Combined Microwave-Laser Processing for Sintering of Oxide Ceramics

Size: px
Start display at page:

Download "Combined Microwave-Laser Processing for Sintering of Oxide Ceramics"

Transcription

1 Combined Microwave-Laser Processing for Sintering of Oxide Ceramics Alexander S. Vanetsev 1, Vassily V. Lennikov 2 and Xerman de la Fuente Leis 2 1 Kurnakov Institute of General and Inorganic Chemistry RAS, Moscow, Russia 2 Instituto de Ciencia de Materiales de Aragon, Zaragoza, Spain The technique of combined microwave and laser treatment of samples was developed and used for preparation of dense ceramics of various oxide compounds, including individual oxides and multicomponent cobaltites and manganites. It was found that simultaneous application of microwave and laser irradiation allows shortening of sintering time by orders of magnitude and leads to the formation of dense (up to 99% relative density) ceramics with uniform grain size distribution. Introduction Microwave treatment possesses many advantages in comparison with conventional heating methods, including higher velocity of heating, homogeneity of heat distribution and lower power inputs [1]. One of the main problems of microwave treatment is the fact that many compounds, for example most dielectric materials, are poor microwave absorbers at room temperature. Previously we, as have other researchers dealing with microwave synthesis and sintering, have used either hybrid microwave heating with SiC, carbon, copper oxide, etc. as initial microwave absorbers [2], or we have used ex situ samples pre-heating in a conventional furnace. Both of these techniques have significant disadvantages. In the case of a hybrid microwave heating technique it is very hard to establish contributions of microwave heating on the one side and conventional heat transfer on the other. Also, contamination by the absorbing material is almost inevitable. On the other hand, pre-heating leads to unpredictable changes in temperature during sample transfer and therefore irreproducible results. Laser treatment also allows us to obtain a very high temperature (>3000 o C) in a rather tight heating zone. Unlike thermocouples, ceramic heaters, etc., laser beam use does not affect the distribution of the electromagnetic field in a microwave cavity and therefore cannot interfere with microwave heating. A combination of microwave treatment with laser treatment enables us to carry out in situ pre-heating of the sample to the desired temperature and enables us to control the sample condition throughout the entire heating process. In the present work we have developed a technique of combined microwave and laser treatment of samples and used it for preparation of dense ceramics of various oxide compounds, including iron oxide (Fe 2 O 3, test sample), zirconia (ZrO 2 ), multicomponent cobaltites for solid oxide fuel cells (La 0.6 Sr 0.4 Co 0.8 Fe 0.2 O z and Nd 0.6 Sr 0.4 Co 0.8 Fe 0.2 O z ) and CMR-manganites (La 0.6 Sr 0.4 MnO 3-z and Nd 0.6 Ba 0.4 MnO 3-z ). Technique As starting materials, corresponding metal nitrates (reagent grade) were used. Nitrates (or stoichiometric nitrate mixtures) were annealed at high temperatures (900 o C for most samples) in order to obtain oxide powders. Phase composition of the obtained powders was controlled by 32

2 Fig. 1. Device for simultaneous laser and microwave treatment. means of powder XRD-analysis. Only single phase powders were used for microwave-laser sintering. The resulting powders were ground in a planetary mill (700 RPM / 30 min.) with the addition of 1 mass % of polyvinyl alcohol as a plasticizer and then pressed into pellets of 8 mm diameter and 2 mm height using cold isostatic pressing. The device used for simultaneous laser and microwave treatment is shown in Fig. 1. We used a Balay 3WM 1918 domestic microwave oven (650 W, 2.45 GHz) and a Rofin-Sinar 2 - laser (300 W, wavelength = 10.6 m) with a parabolic focusing mirror. The laser beam was delivered to the sample through a copper attenuator by means of a system of copper mirrors. In the carrying out preliminary experiments the following regimes of laser operation were used: focused in the pulsed regime, focused in the continuous regime, defocused in the continuous regime. To determine optimal conditions the power of the laser and the impulse length in the pulsed regime varied. As a result of preliminary experiments, it was established that the continuous regime with the unfocussed beam is the optimal source of laser emission for sintering of ceramic materials. Samples were placed into the special container made of porous alumina (Fig. 2). In order to avoid the mechanical destruction of pellets in the beginning of the sintering process, the power of the laser smoothly increased from the minimum possible (5 W) to the working value with a velocity of 0.5 W/min. The power of microwave treatment was always 650 W, sintering temperature varied from 1000 to 1200 o C, and duration of the process of sintering varied from 15 to 90 minutes. Temperature of the samples was measured by means of a specially calibrated IRpyrometer. 33

3 Fig. 2. Container with sample under laser and microwave treatment. Results Experiments on sintering of iron oxide pellets allow us to establish that the optimal regime for treating the tablets of Fe 2 O 3 is 25 % of the maximum power of the laser. Subsequently the optimal power for treating the remaining substances was established by a similar method. The optimal power of the laser for ZrO 2 was found to be 20 % of the maximum; for manganites 20 %, and for cobaltites 25 %. This data could be an additional argument in favor of the use of a gas laser, since the effectiveness of the radiation absorption of diode and solid-state lasers is determined by the color of the treated substance. Study of the processes of densification of compacted powders of oxides (Fig. 3) allows us to establish that the optimal regime for sintering Fe 2 O 3 and manganites is 2 hours at 1100 o C; to achieve maximum density of cobaltite pellets, it is optimal to sinter samples for the same amount of time at 1,200 o C. These results are in the good agreement with the earlier-obtained data concerning sintering of these compounds under microwave treatment without the use of laser of processing. Fig. 4 shows the time dependence of densification of manganite samples at optimal temperature (1100 o C). A clear break of the curve can be seen after 60 min. of laser-microwave sintering. This break is indicative of the transition of the sintering process into its final stage, namely grain growth and curing of isolated porosity. The developed method of sintering is thus most likely optimal, and further increase of final ceramic density will be possible only through modification of the morphology of starting powder. However, in the case of sintering of cobaltites there is no such break of the densification curve, and therefore to obtain higher densities it is necessary to increase either the duration or the temperature of sintering. Unfortunately, for us it is not possible technically to increase the duration of the process, since the magnetron of microwave oven is not designed for such a long period of continuous operation. Comparing densification curves for manganites and cobaltites with those for zirconia and iron oxide, one can conclude that in contrast with microwave sintering without laser treatment 34

4 95 Sample relative density, % Fe 2 O 3 La 0.7 Sr 0.3 MnO 3 La 0.6 Sr 0.4 Co 0.8 Fe 0.2 O z 60 Duration of sintering min Temperature, o C Fig. 3. Temperature dependence of densification of oxide samples. [3], laser-microwave treatment is not very sensitive to electric conductivity of treated compounds. Evidently this effect is connected with the intensive heat supply from the laser beam, which largely neutralizes the difference in absorption of microwaves by different compounds. Thus, it is possible to note higher flexibility of the laser-microwave technique of sintering in comparison with microwave sintering without the application of additional treatment. Study of the microstructure of sintered samples allows us to establish that, similarly to pure microwave sintering, the process of grain growth during laser-microwave sintering is very slow and densification of samples is largely associated with grain gliding and grainboundary diffusion. In complete agreement with the data of geometric density measurements, it is possible to isolate three stages of the sintering process. During the first stage, formation of the isthmuses between the particles of sintered powder occurs. In this stage the shrinkage of the sample is small and occurs mostly due to reorientation and gliding of grains. In the second stage of sintering, we observe intensive binding of grains due to intergranular mass transfer. The second stage is characterized by the most rapid shrinkage of samples due to the removal of intergranular porosity. At this stage only a insignificant increase in grain size occurs. Of the greatest interest from the point of view of comparison of thermal, microwave, and lasermicrowave sintering is the third and final stage of the process of sintering, during which the final removal of porosity and grain-growth occurs. As is well known from literature [3-5], the specific effects of microwave processing consist of decreased velocity of grain growth due to an increase in the intergranular diffusion. It was found that under combined laser and microwave irradiation, the velocity of grain growth is also rather low. Generally we may conclude that microstructures of ceramics sintered under pure microwave and combined laser-microwave treatment are very 35

5 Sample relative density, % La 0.7 Sr 0.3 MnO 3 Nd 0.7 Ba 0.3 MnO Duration of sintering, min. Fig. 4. Time dependence of densification of manganite samples. Fig. 5. Microstructure of La 0.6 Sr 0.4 MnO 3-z sintered at 1100 o C for 2 hours. similar. Nevertheless, as is clearly seen from Fig. 5, using simultaneous laser and microwave actions it is possible to obtain ceramics, which are characterized by high density and high uniformity of microstructure. 36

6 Conclusion Techniques for simultaneous laser and microwave treatment of solid materials were developed. Using these techniques, samples of highly dense ceramics of individual (Fe 2 O 3, ZrO2) and multicomponent (manganites and cobaltites) oxides were synthesized. Results obtained allow us to draw conclusions about the expediency of utilizing simultaneous laser and microwave treatment for sintering highly dense ceramic materials with uniform microstructure. Acknowledgment. This work was supported by RFBR (grants no a and ofi_m) and by the Grant of the President of Russian Federation for Support of Young Scientists (MK ). References [5] E.T. Thostenson and T.-W. Chou, Microwave processing: fundamentals and applications, Composites: Part A, vol. 30, pp , [6] J. Wang, J. Binner, B. Vaidhyanathan, et al, Evidence for the microwave effect during hybrid sintering, J. Am. Ceram. Soc., vol. 89, no. 6, pp , [7] A. Goldstein and M. Kravchik, Sintering of PZT powders in microwave furnace at 2.45 GHz, J. Eur. Ceram. Soc., vol. 19, pp , [8] Microwave processing of materials, D.E. Stein, Ed., National Academy Press, Washington, DC., [9] A.S. Vanetsev and Yu.D. Tretyakov, Microwave-assisted synthesis of individual and multicomponent oxides, Russ. Chem. Rev., vol. 76, no. 5, pp ,

Kinetics of Microwave Sintering and Solid State Synthesis in the Microwave Field: Similarities and Differences

Kinetics of Microwave Sintering and Solid State Synthesis in the Microwave Field: Similarities and Differences Kinetics of Microwave Sintering and Solid State Synthesis in the Microwave Field: Similarities and Differences Alexander S. Vanetsev Kurnakov Institute of General and Inorganic Chemistry RAS, Moscow, Russia

More information

Sintering of oxide and carbide ceramics by electron beam at forevacuum pressure

Sintering of oxide and carbide ceramics by electron beam at forevacuum pressure Sintering of oxide and carbide ceramics by electron beam at forevacuum pressure E Dvilis 1, O Tolkachev 1, V Burdovitsin 2, A Khasanov 1, M Petyukevich 1 1 Department of nanomaterials and nanotechnologies,

More information

Influence of forming method and sintering process on densification and final microstructure of submicrometre alumina ceramics

Influence of forming method and sintering process on densification and final microstructure of submicrometre alumina ceramics Processing and Application of Ceramics 2 [1] (2008) 13-17 Influence of forming method and sintering process on densification and final microstructure of submicrometre alumina ceramics Monika Mikoczyová

More information

Combustion of Al Al 2 O 3 mixtures in air

Combustion of Al Al 2 O 3 mixtures in air Journal of the European Ceramic Society 25 (2005) 1575 1579 Combustion of Al Al 2 O 3 mixtures in air Alexander Gromov, Alexander Ilyin, Alexander Ditts, Vladimir Vereshchagin Chemical Department, Tomsk

More information

DEVELOPMENT OF IN-SITU MONITORING SYSTEM FOR SINTERING OF CERAMICS USING LASER AE TECHNIQUE

DEVELOPMENT OF IN-SITU MONITORING SYSTEM FOR SINTERING OF CERAMICS USING LASER AE TECHNIQUE DEVELOPMENT OF IN-SITU MONITORING SYSTEM FOR SINTERING OF CERAMICS USING LASER AE TECHNIQUE S. NISHINOIRI and M. ENOKI Department of Materials Engineering, The University of Tokyo, 7-3-1, Hongo, Bunkyo,

More information

MICROWAVES AS AN ENERGY SOURCE FOR PRODUCING MAGNESIA - ALUMINA SPINEL

MICROWAVES AS AN ENERGY SOURCE FOR PRODUCING MAGNESIA - ALUMINA SPINEL MICROWAVES AS AN ENERGY SOURCE FOR PRODUCING MAGNESIA - ALUMINA SPINEL JUAN A. AGUILAR MARIO GONZALEZ IDALIA GOMEZ Universidad Autónoma de Nuevo León, Facultad de Ingeniería Mecánica y Eléctrica Apartado

More information

Improved high-q microwave dielectric resonator using CuO-doped MgNb 2 O 6 ceramics

Improved high-q microwave dielectric resonator using CuO-doped MgNb 2 O 6 ceramics Materials Research Bulletin 38 (2003) 1091 1099 Improved high-q microwave dielectric resonator using CuO-doped MgNb 2 O 6 ceramics Cheng-Shing Hsu a, Cheng-Liang Huang a,*, Jing-Fang Tseng a, Chi-Yuen

More information

Activated sintering of ceramics on the basis of Al 2 O 3

Activated sintering of ceramics on the basis of Al 2 O 3 Activated sintering of ceramics on the basis of Al 2 O 3 S V Matrenin 1, B B Ovechkin 1, B S Zenin 1 and R V Tayukin 1 1 Tomsk Polytechnic University, 30 Lenin Avenue, Tomsk, Russia, 634050 E-mail: msv@tpu.ru

More information

Novosibirsk, Russia 2 Budker Institute of Nuclear Physics, SB RAS, , Novosibirsk,

Novosibirsk, Russia   2 Budker Institute of Nuclear Physics, SB RAS, , Novosibirsk, MANUFACTURE OF PRODUCTS FROM MOLTEN HAFNIUM CARBIDE BY MEANS OF THE TREATMENT OF MECHANOCOMPOSITE WITH A HIGH-INTENSITY FOTON FLUX A.I. Ancharov 1, 2, T.F. Grigoreva 1, G.N. Grachev 3 1 Institute of Solid

More information

PREPARATION AND PROPERTIES OF Cr 2 N-Al 2 O 3 NANOCOMPOSITES

PREPARATION AND PROPERTIES OF Cr 2 N-Al 2 O 3 NANOCOMPOSITES PREPARATION AND PROPERTIES OF Cr 2 N-Al 2 O 3 NANOCOMPOSITES Lian Gao 1 and Yaogang Li 2 1 State Key Lab of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese

More information

The effect of Ta 2 O 5 and Cr 2 O 3 on the electrical properties of TiO 2 varistors

The effect of Ta 2 O 5 and Cr 2 O 3 on the electrical properties of TiO 2 varistors Journal of the European Ceramic Society 22 (2002) 1277 1283 www.elsevier.com/locate/jeurceramsoc The effect of Ta 2 O 5 and Cr 2 O 3 on the electrical properties of TiO 2 varistors V.C. Sousa, E.R. Leite,

More information

Jānis Grabis. Plasma chemical synthesis of multicomponent nanopowders, their characteristics, and processing

Jānis Grabis. Plasma chemical synthesis of multicomponent nanopowders, their characteristics, and processing Jānis Grabis Plasma chemical synthesis of multicomponent nanopowders, their characteristics, and processing Outline Introduction nanoparticles, their preparation methods Experimental synthesis of multicomponent

More information

PROPERTIES OF 2.45 GHZ MICROWAVE SINTERED SiO2 FROM RICE HUSK ASH AND Al2O3

PROPERTIES OF 2.45 GHZ MICROWAVE SINTERED SiO2 FROM RICE HUSK ASH AND Al2O3 PROPERTIES OF 2.45 GHZ MICROWAVE SINTERED SiO2 FROM RICE HUSK ASH AND Al2O3 Muhammad Zamrun Firihu 1 and I. Nyoman Sudiana 2 1 Theoretical and Computational Physics Laboratory, Department of Physics, Faculty

More information

SUPPLEMENTARY INFORMATION

SUPPLEMENTARY INFORMATION Layered oxygen-deficient double perovskite as an efficient and stable anode for direct hydrocarbon solid oxide fuel cells Sivaprakash Sengodan 1, Sihyuk Choi 1, Areum Jun 1, Tae Ho Shin 2, Young-Wan Ju

More information

Effect of HF-Treatment on the Glass Frit upon Crystallizing Behavior and Microstructure of Glass- Ceramics

Effect of HF-Treatment on the Glass Frit upon Crystallizing Behavior and Microstructure of Glass- Ceramics , pp.72-76 http://dx.doi.org/10.14257/astl.2016.130.16 Effect of HF-Treatment on the Glass Frit upon Crystallizing Behavior and Microstructure of Glass- Ceramics Yuna Lee 1, Seunggu Kang 1,* 1 Dept. of

More information

Received June 17, 2013; revised July 19, 2013; accepted July 30, 2013

Received June 17, 2013; revised July 19, 2013; accepted July 30, 2013 Journal of Minerals and Materials Characterization and Engineering, 2013, 1, 217-221 http://dx.doi.org/10.4236/jmmce.2013.15034 Published Online September 2013 (http://www.scirp.org/journal/jmmce) The

More information

Densification and dielectric properties of barium neodymium titanium oxide ceramics

Densification and dielectric properties of barium neodymium titanium oxide ceramics Materials Science and Engineering B98 (2003) 33/37 www.elsevier.com/locate/mseb Densification and dielectric properties of barium neodymium titanium oxide ceramics Chung-Hsin Lu *, Yung-Hsiang Huang Electronic

More information

Low sintering BaNd 2 Ti 4 O 12 microwave ceramics prepared by CuO thin layer coated powder

Low sintering BaNd 2 Ti 4 O 12 microwave ceramics prepared by CuO thin layer coated powder Journal of the European Ceramic Society 27 (2007) 2835 2839 Low sintering BaNd 2 Ti 4 O 12 microwave ceramics prepared by CuO thin layer coated powder M.-C. Wu a, M.-K. Hsieh b, C.-W. Yen a, Y.-C. Huang

More information

Sintering Behavior of Porous Nanostructured Sr-Doped Lanthanum Manganite as SOFC Cathode Material

Sintering Behavior of Porous Nanostructured Sr-Doped Lanthanum Manganite as SOFC Cathode Material Int. J. Nanosci. Nanotechnol., Vol. 9, No. 2, June 2013, pp. 71-76 Sintering Behavior of Porous Nanostructured Sr-Doped Lanthanum Manganite as SOFC Cathode Material H. Tamaddon *, A. Maghsoudipour Ceramics

More information

By *T.Khalil, **J. Bossert,***A.H.Ashor and *F. Abou EL-Nour

By *T.Khalil, **J. Bossert,***A.H.Ashor and *F. Abou EL-Nour WM 11 EG0100132 Seventh Conference of Nuclear Sciences & Applications 6-10 February 2000. Cairo, Egypt Preparation, Characterization and application of Alumina powder Produced by advanced Preparation Techniques

More information

Activation of consolidation processes of alumina ceramics

Activation of consolidation processes of alumina ceramics IOP Conference Series: Materials Science and Engineering PAPER OPEN ACCESS Activation of consolidation processes of alumina ceramics To cite this article: S V Matrenin et al 2016 IOP Conf. Ser.: Mater.

More information

Microwave dielectric properties and microstructures of MgTa 2 O 6 ceramics with CuO addition

Microwave dielectric properties and microstructures of MgTa 2 O 6 ceramics with CuO addition Materials Chemistry and Physics 90 (2005) 373 377 Microwave dielectric properties and microstructures of MgTa 2 O 6 ceramics with CuO addition Cheng-Liang Huang a,, Kuo-Hau Chiang a, Chi-Yuen Huang b a

More information

Experimental O 3. Results and discussion

Experimental O 3. Results and discussion Introduction Surface coatings to protect against oxidation extend the service temperature and the service life of basic metals. The commercially used coating systems can be divided into three main groups:

More information

PREPARATION AND CHARACTERISTICS OF NANOSIZED ZIRCONIA-MULLITE POWDERS

PREPARATION AND CHARACTERISTICS OF NANOSIZED ZIRCONIA-MULLITE POWDERS Powder Metallurgy Progress, Vol.6 (2006), No 2 94 PREPARATION AND CHARACTERISTICS OF NANOSIZED ZIRCONIA-MULLITE POWDERS J. Grabis, I. Steins, D. Rasmane, A. Krumina Abstract Nanosized spherical Al 2 O

More information

CHAPTER 8 CONCLUSIONS AND SUGGESTIONS FOR FUTURE WORK

CHAPTER 8 CONCLUSIONS AND SUGGESTIONS FOR FUTURE WORK CHAPTER 8 CONCLUSIONS AND SUGGESTIONS FOR FUTURE WORK 8.1. Conclusions Referring to the aims of the research project in Chapter 4, the following conclusions can be drawn on the basis of the present work:

More information

PART I BASIS OF SINTERING SCIENCE

PART I BASIS OF SINTERING SCIENCE [26.6.2004 12:22am] [1 8] [Page No. 1] PART I BASIS OF SINTERING SCIENCE When thermal energy is applied to a powder compact, the compact is densified and the average grain size increases. The basic phenomena

More information

Keywords: hydroxyapatite, fluorapatite, composite materials, microhardness

Keywords: hydroxyapatite, fluorapatite, composite materials, microhardness PRODUCTION OF HYDROXYAPATITE BASED FLUORINE-CONTAINING COMPOSITE MATERIALS Bogdanova Е.А., Skachkova О.V., Skachkov V.М., Sabirzyanov N.А. Federal State government-financed institution of science Institute

More information

Thermal Conductivity and Sintering Behavior of Hafnia-based Thermal Barrier Coating Using EB-PVD

Thermal Conductivity and Sintering Behavior of Hafnia-based Thermal Barrier Coating Using EB-PVD Proceedings of the International Gas Turbine Congress 2003 Tokyo November 2-7, 2003 IGTC2003Tokyo TS-131 Thermal Conductivity and Sintering Behavior of Hafnia-based Thermal Barrier Coating Using EB-PVD

More information

Densification and mechanical properties of mullite SiC nanocomposites synthesized through sol gel coated precursors

Densification and mechanical properties of mullite SiC nanocomposites synthesized through sol gel coated precursors Bull. Mater. Sci., Vol. 24, No. 2, April 2001, pp. 191 195. Indian Academy of Sciences. Densification and mechanical properties of mullite SiC nanocomposites synthesized through sol gel coated precursors

More information

Study Properties of Alumina by Adding Different Ratio of Copper

Study Properties of Alumina by Adding Different Ratio of Copper International Journal of Engineering and Technology Volume 6 No.6, June, 2016 Study Properties of Alumina by Adding Different Ratio of Copper Assist. Prof. Dr. Elham Abd Al-Majeed, Sundus Abbas College

More information

INTRODUCTION Barium Hexaferrite with hexagonal structure (BaFe 12

INTRODUCTION Barium Hexaferrite with hexagonal structure (BaFe 12 EFFECT OF FE 3+ /BA 2+ MOLE RATIO AND SINTERING TEMPERATURES ON THE MICROSTRUCTURE AND MAGNETIC PROPERTIES OF NANO PARTICLE BARIUM HEXAFERRITE (BAM) PRODUCED BY SOL GEL AUTO COMBUSTION Widyastuti, Felly

More information

Syntheses of Fe TiC nanocomposite from ilmenite concentrate via microwave heating

Syntheses of Fe TiC nanocomposite from ilmenite concentrate via microwave heating Bull. Mater. Sci., Vol. 32, No. 2, April 2009, pp. 155 160. Indian Academy of Sciences. Syntheses of Fe ic nanocomposite from ilmenite concentrate via microwave heating MANSOUR RAZAVI, MOHAMMAD REZA RAHIMIPOUR*,

More information

SYNERGISTIC EFFECTS IN MICROWAVE-LASER HYBRIDIZATION AND ITS APPLICATION TO CERAMICS SINTERING

SYNERGISTIC EFFECTS IN MICROWAVE-LASER HYBRIDIZATION AND ITS APPLICATION TO CERAMICS SINTERING SYNERGISTIC EFFECTS IN MICROWAVE-LASER HYBRIDIZATION AND ITS APPLICATION TO CERAMICS SINTERING P.D.Ramesh 1, Rustum Roy and Andrzej Badzian Materials Research Institute The Pennsylvania State University

More information

Development of Al-SiC Compsite Material By Powder Metaullargy Route

Development of Al-SiC Compsite Material By Powder Metaullargy Route Scientific Journal of Impact Factor(SJIF): 3.134 e-issn(o): 2348-4470 p-issn(p): 2348-6406 International Journal of Advance Engineering and Research Development Volume 2,Issue 3, March -2015 Development

More information

MICROWAVE DIELECTRIC PROPERTIES OF Ba 0.75 Sr 0.25 (Nd x Bi 1-x ) 2 Ti 4 O 12 SOLID SOLUTION

MICROWAVE DIELECTRIC PROPERTIES OF Ba 0.75 Sr 0.25 (Nd x Bi 1-x ) 2 Ti 4 O 12 SOLID SOLUTION Original papers MICROWAVE DIELECTRIC PROPERTIES OF Ba 0.75 Sr 0.25 (Nd x Bi 1-x ) 2 Ti 4 O 12 SOLID SOLUTION Long Mingzhu, ZHuang WENDONG*, # Tang Bin, Yu Shengquan, Zhou Xiaohua, Zhang Shuren State Key

More information

CRYSTALLIZATION BEHAVIOR OF HYBRID PREMULLITE POWDERS SYNTHESIZED BY SOL-GEL METHOD

CRYSTALLIZATION BEHAVIOR OF HYBRID PREMULLITE POWDERS SYNTHESIZED BY SOL-GEL METHOD 9. Savjetovanje o materijalima, tehnologijama, trenju i trošenju 9. Conference on Materials, Processes, Friction and Wear MATRIB 04, Vela Luka, 23-25.06.2004. CRYSTALLIZATION BEHAVIOR OF HYBRID PREMULLITE

More information

Selective laser melting of copper using ultrashort laser pulses

Selective laser melting of copper using ultrashort laser pulses Lasers in Manufacturing Conference 2017 Selective laser melting of copper using ultrashort laser pulses Lisa Kaden a,*, Gabor Matthäus a, Tobias Ullsperger a, Andreas Tünnermann a,b, Stefan Nolte a,b a

More information

Printed Electronics: Photonic Curing and Enabled Materials

Printed Electronics: Photonic Curing and Enabled Materials Printed Electronics: Photonic Curing and Enabled Materials Kurt Schroder, Dave Pope, Ian Rawson NovaCentrix 200-B Parker Dr Suite 580 Austin, TX 78728 Extended Abstract Introduction Photonic curing is

More information

PHYSICAL PROPERTIES OF La 0.9 Sr 0.1 Cr 1-X Ni X O 3-δ (X = 0-0.6) SYNTHESIZED VIA CITRATE GEL COMBUSTION

PHYSICAL PROPERTIES OF La 0.9 Sr 0.1 Cr 1-X Ni X O 3-δ (X = 0-0.6) SYNTHESIZED VIA CITRATE GEL COMBUSTION PHYSICAL PROPERTIES OF La 0.9 Sr 0.1 Cr 1-X Ni X O 3-δ (X = 0-0.6) SYNTHESIZED VIA CITRATE GEL COMBUSTION Anuchit Ruangvittayanon * and Sutin Kuharuangrong Received: Sept 29, 2009; Revised: Nov 17, 2009;

More information

Synthesis and Characterization of nanocrystalline Ni-Co-Zn ferrite by Sol-gel Auto-Combustion method.

Synthesis and Characterization of nanocrystalline Ni-Co-Zn ferrite by Sol-gel Auto-Combustion method. International Journal of Scientific & Engineering Research Volume 3, Issue 12, December-212 1 Synthesis and Characterization of nanocrystalline Ni-Co- ferrite by Sol-gel Auto-Combustion method. R. B. Bhise

More information

Hardening of Ceramic Heat-Protective Layers on Metallic Substances Ilsur Zakirov, Andrei Niculin, and Nicolay Obabkov

Hardening of Ceramic Heat-Protective Layers on Metallic Substances Ilsur Zakirov, Andrei Niculin, and Nicolay Obabkov Hardening of Ceramic Heat-Protective Layers on Metallic Substances Ilsur Zakirov, Andrei Niculin, and Nicolay Obabkov Department of Rare Metals and Nanomaterials, Institute of Physics and Technology, Ural

More information

This article appeared in a journal published by Elsevier. The attached copy is furnished to the author for internal non-commercial research and

This article appeared in a journal published by Elsevier. The attached copy is furnished to the author for internal non-commercial research and This article appeared in a journal published by Elsevier. The attached copy is furnished to the author for internal non-commercial research and education use, including for instruction at the authors institution

More information

Powder metallurgy. R.D.Makwana, IT, NU

Powder metallurgy. R.D.Makwana, IT, NU Powder metallurgy History 1829 Woolaston- paper published Edison-electric light-filament 1909 Coolidge tungsten worked at elevated temperature New method of fabrication-refractory metals 1 Advantages of

More information

Development of Low-Cost, Compact, Reliable, High Energy Density Ceramic Nanocomposite Capacitors

Development of Low-Cost, Compact, Reliable, High Energy Density Ceramic Nanocomposite Capacitors Development of Low-Cost, Compact, Reliable, High Energy Density Ceramic Nanocomposite Capacitors Todd C. Monson, Chris B. Diantonio, Michael R. Winter, Dale L. Huber, Alex W. Roesler, Tom P. Chavez, Tyler

More information

Fabrication and thermal properties of Al 2 TiO 5 /Al 2 O 3 composites

Fabrication and thermal properties of Al 2 TiO 5 /Al 2 O 3 composites Materials Science-Poland, Vol. 28, No. 3, 2010 Fabrication and thermal properties of Al 2 TiO 5 /Al 2 O 3 composites M. LI, F. CHEN, Q. SHEN *, L. ZHANG State Key Lab of Advanced Technology for Materials

More information

Microwave processing of electroceramic materials and devices

Microwave processing of electroceramic materials and devices J Electroceram (2009) 22:125 130 DOI 10.1007/s10832-008-9441-2 Microwave processing of electroceramic materials and devices Chris Y. Fang & Clive A. Randal & Michael T. Lanagan & Dinesh K. Agrawal Received:

More information

Ceramic Processing. Engineering Materials. 7/15/2009 Ceramic Processing/S.Rattanachan 1

Ceramic Processing. Engineering Materials. 7/15/2009 Ceramic Processing/S.Rattanachan 1 Ceramic Processing Engineering Materials 7/15/2009 Ceramic Processing/S.Rattanachan 1 Ceramic Processing Ceramic powders/raw materials + Additives Mixing Forming Firing Densification Sintering Vitrification

More information

Ceramic Processing Research

Ceramic Processing Research Journal of Ceramic Processing Research. Vol. 17, No. 7, pp. 747~751 (2016) J O U R N A L O F Ceramic Processing Research Synthesis of low thermal expansion ceramics prepared from pyrophyllite and lithium

More information

Application of Microwave Energy for Synthesis and Sintering of Al 2 O 3 -TiC Ceramics

Application of Microwave Energy for Synthesis and Sintering of Al 2 O 3 -TiC Ceramics การประช มเช งว ชาการเคร อข ายพล งงานแห งประเทศไทยคร งท 2 27-29 กรกฎาคม 2549 มหาว ทยาล ยเทคโนโลย ส รนาร จ งหว ดนครราชส มา Application of Microwave Energy for Synthesis and Sintering of Al 2 O 3 -TiC Ceramics

More information

FULL-DENSIFICATION OF SLS PARTS BY RE-MELTING. Abstract

FULL-DENSIFICATION OF SLS PARTS BY RE-MELTING. Abstract FULL-DENSIFICATION OF SLS PARTS BY RE-MELTING T. NIINO and H. YAMADA Institute of Industrial Science, The University of Tokyo 4-6-1 Komaba Meguro Tokyo, 153-8505 Japan Reviewed, accepted August 4, 2004

More information

Preparation and Investigation of Cu-Co- Al2O3 Nanocrystalline Metal Matrix Composites

Preparation and Investigation of Cu-Co- Al2O3 Nanocrystalline Metal Matrix Composites Preparation and Investigation of Cu-Co- Al2O3 Nanocrystalline Metal Matrix Composites R.Venkatesh Research Scholar Sathyabama University, Chennai TamilNadu, India S.Kumaraguru U.G Student Department of

More information

An Investigation of the Synthesis of Ti-50 At. Pct Ni Alloys through Combustion Synthesis and Conventional Powder Sintering

An Investigation of the Synthesis of Ti-50 At. Pct Ni Alloys through Combustion Synthesis and Conventional Powder Sintering An Investigation of the Synthesis of Ti-50 At. Pct Alloys through Combustion Synthesis and Conventional Powder Sintering BING-YUN LI, LI-JIAN RONG, YI-YI LI, and V.E. GJUNTER * Institute of Metal Research,

More information

Microstructure and characteristics of BaTiO 3 ceramic with 4PbO B 2 O 3 (sintering aid)

Microstructure and characteristics of BaTiO 3 ceramic with 4PbO B 2 O 3 (sintering aid) Journal of the Ceramic Society of Japan 116 [7] 797-802 2008 Paper Microstructure and characteristics of BaTiO 3 ceramic with 4PbO B 2 O 3 (sintering aid) Chun-Huy WANG Department of Electronic Engineering,

More information

Synthesis and Characterization of α-alumina Membrane Support and Effects of Binders

Synthesis and Characterization of α-alumina Membrane Support and Effects of Binders Synthesis and Characterization of α-alumina Membrane Support and Effects of Binders M. Khalili a,*, S. Sabbaghi a, H. Daneshmand a, M.M. Zerafat b a Faculty of Nanotechnology, Nano Chemical Engineering

More information

VARIATION OF MECHANICAL PROPERTIES OF COPPER COMPACTS PROCESSED IN HIGH ENERGY BALL MILLING

VARIATION OF MECHANICAL PROPERTIES OF COPPER COMPACTS PROCESSED IN HIGH ENERGY BALL MILLING International Journal of Mechanical Engineering and Technology (IJMET) Volume 9, Issue 10, October 2018, pp. 260 265, Article ID: IJMET_09_10_025 Available online at http://www.iaeme.com/ijmet/issues.asp?jtype=ijmet&vtype=9&itype=10

More information

Enhancement of connectivity and flux pinning in MgB2 superconducting bulks and wires

Enhancement of connectivity and flux pinning in MgB2 superconducting bulks and wires University of Wollongong Research Online University of Wollongong Thesis Collection 1954-2016 University of Wollongong Thesis Collections 2009 Enhancement of connectivity and flux pinning in MgB2 superconducting

More information

SOLID OXIDE FUEL CELLS: Sr-DOPED LANTHANUM MANGANITES PROPERTIES

SOLID OXIDE FUEL CELLS: Sr-DOPED LANTHANUM MANGANITES PROPERTIES SOLID OXIDE FUEL CELLS: Sr-DOPED LANTHANUM MANGANITES PROPERTIES Seo Miyamaru, E. S. 1 ; Couto, A. A. 1 ; Lima, N. B. 1, Köhler A. C. 1 ; Pereira Soares E. 1 1 IPEN Instituto de Pesquisas Energéticas e

More information

Preparation of mullite by the reaction sintering of kaolinite and alumina

Preparation of mullite by the reaction sintering of kaolinite and alumina Journal of the European Ceramic Society 20 (2000) 2519±2525 Preparation of mullite by the reaction sintering of kaolinite and alumina C.Y. Chen, G.S. Lan, W.H. Tuan * Institute of Materials Science and

More information

Volume 8, ISSN (Online), Published at:

Volume 8, ISSN (Online), Published at: IMPACT OF POWDERY OXIDE LAYER IN THE TITANIUM/RUTILE SYSTEM PREPARED BY OXIDATIVE CONSTRUCTING OF CERAMIC MATERIALS Sergey V. Shevtsov, Nikolay A. Alad ev, Konstantin A. Solntsev Baikov Institute of Metallurgy

More information

COMPACTION AND PROPERTIES OF HIGHLY POROUS POWDER PARTS PRODUCED WITH VARIOUS PORE FORMERS

COMPACTION AND PROPERTIES OF HIGHLY POROUS POWDER PARTS PRODUCED WITH VARIOUS PORE FORMERS 82 Mechanical Testing and Diagnosis ISSN 2247 9635, 2011 (I), Volume 1, 82-87 COMPACTION AND PROPERTIES OF HIGHLY POROUS POWDER PARTS PRODUCED WITH VARIOUS PORE FORMERS Natalia RUDENKO, Alexander LAPTEV

More information

CERAMICS BASED ON ZIRCONIA WITH A LOW SINTERING TEMPERATURE

CERAMICS BASED ON ZIRCONIA WITH A LOW SINTERING TEMPERATURE Powder Metallurgy Progress, Vol.14 (2014), No 3 148 CERAMICS BASED ON ZIRCONIA WITH A LOW SINTERING TEMPERATURE V. V. Smirnov, S. V Smirnov, A. I. Krylov, O. S. Antonova, M. A. Goldberg, L. I. Shvorneva,

More information

GRAIN SIZE EFFECT ON STRUCTURE AND PROPERTIES OF DOPED BARIUM TITANATE

GRAIN SIZE EFFECT ON STRUCTURE AND PROPERTIES OF DOPED BARIUM TITANATE GRAIN SIZE EFFECT ON STRUCTURE AND PROPERTIES OF DOPED BARIUM TITANATE B.D.Stojanovic, C.R. Foschini, M.A. Zaghete, Cilence M.(1); F.O.S.Viera, K.Peron J.A.Varela LIEC: Instituto de Química, UNESP, Araraquara,

More information

PHYSICAL PROPERTIES OF AL/CALCINED DOLOMITE METAL MATRIX COMPOSITE BY POWDER METALLURGY ROUTE

PHYSICAL PROPERTIES OF AL/CALCINED DOLOMITE METAL MATRIX COMPOSITE BY POWDER METALLURGY ROUTE PHYSICAL PROPERTIES OF AL/CALCINED DOLOMITE METAL MATRIX COMPOSITE BY POWDER METALLURGY ROUTE B.Johar, N.A.Rejab, N.K.Su, M.S.Talib, A.F.Osman, N.M.S.Adzali, M.H.Musa, UniMAP, Academics Complex-Jejawi

More information

Study Properties of Alumina by Adding Different Ratio of Copper

Study Properties of Alumina by Adding Different Ratio of Copper International Journal of Engineering and Technology Volume 6 No., October, 6 Study Properties of Alumina by Adding Different Ratio of Copper Elham Abd Al-Majeed & Sundus Abbas College of Materials Engineering,

More information

PHYSICO-MECHANICAL AND PHYSICO-CHEMICAL PROPERTIES OF BIO-INERT COMPOSITE CERAMICS

PHYSICO-MECHANICAL AND PHYSICO-CHEMICAL PROPERTIES OF BIO-INERT COMPOSITE CERAMICS PHYSICO-MECHANICAL AND PHYSICO-CHEMICAL PROPERTIES OF BIO-INERT COMPOSITE CERAMICS Anna PETROVA 1, Silvia SIMEONOVA 1, Radoslav VALOV 2 and Vladimir PETKOV 2 1 Space Research Institute, Bulgarian Academy

More information

Special Electrically Resistant Heated Furnaces

Special Electrically Resistant Heated Furnaces Special Electrically Resistant Heated Furnaces Drying of Ceramic Components Autor: Roland Waitz, Malte Möller Many ceramic masses are fabricated in plastic or liquid condition by addition of water. In

More information

The Origin of EPR Signals in SrCuO 2 Ceramics

The Origin of EPR Signals in SrCuO 2 Ceramics Vol. 108 (2005) ACTA PHYSICA POLONICA A No. 2 Proceedings of the XXI International Meeting on Radio and Microwave Spectroscopy RAMIS 2005, Poznań-Bȩdlewo, Poland, April 24 28, 2005 The Origin of EPR Signals

More information

SYNTHESIS OF NANOSIZE SILICON CARBIDE POWDER BY CARBOTHERMAL REDUCTION OF SiO 2

SYNTHESIS OF NANOSIZE SILICON CARBIDE POWDER BY CARBOTHERMAL REDUCTION OF SiO 2 2nd International Conference on Ultrafine Grained & Nanostructured Materials (UFGNSM) International Journal of Modern Physics: Conference Series Vol. 5 (2012) 263 269 World Scientific Publishing Company

More information

Characterization of porous materials by small-angle scattering

Characterization of porous materials by small-angle scattering PRAMANA c Indian Academy of Sciences Vol. 63, No. 1 journal of July 2004 physics pp. 165 173 Characterization of porous materials by small-angle scattering S MAZUMDER, D SEN and A K PATRA Solid State Physics

More information

Low-temperature sintering of Z-type hexagonal ferrite by addition of fluorine containing glass powder

Low-temperature sintering of Z-type hexagonal ferrite by addition of fluorine containing glass powder Title Low-temperature sintering of Z-type hexagonal ferrite by addition of fluorine containing glass powder Author s Name Yasutaka MIZUNO, Seiichi TARUTA and Kunio KITAJIMA Author s Affiliation Department

More information

Fabrication of transparent hydroxyapatite ceramics by ambient-pressure sintering

Fabrication of transparent hydroxyapatite ceramics by ambient-pressure sintering April 1995 Materials Letters 23 (1995) 147-151 Fabrication of transparent hydroxyapatite ceramics by ambient-pressure sintering Y. Fang, D.K. Agrawal, D.M. Roy, R. Roy ntercollege Materials Research Laboratory,

More information

THE INFLUENCE OF MECHANICAL ALLOYING DURATION ON SELECTED PROPERTIES OF SINTERED DISTALOY SE SAMPLES

THE INFLUENCE OF MECHANICAL ALLOYING DURATION ON SELECTED PROPERTIES OF SINTERED DISTALOY SE SAMPLES ANNALS of Faculty Engineering Hunedoara International Journal of Engineering Tome XIV [2016] Fascicule 2 [May] ISSN: 1584-2665 [print; online] ISSN: 1584-2673 [CD-Rom; online] a free-access multidisciplinary

More information

Dielectric properties of LCTO ceramics with various sintering temperature. Chompoonuch Warangkanagool *

Dielectric properties of LCTO ceramics with various sintering temperature. Chompoonuch Warangkanagool * NU Science Journal 2013; 10(1): 30-37 Dielectric properties of LCTO ceramics with various sintering temperature Chompoonuch Warangkanagool * Department of Physics, Faculty of Science, Naresuan University,

More information

Fabrication of Magnesium Oxide Ceramics with Density Close to Theoretical Using Nanopowders

Fabrication of Magnesium Oxide Ceramics with Density Close to Theoretical Using Nanopowders Fabrication of Magnesium Oxide Ceramics with Density Close to Theoretical Using Nanopowders Jing Yang, Tzu-Chieh Lin, Bill Manett, Jeremy Young, Dan Rooney Eugene Medvedovski SCI Engineered Materials,

More information

Effects of CaO B 2 O 3 Glass on Sintering and Microwave Properties of Cordierite Ceramics for Low-Temperature Cofired

Effects of CaO B 2 O 3 Glass on Sintering and Microwave Properties of Cordierite Ceramics for Low-Temperature Cofired Ahmed M. Jasim * Hussain J. Hameed Department of Mechanical Engineering, College of Engineering, University of Babil, Hilla, Babil, IRAQ * ahmedm80@hotmail.com Effects of CaO B 2 O 3 Glass on Sintering

More information

ZINC OXIDE SEMICONDUCTOR CERAMIC WITH NELINEAR ELECTRIC PROPERTIES OBTAINED BY COPRECIPITATION METHOD

ZINC OXIDE SEMICONDUCTOR CERAMIC WITH NELINEAR ELECTRIC PROPERTIES OBTAINED BY COPRECIPITATION METHOD Journal of Optoelectronics and Advanced Materials Vol. 2, No. 5, October 2000, p. Section 3: Ceramic materials ZINC OXIDE SEMICONDUCTOR CERAMIC WITH NELINEAR ELECTRIC PROPERTIES OBTAINED BY COPRECIPITATION

More information

Properties of Ceramic Materials

Properties of Ceramic Materials 1-5 Superplasticity: There are two basic types of superplasticity, termed transformation and structural superplasticity respectively. (A third type of superplasticity, termed temperature-cycling superplasticity,

More information

Microstructural Evolution of the Al2O3-ZrO2 Composite and its Correlation with Electrical Conductivity

Microstructural Evolution of the Al2O3-ZrO2 Composite and its Correlation with Electrical Conductivity Materials Research, Vol. 2, No. 3, 205-210, 1999. 1999 Microstructural Evolution of the Al2O3-ZrO2 Composite and its Correlation with Electrical Conductivity Carlos A. Fortulan, Dulcina P.F. de Souza Departamento

More information

SINTERING ENVIRONMENT INFLUENCE ON THE PROPERTIES OF ALUMINA SILICON CARBIDE COMPOSITES

SINTERING ENVIRONMENT INFLUENCE ON THE PROPERTIES OF ALUMINA SILICON CARBIDE COMPOSITES U.P.B. Sci. Bull., Series B, Vol. 78, Iss. 4, 2016 ISSN 1454-2331 SINTERING ENVIRONMENT INFLUENCE ON THE PROPERTIES OF ALUMINA SILICON CARBIDE COMPOSITES Răzvan STATE 1, Enikö VOLCEANOV 2, Adrian VOLCEANOV

More information

THE DEVELOPMENT OF GAS TIGHT THIN FILMS OF (La,Sr)(Ga,Fe)O 3. , (La,Sr)(Co,Fe)O 3 AND La 2 FOR OXYGEN SEPARATION. NiO 4 INTRODUCTION

THE DEVELOPMENT OF GAS TIGHT THIN FILMS OF (La,Sr)(Ga,Fe)O 3. , (La,Sr)(Co,Fe)O 3 AND La 2 FOR OXYGEN SEPARATION. NiO 4 INTRODUCTION THE DEVELOPMENT OF GAS TIGHT THIN FILMS OF (La,Sr)(Ga,Fe), (La,Sr)(Co,Fe) AND La 2 FOR OXYGEN SEPARATION R. Muydinov, M. Novojilov, O. Gorbenko, I. Korsakov, A. Kaul Moscow State University, Russia S.

More information

Microwave sintering of AlN powder synthesized by a SHS method

Microwave sintering of AlN powder synthesized by a SHS method Journal of the European Ceramic Society 27 (2007) 343 350 Microwave sintering of AlN powder synthesized by a SHS method Cheng-Yu Hsieh a, Chun-Nan Lin a, Shyan-Lung Chung b,, Jiping Cheng c, Dinesh K.

More information

STRUCTURE OF A CERAMIC MATERIAL DEVELOPED BY LASER PROTOTYPING TECHNIQUES

STRUCTURE OF A CERAMIC MATERIAL DEVELOPED BY LASER PROTOTYPING TECHNIQUES Structure Rev. Adv. Mater. of a ceramic Sci. 29 material (2011) 175-179 developed by laser prototyping techniques 175 STRUCTURE OF A CERAMIC MATERIAL DEVELOPED BY LASER PROTOTYPING TECHNIQUES Received:

More information

PREPARATION AND PROPERTIES OF POROUS ALUMINA CERAMIC PRODUCED BY AN EXTRUSION PROCESS

PREPARATION AND PROPERTIES OF POROUS ALUMINA CERAMIC PRODUCED BY AN EXTRUSION PROCESS Suranaree J. Sci. Technol. Vol. 21 No. 1; January - March 2014 41 PREPARATION AND PROPERTIES OF POROUS ALUMINA CERAMIC PRODUCED BY AN EXTRUSION PROCESS Thanakorn Wasanapiarnpong 1,2*, Yolnapa Ngoenngam

More information

Effect of Addition of B 2 O 3 on Dielectric Properties of BMN, BZN, BMNT and BZNT

Effect of Addition of B 2 O 3 on Dielectric Properties of BMN, BZN, BMNT and BZNT (An ISO 3297: 27 Certified Organization) Vol. 3, Issue 6, June 214 Effect of Addition of B 2 O 3 on Dielectric Properties of BMN, BZN, BMNT and BZNT M.Y. Khaladkar, N. S. Saraf, R. R. Purandare* College

More information

Advanced Materials Thermal and Environmental Barrier Coatings Solid Oxide Fuel Cells Custom Compositions

Advanced Materials Thermal and Environmental Barrier Coatings Solid Oxide Fuel Cells Custom Compositions Advanced Materials Thermal and Environmental Barrier Coatings Solid Oxide Fuel Cells Custom Compositions Advanced Materials With over 50 years of advanced ceramic expertise, Skyworks Solutions, through

More information

Fabrication of Calcium Doped PlSZT Ceramics using High Planetary Mill Method

Fabrication of Calcium Doped PlSZT Ceramics using High Planetary Mill Method Journal of Physics: Conference Series PAPER OPEN ACCESS Fabrication of Calcium Doped PlSZT Ceramics using High Planetary Mill Method To cite this article: T.N. I. Tuan Ab Rashid et al 2018 J. Phys.: Conf.

More information

Effect of Nano-Sized Fe 2 O 3 on Microstructure and Hydration Resistance of MgO-CaO Refractories

Effect of Nano-Sized Fe 2 O 3 on Microstructure and Hydration Resistance of MgO-CaO Refractories Int. J. Nanosci. Nanotechnol., Vol. 12, No. 1, March. 2016, pp. 19-26 Effect of Nano-Sized Fe 2 O 3 on Microstructure and Hydration Resistance of MgO-CaO Refractories S. G. Kahrizsangi*, A. Nemati, A.

More information

HEATING OF EN9 STEEL BY USING MICROWAVE ENERGY AND COMPARING WITH CONVENTIONAL HEATING TECHNIQUE WITH THE HELP OF MICROSTRUCTURE

HEATING OF EN9 STEEL BY USING MICROWAVE ENERGY AND COMPARING WITH CONVENTIONAL HEATING TECHNIQUE WITH THE HELP OF MICROSTRUCTURE International Journal of Advance Research In Science And Engineering http://www.ijarse.com HEATING OF EN9 STEEL BY USING MICROWAVE ENERGY AND COMPARING WITH CONVENTIONAL HEATING TECHNIQUE WITH THE HELP

More information

Microstructural Evolution of W-Ni-Fe During Liquid Phase Sintering A Quenching Study

Microstructural Evolution of W-Ni-Fe During Liquid Phase Sintering A Quenching Study Microstructural Evolution of W-Ni-Fe During Liquid Phase Sintering A Quenching Study N.B. Erhardt*, P. Suri, R.M. German, Center for Innovative Sintered Products, 147 Research West, The Pennsylvania State

More information

The effects of Fe/Al 2 O 3 preparation technique as a catalyst on synthesized CNTs in CVD method.

The effects of Fe/Al 2 O 3 preparation technique as a catalyst on synthesized CNTs in CVD method. Science Journal of Physics Science Journal Publication Science Journal of Physics Web: http://www.sjpublication.com/sjp.html The effects of Fe/Al 2 O 3 preparation technique as a catalyst on synthesized

More information

Supplementary Information for A Shortcut to Garnet-type Fast Li-Ion Conductors for All Solid State Batteries

Supplementary Information for A Shortcut to Garnet-type Fast Li-Ion Conductors for All Solid State Batteries Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2015 Supplementary Information for A Shortcut to Garnet-type Fast Li-Ion Conductors

More information

Considerations in Developing High Energy ZnO MOV Blocks RAMÓN PUYANÉ

Considerations in Developing High Energy ZnO MOV Blocks RAMÓN PUYANÉ Considerations in Developing High Energy ZnO MOV Blocks RAMÓN PUYANÉ R. Puyané Advanced Varistor Consulting Limited Caraban House Caraban Ravensdale Dundalk IRELAND MOV blocks are the working component

More information

PROPERTIES AND MICROSTRUCTURE OF PRESSURELESS SINTERED AND MICROWAVE SINTERED SIC-ALN CERAMICS

PROPERTIES AND MICROSTRUCTURE OF PRESSURELESS SINTERED AND MICROWAVE SINTERED SIC-ALN CERAMICS 21 st International Conference on Composite Materials Xi an, 20-25 th August 2017 PROPERTIES AND MICROSTRUCTURE OF PRESSURELESS SINTERED AND MICROWAVE SINTERED SIC-ALN CERAMICS Shuang Zhao 1, Zichun Yang

More information

CENTRIFUGAL THERMIT PROCESS AN OVERVIEW

CENTRIFUGAL THERMIT PROCESS AN OVERVIEW CENTRIFUGAL THERMIT PROCESS AN OVERVIEW A.Arul Paligan, V. Shubha and T.G. Ramesh Materials Science Division, National Aerospace Laboratories, Bangalore, India. email: vshubha@css.nal.res.in ABSTRACT:

More information

3D Printing Park Hong-Seok. Laboratory for Production Engineering School of Mechanical and Automotive Engineering University of ULSAN

3D Printing Park Hong-Seok. Laboratory for Production Engineering School of Mechanical and Automotive Engineering University of ULSAN 3D Printing 2016. 05. 25 Park Hong-Seok Laboratory for Production Engineering School of Mechanical and Automotive Engineering University of ULSAN http://lpe.ulsan.ac.kr Why Do We Need 3d Printing? Complexity

More information

Development of LSCF: CGO Composite Cathodes for SOFCs by Suspension Spraying and Sintering

Development of LSCF: CGO Composite Cathodes for SOFCs by Suspension Spraying and Sintering Development of LSCF: CGO Composite Cathodes for SOFCs by Suspension Spraying and Sintering R. Costa *, R. Spotorno, Z. Ilhan, A. Ansar German Aerospace Center, Institute of Technical Thermodynamics, Pfaffenwaldring

More information

Low Temperature Sintering Glass Binder for Al 2 O 3 Grinding Wheel

Low Temperature Sintering Glass Binder for Al 2 O 3 Grinding Wheel Low Temperature Sintering Glass Binder for Al 2 O 3 Grinding Wheel Wenyan Luo 1, a, Zhuohao Xiao 1, b, Weimin Yi 2, c and Minhua Luo 1, d 1 School of materials Science and Engineering, Jingdezhen Ceramic

More information

NEW WAYS OF OBTAINMENT OF NANOCRYSTALS ALUMINUM HYDROXIDES AND OXIDES

NEW WAYS OF OBTAINMENT OF NANOCRYSTALS ALUMINUM HYDROXIDES AND OXIDES 1 NEW WAYS OF OBTAINMENT OF NANOCRYSTALS ALUMINUM HYDROXIDES AND OXIDES G.P. Panasyuk, L.A. Azarova, I.L. Voroshilov,V.N.Belan I.V.Kozerozhets, I.V.Luchkov N. S. Kurnakov Institute of General and Inorganic

More information

Porous NiTi alloy prepared from elemental powder sintering

Porous NiTi alloy prepared from elemental powder sintering Porous Ti alloy prepared from elemental powder sintering Bing-Yun Li, Li-Jian Rong and Yi-Yi Li Laboratory of Atomic Imaging of Solids, Institute of Metal Research Chinese Academy of Sciences, Shenyang

More information

LASER CLADDING OF ALUMINIUM USING TiB 2

LASER CLADDING OF ALUMINIUM USING TiB 2 LASER CLADDING OF ALUMINIUM USING TiB 2 (Paper Number 1202) Sanjay Kumar and Sisa Pityana CSIR National Laser Centre, PO Box 395, Pretoria 0001, South Africa Abstract Modification of Aluminium surface

More information