Deposition of Silica Aluminum Using an Alkali Solution of Fly Ash
|
|
- Lily Brooks
- 6 years ago
- Views:
Transcription
1 2016 International Conference on Materials, Information, Mechanical, Electronic and Computer Engineering (MIMECE 2016) ISBN: Deposition of Silica Aluminum Using an Alkali Solution of Fly Ash Ben-jun Xu, Gang Feng, Wen-bin He and Cai-juan Huang ABSTRACT This study investigated the deposition process of fly ash alkali solution containing silica. The effects of deposition ph, temperature, speed, and time on silicon and aluminum deposition rates were studied. Oil value was analyzed because of the presence of aluminum silica in white carbon black. Results show that the optimum deposition conditions are as follows: ph of 7, deposition temperature of 60 C, deposition rotation rate of 100 r/min, and deposition time of 4 h. EXPERIMENTAL SECTION Raw Materials and Equipment Fly ash from a thermal power plant was used. This ash has a silicon content of about 28% and the mass fraction of aluminum is about 44%, which is mainly in the form of calcium aluminum silicate and mullite. The contents of silicon and aluminum in acid solution are and g/ml, respectively. Box-type resistance furnace (SPJX-8-13 type), glass reaction vessel, vacuum pump (2XZ-2), constant temperature drying box (DNG-9090B), and T890 automatic titration were used in the experiments. Test Principle and Method Fly ash was mixed with soda ash, and high temperature calcination was performed. Acid dissolution of the sample was also conducted using acid leaching solution. Acid liquid titration was carried out by dissolving the sodium hydroxide solution in the automatic titration instrument. After sediment filtration, the obtained Ben-jun Xu. Gang Feng. Wen-bin He. Cai-juan Huang. Guizhou University, China 247
2 silica containing residue was dried. The silicon and aluminum contents in acid leaching solution and filter residue were analyzed. The silicon and aluminum contents and silica deposition rates were calculated. Determination of SiO2 by silicon molybdenum blue spectrophotometry Al2O3 was determined by EDTA titration. For the determination of aluminum containing amorphous silica value, the determination method for oil GB/T national standard for carbon black pigment was used. EXPERIMENTAL RESULTS AND DISCUSSION Influence of ph Value on the Deposition Test condition: The deposition temperature is 50 C, the deposition rotation rate is 200 r/min, and the deposition time is 4 h. Figure 1 shows the effect of the deposition ph on the silica and alumina contents and silica deposition rate of silicon. Figure 2 presents the influence of ph on the oil absorption of white carbon black. The ph was between 6 and 10, thus silica sol has the fastest floc settling down time under neutral conditions. SiO2 in strong alkali medium are mainly H2SiO4 2 and H3SiO4 2 and are negatively charged and not gelling. Under acidic conditions, H4SiO4 exists, which is the most prone to gelling. In neutral ph condition, the acid easily forms a continuous 3D network structure, which is formed by the Si O Si bond of water loss. Hence, the most suitable ph for deposition is 7. Figure 1. Effect of ph on the deposition rate of silicon and silicon aluminum content. 248
3 Effects of Deposition Temperature Figure 2. Effect of ph on oil absorption value. Test condition: The deposition ph is 5, the deposition rotation rate is 200 r/min, and the deposition time is 4 h. Figure 3 presents the influence of deposition temperature on the deposition rate of silicon aluminum and silica silicon aluminum contents. Figure 4 shows the influence of deposition temperature on the oil absorption of white carbon black. When the temperature is not up to the nucleation temperature, no silica formation was observed, instead silica sol. However, beyond 60 C, the particle growth was faster with the increase of temperature, and particle acceleration collision structure was closed to the nuclear periphery; moreover, white carbon black was more dispersed. Thus, the optimum deposition temperature considered is 60 C. Figure 3. Effect of deposition temperature on the deposition rate of aluminum and silicon content. 249
4 Figure 4. Effect of deposition temperature on the oil absorption value. Influence of Deposition Rotation Rate Test condition: The deposition ph is 5, the deposition temperature is 60 C, and the deposition time is 4 h. Figure 5 shows the influence of deposition rotation rate on the silicon aluminum content and deposition rate. Figure 6 presents the influence of the deposition rotation rate on the oil absorption of white carbon black. Increased speed can exacerbate the mixture in the material system and accelerate the molecular movement and collision; with faster collision, firmer structure is formed, hence the optimum deposition speed considered is 100 r/min. Figure 5. Effect of deposition rotation rate on silicon aluminum content and deposition rate. 250
5 Figure 6. Effect of deposition rotation rate on the oil absorption value. Influence of Deposition Time Test condition: The deposition ph is 5, the deposition temperature is 60 C, and the deposition rotation rate is 200 r/min. Figure 7 shows the effect of deposition time on the deposition rate and content of the silicon and aluminum. Figure 8 presents the effect of deposition time on the oil absorption of white carbon black. At the deposition time of 2 h, particle agglomeration was observed; at 4 h, after complete deposition, the colloidal particles moved to the nuclear center for a continuous connection. Consequently, the particles are tightly around the nuclear periphery, and white carbon black dispersion is worse. Therefore, the optimum deposition time is considered at 4 h. Figure 7. Effect of deposition time on the content of silicon and aluminum and deposition rate. 251
6 Figure 8. Effect of deposition time on oil absorption value. CONCLUSIONS Results show that fly ash with alkali solution can be employed in the deposition of aluminum containing white carbon black under the following optimal conditions: ph of 7, deposition temperature of 60 C, deposition rotation rate of 100 r/min, and deposition time of 4 h. Under the optimal conditions, the silicon and aluminum deposition rates were 97.43% and 66.45%, respectively. The silicon and aluminum contents in the aluminum silica were 93.25% and 7.97%, respectively. In addition, the oil absorption value of 1 g of fly ash was 200 ml g 1. Therefore, the fly ash alkali solution has satisfied the standards for industrial production. REFERENCE 1. Xue Lin, Liu Jianlu. Aluminum salt in the precipitated silica application [J]. Guizhou Chemical Industry, 2005, 03: Wang Ping, Li Liaosha. Preparation of fly ash silica [J]. Chinese Exploratory Study on the Comprehensive Utilization of Resources, 2004, 07: General Hu. [J]. Environmental Science and Technology Research of 1996 Acid Leaching From Fly Ash in the Preparation of White Carbon Black, (2): Yu Hairong. Agent and silica [J]. Electric Power Environmental Protection by Mixing Aluminum and Iron Fly Ash, 1992, 8 (2): Jing and Yi Maosen, Zhong Wen Zhang. Fly Ash Extraction of Silica and Alumina [J]. China Engineering Science, 2012, 14 (2) 6. Zhou Xiaping, Ke Wei Jing, Yilong. Fly ash short process preparation of white carbon black [J]. Coal Mine Environmental Protection, 2011,17 (6):
7 7. General Hu, Chen Ding. Study on alkali fusion method from fly ash and preparation of white carbon black. Application of the Technology Market, 1995, (5): 14-15, Li Xiuti, Yao Zhitong, Sun Jie. Using fly ash preparation of white carbon black and its surface modification [J]. Functional Materials, 2011 (6): Zhang Mingxu, Xu Zifang, Li Xinyun. The Al2O3 and SiO2[J]. are Extracted From Fly Ash by Low Temperature Calcination Method. 2009, 32 (1): Fu Xiufeng, Xu Benjun, Huang Caijuan. Experimental Study on the Leaching of Silicon and Aluminum From Fly Ash by Microwave Alkali Dissolution Method, [J]. Method, 2014, 03: Jun Fang. Fly ash wet preparation of water glass and black white carbon [D]. Anhui University Of Science And Technology,
Alkali Fusion-Leaching Method for Comprehensive Processing of Fly Ash
International Conference with Elements of School for Young Scientists on Recycling and Utilization of Technogenic Formations (2017) Conference Paper Alkali Fusion-Leaching Method for Comprehensive Processing
More informationSTUDY ON ALKALI LIQUOR ROASTING AND SULPHURIC ACID LEACHING OF BAYAN OBO RARE EARTH CONCENTRATE
W. L. GUO, Y. H. XU, D. Q. CANG, S. F. MA, H. TIAN, Z. J. MENG, X. X. ZHANG ISSN 0543-5846 METABK 57(3) 157-161 (2018) UDC UDK 669.051.052:661.86:541.454:546.655.841:661.25=111 STUDY ON ALKALI LIQUOR ROASTING
More informationDispersion stability of nano-tungsten disulfide particulates
41 2 ( ) Vol.41 No.2 2010 4 Journal of Central South University (Science and Technology) Apr. 2010 1 1 2 (1. 410083 2. 410083) TF123.7 TH117.2 A 1672 7207(2010)02 0476 07 Dispersion stability of nano-tungsten
More informationNo. Name College Major Email 1 Ke Yang Chuan College of Science Chemistry key@cup.edu.cn 2 Wang Li Qun College of Science Mathematics wliqunhmily@gmail.com 3 Xu Tao College of Science Mathematics xutao@cup.edu.cn
More informationDepartment of Civil Engineering, Changzhou University, Changzhou213164, China
7 International Conference on Energy, Power and Environmental Engineering (ICEPEE 7) ISBN: 978--595-5- Research on the Influence of Additive Quantity on Properties of Silica Aerogels/Glazed Hollow Beads
More informationSeparation and recovery of Ni, Co and Mn from spent lithium-ion batteries
21 5 2011 5 Vol.21 No.5 The Chinese Journal of Nonferrous Metals May 2011 1004-0609(2011)05-1192-07 1, 1, 2, 1, 1, 1 (1., 410083 2., 410083) H 2 SO 4 +H 2 O 2 N902 10:1 H 2 SO 4 2.5 mol/l H 2 O 2 2.0 ml/g(
More informationThis section describes the chemicals, apparatus and experimental procedure used.
7 EXPERIMENTAL 7.1 Introduction This section describes the chemicals, apparatus and experimental procedure used. 7.2 Apparatus and Reagents 7.2.1 Reagents Table 7.1: Reagents used Name Purity Supplier
More informationEffects of Curing Conditions on Properties of Fly Ash-based Geopolymer Concrete
International Conference on Material Science and Application (ICMSA 2015) Effects of Curing Conditions on Properties of Fly Ash-based Geopolymer Concrete Xue-Hua YE 1,a,*, Jin-Yu XU 1,2,b 1 College of
More informationJournal of Chemical and Pharmaceutical Research, 2014, 6(10): Research Article
Available online www.jocpr.com Journal of Chemical and Pharmaceutical Research, 2014, 6(10):468-472 Research Article ISSN : 0975-7384 CODEN(USA) : JCPRC5 Case study- from photovoltaic industry recycled
More informationHigh Purity Alumina and Zeolite from Local Low Grade Kaolin
High Purity Alumina and Zeolite from Local Low Grade Kaolin Meor Yusoff M.S., Masliana Muslim, Choo Tye Foo and Julie Andrianny Murshidi Materials Technology Group, Industrial Technology Division, Malaysian
More informationReduction smelting on bismuth oxide residue in FeO SiO 2 CaO ternary slag system
J. Cent. South Univ. (2016) 23: 1326 1331 DOI: 10.1007/s11771-016-3183-0 Reduction smelting on bismuth oxide residue in FeO SiO 2 CaO ternary slag system ZHANG Du-chao( ), ZHANG Xin-wang( ), YANG Tian-zu(
More informationIMPROVEMENT OF CONCRETE DURABILITY BY COMPLEX MINERAL SUPER-FINE POWDER
277 IMPROVEMENT OF CONCRETE DURABILITY BY COMPLEX MINERAL SUPER-FINE POWDER Chen Han-bin, Chen Jian-xiong, Xiao Fei, and Cui Hong-ta College of Material Science, Chongqing University, Chongqing, PRC Abstract
More informationKinetics of Recovery of Alumina from Coal Fly Ash through Fusion with Sodium Hydroxide
American Journal of Materials Engineering and Technology, 2013, Vol. 1, No. 3, 54-58 Available online at http://pubs.sciepub.com/materials/1/3/6 Science and Education Publishing DOI:10.12691/materials-1-3-6
More informationWind Energy And Wind Power Technology (2) By ZHANG ZHI YING?ZHAO PING?LI YIN FENG DENG
Wind Energy And Wind Power Technology (2) By ZHANG ZHI YING?ZHAO PING?LI YIN FENG DENG Chinese Physics Letters, Volume 26, Number 1, - Number 1, January 2009 Zhou Xu-Rong, Zhang Xiao-Min, Yu Tong-Jun,
More informationOne step purification of impurities in the leachate of weathered crust elution-deposited rare earth ores
Physicochem. Probl. Miner. Process. 53(2), 17, 1188 1199 www.minproc.pwr.wroc.pl/journal Physicochemical Problems of Mineral Processing ISSN 1643-149 (print) ISSN 84-4735 (online) Received January 6, 17;
More informationLecture No. (7) Rubber Fillers
Lecture No. (7) Rubber Fillers Introduction of Rubber Fillers Rubbers in general are seldom used in their only form because of they are too weak to fulfill practical requirements for many applications
More informationThe Study of Method for Complex Processing Turgay Sub-Standard Aluminum-Containing Raw Materials
Advances in Materials Physics and Chemistry, 2012, 2, 216-220 doi:10.4236/ampc.2012.24b055 Published Online December 2012 (http://www.scirp.org/journal/ampc) The Study of Method for Complex Processing
More informationWind Energy And Wind Power Technology (2) By ZHANG ZHI YING?ZHAO PING?LI YIN FENG DENG
Wind Energy And Wind Power Technology (2) By ZHANG ZHI YING?ZHAO PING?LI YIN FENG DENG If you are searched for the ebook Wind energy and wind power technology (2) by ZHANG ZHI YING?ZHAO PING?LI YIN FENG
More information2nd International Conference on Architectural, Civil and Hydraulics Engineering (ICACHE 2016)
2nd International Conference on Architectural, Civil and Hydraulics Engineering (ICACHE 2016) Experimental Study on the Effect of Short Basalt Fiber on Properties of Lightweight Aggregate Concrete Li-guang
More informationIntroduction. Raw materials and experimental methods
Key Engineering Materials Submitted: 2014-07-21 ISSN: 1662-9795, Vols. 629-630, pp 481-486 Revised: 2014-08-06 doi:10.4028/www.scientific.net/kem.629-630.481 Accepted: 2014-08-06 2015 Trans Tech Publications,
More informationENVIRONMENT-PROTECTING UNBAKED CEMENT AND ITS HYDRATE MECHANISM
131 ENVIRONMENT-PROTECTING UNBAKED CEMENT AND ITS HYDRATE MECHANISM An Ming-zhe, 1 Zhang Li-jun, 1 Zhang Meng, 1 and Wang Fu-chuan 2 1 College of Civil Engineering and Architecture, Beijing Jiaotong University,
More information660 MW. Vol. 31 No. 3 Mar NO x N /600 /620 45% 40% Fig. 1 Diagram of a principle thermal system for low temperature economizers 660 MW
31 1 2016 1 JOURNAL OF ENGINEERING FOR THERMAL ENERGY AND POWER Vol. 31 No. 3 Mar. 2016 1001-2060201603 - 0083-04 660 MW 310014 5 660 MW 2. 33 g / kwh / 1 000 Nm / kg TK223. 3 + 3 A DOI10. 16146 /j. cnki.
More informationAnalysis on Characteristics of Fly Ash from Coal Fired Power Stations
Available online at www.sciencedirect.com Energy Procedia 17 (2012 ) 3 9 2012 International Conference on Future Electrical Power and Energy Systems Analysis on Characteristics of Fly Ash from Coal Fired
More informationMSE 352 Engineering Ceramics II
Kwame Nkrumah University of Science & Technology, Kumasi, Ghana MSE 352 Engineering Ceramics II Ing. Anthony Andrews (PhD) Department of Materials Engineering Faculty of Mechanical and Chemical Engineering
More informationThe Function of Ca(OH) 2 and Na 2 CO 3 as Additive on the Reduction of High-Phosphorus Oolitic Hematite-coal Mixed Pellets
, pp. 427 433 The Function of Ca(OH) 2 and Na 2 CO 3 as Additive on the Reduction of High-Phosphorus Oolitic Hematite-coal Mixed Pellets Wen YU, Tichang SUN,* Jue KOU, Yuxia WEI, Chengyan XU and Zhenzhen
More informationSilica Scaling in Water Treatment: Mechanism and Mitigation
Silica Scaling in Water Treatment: Mechanism and Mitigation XIAODA XU EMAIL: CORROSIONGURU.COM@GMAIL.COM Abstract Managing the silica scaling is a challenging task in reverse osmosis and thermal desalination
More information2017 International Conference on Electronic, Control, Automation and Mechanical Engineering (ECAME 2017) ISBN:
2017 International Conference on Electronic, Control, Automation and Mechanical Engineering (ECAME 2017) ISBN: 978-1-60595-523-0 Effect of Eutectic Silicon Particle Morphology on the Fluidity of 4045 Aluminum
More informationAdvances in Engineering Research, volume 103 Proceedings of the 3rd International Conference on Material Engineering and Application (ICMEA 2016)
Advances in Engineering Research, volume 103 Proceedings of the 3rd International Conference on Material Engineering and Application (ICMEA 2016) Effects of Recycled Coarse Aggregate Reinforcing Treated
More informationJournal of Chemical and Pharmaceutical Research, 2014, 6(3): Research Article
Available online www.jocpr.com Journal of Chemical and Pharmaceutical Research, 204, ():7-78 Research Article ISSN : 0975-784 CODEN(USA) : JCPRC5 Study of the mechanism of the direct reduction roasting
More informationEnergy Saving Measures in. Cement Industry
CH2356 Energy Engineering Energy Saving Measures in Cement Industry Dr. M. Subramanian Associate Professor Department of Chemical Engineering Sri Sivasubramaniya Nadar College of Engineering Kalavakkam
More informationN McEwan, Verref. Chromite A critical raw material for the Refractory Manufacturer
N McEwan, Verref Chromite A critical raw material for the Refractory Manufacturer Agenda: Introduction to Marico Chrome Corporation Marico Chromite deposit Refractory materials Suitability of chromite
More informationInfluences of Admixtures on Properties of Foam Concrete with Iron Tailings
Key Engineering Materials Online: 2014-02-27 ISSN: 1662-9795, Vol. 599, pp 61-65 doi:10.4028/www.scientific.net/kem.599.61 2014 Trans Tech Publications, Switzerland Influences of Admixtures on Properties
More informationEffect of Al5Ti1B master alloy on microstructures and properties of AZ61 alloys
Effect of Al5Ti1B master alloy on microstructures and properties of AZ61 alloys MA Xu-liang( ) 1, 2, WANG Xiang( ) 2, LI Xin-lin( ) 2, YANG Lei( ) 2 1. School of Materials Science and Engineering, Harbin
More informationHydrophobic modification of PP membrane coated by Al(OH) 3 colloids Feng-Xiang GUO1, a*, Lei LI1,b, Zhong-Hai ZHOU1,c, Qi-Wei WANG1,d, Yi-Meng HU1,e
Proceedings of the 3rd International Conference on Material Engineering and Application (ICMEA 2016) Hydrophobic modification of PP membrane coated by Al(OH) 3 colloids Feng-Xiang GUO1, a*, Lei LI1,b,
More informationWeathering is the principal process that acts upon the earth s primary minerals to form the smaller and finer particles that we call soil.
WEATHERING OF SOIL MINERALS AND CHANGE IN MINERAL COMPOSITION Weathering is the principal process that acts upon the earth s primary minerals to form the smaller and finer particles that we call soil.
More informationChina. Keywords: Automotive manufacturing, Servitization, Total factor productivity (TFP), Research and development (R&D).
2016 3 rd International Conference on Social Science (ICSS 2016) ISBN: 978-1-60595-410-3 The SWOT and Countermeasures Analysis about Automotive Manufacturing Servitization in Guangxi Based on the Perspective
More informationAli Allahverdi, Kamyar Mehrpour & Ebrahim Najafi Kani
IUST International Journal of Engineering Science, Vol. 19, No.3, 8, Page 1-5 Chemical & Civil Engineering, Special Issue TAFTAN POZZOLAN-BASED GEOPOLYMER CEMENT Ali Allahverdi, Kamyar Mehrpour & Ebrahim
More informationExtraction of vanadium from sulfuric acid leaching solution of stone coal by ion exchange
Bulgarian Chemical Communications, Volume 7, Special Issue D (pp. 99 10) 2015 Extraction of vanadium from sulfuric acid leaching solution of stone coal by ion exchange Xiao Yang, Yi-min Zhang*, Shen-xu
More informationMitigative Capacities of Plant Disposition Types and Space Types on. Urban Heat Island Effect. LU & Bo WANG b
Mitigative Capacities of Plant Disposition Types and Space Types on Urban Heat Island Effect Ying-ying LIUa & Yu-chen GUO & Xiang-dong XIAO & Sai WANG & Xiao-ping LU & Bo WANG b Department of horticulture,
More informationSoda Ash ( Sodium carbonate) Manufacture
Soda Ash ( Sodium carbonate) Manufacture Pertinent properties Mol. Wt. 106 M.P. 851deg.C. B.P. Decomposes Soluble in water 8.9 gm/100gm at 20 deg.cel. Grade s: 99% sodium carbonate washing soda ( Na 2
More informationA study of bauxite tailing quality improvement by reverse flotation
IOP Conference Series: Materials Science and Engineering PAPER OPEN ACCESS A study of bauxite tailing quality improvement by reverse flotation To cite this article: W Wulandari et al 2018 IOP Conf. Ser.:
More informationCHARACTERISTICS OF SLUDGE FROM DIFFERENT WATER TREATMENT PLANTS
Journal of Experimental Research December 2017, Vol 5 No 2 www.er-journal.com Email: editor-in-chie f@er-journal.com Received: December, 2016 Accepted for Publication: June, 2017 CHARACTERISTICS OF SLUDGE
More informationAPPLICATIONS OF GEOPOLYMER IN BUILDING MATERIALS AND RETROFITTING
APPLICATIONS OF GEOPOLYMER IN BUILDING MATERIALS AND RETROFITTING PROJECT REFERENCE NO. : 37S0126 COLLEGE : B.V.BHOOMARADDI COLLEGE OF ENGINEERING & TECHNOLOGY, HUBLI BRANCH : CIVIL ENGINEERING GUIDE :
More informationProperties of waste-based geopolymer building blocks
Applied Mechanics and Materials Online: 2013-08-08 ISSN: 1662-7482, Vols. 357-360, pp 935-938 doi:10.4028/www.scientific.net/amm.357-360.935 2013 Trans Tech Publications, Switzerland Properties of waste-based
More informationInfluence of diameter of quartz raw material on the quality of fused. quartz product
5th International Conference on Advanced Design and Manufacturing Engineering (ICADME 2015) Influence of diameter of quartz raw material on the quality of fused quartz product W.H. ZHOU 1 & S.G. ZHU 1
More informationChemical Activation of Low Calcium Fly Ash Part 1: Identification of Suitable Activators and their Dosage
Chemical Activation of Low Calcium Fly Ash Part 1: Identification of Suitable Activators and their Dosage P. Arjunan 1, M. R. Silsbee 2, and D. M. Roy 2, 1 Custom Building Products, 6515, Salt Lake Ave,
More informationThe Effect of Regulators on Flotation Desulfurization of High-sulfur Bauxites
The Effect of Regulators on Flotation Desulfurization of High-sulfur Bauxites Li Hua-xia and Chen Xiang-qing School of Chemical Engineering and Energy, Zhengzhou University, Zhengzhou, China Corresponding
More informationDEVELOPMENT OF SLUDGE WASTE TREATMENT PROCESS
DEVELOPMENT OF SLUDGE WASTE TREATMENT PROCESS D. S. Hwang, J. H. Oh, K. I. Lee, Y. D. Choi, S. T. Hwang, J. H. Park Korea Atomic Energy Research Institute ABSTRACT Korea Atomic Energy Research Institute
More informationEffect of Physical Properties of Pr-Nd Oxide on Its Melton Salt Electrolysis
International Journal of Materials Science and Applications 2018; 7(5): 186-191 http://www.sciencepublishinggroup.com/j/ijmsa doi: 10.11648/j.ijmsa.20180705.13 ISSN: 2327-2635 (Print); ISSN: 2327-2643
More informationLiquid Filtration for Chlor- Alkali Plants
Liquid Filtration for Chlor- Alkali Plants November 17, 2016 Dwight Davis W.L. Gore & Inc. What are the 3 most important parameters in operating a chlor-alkali plant? 1. Brine Quality 1. Brine Quality
More informationFLYASH BRICKS 1. INTRODUCTION 2. PRODUCTS AND ITS APPLICATION. Profile No.: 17 NIC Code: 23921
Profile No.: 17 NIC Code: 23921 FLYASH BRICKS 1. INTRODUCTION Fly Ash Bricks are manufactured using Major percentage of fly ash generated from Thermal Power stations. Other raw materials used along with
More informationBiofuels GS 2 Measuring Course Part II, DTU, Feb 2 6, 2009 Experiments in the entrained flow reactor
Biofuels GS 2 Measuring Course Part II, DTU, Feb 2 6, 2009 Experiments in the entrained flow reactor Frida Claesson (ÅA) Johanna Olsson (CTU) Kavitha Pathmanathan (NTNU) Samira Telschow (DTU) Liang Wang
More informationCHARACTERIZATION OF CERAMIC SHELLS FABRICATED USING YTTRIA AS REINFORCING FILLER
CHARACTERIZATION OF CERAMIC SHELLS FABRICATED USING YTTRIA AS REINFORCING FILLER A. Chennakesava Reddy Assistant Professor, Department of Mechanical Engineering M.J. College of Engineering & Technology,
More informationCu 70 Zr 30. Effects of cooling rate on primary phase and peritectic transformation in Cu 70 Zr 30 alloy (2014)
24 9 2014 9 Volume 24 Number 9 The Chinese Journal of Nonferrous Metals September 2014 1004-0609(2014)09-2295-07 Cu 70 Zr 30 1, 2 1 1, 2 1 1 3 (1. 330063 2. 330063 3. 710072) Cu 70 Zr 30 1042 957 5 m Cu
More informationSilica Fume in Concrete
Silica Fume in Concrete Silica Fume... Very fine noncrystalline silica produced in electric arc furnaces as a byproduct of the production of elemental silicon or alloys containing silicon; also known as
More informationBonding and abrasion resistance of geopolymeric repair material made with steel slag
Cement & Concrete Composites 30 (2008) 239 244 www.elsevier.com/locate/cemconcomp Bonding and abrasion resistance of geopolymeric repair material made with steel slag Shuguang Hu a, Hongxi Wang a,b, *,
More informationResearch on the High Strength Glass Ceramics/Mullite Ceramics Composites
New Journal of Glass and Ceramics, 2011, 1, 53-57 doi:10.4236/njgc.2011.12009 Published Online July 2011 (http://www.scirp.org/journal/njgc) 53 Research on the High Strength Glass Ceramics/Mullite Ceramics
More informationTreatment of Dye Wastewater by Flocculation and Sedimentation-Micro-electrolysis-Fenton Oxidation Process
79 A publication of CHEMICAL ENGINEERING TRANSACTIONS VOL. 62, 2017 Guest Editors: Fei Song, Haibo Wang, Fang He Copyright 2017, AIDIC Servizi S.r.l. ISBN 978-88-95608-60-0; ISSN 2283-9216 The Italian
More informationRecovery of niobium and tantalum from low grade tin slag - A hydrometallurgical approach
Environmental and Waste Management (ISSN : 0971-9407) Eds. - A. 8andopadhyay, N.G. Goswami and P.R. Rao 5 NML, Jamshedpur - 831 007, 1998, pp. 100-107 Recovery of niobium and tantalum from low grade tin
More informationInvestigation and Comparison of the Strength Properties of Lightweight Concretes Containing LECA and Waste Glass
J. Appl. Environ. Biol. Sci., (12S) 21-26, 201 201, TextRoad Publication ISSN: 2090-4274 Journal of Applied Environmental and Biological Sciences www.textroad.com Investigation and Comparison of the Strength
More informationExperimental Study of Boiling Crisis Phenomena in Nanofluids
Experimental Study of Boiling Crisis Phenomena in Nanofluids Craig Gerardi Advisors/Contributors: Professor Jacopo Buongiorno Dr. Lin-Wen Hu Dr. In Cheol Bang Massachusetts Institute of Technology, Nuclear
More informationSupporting Information
Supporting Information Vertically Aligned and Interconnected SiC Nanowire Networks Leading to Significantly Enhanced Thermal Conductivity of Polymer Composites Yimin Yao,, Xiaodong Zhu,, Xiaoliang Zeng,
More informationIMPACT OF CALCIUM HYDROXIDE ON THE EQUIPMENT AND PROCESS OF OIL SANDS TAILINGS TREATMENT
IMPACT OF CALCIUM HYDROXIDE ON THE EQUIPMENT AND PROCESS OF OIL SANDS TAILINGS TREATMENT Jesse Fox- Graymont Ken Rahal- FLSmidth Tailings & Mining Waste- 2018 Keystone, CO Agenda Coagulation vs Flocculation
More informationPressure leaching of zinc silicate ore in sulfuric acid medium
Pressure leaching of zinc silicate ore in sulfuric acid medium LI Cun-xiong( 李存兄 ), XU Hong-sheng( 徐红胜 ), DENG Zhi-gan( 邓志敢 ), LI Xing-bin( 李兴彬 ), LI Ming-tin( 李旻廷 ), WEI Chang( 魏昶 ) Faculty of Metallurgical
More informationBeijing , China
2016 International Conference on Advanced Materials Science and Technology (AMST 2016) ISBN: 978-1-60595-397-7 Research on Analysis of Tailing Mineral Materials Based on Chemical Analysis and Spectral
More informationIn the 21st century, with more understanding of the importance
An improved sodium silicate binder modified by ultra-fine powder materials *WANG Ji-na 1, FAN Zi-tian 1, WANG Hua-fang 2, DONG Xuan-pu 1, HUANG Nai-yu 1 (1. State Key Laboratory of Plastic Simulation and
More informationProcess Instruments (UK) Ltd.
Process Instruments (UK) Ltd. Coagulation Control; Past, Present and Future Mike Riding Process Instruments (UK) Ltd. What We Sell Biofilm ph Conductivity Dissolved Oxygen Free & Total Chlorine CRONOS
More informationPREPARATION OF GEOPOLYMER USING FLY ASH AND RICE HUSK SILICA AS RAW MATERIALS
18 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS PREPARATION OF GEOPOLYMER USING FLY ASH AND RICE HUSK SILICA AS RAW MATERIALS P. Chaiyapoom 1,2, S. Jiemsirilers 1,2*, S. Wada 1,2, K. Hemra 3, P.
More informationElectronic Supporting Information. Synthesis of single crystalline hexagonal nanobricks of
Electronic Supporting Information Synthesis of single crystalline hexagonal nanobricks of LiNi 1/3 Co 1/3 Mn 1/3 O 2 with high percentage of exposed {010} active facets as high rate performance cathode
More informationPreparation and characterisation of amorphous silica/anatase composite through mechanochemical method
Preparation and characterisation of amorphous silica/anatase composite through mechanochemical method X. F. Hou 1,2, H. Ding* 1, Y. X. Zheng 1 and M. M. Wang 1 In order to solve the issues in the production
More informationLuoyang , Henan, China. Keywords: Cr-Mo Steel, Heat Treatment, Microstructure, Impact Toughness.
2017 International Conference on Mechanical Engineering and Control Automation (ICMECA 2017) ISBN: 978-1-60595-449-3 Effects of Quenching Temperature on Microstructure and Mechanical Properties of 75Cr-Mo
More informationPrecipitated Silica from Pumice and Carbon Dioxide Gas (Co 2. ) in Bubble Column Reactor
Journal of Physics: Conference Series PAPER OPEN ACCESS Precipitated Silica from Pumice and Carbon Dioxide Gas (Co 2 ) in Bubble Column Reactor To cite this article: R Dewati et al 2018 J. Phys.: Conf.
More informationSilica Pigments for Use in Commercial Color Inkjet, High-Volume, On-Demand Printing Systems
Silica Pigments for Use in Commercial Color Inkjet, High-Volume, On-Demand Printing Systems Demetrius Michos, W. R. Grace & Co. Natalia Krupkin, W. R. Grace & Co. TRENDS IN DIGITAL MEDIA WORLD New installations
More informationCalcified roasting-acid leaching process of vanadium from low-grade vanadium-containing stone coal
Chin.J.Geochem.(2014)33:163 167 DOI: 10.1007/s11631-014-0672-4 Calcified roasting-acid leaching process of vanadium from low-grade vanadium-containing stone coal WANG Taiying 1, XU Longjun 1*, LIU Chenlun
More informationAn Experimental Investigation on the behaviour of Portland Cement Concrete and Geopolymer Concrete in acidic environment
An Experimental Investigation on the behaviour of Portland Cement and Geopolymer in acidic environment Kolli Venkata Manjeeth, J. Sri Kalyana Rama 1 (Student, Civil Engineering Department, BITS PILANI
More informationISSN (PRINT): , (ONLINE): , VOLUME-4, ISSUE-11,
EXPERIMENTAL INVESTIGATIONS ON THERMAL DIFFUSIVITY OF CO2 SILICATE MOULDS Dr.R. Venkat Reddy Dept.of Mech.Engg., Anurag Group of Institutions, Hyderabad ABSTRACT The present study was carried out to determine
More informationGB/T Translated English of Chinese Standard: GB/T
Translated English of Chinese Standard: GB/T223.68-1997 www.chinesestandard.net Sales@ChineseStandard.net GB NATIONAL STANDARD OF THE PEOPLE S REPUBLIC OF CHINA ICS 77.080 H 11 GB/T 223.68-1997 Replacing
More informationAdmixtures. Lecture No. 12
Admixtures Lecture No. 12 Set-Retarding This type of chemical admixtures decreases the initial rate of reaction between cement and water and thereby retards the setting of concrete. It functions by coating
More informationEffect of Silicon Carbide on Reactions between Molten Steel and Fused Magnesia Silicon Carbide Composite Refractory
Effect of Silicon Carbide on Reactions between Molten Steel and Fused Magnesia Silicon Carbide Composite Refractory Interactions between MgO SiC composite and liquid steel resulted in decomposition of
More informationEnhancement of the Reactivities of Iron Blast Furnace Slag/Hydrated Lime Sorbents toward SO 2 by NaOH
J. Chin. Inst. Chem. Engrs., Vol. 34, No. 5, 525-530, 2003 Enhancement of the Reactivities of Iron Blast Furnace Slag/Hydrated Lime Sorbents toward SO 2 by NaOH Chiung-Fang Liu [1] and Shih-Min Shih [2]
More informationStudy On Application Of Alumina In High-Purity Andalusite Based Refractory
Journal of Minerals & Materials Characterization & Engineering, Vol. 3, No.2, pp 81-89, 2004 jmmce.org Printed in the USA. All rights reserved Study On Application Of Alumina In High-Purity Andalusite
More informationCARBONATION OF WOLLASTONITE USING SUPERCRITICAL CARBON DIOXIDE
CARBONATION OF WOLLASTONITE USING SUPERCRITICAL CARBON DIOXIDE Clifford Y. Tai*, W.-R. Chen and Shin-Min Shih Department of Chemical Engineering National Taiwan University Email: cytai@ntu.edu.tw The feasibility
More informationVacuum filter and direct current electro-osmosis dewatering of fine coal slurry
Procedia Earth and Planetary Science 1 (2009) 685 693 Procedia Earth and Planetary Science www.elsevier.com/locate/procedia The 6 th International Conference on Mining Science & Technology Vacuum filter
More informationEffects of size distribution on flotation kinetics of Chalcopyrite
International Conference on Environment Science and Engineering IPCBEE vol.8 () () IACSIT Press, Singapore Effects of size distribution on flotation kinetics of Chalcopyrite Luo Xian-ping College of Resource
More informationEFFECTS OF STONE POWDER SLUDGE ON THE STRENGTH AND MICROSTRUCTURE OF ALKALI-ACTIVATED FLY ASH PASTES
- Technical paper - EFFECTS OF STONE POWDER SLUDGE ON THE STRENGTH AND MICROSTRUCTURE OF ALKALI-ACTIVATED FLY ASH PASTES Sejin CHOI *1 Paulo J MONTEIRO *2 Moohan KIM *3 ABSTRACT Stone powder sludge is
More informationSilica Extraction at Mammoth Lakes, California
Silica Extraction at Mammoth Lakes, California William Bourcier, William Ralph, Mackenzie Johnson, Carol Bruton Energy and Environment Directorate Lawrence Livermore National Laboratory Bourcier1@llnl.gov
More informationDry CFB-FGD By-Product Utilization - International Prospectives
World of Coal Ash (WOCA) Conference - May 9-12, 2011, in Denver, CO, USA http://www.flyash.info/ Dry CFB-FGD By-Product Utilization - International Prospectives Yabing Jiang, Muh-Cheng M. Wu (1), Qingfa
More informationHydration and Hardness Features of Green Concrete
Hydration and Hardness Features of Green Concrete Sun Wen-biao Department of Safety Engineering Henan Institute of Engineering Zhengzhou, China ABSTRACT Green cement that contained about 7 percent of slag
More informationUnderstanding Pretreatment. WesTech Engineering, Inc. Salt Lake City, Utah, USA
Understanding Pretreatment WesTech Engineering, Inc. Salt Lake City, Utah, USA Industrial Water Usage Water is required in almost every industry For: Cooling Boiler feed Process Drinking Cleaning In 2005
More informationTemperature dependence on reaction of CaCO 3 and SO 2 in O 2 /CO 2 coal combustion
DOI: 10.1007/s11771 009 0140 1 Temperature dependence on reaction of CaCO 3 and SO 2 in O 2 /CO 2 coal combustion WANG Hong( ) 1, 2, XU Hui-bi( ) 2, ZHENG Chu-guang( ) 1, QIU Jian-rong( ) 1 (1. National
More informationEnvironment Protection Engineering ENHANCING SO2 REMOVAL EFFICIENCY BY LIME MODIFIED WITH SEWAGE SLUDGE IN A NOVEL INTEGRATED DESULFURIZATION PROCESS
Environment Protection Engineering Vol. 43 2017 No. 4 DOI: 10.5277/epe170402 LINBO QIN, JUN HAN 1, WANGSHENG CHEN 1, ZHANZHUANG LIU 1, MENGXIA HE 1, FUTANG XING 1 ENHANCING SO2 REMOVAL EFFICIENCY BY LIME
More informationSupplementary Cementitious Materials (SCMs) Cement Hydration: 3/29/2017. SCMs effect on hydration. Hydration Schematic
Supplementary Cementitious Materials (SCMs) Ohio Precast Concrete Association March 2017 Meeting Jay Whitt Lehigh Cement Technical Services Engineer Supplementary Cementitious Materials (SCMs) Cement Hydration:
More informationA NOVEL VACUUM ALUMINOTHERMIC REDUCTION LITHIUM PROCESS
4th International Symposium on High-Temperature Metallurgical Processing Edited by: Tao Jiang, Jiann-YangHwang, Phillip J. Mackey, Onuralp Yucel, and Guifeng Zhou TMS (The Minerals, Metals & Materials
More informationPerformance of Sulfuric Acid Leaching of Titanium from Titanium-Bearing Electric Furnace Slag
Journal of Materials Science Research; Vol. 5, No. 4; 2016 ISSN 1927-0585 E-ISSN 1927-0593 Published by Canadian Center of Science and Education Performance of Sulfuric Acid Leaching of Titanium from Titanium-Bearing
More informationCharacteristics of the Geopolymer using Fly Ash and Blast Furnace Slag with Alkaline Activators
2012 4th International Conference on Chemical, Biological and Environmental Engineering IPCBEE vol.43 (2012) (2012) IACSIT Press, Singapore DOI: 10.7763/IPCBEE. 2012. V43. 32 Characteristics of the Geopolymer
More informationMullite whiskers prepared by molten salt method using Si powders
Journal of Advanced Ceramics 2012, 1(4): 283-289 DOI: 10.1007/s40145-012-0028-7 ISSN 2226-4108 Research Article Mullite whiskers prepared by molten salt method using Si powders Wei WANG a,*, Hongwei LI
More informationVol. 31 No. 5 May x HCN / HCN /NH Hayhurst. Gardon. Fe 2 O 3 Fe. NO x NO x. Fe 2 O 3. 1 mg Fe 2 O 3 NO NO
31 5 2016 5 JOURNAL OF ENGINEERING FOR THERMAL ENERGY AND POWER Vol. 31 No. 5 May. 2016 1001-2060 2016 05-0129 - 06 NO 1 1 2 1. 200093 2. 201620 NO x Fe NO NO Fe Fe 2 O 3 NO x HCN / 100 mg700 800 900 NO
More informationStudy on reduction behavior of molybdenum trioxide in molten steel
Indian Journal of Engineering & Materials Sciences Vol. 22, August 2015, pp. 460-464 Study on reduction behavior of molybdenum trioxide in molten steel Hangyu Zhu*, Jianli Li, Zhengliang Xue & Wei Wang
More informationAdmixtures CIVL
Admixtures CIVL 3137 88 Admixtures admixture (n.) any material other than water, aggregates, hydraulic cement and fiber reinforcement, used as an ingredient of concrete or mortar, and added to the batch
More informationINVESTIGATION AND OPTIMIZATION OF USE OF ANIONIC COLLECTORS IN DIRECT FLOTATION OF BAUXITE ORES
Physicochem. Probl. Miner. Process. 52(2), 216, 932 942 www.minproc.pwr.wroc.pl/journal/ Physicochemical Problems of Mineral Processing ISSN 1643-149 (print) ISSN 284-4735 (online) Received August 8, 215;
More information