1 SURFACE VEHICLE STANDARD J434 Issued Revised REV. FEB2004 Superseding J434 JUN1986 (R) Automotive Ductile (Nodular) Iron Castings 1. Scope This SAE standard covers the minimum mechanical properties measured on separately cast test pieces of varying thickness and microstructural requirements for ductile iron castings used in automotive and allied industries. Castings may be specified in the as-cast or heat-treated condition. If castings are heattreated, prior approval from the customer is required. The appendix provides general information on chemical composition, microstructure and casting mechanical properties, as well as other information for particular service conditions. In this standard SI units are primary and in-lb units are derived. 2. References 2.1 Applicable Publications The following publications form a part of the specification to the extent specified herein. Unless otherwise indicated, the latest revision of SAE publications shall apply ASTM INTERNATIONAL PUBLICATIONS Available from ASTM INTERNATIONAL, 100 Barr Harbor Drive, West Conshohocken, PA ASTM E10 -Standard Test Method for Brinell Hardness of Metallic Materials ASTM E23 Standard Test Methods for Notched Bar Impact Testing of Metallic Materials ASTM E111 Standard Test Method for Young's Modulus, Tangent Modulus and Chord Modulus ASTM A247 Standard Test Method for Evaluation the Microstructure of Graphite in Iron Castings ASTM A536 Standard Specification for Ductile Iron Castings STP-455 Gray, Ductile, and Malleable Iron Castings Current Capabilities (out-of-print) SAE Technical Standards Board Rules provide that: This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising therefrom, is the sole responsibility of the user. SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2004 SAE International All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: (inside USA and Canada) Tel: (outside USA) Fax: custsvc@sae.org SAE WEB ADDRESS:

2 2.1.2 OTHER PUBLICATION Metals Handbook, Vol. 1, 2, and 5, 8th Edition, American Society for Metals, Metals Park, OH Gray and Ductile Iron Castings Handbook, Gray and Ductile Iron Founder Society, Cleveland, OH H. D. Angus, Physical Engineering Properties of Cast Iron, British Cast Iron Research Association, Birmingham, England 3. Grades The grades, mechanical properties and metallurgical description are shown in Table 1. TABLE 1 GRADES OF DUCTILE IRON Grade Typical Hardness Range (MPa) Description Relative Wall Thickness Tensile Strength Yield Strength MPa ksi MPa ksi % Elongation D400 (D4018) HBW ( ) or as agreed Ferrite <=20mm >20mm-<=40mm >40mm-<=60mm D450 (D4512) HBW ( ) or as agreed Ferrite- Pearlite <=20mm >20mm-<=40mm >40mm-<=60mm D500 (D5006) HBW ( ) or as agreed Ferrite- Pearlite <=20mm >20mm-<=40mm >40mm-<=60mm D550 (D5504) HBW ( ) or as agreed Pearlite- Ferrite <=20mm >20mm-<=40mm >40mm-<=60mm D700 (D7003) HBW ( ) or as agreed Pearlite <=20mm >20mm-<=40mm >40mm-<=60mm D HBW ( ) or as agreed Pearlite or Tempered Martensite <=20mm >20mm-<=40mm >40mm-<=60mm DQ&T Range Specified By Agreement Tempered Martensite A wide variety of properties are possible. Minimum properties are specified by agreement Between manufacturer and purchaser. NOTE Please refer to ISO 6506 /ASTM E 10 for Brinell Hardness of Metallic Materials Casting properties and microstructure may vary due to chemistry, section size/cooling rate and other parameters. It is desired that separately cast test bars reflect properties of the castings they represent. Casting process for separately cast test pieces shall be agreed upon between manufacturer and purchaser. Refer to ASTM A

3 4. Hardness The hardness ranges shown in Table 1 are for guidelines only. 4.1 The area or areas on the castings where hardness is to be checked should be established by agreement between manufacturer and purchaser. 4.2 The foundry shall exercise the necessary controls and inspection techniques to insure compliance with the typical hardness range. Brinell hardness shall be determined according to ASTM E 10, Standard Test Method for Brinell Hardness of Metallic Materials, after sufficient material has been removed from the casting surface to insure representative hardness readings. The 10mm tungsten ball and 3000kg load shall be used unless otherwise agreed upon. 5. Heat Treatment 5.1 The heat treatment of castings and test specimens produced to this standard in order to meet hardness or other mechanical property requirements, for thermal stress relief or for other purposes is permissible only with the express approval of the casting purchaser. 5.2 Purchaser approval may be blanket or may be issued on a case-by-case basis, as agreed. 5.3 Unless otherwise agreed, the heat treat cycles employed; times, temperatures, rates, quenchants, etc. shall be at the option of the manufacturer. 5.4 Unless otherwise agreed, any separately cast test specimens or any removed from the castings, must accompany the castings they represent as part of the same heat treatment lot(s) or be subjected to the same thermal cycle as the castings they represent, in all respects. 6. Microstructure The graphite component of the microstructure shall consist of at least 80% spheroidal graphite conforming to Types I and II (per ASTM A247) in Fig. 1 (nodularity rating chart developed by the Ductile Iron Society may be used as a guide). The matrix microstructure shall consist of ferrite, ferrite and pearlite, pearlite, tempered pearlite, or tempered martensite, or a combination of these. The microstructure shall be substantially free of primary cementite. The microstructure shall be substantially free of undesirable carbides, the details of which are agreed upon between the casting manufacturer and the purchaser. Examples of matrix microstructures for each grade are shown in Fig

4 FIGURE 1 CLASSIFICATION OF GRAPHITE SHAPE IN CAST IRONS (FROM ASTM A 247) - 4 -

5 D400 D450 FIGURE 2 TYPICAL MATRIX MICROSTRUCTURES (PHOTOS COURTESY OF CLIMAX RESEARCH SERVICES) - 5 -

6 D500 D550 FIGURE 2 TYPICAL MATRIX MICROSTRUCTURES (CONTINUED) (PHOTOS COURTESY OF CLIMAX RESEARCH SERVICES) - 6 -

7 D700 D800 FIGURE 2 TYPICAL MATRIX MICROSTRUCTURES (CONTINUED) (PHOTOS COURTESY OF CLIMAX RESEARCH SERVICES) - 7 -

8 7. Quality Assurance It is the responsibility of the manufacturer to demonstrate process capability. The specimen(s) used to do so shall be of a configuration and from a location agreed upon between the manufacturer and the purchaser. Sampling plans shall be agreed upon between the manufacturer and purchaser. The manufacturer shall employ adequate controls to ensure that the parts conform to the agreed upon requirements. 8. General 8.1 Castings furnished to this standard shall be representative of good foundry practice and shall conform to dimensions and tolerances specified on the casting drawing. 8.2 Minor imperfections usually not associated with the structural functioning may occur in castings. These imperfections are often repairable; however, repairs should be made only in areas and by methods approved by the purchaser. 8.3 Purchaser and manufacturer may agree to additional casting requirements, such as manufacturer identification, other casting information, and special testing. These should appear as additional product requirements on the casting drawing. 9. Notes 9.1 Marginal Indicia The change bar (l) located in the left margin is for the convenience of the user in locating areas where technical revisions have been made to the previous issue of the report. An (R) symbol to the left of the document title indicates a complete revision of the report. PREPARED BY THE SAE AUTOMOTIVE IRON & STEEL CASTINGS COMMITTEE - 8 -

9 A.1 Definition and Classification APPENDIX A APPENDIX DUCTILE (NODULAR) IRON (FOR INFORMATION ONLY) Ductile (nodular) iron, also known as spheroidal graphite iron, is cast iron in which the graphite is present as spheroids, instead of flakes as in gray iron or temper carbon nodules as in malleable iron. A.2 Chemical Composition The typical chemical composition of unalloyed iron generally conforms to the following ranges: TABLE A1 Carbon Silicon Manganese Phosphorus Sulfur Magnesium % % % 0.050% max % max % Individual foundries will produce to narrower ranges than those shown above. The spheroidal graphite structure is produced by alloying the molten iron with small amounts of one or more elements such as magnesium or cerium. The matrix microstructure may be controlled by addition of other alloying elements, such as: copper, tin, nickel, chromium and molybdenum. A.3 Microstructure A.3.1 A.3.2 A.3.3 A.3.4 The microstructure of the various grades of ductile iron consists of spheroidal graphite in a matrix of ferrite, pearlite, tempered pearlite, tempered martensite, or certain combinations of these. The relative amounts of each of these constituents is dependent upon the grade of material specified, casting design as it affects cooling rate, and heat treatments, if any. The matrix microstructure of as-cast ductile iron depends to a great extent on the solidification rate and cooling rate of the casting. If a section solidifies rapidly, especially sections of 0.25 in. (6mm) or less, some amount of carbide may be present in the casting. If a section cools slowly, as in a massive, heavy casting, a largely ferritic matrix may result. Alloying elements also can alter the microstructure, usually resulting in increased amounts of pearlite. Large variations in structure can be eliminated or minimized by modifying the casting design or the runner system or both, by controlled cooling, or any combination of these. Primary carbides, and/or pearlite can be decomposed by appropriate heat treatments. A rim may occur on heat-treated castings consisting of a graphite-free layer sometimes containing more or less combined carbon than the underlying material

10 A.3.5 Typical microstructures of the grades of ductile iron are as follows: D400 (D4018) is a ferritic ductile iron most commonly made by annealing. The annealing time and temperature cycle is such that primary carbides, if present in the as-cast structure, are decomposed, and the resulting matrix is ferritic. D450 (D4512) is ferritic ductile iron supplied either as-cast or heat-treated. The matrix, is predominantly ferrite, but this grade can contain pearlite, depending on section size. D500 (D5006) is ferritic-pearlite ductile iron supplied either as-cast or heat-treated. The matrix, is essentially pearlite. This grade may contain substantially more ferrite than Grade D550. D550 (D5504) is pearlitic-ferritic ductile iron supplied either as-cast or heat-treated. The matrix, is essentially pearlite. This grade may contain less ferrite than D500. D700 (D7003) is either as-cast or air quenched to a specified hardness range. The resulting matrix is pearlite. D800 is either as-cast or air or liquid quenched and tempered to a specified hardness range. The resulting matrix is pearlite or tempered martensite. DQ&T is a liquid quenched and tempered grade. The resulting matrix is tempered martensite. A.4 Casting Mechanical Properties A.4.1 A.4.2 A.4.3 A.4.4 A.4.5 The mechanical properties are shown in Table 1. Since properties may vary with location in a given casting, the suitability of a particular grade for an intended use is best determined by laboratory or service tests. The mechanical properties will vary with microstructure that, especially in the as-cast condition, is dependent upon section size as well as chemical composition and some foundry processes. For optimum mechanical properties in the quenched and tempered grade, section size for unalloyed iron should generally not exceed 19mm (3/4 inch) to insure uniform, thorough hardened structure. A young's Modulus value of 166GPa (24Mpsi) is typically found for ductile iron when measured per ASTM E111, Standard Test Method for Young's Modulus, Tangent Modulus and Chord Modulus. Ductile Iron components used for high strain rate applications should use a reduced value of the modulus stated above (some designers have used up to 15% less than the modulus stated above). Typical un-notched Charpy impact energy properties are shown in Table A2. These typical results are from low residual element content iron (especially phosphorus). Impact values are affected by microstructure and section size

11 TABLE A2 CHARPY UN-NOTCHED IMPACT ENERGY GRADE TYPICAL IMPACT VALUE (JOULES) (FT-LBS) D400 (D4018) D450 (D4512) D500 (D5006) D550 (D5504) D700 (D7003) Properties are obtained from separately cast test bars 22C +/- 2C (72F +/- 4F). For details of Charpy Test, please refer to ASTM Impact Test (ASTM E 23). A.5 Typical Applications A.5.1 A.5.2 A.5.3 A.5.4 A.5.5 A.5.6 A.5.7 D400 (D4018) is used in moderately stressed parts requiring high ductility and good machinability. D450 (D4512) is used for moderately stressed parts where machinability is less important. D500 (D5006) is used for moderately stressed parts where machinability is less important. D550 (D5504) is used for more highly stressed parts. D700 (D7003) is used where high strength and/or improved wear resistance are required and where selective hardening is to be employed. D800 is used where high strength and/or improved wear resistance are required and where selective hardening is to be employed. DQ&T is used where the uniformity of a heat-treated material is required to control the range of mechanical properties or machinability. A.6 Additional Information 1. ASM Metals Handbook. Vol. 1. Properties & Specifications. Iron and Steel. Ninth Edition. ASM International 1996, Materials Park, OH ASM Specialty Handbook, Cast Irons. ASM International 1996, Materials Park, OH Gray and Ductile Iron Castings Handbook, Gray and Ductile Iron Foundry Society, Cleveland, OH. 4. H.T. Angus, Cast Iron: Physical Engineering, BCIRA, 1976, Birmingham, U.K. 5. Gray, Ductile and Malleable Iron Castings Current Capabilities. STP-455, American Society For Testing Materials, 1916 Race Street, Philadelphia, PA Ductile Iron Data for Design Engineers. Published by Q.I.T., a member of Ductile Iron Group, 1996, Materials Park, OH

12 Rationale Not Applicable. Relationship of SAE Standard to ISO Standard Not Applicable. Application This SAE standard covers the minimum mechanical properties measured on separately cast test pieces of varying thickness and microstructural requirements for ductile iron castings used in automotive and allied industries. Castings may be specified in the as-cast or heat-treated condition. If castings are heattreated, prior approval from the customer is required. The appendix provides general information on chemical composition, microstructure and casting mechanical properties, as well as other information for particular service conditions. In this standard SI units are primary and in-lb units are derived. Reference Section ASTM E10 Standard Test Method for Brinell Hardness of Metallic Materials ASTM E23 Standard Test Methods for Notched Bar Impact Testing of Metallic Materials ASTM E111 Standard Test Method for Young's Modulus, Tangent Modulus and Chord Modulus ASTM A247 Standard Test Method for Evaluation the Microstructure of Graphite in Iron Castings ASTM A536 Standard Specification for Ductile Iron Castings STP-455 Gray, Ductile, and Malleable Iron Castings Current Capabilities (out-of-print) Metals Handbook, Vol. 1,2 and 5, 8 th Edition, ASM International, Materials Park, OH (out-of-print) Gray and Ductile Iron Castings Handbook, Gray and Ductile Iron Founder's Society, Cleveland, OH H.D. Angus, Physical Engineering Properties of Cast Iron, British Cast Iron Research Association, Birmingham, England Developed by the SAE Automotive Iron & Steel Castings Committee

AEROSPACE MATERIAL SPECIFICATION

AEROSPACE MATERIAL SPECIFICATION AEROSPACE MATERIAL SPECIFICATION AMS 5643Q Issued OCT 1951 Revised JAN 2003 Superseding AMS 5643P Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing, and Rings 16Cr - 4.0Ni - 0.30Cb - 4.0Cu Solution

More information

AEROSPACE MATERIAL SPECIFICATION

AEROSPACE MATERIAL SPECIFICATION AEROSPACE MATERIAL SPECIFICATION Licensed to Juan Rodriguez AMS 5754M Issued MAY 1954 Revised AUG 2007 Superseding AMS 5754L Nickel Alloy, Corrosion and Heat-Resistant, Bars, Forgings, and Rings 47.5Ni

More information

AEROSPACE MATERIAL SPECIFICATION

AEROSPACE MATERIAL SPECIFICATION AEROSPACE MATERIAL SPECIFICATION AMS 6414K Issued JAN 1964 Revised FEB 2007 Superseding AMS 6414J Steel, Bars, Forgings, and Tubing 0.80Cr - 1.8Ni - 0.25Mo (0.38-0.43C) (SAE 4340) Vacuum Consumable Electrode

More information

AEROSPACE MATERIAL SPECIFICATION

AEROSPACE MATERIAL SPECIFICATION AEROSPACE MATERIAL SPECIFICATION AMS 2759/3D Issued OCT 1984 Revised FEB 2005 Superseding AMS 2759/3C Treatment Precipitation-Hardening Corrosion-Resistant and Maraging Steel Parts 1. SCOPE: This specification,

More information

Standard Specification for Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip 1

Standard Specification for Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip 1 Designation: A69 06 Standard Specification for Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip 1 This standard is issued under the fixed designation A69; the number immediately

More information

SURFACE VEHICLE STANDARD

SURFACE VEHICLE STANDARD 400 Commonwealth Drive, Warrendale, PA 15096-0001 SURFACE VEHICLE STANDARD J403 Issued 1911-06 Revised 2001-11 Superseding J403 JUN2000 REV. NOV2001 s of SAE Carbon Steels 1. Scope In 1941, the SAE Iron

More information

Molybdenum. Standard Specification for Pressure Vessel Plates, Alloy Steel, Chromium- Designation: A 387/A 387M 03

Molybdenum. Standard Specification for Pressure Vessel Plates, Alloy Steel, Chromium- Designation: A 387/A 387M 03 Designation: A 387/A 387M 03 Used in USDOE-NE Standards Standard Specification for Pressure Vessel Plates, Alloy Steel, Chromium- Molybdenum 1 This standard is issued under the fixed designation A 387/A

More information

Resource Guide. Section 4: Ni-Resist

Resource Guide. Section 4: Ni-Resist Resource Guide Section 4: Ni-Resist Section 4 Ni-Resist Description of Grades... 4-3 201 (Type 1) Ni-Resist... 4-4 202 (Type 2) Ni-Resist... 4-6 Stock Listings... 4-8 4-2 Ni-Resist Description of Grades

More information

Ferrous Alloys. Metal Alloys. Ferrous. Non ferrous. Grey iron. Carbon Low Alloy High Alloy. Nodular iron White iron Malleable iron Alloy cast irons

Ferrous Alloys. Metal Alloys. Ferrous. Non ferrous. Grey iron. Carbon Low Alloy High Alloy. Nodular iron White iron Malleable iron Alloy cast irons Metal Alloys Most engineering metallic materials are alloys. Metals are alloyed to enhance their properties, such as strength, hardness or corrosion resistance, and to create new properties, such as shape

More information

Standard Specification for Seamless and Welded Austenitic Stainless Steel Sanitary Tubing 1

Standard Specification for Seamless and Welded Austenitic Stainless Steel Sanitary Tubing 1 Designation: A 270 01 An American National Standard Standard Specification for Seamless and Welded Austenitic Stainless Steel Sanitary Tubing 1 This standard is issued under the fixed designation A 270;

More information

Standard Specification for Carbon and Alloy Steel Bars Subject to End-Quench Hardenability Requirements 1

Standard Specification for Carbon and Alloy Steel Bars Subject to End-Quench Hardenability Requirements 1 Designation: A 304 04 An American National Standard Standard Specification for Carbon and Alloy Steel Bars Subject to End-Quench Hardenability Requirements 1 This standard is issued under the fixed designation

More information

Ferrous Alloys. Steels

Ferrous Alloys. Steels Ferrous Alloys Ferrous alloys those of which iron is the prime constituent are produced in larger quantities than any other metal type. They are especially important as engineering construction materials.

More information

RELIABLE PIPES & TUBES LTD.

RELIABLE PIPES & TUBES LTD. RELIABLE PIPES & TUBES LTD. OHSAS 800:2007 CERTIFIED ISO 900:2008 CERTIFIED ISO 400:2004 CERTIFIED PED CERT NO 0 202 IND/Q--00 GOVT. RECOGNIZED EXPORT HOUSE Manufacturer & Exporters of Monel, Inconel,

More information

Mat E 272 Lecture 19: Cast Irons

Mat E 272 Lecture 19: Cast Irons Mat E 272 Lecture 19: Cast Irons November 8, 2001 Introduction: One reason steels and cast iron alloys find such wide-ranging applications and dominate industrial metal production is because of how they

More information

Standard Specification for Stainless Steel Wire 1

Standard Specification for Stainless Steel Wire 1 Designation: A 580/A 580M 06 Standard Specification for Stainless Steel Wire 1 This standard is issued under the fixed designation A 580/A 580M; the number immediately following the designation indicates

More information

Heat Treatment of Steels

Heat Treatment of Steels Heat Treatment of Steels Heat Treating is the process of heating and cooling a steel to obtain desired properties. Various types of heat treatment processes are used to change the following properties

More information

Resource Guide. Section 3: Ductile Iron

Resource Guide. Section 3: Ductile Iron Resource Guide Section 3: Ductile Iron Section 3 Ductile Iron Description of Grades... 3-3 65-45-12 Ferritic... 3-4 80-55-06 Partially Pearlitic... 3-6 100-70-02 Pearlitic... 3-8 4512 HRDS Heat Resistant...

More information

Standard Specification for Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes 1

Standard Specification for Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes 1 Designation: A 213/A 213M 99a e1 An American National Standard Used in USDOE-NE standards Standard Specification for Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger

More information

APPLICATIONS OF Fe-C PHASE DIAGRAM

APPLICATIONS OF Fe-C PHASE DIAGRAM APPLICATIONS OF Fe-C PHASE DIAGRAM KEY POINTS OF Fe-C Diagram Phases: Liquid Fe-Tmin=1148C @ 4.3%C 1394 C

More information

Standard Specification for Seamless and Welded Austenitic Stainless Steel Tubing for General Service 1

Standard Specification for Seamless and Welded Austenitic Stainless Steel Tubing for General Service 1 Designation: A 269 04 Standard Specification for Seamless and Welded Austenitic Stainless Steel Tubing for General Service 1 This standard is issued under the fixed designation A 269; the number immediately

More information

Analysis of Cast Iron Using Shimadzu PDA-7000

Analysis of Cast Iron Using Shimadzu PDA-7000 Analysis of Cast Iron Using Shimadzu PDA-7000 C112-0510M The analysis of low and high alloy cast iron by optical emission spectrometry is presented. Cast iron alloys are classified by their mechanical

More information

Resource Guide. Section 2: Gray Iron

Resource Guide. Section 2: Gray Iron Resource Guide Section 2: Gray Iron Section 2 Gray Iron Description of Grades... 2-3 G1 Partially Ferritic... 2-4 G1A Ferritic... 2-6 G2 Highly Pearlitic... 2-8 G2A Highly Perlitic High-Strength... 2-10

More information

ISO INTERNATIONAL STANDARD. Founding Ausferritic spheroidal graphite cast irons Classification

ISO INTERNATIONAL STANDARD. Founding Ausferritic spheroidal graphite cast irons Classification INTERNATIONAL STANDARD ISO 17804 First edition 2005-11-01 Founding Ausferritic spheroidal graphite cast irons Classification Fonderie Fonte ausferritique à graphite sphéroïdal Classification Reference

More information

ISO 185 INTERNATIONAL STANDARD. Grey cast irons Classification. Fontes à graphite lamellaire Classification. Second edition

ISO 185 INTERNATIONAL STANDARD. Grey cast irons Classification. Fontes à graphite lamellaire Classification. Second edition INTERNATIONAL STANDARD ISO 185 Second edition 2005-08-15 Grey cast irons Classification Fontes à graphite lamellaire Classification Reference number ISO 185:2005(E) ISO 2005 PDF disclaimer This PDF file

More information

Standard Specification for Low-Carbon Magnetic Iron 1

Standard Specification for Low-Carbon Magnetic Iron 1 Designation: A 848 01 Standard Specification for Low-Carbon Magnetic Iron 1 This standard is issued under the fixed designation A 848; the number immediately following the designation indicates the year

More information

Martensitic. stainless steels. Types 410, 420, 425 Mod, and 440A TECHNICAL DATA BLUE SHEET GENERAL PROPERTIES APPLICATIONS PRODUCT FORM

Martensitic. stainless steels. Types 410, 420, 425 Mod, and 440A TECHNICAL DATA BLUE SHEET GENERAL PROPERTIES APPLICATIONS PRODUCT FORM TECHNICAL DATA BLUE SHEET Martensitic Stainless Steels s 410, 420, 425 Mod, and 440A GENERAL PROPERTIES Allegheny Ludlum s 410, 420, 425 Modified, and 440A (see composition on Page 2) are hardenable, straight-chromium

More information

Standard Specification for Nickel-Copper Alloy (UNS N04400)* Seamless Pipe and Tube 1

Standard Specification for Nickel-Copper Alloy (UNS N04400)* Seamless Pipe and Tube 1 Designation: B 65 05 Standard Specification for Nickel-Copper Alloy (UNS N04400)* Seamless Pipe and Tube This standard is issued under the fixed designation B 65; the number immediately following the designation

More information

Custom 450 Stainless Steel, UNS S45000

Custom 450 Stainless Steel, UNS S45000 Custom 450 Stainless Steel, UNS S45000 Shaped, Flat, Square, Round, Fine Wire, Plated and Bare Wire Specifications: AMS5763, AMS 5773, AMS 5863, ASTM A 564, ASTM A693, ASTM A 959 Custom 450 Alloy Description

More information

Introduction: Ferrous alloys - Review. Outline. Introduction: Ferrous alloys

Introduction: Ferrous alloys - Review. Outline. Introduction: Ferrous alloys Introduction: Ferrous alloys - Review Outline Introduction - Review - Ferritic SS - Austinitic SS - Matensitic SS - Precipitation Hardenable SS Cast Irons - Gray CI - Ductile CI - White CI - Malleable

More information

Standard Specification for Seamless and Welded Steel Pipe for Low-Temperature Service 1

Standard Specification for Seamless and Welded Steel Pipe for Low-Temperature Service 1 Designation: A 333/A 333M 04a Standard Specification for Seamless and Welded Steel Pipe for Low-Temperature Service This standard is issued under the fixed designation A 333/A 333M; the number immediately

More information

AEROSPACE MATERIAL SPECIFICATION

AEROSPACE MATERIAL SPECIFICATION AEROSPACE MATERIAL SPECIFICATION AMS 2759/12A Issued 2007-07 Revised 2007-11 Gaseous Nitrocarburizing, Automatically Controlled by Potentials Superseding AMS 2759/12 RATIONALE AMS 2759/12A is the result

More information

RA17-4 stainless. Introduction

RA17-4 stainless. Introduction RA17-4 stainless Introduction RA17-4 is an age-hardening martensitic alloy combining high strength with the corrosion resistance of stainless steel. Hardening is achieved by a short-time, simple lowtemperature

More information

Standard Specification for Welded Stainless Steel Mechanical Tubing 1

Standard Specification for Welded Stainless Steel Mechanical Tubing 1 Designation: A 554 0 Standard Specification for Welded Stainless Steel Mechanical Tubing This standard is issued under the fixed designation A 554; the number immediately following the designation indicates

More information

Standard Specification for Seamless and Welded Ferritic and Martensitic Stainless Steel Tubing for General Service 1

Standard Specification for Seamless and Welded Ferritic and Martensitic Stainless Steel Tubing for General Service 1 Designation: A 268/A 268M 0 An American National Standard Standard Specification for Seamless and Welded Ferritic and Martensitic Stainless Steel Tubing for General Service This standard is issued under

More information

J = D C A C B x A x B + D C A C. = x A kg /m 2

J = D C A C B x A x B + D C A C. = x A kg /m 2 1. (a) Compare interstitial and vacancy atomic mechanisms for diffusion. (b) Cite two reasons why interstitial diffusion is normally more rapid than vacancy diffusion. (a) With vacancy diffusion, atomic

More information

Marc King. Hiler Industries LaPorte, IN

Marc King. Hiler Industries LaPorte, IN Carbidic Ductile Iron Marc King Metallurgist Hiler Industries LaPorte, IN Why would anybody in their right mind want to add carbides to ductile iron? Ductile Iron is a great engineering material: Great

More information

Standard Specification for Welded Stainless Steel Mechanical Tubing 1

Standard Specification for Welded Stainless Steel Mechanical Tubing 1 Designation: A 554 98 e An American National Standard Standard Specification for Welded Stainless Steel Mechanical Tubing This standard is issued under the fixed designation A 554; the number immediately

More information

DATA SHEET ZERON 100 UNS S32760 THE GLOBAL LEADER IN SPECIALTY ALLOYS ALLOYS AND PROCESSING

DATA SHEET ZERON 100 UNS S32760 THE GLOBAL LEADER IN SPECIALTY ALLOYS ALLOYS AND PROCESSING DATA SHEET ZERON 100 UNS S32760 THE GLOBAL LEADER IN SPECIALTY ALLOYS ALLOYS AND PROCESSING ZERON 100 Data Sheet Contents Specifications, Chemical Composition, Applications and Features...2 Performance

More information

Identification. Type Analysis

Identification. Type Analysis Page 1 of 16 Unit Display: Metric Print Now Custom 465 Stainless E-Mail Datasheet Add to My Materials Request More Information U.S. Patent Number Identification 5,681,528 5,855,844 UNS Number S46500 Type

More information

SPECIFICATION FOR PRESSURE VESSEL PLATES, CARBON STEEL, FOR MODERATE- AND LOWER-TEMPERATURE SERVICE

SPECIFICATION FOR PRESSURE VESSEL PLATES, CARBON STEEL, FOR MODERATE- AND LOWER-TEMPERATURE SERVICE Technical Literature: ASME SA-516 [ASTM A516] Company Website: www.metalspiping.com SA-516/SA-516M Carbon & Low Alloy Steels From Hebei Metals Industrial Limited SPECIFICATION FOR PRESSURE VESSEL PLATES,

More information

Licensed Copy: John May, Powertrain Ltd., February 20, 2002, Uncontrolled Copy, (c) BSI

Licensed Copy: John May, Powertrain Ltd., February 20, 2002, Uncontrolled Copy, (c) BSI BRITISH STANDARD BS 70-3: Incorporating Amendment Nos. 1 and 2 Specification for Wrought steel for mechanical and allied engineering purposes Part 3: Bright bars for general engineering purposes BS70-3:

More information

ATI 825 ATI 825. Technical Data Sheet. Nickel-base Alloy INTRODUCTION PRODUCT FORMS SPECIFICATIONS & CERTIFICATES (UNS N08825)

ATI 825 ATI 825. Technical Data Sheet. Nickel-base Alloy INTRODUCTION PRODUCT FORMS SPECIFICATIONS & CERTIFICATES (UNS N08825) ATI 825 Nickel-base (UNS N08825) INTRODUCTION ATI 825 alloy (UNS N08825) is an austenitic nickel-iron-chromium-molybdenum-copper alloy containing high levels of chromium, nickel, molybdenum and copper

More information

ISO INTERNATIONAL STANDARD. Implants for surgery Metallic materials Part 1: Wrought stainless steel

ISO INTERNATIONAL STANDARD. Implants for surgery Metallic materials Part 1: Wrought stainless steel INTERNATIONAL STANDARD ISO 5832-1 Fourth edition 2007-06-15 Implants for surgery Metallic materials Part 1: Wrought stainless steel Implants chirurgicaux Matériaux métalliques Partie 1: Acier inoxydable

More information

Steel Properties. History of Steel

Steel Properties. History of Steel History of Steel Steel Properties Cast Iron Cast iron preceded wrought iron. It is brittle, has high carbon content with low tensile strength. It has excellent casting properties. It was mainly used to

More information

The ATI 17-4 precipitation hardening stainless steel (S17400) is covered by the following wrought product specifications.

The ATI 17-4 precipitation hardening stainless steel (S17400) is covered by the following wrought product specifications. ATI 17-4 Precipitation Hardening Stainless Steel (UNS S17400) INTRODUCTION ATI 17-4 precipitation hardening stainless steel (S17400), Type 630, is a chromium-nickel-copper precipitation hardening stainless

More information

Free Machining Martensitic stainless steel. Oxidation resistance in continuous service to 1200 F (650 C).

Free Machining Martensitic stainless steel. Oxidation resistance in continuous service to 1200 F (650 C). Description 416 is a free machining martensitic grade. The unique production process developed exclusively by Ugitech results in a product that delivers superior productivity and tool life, and improves

More information

XI'AN LINKUN STEEL PIPE CO., LTD

XI'AN LINKUN STEEL PIPE CO., LTD Designation: A 511 04 Standard Specification for Seamless Stainless Steel Mechanical Tubing 1 This standard is issued under the fixed designation A 511; the number immediately following the designation

More information

ISO/TR TECHNICAL REPORT. Designation system for cast irons and pig irons. Système de désignation pour la fonte et la fonte brute

ISO/TR TECHNICAL REPORT. Designation system for cast irons and pig irons. Système de désignation pour la fonte et la fonte brute TECHNICAL REPORT ISO/TR 15931 First edition 2004-08-15 Designation system for cast irons and pig irons Système de désignation pour la fonte et la fonte brute Reference number ISO/TR 15931:2004(E) ISO 2004

More information

Steel Haseeb Ullah Khan Jatoi Department of Chemical Engineering UET Lahore

Steel Haseeb Ullah Khan Jatoi Department of Chemical Engineering UET Lahore Steel Haseeb Ullah Khan Jatoi Department of Chemical Engineering UET Lahore Recap Eutectic phase diagram Eutectic phase diagram Eutectic isotherm Invariant point Eutectic Reaction Compositions of components

More information

AEROSPACE MATERIAL SPECIFICATION

AEROSPACE MATERIAL SPECIFICATION AEROSPACE MATERIAL SPECIFICATION AMS 2759/7A Issued OCT 1991 Revised OCT 2001 Reaffirmed FEB 2006 Superseding AMS 2759/7 Carburizing and Heat Treatment of Carburizing Grade Steel Parts 1. SCOPE: This specification,

More information

Standard Specification for Stainless Steels for Surgical Instruments 1

Standard Specification for Stainless Steels for Surgical Instruments 1 Designation: F 899 02 Standard Specification for Stainless Steels for Surgical Instruments 1 This standard is issued under the fixed designation F 899; the number immediately following the designation

More information

Standard Specification for Cold-Formed Welded and Seamless Carbon Steel Structural Tubing in Rounds and Shapes 1

Standard Specification for Cold-Formed Welded and Seamless Carbon Steel Structural Tubing in Rounds and Shapes 1 Designation: A 500 03a Standard Specification for Cold-Formed Welded and Seamless Carbon Steel Structural Tubing in Rounds and Shapes This standard is issued under the fixed designation A 500; the number

More information

Steel Making. Modern Long Product Manufacturing. Process Flow Chart

Steel Making. Modern Long Product Manufacturing. Process Flow Chart Rolling Process Metallurgical Aspects Material Specifications and Chemistries Standard Mill Practices Miscellaneous Tables & Data Elastic Section Modulus Plastic Section Modulus Moment of Inertia SI Conversion

More information

Heat Treating Basics-Steels

Heat Treating Basics-Steels Heat Treating Basics-Steels Semih Genculu, P.E. Steel is the most important engineering material as it combines strength, ease of fabrication, and a wide range of properties along with relatively low cost.

More information

11.3 The alloying elements in tool steels (e.g., Cr, V, W, and Mo) combine with the carbon to form very hard and wear-resistant carbide compounds.

11.3 The alloying elements in tool steels (e.g., Cr, V, W, and Mo) combine with the carbon to form very hard and wear-resistant carbide compounds. 11-2 11.2 (a) Ferrous alloys are used extensively because: (1) Iron ores exist in abundant quantities. (2) Economical extraction, refining, and fabrication techniques are available. (3) The alloys may

More information

Specification ALLOYED STEEL FOR QUENCHING AND TEMPERING, HIGH STRENGTH All.steel f.quen.a.temp, h.str.

Specification ALLOYED STEEL FOR QUENCHING AND TEMPERING, HIGH STRENGTH All.steel f.quen.a.temp, h.str. Class: Heat-treatable steel Specification 16-09 ALLOYED STEEL FOR QUENCHING AND TEMPERING, HIGH STRENGTH Class No.:11 JED 723 Previous Edition Abbreviated Title 15-07 All.steel f.quen.a.temp, h.str. 8

More information

Carbidic Austempered Ductile Iron (CADI)

Carbidic Austempered Ductile Iron (CADI) 28 November 2000 (Rev. 13 Feb 01) Carbidic Austempered Ductile Iron (CADI) John R. Keough, PE Kathy L. Hayrynen, PhD Applied Process Inc. Technologies Div.- Livonia, Michigan, USA ABSTRACT Carbidic Austempered

More information

Standard Specification for Investment Castings, Steel and Alloy, Common Requirements, for General Industrial Use 1

Standard Specification for Investment Castings, Steel and Alloy, Common Requirements, for General Industrial Use 1 Designation: A 957 05 Standard Specification for Investment Castings, Steel and Alloy, Common Requirements, for General Industrial Use 1 This standard is issued under the fixed designation A 957; the number

More information

CTS-XHP Alloy. Patent Number 5,370,750

CTS-XHP Alloy. Patent Number 5,370,750 CTSXHP Alloy Patent Number 5,370,750 Type Analysis Carbon 1.60% Chromium 16.00% Silicon 0.40% Molybdenum 0.80% Nickel 0.35% Vanadium 0.45% Manganese 0.50% Iron Balance Description CTSXHP alloy is an airhardening,

More information

Stainless Steel & Stainless Steel Fasteners Chemical, Physical and Mechanical Properties

Stainless Steel & Stainless Steel Fasteners Chemical, Physical and Mechanical Properties Stainless Steel & Stainless Steel Fasteners Chemical, Physical and Mechanical Properties Stainless steel describes a family of steels highly resistant to tarnishing and rusting that contain at least two

More information

Standard Specification for Stainless Chromium-Nickel Steel-Clad Plate 1

Standard Specification for Stainless Chromium-Nickel Steel-Clad Plate 1 Enclosed is a computer file in PDF format containing one or more ASTM Standards. The documents contained in this e-mail are complimentary, prepublication copies of the final edited documents. These documents

More information

SPECIFICATION FOR TITANIUM AND TITANIUM ALLOY FORGINGS

SPECIFICATION FOR TITANIUM AND TITANIUM ALLOY FORGINGS TECHNICAL LITERATURE: ASME SB-381 [ASTM B381] Company Website: www.metalspiping.com Your Reliable Supplier of Titanium & Nickel Alloys SB-381 SPECIFICATION FOR TITANIUM AND TITANIUM ALLOY FORGINGS ð13þ

More information

Subway Cars. Applications Potential

Subway Cars. Applications Potential 301 STAINLESS STEEL P R O D U C T D ATA B U L L E T I N Aircraft Structural Parts Roof Drainage Cooking Utensils Automotive Trim Subway Cars Applications Potential Type 301 is an austenitic chromium-nickel

More information

AUTOMOTIVE AND LARGE BORE ENGINE APPLICATIONS. Piston Rings and Piston Ring Elements Cast Iron Materials

AUTOMOTIVE AND LARGE BORE ENGINE APPLICATIONS. Piston Rings and Piston Ring Elements Cast Iron Materials UTOMOTIVE ND LRGE BORE ENGINE PPLICTIONS Issue date: 03.01 and Piston Ring Elements Cast Iron Materials Designation Reference Grade Hardness KS MED E DIN GOE 12 K 1 47 210 6621-3 unalloyed, non heat-treated

More information

With Dura-Bar you will be able to:

With Dura-Bar you will be able to: Dura-Bar Stock List Dura-Bar is an engineered iron designed to meet our customers most critical requirements. It is manufactured to strict process controls that provide world-class quality and uncompromising

More information

Cast Irons, Ductile Irons & Malleable Irons

Cast Irons, Ductile Irons & Malleable Irons Cast Irons, Ductile Irons & Malleable Irons CAST IRONS mium Sulfur Silicon Nickel Chro- Copper Alloying Elements TransverseTest Load Transverse Test Deflection at Center ksi Mpa Lbs. kn in. mm. HI-STRENGTH

More information

Effect of Heat Treatment on Microstructure and Mechanical Properties of Medium Carbon Steel

Effect of Heat Treatment on Microstructure and Mechanical Properties of Medium Carbon Steel International Journal of Engineering Research and Development ISSN: 2278-067X, Volume 2, Issue 1 (July 2012), PP. 07-13 www.ijerd.com Effect of Heat Treatment on Microstructure and Mechanical Properties

More information

HAYNES 25 alloy. Principle Features

HAYNES 25 alloy. Principle Features HAYNES 25 alloy Principle Features Excellent High-Temperature Strength and Good Oxidation Resistance HAYNES 25 alloy (UNS R30605) is a cobalt-nickel- chromium-tungsten alloy that combines excellent high-temperature

More information

AEROSPACE MATERIAL SPECIFICATION

AEROSPACE MATERIAL SPECIFICATION `,,,`,,``,,,`,`,`,,,`,,,,,,,,,``,,`,,`,`,,` AEROSPACE MATERIAL SPECIFICATION Heat Treatment of LowAlloy Steel Parts Minimum 220 ksi (1517 MPa) and Higher AMS 2759/2D Issued OCT 1984 Revised AUG 2007 Superseding

More information

Applications Potential

Applications Potential P R O D U C T D A T A B U L L E T I N STAINLESS 301STEEL UNS S30100 High Strength and Good Ductility When Cold Worked Excellent Corrosion Resistance Readily Welded Readily Formed and Drawn Economical Oxidation

More information

ISO INTERNATIONAL STANDARD. Implants for surgery Metallic materials Part 12: Wrought cobalt-chromium-molybdenum alloy

ISO INTERNATIONAL STANDARD. Implants for surgery Metallic materials Part 12: Wrought cobalt-chromium-molybdenum alloy INTERNATIONAL STANDARD ISO 5832-12 Second edition 2007-05-01 Implants for surgery Metallic materials Part 12: Wrought cobalt-chromium-molybdenum alloy Implants chirurgicaux Matériaux métalliques Partie

More information

ISO INTERNATIONAL STANDARD. Founding Ausferritic spheroidal graphite cast irons Classification

ISO INTERNATIONAL STANDARD. Founding Ausferritic spheroidal graphite cast irons Classification INTERNATIONAL STANDARD ISO 17804 First edition 2005-11-01 Founding Ausferritic spheroidal graphite cast irons Classification Fonderie Fonte ausferritique à graphite sphéroïdal Classification Reference

More information

The heat treatment necessary to produce ADI is essentially a two-stage operation:

The heat treatment necessary to produce ADI is essentially a two-stage operation: The remarkable properties of ADI are developed by a closely controlled heat treatment operation (austempering) which develops a unique matrix structure of bainitic ferrite (6%) and retained (high carbon)

More information

MSE-226 Engineering Materials

MSE-226 Engineering Materials MSE-226 Engineering Materials Lecture-7 ALLOY STEELS Tool Steels TYPES of FERROUS ALLOYS FERROUS ALLOYS Plain Carbon Steels Alloy Steels Cast Irons - Low carbon Steel - Medium carbon steel - High carbon

More information

AWS A5.28/A5.28M:2005 An American National Standard. Specification for Low-Alloy Steel Electrodes and Rods for Gas Shielded Arc Welding

AWS A5.28/A5.28M:2005 An American National Standard. Specification for Low-Alloy Steel Electrodes and Rods for Gas Shielded Arc Welding An American National Standard Specification for Low-Alloy Steel Electrodes and Rods for Gas Shielded Arc Welding Key Words Filler metal specifications, low-alloy steel welding electrodes, gas metal arc

More information

Seam Welded Air-Hardenable Corrosion Resistant Steel Tubing: Automotive Applications Overview

Seam Welded Air-Hardenable Corrosion Resistant Steel Tubing: Automotive Applications Overview KVA, Inc. / 124 S. Market Place, Suite 200 / Escondido, CA. 92029 U.S.A. (760) 489-5821 phone (760) 489-5823 fax 1-888-410-WELD www.kvastainless.com Seam Welded Air-Hardenable Corrosion Resistant Steel

More information

Standard Specification for Piping Fittings of Wrought Carbon Steel and Alloy Steel for Moderate and High Temperature Service 1

Standard Specification for Piping Fittings of Wrought Carbon Steel and Alloy Steel for Moderate and High Temperature Service 1 Designation: A 234/A 234M 02 Used in USDOE-NE Standards An American National Standard Standard Specification for Piping Fittings of Wrought Carbon Steel and Alloy Steel for Moderate and High Temperature

More information

STANDARD STEELS STANDARD STEELS 403

STANDARD STEELS STANDARD STEELS 403 STANDARD STEELS 403 STANDARD STEELS Standard Steels Compositions, Applications, and Heat Treatments Steel is the generic term for a large family of iron carbon alloys, which are malleable, within some

More information

ATI ATI 2205 Alloy (UNS S31803 and S32205) Duplex Stainless Steel. Technical Data Sheet

ATI ATI 2205 Alloy (UNS S31803 and S32205) Duplex Stainless Steel. Technical Data Sheet Alloy (UNS S31803 and S32205) Duplex Stainless Steel GENERAL PROPERTIES alloy (UNS S31803 and/or S32205) is a nitrogenenhanced duplex stainless steel alloy. The nitrogen serves to significantly improve

More information

SURFACE VEHICLE INFORMATION REPORT

SURFACE VEHICLE INFORMATION REPORT 400 Commonwealth Drive, Warrendale, PA 15096-0001 SURFACE VEHICLE INFORMATION REPORT Submitted for recognition as an American National Standard J474 Issued 1930-01 Reaffirmed 1985-02 Superseding J474 JUN72

More information

Implants for surgery Metallic materials

Implants for surgery Metallic materials BRITISH STANDARD Implants for surgery Metallic materials BS ISO 5832-12:2007 Incorporating corrigendum September 2008 Part 12: Wrought cobalt-chromiummolybdenum alloy ICS 11.040.40 NO COPYING WITHOUT BSI

More information

ATI 718 ATI 718. Technical Data Sheet. Nickel-Base Superalloy INTRODUCTION FORMS AND CONDITIONS AVAILABLE SPECIFICATIONS. (UNS Designation N07718)

ATI 718 ATI 718. Technical Data Sheet. Nickel-Base Superalloy INTRODUCTION FORMS AND CONDITIONS AVAILABLE SPECIFICATIONS. (UNS Designation N07718) ATI 718 Nickel-Base Superalloy (UNS Designation N07718) INTRODUCTION ATI 718 alloy (N07718) is an austenitic nickel-base superalloy which is used in applications requiring high strength to approximately

More information

Section 6: Appendices

Section 6: Appendices Section 6: Appendices Section 6 Appendices Tolerances...6-2 ASTM References...6-8 Glossary... 6-13 Useful Formulas/Calculations... 6-21 Typical Hardness Value Conversion Table... 6-24 Mechanical Properties...

More information

Standard Specification for Forged or Rolled Alloy-Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service 1

Standard Specification for Forged or Rolled Alloy-Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service 1 Designation: A 182/A 182M 04 Endorsed by Manufacturers Standardization Society of the Valve and Fittings Industry Used in USDOE-NE Standards Standard Specification for Forged or Rolled Alloy-Steel Pipe

More information

Founding Spheroidal graphite cast irons

Founding Spheroidal graphite cast irons BRITISH STANDARD BS EN 1563:1997 Incorporating Amendment No. 1 Founding Spheroidal graphite cast irons The European Standard EN 1563:1997, with the incorporation of amendment A1:2002 has the status of

More information

Heat Treatment of Steel Lab Report. Justin Lance 11/16/2011 Engineering 45 Lab Section 3 Troy Topping

Heat Treatment of Steel Lab Report. Justin Lance 11/16/2011 Engineering 45 Lab Section 3 Troy Topping Heat Treatment of Steel Lab Report Justin Lance justalance@gmail.com 11/16/2011 Engineering 45 Lab Section 3 Troy Topping troytopping@gmail.com ABSTRACT We observed how the properties of 4140 steel vary

More information

ISO 185 INTERNATIONAL STANDARD. Grey cast irons Classification. Fontes à graphite lamellaire Classification. Second edition

ISO 185 INTERNATIONAL STANDARD. Grey cast irons Classification. Fontes à graphite lamellaire Classification. Second edition INTERNATIONAL STANDARD ISO 185 Second edition 2005-08-15 Grey cast irons Classification Fontes à graphite lamellaire Classification Reference number ISO 185:2005(E) ISO 2005 PDF disclaimer This PDF file

More information

It is our intent to always maintain the highest level of quality metals obtainable from our mill sources.

It is our intent to always maintain the highest level of quality metals obtainable from our mill sources. This stock catalog contains the sizes, weights and descriptions of all standard Steel, Brass, Bronze and Dura-Bar Cast Iron items that are available from stock for immediate delivery. However, new items

More information

Standard Specification for Nickel-Copper Alloy (UNS N04400) Plate, Sheet, and Strip 1

Standard Specification for Nickel-Copper Alloy (UNS N04400) Plate, Sheet, and Strip 1 Designation: B 27 0 Used in USDOE-NE standards Standard Specification for Nickel-Copper Alloy (UNS N04400) Plate, Sheet, and Strip This standard is issued under the fixed designation B 27; the number immediately

More information

Standard Specification for Steel Sheet, Zinc-5 % Aluminum Alloy-Coated by the Hot-Dip Process 1

Standard Specification for Steel Sheet, Zinc-5 % Aluminum Alloy-Coated by the Hot-Dip Process 1 : A 875/A 875M 05 Standard Specification for Steel Sheet, Zinc-5 % Aluminum Alloy-Coated by the Hot-Dip Process 1 This standard is issued under the fixed designation A 875/A 875M; the number immediately

More information

Standards & Specifications

Standards & Specifications Acme Alloys Products Standards & Specifications Page 1 of 12 Standards & Specifications Like any other technology, engineering and science; material science and metallurgy is an ever-widening field with

More information

Standard Specification for Nickel Alloy Forgings 1

Standard Specification for Nickel Alloy Forgings 1 Designation: Standard Specification for Nickel Forgings 1 This standard is issued under the fixed designation B 564; the number immediately following the designation indicates the year of original adoption

More information

The Production Technology of a Modern Material for Heavy Automotive Vehicles - A Compacted Graphite Iron (C.G.I.)

The Production Technology of a Modern Material for Heavy Automotive Vehicles - A Compacted Graphite Iron (C.G.I.) The Production Technology of a Modern Material for Heavy Automotive Vehicles - A Compacted Graphite Iron (C.G.I.) Prof. S. K. PAKNIKAR Metallurgical & Foundry Consultant, Pune- INDIA. skpaknikar@gmail.com

More information

41003 STAINLESS STEEL

41003 STAINLESS STEEL 41003 STAINLESS STEEL D ATA S H E E T Formable and Weldable in Heavy Sections Refined Grain Structure Leads to Good Toughness Ferritic as Annealed Low Cost AK Steel 41003 is an economical ferritic stainless

More information

ATI Datalloy HP TM Alloy

ATI Datalloy HP TM Alloy ATI Datalloy HP TM Alloy UNS N08830 INTRODUCTION ATI Datalloy HP TM alloy is a Ni-Cr-Mo-Fe non-magnetic high strength alloy with exceptional pitting and crevice corrosion resistance, while maintaining

More information

HASTELLOY B-3 alloy Principal Features

HASTELLOY B-3 alloy Principal Features HASTELLOY B-3 alloy Principal Features Exceptional resistance to HCl and H 2 SO 4 and enhanced structural stability HASTELLOY B-3 alloy (UNS N10675) exhibits extremely high resistance to pure hydrochloric,

More information

Edward W. Russell and Brian L. Anderson Lawrence Livermore National Laboratory Prepared by LLNL under Contract DE-AC52-07NA27344

Edward W. Russell and Brian L. Anderson Lawrence Livermore National Laboratory Prepared by LLNL under Contract DE-AC52-07NA27344 Comparison of German and American Fabrication Standards for Transportation and Storage Containments of High Level Radioactive Material Type B Packages 15055 ABSTRACT Edward W. Russell and Brian L. Anderson

More information

Standard Specification for Piping Fittings of Wrought Carbon Steel and Alloy Steel for Low-Temperature Service 1

Standard Specification for Piping Fittings of Wrought Carbon Steel and Alloy Steel for Low-Temperature Service 1 Designation: A 420/A 420M 07 Standard Specification for Piping Fittings of Wrought Carbon Steel and Alloy Steel for Low-Temperature Service This standard is issued under the fixed designation A 420/A 420M;

More information

Engineering Materials

Engineering Materials Engineering Materials Learning Outcome When you complete this module you will be able to: Describe the mechanical properties of ferrous and non-ferrous engineering materials, plus the effects and purposes

More information

Standard Specification for Carbon and Alloy Steel Nuts for Bolts for High Pressure or High Temperature Service, or Both 1

Standard Specification for Carbon and Alloy Steel Nuts for Bolts for High Pressure or High Temperature Service, or Both 1 Designation: A 94/A 94M 0a An American National Standard Endorsed by Manufacturers Standardization Society of the Valve and Fittings Industry Used in USNRC-RDT Standards Standard Specification for Carbon

More information