Formation of Corrosion Resistant Mg(OH) 2 Film Containing Mg-Al Layered Double Hydroxide on Mg Alloy Using Steam Coating

Size: px
Start display at page:

Download "Formation of Corrosion Resistant Mg(OH) 2 Film Containing Mg-Al Layered Double Hydroxide on Mg Alloy Using Steam Coating"

Transcription

1 2017 International Conference on Mechanical and Mechatronics Engineering (ICMME 2017) ISBN: Formation of Corrosion Resistant Mg(OH) 2 Film Containing Mg-Al Layered Double Hydroxide on Mg Alloy Using Steam Coating Takahiro ISHIZAKI 1,*, Mika TSUNAKAWA 2, Yuta SHIMADA 2, Ryota SHIRATORI 2, Kae NAKAMURA 2 and Ai SERIZAWA 1 1 Department of Materials Science and Engineering, College of Engineering, Shibaura Institute of Technology, Toyosu, Koto-ku, Tokyo, Japan 2 Department of Materials Science and Engineering, Graduate School of Engineering and Science, Shibaura Institute of Technology, Toyosu, Koto-ku, Tokyo, Japan *Corresponding author Keywords: Mg alloy, Steam coating, Corrosion resistance, Magnesium hydroxide, Mg-Al layered double hydroxide. Abstract. In recent years, a reduction in weight of materials is highly desirable in the fields of transport industry and information technology devices. Magnesium (Mg) alloys have excellent physical and mechanical properties such as low density, good electromagnetic shielding, and high strength/weight ratio. Unfortunately, they have a great issue that is low corrosion. Thus, it is very important to develop surface treatment technologies to improve the corrosion resistance of magnesium alloys. Many surface treatments such as chemical conversion, anodic oxidization, and electroplating have been developed. However, there processes require multi-step pretreatments and waste liquid treatments. Thus, the development of a simple, easy, and low-cost surface treatment is highly desirable. In this paper, we report a novel preparation method of anticorrosive film on Mg alloy by steam coating and the corrosion resistance of the film. The prepared films were characterized by XRD, SEM, EDX, and electrochemical measurements. Polarization curve measurements demonstrated that the E corr and i corr values were found to be most positive potential and lowest current density in all the samples, indicating that the sample had best corrosion resistant performance. Introduction Magnesium and its alloys are superior materials in lightweight property. Recently, the weight saving in the fields of the transportation application would be one of the most important issues to improve energy conservation. Thus, they are expected to be applied to transportation such as aerospace, aircraft, auto-mobile, and railway [1-4]. However, the low corrosion resistant property of the magnesium alloys limits the use at large scale, so it is necessary to improve the corrosion resistant properties of the magnesium alloys. To improve the fault, various surface treatments for the preparation of protection films such as anodized film, chemical conversion film, and polymer film on magnesium alloys have been developed [5-8]. Among them, the chemical conversion films have been practically applied to Mg components such as parts of automotive components because of easy operation and low cost. Chromate system chemical conversions are well known as the most popular and effective conversion process to produce a protective layer on the various metal surfaces. However, the use of chromate system is being progressively regulated due to the high toxicity of the hexavalent chromium compounds. Therefore, an environmentally friendly surface treatment method to improve the low corrosion resistance of the magnesium alloys is highly desirable. Recently, a chemical conversion method using Mg-Al layered double hydroxide (LDH) has been used as a protect film to improve significantly corrosion resistance [9-13], because the LDHs could be effective agents for delaying the corrosion reaction because of the entrapment functionality of corrosion-relevant anions such as chloride ions in LDHs [14,15]. Thus, the LDHs are promising materials for improving corrosion resistance. For industrial application, it is important to develop 201

2 environmentally-friendly surface treatment methods to prepare anticorrosive film containing LDHs. Recently, we developed a novel preparation method of anticorrosive film on Mg alloy by steam coating [16,17]. The steam coating is a simple, environmentally friendly, and inexpensive surface treatment method. In addition, the film prepared by steam coating was mainly composed of magnesium hydroxide and Mg-Al LDH. In this paper, we report the preparation method of the corrosion resistant Mg(OH) 2 film containing Mg-Al LDH by steam coating and the corrosion resistance of the film coated magnesium alloys.. Experimental Procedures Magnesium alloy AZ31 (composition: 2.98 mass% Al, 0.88 mass% Zn, 0.38 mass% Mn, mass% Si, mass% Cu, mass% Ni, mass% Fe, and the rest is Mg) specimens were used as substrate. Substrates were ultrasonically cleaned in ethanol for 10 min. The cleaned AZ31 substrates were introduced in a Teflon-lined autoclave with a 100 ml capacity. 20 ml of ultrapure water was introduced at the bottom of the autoclave to produce steam. The autoclave was heated to a temperature of 433 K, and then held at this temperature for 2 to 6 h, and was subsequently cooled naturally to room temperature. After the steam treatment, the samples were ultrasonically cleaned in ethanol for 10 min. The surface morphologies and of the corrosion resistant films were observed using a scanning electron microscopy. The crystal phase of the obtained film was investigated using a glancing angle X-ray diffraction (GAXRD) at a glancing angle of 1o with CuKα radiation (40 kv, 40 ma) within the range of 5 and 80 and scanning rate of 2θ = 4 (min 1 ). The corrosion resistance was estimated by electrochemical measurements and immersion tests in a 5 mass% NaCl aqueous solutions. All electrochemical measurements were performed in a 5.0 mass% NaCl aqueous solution at room temperature. The film coated AZ31 and a platinum mesh were used as the working and counter electrodes, respectively. An Ag/AgCl was used as the reference electrode. Potentiodynamic polarization curves were measured with respect to the open circuit potential (OCP) at a scanning rate of 0.5 mv/s from 200 to +800 mv. Results and Discussion Figure 1 shows XRD patterns of the film coated AZ31 by steam coating for (a) 2 h, (b) 4 h, and (c) 6 h. Some peaks attributable to Mg alloy substrate are clearly observed in all the patterns. In particular, the peak intensity attributable to Mg ally substrate for the film coated AZ31 for 2 h was high. This indicates that the film thickness is thin. All peak intensities assigned to Mg alloy substrate decrease with an increase in the treatment time, indicating that the film thickness increases gradually with an increase in the treatment time. A diffraction peak of [101] reflection at around 2θ = 38 becomes stronger with an increase in the treatment time. With an increase in treatment time, several peaks at approximately 2θ = 18, 33, 38, 51, 58, 62, 68, and 72 assigned to the 001, 100, 101, 102, 110, 111, 200, and 201 diffraction peaks of brucite type Mg(OH) 2 are also clearly observed in all the GAXRD patterns. In addition, the two peaks at around 2θ = 11 and 22 assigned to the [003] and [006] reflections of Mg 1-x Al x (OH) 2 (CO 3 ) x/2 nh 2 O (Mg-Al LDH), respectively, can be clearly observed in the XRD patterns of the film prepared for 2 and 4 h. These results indicate that Mg(OH) 2 is initially formed on the Mg alloy substrate and Mg-Al LDH is then grown in the Mg(OH) 2 film. 202

3 Figure 1. XRD patterns of the obtained sample by steam coating for (a) 2, (b) 4, and (c) 6 h. Figure 2 shows SEM images of the sample surfaces treated at 433 K for (a) 2 h, (b) 4 h, and (c) 6h. In the case of 2h of the treatment time, aggregated particles were clearly observed. The particles were composed of nanoparticles with sizes of nm. When the preparation time was prolonged to 4 h, granular structures were clearly observed. The particle size of the sample prepared for 4 h became larger and the film was found to be dense and the surface was perfectly covered with the film. The film treated for 6 h was found to be denser than the sample surface treated for 4 h, and exhibited small amounts of nanosheets that are aligned at fairly inclined angles with respect to the surface. Figure 2. SEM images of the obtained sample by steam coating for (a) 2, (b) 4, and (c) 6 h. Figure 3 shows cross-sectional SEM images and elemental Mg and O mapping images of the samples prepared by steam coating for 2, 4, and 6 h. The film thicknesses for the samples prepared for 2, 4, and 6 h were estimated to be 3.1, 20.2, and 68.0, respectively. The film thickness increases with an increase in the treatment time. The elemental mapping images revealed that the film mainly consisted of Mg and O, which indicates that it was comprised of magnesium hydroxide. This is in agreement well with the XRD results. 203

4 Figure 3. Cross-sectional and elemetal Mg and O mapping images of the obtained sample by steam coating for (a) 2, (b) 4, and (c) 6 h. Figure 4 shows potentiodynamic polarization curves of the samples prepared by steam coating for 2, 4, and 6 h. The potentiodynamic polarization curve for untreated AZ31 is also shown. The corrosion potential, E corr, and corrosion current density, i corr, values for the untreated AZ31 were estimated to be V vs. Ag/AgCl and X 10-5 A/cm 2, respectively. The anodic region of the curve for the bare AZ31 can be divided into three fields: (i) first region beginning from E corr (low anodic overpotential) that exhibits a linear increase in current density with potential; (ii) a range of abrupt increase in current density from -1.4 V, where the dissolution of Mg to Mg + or Mg 2+ ions predominantly occurred [18]; (iii) a current plateau at more positive potentials, where the electrode surface is covered with a film identified as Mg(OH) 2 [19]. In the cathodic branch, hydrogen evolution is more dominant at negative potentials than Ecorr, resulting in an increase in the cathodic current density. The current densities of the anodic and cathodic branches of all samples decreased with film formation, which indicates that the films are effective in improving the corrosion resistance of AZ31 alloy. The E corr for the film coated AZ31 tends to shifted to positive direction with an increase in the treatment time. In addition, the i corr values were lowered with an increase in the treatment time. Clear passive regions can be observed on the curve for the samples treated at 433 K for 4 and 6 h. The E corr and i corr values of the sample treated at 433 K for 6h were estimated to be V and X A/cm 2, respectively. The E corr and i corr values were found to be most positive potential and lowest current density in all the samples, indicating that the sample had best corrosion resistant performance. Figure 4. Potentiodynamic polarizaiton curves of the obtained sample by steam coating for (a) 2, (b) 4, and (c) 6 h. Summary The corrosion resistant Mg(OH) 2 film was successfully formed on AZ31 Mg alloy by steam coating. 204

5 XRD patterns revealed that the film thickness became thicker with an increase in the treatment time tthe film thicknesses of the samples prepared for 2, 4, and 6 h were estimated to be 3.1, 20.2, and 68.0, respectively. Polarization curve measurements demonstrated that the E corr and i corr values for the film coated AZ31 tends to shifted to positive and lower direction, respectively, with an increase in the treatment time. As Mg alloys are one of the more promising materials for reducing vehicle weight, thereby lowering fuel consumption and reducing CO 2 emission, any improvement in their inherently low corrosion resistance is of great value to increasing their wider-scale use. We believe future work should focus on developing the steam coating process described here to greatly improve the corrosion resistance of a range of Mg alloys. Acknowledgement This research was partially supported by a Grant for Advanced Industrial Technology Development from the New Energy and Industrial Technology Development Organization (NEDO) of Japan (No. 11B06024d), a Grant-in-Aid for Young Scientists (B) (No. 16K18249) from the Japan Society for the Promotion of Science, and the Japan Science and Technology Agency (JST), Adaptable and Seamless Technology Transfer Program through Target-driven R&D (A-step: No. AS251Z02997K & AS S) References [1] S.R. Agnew, M.H. Yoo, C.N. Tome, Acta Mater. 49 (2001) [2] M. Furui, C. Xu, T. Aida, M. Inoue, H. Anada, T.G. Langdon, Mater. Sci. Eng. A, 410 (2005) 439. [3] M. Kawasaki, K. Kubota, K.I. Higashi, T.G. Langdon, Mater. Sci. Eng. A, 429 (2006) 334. [4] M.L. Zhang, Y.D. Yan, Z.Y. Hou, L.A. Fan, Z. Chen, D.X.Tang, J. Alloy Compd. 440 (2007) 362. [5] Z. Liu, W. Gao, Surf. Coat. Technol., 200 (2006) [6] J.S. Lian, G.Y. Li, L.Y. Niu, C.D. Gu, Z.H. Jiang, Q. Jiang, Surf. Coat. Technol. 200 (2006) [7] C.-E. Barchiche, E. Rocca, C. Juers, J. Hazan, J. Steinmetz, Electrochim. Acta, 53 (2007) 417. [8] M.F. Montemor, M.G.S. Ferreira, Electrochim. Acta, 52 (2007) [9] A. Collazo, M.Hernández, X.R. Nóvoa, C. Pérez, Electrochim. Acta, 56 (2011) [10] J.K. Lin, J.Y. Uan, Corros. Sci., 51 (2009) [11] J. Chen, Y. Song, D. Shan, E.-H. Han, Corros. Sci., 53 (2011) [12] J.K. Lin, K.L. Jeng, J.Y. Uan, Corros. Sci., 53 (2011) [13] J. Chen, Y. Song, D. Shan, E.-H. Han, Corros. Sci., 63 (2012) 148. [14] J.K. Lin, C.L. Hsia, J.Y. Uan, Scripta Mater., 56 (2007) 927. [15] J. Tedim, A. Kuznetsova, A.N. Salak, M.F. Montemor, D. Snihirova, M. Pilz, M.L. heludkevich, M.G.S. Ferreira, Corros. Sci., 55 (2012) 1. [16] T. Ishizaki, S. Chiba, H. Suzuki, ECS Electrochem. Lett., 2 (2013) C15-C17. [17] T. Ishizaki, S. Chiba, K. Watanabe, H. Suzuki, J. Mater. Chem. A, 1 (2013) [18] D.K. Tanaka, G.G. Long, J. Kruger, Structure of the Passive Films on Cast and Rapidly Solidified Mg Alloys. In: Proceedings of 11th International Corrosion Congress; 2-9, April, 1990; Florence. London: The International Corrosion Council [19] G. Baril, G. Galicia, C. Deslouis, N. Pébère, B. Tribollet, V. Vivier, M.X. Quondam. J. Electrochem. Soc., 154 (2007) C108 C

Effect of Anodizing Potential on the Surface Morphology and Corrosion Property of AZ31 Magnesium Alloy

Effect of Anodizing Potential on the Surface Morphology and Corrosion Property of AZ31 Magnesium Alloy Materials Transactions, Vol. 51, No. 6 (21) pp. 119 to 1113 #21 The Japan Institute of Metals Effect of Anodizing Potential on the Surface Morphology and Corrosion Property of AZ31 Magnesium Alloy S. A.

More information

Effect of ph on Phytic Acid Conversion Coating on AZ31B Magnesium Alloy

Effect of ph on Phytic Acid Conversion Coating on AZ31B Magnesium Alloy Effect of ph on Phytic Acid Conversion Coating on AZ31B Magnesium Alloy Huan-fang Gao 1, Shengtao Zhang 2, Liu Cheng-long 3, Jun-qiang Xu 4, Jun Li 5, Yu Li 6 1,4,5,6 College of Chemistry and Chemical

More information

Short Communication Corrosion Resistance of Super-Hydrophobic Coating on AZ31B Mg Alloy

Short Communication Corrosion Resistance of Super-Hydrophobic Coating on AZ31B Mg Alloy Int. J. Electrochem. Sci., 13 (2018) 6190 6200, doi: 10.20964/2018.07.29 International Journal of ELECTROCHEMICAL SCIENCE www.electrochemsci.org Short Communication Corrosion Resistance of Super-Hydrophobic

More information

THE RELATIONSHIP BETWEEN SURFACE TREATMENTS AND CORROSION RESISTANCE OF HOT-DIP GALVANIZED STEEL. Amirreza Bakhtiari

THE RELATIONSHIP BETWEEN SURFACE TREATMENTS AND CORROSION RESISTANCE OF HOT-DIP GALVANIZED STEEL. Amirreza Bakhtiari Association of Metallurgical Engineers of Serbia AMES Scientific paper UDC: 620.197.2:669.141; 620.193 THE RELATIONSHIP BETWEEN SURFACE TREATMENTS AND CORROSION RESISTANCE OF HOT-DIP GALVANIZED STEEL Amirreza

More information

J. Mater. Sci. Technol., 2010, 26(11),

J. Mater. Sci. Technol., 2010, 26(11), J. Mater. Sci. Technol., 2010, 26(11), 1016-1020. Effects of Current Density on the Microstructure and the Corrosion Resistance of Alumina Coatings Embedded with SiC Nano-particles Produced by Micro-arc

More information

Sealing Mechanism of Anodic Porous Oxide Films Formed on Aluminum in Lithium Hydroxide Solution

Sealing Mechanism of Anodic Porous Oxide Films Formed on Aluminum in Lithium Hydroxide Solution Proceedings of the 12th International Conference on Aluminium Alloys, September 5-9, 2010, Yokohama, Japan 2010 The Japan Institute of Light Metals pp. 1463-1468 1463 Sealing Mechanism of Anodic Porous

More information

Yajuan Liu a, Jinyong Xu a, Ying Gao b, Ye Yuan b, Cheng Gao a

Yajuan Liu a, Jinyong Xu a, Ying Gao b, Ye Yuan b, Cheng Gao a Available online at www.sciencedirect.com Physics Procedia 32 (2012 ) 107 112 18 th International Vacuum Congress (IVC-18) Influences of Additive on the Formation and Corrosion Resistance of Micro-arc

More information

Improvement of anticorrosion and adhesion to magnesium alloy by phosphate coating formed at room temperature

Improvement of anticorrosion and adhesion to magnesium alloy by phosphate coating formed at room temperature Improvement of anticorrosion and adhesion to magnesium alloy by phosphate coating formed at room temperature NIU Li-yuan( ), LIN Ji-xing( ), LI Yong( ), SHI Zi-mu( ), XU Lin-chao( ) Advanced Material Research

More information

Microstructure and Corrosion Properties of Mg-xSn-5Al-1Zn (x ¼ 0, 1, 5 and 9 mass%) Alloys

Microstructure and Corrosion Properties of Mg-xSn-5Al-1Zn (x ¼ 0, 1, 5 and 9 mass%) Alloys Materials Transactions, Vol. 51, No. 3 (2010) pp. 472 to 476 #2010 The Japan Institute of Metals Microstructure and Corrosion Properties of Mg-xSn-5Al-1Zn (x ¼ 0, 1, 5 and 9 mass%) Alloys Kyung Chul Park

More information

EFFECTS OF DIFFERENT ELECTROLYTE SYSTEMS ON THE FORMATION OF MICRO-ARC OXIDATION CERAMIC COATINGS OF 6061 ALUMINUM ALLOY

EFFECTS OF DIFFERENT ELECTROLYTE SYSTEMS ON THE FORMATION OF MICRO-ARC OXIDATION CERAMIC COATINGS OF 6061 ALUMINUM ALLOY 16 Rev. Adv. Mater. Sci. (01) 16-10 Y.J. Liu, EFFECTS OF DIFFERENT ELECTROLYTE SYSTEMS ON THE FORMATION OF MICRO-ARC OXIDATION CERAMIC COATINGS OF 6061 ALUMINUM ALLOY Y.J. Liu 1, J.Y. Xu1, W. Lin, C. Gao

More information

Corrosion Resistance Improvement of Galvanised Steel by Doped Silane Pre-Treatments

Corrosion Resistance Improvement of Galvanised Steel by Doped Silane Pre-Treatments 2015 2 nd International Conference on Material Engineering and Application (ICMEA 2015) ISBN: 978-1-60595-323-6 Corrosion Resistance Improvement of Galvanised Steel by Doped Silane Pre-Treatments J.F.

More information

Preparation of Trivalent Chromium Coating on 6063 Aluminum Alloy Jian-Zhen HUANG 1,a,* and You-Xiong LUO 1,b

Preparation of Trivalent Chromium Coating on 6063 Aluminum Alloy Jian-Zhen HUANG 1,a,* and You-Xiong LUO 1,b 2017 Joint International Conference on Materials Science and Engineering Application (ICMSEA 2017) and International Conference on Mechanics, Civil Engineering and Building Materials (MCEBM 2017) ISBN:

More information

Synthesis and characterization of functional nanocontainers for active corrosion protection. João Tedim

Synthesis and characterization of functional nanocontainers for active corrosion protection. João Tedim 2010 INTERNATIONAL WORKSHOP ON ENVIRONMENT AND ENERGY San Diego, California November 2-4, 2010 Synthesis and characterization of functional nanocontainers for active corrosion protection João Tedim University

More information

CORROSION RESISTANCE OF PLASMA NITRIDED AND NITROCARBURIZED AISI 316L AUSTENITIC STAINLESS STEEL

CORROSION RESISTANCE OF PLASMA NITRIDED AND NITROCARBURIZED AISI 316L AUSTENITIC STAINLESS STEEL CORROSION RESISTANCE OF PLASMA NITRIDED AND NITROCARBURIZED AISI 316L AUSTENITIC STAINLESS STEEL F.A.P. Fernandes 1*, J. Gallego 2, G.E. Totten 3, C.A. Picon 2, L.C. Casteletti 1 1 Department of Materials

More information

Electroless deposition of Ni W P coating on AZ91D magnesium alloy

Electroless deposition of Ni W P coating on AZ91D magnesium alloy Applied Surface Science 253 (2007) 5116 5121 www.elsevier.com/locate/apsusc Electroless deposition of Ni W P coating on AZ91D magnesium alloy W.X. Zhang, N. Huang, J.G. He, Z.H. Jiang, Q. Jiang, J.S. Lian

More information

The Corrosion Behavior of Sputter deposited Ternary Zr (12 18)Cr W Alloys in 12 M HCl Solution

The Corrosion Behavior of Sputter deposited Ternary Zr (12 18)Cr W Alloys in 12 M HCl Solution The Corrosion Behavior of Sputter deposited Ternary Zr (12 18)Cr W Alloys in 12 M HCl Solution Jagadeesh Bhattarai * Central Department of Chemistry, Tibhuvan University, GPO Box 2040, Kathmandu, Nepal

More information

The Composition of the Rare Earth Based Conversion Coating Formed on AZ91D Magnesium Alloy

The Composition of the Rare Earth Based Conversion Coating Formed on AZ91D Magnesium Alloy CORROSION SCIENCE AND TECHNOLOGY, Vol.17, No.1(2018), pp.1~5 pissn: 1598-6462 / eissn: 2288-6524 [Research Paper] DOI: https://doi.org/10.14773/cst.2018.17.1.1 The Composition of the Rare Earth Based Conversion

More information

CORROSION PROPERTIES OF CERMET COATINGS SPRAYED BY HIGH-VELOCITY OXYGEN-FUEL. Dragos UŢU, Iosif HULKA, Viorel-Aurel ŞERBAN, Hannelore FILIPESCU

CORROSION PROPERTIES OF CERMET COATINGS SPRAYED BY HIGH-VELOCITY OXYGEN-FUEL. Dragos UŢU, Iosif HULKA, Viorel-Aurel ŞERBAN, Hannelore FILIPESCU Abstract CORROSION PROPERTIES OF CERMET COATINGS SPRAYED BY HIGH-VELOCITY OXYGEN-FUEL Dragos UŢU, Iosif HULKA, Viorel-Aurel ŞERBAN, Hannelore FILIPESCU Politehnica University of Timisoara, Romania, dragosutu@yahoo.com,

More information

ELECTROCHEMICAL SYNTHESIS OF POLYPYRROLE (PPy) and PPy METAL COMPOSITES ON COPPER and INVESTIGATION OF THEIR ANTICORROSIVE PROPERTIES

ELECTROCHEMICAL SYNTHESIS OF POLYPYRROLE (PPy) and PPy METAL COMPOSITES ON COPPER and INVESTIGATION OF THEIR ANTICORROSIVE PROPERTIES ELECTROCHEMICAL SYNTHESIS OF POLYPYRROLE (PPy) and PPy METAL COMPOSITES ON COPPER and INVESTIGATION OF THEIR ANTICORROSIVE PROPERTIES Sibel Zor, Hatice Özkazanç Kocaeli University, Department of Chemistry,

More information

Stability of Surface Films Formed on Mg by Exposure Aqueous Solutions

Stability of Surface Films Formed on Mg by Exposure Aqueous Solutions Stability of Surface Films Formed on Mg by Exposure Aqueous Solutions By: Mehdi Taheri Supervisor: Dr. Joseph Kish Walter W. Smeltzer Corrosion Lab McMaster University 1 2 nd MSE 702 Graduate Seminar Sept

More information

Characterization of Oxide Film Formed on Ck45 Steel by Plasma Electrolytic Oxidation Method

Characterization of Oxide Film Formed on Ck45 Steel by Plasma Electrolytic Oxidation Method Journal of Mechanical Research and Application ISSN: 2251-7383, eissn: 2251-7391 Vol. 4, No. 2, 2012, 57-61 Characterization of Oxide Film Formed on Ck45 Steel by Plasma Electrolytic Oxidation Method JMRA

More information

School of Marine Science and Technology, Harbin Institute of Technology, Weihai , China;

School of Marine Science and Technology, Harbin Institute of Technology, Weihai , China; Int. J. Electrochem. Sci., 7 (2012) 8337-8355 International Journal of ELECTROCHEMICAL SCIENCE www.electrochemsci.org The Deposition Process and the Properties of Direct Electroless Nickel-Phosphorous

More information

Zn Ni alloy coatings pulse-plated on magnesium alloy

Zn Ni alloy coatings pulse-plated on magnesium alloy Surface & Coatings Technology 191 (2005) 393 399 www.elsevier.com/locate/surfcoat Zn Ni alloy coatings pulse-plated on magnesium alloy Y.F. Jiang*, C.Q. Zhai, L.F. Liu, Y.P. Zhu, W.J. Ding National Engineering

More information

on Electrochemical Etching of Pure Aluminium Foil for Aluminium Electrolytic Capacitor

on Electrochemical Etching of Pure Aluminium Foil for Aluminium Electrolytic Capacitor Volume 6 Paper C145 Effect of SO 4 2-, S 2 O 2-3 and HSO - 4 Ion Additives on Electrochemical Etching of Pure Aluminium Foil for Aluminium Electrolytic Capacitor S.-I. Pyun and K.-H. Na Dept. Mat. Sci.

More information

Lightweight Materials for Applications

Lightweight Materials for Applications Protection of Magnesium Alloys as Lightweight Materials for Applications in the Aerospace Industry Lénia M. Calado 1, Maryna Taryba 1, Maria J. Carmezim 1,2, M. Fátima Montemor 1 1 CQE, DEQ, Instituto

More information

Microstructure and Corrosion Resistance Property of a Zn-Al-Mg Alloy with Different Solidification Processes

Microstructure and Corrosion Resistance Property of a Zn-Al-Mg Alloy with Different Solidification Processes MATEC Web of Conferences 109, 0100 (2017) DOI: 10.1051/ matecconf/20171090100 Microstructure and Corrosion Resistance Property of a Zn-Al-Mg Alloy with Different Solidification Processes Guang-rui Jiang

More information

Preparation of porous manganese hydroxide film and its application in supercapacitors

Preparation of porous manganese hydroxide film and its application in supercapacitors Indian Journal of Chemistry Vol. 46A, May 2007, pp. 736-741 Preparation of porous manganese hydroxide film and its application in supercapacitors Zhen Fan, Jinhua Chen*, Feng Sun, Lei Yang, Yan Xu & Yafei

More information

Formation mechanism of new corrosion resistance magnesium thin films by PVD method

Formation mechanism of new corrosion resistance magnesium thin films by PVD method Surface and Coatings Technology 169 170 (2003) 670 674 Formation mechanism of new corrosion resistance magnesium thin films by PVD method a, a a a b M.H. Lee *, I.Y. Bae, K.J. Kim, K.M. Moon, T. Oki a

More information

Three-dimensional NiFe Layered Double Hydroxide Film for Highefficiency

Three-dimensional NiFe Layered Double Hydroxide Film for Highefficiency Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2014 Three-dimensional NiFe Layered Double Hydroxide Film for Highefficiency Oxygen Evolution Reaction

More information

Electrodeposition and Properties of ZnFeNi Alloys. Ismail Hakki Karahan

Electrodeposition and Properties of ZnFeNi Alloys. Ismail Hakki Karahan CHINESE JOURNAL OF PHYSICS VOL. 46, NO. 1 FEBRUARY 2008 Electrodeposition and Properties of ZnFeNi Alloys Ismail Hakki Karahan Department of Physics, Faculty of Science and Arts, Kilis 7 Aralik Universty,

More information

Kinetic Characteristics of Different Materials used for Bolting Applications

Kinetic Characteristics of Different Materials used for Bolting Applications Kinetic Characteristics of Different Materials used for Bolting Applications Report Kinetic Characteristics of Different Materials used for Bolting Applications Overview One of the most common problems

More information

Preparation and Corrosion Resistance of Electroless Ni-P Coating on Open-Cell Aluminum Foams

Preparation and Corrosion Resistance of Electroless Ni-P Coating on Open-Cell Aluminum Foams Int. J. Electrochem. Sci., 7 (2012) 5951-5961 International Journal of ELECTROCHEMICAL SCIENCE www.electrochemsci.org Preparation and Corrosion Resistance of Electroless Ni-P Coating on Open-Cell Aluminum

More information

FORMATION OF TiO 2 THIN FILM BY ION-BEAM-MIXING METHOD AND ITS APPLICATION AS THE CORROSION PROTECTING FILM

FORMATION OF TiO 2 THIN FILM BY ION-BEAM-MIXING METHOD AND ITS APPLICATION AS THE CORROSION PROTECTING FILM ORAL REFERENCE:ICF100266OR FORMATION OF TiO 2 THIN FILM BY ION-BEAM-MIXING METHOD AND ITS APPLICATION AS THE CORROSION PROTECTING FILM Yuji KIMURA 1 and Hirotsugu SAITO 1 1 Dept. of Materials Science and

More information

Galvanic Corrosion of a Zn/steel Couple in Aqueous NaCl

Galvanic Corrosion of a Zn/steel Couple in Aqueous NaCl , pp. 1882 1889 Galvanic Corrosion of a Zn/steel Couple in Aqueous NaCl Eiji TADA 1) * and Hiroyuki KANEKO 2) 1) Department of Materials Science and Engineering, Graduate School of Engineering and Resource

More information

Optimized by Disorder Engineering on Iron doped Ni 3 S 2. nanosheets for Oxygen Evolution Reaction

Optimized by Disorder Engineering on Iron doped Ni 3 S 2. nanosheets for Oxygen Evolution Reaction Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2018 Supplementary Data Optimized by Disorder Engineering on Iron doped Ni 3 S 2 nanosheets for Oxygen

More information

Development of Environmentally Friendly Silica-Based Conversion Coatings for Zn-Ni Alloys

Development of Environmentally Friendly Silica-Based Conversion Coatings for Zn-Ni Alloys Development of Environmentally Friendly Silica-Based Conversion Coatings for Zn-Ni Alloys James F. O Keefe Vanderbilt University Advisor: Dr. Branko N. Popov, Dr. Prabhu Ganesan July 26 th, 2007 Corrosion

More information

Corrosion Protect DLC Coating on Steel and Hastelloy

Corrosion Protect DLC Coating on Steel and Hastelloy Materials Transactions, Vol. 49, No. 6 (2008) pp. 1333 to 1337 #2008 The Japan Institute of Metals Corrosion Protect DLC Coating on Steel and Hastelloy Hironobu Miya and Jie Wang Semiconductor Equipment

More information

Influences of current density on structure and corrosion resistance of ceramic coatings on Ti 6Al 4V alloy by micro-plasma oxidation

Influences of current density on structure and corrosion resistance of ceramic coatings on Ti 6Al 4V alloy by micro-plasma oxidation Thin Solid Films 468 (2004) 120 124 www.elsevier.com/locate/tsf Influences of current density on structure and corrosion resistance of ceramic coatings on Ti 6Al 4V alloy by micro-plasma oxidation Zhongping

More information

Hydrogen Permeation of Pipeline Steel under Sour Condensate Film Condition

Hydrogen Permeation of Pipeline Steel under Sour Condensate Film Condition Hydrogen Permeation of Pipeline Steel under Sour Condensate Film Condition Zhaoyang Cui, Lei Zhang, Yanni Sun, Rufei Ma, Mingliang Liu and Minxu Lu Institute of Advanced Materials and Technology, University

More information

Roles of Alloying Elements on the Corrosion Behavior of Amorphous W Zr (15 33)Cr Alloys in 1 M NaOH Solution

Roles of Alloying Elements on the Corrosion Behavior of Amorphous W Zr (15 33)Cr Alloys in 1 M NaOH Solution Roles of Alloying Elements on the Corrosion Behavior of Amorphous W Zr (15 33)Cr Alloys in 1 M NaOH Solution Raju Ram Kumal and Jagadeesh Bhattarai * Central Department of Chemistry, Tribhuvan University,

More information

Galvanic Corrosion Between AISI304 Stainless Steel and Carbon Steel in Chloride Contaminated Mortars

Galvanic Corrosion Between AISI304 Stainless Steel and Carbon Steel in Chloride Contaminated Mortars Int. J. Electrochem. Sci., 11 (216) 5226 5233, doi: 1.2964/216.6.24 International Journal of ELECTROCHEMICAL SCIENCE www.electrochemsci.org Galvanic Corrosion Between AISI34 Stainless Steel and Carbon

More information

Alkaline Rechargeable Ni/Co Batteries: Cobalt Hydroxides as. Negative Electrode Materials

Alkaline Rechargeable Ni/Co Batteries: Cobalt Hydroxides as. Negative Electrode Materials Supplementary Information: Alkaline Rechargeable Ni/Co Batteries: Cobalt Hydroxides as Negative Electrode Materials X. P. Gao, S. M. Yao, T. Y. Yan, Z. Zhou Institute of New Energy Material Chemistry,

More information

Corrosion of an aluminum alloy chilled in flowing seawater. and the effect of cathodic prevention

Corrosion of an aluminum alloy chilled in flowing seawater. and the effect of cathodic prevention Corrosion of an aluminum alloy chilled in flowing seawater and the effect of cathodic prevention Akihiro Yabuki *, David T. Yasunaga a, Toshihiro Shibutani b, Koichi Shinkai b * Graduate School of Engineering,

More information

Novel concept of rechargeable battery using iron oxide nanorods. anode and nickel hydroxide cathode in aqueous electrolyte

Novel concept of rechargeable battery using iron oxide nanorods. anode and nickel hydroxide cathode in aqueous electrolyte Supplementary Information for: Novel concept of rechargeable battery using iron oxide nanorods anode and nickel hydroxide cathode in aqueous electrolyte Zhaolin Liu *, Siok Wei Tay and Xu Li Institute

More information

Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloys with 14H Long Period Ordered Structure

Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloys with 14H Long Period Ordered Structure Materials Transactions, Vol. 47, No. 4 (2006) pp. 959 to 965 Special Issue on Platform Science and Technology for Advanced Magnesium Alloys, III #2006 The Japan Institute of Light Metals Microstructure

More information

Corrosion behavior of silicon nitride bonding silicon carbide in molten magnesium and AZ91 magnesium alloy

Corrosion behavior of silicon nitride bonding silicon carbide in molten magnesium and AZ91 magnesium alloy Materials Science and Engineering A 45 (2006) 29 296 Corrosion behavior of silicon nitride bonding silicon carbide in molten magnesium and AZ9 magnesium alloy Hukui Chen, Jianrui Liu, Weidong Huang State

More information

Corrosion Behavior of Cu Zr Ti Nb Bulk Glassy Alloys

Corrosion Behavior of Cu Zr Ti Nb Bulk Glassy Alloys Materials Transactions, Vol. 44, No. 4 (3 pp. 749 to 753 #3 The Japan Institute of Metals Corrosion Behavior of Cu Bulk Glassy Alloys Chunling Qin 1; *, Katsuhiko Asami 1, Tao Zhang 1, Wei Zhang 2 and

More information

Novel Mn 1.5 Co 1.5 O 4 spinel cathodes for intermediate temperature solid oxide fuel cells

Novel Mn 1.5 Co 1.5 O 4 spinel cathodes for intermediate temperature solid oxide fuel cells Novel Mn 1.5 Co 1.5 O 4 spinel cathodes for intermediate temperature solid oxide fuel cells Huanying Liu, a, b Xuefeng Zhu, a * Mojie Cheng, c You Cong, a Weishen Yang a * a State Key Laboratory of Catalysis,

More information

Supporting Information

Supporting Information Supporting Information Enhanced Oxygen Evolution Reaction Electrocatalysis via Electrodeposited Amorphous α Phase Nickel-Cobalt Hydroxide Nanodendrite Forests By Anirudh Balram, Hanfei Zhang, and Sunand

More information

Corrosion behavior of Al Si Cu (Sn, Zn) brazing filler metals

Corrosion behavior of Al Si Cu (Sn, Zn) brazing filler metals Materials Characterization 47 (2001) 401 409 Corrosion behavior of Al Si Cu (Sn, Zn) brazing filler metals S.S. Wang, M.D. Cheng, L.C. Tsao, T.H. Chuang* Institute of Materials Science and Engineering,

More information

Microstructures & Properties Changes Induced by Nitrogen Ion Implantation on Chromium Films

Microstructures & Properties Changes Induced by Nitrogen Ion Implantation on Chromium Films International Journal of ChemTech Research CODEN( USA): IJCRGG ISSN : 09744290 Vol. 3, No.1, pp 9313, JanMar 11 Microstructures & Properties Changes Induced by Nitrogen Ion Implantation on Chromium Films

More information

The Effect of Calcium Nitrite on the Electrochemical Characterization of 3003 Aluminum Alloys in Sea Water. H.Mogawer and R.Brown

The Effect of Calcium Nitrite on the Electrochemical Characterization of 3003 Aluminum Alloys in Sea Water. H.Mogawer and R.Brown The Effect of Calcium Nitrite on the Electrochemical Characterization of 3003 Aluminum Alloys in Sea Water H.Mogawer and R.Brown Department of Chemical Engineering, University of Rhode Island, Kingston,

More information

MICROSTRUCTURE AND CORROSION RESISTANCE OF ELECTRODEPOSITED Zn-Ni-P THIN FILMS

MICROSTRUCTURE AND CORROSION RESISTANCE OF ELECTRODEPOSITED Zn-Ni-P THIN FILMS U.P.B. Sci. Bull., Series B, Vol. 78, Iss. 1, 2016 ISSN 1454-2331 MICROSTRUCTURE AND CORROSION RESISTANCE OF ELECTRODEPOSITED Zn-Ni-P THIN FILMS Ionuţ CONSTANTIN 1, Petru MOLDOVAN 2 Ternary Zn-Ni-P alloy

More information

Bonding strength of Al/Mg/Al alloy tri-metallic laminates fabricated

Bonding strength of Al/Mg/Al alloy tri-metallic laminates fabricated Bull. Mater. Sci., Vol. 34, No. 4, July 2011, pp. 805 810. Indian Academy of Sciences. Bonding strength of Al/Mg/Al alloy tri-metallic laminates fabricated by hot rolling X P ZHANG, *, M J TAN, T H YANG,

More information

This article appeared in a journal published by Elsevier. The attached copy is furnished to the author for internal non-commercial research and

This article appeared in a journal published by Elsevier. The attached copy is furnished to the author for internal non-commercial research and This article appeared in a journal published by Elsevier. The attached copy is furnished to the author for internal non-commercial research and education use, including for instruction at the authors institution

More information

Mechanism of Corrosion Protection of Anodized Magnesium Alloys

Mechanism of Corrosion Protection of Anodized Magnesium Alloys Materials Transactions, Vol. 49, No. 5 (2008) pp. 1057 to 1064 Special Issue on Platform Science and Technology for Advanced Magnesium Alloys, IV #2008 The Japan Institute of Metals Mechanism of Corrosion

More information

ELECTROCHEMICAL AND SPONTANEOUS PASSIVATION OF THE CoCr ALLOY AS CORROSION PROTECTION

ELECTROCHEMICAL AND SPONTANEOUS PASSIVATION OF THE CoCr ALLOY AS CORROSION PROTECTION Applied Engineering Letters Vol. 2, No. 1, 43-47 (2017) e-issn: 2466-4847 ELECTROCHEMICAL AND SPONTANEOUS PASSIVATION OF THE CoCr ALLOY AS CORROSION PROTECTION Łukasz Reimann 1 1 Silesian University of

More information

Corrosion resistance of Au/Ni thin films coated stainless steel used for a PEFC separator

Corrosion resistance of Au/Ni thin films coated stainless steel used for a PEFC separator Materials Characterisation VI 217 Corrosion resistance of Au/Ni thin films coated stainless steel used for a PEFC separator Y. Kimura 1 & M. Hirano 2 1 Department of Environmental and Energy Chemistry,

More information

Research Article The Corrosion Behavior of Carburized Aluminum Using DC Plasma

Research Article The Corrosion Behavior of Carburized Aluminum Using DC Plasma Metallurgy Volume 212, Article ID 25821, 4 pages doi:1.1155/212/25821 Research Article The Corrosion Behavior of Carburized Aluminum Using DC Plasma Somayeh Pirizadhejrandoost, Mehdi Bakhshzad Mahmoudi,

More information

Effect of Chloride on Localized Corrosion Initiation of Carbon Steel in a CO 2 Aqueous Environment Xin Gao, Bruce Brown, Srdjan Nesic

Effect of Chloride on Localized Corrosion Initiation of Carbon Steel in a CO 2 Aqueous Environment Xin Gao, Bruce Brown, Srdjan Nesic Paper No. 3880 Effect of Chloride on Localized Corrosion Initiation of Carbon Steel in a CO 2 Aqueous Environment Xin Gao, Bruce Brown, Srdjan Nesic Institute for Corrosion and Multiphase Technology Ohio

More information

Microstructural Evolution of Ti-Mo-Ni-C Powder by Mechanical Alloying

Microstructural Evolution of Ti-Mo-Ni-C Powder by Mechanical Alloying Materials Transactions, Vol. 50, No. 1 (2009) pp. 117 to 122 #2009 The Japan Institute of Metals Microstructural Evolution of -Mo-Ni-C Powder by Mechanical Alloying Hiroyuki Hosokawa, Kiyotaka Kato, Koji

More information

A Zinc and Manganese Phosphate Coating on Automobile Iron Castings

A Zinc and Manganese Phosphate Coating on Automobile Iron Castings , pp. 1326 1330 A Zinc and Manganese Phosphate Coating on Automobile Iron Castings G.-Y. LI, J.-S. LIAN, L.-Y. NIU and Z.-H. JIANG Key Laboratory of Automobile Materials, Ministry of Education, College

More information

CORROSION BEHAVIOUR OF COATED HOLLOW SPHERES IN ACETATE BUFFER WITH KCl

CORROSION BEHAVIOUR OF COATED HOLLOW SPHERES IN ACETATE BUFFER WITH KCl Powder Metallurgy Progress, Vol.7 (2007), No 2 103 CORROSION BEHAVIOUR OF COATED HOLLOW SPHERES IN ACETATE BUFFER WITH KCl A. Fedorková, R. Oriňáková, M. Kupková, E. Dudrová, M. Kabátová Abstract The potentiodynamic

More information

Corrosion Rate Measurement on C-Steel

Corrosion Rate Measurement on C-Steel Measurements of corrosion rate on Carbon-steel using Electrochemical (potentiodynamic Polarization, EIS etc.) technique. Corrosion Rate Measurement on C-Steel Abdullah Al Ashraf 1. Introduction: The degradation

More information

CHAPTER 2 MATERIALS AND METHODS

CHAPTER 2 MATERIALS AND METHODS 37 CHAPTER 2 MATERIALS AND METHODS This chapter discusses the methodology adopted for the development of zinc phosphate coating utilizing galvanic coupling and to evaluate the effect of cathode materials

More information

A Comparative Study on Zn and Zn-Y Coatings on 42CrMo Steel by Pack Cementation Process

A Comparative Study on Zn and Zn-Y Coatings on 42CrMo Steel by Pack Cementation Process Int. J. Electrochem. Sci., 12 (2017) 9575 9587, doi: 10.20964/2017.10.22 International Journal of ELECTROCHEMICAL SCIENCE www.electrochemsci.org A Comparative Study on Zn and Zn-Y Coatings on 42CrMo Steel

More information

6th International Conference on Advanced Design and Manufacturing Engineering (ICADME 2016)

6th International Conference on Advanced Design and Manufacturing Engineering (ICADME 2016) 6th International Conference on Advanced Design and Manufacturing Engineering (ICADME 2016) Porous Co3O4 irregular Micro-cubes with lithium storage performances Ting Wanga, Hao Zhengb, Jinsong Chengc,

More information

Electrochemical study on magnesium anodes in NaCl and CaSO 4 Mg(OH) 2 aqueous solutions

Electrochemical study on magnesium anodes in NaCl and CaSO 4 Mg(OH) 2 aqueous solutions Electrochimica Acta xxx (2005) xxx xxx Electrochemical study on magnesium anodes in NaCl and CaSO 4 Mg(OH) 2 aqueous solutions Fidel Guadarrama-Muñoz a, Juan Mendoza-Flores a, Ruben Duran-Romero a, J.

More information

DEVELOPMENT OF ELECTROLESS PROCESS FOR DEPOSITION OF ZN SILICATE COATINGS

DEVELOPMENT OF ELECTROLESS PROCESS FOR DEPOSITION OF ZN SILICATE COATINGS REPORT OF THE FINAL PROJECT ENTITLED: DEVELOPMENT OF ELECTROLESS PROCESS FOR DEPOSITION OF ZN SILICATE COATINGS by Veeraraghavan S Basker Department of Chemical Engineering University of South Carolina

More information

CORROSION BEHAVIOR OF LASER SURFACE MELTED 2014 ALUMINIUM ALLOY IN T6 AND T451 TEMPERS. P.H. Chong*, Z. Liu, P. Skeldon and G. E.

CORROSION BEHAVIOR OF LASER SURFACE MELTED 2014 ALUMINIUM ALLOY IN T6 AND T451 TEMPERS. P.H. Chong*, Z. Liu, P. Skeldon and G. E. CORROSION BEHAVIOR OF LASER SURFACE MELTED 2014 ALUMINIUM ALLOY IN T6 AND T451 TEMPERS P.H. Chong*, Z. Liu, P. Skeldon and G. E. Thompson Corrosion and Protection Centre, University of Manchester Institute

More information

CORROSION PROTECTION OF IRON USING COMPOSITE COATINGS BASED ON ZINC AND ZINC ALLOYS

CORROSION PROTECTION OF IRON USING COMPOSITE COATINGS BASED ON ZINC AND ZINC ALLOYS MK0400057 CORROSION PROTECTION OF IRON USING COMPOSITE COATINGS BASED ON. CORROSION PROTECTION OF IRON USING COMPOSITE COATINGS BASED ON ZINC AND ZINC ALLOYS G. Raichevski*, N. Boshkov*, D. Koleva*, Ch.

More information

Phase Formation in Gold-Tin Alloys Electroplated from a Non-cyanide Bath

Phase Formation in Gold-Tin Alloys Electroplated from a Non-cyanide Bath Phase Formation in Gold-Tin Alloys Electroplated from a Non-cyanide Bath Yahui Zhang and Douglas G. Ivey Department of Chemical and Materials Engineering, University of Alberta, Edmonton, Alberta, Canada

More information

LASER SURFACE MELTING OF 17-4 PH PRECIPITATION-HARDENABLE STAINLESS STEEL Paper 1203

LASER SURFACE MELTING OF 17-4 PH PRECIPITATION-HARDENABLE STAINLESS STEEL Paper 1203 LASER SURFACE MELTING OF 7- PH PRECIPITATION-HARDENABLE STAINLESS STEEL Paper 0 Zhichao Cheng, Chi Tat Kwok, Kin Ho Lo, Department of Electromechanical Engineering, University of Macau, Taipa, Macau Abstract

More information

Investigation of Stress Corrosion Cracking Behaviors of an AZ91 Magnesium Alloy in 0.1 kmol/m 3 Na 2 SO 4 Solution Using Slow Strain Rate Test

Investigation of Stress Corrosion Cracking Behaviors of an AZ91 Magnesium Alloy in 0.1 kmol/m 3 Na 2 SO 4 Solution Using Slow Strain Rate Test Materials Transactions, Vol. 49, No. 5 (2008) pp. 1052 to 1056 Special Issue on Platform Science and Technology for Advanced Magnesium Alloys, IV #2008 The Japan Institute of Metals Investigation of Stress

More information

Surface & Coatings Technology

Surface & Coatings Technology Surface & Coatings Technology 203 (2009) 1107 1113 Contents lists available at ScienceDirect Surface & Coatings Technology journal homepage: www.elsevier.com/locate/surfcoat A novel phosphate conversion

More information

Effect of Amorphous Transformation on Electrochemical Capacities of Rare Earth Mg Based Alloys

Effect of Amorphous Transformation on Electrochemical Capacities of Rare Earth Mg Based Alloys Z. Phys. Chem. 220 (2006) 631 639 / DOI 10.1524/zpch.2006.220.5.631 by Oldenbourg Wissenschaftsverlag, München Effect of Amorphous Transformation on Electrochemical Capacities of Rare Earth Mg Based Alloys

More information

Performance Evaluation of Zinc Deposited Mild Steel in Chloride Medium.

Performance Evaluation of Zinc Deposited Mild Steel in Chloride Medium. Int. J. Electrochem. Sci., 6 (2011) 3254-3263 International Journal of ELECTROCHEMICAL SCIENCE www.electrochemsci.org Performance Evaluation of Zinc Deposited Mild Steel in Chloride Medium. Popoola A.P.I

More information

SIGNIFICANCE OF HYDROGEN EVOLUTION IN CATHODIC PROTECTION OF STEEL IN SEAWATER

SIGNIFICANCE OF HYDROGEN EVOLUTION IN CATHODIC PROTECTION OF STEEL IN SEAWATER SIGNIFICANCE OF HYDROGEN EVOLUTION IN CATHODIC PROTECTION OF STEEL IN SEAWATER Trine Okstad, Øyvind Rannestad, Roy Johnsen () and Kemal Nisancioglu Department of Materials Science and Engineering ( ()

More information

Synthesis, Characterization and Optical Properties of ZnS Thin Films

Synthesis, Characterization and Optical Properties of ZnS Thin Films Synthesis, Characterization and Optical Properties of ZnS Thin Films H. R. Kulkarni KJ College of Engineering and Management Research, Pune, India Abstract: ZnS thin films were prepared by pulsed electrodeposition

More information

The Electrochemical Behavior of Carbon Steel Wires of Nepal in Different Environments

The Electrochemical Behavior of Carbon Steel Wires of Nepal in Different Environments The Electrochemical Behavior of Carbon Steel Wires of Nepal in Different Environments Jagadeesh Bhattarai * Central Department of Chemistry, Tribhuvan University, GPO Box 2040, Kathmandu, Nepal. e-mail:bhattarai_05@yahoo.com.

More information

Leena Das and Der-Tau Chin Department of Chemical Engineering, Clarkson University Potsdam, New York

Leena Das and Der-Tau Chin Department of Chemical Engineering, Clarkson University Potsdam, New York EFFECT OF MICROSTRUCTURE OF FERROUS SUBSTRATE ON POROSITY OF ELECTROLESS NICKEL COATING Leena Das and Der-Tau Chin Department of Chemical Engineering, Clarkson University Potsdam, New York 13699-575 1

More information

Investigation of Formation Process of the Chrome-free Passivation Film of Electrodeposited Zinc

Investigation of Formation Process of the Chrome-free Passivation Film of Electrodeposited Zinc Chinese Journal of Aeronautics 20(2007) 129-133 Chinese Journal of Aeronautics www.elsevier.com/locate/cja Investigation of Formation Process of the Chrome-free Passivation Film of Electrodeposited Zinc

More information

Short Communication Effect of a High Concentration of Chloride Ions on the Corrosion Behaviour of X80 Pipeline Steel in 0.5 mol L -1 NaHCO 3 Solutions

Short Communication Effect of a High Concentration of Chloride Ions on the Corrosion Behaviour of X80 Pipeline Steel in 0.5 mol L -1 NaHCO 3 Solutions Int. J. Electrochem. Sci., 13 (2018) 1283 1292, doi: 10.20964/2018.02.03 International Journal of ELECTROCHEMICAL SCIENCE www.electrochemsci.org Short Communication Effect of a High Concentration of Chloride

More information

Studies on the in uence of chloride ion and ph on the corrosion and electrochemical behaviour of AZ91D magnesium alloy

Studies on the in uence of chloride ion and ph on the corrosion and electrochemical behaviour of AZ91D magnesium alloy Journal of Applied Electrochemistry 30: 865±874, 2000. 865 Ó 2000 Kluwer Academic Publishers. Printed in the Netherlands. Studies on the in uence of chloride ion and ph on the corrosion and electrochemical

More information

COATING OF ALUMINUM ALLOYS BY MICRO ARC OXIDATION IN NITRATE SALT

COATING OF ALUMINUM ALLOYS BY MICRO ARC OXIDATION IN NITRATE SALT COATING OF ALUMINUM ALLOYS BY MICRO ARC OXIDATION IN NITRATE SALT Alexander Sobolev, Alexey Kossenko, Michael Zinigrad, Konstantin Borodianskiy Zimin Advanced Materials Laboratory, Department of Chemical

More information

Effect of Continuous Rotation Evolutional Control on the Pitting Corrosion Resistance of Anodized Aluminum-Magnesium Alloy* 1

Effect of Continuous Rotation Evolutional Control on the Pitting Corrosion Resistance of Anodized Aluminum-Magnesium Alloy* 1 Materials Transactions, Vol. 5, No. 8 (29) pp. 1985 to 1991 #29 The Japan Institute of Metals Effect of Continuous Rotation Evolutional Control on the Pitting Corrosion Resistance of Anodized Aluminum-Magnesium

More information

IOP Conference Series: Earth and Environmental Science PAPER OPEN ACCESS

IOP Conference Series: Earth and Environmental Science PAPER OPEN ACCESS IOP Conference Series: Earth and Environmental Science PAPER OPEN ACCESS Influence of anodizing concentration and electric potential on surface morphology and corrosion behavior of anodized magnesium in

More information

The Influence of Critical Flow Velocity on Corrosion of Stainless Steel

The Influence of Critical Flow Velocity on Corrosion of Stainless Steel J Fail. Anal. and Preven. (2017) 17:4 1240 DOI 10.1007/s11668-017-0369-1 TECHNICAL ARTICLE PEER-REVIEWED The Influence of Critical Flow Velocity on Corrosion of Stainless Steel Zhen Li. Jiding Zhang. Jiarui

More information

Supporting Information for. Exploring a wider range of Mg-Ca-Zn metallic glass as biocompatible alloys using combinatorial sputtering

Supporting Information for. Exploring a wider range of Mg-Ca-Zn metallic glass as biocompatible alloys using combinatorial sputtering Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2017 Supporting Information for Exploring a wider range of Mg-Ca-Zn metallic glass as biocompatible

More information

Effects of zincate treatment on adhesion of electroless Ni-P coating onto various aluminum alloys

Effects of zincate treatment on adhesion of electroless Ni-P coating onto various aluminum alloys Effects of zincate treatment on adhesion of electroless Ni-P coating onto various aluminum alloys Makoto HINO 1, Koji MURAKAMI 1, Yutaka MITOOKA 1, Ken MURAOKA 1, Teruto KANADANI 2 1. Industrial Technology

More information

Effect of melt temperature on the oxidation behavior of AZ91D magnesium alloy in 1,1,1,2-tetrafluoroethane/air atmospheres

Effect of melt temperature on the oxidation behavior of AZ91D magnesium alloy in 1,1,1,2-tetrafluoroethane/air atmospheres available at www.sciencedirect.com www.elsevier.com/locate/matchar Effect of melt temperature on the oxidation behavior of AZ91D magnesium alloy in 1,1,1,2-tetrafluoroethane/air atmospheres Hukui Chen

More information

Evaluation of Corrosion Resistance of Anodized Aluminum by Polarization Resistance Method

Evaluation of Corrosion Resistance of Anodized Aluminum by Polarization Resistance Method Technical Paper Boshoku Gijutsu, 34,265-269 (1981) UDC 669.716.9:620.19 541.135.6 Evaluation of Corrosion Resistance of Anodized Aluminum by Polarization Resistance Method Phan Trung Thanh*, Akiyane Akiyama*

More information

Applied Surface Science

Applied Surface Science Applied Surface Science 255 (2009) 4192 4196 Contents lists available at ScienceDirect Applied Surface Science journal homepage: www.elsevier.com/locate/apsusc Electrodeposited ruthenium oxide thin films

More information

Physiochemical Characterization of Sn-Zn Coatings Electrodeposited from an Acidic Chloride Bath in the Absence of Complexing Agent

Physiochemical Characterization of Sn-Zn Coatings Electrodeposited from an Acidic Chloride Bath in the Absence of Complexing Agent International Journal of Current Science, Engineering & Technology Original Research Article Open Access AMCT 2017 Malaysia Special Issue ISSN : 2581-4311 Physiochemical Characterization of Sn-Zn Coatings

More information

What happens if we connect Zn and Pt in HCl solution? Corrosion of platinum (Pt) in HCl. 1. If Zn and Pt are not connected

What happens if we connect Zn and Pt in HCl solution? Corrosion of platinum (Pt) in HCl. 1. If Zn and Pt are not connected Corrosion of platinum (Pt) in HCl Now if we place a piece of Pt in HCl, what will happen? Pt does not corrode does not take part in the electrochemical reaction Pt is a noble metal Pt acts as a reference

More information

Some Corrosion Characteristics of Aged Aluminum Alloy 6061 in Neutral and Alkaline Solutions

Some Corrosion Characteristics of Aged Aluminum Alloy 6061 in Neutral and Alkaline Solutions Some Corrosion Characteristics of Aged Aluminum Alloy 6061 in Neutral and Alkaline Solutions K.El-Menshawy 1, A.A.El-Sayed 1, M.E.El-Bedawy 1, H. A.Ahmed 2 and S.M.El-Raghy 2 1- Metallurgy Department,

More information

Electroless plating of Cu Ni P alloy on PET fabrics and effect of plating parameters on the properties of conductive fabrics

Electroless plating of Cu Ni P alloy on PET fabrics and effect of plating parameters on the properties of conductive fabrics Journal of Alloys and Compounds 455 (2008) 308 313 Electroless plating of Cu Ni P alloy on PET fabrics and effect of plating parameters on the properties of conductive fabrics Xueping Gan, Yating Wu, Lei

More information

Hydrothermal Synthesis of CoWO4 as Active Material for Supercapacitor Electrode

Hydrothermal Synthesis of CoWO4 as Active Material for Supercapacitor Electrode , pp.409-413 http://dx.doi.org/10.14257/astl.2016.139.81 Hydrothermal Synthesis of CoWO4 as Active Material for Supercapacitor Electrode Vaibhav Lokhande 1, Taeksoo Ji 1 * 1 Department of Electronics and

More information

Membraneless Hydrogen Peroxide Micro Semi-Fuel Cell for Portable Applications

Membraneless Hydrogen Peroxide Micro Semi-Fuel Cell for Portable Applications Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2014 Electronic Supplementary Information for Membraneless Hydrogen Peroxide Micro Semi-Fuel Cell

More information

Corrosion Resistance of Plasma-Anodized AZ91 Mg Alloy in the Electrolyte with/without Potassium Fluoride

Corrosion Resistance of Plasma-Anodized AZ91 Mg Alloy in the Electrolyte with/without Potassium Fluoride Materials Transactions, Vol. 5, No. 3 (29) pp. 671 to 678 #29 The Japan Institute of Metals EXPRESS REGULAR ARTICLE Corrosion Resistance of Plasma-Anodized AZ91 Mg Alloy in the Electrolyte with/without

More information