1040R UNIVERSAL 2K PRIMER GREY

Transcription

1 Description 2component high solids primer with 3 methods of application: a. maxi filler; b. high solids surfacer; c. high solids nonsanding primer. Colour: light grey. Composition based on functional acrylic copolymer. Products 1010R AK S 1025R 1030R Universal 2K Primer Grey Activator Fast 2K Activator Activator Fast High Solids Primer Thinner High Solids Nonsanding Convertor Properties Easy to apply, smooth flow. Very easy to sand, many days after application. Superb filling. Can be tinted with up to 10 % maximum with AM Centari MasterTints. Can be coated with all DuPont topcoats. Substrates OEM finishes or cured repaired finishes sanded polyester putty DuPont primers: 820R, 830R, 1141S1144S1147S REF 8 ANZ p. 16 The DuPont Oval, Centari and MasterTint are registered trademarks of DuPont or its affiliates.

2 PRODUCT PREPARATION Mixing ratio 1010R or AK R 1030R Volume 4 1 Maxi Primer surfacer Nonsanding Weight Volume Weight Volume VOC 530 gli 628 gli 626 gli Pot life With 1010R 45 min. 1 h 2 h With AK210 1 h 2 h 3 h viscosity equipment pressure Number of coats Flash time DIN 4 FORD 4 AFNOR 4 Fluid tip (mm) distance (cm) bar 33.5 bar 46 bar 1618 s 1618 s 1820 s Fluid tip (mm) distance (cm) bar 34 bar 46 bar 1516 s 1516 s 1617 s Fluid tip (mm) Weight distance (cm) bar 34 bar 46 bar minimum Between coats till flat. before bake. Between coats till flat. 10 min. before bake. 15 min. (till 8 h maximum) before topcoating. DFT 6080 µcoat 4060 µcoat 3040 µ Dry to sand at 15 C at 40 C at 60 C 1216 h 812 h 40 min. 46 h 3 h 25 min. Not applicable IR drying* Distance Half power Full power 80 cm 5 min min. * guideline for shortmedium wave IR equipment This data relates only to the material designated herein and does not apply to use in combination with any other material or any process. The data is not to be considered as a warranty or quality specification and we assume no liability in connection with its use. REF 8 ANZ p. 26

3 PRODUCT PREPARATION (con d) Mixing ratio 256S 1025R 1030R Volume 5 1 Maxi Weight Volume VOC 256S 493 gli 587 gli Pot life 45 min. 1 h viscosity equipment pressure Number of coats Flash time DIN 4 FORD 4 AFNOR 4 Primer surfacer Weight s 1618 s 1820 s Fluid tip distance Fluid tip distance 1.82 mm mm 1.2 mm 33.5 bar 33.5 bar 46 bar 2025 cm 15 cm 1520 cm Between coats till flat. before bake mm mm mm mm 34 bar 34 bar 46 bar Between coats till flat. 10 min. before bake. DFT 6080 µcoat 4060 µcoat Dry to sand at 15 C at 40 C at 60 C 1216 h 812 h 40 min. 46 h 3 h 25 min. IR drying* Distance Half power Full power 80 cm 5 min min cm 2025 cm 15 cm 2025 cm * guideline for shortmedium wave IR equipment This data relates only to the material designated herein and does not apply to use in combination with any other material or any process. The data is not to be considered as a warranty or quality specification and we assume no liability in connection with its use. REF 8 ANZ p. 36

4 RECOMMENDED USE Surface preparation OEM and cured repaired finishes 1. Clean surface with water and soap. Rinse and dry. 2. Degrease with 3919S. Wipe dry. 3. Sand: a) maxi: mechanical with P80 P120, wet with P150 P240; b) primer surfacer: mechanical with P220 P280, wet with P360 P500; c) nonsanding: mechanical with P220 P320, wet with P360 P600.! Treat bare metal spots in sand through areas as described below: Apply 5717S, rinse with plenty of water and dry. 5717S is not recommended if polyester putty is required (see specific TDS). Clean surface with 3920S. Apply 1 coat 820R or 830R (see specific TDS). Bare metals (steel, galvanised steel, aluminium or surface treated aluminium) 1. Clean surface with 3608S. 2. Sand and eliminate all rust or corrosion. 3. Clean with 3920S. 4. Wipe dry before priming. 5. Apply 1 coat 820R or 830R (see specific TDS) and proceed with application. Application selection Maxi filler: To isolate polyester putty spots, to fill up small sand scratches or sand throughs. Primer surfacer: Normal car priming; spot, panel and overall repair. Nonsanding: To reduce sanding work and increase output of spray booth. REF 8 ANZ p. 46

5 RECOMMENDED USE (con d) Equipment cleaning Use 3608S. Remarks Do not use activated beyond the pot life nor reduce it further to get viscosity down again. If is applied over thermoplastic acrylic finishes, complete panel or overall car has to be primed. Spot priming or sand throughs of the primer can result in spot marking or lifting when applying basecoat. Do NOT exceed recommended film thickness to avoid film defects, poor film through cure and poor adhesion. Respect mixing ratios, drying times, spray pressure and DFT to avoid poor sandability and paper filling. Activated material should not be returned to original can of nonactivated material. Close can of 1010R, AK210 and 256S tightly immediately after use, as these products will react with humid air and water and lose their hardening effect. Material has to be at room temperature (1820 C) before use. Product data Package viscosity: cp Theoretical coverage: Maxi m²li at recommended DFT readytospray PS m²li at recommended DFT readytospray NS m²li at recommended DFT readytospray Products Packages (li) Storability (year) R AK S R R Safety Consult Material Safety Data Sheet prior to use. Observe the precautionary notices displayed on the container. REF 8 ANZ p. 56

6 REPAIR SYSTEMS Preparation method for spot repair P280 P320 P360 PE 1. Sand through, end with P Fill the spot with polyester putty and sand with P Sand the surrounding area with P320 and finish on the OEM finish with P Apply 1 coat of 820R or 830R over the polyester putty to isolate the substrate and flash till flat. 5. Apply 1 st coat of primer surfacer over the entire prepared area. Flash till completely flat. Apply 2 nd coat of primer surfacer, staying inside the 1 st coat area. Flash till flat. REF 8 ANZ p. 66