Reproducible evaluation of material properties. Static Testing Material response to constant loading
|
|
- June Barnett
- 6 years ago
- Views:
Transcription
1 Material Testing
2 Material Testing Reproducible evaluation of material properties Static Testing Material response to constant loading Dynamic Testing Material response to varying loading conditions, including magnitude, cycling, and mode
3 Static Material Testing Evaluation of Material Strength Deformation Fracture Design requirement compliance Standardized Tests Tensile test Compression test Hardness test
4 Tensile Test Uniaxial A straight line axial force is applied to a test sample (typically in the y axis) Image courtesy of NSW Department of Education and Training Destructive Force is applied until sample fails Hounsfield Tensometer
5 Tensile Test Standard Test Sample (dog bone) Ensures meaningful and reproducible results Uniform cross section
6 Tensile Test Procedure Dog bone is created to test specifications Dog bone is secured in tester
7 Tensile Test Procedure A tension force (F) is applied to the dog bone until failure occurs Simultaneously the applied tension force (F) and dog bone elongation L are recorded F L A plot is created from the stored load elongation data
8 Tensile Test Data A B F L Test sample A and B are 230 red brass. Test sample A has a diameter of in. Test sample B has a diameter of in. If both samples are tested to failure, will the applied tension force and elongation be the same for both tests? NO Why?
9 Tensile Test Data Load-elongation results are dependent upon sample size Larger sample indicates larger load-elongation How can test data be manipulated to represent a material and not an individual test sample?
10 Tensile Test Data To eliminate test results based on sample size, calculate sample stress Stress is load per unit area Divide load (F) by the original test sample cross-sectional area (A 0 ) load stress = area F σ = A
11 Tensile Test Data Calculate the stress in the dog bone with a 430 lb applied force. F σ = A 2 area = r 2 area = ( in.) 2 area = in.
12 Tensile Test Data Manipulating Elongation Results To eliminate test results based on sample size, calculate sample strain Strain - the amount of stretch per unit length Elongation under load divided by the original Length (L 0 ) strain = amount of stretch original length
13 Tensile Test Data Calculate the strain in the dog bone with an elongation of in in. ε = 1.000in. =
14 Tensile Test Stress-Strain Curve
15 Tensile Test Stress-Strain Curve Initial response is linear Stress and strain are proportional to one another Elastic Range Proportional Limit (The stress at which proportionality ceases)
16 Tensile Test Stress-Strain Curve Modulus of Elasticity (E) The proportional constant (ratio of stress and strain) σ E = = ε stress strain A measure of stiffness The ability of a material to resist stretching when loaded An inherent property of a given material
17 Tensile Test Stress-Strain Curve If the load is removed, the test sample will return to its original length The response is elastic or recoverable Exaggerated stretch to illustrate principle
18 Tensile Test Stress-Strain Curve Elastic Limit Uppermost stress of elastic behavior Elastic and proportional limit are almost identical, with the elastic limit being slightly higher
19 2Tensile Test Stress-Strain Curve Resilience The amount of energy per unit volume that a material can absorb while in the elastic range Area under the stress-strain curve Why would this be important to designers? Hint: car bumper1bh
20 Tensile Test Stress-Strain Curve Yield Point When the elastic limit is exceeded A very small increase in stress produces a much greater strain Most materials do not have a welldefined yield point
21 Tensile Test Stress-Strain Curve Offset Yield Strength Defines the stress required to produce a tolerable amount of permanent strain Common value is 0.2%
22 Tensile Test Stress-Strain Curve Plastic Deformation Unrecoverable elongation beyond the elastic limit When the load is removed, only the elastic deformation will be recovered
23 Tensile Test Strength Properties Stress Strain Curve Plastic deformation represents failure Part dimensions will now be outside of allowable tolerances
24 Tensile Test Stress-Strain Curve Deformation Test sample elongation Cross-sectional area decreases Load bearing ability increases Why? The material is getting stronger How?
25 Tensile Test Stress-Strain Curve Weakest point is stretched and becomes stronger New weakest point is stretched and becomes stronger, and so on This keeps occurring until the decrease in area overcomes the increase in strength
26 Tensile Test Stress-Strain Curve Tensile Strength Load bearing ability peaks Force required to continue straining the test sample decreases Weakest location at the peak continues to decrease in area Necking
27 Tensile Test Stress-Strain Curve Failure If continued force is applied, necking will continue until fracture occurs Ductility Amount of plasticity before fracture The greater the ductility, the more a material can be deformed
28 Tensile Test Samples Compare the material properties of these three metal samples
29 Tensile Test Stress-Strain Curve Brittleness Material failure with little or no ductility Lack of ductility, not lack of strength
30 Tensile Test Stress-Strain Curve Toughness Work per unit volume required to fracture a material Total area under the stress-strain curve from test initiation to fracture (both strength and ductility)
31 Compression Test Stress and strain relationships are similar to tension tests elastic and plastic behavior Test samples must have large cross-sectional area to resist bending and buckling Material strengthens by stretching laterally and increasing its cross-sectional area
32 Hardness Testing Resistance to permanent deformation Resistance to scratching, wear, cutting or drilling, and elastic rebound Brinell Hardness Test A tungsten carbide ball is held with a 500lb force for 15 sec into the material The resulting crater is measured and compared
33 Hardness Testing Rockwell Test A small diamond-tipped cone is forced into the test sample by a predetermined load Depth of penetration is measured and compared
34 Image Resources NSW Department of Education and Training (2011). Retrieved from g/index.htm?signature=%287e02281c-318a-461b-a8ed- 3394db0c4fe6%29
Reproducible evaluation of material properties. Static Testing Material response to constant loading
Material Testing Material Testing Reproducible evaluation of material properties Static Testing Material response to constant loading Dynamic Testing Material response to varying loading conditions, including
More information11/2/2018 7:58 PM. Chapter 6. Mechanical Properties of Metals. Mohammad Suliman Abuhaiba, Ph.D., PE
1 Chapter 6 Mechanical Properties of Metals 2 Assignment 7, 13, 18, 23, 30, 40, 45, 50, 54 4 th Exam Tuesday 22/11/2018 3 WHY STUDY Mechanical Properties of Metals? How various mechanical properties are
More informationME -215 ENGINEERING MATERIALS AND PROCESES
ME -215 ENGINEERING MATERIALS AND PROCESES Instructor: Office: MEC325, Tel.: 973-642-7455 E-mail: samardzi@njit.edu PROPERTIES OF MATERIALS Chapter 3 Materials Properties STRUCTURE PERFORMANCE PROCESSING
More informationWelcome to ENR116 Engineering Materials. This lecture summary is part of module 2, Material Properties.
Welcome to ENR116 Engineering Materials. This lecture summary is part of module 2, Material Properties. 1 2 Mechanical properties. 3 The intended learning outcomes from this lecture summary are that you
More informationMECHANICAL PROPERTIES AND TESTS. Materials Science
MECHANICAL PROPERTIES AND TESTS Materials Science Stress Stress is a measure of the intensity of the internal forces acting within a deformable body. Mathematically, it is a measure of the average force
More informationChapter 7. Mechanical properties 7.1. Introduction 7.2. Stress-strain concepts and behaviour 7.3. Mechanical behaviour of metals 7.4.
Chapter 7. Mechanical properties 7.1. Introduction 7.2. Stress-strain concepts and behaviour 7.3. Mechanical behaviour of metals 7.4. Mechanical behaviour of ceramics 7.5. Mechanical behaviour of polymers
More informationBFF1113 Engineering Materials DR. NOOR MAZNI ISMAIL FACULTY OF MANUFACTURING ENGINEERING
BFF1113 Engineering Materials DR. NOOR MAZNI ISMAIL FACULTY OF MANUFACTURING ENGINEERING Course Guidelines: 1. Introduction to Engineering Materials 2. Bonding and Properties 3. Crystal Structures & Properties
More informationMECHANICAL PROPERTIES OF MATERIALS
MECHANICAL PROPERTIES OF MATERIALS Stress-Strain Relationships Hardness Effect of Temperature on Properties Fluid Properties Viscoelastic Behavior of Polymers Mechanical Properties in Design and Manufacturing
More informationEngineering Materials
Engineering Materials Mechanical Properties of Engineering Materials Mechanical testing of engineering materials may be carried out for a number of reasons: The tests may simulate the service conditions
More informationMATERIALS: Clarifications and More on Stress Strain Curves
A 3.0 m length of steel rod is going to be used in the construction of a bridge. The tension in the rod will be 10 kn and the rod must extend by no more than 1.0mm. Calculate the minimum cross-sectional
More informationMechanical Properties of Materials
INTRODUCTION Mechanical Properties of Materials Many materials, when in service, are subjected to forces or loads, it is necessary to know the characteristics of the material and to design the member from
More informationCE 221: MECHANICS OF SOLIDS I CHAPTER 3: MECHANICAL PROPERTIES OF MATERIALS
CE 221: MECHANICS OF SOLIDS I CHAPTER 3: MECHANICAL PROPERTIES OF MATERIALS By Dr. Krisada Chaiyasarn Department of Civil Engineering, Faculty of Engineering Thammasat university Outline Tension and compression
More informationProperties of Engineering Materials
Properties of Engineering Materials Syllabus Mechanical Properties, Tensile, Fatigue, Creep, Impact, Hardness, Chemical Properties, Physical properties, Corrosion and Cathodic Protection, Carbon Steel,
More informationChapter Outline Mechanical Properties of Metals How do metals respond to external loads?
Chapter Outline Mechanical Properties of Metals How do metals respond to external loads?! Stress and Strain " Tension " Compression " Shear " Torsion! Elastic deformation! Plastic Deformation " Yield Strength
More informationThe strength of a material depends on its ability to sustain a load without undue deformation or failure.
TENSION TEST The strength of a material depends on its ability to sustain a load without undue deformation or failure. This strength is inherent in the material itself and must be determined by experiment.
More informationMechanical Properties of Metals. Goals of this unit
Mechanical Properties of Metals Instructor: Joshua U. Otaigbe Iowa State University Goals of this unit Quick survey of important metal systems Detailed coverage of basic mechanical properties, especially
More information3. MECHANICAL PROPERTIES OF STRUCTURAL MATERIALS
3. MECHANICAL PROPERTIES OF STRUCTURAL MATERIALS Igor Kokcharov 3.1 TENSION TEST The tension test is the most widely used mechanical test. Principal mechanical properties are obtained from the test. There
More informationChapter 6: Mechanical Properties: Part One
Slide 1 Chapter 6: Mechanical Properties: Part One ` 6-1 Slide 2 Learning Objectives 1. Technological significance 2. Terminology for mechanical properties 3. The tensile test: Use of the stress strain
More informationMECHANICAL PROPERTIES
MECHANICAL PROPERTIES Mechanical Properties: In the course of operation or use, all the articles and structures are subjected to the action of external forces, which create stresses that inevitably cause
More informationME 212 EXPERIMENT SHEET #2 TENSILE TESTING OF MATERIALS
ME 212 EXPERIMENT SHEET #2 TENSILE TESTING OF MATERIALS 1. INTRODUCTION & THEORY The tension test is the most commonly used method to evaluate the mechanical properties of metals. Its main objective is
More informationChapter 4 MECHANICAL PROPERTIES OF MATERIAL. By: Ardiyansyah Syahrom
Chapter 4 MECHANICAL PROPERTIES OF MATERIAL By: Ardiyansyah Syahrom Chapter 2 STRAIN Department of Applied Mechanics and Design Faculty of Mechanical Engineering Universiti Teknologi Malaysia 1 Expanding
More informationFME201 Solid & Structural Mechanics I Dr.Hussein Jama Office 414
FME201 Solid & Structural Mechanics I Dr.Hussein Jama Hussein.jama@uobi.ac.ke Office 414 Lecture: Mon 11am -1pm (CELT) Tutorial Tue 12-1pm (E207) 10/1/2013 1 CHAPTER OBJECTIVES Show relationship of stress
More informationTrue Stress and True Strain
True Stress and True Strain For engineering stress ( ) and engineering strain ( ), the original (gauge) dimensions of specimen are employed. However, length and cross-sectional area change in plastic region.
More informationMECHANICAL PROPERTIES.
MECHANICAL PROPERTIES. Hardness, strength, ductility and elasticity are among the mechanical properties of a material that would probably first come to mind. In order to know how each of these characteristics
More informationThe Mechanical Properties of Polymers
The Mechanical Properties of Polymers Date: 14/07/2018 Abu Zafar Al Munsur Behavior Of Material Under Mechanical Loads = Mechanical Properties. Term to address here Stress and strain: These are size-independent
More informationQuiz 1 - Mechanical Properties and Testing Chapters 6 and 8 Callister
Quiz 1 - Mechanical Properties and Testing Chapters 6 and 8 Callister You need to be able to: Name the properties determined in a tensile test including UTS,.2% offset yield strength, Elastic Modulus,
More informationTensile/Tension Test Fundamentals
CIVE.3110 Engineering Materials Laboratory Fall 2016 Tensile/Tension Test Fundamentals Tzuyang Yu Associate Professor, Ph.D. Structural Engineering Research Group (SERG) Department of Civil and Environmental
More informationMECHANICAL PROPERTIES PROPLEM SHEET
MECHANICAL PROPERTIES PROPLEM SHEET 1. A tensile test uses a test specimen that has a gage length of 50 mm and an area = 200 mm 2. During the test the specimen yields under a load of 98,000 N. The corresponding
More informationMaterials Engineering 272-C Fall 2001, Lectures 9 & 10. Introduction to Mechanical Properties of Metals
Materials Engineering 272-C Fall 2001, Lectures 9 & 10 Introduction to Mechanical Properties of Metals From an applications standpoint, one of the most important topics within Materials Science & Engineering
More informationMechanical behavior of crystalline materials- Comprehensive Behaviour
Mechanical behavior of crystalline materials- Comprehensive Behaviour In the previous lecture we have considered the behavior of engineering materials under uniaxial tensile loading. In this lecture we
More informationNDT Deflection Measurement Devices: Benkelman Beam (BB) Sri Atmaja P. Rosyidi, Ph.D., P.E. Associate Professor
NDT Deflection Measurement Devices: Benkelman Beam (BB) Sri Atmaja P. Rosyidi, Ph.D., P.E. Associate Professor NDT Deflection Measurement Devices on Pavement Structure NDT measurement of pavement surface
More informationMechanical Properties
Stress-strain behavior of metals Elastic Deformation Plastic Deformation Ductility, Resilience and Toughness Hardness 108 Elastic Deformation bonds stretch δ return to initial Elastic means reversible!
More informationMechanical Characterisation of Materials
Department of Materials and Metallurgical Engineering Bangladesh University of Engineering and Technology, Dhaka MME298 Structure and Properties of Biomaterials Sessional 1.50 Credits 3.00 Hours/Week July
More informationEngineering Materials
Engineering Materials PREPARED BY Academic Services August 2011 Institute of Applied Technology, 2011 Module Objectives After the completion of this module, the student will be able to: Explain the terms
More informationEXPERIMENT NO.1 AIM: - OBJECT: - To determined tensile test on a metal. APPRETERS:- THEORY:-
EXPERIMENT NO.1 AIM: - OBJECT: - APPRETERS:- DIAGRAM:- THEORY:- To determined tensile test on a metal. To conduct a tensile test on a mild steel specimen and determine the following: (i) Limit of proportionality
More information3. Mechanical Properties of Materials
3. Mechanical Properties of Materials 3.1 Stress-Strain Relationships 3.2 Hardness 3.3 Effect of Temperature on Properties 3.4 Fluid Properties 3.5 Viscoelastic Properties Importance of Mechanical Properties
More informationMechanical behavior of crystalline materials - Stress Types and Tensile Behaviour
Mechanical behavior of crystalline materials - Stress Types and Tensile Behaviour 3.1 Introduction Engineering materials are often found to posses good mechanical properties so then they are suitable for
More informationAERO 214. Introduction to Aerospace Mechanics of Materials. Lecture 2
AERO 214 Introduction to Aerospace Mechanics of Materials Lecture 2 Materials for Aerospace Structures Aluminum Titanium Composites: Ceramic Fiber-Reinforced Polymer Matrix Composites High Temperature
More informationChapter 7: Mechanical Properties 1- Load 2- Deformation 3- Stress 4- Strain 5- Elastic behavior
-1-2 -3-4 ( ) -5 ( ) -6-7 -8-9 -10-11 -12 ( ) Chapter 7: Mechanical Properties 1- Load 2- Deformation 3- Stress 4- Strain 5- Elastic behavior 6- Plastic behavior 7- Uniaxial tensile load 8- Bi-axial tensile
More informationWhen an axial load is applied to a bar, normal stresses are produced on a cross section perpendicular to the axis of the bar.
11.1 AXIAL STRAIN When an axial load is applied to a bar, normal stresses are produced on a cross section perpendicular to the axis of the bar. In addition, the bar increases in length, as shown: 11.1
More informationCHAPTER 3 OUTLINE PROPERTIES OF MATERIALS PART 1
CHAPTER 3 PROPERTIES OF MATERIALS PART 1 30 July 2007 1 OUTLINE 3.1 Mechanical Properties 3.1.1 Definition 3.1.2 Factors Affecting Mechanical Properties 3.1.3 Kinds of Mechanical Properties 3.1.4 Stress
More informationMaterial Properties 3
Material Properties 3 Real Stress and Strain True M Corrected Stress M Engineering Strain Several Alloys Material n MPa psi Low-carbon steel 0.26 530 77,000 (annealed) Alloy steel 0.15 640 93,000 (Type
More informationMECHANICS OF MATERIALS. Mechanical Properties of Materials
MECHANICS OF MATERIALS Mechanical Properties of Materials By NUR FARHAYU ARIFFIN Faculty of Civil Engineering & Earth Resources Chapter Description Expected Outcomes Understand the concept of tension and
More informationLab Exercise #2: Tension Testing (Uniaxial Stress)
Lab Exercise #2: (Uniaxial Stress) Learning Outcomes: 1. Understand the basic concepts of stress and strain 2. Identify the engineering material properties 3. Connect stress and strain through Hooke s
More informationMECHANICAL PROPERTIES. (for metals)
MECHANICAL PROPERTIES (for metals) 1 Chapter Outline Terminology for Mechanical Properties The Tensile Test: Stress-Strain Diagram Properties Obtained from a Tensile Test True Stress and True Strain The
More informationChapter 6: Mechanical Properties
Chapter 6: Mechanical Properties ISSUES TO ADDRESS... Stress and strain: What are they and why are they used instead of load and deformation? Elastic behavior: When loads are small, how much deformation
More informationChapter 6: Mechanical Properties
Chapter 6: Mechanical Properties Elastic behavior: When loads are small, how much deformation occurs? What materials deform least? Stress and strain: What are they and why are they used instead of load
More informationModule 5: Mechanical Properties January 29, 2010
Module 5: Mechanical Properties January 29, 2010 Module Content: 1. Mechanical properties of material are usually measured by a tensile test, and are usually presented in a stress-strain plot. 2. The stress-strain
More informationProperties of Dental Materials
Properties of Dental Materials Importance of Studying Properties of Materials Materials used to replace teeth or parts of teeth must withstand oral environment and forces of mastication Materials must
More informationChapter 6: Mechanical Properties
Chapter 6: Mechanical Properties ISSUES TO ADDRESS... Stress and strain: What are they and why are they used instead of load and deformation? Elastic behavior: When loads are small, how much deformation
More informationENGINEERING MATERIAL 100
Department of Applied Chemistry Division of Science and Engineering SCHOOL OF ENGINEERING ENGINEERING MATERIAL 100 Experiments 4 and 6 Mechanical Testing and Applications of Non-Metals Name: Yasmin Ousam
More informationPlastic stress-strain behaviour of metals Energy of mechanical ldeformation Hardness testing Design/safety factors
Mechanical Properties of Materials 2 Prof. A.K.M.B. Rashid Department of MME BUET, Dhaka Plastic stress-strain behaviour of metals Energy of mechanical ldeformation Hardness testing Design/safety factors
More informationENGR 151: Materials of Engineering LECTURE #12-13: DISLOCATIONS AND STRENGTHENING MECHANISMS
ENGR 151: Materials of Engineering LECTURE #12-13: DISLOCATIONS AND STRENGTHENING MECHANISMS RECOVERY, RECRYSTALLIZATION, AND GRAIN GROWTH Plastically deforming metal at low temperatures affects physical
More informationبسم الله الرحمن الرحیم. Materials Science. Chapter 7 Mechanical Properties
بسم الله الرحمن الرحیم Materials Science Chapter 7 Mechanical Properties 1 Mechanical Properties Can be characterized using some quantities: 1. Strength, resistance of materials to (elastic+plastic) deformation;
More informationMECHANICAL TESTING OF METALLIC MATERIALS
MECHANICAL TESTING OF METALLIC MATERIALS Outline Hardness Testing Tensile Testing Impact Testing Fatigue Testing Creep Testing Wear Testing 22-Jan-11 11111 2 MATERIALS PROPERTIES Design Engineer - Materials
More informationCHAPTER 3 - MECHANICAL PROPERTIES. Mechanical properties are the characteristic responses of a material to applied stresses. Selection of mechanical
CHAPTER 3 - MECHANICAL PROPERTIES Mechanical properties are the characteristic responses of a material to applied stresses. Selection of mechanical tests for a particular application is based primarily
More informationChapter 8: Mechanical Properties of Metals. Elastic Deformation
Chapter 8: Mechanical Properties of Metals ISSUES TO ADDRESS... Stress and strain: What are they and why are they used instead of load and deformation? Elastic behavior: When loads are small, how much
More informationP A (1.1) load or stress. elongation or strain
load or stress MEEN 3145 TENSION TEST - BACKGROUND The tension test is the most important and commonly used test in characterizing properties of engineering materials. This test gives information essential
More informationConcepts of stress and strain
Chapter 6: Mechanical properties of metals Outline Introduction Concepts of stress and strain Elastic deformation Stress-strain behavior Elastic properties of materials Plastic deformation Yield and yield
More informationToday s Topics. Plastic stress-strain behaviour of metals Energy of mechanical ldeformation Hardness testing Design/safety factors
MME 291: Lecture 10 Mechanical Properties of Materials 2 Prof. A.K.M.B. Rashid Department of MME BUET, Dhaka Today s Topics Plastic stress- behaviour of metals Energy of mechanical ldeformation Hardness
More informationTHE MECHANICAL PROPERTIES OF STAINLESS STEEL
THE MECHANICAL PROPERTIES OF STAINLESS STEEL Stainless steel is primarily utilised on account of its corrosion resistance. However, the scope of excellent mechanical properties the within the family of
More informationProperties in Shear. Figure 7c. Figure 7b. Figure 7a
Properties in Shear Shear stress plays important role in failure of ductile materials as they resist to normal stress by undergoing large plastic deformations, but actually fail by rupturing under shear
More informationChapter 6: Mechanical Properties
ISSUES TO ADDRESS... Stress and strain Elastic behavior: When loads are small, how much reversible deformation occurs? What material resist reversible deformation better? Plastic behavior: At what point
More informationCITY AND GUILDS 9210 Unit 130 MECHANICS OF MACHINES AND STRENGTH OF MATERIALS OUTCOME 1 TUTORIAL 1 - BASIC STRESS AND STRAIN
CITY AND GUILDS 910 Unit 130 MECHANICS O MACHINES AND STRENGTH O MATERIALS OUTCOME 1 TUTORIAL 1 - BASIC STRESS AND STRAIN Outcome 1 Explain static equilibrium, Newton's laws, and calculation of reaction
More informationChapter 7. Mechanical Properties
Chapter 7 Mechanical Properties Chapter 7 Plastic Deformation, Ductility and Toughness Issues to address Stress and strain: What are they and why are they used instead of load and deformation? Elastic
More informationCE205 MATERIALS SCIENCE PART_6 MECHANICAL PROPERTIES
CE205 MATERIALS SCIENCE PART_6 MECHANICAL PROPERTIES Dr. Mert Yücel YARDIMCI Istanbul Okan University Deparment of Civil Engineering Chapter Outline Terminology for Mechanical Properties The Tensile Test:
More informationChapter 6: Mechanical Properties
Chapter 6: Mechanical Properties ISSUES TO ADDRESS... Stress and strain: What are they and why are they used instead of load and deformation? Elastic behavior: When loads are small, how much deformation
More informationMaterials Properties 2
Materials Properties 2 Elastic Deformation Most metals can only obey hook s law for s up to 0.005 Elastic Plastic y P Nearly all engineering is performed in the elastic region 0.002 Elastic Plastic y P
More informationWEEK FOUR. This week, we will Define yield (failure) in metals Learn types of stress- strain curves Define ductility.
WEEK FOUR Until now, we Defined stress and strain Established stress-strain relations for an elastic material Learned stress transformation Discussed yield (failure) criteria This week, we will Define
More informationChapter 2: Mechanical Behavior of Materials
Chapter : Mechanical Behavior of Materials Definition Mechanical behavior of a material relationship - its response (deformation) to an applied load or force Examples: strength, hardness, ductility, stiffness
More informationSMU 2113 ENGINEERING SCIENCE. PART 1 Introduction to Mechanics of Materials and Structures
SMU 2113 ENGINEERING SCIENCE PART 1 Introduction to Mechanics of Materials and Structures These slides are designed based on the content of these reference textbooks. OBJECTIVES To introduce basic principles
More informationWhen an axial load is applied to a bar, normal stresses are produced on a cross section perpendicular to the axis of the bar.
11.1 AXIAL STRAIN When an axial load is applied to a bar, normal stresses are produced on a cross section perpendicular to the axis of the bar. In addition, the bar increases in length, as shown: 11.1
More informationFACULTY OF ENGINEERING UNIVERSITY OF MAURITIUS. Mechanical properties of Materials UTOSP 1293 Basics of Metallurgy Prepared by s.
FACULTY OF ENGINEERING UNIVERSITY OF MAURITIUS Mechanical properties of Materials UTOSP 1293 Basics of Metallurgy Prepared by s. Venkannah MECHANICAL PROPERTIES Engineers are basically concerned with the
More informationChapter 6:Mechanical Properties
Chapter 6:Mechanical Properties Why mechanical properties? Need to design materials that can withstand applied load e.g. materials used in building bridges that can hold up automobiles, pedestrians materials
More informationEngineering Materials
Engineering Materials PREPARED BY IAT Curriculum Unit August 2010 Institute of Applied Technology, 2010 Module Objectives After the completion of this module, the student will be able to: Explain the difference
More informationREVISED PAGES IMPORTANT TERMS AND CONCEPTS REFERENCES QUESTIONS AND PROBLEMS. 166 Chapter 6 / Mechanical Properties of Metals
1496T_c06_131-173 11/16/05 17:06 Page 166 166 Chapter 6 / Mechanical Properties of Metals IMPORTANT TERMS AND CONCEPTS Anelasticity Design stress Ductility Elastic deformation Elastic recovery Engineering
More informationSTRENGTH OF MATERIALS laboratory manual
STRENGTH OF MATERIALS laboratory manual By Prof. Shaikh Ibrahim Ismail M.H. Saboo Siddik College of Engineering, MUMBAI TABLE OF CONTENT Sr. No. Title of Experiment page no. 1. Study of Universal Testing
More informationLaboratory 6. Metals Tested in Tension. Jeremy Wheeless. Group Members: entire laboratory section. Submittal date: 4/10/2014
Laboratory 6 Metals Tested in Tension Jeremy Wheeless Group Members: entire laboratory section Submittal date: 4/10/2014 Section Information: Thursday, 9:30a-1230p Laboratory TA: Wenyu Cai Results and
More informationAML 883 Properties and selection of engineering materials
AML 883 Properties and selection of engineering materials LECTURE 8. Plasticity M P Gururajan Email: guru.courses@gmail.com Room No. MS 207/A 3 Phone: 1340 Problem Sheet 3 Problems on strength limited
More informationMECHANICAL PROPERTIES OF MATERIALS. Manufacturing materials, IE251 Dr M. Eissa
MECHANICAL PROPERTIES OF MATERIALS, IE251 Dr M. Eissa MECHANICAL PROPERTIES OF MATERIALS 1. Bending Test (Slide 3) 2. Shear Test (Slide 8) 3. Hardness (Slide 14) 4. Effect of Temperature on Properties
More informationTensile/Tension Test Advanced Topics
CIVE.3110 Engineering Materials Laboratory Fall 2017 Tensile/Tension Test Advanced Topics Tzuyang Yu Associate Professor, Ph.D. Structural Engineering Research Group (SERG) Department of Civil and Environmental
More informationTRUE STRESS AND STRAIN
TRUE STRESS AND STRAIN TS M F Implies the material is getting weaker? Stress True stress Strain TRUE STRAIN True strain of system Assuming no volume change i.e. RELATION BETWEEN TRUE STRESS AND STRAIN
More informationTensile Testing of Plastics
German Jordanian University (GJU) Material Science Laboratory IE 2210 Summer Semester 2008 2009 i i Experiment 10 Tensile Testing of Plastics Mahmood Hisham Shubbak Title Mark Objective /10 Introduction
More informationHigh Temperature Materials. By Docent. N. Menad. Luleå University of Technology ( Sweden )
of Materials Course KGP003 Ch. 6 High Temperature Materials By Docent. N. Menad Dept. of Chemical Engineering and Geosciences Div. Of process metallurgy Luleå University of Technology ( Sweden ) Mohs scale
More informationEngineering Materials
Engineering Materials PREPARED BY Academic Services August 2011 Applied Technology High Schools, 2011 Module Objectives After the completion of this module, the student will be able to: Explain the difference
More informationIssues to address. Why Mechanical Test?? Mechanical Properties. Why mechanical properties?
Mechanical Properties Why mechanical properties? Folsom Dam Gate Failure, July 1995 Need to design materials that can withstand applied load e.g. materials used in building bridges that can hold up automobiles,
More informationME 207 Material Science I
ME 207 Material Science I Chapter 4 Properties in Bending and Shear Dr. İbrahim H. Yılmaz http://web.adanabtu.edu.tr/iyilmaz Automotive Engineering Adana Science and Technology University Introduction
More informationDeformation, plastic instability
Deformation, plastic instability and yield-limited design Engineering Materials 2189101 Department of Metallurgical Engineering Chulalongkorn University http://pioneer.netserv.chula.ac.th/~pchedtha/ Material
More informationWorkshop Practice TA 102
Workshop Practice TA 102 Lec 2 & 3 :Engineering Materials By Prof.A.Chandrashekhar Engineering Materials Materials play an important role in the construction and manufacturing of equipment/tools. Right
More informationProduct Design Theory
Product Design Theory & Basic Engineering Properties CRANE MATERIALS INTERNATIONAL A Whitepaper by: Michael Yeats Physical properties are defined by ASTM testing standards, The Aluminum Association Design
More informationExperiment 4 - Testing of Materials in Tension
Experiment 4 - Testing of Materials in Tension Object: The object of this experiment is to measure the tensile properties of two polymeric materials, steel and aluminum at a constant strain rate on the
More informationPLASTIC DEFORMATION AND THE ONSET OF TENSILE INSTABILITY
PLASTIC DEFORMATION AND THE ONSET OF TENSILE INSTABILITY Introduction In this experiment the plastic deformation behavior and the onset of plastic instability of some common structural alloys is investigated.
More informationQWC spelling of technical terms must be correct and the answer must be organised in a logical sequence
1 Explain the difference between elastic deformation and plastic deformation QWC spelling of technical terms must be correct and the answer must be organised in a logical sequence Elastic returns to original
More informationCH 6: Fatigue Failure Resulting from Variable Loading
CH 6: Fatigue Failure Resulting from Variable Loading Some machine elements are subjected to statics loads and for such elements, statics failure theories are used to predict failure (yielding or fracture).
More informationChapter 10 Polymer Characteristics. Dr. Feras Fraige
Chapter 10 Polymer Characteristics Dr. Feras Fraige Stress Strain Behavior (I) The description of stress-strain behavior is similar to that of metals Polymers can be brittle (A), plastic (B), or highly
More informationMetals are generally ductile because the structure consists of close-packed layers of
Chapter 10 Why are metals ductile and ceramics brittle? Metals are generally ductile because the structure consists of close-packed layers of atoms that allow for low energy dislocation movement. Slip
More informationME254: Materials Engineering Second Midterm Exam 1 st semester December 10, 2015 Time: 2 hrs
ME254: Materials Engineering Second Midterm Exam 1 st semester 1436-1437 December 10, 2015 Time: 2 hrs Problem 1: (24 points) A o = π/4*d o 2 = π/4*17 2 = 227 mm 2 L o = 32 mm a) Determine the following
More informationTensile Testing. Objectives
Laboratory 3 Tensile Testing Objectives Students are required to understand the principle of a uniaxial tensile testing and gain their practices on operating the tensile testing machine to achieve the
More informationDharmapuri LAB MANUAL. Regulation : 2013 Branch. : B.E. Civil Engineering CE6411 STRENGTH OF MATERIALS LABORATORY
Dharmapuri 636 703 LAB MANUAL Regulation : 2013 Branch Year & Semester : B.E. Civil Engineering : II Year / IV Semester CE6411 STRENGTH OF MATERIALS LABORATORY OBJECTIVE: ANNA UNIVERSITY CE-6411 STRENGTH
More informationMACHINES DESIGN SSC-JE STAFF SELECTION COMMISSION MECHANICAL ENGINEERING STUDY MATERIAL MACHINES DESIGN
1 SSC-JE STAFF SELECTION COMMISSION MECHANICAL ENGINEERING STUDY MATERIAL C O N T E N T 2 1. MACHINE DESIGN 03-21 2. FLEXIBLE MECHANICAL ELEMENTS. 22-34 3. JOURNAL BEARINGS... 35-65 4. CLUTCH AND BRAKES.
More information