords: Adhesion wear, Blanking die, Stainless steel, Tool steel, Blanking Punch 1. Introduction One of important process in the metal forming is the blanking process. Blanking and piercing operations are widely used to cut sheet metal or plates by a shearing process between punch and die for mass production of precision engineering components. The quality of the parts, evaluated by the profile of the shaped surface depends on many factors such as tool design; punch material properties, stamping conditions and especially tool wear [1]. Tool wear in blanking process is very important in case of cutting high production. Hence the studies on tool wear have been able recently because the wear mechanism and contact conditions such as punch material conditions, surface roughness and generation of wear particles can not be explained. Many experimental researches have been done to investigate the wear phenomenon under the relatively simple tests [2 8] but the researches have been related to experimental observation of wear profiles on blanking tool could not explain wear phenomenon according to the increase of the number of pieces. Furthemore, the high precision of the parts, smooth sheared edges and high tool life, many research have been conducted. Takaishi [9] measured the wear contour on die and punch in the shearing process of stainless steel sheets according to various clearances between die and punch. Choy and Balendra [10] analyzed the wear phenomenon with describing the wear punch profile as the changes of radius around punch edge. Aoki [11] observed wear profiles on punch during sheet metal shearing process. Tronel and Chenot [12] predicted tool wear in hot forging process by the finite element method. In this paper focuses wear behaviors of the punch using three kinds punches materials are investigated. In addition, the behaviors of adhesive wear on blanking punch investigate by SEM and EDS analysis. + Corresponding Author Tel.: fax: address: Komgrit.law@Kmutt.ac.th., Natthasak_idt@Hotmail.com, Ghit@Tistr.mail.go.th 25
2 2. Experimental Procedure The Stainless steel SUS 430 [JIS] is employed in the experiments. The chemical property of workpiece material was shown in table 1. Sheet strip of workpiece material thickness is 2 mm and 30 mm in width. A mechanical property of workpiece material was shown in table 2. The workpiece strip is shown in Fig. 1. The chemical properties of punch materials were illustrated in table 3. The blanking tool was designed to blank circular part of 25 mm diameter. The punch cutting edge insert and die button were made from JIS SKD11, and steel fixed hardened to 60 HRC [Fig.2]. The cutting edge was designed as an insert to the punch shank as shown in Fig. 3 in order to be easily removed [Fig.3]. Tool clearance employed in this experiment was 5% of sheet thickness [0.1 mm]. The photograph of blanking tool and die set is shown in Fig. 4. Air feeder installed with die set was used in the experiment. Experiments were carried out using a 60 tons mechanical press [Fig.5]. Blanking operations were performed without lubricant. 25 mm Fig. 1: Workpiece strip Fig. 2: Blanking punch Fig. 3: Shank of punch Fig. 4: Blanking die set with feeder Fig. 5: Mechanical press 60 tons In general, the degree of wear is higher for blanking punch than die. Therefore only blanking punch cutting edge is measured to quantity wear. The flank wear length and face wear length [Fig.6.] were measured under Optical microscope with program Axivo Version 5. Moreover, adhesive wear on blanking were observed by Scanning Electron Microscopy [SEM] and Energy Dispersive Spectrometry [EDS] analysis. Wear measurement have been made after 100, 200, 300, 500, 800, 1,000 and 2,000 strokes. Table 1: Chemical compositions of workpiece material.(%) C Si Fe Table 2: Mechanical properties of workpiece material. Yield Strength Tensile Strength Elongation Hardness 289 N/mm N/mm 2 27 % 142 HV 26
3 Table 3: Chemical compositions of punch materials (%) Material C Si Fe W Mn Ni Mo V Face wear length Flank wear length Face wear position Flank wear position Fig. 6: Measurement on punch cutting edge 3. Results and Discussions 3.1. Influence of Particle Adhesion to Tool Wears In the blanking experiments the level of face wear length is lower than flank wear length because punch side slides back and forth against workpiece material during the blanking operation. Where as there is no sliding action between punch face and workpiece material. The results of flank wear length and face wear length of blanking punch with number of workpiece are shown in Fig.7 and 8, respectively. From Fig. 7 and 8 the wear length on punch has been investigated up to 2,000 strokes. It was found that the flank wear length quickly increases at the beginning of experiments up to 500 strokes. After 1,000 strokes, wear length becomes to stable. In Fig. 11, face wear length quickly increases at the beginning of experiment up to 500 strokes. After 500 strokes, wear length becomes to stable. 1.4 Flank wear length (mm) Flank wear Number of workpiece Fig. 7: The relationship of flank wears with number of parts. It was found that the flank and face wear length of punch material had shown lower wear rate than and respectively. The higher tungsten, molybdenum and vanadium content of increase the amount of carbide compound caused hard and durable of cutting edge. The flank and face wear length of punch material JIS; is larger than punch material JIS; and, respectively. Since punch material has low molybdenum and chromium composition that show low wear resistance. On the other hand punch material JIS; and JIS; had shown nearly wear resistance trend. Moreover JIS; had shown adhesion of workpiece to blanking punch more than punch material JIS; 27
4 . Further more,it was found that punch material JIS; high chromium similar workpiece [SUS 430] has compatibility of element. s 0.5 Face wear length (mm) Flank wear Number of workpiece Fig. 8: The relationship of face wears with number of parts. Adhesion phenomenal of workpiece material with cutting had shown Fig Adhesion of workpiece on punch is large than punch and. It was found that compatibility between workpiece material [high chromium content] and punch material [ high chromium content] caused of adhesion on the surface. The compatibility of metal element caused of high adhesion, friction and wear rate. Adhesion of workpiece to blanking punch make sure the result of adhesion by EDS had shown in Fig.9. Adhesion of workpiece 100 Strokes Fig. 9: SEM image at 100X and EDS analysis of the adhesion on cutting edge of. 100 Strokes Fig. 10: SEM image at 100X and EDS analysis of the adhesion on cutting edge of. 28
5 100 Strokes Fig. 11: SEM image at 100X and EDS analysis of the adhesion on cutting edge of The results of SEM and EDS analysis from the experiments after 2000 strokes had shown in Fig.11- Fig.13. It was found that Fig SEM image of surface cutting punch does not show adhesion of workpieces because junction of adhesion separated occurs at the interface. High pickup of workpiece on punch surface caused of high adhesion and high wear rate. EDS analysis had shown insignificant amount of adhesion on cutting edge. Furthermore, in the case of [Fig.11] had shown EDS analysis confirmed that there the high corrosion around surface Strokes Fig. 12: SEM image at 100X and EDS analysis of the adhesion on cutting edge of Strokes Fig. 13: SEM image at 100X and EDS analysis of the adhesion on cutting edge of. Corrosion 2000 Strokes Cl Fig. 14: SEM image at 100X and EDS analysis of the adhesion on cutting edge of SKD 3 29
6 4. Summary The aim of the study was explorations of adhesion wear on blanking die. Tool steel of higher tungsten, molybdenum and vanadium content had shown high wear resistance and durable of cutting edge. Moreover, punch high chromium content had shown compatibility of metal elements cased of high adhesion, friction and wear rate. Punch material had shown high wear rate and high corrosion because low chemical composition content. 5. Acknowledgements The authors would like to give our attitude to Department of Tools and Material King Mongkut s University of Technology Thonburi (Thailand) for supporting the die equipment and Office of the Higher Education Commission for funding of the research. 6. References [1] X.T. Zeng, S. Zhang, and T. Muramatsu. Comparison of three advanced hard coatings for stamping applications. Surface and Coatings Technology. 2000, 127: [2] B. W. Rooks. The Effect of Die Temperature on Metal Flow and Die Wear During High Speed Hot Forging. Proceedings of the 15th MTDR Conference, Birmingham, England. 1974, 4: [3] American Society for Metals, Failure Analysis and Prevention. Metals Handbook, 8th Edition, Vol. 10, ASM Handbook committee, ASM, Metals Park, OH, USA, 1974, pp [4] P. H. Hansen and P. H. Bay. A flexible computer based system for prediction of wear distribution in forming tools. Adv. Technol. 1990, Plasticity 1: [5] M. J. Liou and H. S. Hasio. Prediction of die wear in high speed hot upset forging. ERC/NSDM Report, OSU. 1989, pp [6] J. P. Cescutti, N. Soyris, G. Surdon, and J. L. Chenot. Thermo-mechanical finite element calculation of three dimensional hot forging with remeshing. In: Proceedings of the Conference on Advanced Technology of Plasticity. Stuttgart, 1987, pp [7] S. M. J. Ali, B. W. Rooks, and S. A. Tobias. The effect of dwell time on die wear in high speed hot forging. Proc. Inst. Mech. Eng. 1971, 185: [8] E. Doege, P. Groche, and T. Bobke. Application of adhesion theory to frictional and wear processes in hot die forging. Adv. Technol. 1990, Plasticity 1: [9] K. Takaishi. Wear characteristics of the tools for perforating small holes in stainless steel stripes. J. Jpn. Soc. Technol. Plasticity 1988, 29 (330): [10] C.M. Choy and R. Balendra. Simulation of the effect of tool geometry changes on blanking operations. In: Proceedings of the 9th International Cold Forging Congress, Solihull, UK. 1995, pp [11] I. Aoki. Tool wear in shearing of amorphous alloy foils: shearing of amorphous alloy foils II. J. Jpn. Soc. Technol. Plasticity 1986, 27 (308): [12] Y. Tronel and J. L. Chenot. Prediction of tool wear using finite element software for the three-dimensional simulation of the hot-forging process. J. Mater. Proc. Tech. 1992, 31:
WEAR AND BLANKING PERFORMANCE OF AlCrN PVD-COATED PUNCHES
Materials Science, Vol. 48, No. 4, January, 2013 (Ukrainian Original Vol. 48, No. 4, July August, 2012) WEAR AND BLANKING PERFORMANCE OF AlCrN PVD-COATED PUNCHES M. Çöl, 1 D. Kir, 2 and E. Erişir 1,3 Blanking
More informationFrictional Condition Evaluation in Hot Magnesium Forming Using T- Shape and Ring Compression Tests
College of Engineering Society of Manufacturing University of Tehran Engineering of Iran 3 rd International Conference on Manufacturing Engineering ICME211, Tehran, Iran 27-29 December 211 Frictional Condition
More informationThe Influences of the Friction Stir Welding on the Microstructure and Hardness of Aluminum 6063 and 7075
2011 International Conference on Advanced Materials Engineering IPCSIT vol.15 (2011) (2011) IACSIT Press, Singapore The Influences of the Friction Stir Welding on the Microstructure and Hardness of Aluminum
More informationOverview. Tool Steel Failures. Define Tool Steel Properties. Determine Modes of Failures. Identify Probable Failure Causes. Recommend Solutions.
Overview Tool Steel Failures Define Tool Steel Properties. Determine Modes of Failures. Identify Probable Failure Causes. Recommend Solutions. Important Properties of Tool Steel Harden Ability Ability
More informationModelling and Experimental Research in Hot Precision Forging of Duplicate Gear Blank Zhi Li1, a, Baoyu Wang1, b
4th International Conference on Mechatronics, Materials, Chemistry and Computer Engineering (ICMMCCE 2015) Modelling and Experimental Research in Hot Precision Forging of Duplicate Gear Blank Zhi Li1,
More informationArch. Metall. Mater. 62 (2017), 2B,
Arch. Metall. Mater. 62 (2017), 2B, 1319-1323 DOI: 10.1515/amm-2017-0201 C.K. LEE*, Y.C. KIM** # A STUDY ON CHANGES IN THICKNESS OF STS304 MATERIAL IN THE PROGRESSIVE DRAWING PROCESS In the drawing process,
More informationResearch on the Near-net Forging Processes for the Shell Body Made by High-strength Steel Taibin Wu1, a, b
International Conference on Mechanics, Materials and Structural Engineering (ICMMSE 2016) Research on the Near-net Forging Processes for the Shell Body Made by High-strength Steel Taibin Wu1, a, b 1 Research
More informationAvailable online at ScienceDirect. Procedia Engineering 81 (2014 )
Available online at www.sciencedirect.com ScienceDirect Procedia Engineering 81 (2014 ) 2494 2498 11th International Conference on Technology of Plasticity, ICTP 2014, 19-24 October 2014, Nagoya Congress
More informationPrecision feeler gage, calibrated shim steel and Specialty Spring Steels
Precision feeler gage, calibrated shim steel and Specialty Spring Steels 2011 Your partner for precision steels We offer an extensive range of precision feeler gages and shim steel which covers most product
More informationEffect of Isothermal Annealing Temperatures and Roller Burnishing on the Microhardness and Surface Quality of H13 Alloy Steel
J. Appl. Res. Ind. Eng. Vol. 4, No. 3 (217) 25 214 Journal of Applied Research on Industrial Engineering www.journal-aprie.com Effect of Isothermal Annealing Temperatures and Roller Burnishing on the Microhardness
More informationTribology in Industry. PVD-Alumina Coatings on Cemented Carbide Cutting Tools: A Study About the Effect on Friction and Adhesion Mechanism
Vol. 34, N o 1 (2012) 24-28 Tribology in Industry www.tribology.fink.rs RESEARCH PVD-Alumina Coatings on Cemented Carbide Cutting Tools: A Study About the Effect on Friction and Adhesion Mechanism S.E.
More informationEffects of TiCN Composite Die with Low Thermal Conductivity on Hot Forging Performances
Journal of Mechanics Engineering and Automation 6 (216) 59-65 doi: 1.17265/2159-5275/216.2.1 D DAVID PUBLISHING Effects of TiCN Composite Die with Low Thermal Conductivity on Hot Forging Performances Ryo
More informationMicrostructural evolution of SKD11 tool steel during multi-stage thixoforming and subsequent heat treatments
Microstructural evolution of SKD11 tool steel during multi-stage thixoforming and subsequent heat treatments Yi Meng 1, a *, Hui-Min Zhou 1, Jia-Lin Gan 1 and Sumio Sugiyama 2 1 College of Materials Science
More informationVTU NOTES QUESTION PAPERS NEWS RESULTS FORUMS
Sheet Metal Forming Introduction Sheet metal is simply metal formed into thin and flat pieces. It is one of the fundamental forms used in metalworking, and can be cut and bent into a variety of different
More informationPress Forging of Magnesium Alloy AZ31 Sheets
Materials Science Forum Online: 2007-03-15 ISSN: 1662-9752, Vols. 539-543, pp 1753-1758 doi:10.4028/www.scientific.net/msf.539-543.1753 2007 Trans Tech Publications, Switzerland Press Forging of Magnesium
More informationApplication of Mechanical Trimming to Hot Stamped 22MnB5 Parts for Energy Saving
INTERNATIONAL JOURNAL OF PRECISION ENGINEERING AND MANUFACTURING Vol. 15, No. 6, pp. 1087-1093 JUNE 2014 / 1087 DOI: 10.1007/s12541-014-0441-7 Application of Mechanical Trimming to Hot Stamped 22MnB5 Parts
More informationFORMING OF FULLERENE-DISPERSED ALUMINUM COMPOSITE BY THE COMPRESSION SHEARING METHOD
FORMING OF FULLERENE-DISPERSED ALUMINUM COMPOSITE BY THE COMPRESSION SHEARING METHOD Noboru NAKAYAMA Akita Prefectural University, 84-4 Tsuchiya-Ebinokuti, Yurihonjyo, Akita/ 15-55, JAPAN nakayama@akita-pu.ac.jp
More informationEffect of TiN powder mixed in Electrical Discharge Machining
IOP Conference Series: Materials Science and Engineering PAPER OPEN ACCESS Effect of TiN powder mixed in Electrical Discharge Machining To cite this article: A Muttamara and J Mesee 2016 IOP Conf. Ser.:
More informationMACHINING PERFORMANCE AND WEAR MECHANISM OF TiAlN-COATED INSERT
International Journal of Mechanical and Materials Engineering (IJMME), Vol.6 (2011), No.3, 414-418 MACHINING PERFORMANCE AND WEAR MECHANISM OF -COATED INSERT R.J. Talib, H.M. Ariff and M.F. Fazira AMREC,
More informationProperties of Cold Work Tool Steel Shot Peened by 1200 HV-Class Fe-Cr-B Gas Atomized Powder as Shot Peening Media
Materials Transactions, Vol. 51, No. 4 (20) pp. 735 to 739 #20 The Japan Institute of Metals Properties of Cold Work Tool Steel Shot Peened by 1200 HV-Class Fe-Cr-B Gas Atomized Powder as Shot Peening
More informationSLDi. June 2016 Hitachi Metals America
SLDi June 2016 Hitachi Metals America 1 Elongation (%) 1.1 Sheet Metals Trends 70 ~1995 60 1995~2000 50 2000~2015 40 30 20 10 IF 2015~ 0 200 400 600 800 1000 1200 1400 1600 Tensile Strength MPa Cast Iron
More informationBonding strength of Al/Mg/Al alloy tri-metallic laminates fabricated
Bull. Mater. Sci., Vol. 34, No. 4, July 2011, pp. 805 810. Indian Academy of Sciences. Bonding strength of Al/Mg/Al alloy tri-metallic laminates fabricated by hot rolling X P ZHANG, *, M J TAN, T H YANG,
More informationA CRITICAL EVALUATION OF THE DOUBLE CUP EXTRUSION TEST FOR SELECTION OF COLD FORGING LUBRICANTS
A CRITICAL EVALUATION OF THE DOUBLE CUP EXTRUSION TEST FOR SELECTION OF COLD FORGING LUBRICANTS Timothy Schrader, Manas Shirgaokar, Taylan Altan ERC for Net Shape Manufacturing, the Ohio State University,
More informationFINITE ELEMENT ANALYSIS OF FRICTION PARAMETERS ON 6060 ALUMINIUM ALLOY IMPRESSION DIE COLD FORGING PROCESS
STUDIA UBB PHYSICA, Vol. 61 (LXI), 1, 2016, pp. 35-46 (RECOMMENDED CITATION) Dedicated to Professor Dr. Cozar Onuc on His 70 th Anniversary FINITE ELEMENT ANALYSIS OF FRICTION PARAMETERS ON 6060 ALUMINIUM
More informationDie Design Software and Simulation Technology Experience
Die Design Software and Simulation Technology Experience The Influence of Material Properties on Die Design Peter Ulintz Technical Director Precision Metalforming Association The Influence of Sheet Metal
More informationChapter 14: Metal-Forging Processes and Equipments
Manufacturing Engineering Technology in SI Units, 6 th Edition Chapter 14: Metal-Forging Processes and Equipments Chapter Outline Introduction Open-die Forging Impression-die and Closed-die Forging Various
More informationHANDBOOK OF DIE DESIGN
HANDBOOK OF DIE DESIGN Ivana Suchy Consultant, Design Engineer Fair Lawn, New Jersey Second Edition McGRAW-HILL New York Chicago San Francisco Lisbon London Madrid Mexico City Milan New Delhi San Juan
More informationUpset forging of a circular disc in open die forging. Analysis involves cylindrical coordinates
12 Upset forging of a circular disc in open die forging Analysis involves cylindrical coordinates The stresses acting on an elemental volume in a disc are: σ r = radial stress responsible for increase
More informationTOOL ROOM FOR SHEET METAL DIES
Profile No.: 28 NIC Code: 24209 TOOL ROOM FOR SHEET METAL DIES 1. INTRODUCTION: Sheet metal forming processes are complex and have interaction several parameters of material like geometry, surface topology,
More informationEffects of particle shape and temperature on compaction of copper powder at micro scale
Effects of particle shape and on compaction of copper powder at micro scale hao-heng hang * and Ming-Ru Wu Department of Mold and Die Engineering, National Kaohsiung University of pplied Sciences, Kaohsiung,
More informationEffect of Sheet Thickness and Type of Alloys on the Springback Phenomenon for Cylindrical Die
AMERICAN JOURNAL OF SCIENTIFIC AND INDUSTRIAL RESEARCH 01, Science Huβ, http://www.scihub.org/ajsir ISSN: 153-69X, doi:10.551/ajsir.01.3.6.80.86 Effect of Sheet Thickness and Type of Alloys on the Springback
More informationCoating and Reconditioning Services
The Tool Company TWIST DRILLS REAMERS DIAMOND TOOLS TAPS END MILLS MODULAR TOOL SYSTEMS RECONDITIONING & COATING Coating and Reconditioning Services Guhring s Reconditioning Division turns worn cutting
More informationMANUFACTURING SCIENCE-I Time: 1 hour (EME-402) Max. marks:30
B.Tech. [SEM-IV (ME-41,42,43 & 44] QUIZ TEST-1 (Session: 2010-11) MANUFACTURING SCIENCE-I Time: 1 hour (EME-402) Max. marks:30 Note: All questions are compulsory. Q-1). Why there is no material wastage
More informationHOT WORKING TOOL STEELS
HOT WORKING TOOL STEELS 1 Characteristics of YSS Hot Work Tool Steels Warm forging 56~58HRC Precision hot forging 47~56HRC High temperatrure strength, Wear resistance High speed hot forging 47~54HRC F
More informationFailure analysis of diesel engine cylinder head bolts
Engineering Failure Analysis 13 (2006) 826 834 www.elsevier.com/locate/engfailanal Failure analysis of diesel engine cylinder head bolts Zhiwei Yu, Xiaolei Xu * Institute of Metal and Technology, Dalian
More informationEFFECT ON FINITE ELEMENT SIMULATION OF TUBE HYDROFORMING PROCESS
EFFECT ON FINITE ELEMENT SIMULATION OF TUBE HYDROFORMING PROCESS Vishnu P. Sharma 1, Kamlesh Kushwaha 2 1 M.E. Scholar, MPCT, Gwalior, 2 Assistant Professor, MPCT, Gwalior Abstract: - Hydroforming process
More informationA New Less-Loading Extrusion Technology of Mg Alloy Tube Workpiece
2nd International Forum on Electrical Engineering and Automation (IFEEA 215) A New Less-Loading Extrusion Technology of Mg Alloy Tube Workpiece Qiang Wang1,a, Zhimin Zhang2,b, Yong Xue1,Jianmin Yu2 1 Dept.
More informationAISI A2 Cold work tool steel
T OOL STEEL FACTS AISI A2 Cold work tool steel Great Tooling Starts Here! General AISI A2 is an air- or oil hardening chromiummolybdenum-vanadium alloyed tool steel characterized by: Good machinability
More informationThe die failure prediction and prevention of the orbital forging process
journal of materials processing technology 201 (2008) 9 13 journal homepage: www.elsevier.com/locate/jmatprotec The die failure prediction and prevention of the orbital forging process J.J. Sheu, C.H.
More informationAvailable online at ScienceDirect. Procedia Engineering 81 (2014 )
Available online at www.sciencedirect.com ScienceDirect Procedia Engineering 81 (2014 ) 712 717 11th International Conference on Technology of Plasticity, ICTP 2014, 19-24 October 2014, Nagoya Congress
More informationEffect of Fine Particle Bombarding on Thermal Fatigue Property of Tool Steel for Die Casting
Effect of Fine Particle Bombarding on Thermal Fatigue Property of Tool Steel for Die Casting Shinichi Takagi, Masao Kumagai, Toshitaka Satsuta and Akihiko Sano 1, Eiji Shimodaira 2 1 Kanagawa Industrial
More informationCompare with Rolling process which generally produces continuous plates, sheets, shapes
1 One of oldest and most important metal working processes 4000 BC First used to make jewelry, coins, implements by hammering metals with stone Now: Large rotors for turbines Gears Bolts and rivets Cutlery
More informationTribological Properties of Hybrid Process DLC Coating against Magnesium Alloy
Materials Transactions, Vol. 47, No. 4 (2006) pp. 1008 to 1012 Special Issue on Platform Science and Technology for Advanced Magnesium Alloys, III #2006 The Japan Institute of Metals Tribological Properties
More informationIn-situ heat treatment system for die steels using YAG laser with a machining center
Precision Engineering Journal of the International Societies for Precision Engineering and Nanotechnology 25 (2001) 212 217 In-situ heat treatment system for die steels using YAG laser with a machining
More informationMSE-226 Engineering Materials
MSE-226 Engineering Materials Lecture-7 ALLOY STEELS Tool Steels TYPES of FERROUS ALLOYS FERROUS ALLOYS Plain Carbon Steels Alloy Steels Cast Irons - Low carbon Steel - Medium carbon steel - High carbon
More informationPUNCH FORCE BEHAVIOR DURING MICRO V-BENDING PROCESS OF THE COPPER FOIL
International Journal of Technology (017) 7: 1314-130 ISSN 086-9614 IJTech 017 PUNCH FORCE BEHAVIOR DURING MICRO V-BENDING PROCESS OF THE COPPER FOIL Gandjar Kiswanto 1*, Aida Mahmudah 1,, Dedi Priadi
More informationInfluences of Reduction Ratio on Mechanical Properties and Transformation Temperature of NiTi Drawn Wires.
Influences of Reduction Ratio on Mechanical Properties and Transformation Temperature of NiTi Drawn Wires. Abstracts N.Noonai 1, A.Khantachawana 1,2 *, P.Kaewtathip 1 and J. Kajornchaiyakul 3 1 Department
More informationSANDVIK CHROMFLEX STRIP STEEL
SANDVIK CHROMFLEX STRIP STEEL DATASHEET Sandvik Chromflex is a family of hardened and tempered martensitic chromium steels characterized by: High strength combined with good shape High standard of surface
More informationLubrication in tube hydroforming (THF) Part II. Performance evaluation of lubricants using LDH test and pear-shaped tube expansion test
Journal of Materials Processing Technology 146 (2004) 116 123 Lubrication in tube hydroforming (THF) Part II. Performance evaluation of lubricants using LDH test and pear-shaped tube expansion test Gracious
More informationFINITE VOLUME ANALYSIS OF TWO-STAGE FORGING PROCESS FOR ALUMINIUM 7075 ALLOY
FINITE VOLUME ANALYSIS OF TWO-STAGE FORGING PROCESS FOR ALUMINIUM 7075 ALLOY M. Vidya Sagar a and A. Chennakesava Reddy b a Associate Professor, Department of Mechanical Engineering, JNTUH College of Engineering,
More informationA STUDY OF FINE BLANKING PROCESS BY FEM SIMULATION. G. Fang, P. Zeng
Key Engineering Materials Vols. 261-263 (2004) pp 603-608 Online available since 2004/Apr/15 at www.scientific.net (2004) Trans Tech Publications, Switzerland doi:10.4028/www.scientific.net/kem.261-263.603
More informationResearch on Improvement of Blank Precision and Life Span Extension of Nail Clipper Die with Uneven Shear Area
Research on Improvement of Blank Precision and Life Span Extension of Nail Clipper Die with Uneven Shear Area Sei-Hwan Kim 1 and Kye-Kwang Choi * 1 1 Dept. of Metalmold Design Engineering, College of Engineering,
More informationThe Effect of Corner Radii and Part Orientation on Stress Distribution of Cold Forging Die
merican Journal of pplied Sciences 5 (4): 296-300, 2008 ISSN 1546-9239 2008 Science Publications The Effect of Corner Radii and Part Orientation on Stress Distribution of Cold Forging Die hmad aharuddin
More informationKinetics of low temperature plasma carburizing of austenitic stainless steels
Journal of Materials Processing Technology 168 (2005) 189 194 Kinetics of low temperature plasma carburizing of austenitic stainless steels Y. Sun School of Materials Engineering, Nanyang Technological
More informationCHAPTER 3 EXPERIMENTAL CONDITIONS AND PROCEDURE
50 CHAPTER 3 EXPERIMENTAL CONDITIONS AND PROCEDURE This study was undertaken to perform milling operations on AISI D2, AISI D3, AISI H13 and AISI P20 steels, using different carbide cutting tool inserts
More informationSelection of Tool & Die Steels
Selection of Tool & Die Steels Introduction The success of a metal forming tool depends on optimizing all the factors affecting its performance. Usually, operating conditions (applied loads, abrasive environments,
More informationNominal Analysis (AISI 01) Carbon-.90 Tungsten / / / /32 7/64 1/8
OIL HARDENING PRECISION Ground FLAT STOCK (REGULAR SIZE AND OVERSIZED) STARRETT SERIES 783: 18 Lengths STARRETT SERIES 784: 36 Lengths For Tolerances see page 625. Nominal Analysis (AISI 01) Carbon-.90
More informationFinite Element Investigation of Friction Condition in a Backward Extrusion of Aluminum Alloy
Yong-Taek Im Professor, Fellow ASME E-mail: ytim@mail.kaist.ac.kr Seong-Hoon Kang Jae-Seung Cheon Computer Aided Materials Processing Laboratory, Department of Mechanical Engineering, ME3227, Korea Advanced
More informationEdition 3, The latest revised edition of this brochure is the English version, which is always published on our web site
This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty of specific properties
More informationDesign optimization of Blanking and Bending Press tool to produce Anchor Bracket component using Finite Element Method
Design optimization of Blanking and Bending Press tool to produce Anchor Bracket component using Finite Element Method Anudeep S 1, N. Ramesha 2 1. Student M. Tech, Government Tool Room and Training Centre,
More informationAISI D2 Cold work tool steel
T OOL STEEL FACTS AISI D2 Cold work tool steel Great Tooling Starts Here! This information is based on our present state of knowledge and is intended to provide general notes on our products and their
More informationDie Steel Improvements for AHSS Applications
Die Steel Improvements for AHSS Applications Thomas Bell HITACHI METALS LTD Arlington Hts, IL GDIS2018 AGENDA 2 HITACHI Intro Steel Production Methods for Die & Tooling Steels Typical Failure modes of
More informationMULTI-STAGE COLD FORGING
MULTI-STAGE COLD FORGING June 2018 For more information about our products and services, please contact your nearest Unisteel representative. Alternatively, visit our website now at www.unisteeltech.com
More informationInvestigation on the Cutting Process of Plasma Sprayed Iron Base Alloys
Key Engineering Materials Online: 2010-09-06 ISSN: 1662-9795, Vols. 447-448, pp 821-825 doi:10.4028/www.scientific.net/kem.447-448.821 2010 Trans Tech Publications, Switzerland Investigation on the Cutting
More informationUddeholm Vanadis 8 SuperClean
Uddeholm Vanadis 8 SuperClean Uddeholm Vanadis 8 Superclean The next generation of Powder Metallurgical Tool Steel ABRASIVE WEAR RESISTANCE ABRASIVE WEAR RESISTANCE 15% MC C+V= Vanadium carbide Hardness:
More informationEffect of die coating on Forming of Micro-parts by Forward-Backward Extrusion of 6063 Aluminum Alloy
IWMF214, 9 th INTERNATIONAL WORKSHOP ON MICROFACTORIES OCTOBER -8, 214, HONOLULU, U.S.A. / 1 Effect of die coating on Forming of Micro-parts by Forward-Backward Extrusion of 663 Aluminum Alloy Norio Takatsuji
More informationA New Rolling Pressure Model for an Actual Reversing Cold Rolling Strip Mill
Int J Advanced Design and Manufacturing Technology, Vol. 8/ No. 2/ June - 2015 73 A New Rolling Pressure Model for an Actual Reversing Cold Rolling Strip Mill M. Heydari Vini Department of Mechanical Engineering,
More informationPlastic deformation analysis of wear on insert component and die service life in hot forging process
Indian Journal of Engineering & Materials Sciences Vol. 22, December 2015, pp. 686-692 Plastic deformation analysis of wear on insert component and die service life in hot forging process R Rajiev a *
More informationStudy and analysis of PCD 1500 and 1600 Grade inserts on turning Al 6061alloy with 15% reinforcement of SiC particles on MMC
2012 International Conference on Industrial and Intelligent Information (ICIII 2012) IPCSIT vol.31 (2012) (2012) IACSIT Press, Singapore Study and analysis of PCD 1500 and 1600 Grade inserts on turning
More informationAvailable online at ScienceDirect. Procedia Materials Science 6 (2014 )
Available online at www.sciencedirect.com ScienceDirect Procedia Materials Science 6 (2014 ) 674 681 3rd International Conference on Materials Processing and Characterisation (ICMPC 2014) Deformation Behavior
More informationStamping Basics. Die Components Class of Tools Cost Drivers
Stamping Basics Die Components Class of Tools Cost Drivers Basic Types Of Tools Compound Progressive Draw Secondary Tools Compound Die Lower Volume Flatter Parts No Forms Burrs All One Direction Progressive
More informationStudies on the Punching Characteristics of Rigid Copper Clad Laminates
Journal of National Kaohsiung University of Applied Sciences, Vol. 33 (2004), pp. 31-40 Studies on the Punching Characteristics of Rigid Copper Clad Laminates Quang-Cherng Hsu * Abstract In this paper,
More informationHastelloy G-30 (UNS N06030) Chemical Composition
Hastelloy G-30 (UNS N06030) Hastelloy G-30 is commonly used for providing excellent resistance to chemical conditions. It offers resistance to nitric acid, phosphoric acid, hydrochloric acid and hydrofluoric
More informationInvestigation on Microstructure and Wear Resistance of the Plain Carbon Steel Hardfaced by the Fe-Cr-C Electrodes Containing Mo, W, V Elements
Investigation on Microstructure and Wear Resistance of the Plain Carbon Steel Hardfaced by the Fe-Cr-C Electrodes Containing Mo, W, V Elements M.R. Khanzadeh GharahShiran 1,*, H. Bakhtiari 2, A. Dadvar
More informationInvestigation on Effect of Cutting Fluid Pressure Toward Machinability Using Stainless Steel 304 With Coated Cemented
AENSI Journals Australian Journal of Basic and Applied Sciences ISSN:1991-8178 Journal home page: www.ajbasweb.com Investigation on Effect of Cutting Fluid Pressure Toward Machinability Using Stainless
More informationDetermination of Optimal Preform Part for Hot Forging Process of the Manufacture Axle Shaft by Finite Element Method
AIJSTPME (2013) 6(1): 35-42 Determination of Optimal Preform Part for Hot Forging Process of the Manufacture Axle Shaft by Finite Element Method Sukjantha V. Department of Production Engineering, the Sirindhorn
More informationREGIN 3. Cold work tool steel
Cold work tool steel This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. It should not therefore be construed as a warranty
More informationA. Wong. P.K.Thay. W. Furtner. H. Makovec, H. Eder, F. Russ
MEET THE JOB SPECIFICATION FROM THE CUSTOMER the evaluation of a high wear resisting tool steel for a progressive die for the production of components of safety belts A. Wong Ngai Cheong Metal Industries
More informationINTERNATIONAL JOURNAL OF RESEARCH IN AERONAUTICAL AND MECHANICAL ENGINEERING
ISSN (ONLINE): 2321-3051 INTERNATIONAL JOURNAL OF RESEARCH IN AERONAUTICAL AND MECHANICAL ENGINEERING Finite element analysis of deflection of rolls and its correction by providing camber on rolls Vijay
More informationManufacturing Process - I
Manufacturing Process - I UNIT II Metal Forming Processes Prepared By Prof. Shinde Vishal Vasant Assistant Professor Dept. of Mechanical Engg. NDMVP S Karmaveer Baburao Thakare College of Engg. Nashik
More informationTool Wear Investigation in CNC Turning Operation
, July 4-6, 2018, London, U.K. Tool Wear Investigation in CNC Turning Operation Yousuf Al Kindi, Murali R V, Salim R K Abstract The aim of this attempt is to experimentally investigate the cutting tool
More informationThe Relationship between Constant Friction Factor and Coefficient of Friction in Metal Forming Using Finite Element Analysis
IJMF, Iranian Journal of Materials Forming, Vol. 1, No. 2, pp 14-22 Printed in The Islamic Republic of Iran, 2014 Shiraz University The Relationship between Constant Friction Factor and Coefficient of
More informationInfluence of Parameters of Gas Metal Arc Welding on Macrostructures and Mechanical Properties of Austenitic Stainless Steels
6th WSEAS International Conference on SYSTEM SCIENCE and SIMULATION in ENGINEERING, Venice, Italy, November 21-23, 2007 144 Influence of Parameters of Gas Metal Arc Welding on Macrostructures and Mechanical
More informationHigh speed end milling of AISI 304 stainless steel using new geometrically developed carbide inserts
High speed end milling of AISI 34 stainless steel using new geometrically developed carbide inserts K.A. Abou-El-Hossein, Z. Yahya Department of Mechanical Engineering, Universiti Tenaga Nasional, 49,
More informationFabrication of Al/Cu Clad Sheet by Shear Extrusion
Vol:7, No:4, 13 Fabrication of / Clad Sheet by Shear Extrusion Joon Ho Kim, Duck Su Kim, and Tae Kwon Ha Digital Open Science Index, Mechanical and Mechatronics Engineering Vol:7, No:4, 13 waset.org/publication/14261
More informationGround Precision Components
E2 Ground Precision Components Ground Precision Components FIBRO Precision Components cover a very wide range of materials, shapes and sizes and thus permit virtually unrestricted selection even to highly
More informationCHAPTER 2: LITERATURE SURVEY
7 CHAPTER 2: LITERATURE SURVEY 2.1. Introduction The powder metallurgy processing is one of the oldest and economic routes for producing critical and complex shaped products [1-3]. P/M is one of the most
More informationCHAPTER 3 EXPERIMENTAL PROCEDURE
60 CHAPTER 3 EXPERIMENTAL PROCEDURE The objective of this study is to evaluate the performance of cermet tools which is subjected to either plain, coated, cryogenically treated. In order to evaluate these
More informationEffect of surface treatments on wear resistance of spring steel wire as a work-piece material of a fishing net-weaving machine component
Indian Journal of Engineering & Materials Sciences Vol. 23, February 2016, pp. 79-87 Effect of surface treatments on wear resistance of spring steel wire as a work-piece material of a fishing net-weaving
More informationTaylan Altan, PhD, Professor Emeritus Center for Precision Forming the Ohio State University.
ADVANCED METHODS for FORMING AHSS and UHS Al ALLOYS Taylan Altan, PhD, Professor Emeritus Center for Precision Forming the Ohio State University www.cpforming.org www.ercnsm.org January 2015 Center for
More informationThinning behavior of laminated sheets metal in warm deep-drawing process under various grain sizes
Thinning behavior of laminated sheets metal in warm deep-drawing process under various grain sizes Mehran Kadkhodayan a and Ehsan Afshin Department of Mechanical Engineering, The Ferdowsi University of
More informationNucleus geometry and mechanical properties of resistance spot welded coated uncoated DP automotive steels
Bull. Mater. Sci., Vol. 36, No. 6, November 2013, pp. 1049 1055. c Indian Academy of Sciences. Nucleus geometry and mechanical properties of resistance spot welded coated uncoated DP automotive steels
More informationCoatings. Tel PVD Coating Service. Correctly coated - for long-term use
Coatings PVD Coating Service Your coating plan for greater economy DME standard coatings LAM-A = chromium nitride (CrN) LAM-B = titanium nitride (TiN) LAM-C = titanium carbon nitride (TiCN) LAM-D = titanium
More informationSelecting the Right Tool Steel for Your Metalforming Application.
Selecting the Right Tool Steel for Your Metalforming Application. Patricia Miller, Senior Technical Manager What parameters drive your tooling material choice? Application Work materials Failure mechanism
More informationEditor s Note: This is Part I of a two-part series that discusses factors affecting the
PROOFED R&D Update Nov/Dec 17 STAMPING Journal Blanking and edge fracture in flanging of AHSS, Part I Test methods for evaluation By David Diaz and Dr. Taylan Altan Editor s Note: This is Part I of a two-part
More informationINTRODUCTION. Think HSS
INTRODUCTION Think HSS SUMMARY METALLURGY 2 Excellent strength 3 A super sharp edge 4 Safe and reliable tools Alloy elements 6 The influence of alloy elements 7 Standard compositions of HSS 8 The HSS-PM
More informationSAUTER HMM Version /2018 GB
Sauter GmbH Ziegelei 1 D-72336 Balingen E-Mail: info@sauter.eu Tel.: +49-[0]7433-9933-199 Fax: +49-[0]7433-9933-149 Internet: www.sauter.eu Instruction Manual Mobile Leeb Hardness Tester SAUTER HMM Version
More informationVDM Alloy 80 A Nicrofer 7520 Ti
VDM Alloy 80 A Nicrofer 7520 Ti Material Data Sheet No. 4048 February 2017 February 2017 VDM Alloy 80 A 2 VDM Alloy 80 A Nicrofer 7520 Ti VDM Alloy 80 A is a nickel-chromium alloy that can be age-hardened.
More informationBall Corner Radius YE-EI10 INSERTS & STEEL / CARBIDE HOLDERS INSERTS & STEEL / CARBIDE HOLDERS
YE-EI10 Ball Corner Radius Ball Corner Radius INSERTS & STEEL / CARBIDE HOLDERS HEAD OFFICE 68, Cheongcheon-Dong, Bupyeong-Gu, Incheon 4-0, KOREA PHONE :+82--526-09, FAX:+82--526-4373 Http://www.yg1.kr
More informationStainless Steel & Stainless Steel Fasteners Chemical, Physical and Mechanical Properties
Stainless Steel & Stainless Steel Fasteners Chemical, Physical and Mechanical Properties Stainless steel describes a family of steels highly resistant to tarnishing and rusting that contain at least two
More information