1 More Info at Open Access Database Non-Destructive Evaluation of Dissimilar Aluminum Alloys (AA1100 & AA2014) Welded Using Friction Stir Welding P.Balaji, V.Kalyanavalli, D.Sastikumar, S.Muthukumaran 1 and S.Venukumar 1 Physics Department, National Institute of Technology, Tiruchirappalli, India Metallurgical and Materials Engineering Department,1 National Institute of Technology, Tiruchirappalli, India p.balaji.mechanical@gmail.com ABSTRACT: Friction Stir Welding is a solid state welding process for joining materials like aluminum, magnesium, zinc and copper alloys which are employed in aerospace, rail, automobile and marine industries. Generally AA2014 and AA1100 are welded using conventional welding technique in marine industries for galvanizing purpose. The drawbacks in the conventional welding process in aluminum is the presence of a oxide layer, high thermal conductivity, high coefficient of thermal expansion, solidification shrinkage and above all the high solubility of hydrogen and other gases in molten state. These lead to use of vacuum setup in the conventional welding process which is costly. But in FSW, the welding process is done by solid state welding of the material and not by melting the materials, thus the above said problems are solved. In this work, FSW joints have been made between AA1100 and AA2014 of aluminum plates dimension (140 x 70 x 5) mm using different combinations of process parameters. The non destructive analyses have been done to check the weld quality using ultrasonic C-scan and radiography. The defects that are mostly present in the friction stir welding process are disbanding, tunnel defect and kissingbond, are analyzed using ultrasonic C-scan technique. Key Words: Friction Stir Welding; ultrasonic A, B & C-scan;. INTRODUCTION: Aluminum (Al) alloy is a light weight material and has many industrial application. But they are not easily weldable by conventional fusion welding techniques because the quality of the welded joint is deteriorated due to the presence of porosity, hot cracking and distortion [3]. To overcome this, The Welding Institute (TWI), United Kingdom in December 1991, has invented Friction Stir Welding (FSW) as a solid-state joining technique, and it was initially applied to aluminum alloys [1]. FSW has shown great results for joining metals together without significantly altering the original properties of the parent metals. FSW is a solid-state joining process which is applicable to all metals and plastics. The popularity of this welding procedure is due to the fact that unlike conventional welding, it does not create brittle bonds caused by the Localized heating of metal. A major weld quality aspect in question is how to be able to detect the internal defect formed in the weld and a Non-Destructive Testing (NDT) technique is most appropriate in this regard. Non-Destructive Testing rose from the necessity to detect flaws within components to avoid detrimental and repetitive failures. NDT is a wide group of analysis techniques used in science and industry to evaluate the characteristics of a material or component without causing damage to it. The techniques used are non-invasive. NDT does not permanently alter the article being inspected; they are highly valuable techniques that can save both money and time.
2 Many different types of NDT methods exist, the most commonly used testing methods on FSW of AA2014 and AA-1100 aluminium alloy being ultrasonic testing and eddy current testing. The techniques successfully employed include the x-ray detection and ultrasonic C-scan. The Ultrasonic C-scan testing was found to do well at detecting porosity and tiny voids in the joints, while the liquid penetrating fluid inspection was suitable for revealing the Hidden root crack-like flaws. However, there is no published literature on non-destructive testing on friction stir welds of dissimilar materials. Non-destructive testing for defects deduction is the most effective method of determining the integrity of a friction stir weld, hence research studies into non-destructive techniques of dissimilar joints between aluminium and aluminium alloys will ultimately lead to achieving optimized setting to produce quality welds and increase material performance in this regard. The aim of this paper therefore, is to present results of non-destructive testing techniques on dissimilar friction stir welds of aluminum AA1100 and AA2014 alloys. II. EXPERIMENTAL : A.SAMPLE PREPARATION: The Friction Stir welds consisting of aluminum alloy AA-1100 and AA-2014-T6 were successfully produced using modified vertical milling machine at the department of metallorgy, National Institute of Technology, Tiruchirappalli. The chemical composition of the weld is shown in table-i. The dimension of the weld coupon was (140mm x 70mm x 5mm) and butt joint configuration was considered in this research. The plates were grounded in grinding machine and cleaned with acetone to degrease before the welding procedure. The composition of the aluminum alloy was shown in Table-I. Table-I: Composition of the aluminum alloy AA 1100 & AA 2014: Elements Cu Mg Mn Fe Si Cr Zn Ti AA AA The Friction Stir Welds were produced by varying the rotational speeds between 710 and 1200 rpm and the feed rate between 20 and 50 mm/minute. Rotational speeds of 710, 900, and 1200 rpm were employed while 20, 40 and 50 mm/min were the feed rates considered representing the low, medium and high settings respectively. The tool geometry also has been varied. The tool employed was cylindrical 10mm diameter pin with the depth of 4 mm and another tool pin of 10 mm diameter tapered to 8 mm diameter with 4 mm depth. The AA1100 was placed in tool advancing side and AA2014 was placed in tool retreating side. A weld length of 110 mm was produced for every setting. Visual testing and liquid penetrate testing were carried out in the welded sample for surface cracks. The aluminum alloy and their quality of welded sample were shown in table-ii.
3 Table-II: Weld Matrix And Samplle Designation: Specimen Designation A-1-C Cylindrical pin Rotational Tool Speed (rpm) Feed Rate (mm/min) Defective Remarks of sample testing and LPT A-2-T Tapered pin Comparatively less defective B-1-C Cylindrical pin Less defective B-2-T Tapered pin Defect less C-1-C Cylindrical pin Distortion in sample C-2-T Tapered pin Less distortion in sample in visual Image of the samples welded using cylindrical pin & tapered pin:
4 Fig-1 Image of the welded samples: B. IMMERSION ULTRASONIC TESTING: Immersion Ultrasonic C scan testing had been carried out using a probe with frequency of 5 MHz, focal length of 2 and water acting as a couplant. The sound wave velocity of aluminium is 6300 m/s. sound velocity in water 1500 m/s. Water path distance was 50.8 mm.the acqut software had been used to load the requires data for the scan. The sample was scanned with resolution of 0.1 mm along the joining as well as across the joining. The scanning was done along y-axis for a length of 130 mm and indexed along x- axis for the length of 45 mm. The first signal amplitude from the ultrasonic test method shows the front wall echo whereas the second signal amplitude shows the back wall echo. Detection and localization of defect were done by the A, B and C scan. RESULTS AND DISCUSSION: C-scan ultrasonic studies were carried out on the FSW joint using a 5 MHz point focused immersion transducer, focused at the weld region. A reference standard was created for AA 1100 and AA 2014 to interpret the signals coming from the defect. Out of six samples two samples were taken for the study. Each and every point in the samples was scanned and interpreted. Reference sample was taken for predicting the nature and kind of different defect in A-2-T and B-2-T samples.
5 Result of varies echo coming from different artificial defects in reference standard: Fig-2 C-scan image of the reference sample Thus using reference sample it was easy to understand how the ultrasonic signal respond to the different defects oriented at different location was studied. The C-scan image of the sample A-2-T was taken and it had been analyzed for the defect using exqut software. With the combined aid of A-Scan it was easy to point out the orientation of defects in the sample. Result of the A-2-T sample (710 rpm& 20 mm/min.):
6 Fig-3 C-scan image of A-2-T sample welded at 710 rpm with feed rate of 20 mm/min. Result of B-2-T (900 rpm & 40 mm/min):
7 Fig-4 C-scan image of B-2-T sample welded at 900 rpm with feed rate of 40 mm/min. The complete interpretation of the weld region of the sample B-2-T was done using C-Scan with the combined aid of A-scan and B-scan it has been concluded that B-2-T sample is free from defects. Thus from the above study it is clear that C-scan can be effectively used for assessing the bond integrity of FSW joints in a Non-destructive way. The detailed analysis also can pinpoint the de-bond location and help in the accept/reject criteria for such joints. CONCLUSIONS: In the present study, ultrasonic C-scan evaluation was carried out on Aluminium alloy dissimilar metal joint welded using FSW. The study revealed that there were disbonds, tunnel defect,cavity and kissing-bond present in the joint. Visual testing and liquid penrtrant testing were carried out on the welded sample. Out of six samples four has been pointed as defective samples visualy. The sample A-2-T and B-2-T had been taken liquid penetrant testing for pin pointing the surface cracks. The A-2-T is found to have surface defects and B-2-T is free from defects. Furter the sample A-2-T and B-2-T had been taken ultrasonic C- scan. The sample A-2-T has different internal defects. The shape and orientation of the defect had been studied using C-scan. With A-scan it had been studied how the defects responds to the ultrasonic signal. Detailed analysis showed that the sample welded at the speed of 900 rpm with feed rate of 40 mm/min feed rate was free from defects. References: 1. E.D. Nicholas and W.M. Thomas, A Review of Friction Processes for Aerospace Applications, Int. J. Mater. Prod. Technol., 1998, 13(1 2), p 45 55
8 2. Berger DD. Vacuum brazing titanium to inconel. Welding Journal 1995; 74 (11): Y.S. Sato, H. Kokowa, M. Enomoto, and S. Jogan, Microstructural Evolution of 6063 Aluminum During Friction-Stir Welding, Metall. Mater. Trans. A, 1999, 30A, p S. Xu, X. Deng, A.P. Reynolds, and T.U. Seidel, Finite Element Simulation of Material Flow in Friction Stir Welding, Sci. Technol. Weld. Join., 2001, 6(3), p P.L. Threadgill, A.J. Leonard, H.R. Shercliff, and P.J. Withers, Friction StirWelding of Aluminium Alloys, Int. Mater. Rev., 2009, 54(2), p R.S. Mishra and Z.Y. Ma, Friction Stir Welding and Processing, Mater. Sci. Eng. R, 2005, 50, p Gordon GA, Canumallas, Tittmann BR. Ultrasonic C-scan imaging for materials characterization. Ultrasonics 1993; 31 (5): Moghisi M, Almond DP. An inexpensive computer-controlled ultrasonic C scan system. NDT Intl. 1983; 16 (1) Anish Kumar et al. Development and applications of C-scan Ultrasonic Facility BARC News Letter Founder s day Special. 2007;
Non-Destructive Testing of Dissimilar Friction Stir Welds
, July 4-6, 2012, London, U.K. Non-Destructive Testing of Dissimilar Friction Stir Welds Esther T. Akinlabi Member, IAENG, Adrian C. S. Levy and Stephen A. Akinlabi Member, IAENG Abstract This paper reports
More informationTensilel Properties of AA6061-T6/SiC p Surface Metal Matrix Composite Produced By Friction Stir Processing
Tensilel Properties of AA6061-T6/SiC p Surface Metal Matrix Composite Produced By Friction Stir Processing Devaraju Aruri, Adepu Kumar & B Kotiveerachary Department of Mechanical Engineering, National
More informationPROPERTIES OF AW 5059 ALUMINIUM ALLOY JOINTS WELDED BY MIG AND FRICTION STIR WELDING (FSW)
Journal of KONES Powertrain and Transport, Vol. 20, No. 3 2013 PROPERTIES OF AW 5059 ALUMINIUM ALLOY JOINTS WELDED BY MIG AND FRICTION STIR WELDING (FSW) Miros aw Czechowski Gdynia Maritime University
More informationFriction Stir Welding of AA2024-T3 plate the influence of different pin types
Mech. Sci., 6, 5155, 2015 doi:10.5194/ms-6-51-2015 Author(s) 2015. CC Attribution 3.0 License. Friction Stir Welding of AA2024-T3 plate the influence of different pin types D. Trimble, H. Mitrogiannopoulos,
More informationInternational Journal of Advance Engineering and Research Development Volume 4, Issue 2, February -2017
Scientific Journal of Impact Factor (SJIF): 4.72 e-issn (O): 2348-4470 p-issn (P): 2348-6406 International Journal of Advance Engineering and Research Development Volume 4, Issue 2, February -2017 Optimization
More informationA Study of Influence of Parameters of Dissimilar Materials Joining on Friction Stir Welding Process by Design of Experimental
Proceedings of the 5th IASME/WSEAS Int. Conference on Heat Transfer, Thermal Engineering and Environment, Athens, Greece, August 25-27, 2007 129 A Study of Influence of Parameters of Dissimilar Materials
More informationLap Joint of A5083 Aluminum Alloy and SS400 Steel by Friction Stir Welding
Materials Transactions, Vol. 46, No. 4 (2005) pp. 835 to 841 #2005 The Japan Institute of Metals Lap Joint of A5083 Aluminum Alloy and SS400 Steel by Friction Stir Welding Kittipong Kimapong* and Takehiko
More informationParametric Optimization for Friction Stir Welding of Al6061 Alloy using Taguchi Technique
Parametric Optimization for Friction Stir Welding of Al6061 Alloy using Taguchi Technique Lingam Satyavinod 1, R Harikishore 2 1 Student, Department of Mechanical Engineering, DNREng College, Bhimavaram,
More informationResidual Stress Measurement Techniques: A Review
Residual Stress Measurement Techniques: A Review Nasir Khan 1, Research Scholar Amity University, Gwalior Dr. Anshul Gangele 2 Professor, Amity University Gwalior Abstract Compressive residual stresses
More informationINFLUENCE OF FRICTION STIR WELDING ON CORROSION PROPERTIES OF AW-7020M ALLOY IN SEA WATER
DOI: 10.1515/adms-2015-0002 K. Dudzik 1, W. Jurczak 2 1 Gdynia Maritime University, Faculty of Marine Engineering, Marine Maintenance Department, Gdynia, Poland 2 Polish Naval Academy, Mechanical Electrical
More informationFriction Stir Welding of High Carbon Tool Steel (SK85) below Eutectoid Temperature
Friction Stir Welding of High Carbon Tool Steel (SK85) below Eutectoid Temperature CHUNG Young Dong*, FUJII Hidetoshi**, NAKATA Kazuhiro*** and NOGI Kiyoshi*** Abstract The present study is concerned with
More informationMacro and Micro Structural Characteristics of Dissimilar Friction Stir Welded AA7075 T651- AA6061 T651 Butt Joint
, July 3-5, 2013, London, U.K. Macro and Micro Structural Characteristics of Dissimilar Friction Stir Welded AA7075 T651- AA6061 T651 Butt Joint S.Ravikumar, Member, IAENG, V.Seshagiri Rao, R.V.Pranesh,
More informationFRICTION STIR WELDING PROCESS PARAMETERS FOR JOINING DISSIMILAR ALUMINUM ALLOYS
International Journal Journal of Mechanical of Mechanical Engineering Engineering and Technology (IJMET), ISSN 0976 6340(Print), ISSN and Technology (IJMET), ISSN 0976 6340(Print) ISSN 0976 6359(Online)
More informationEffect Of Friction Stir Processing On Mechanical Properties And Microstructure Of The Cast Pure Aluminum
INTERNATIONAL JOURNAL OF SCIENTIFIC & TECHNOLOGY RESEARCH VOLUME 2, ISSUE 12, DECEMBER 2013 ISSN 2277-8616 Effect Of Friction Stir Processing On Mechanical Properties And Microstructure Of The Cast Pure
More informationEffect of Low Feed Rate FSP on Microstructure and Mechanical Properties of Extruded Cast 2285 Aluminum Alloy
614 J. Mater. Sci. Technol., Vol.23 No.5, 2007 Effect of Low Feed Rate FSP on Microstructure and Mechanical Properties of Extruded Cast 2285 Aluminum Alloy L.Karthikeyan 1), V.S.Senthilkumar 2), D.Viswanathan
More informationNUMERICAL SIMULATION OF FRICTION STIR BUTT WELDING PROCESSES FOR AZ91 MAGNESIUM ALLOY
NUMERICAL SIMULATION OF FRICTION STIR BUTT WELDING PROCESSES FOR AZ91 MAGNESIUM ALLOY K. Senthil Kumar 1, M. Sivasangari 2, V. Rubesh Raj 3, L. Nirmal Raj 4 1 Assistant Professor, MAR College of Engg &
More informationMetallurigical and Materials Engineering Department, National Institute of Technology, Tiruchirappalli, India
More Info at Open Access Database www.ndt.net/?id=15212 Non-Destructive Evaluation Of Aluminum A6061-T6 Welds Produced by Friction Stir spot Welding Y.V.V.M. Mohana Rao 1, V.Kalyanavalli 1, D.Sastikumar
More informationTHE APPLICATION OF FRICTION STIR WELDING (FSW) OF ALUMINIUM ALLOYS IN SHIPBUILDING AND RAILWAY INDUSTRY
Journal of KONES Powertrain and Transport, Vol. 24, No. 2 2017 THE APPLICATION OF FRICTION STIR WELDING (FSW) OF ALUMINIUM ALLOYS IN SHIPBUILDING AND RAILWAY INDUSTRY Grzegorz Gesella, Mirosław Czechowski
More informationFriction Stir Lap Welding of Magnesium Alloy and Zinc-Coated Steel
Materials Transactions, Vol. 5, No. 11 (29) pp. 2598 to 263 #29 The Japan Institute of Metals Friction Stir Lap Welding of Magnesium Alloy and Zinc-Coated Steel Y. C. Chen* and K. Nakata Joining and Welding
More informationExperimental Investigation of Tensile Strength and Deflection Characteristics of Friction Stir Welded Aluminum AA 6351 Alloy Joint
IOSR Journal of Mechanical and Civil Engineering (IOSR-JMCE) e-issn: 2278-1684,p-ISSN: 2320-334X, Volume 7, Issue 5 (Jul. - Aug. 2013), PP 01-06 Experimental Investigation of Tensile Strength and Deflection
More informationEVALUATION OF MECHANICAL PROPERTIES OF FRICTION WELDED JOINTS OF EN-24 STEEL CYLINDRICAL RODS
Research Paper ISSN 227 049 www.ijmerr.com Vol. 3, No. 4, October, 204 204 IJMERR. All Rights Reserved EVALUATION OF MECHANICAL PROPERTIES OF FRICTION WELDED JOINTS OF STEEL CYLINDRICAL RODS G Samuthiram
More informationCOMPUTER SIMULATION AND EXPERIMENTAL RESEARCH OF CAST PISTON POROSITY
Tome V (year 2007), Fascicole 2, (ISSN 1584 2665) COMPUTER SIMULATION AND EXPERIMENTAL RESEARCH OF CAST PISTON POROSITY D. KAKAS, L. KOVACEVIC, P. TEREK UNIVERSITY OF NOVI SAD, FACULTY OF TECHNICAL SCIENCES,
More informationWeld defects analysis of 60 mm thick SS316L mock-ups of TIG and EB welds by Ultrasonic inspection for fusion reactor vacuum vessel applications
More info about this article: http://www.ndt.net/?id=21122 Weld defects analysis of 60 mm thick SS316L mock-ups of TIG and EB welds by Ultrasonic inspection for fusion reactor vacuum vessel applications
More informationMACROSTRUCTURE, MICROSTRUCTURE AND MICROHARDNESS ANALYSIS
109 Chapter 5 MACROSTRUCTURE, MICROSTRUCTURE AND MICROHARDNESS ANALYSIS 5.1 INTRODUCTION The microstructural studies of friction welding helps in understanding microstructural changes occurred during friction
More informationrelated to the welding of aluminium are due to its high thermal conductivity, high
Chapter 7 COMPARISON FSW WELD WITH TIG WELD 7.0 Introduction Aluminium welding still represents a critical operation due to its complexity and the high level of defect that can be produced in the joint.
More informationFriction Stir Processing of 304L Stainless Steel for Crack Repair
Friction Stir Processing of 304L Stainless Steel for Crack Repair M.P. Miles, C. Gunter, F. Liu and T.W. Nelson Abstract Friction stir processing (FSP) was investigated as a method for repairing cracks
More informationFriction Stir Welding of Dissimilar Materials Statistical Analysis of the Weld Data
Friction Stir Welding of Dissimilar Materials Statistical Analysis of the Weld Data Esther T. Akinlabi Member, IAENG and Stephen A. Akinlabi, Member, IAENG Abstract This paper reports the results of statistical
More informationNon Destructive Evaluation of Rolls of Hot Strip Mill of Tata Steel
Non Destructive Evaluation of Rolls of Hot Strip Mill of Tata Steel J C Pandey, Manish Raj, & O N Mohanty NDE2002 predict. assure. improve. National Seminar of ISNT Chennai, 5. 7. 12. 2002 www.nde2002.org
More informationOPTIMIZATION OF WELDING PARAMETER ON AA2014 IN GMAW
OPTIMIZATION OF WELDING PARAMETER ON AA2014 IN GMAW P.Venkadeshwaran 1*, R.Sakthivel 1, R.Sridevi 1, R.Ahamed Meeran 1, K.Chandrasekaran 1 1 Department of Mechanical Engineering, Nadar Saraswathi College
More informationWear Characteristics of Unalloyed and alloyed LM25-Aluminium casting
Wear Characteristics of Unalloyed and alloyed LM25-Aluminium casting Patel Hiteshkumar 1*, Menghani Jyoti 2 S.V. National Institute of Technology, Surat 395 007, Gujarat, India * Corresponding author (E-mails:
More informationAutomated ultrasonic tube-to-tube sheet weld scanning
White Paper Automated ultrasonic tube-to-tube sheet weld scanning By: J. Peter Bertelsen & Zdravko Kishev, Advanced NDT Global Abstract This paper describes an advantageous ultrasonic technique for in-depth
More informationJoining of Dissimilar Automotive Materials
Joining of Dissimilar Automotive Materials P.K. Mallick William E. Stirton Professor of Mechanical Engineering Director, Center for Lighweighting Automotive Materials and Processing University of Michigan-Dearborn
More informationEFFECT OF REINFORCED PARTICULATES (SiC and Al 2 O 3 ) ON FRICTION STIR WELDED JOINT OF MAGNESIUM ALLOY AZ91
International Journal of Scientific & Engineering Research, Volume 6, Issue 4, April-2015 1219 EFFECT OF REINFORCED PARTICULATES (SiC and Al 2 O 3 ) ON FRICTION STIR WELDED JOINT OF MAGNESIUM ALLOY AZ91
More informationEvaluation of Friction Stir Spot Welding Process by Laser Ultrasonic Method with Synthetic Aperture Focusing Technique
9 th World Conference on Non-Destructive Testing 6 Evaluation of Friction Stir Spot Welding Process by Laser Ultrasonic Method with Synthetic Aperture Focusing Technique Zhenggan ZHOU, Kuanshuang ZHANG
More informationMECHANICAL PROPERTIES ON FRICTION STIR WELDING OF ALUMINUM ALLOY 5052
MECHANICAL PROPERTIES ON FRICTION STIR WELDING OF ALUMINUM ALLOY 5052 Rusdi Nur 1, 2, Ahmad Zubair Sultan 1, 2 and Muhammad Arsyad Suyuti 1, 2 1 Department of Mechanical Engineering, Politeknik Negeri
More informationUltrasonic Inspection of Sub-Surface Defects In Aluminium Die-Castings 71
Ultrasonic Inspection of Sub-Surface Defects In Aluminium Die- Castings by Suresh Palanisamy (CAST) A/Prof. Romesh Nagarajah Dr. Pio Iovenitti Abstract Non-destructive testing using ultrasonic measurement
More informationThe effect of ER4043 and ER5356 filler metal on welded Al 7075 by metal inert gas welding
This paper is part of the Proceedings of the 2 International Conference on nd High Performance and Optimum Design of Structures and Materials (HPSM 2016) www.witconferences.com The effect of ER4043 and
More informationUSE OF LASER AND FRICTION STIR WELDING FOR AEROSPACE MAGNESIUM ALLOYS
Proceedings of the Light Metals Technology Conference 27 USE OF LASER AND FRICTION STIR WELDING FOR AEROSPACE MAGNESIUM ALLOYS X. Cao, M. Jahazi Aerospace Manufacturing Technology Centre, Institute for
More informationWear characteristics of a WC Co tool in friction stir welding of AC4AC30 vol%sicp composite
International Journal of Machine Tools & Manufacture 45 (2005) 1635 1639 www.elsevier.com/locate/ijmactool Wear characteristics of a WC Co tool in friction stir welding of AC4AC30 vol%sicp composite H.J.
More informationMicrostructural Characteristics and Mechanical Properties of Single-Mode Fiber Laser Lap-Welded Joint in Ti and Al Dissimilar Metals
Transactions of JWRI, Vol.42 (2013), No. 1 Microstructural Characteristics and Mechanical Properties of Single-Mode Fiber Laser Lap-Welded Joint in Ti and Al Dissimilar Metals Su-Jin LEE Su-Jin*, LEE*,
More informationSurface Morphology and Mechanical Properties. of Aluminum-Copper Joints Welded. by Friction Stir Welding
Contemporary Engineering Sciences, Vol. 7, 2014, no. 5, 219-230 HIKARI Ltd, www.m-hikari.com http://dx.doi.org/10.12988/ces.2014.31167 Surface Morphology and Mechanical Properties of Aluminum-Copper Joints
More informationEFFECT OF WELDING PARAMETERS ON THE MECHANICAL PROPERTIES OF FRICTION STIR WELDED DISSIMILAR ALUMINIUM ALLOYS 6101 & 6082
EFFECT OF WELDING PARAMETERS ON THE MECHANICAL PROPERTIES OF FRICTION STIR WELDED DISSIMILAR ALUMINIUM ALLOYS 6101 & 6082 Omesh Jindal 1, Sandeep Sharma 2, Lovepreet Singh 3 1 Assistant Professor, Mechanical
More informationFriction Welding of magnesium alloys
5th International Conference on Advanced Design and Manufacturing Engineering (ICADME 2015) Friction Welding of magnesium alloys Zhongbao Shen 1, Ranfeng. Qiu 2,Qingzhe Li, Longlong Hou, Lihu Cui Materials
More informationAIR QUENCHING OF ALUMINUM: THE AFFECT OF QUENCH ORIENTATION AND AIR VELOCITY
AIR QUENCHING OF ALUMINUM: THE AFFECT OF QUENCH ORIENTATION AND AIR VELOCITY A Major Qualifying Project Report Submitted to the Faculty of WORCESTER POLYTECHNIC INSTITUTE In partial fulfillment of the
More informationMODERN ULTRASONIC TECHNIQUES FOR DEFECT DETECTION IN CAST MATERIALS
MODERN ULTRASONIC TECHNIQUES FOR DEFECT DETECTION IN CAST MATERIALS INTRODUCTION S. Palit Sagar National Metallurgical Laboratory, Jamshedpur 831007 e-mail : sarmi@nmlindia.org In casting flaw detection
More informationAgeing Behavior of Friction Stir Welding AA7075-T6 Aluminum Alloy
Ageing Behavior of Friction Stir Welding AA7075-T6 Aluminum Alloy T. AZIMZADEGAN*, GH.KHALAJ*, M.M. KAYKHA**, A.R.HEIDARI*** *Department of Materials Science and Engineering, Saveh branch, Islamic Azad
More informationCHAPTER 4 OPTIMIZATION OF PROCESS PARAMETER OF FSW ON AA 5083 USING TAGUCHI METHOD (SINGLE OBJECTIVE)
52 CHAPTER 4 OPTIMIZATION OF PROCESS PARAMETER OF FSW ON AA 5083 USING TAGUCHI METHOD (SINGLE OBJECTIVE) 4.1 INTRODUCTION Welding is one of the vital and widely used manufacturing processes in any manufacturing
More informationMicrostructure Study of Diffusion Bonding of Centrifuged Structural Steel-Bronze
ARCHIVES of FOUNDRY ENGINEERING DOI: 10.1515/afe-2016-0034 Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (2299-2944) Volume 16 Issue 2/2016 99 104 Microstructure
More informationReading assignment. Nondestructive evaluation (NDE) Nondestructive testing (NDT) Penetrant. Conventional NDE mthods. Topic 7
Reading assignment Nondestructive evaluation (NDE) Topic 7 Notes on Nondestructive Evaluation in the course website. Sec. 8.2, 8.3 and 8.4, William Callister, Materials Science and Engineering, 6 th Ed.
More informationSTUDIES ON MICROSTRUCTUREAND MECHANICAL PROPERTIES OFMODIFIED LM25 ALUMINIUM ALLOY
STUDIES ON MICROSTRUCTUREAND MECHANICAL PROPERTIES OFMODIFIED LM25 ALUMINIUM ALLOY Venkatachalam G 1, Kumaravel A 2,Arun Kumar N 3, Dhanasekaran Rajagopal 4 1,2,4 Department of Mechanical Engineering,
More informationRoll Bonding or Roll Welding
1 2 3 4 Roll Bonding or Roll Welding The pressure required for welding is applied through a pair of rolls Can be performed hot (Hot Roll Bonding) Surface preparation is important for interfacial bonding
More informationSolid State Friction Stir Welding (FSW) on Similar and Dissimilar Metals
, July 3-5, 2013, London, U.K. Solid State Friction Stir Welding (FSW) on Similar and Dissimilar Metals Sivaprakasam Thamizhmanii, Mohd Azizee Sukor, and Sulaiman Abstract Welding is a process which helps
More informationMonitoring Of Adhesive Cure Process and Following Evaluation of Adhesive Joint Structure by Acoustic Techniques
ECNDT 006 - We... Monitoring Of Adhesive Cure Process and Following Evaluation of Adhesive Joint Structure by Acoustic Techniques Elena Yu. MAEVA, Ina SEVIARYNA, Gilbert B. CHAPMAN, Fedar M. SEVERIN University
More informationResearch and Development on NDE field
VTT TECHNICAL RESEARCH CENTRE OF FINLAND LTD Research and Development on NDE field IAEA Technical Meeting on the Optimization of Non-Destructive Examination and In-Service Inspection to Improve Nuclear
More informationFSW Welding of Aluminium Casting Alloys
ARCHIVES of FOUNDRY ENGINEERING DOI: 10.1515/afe-2016-0038 Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (2299-2944) Volume 16 Issue 2/2016 119 124 FSW
More informationChapter 30 Fundamentals of Joining. Materials Processing. Topics. MET Manufacturing Processes
MET 33800 Manufacturing Processes Chapter 30 Fundamentals of Joining Before you begin: Turn on the sound on your computer. There is audio to accompany this presentation. Materials Processing Chapters 11-13
More informationArch. Metall. Mater., Vol. 61 (2016), No 2B, p
Arch. Metall. Mater., Vol. 61 (2016), No 2B, p. 997 1001 DOI: 10.1515/amm-2016-0170 B. SZWED* #, M. KONIECZNY* MICROSTRUCTURE AND MECHANICAL PROPERTIES OF JOINTS OF TITANIUM WITH STAINLESS STEEL PERFORMED
More informationAmerican International Journal of Research in Formal, Applied & Natural Sciences
American International Journal of Research in Formal, Applied & Natural Sciences Available online at http://www.iasir.net ISSN (Print): 2328-3777, ISSN (Online): 2328-3785, ISSN (CD-ROM): 2328-3793 AIJRFANS
More informationANALYSIS AND DESIGN OF FRICTION STIR WELDING
Int. J. Mech. Eng. & Rob. Res. 2013 A M Khourshid and I Sabry, 2013 Research Paper ISSN 2278 0149 www.ijmerr.com Vol. 2, No. 3, July 2013 2013 IJMERR. All Rights Reserved ANALYSIS AND DESIGN OF FRICTION
More informationCharacterization of Titanium Alloy Friction Stir Butt-Welds TIMET 54M, ATI 425 and BOATI Standard Grain
Characterization of Titanium Alloy Friction Stir Butt-Welds TIMET 54M, ATI 425 and BOATI Standard Grain A. Cantrell, K. Gangwar, and M. Ramulu University of Washington Dan Sanders The Boeing Company 7th
More informationEffect of weld parameter on mechanical and metallurgical properties of dissimilar joints AA6082 AA6061 in T 6 condition produced by FSW
H.S. Patil et alii, Frattura ed Integrità Strutturale, 24 (2013) 151-160; DOI: 10.3221/IGF-ESIS.24.16 Effect of weld parameter on mechanical and metallurgical properties of dissimilar joints AA6082 AA6061
More informationNOVEL NONDESTRUCTIVE EVALUATION TECHNIQUES FOR
NOVEL NONDESTRUCTIVE EVALUATION TECHNIQUES FOR INERTIA-FRICTION WELDS IN A SiC-REINFORCED HIGH-TEMPERATURE ALUMINUM ALLOY Peter B. Nagy, Laszlo Adler and William A. Baeslack III Department of Industrial,
More informationCHAPTER 3: TYPES OF WELDING PROCESS, WELD DEFECTS AND RADIOGRAPHIC IMAGES. Welding is the process of coalescing more than one material part at
41 CHAPTER 3: TYPES OF WELDING PROCESS, WELD DEFECTS AND RADIOGRAPHIC IMAGES 3.0. INTRODUCTION Welding is the process of coalescing more than one material part at their surface of contact by the suitable
More informationThe Need For Protecting The Weld And Rationale
The Need For Protecting The Weld And Rationale This chapter presents the need of protecting the weld and rationale behind variations in cleanliness of the weld developed by different welding processes.
More informationEffective PA UT Inspection Techniques for Austenitic Welds
Effective PA UT Inspection Techniques for Austenitic Welds Guy MAES, Johan BERLANGER, Frédéric LAPRISE (Zetec, Quebec, Canada) NDTMA 2017 Las Vegas, February 15, 2017 Zetec Inc. All right reserved 1 Introduction
More informationEXPERIMENTAL INVESTIGATIONS ON TIG WELDING OF ALUMINIUM 6351 ALLOY
EXPERIMENTAL INVESTIGATIONS ON TIG WELDING OF ALUMINIUM 6351 ALLOY * Venkata Ramana M 1, Sriram P S N 2 and Jayanthi A 3 Department of Automobile Engineering, VNR Vignana Jyothi Institute of Engineering
More informationEffect of Process Parameters on Resistance Spot Welding - A Review
Effect of Process Parameters on Resistance Spot Welding - A Review Jeevan A. Karande 1, Dr. K. H. Inamdar 2 1 PG Student, 2 Associate Professor, Department of Mechanical Engineering, Walchand College of
More informationULTRASONIC NON-DESTRUCTIVE EVALUATION FOR SPOT WELDING IN THE AUTOMOTIVE INDUSTRY
ULTRASONIC NON-DESTRUCTIVE EVALUATION FOR SPOT WELDING IN THE AUTOMOTIVE INDUSTRY N. Wylie 1, S.R. Wylie. J.D. Cullen and A.I. Al-Shamma a Liverpool John Moores University, RF and Microwave Group, Byrom
More informationWEAR AND MECHANICAL PROPERTIES OF ALUMINIUM HYBRID COMPOSITE (AL2024/AL 2 O 3 /GRAPHITE) FABRICATED BY POWDER METALLURGY
Volume 116 No. 23 2017, 231-236 ISSN: 1311-8080 (printed version); ISSN: 1314-3395 (on-line version) url: http://www.ijpam.eu ijpam.eu WEAR AND MECHANICAL PROPERTIES OF ALUMINIUM HYBRID COMPOSITE (AL2024/AL
More informationA COMPARATIVE STUDY OF LASER, CMT, LASER-PULSE MIG HYBRID AND LASER-CMT HYBRID WELDED ALUMINIUM ALLOY Paper 1304
A COMPARATIVE STUDY OF LASER, CMT, LASER-PULSE MIG HYBRID AND LASER-CMT HYBRID WELDED ALUMINIUM ALLOY Paper 1304 Chen Zhang, Ming Gao, Geng Li, Xiaoyan Zeng Wuhan National Laboratory for Optoelectronics,
More informationOPTIMIZATION OF PROCESS PARAMETERS FOR FRICTION STIR WELDED AA7075 SIC COMPOSITE JOINTS BY TAGUCHI METHOD
OPTIMIZATION OF PROCESS PARAMETERS FOR FRICTION STIR WELDED AA7075 SIC COMPOSITE JOINTS BY TAGUCHI METHOD Dhairya Pratap Singh Department of Mechanical Engineering YMCAUST Faridabad (HR), India e-mail:
More informationPhased Array Ultrasonic Testing for Heavy Wall Austenitic Stainless Steel Welds. Abstract
Phased Array Ultrasonic Testing for Heavy Wall Austenitic Stainless Steel Welds More info about this article: http://www.ndt.net/?id=21155 YokeshG Ravichandran,P. S. SanathThampi, Suresh Jakkula, G.Selvakumar,
More informationFriction Stir Welding of Iron and Nickel Alloys
Friction Stir Welding of Iron and Nickel Alloys Carl D. Sorensen Brigham Young University Acknowledgements Tool materials and fabrication provided by Megastir Technologies, a business alliance between
More informationThe Influence of Grain Size of Dissimilar Welding between Carbon Steel and Stainless Steel on Ultrasonic Testing
International Conference on Test, Measurement and Computational Method (TMCM 2015) The Influence of Grain Size of Dissimilar Welding between Carbon Steel and Stainless Steel on Ultrasonic Testing Kwanruethai
More informationMechanical and Die Soldering Properties of Al-Si-Mg Alloys with Vacuum HPDC Process
Proceedings of the 12th International Conference on uminium loys, September 5-9, 21, Yokohama, Japan 21 The Japan Institute of Light Metals pp. 1768-1773 1768 Mechanical and Soldering Properties of -Si-Mg
More informationDRY SLIDING WEAR BEHAVIOUR OF STIR CAST LM 25/ZrO 2 METAL MATRIX COMPOSITES
Govindan Karthikeyan GowthamiThankachi Raghuvaran Jinu ISSN 1333-1124 eissn 1849-1391 DRY SLIDING WEAR BEHAVIOUR OF STIR CAST LM 25/O 2 METAL MATRIX COMPOSITES Summary In the present study, an investigation
More informationLaser Additive Manufacturing as a Key Enabler for the Manufacture of Next Generation Jet Engine Components - Technology Push
Laser Additive Manufacturing as a Key Enabler for the Manufacture of Next Generation Jet Engine Components - Technology Push EU Project Merlin New Challenges and Perspectives for LAM Processes Carl Hauser,
More informationInternational Journal of Scientific & Engineering Research Volume 3, Issue 7, July ISSN
International Journal Scientific & Engineering Research Volume 3, Issue 7, July-01 1 EFFECT OF MAGNESIUM ENHANCEMENT ON MECHANICAL PROPERTY AND WEAR BEHAVIOUR OF LM6 ALUMINUM ALLOY R. S. Rana and Rajesh
More informationEffects of Laser Peening, and Shot Peening on Friction Stir Welding
Effects of Laser Peening, and Shot Peening on Friction Stir Welding Omar Hatamleh, PhD omar.hatamleh1@.hatamleh1@jsc.nasa.gov Structural Engineering Division NASA Johnson Space Center Lloyd Hackel, Jon
More informationNS 1.0 Nobles Specification Technical and Quality Requirements for Castings
1. Scope The scope of this specification is to define the technical and quality requirements of casting to be used by Nobles Worldwide in the production of military products. The primary focus of this
More informationMechanical Properties, Welding Joints of Similar & Disimilar Aluminium Alloys Aa6061
International Refereed Journal of Engineering and Science (IRJES) ISSN (Online) 2319-183X, (Print) 2319-1821 Volume 4, Issue 6 (June 2015), PP.116-125 Mechanical Properties, Welding Joints of Similar &
More informationHigh speed friction stir welding of aluminium alloys
High speed friction stir welding of aluminium alloys D. M. Rodrigues* 1, C. Leitão 1, R. Louro 2, H. Gouveia 2 and A. Loureiro 1 In this paper, the weldability of AA 5083-H111 (non-heat treatable) and
More informationAdemand for lighter and stronger aluminium armour
International Journal of Agricultural Engineering, Vol. 2 No. 2 (October 2009 to March 2010) : 202-206 Research Paper : Process optimization in joining aluminium alloy 7039 using TIG arc welding process
More informationStephen Cater FRIN MEI Friction and Forge Processes Department Joining Technologies Group
Title: Authors: Friction stir welding of steel for marine applications Athanasios Toumpis a, Alexander Galloway a, Stephen Cater b, Paul Burling b Chris Stanhope b a University of Strathclyde, Glasgow,
More informationSAFEJOINT Workshop 3-4 July 2014, Athens
Enhancing structural efficiency through novel dissimilar material joining techniques National Technical University of Athens School of Chemical Engineering Department of Materials Science and Engineering
More informationMetallurgy and Friction Stir Welding. Anne Denquin Onera, Châtillon, France Department of Metallic Structures and Materials
Metallurgy and Friction Stir Welding Anne Denquin Onera, Châtillon, France Department of Metallic Structures and Materials Basics of the FSW Process Typical temperature domain for Al alloys : 200 C ()
More information1. IMPERFECTIONS OF THE WELDED CONNECTION
1. IMPERFECTIONS OF THE WELDED CONNECTION A. Classification of imperfections in the welds acc. to EN 26520 (ISO 6520) Crack (100) - imperfection produced by a local rupture in the solid state which can
More informationWeldability Analysis of 316 Stainless Steel and AA1100 Alloy Hollow Tubes using Rotational Friction Welding Process
ISSN (Online): 9-7064 Index Copernicus Value (0): 6.4 Impact Factor (05): 6.9 Weldability Analysis of 6 Stainless Steel and AA00 Alloy Hollow Tubes using Rotational Friction Welding Process Y. Lekhana,
More informationDesign and Analysis of Molybdenum Super Alloy FSW Tools
Research Article International Journal of Current Engineering and Technology E-ISSN 2277 4106, P-ISSN 2347-5161 2014 INPRESSCO, All Rights Reserved Available at http://inpressco.com/category/ijcet Design
More informationADHESIVE CURE MONITORING WITH ACOUSTIC METHOD
ADHESIVE CURE MONITORING WITH ACOUSTIC METHOD I. Severina, E. Maeva Industrial Research Chair In Applied Solid State Physics and Material Characterization, University of Windsor, Windsor, Canada Abstract:
More informationMichael T. Anderson, Stephen E. Cumblidge, Steven R. Doctor Pacific Northwest National Laboratory, Richland, WA, USA
THROUGH WELD INSPECTION OF WROUGHT STAINLESS STEEL PIPING USING PHASED ARRAY ULTRASONIC PROBES Michael T. Anderson, Stephen E. Cumblidge, Steven R. Doctor Pacific Northwest National Laboratory, Richland,
More informationTHE IMPORTANCE OF FRICTION STIR WELDING TOOL
Production Processes and Systems, vol. 6. (2013) No. 1., pp. 25-34. THE IMPORTANCE OF FRICTION STIR WELDING TOOL Ákos Meilinger, Imre Török University of Miskolc, Department of Mechanical Technology Abstract
More informationAvailable online at ScienceDirect. Procedia Engineering 183 (2017 )
Available online at www.sciencedirect.com ScienceDirect Procedia Engineering 183 (2017 ) 245 250 17th International Conference on Sheet Metal, SHEMET17 Mechanical properties and formability of cold rolled
More informationNEW HEAT TREATMENT FOR Al HIGH PRESSURE DIE-CASTINGS
NEW HEAT TREATMENT FOR Al HIGH PRESSURE DIE-CASTINGS Conventionally produced H aluminum alloy high pressure die-castings containing normal porosity levels can be successfully heat treated without incurring
More informationApplication of Non-Destructive Testing Techniques for the Assessment of Casting of AA5083 Alloy
Application of Non-Destructive Testing Techniques for the Assessment of Casting of AA5083 Alloy J. Idris *,a and A. Al-Bakoosh b Department of Materials Engineering, Faculty of Mechanical Engineering,
More informationResidual stresses distribution in TIG weldments of AA 6061 T6 Aluminium alloy
Residual stresses distribution in TIG weldments of AA 6061 T6 Aluminium alloy 1 Hemadri Naidu.T, 2 Chennakeshavalu K 1 Research Scholar, KSIT, VTU, Bangalore, Karnataka, 560062, India. 2 Principal, EWIT,VTU,
More informationAvailable online at ScienceDirect. Procedia Engineering 183 (2017 )
Available online at www.sciencedirect.com ScienceDirect Procedia Engineering 183 (2017 ) 213 218 17th International Conference on Sheet Metal, SHEMET17 Design of stamping processes of pinless FSWed thin
More information