atoms = 1.66 x g/amu

Size: px
Start display at page:

Download "atoms = 1.66 x g/amu"

Transcription

1 CHAPTER 2 Q1- How many grams are there in a one amu of a material? A1- In order to determine the number of grams in one amu of material, appropriate manipulation of the amu/atom, g/mol, and atom/mol relationships is all that is necessary, as # g/amu = 1 mol 1 g / mol x atoms 1 amu / atom = 1.66 x g/amu Q2- Show the electron configuration for Fe 3+, Cu +, and S 2- A2- Fe s 2 2s 2 2p 6 3s 2 3p 6 3d 5 Cu + - 1s 2 2s 2 2p 6 3s 2 3p 6 3d 10 S s 2 2s 2 2p 6 3s 2 3p 6 Q3. Why water expands on freezing? A3. The geometry of the H 2 O molecules, which are hydrogen bonded to one another, is more restricted in the solid phase than for the liquid. This results in a more open molecular structure in the solid, and a less dense solid phase. CHAPTER 3 Q1- What is the difference between a crystal structure and a crystal system? A1- A crystal structure is described by both the geometry of, and atomic arrangements within, the unit cell, whereas a crystal system is described only in terms of the unit cell geometry. For example, face-centered cubic and body-centered cubic are crystal structures that belong to the cubic crystal system. Q2- Show that the ideal c/a ratio for HCP is A2- A sketch of one-third of an HCP unit cell is shown below. Consider the tetrahedron labeled as JKLM, which is reconstructed as

2 The atom at point M is midway between the top and bottom faces of the unit cell--that is MH = c/2. And, since atoms at points J, K, and M, all touch one another, JM =JK=2R=a where R is the atomic radius. Furthermore, from triangle JHM, (JM) 2 =(JH) 2 + (MH) 2,or a 2 = (JH) 2 + c 2 2 Now, we can determine the JH length by consideration of triangle JKL, which is an equilateral triangle, cos 30 = a/2 JH = 3 2, and a JH = 3 Substituting this value for JH in the above expression yields a 2 2 a = + c 2 = a c2 4 and, solving for c/a c a = 8 3 = Q3- Calculate the unit cell volume for Co which has an HCP crystal structure. A3- In order to do this, it is necessary to use a result of Problem 3.7, that is V C = 6R 2 c 3 The problem states that c = 1.623a, and a = 2R. Therefore V C = (1.623)(12 3 )R 3 = (1.623)(12 3) ( x 10-8 cm) 3 = 6.64 x cm 3 = 6.64 x 10-2 nm 3 Q4- List the point coordinates for all of the atoms that are associated with the FCC unit cell. A4- From Figure 3.1b, the atom located of the origin of the unit cell has the coordinates 000. Coordinates for other atoms in the bottom face are 100, 110, 010, and (The z coordinate 2 2 for all these points is zero.)

3 For the top unit cell face, the coordinates are 001, 101, 111, 011, and (These 2 2 coordinates are the same as bottom-face coordinates except that the 0 z coordinate has been replaced by a 1.) Coordinates for only those atoms that are positioned at the centers of both side faces, and centers of both front and back faces need to be specified. For the front and back-center face atoms, the coordinates are and 0 1 1, respectively. While for the left and right side 2 2 center-face atoms, the respective coordinates are and Q&A5- Some crystallographic directions in the cubic cell. Q&A6- Some crystallographic planes in the cubic unit cells are shown below:

4 Q7- Calculate d 111 for α-iron. A7- α-iron has a BCC crystal structure and an atomic radius of nm. Using Equation (3.3) the lattice parameter, a, may be computed as a= 4R (4)( nm) = = nm 3 3 Now, the d 111 interplanar spacing may be determined using Equation (3.3W) as d 111 = a nm (1) 2 + (1) 2 = = nm 2 + (1) 3 CHAPTER 4 Q1- Cite which of the elements listed form with Cu the three possible solid solution types. A1- For complete substitutional solubility the following criteria must be met: 1) the difference in atomic radii between Cu and the other element (ΔR%) must be less than ±15%, 2) the crystal structures must be the same, 3) the electronegativities must be similar, and 4) the valences should be the same, or nearly the same. Below are tabulated, for the various elements, these criteria. Crystal ΔElectro- Element ΔR% Structure negativity Valence Cu FCC 2+ C -44 H -64 O -53 Ag +13 FCC 0 1+ Al +12 FCC Co -2 HCP Cr -2 BCC Fe -3 BCC Ni -3 FCC Pd +8 FCC Pt +9 FCC Zn +4 HCP (a) Ni, Pd, and Pt meet all of the criteria and thus form substitutional solid solutions having complete solubility. (b) Ag, Al, Co, Cr, Fe, and Zn form substitutional solid solutions of incomplete solubility. All these metals have either BCC or HCP crystal structures, and/or the difference between their atomic radii and that for Cu are greater than ±15%, and/or have a valence different than 2+. (c) C, H, and O form interstitial solid solutions. These elements have atomic radii that are significantly smaller than the atomic radius of Cu. Q2- Determine the weight percent of Ge that must be added to Si such that the resultant alloy will contain 2.43 x10 21 Ge atoms per cubic centimeter. A2- To solve this problem, employment of Equation (4.18) is necessary, using the following values: N 1 = N Ge = 2.43 x atoms/cm 3 Thus ρ 1 = ρ Ge = 5.32 g/cm 3 ρ 2 = ρ Si = 2.33 g/cm 3 A 1 = A Ge = g/mol A 2 = A Si = g/mol C Ge = N A ρ Si N Ge A Ge ρ Si ρ Ge

5 = ( x10 23 atoms/ mol)(2.33 g/cm 3 ) ( 2.43 x10 21 atoms / cm 3 )(72.59 g /mol) = 11.7 wt% 2.33 g/ cm g/ cm 3 Q3- Compare the energies of a) a surface to a grain boundary and b) a small angle boundary to high angle boundary. A3- (a) The surface energy will be greater than the grain boundary energy since some atoms on one side of the boundary will bond to atoms on the other side--i.e., there will be fewer unsatisfied bonds along a grain boundary. (b) The small angle grain boundary energy is lower than for a high angle one because more atoms bond across the boundary for the small angle, and, thus, there are fewer unsatisfied bonds. CHAPTER 5 Q1- Compare self-diffusion and interdiffusion. A1- Self-diffusion is atomic migration in pure metals--i.e., when all atoms exchanging positions are of the same type. Interdiffusion is diffusion of atoms of one metal into another metal. Q2- How do you monitor self diffusion? A2- Self-diffusion may be monitored by using radioactive isotopes of the metal being studied. The motion of these isotopic atoms may be monitored by measurement of radioactivity level. Q3- A sheet of 1.5 mm thick steel has nitrogen atmosphere on both sides at 1200 o C and is permitted to achieve a steady-state diffusion condition. D = 6x10-11 m 2 /s and diffusion flux is found to be 1.2x10-7 kg/m 2 s. Also, it is known that the concentration of nitrogen in the steel at the high pressure surface is 4 kg/m 3. How far into the sheet from this high pressure side will the concentration be 2.0 kg/m 3? Assume a linear concentration profile. A3- We are asked to determine the position at which the nitrogen concentration is 2 kg/m 3. This problem is solved by using Equation (5.3) in the form J = D C A C B x x A B If we take C A to be the point at which the concentration of nitrogen is 4 kg/m 3, then it becomes necessary to solve for x B, as C x B = x A + D A C B J Assume x is zero at the surface, in which case A ( ) x B = x m 2 /s = 1 x 10-3 m = 1 mm ( 4 kg/m 3 2 kg/m 3 ) 1.2 x 10 7 kg /m 2 -s CHAPTER 6 Q1- Calculate the elastic strain that results for an aluminum specimen stressed in tension. The crosssectional area is (10 mm) x (12.7 mm) = 127 mm 2 (= 1.27 x 10-4 m 2 = 0.20 in. 2 ); also, the elastic modulus for Al is 69 GPa (or 69 x 10 9 N/m 2 ). A1- By using Hooke s law: ε = σ E = F A o E = 35,500 N 1.27 x 10 4 m 2 ( )( 69 x 109 N/m 2 ) = 4.1 x 10-3

6 CHAPTER 7 Q1- Consider a single crystal of silver oriented such that a tensile stress is applied along a [001] direction. If slip occurs on a (111) plane and in a [ 101 ] direction, and is initiated at an applied tensile stress of 1.1 MPa, compute the critical resolved shear stress. A1- This problem asks that we compute the critical resolved shear stress for silver. In order to do this, we must employ Equation (7.3), but first it is necessary to solve for the angles λ and φ from the sketch below. If the unit cell edge length is a, then λ = tan -1 a =45 a For the angle φ, we must examine the triangle OAB. The length of line OA is just a, whereas, the length of AB is a 2. Thus, φ = tan -1 a 2 = 54.7 a And, finally τ crss = σ y (cos φ cos λ) = (1.1MPa) [ cos(54.7) cos(45) ] = 0.45 MPa

7 CHAPTER 8 Q1. A1. CHAPTER 9 Q1- For an alloy of composition 52wt% Zn 48wt% Cu (Fig. 9.19, 7 th Ed.), cite the phases present and their mass fractions at the following temperatures: 1000 o C, 800 o C, 500 o C, and 300 o C. A1- At 1000 C, a liquid phase is present; W L = 1.0 At 800 C, the β phase is present, and W β = 1.0 At 500 C, β and γ phases are present, and W γ = C o C β C γ C β = = 0.33 W β = = 0.67 At 300 C, the β' and γ phases are present, and W β' = C γ C o = C C γ β' = 0.78 W γ = = 0.22

Homework #4 PROBLEM SOLUTIONS

Homework #4 PROBLEM SOLUTIONS Homework #4 PROBLEM SOLUTIONS 4.2 Determination of the number of vacancies per cubic meter in gold at 900 C (1173 K) requires the utilization of Equations (4.1) and (4.2) as follows: N V N exp Q V kt N

More information

Impurities in Solids. Crystal Electro- Element R% Structure negativity Valence

Impurities in Solids. Crystal Electro- Element R% Structure negativity Valence 4-4 Impurities in Solids 4.4 In this problem we are asked to cite which of the elements listed form with Ni the three possible solid solution types. For complete substitutional solubility the following

More information

CHAPTER 5 IMPERFECTIONS IN SOLIDS PROBLEM SOLUTIONS ev /atom = exp. kt ( =

CHAPTER 5 IMPERFECTIONS IN SOLIDS PROBLEM SOLUTIONS ev /atom = exp. kt ( = CHAPTER 5 IMPERFECTIONS IN SOLIDS PROBLEM SOLUTIONS Vacancies and Self-Interstitials 5.1 Calculate the fraction of atom sites that are vacant for copper at its melting temperature of 1084 C (1357 K). Assume

More information

CHAPTER 5 IMPERFECTIONS IN SOLIDS PROBLEM SOLUTIONS

CHAPTER 5 IMPERFECTIONS IN SOLIDS PROBLEM SOLUTIONS CHAPTER 5 IMPERFECTIONS IN SOLIDS PROBLEM SOLUTIONS Vacancies and Self-Interstitials 5.1 Calculate the fraction of atom sites that are vacant for copper at its melting temperature of 1084 C (1357 K). Assume

More information

3.40 Sketch within a cubic unit cell the following planes: (a) (01 1 ) (b) (112 ) (c) (102 ) (d) (13 1) Solution

3.40 Sketch within a cubic unit cell the following planes: (a) (01 1 ) (b) (112 ) (c) (102 ) (d) (13 1) Solution 3.40 Sketch within a cubic unit cell the following planes: (a) (01 1 ) (b) (11 ) (c) (10 ) (d) (13 1) The planes called for are plotted in the cubic unit cells shown below. 3.41 Determine the Miller indices

More information

N = N A ρ Pb A Pb. = ln N Q v kt. 지난문제. Below are shown three different crystallographic planes for a unit cell of some hypothetical metal.

N = N A ρ Pb A Pb. = ln N Q v kt. 지난문제. Below are shown three different crystallographic planes for a unit cell of some hypothetical metal. 지난문제. Below are shown three different crystallographic planes for a unit cell of some hypothetical metal. The circles represent atoms: (a) To what crystal system does the unit cell belong? (b) What would

More information

Point Defects in Metals

Point Defects in Metals CHAPTER 5 IMPERFECTIONS IN SOLIDS PROBLEM SOLUTIONS Point Defects in Metals 5.1 Calculate the fraction of atom sites that are vacant for lead at its melting temperature of 327 C (600 K). Assume an energy

More information

N = N A Al A Al. = ( atoms /mol)(2.62 g /cm 3 ) g /mol. ln N v = ln N Q v kt. = kt ln v. Q v

N = N A Al A Al. = ( atoms /mol)(2.62 g /cm 3 ) g /mol. ln N v = ln N Q v kt. = kt ln v. Q v 4.3 alculate the activation energy for vacancy formation in aluminum, given that the equilibrium number of vacancies at 500 (773 K) is 7.57 10 23 m -3. The atomic weight and density (at 500 ) for aluminum

More information

CHAPTER 8 DEFORMATION AND STRENGTHENING MECHANISMS PROBLEM SOLUTIONS

CHAPTER 8 DEFORMATION AND STRENGTHENING MECHANISMS PROBLEM SOLUTIONS CHAPTER 8 DEFORMATION AND STRENGTHENING MECHANISMS PROBLEM SOLUTIONS Slip Systems 8.3 (a) Compare planar densities (Section 3.15 and Problem W3.46 [which appears on the book s Web site]) for the (100),

More information

ME 254 MATERIALS ENGINEERING 1 st Semester 1431/ rd Mid-Term Exam (1 hr)

ME 254 MATERIALS ENGINEERING 1 st Semester 1431/ rd Mid-Term Exam (1 hr) 1 st Semester 1431/1432 3 rd Mid-Term Exam (1 hr) Question 1 a) Answer the following: 1. Do all metals have the same slip system? Why or why not? 2. For each of edge, screw and mixed dislocations, cite

More information

Engineering 45: Properties of Materials Final Exam May 9, 2012 Name: Student ID number:

Engineering 45: Properties of Materials Final Exam May 9, 2012 Name: Student ID number: Engineering 45: Properties of Materials Final Exam May 9, 2012 Name: Student ID number: Instructions: Answer all questions and show your work. You will not receive partial credit unless you show your work.

More information

Dept.of BME Materials Science Dr.Jenan S.Kashan 1st semester 2nd level. Imperfections in Solids

Dept.of BME Materials Science Dr.Jenan S.Kashan 1st semester 2nd level. Imperfections in Solids Why are defects important? Imperfections in Solids Defects have a profound impact on the various properties of materials: Production of advanced semiconductor devices require not only a rather perfect

More information

Chapter 8 Strain Hardening and Annealing

Chapter 8 Strain Hardening and Annealing Chapter 8 Strain Hardening and Annealing This is a further application of our knowledge of plastic deformation and is an introduction to heat treatment. Part of this lecture is covered by Chapter 4 of

More information

Single vs Polycrystals

Single vs Polycrystals WEEK FIVE This week, we will Learn theoretical strength of single crystals Learn metallic crystal structures Learn critical resolved shear stress Slip by dislocation movement Single vs Polycrystals Polycrystals

More information

Structure of silica glasses (Chapter 12)

Structure of silica glasses (Chapter 12) Questions and Problems 97 Glass Ceramics (Structure) heat-treated so as to become crystalline in nature. The following concept map notes this relationship: Structure of noncrystalline solids (Chapter 3)

More information

Problems to the lecture Physical Metallurgy ( Materialkunde ) Chapter 6: Mechanical Properties

Problems to the lecture Physical Metallurgy ( Materialkunde ) Chapter 6: Mechanical Properties Institut für Metallkunde und Metallphysik Direktor: Prof. Dr. rer. nat. Günter Gottstein RWTH Aachen, D-52056 Aachen Internet: http://www.imm.rwth-aachen.de E-mail: imm@imm.rwth-aachen.de Tel.: +49 241

More information

Density Computations

Density Computations CHAPTER 3 THE STRUCTURE OF CRYSTALLINE SOLIDS Fundamental Concepts 3.1 What is the difference between atomic structure and crystal structure? Unit Cells Metallic Crystal Structures 3.2 If the atomic radius

More information

a. 50% fine pearlite, 12.5% bainite, 37.5% martensite. 590 C for 5 seconds, 350 C for 50 seconds, cool to room temperature.

a. 50% fine pearlite, 12.5% bainite, 37.5% martensite. 590 C for 5 seconds, 350 C for 50 seconds, cool to room temperature. Final Exam Wednesday, March 21, noon to 3:00 pm (160 points total) 1. TTT Diagrams A U.S. steel producer has four quench baths, used to quench plates of eutectoid steel to 700 C, 590 C, 350 C, and 22 C

More information

Student Name: ID Number:

Student Name: ID Number: Student Name: ID Number: DEPARTMENT OF MECHANICAL ENGINEERING CONCORDIA UNIVERSITY MATERIALS SCIENCE - MECH 1/ - Sections T & X MIDTERM 003 Instructors: Dr. M.Pugh & Dr. M.Medraj Time Allowed: one (1)

More information

Tutorial 2 : Crystalline Solid, Solidification, Crystal Defect and Diffusion

Tutorial 2 : Crystalline Solid, Solidification, Crystal Defect and Diffusion Tutorial 1 : Introduction and Atomic Bonding 1. Explain the difference between ionic and metallic bonding between atoms in engineering materials. 2. Show that the atomic packing factor for Face Centred

More information

Chapter 7: Dislocations and strengthening mechanisms

Chapter 7: Dislocations and strengthening mechanisms Chapter 7: Dislocations and strengthening mechanisms Introduction Basic concepts Characteristics of dislocations Slip systems Slip in single crystals Plastic deformation of polycrystalline materials Plastically

More information

Chapter Outline Dislocations and Strengthening Mechanisms. Introduction

Chapter Outline Dislocations and Strengthening Mechanisms. Introduction Chapter Outline Dislocations and Strengthening Mechanisms What is happening in material during plastic deformation? Dislocations and Plastic Deformation Motion of dislocations in response to stress Slip

More information

Fundamental concepts and language Unit cells Crystal structures! Face-centered cubic! Body-centered cubic! Hexagonal close-packed Close packed

Fundamental concepts and language Unit cells Crystal structures! Face-centered cubic! Body-centered cubic! Hexagonal close-packed Close packed Fundamental concepts and language Unit cells Crystal structures! Face-centered cubic! Body-centered cubic! Hexagonal close-packed Close packed crystal structures Density computations Crystal structure

More information

STRENGTHENING MECHANISM IN METALS

STRENGTHENING MECHANISM IN METALS Background Knowledge Yield Strength STRENGTHENING MECHANISM IN METALS Metals yield when dislocations start to move (slip). Yield means permanently change shape. Slip Systems Slip plane: the plane on which

More information

Defect in crystals. Primer in Materials Science Spring

Defect in crystals. Primer in Materials Science Spring Defect in crystals Primer in Materials Science Spring 2017 11.05.2017 1 Introduction The arrangement of the atoms in all materials contains imperfections which have profound effect on the behavior of the

More information

ASE324: Aerospace Materials Laboratory

ASE324: Aerospace Materials Laboratory ASE324: Aerospace Materials Laboratory Instructor: Rui Huang Dept of Aerospace Engineering and Engineering Mechanics The University of Texas at Austin Fall 2003 Lecture 3 September 4, 2003 Iron and Steels

More information

Point coordinates. Point coordinates for unit cell center are. Point coordinates for unit cell corner are 111

Point coordinates. Point coordinates for unit cell center are. Point coordinates for unit cell corner are 111 Point coordinates c z 111 Point coordinates for unit cell center are a/2, b/2, c/2 ½ ½ ½ Point coordinates for unit cell corner are 111 x a z 000 b 2c y Translation: integer multiple of lattice constants

More information

Problem Set 2 Solutions

Problem Set 2 Solutions M 4733: Deformation and Fracture of ngineering Materials Spring 00 Problem Set Solutions *) Prove that for the case of cubic crystals the modulus of elasticity in any given direction may be given by the

More information

5. A round rod is subjected to an axial force of 10 kn. The diameter of the rod is 1 inch. The engineering stress is (a) MPa (b) 3.

5. A round rod is subjected to an axial force of 10 kn. The diameter of the rod is 1 inch. The engineering stress is (a) MPa (b) 3. The Avogadro's number = 6.02 10 23 1 lb = 4.45 N 1 nm = 10 Å = 10-9 m SE104 Structural Materials Sample Midterm Exam Multiple choice problems (2.5 points each) For each problem, choose one and only one

More information

Chapter Outline. How do atoms arrange themselves to form solids?

Chapter Outline. How do atoms arrange themselves to form solids? Chapter Outline How do atoms arrange themselves to form solids? Fundamental concepts and language Unit cells Crystal structures! Face-centered cubic! Body-centered cubic! Hexagonal close-packed Close packed

More information

Ex: NaCl. Ironically Bonded Solid

Ex: NaCl. Ironically Bonded Solid Ex: NaCl. Ironically Bonded Solid Lecture 2 THE STRUCTURE OF CRYSTALLINE SOLIDS 3.2 FUNDAMENTAL CONCEPTS SOLIDS AMORPHOUS CRYSTALLINE Atoms in an amorphous Atoms in a crystalline solid solid are arranged

More information

MEMS 487. Class 04, Feb. 13, K.J. Hemker

MEMS 487. Class 04, Feb. 13, K.J. Hemker MEMS 487 Class 04, Feb. 13, 2003 Materials Come As:!Amorphous Glasses, polymers, some metal alloys Processing can result in amorphous structures! Crystalline Single crystals Textured crystals Polycrystalline

More information

CHAPTER 4 INTRODUCTION TO DISLOCATIONS. 4.1 A single crystal of copper yields under a shear stress of about 0.62 MPa. The shear modulus of

CHAPTER 4 INTRODUCTION TO DISLOCATIONS. 4.1 A single crystal of copper yields under a shear stress of about 0.62 MPa. The shear modulus of CHAPTER 4 INTRODUCTION TO DISLOCATIONS 4.1 A single crystal of copper yields under a shear stress of about 0.62 MPa. The shear modulus of copper is approximately. With this data, compute an approximate

More information

Crystal structure of the material :- the manner in which atoms, ions, or molecules are spatially.

Crystal structure of the material :- the manner in which atoms, ions, or molecules are spatially. Crystal structure A crystalline material :- is one in which the atoms are situated in a repeating or periodic array over large atomic distances. Crystal structure of the material :- the manner in which

More information

Chapter Outline How do atoms arrange themselves to form solids?

Chapter Outline How do atoms arrange themselves to form solids? Chapter Outline How do atoms arrange themselves to form solids? Fundamental concepts and language Unit cells Crystal structures Face-centered cubic Body-centered cubic Hexagonal close-packed Close packed

More information

Materials Science and Engineering

Materials Science and Engineering Introduction to Materials Science and Engineering Chap. 3. The Structures of Crystalline Solids How do atoms assemble into solid structures? How does the density of a material depend on its structure?

More information

Point coordinates. x z

Point coordinates. x z Point coordinates c z 111 a 000 b y x z 2c b y Point coordinates z y Algorithm 1. Vector repositioned (if necessary) to pass through origin. 2. Read off projections in terms of unit cell dimensions a,

More information

Chapter 5. Imperfections in Solids

Chapter 5. Imperfections in Solids Chapter 5 Imperfections in Solids Chapter 5 2D Defects and Introduction to Diffusion Imperfections in Solids Issues to Address... What types of defects arise in solids? Can the number and type of defects

More information

Movement of edge and screw dislocations

Movement of edge and screw dislocations Movement of edge and screw dislocations Formation of a step on the surface of a crystal by motion of (a) n edge dislocation: the dislocation line moves in the direction of the applied shear stress τ. (b)

More information

ME254: Materials Engineering Second Midterm Exam 1 st semester December 10, 2015 Time: 2 hrs

ME254: Materials Engineering Second Midterm Exam 1 st semester December 10, 2015 Time: 2 hrs ME254: Materials Engineering Second Midterm Exam 1 st semester 1436-1437 December 10, 2015 Time: 2 hrs Problem 1: (24 points) A o = π/4*d o 2 = π/4*17 2 = 227 mm 2 L o = 32 mm a) Determine the following

More information

Strengthening Mechanisms

Strengthening Mechanisms ME 254: Materials Engineering Chapter 7: Dislocations and Strengthening Mechanisms 1 st Semester 1435-1436 (Fall 2014) Dr. Hamad F. Alharbi, harbihf@ksu.edu.sa November 18, 2014 Outline DISLOCATIONS AND

More information

Energy and Packing. typical neighbor bond energy. typical neighbor bond energy. Dense, regular-packed structures tend to have lower energy.

Energy and Packing. typical neighbor bond energy. typical neighbor bond energy. Dense, regular-packed structures tend to have lower energy. Energy and Packing Non dense, random packing Energy typical neighbor bond length typical neighbor bond energy r Dense, regular packing Energy typical neighbor bond length typical neighbor bond energy r

More information

بسم هللا الرحمن الرحیم. Materials Science. Chapter 3 Structures of Metals & Ceramics

بسم هللا الرحمن الرحیم. Materials Science. Chapter 3 Structures of Metals & Ceramics بسم هللا الرحمن الرحیم Materials Science Chapter 3 Structures of Metals & Ceramics 1 ISSUES TO ADDRESS... How do atoms assemble into solid structures? How does the density of a material depend on its structure?

More information

Chapter 4: Imperfections (Defects) in Solids

Chapter 4: Imperfections (Defects) in Solids Chapter 4: Imperfections (Defects) in Solids ISSUES TO ADDRESS... What types of defects exist in solids? How do defects affect material properties? Can the number and type of defects be varied and controlled?

More information

Strengthening Mechanisms

Strengthening Mechanisms Strengthening Mechanisms The ability of a metal/ alloy to plastically deform depends on the ability of dislocations to move. Strengthening techniques rely on restricting dislocation motion to render a

More information

(12) 1. Just one True and False question and a couple of multiple choice calculations, circle one answer for each problem, no partial credit.

(12) 1. Just one True and False question and a couple of multiple choice calculations, circle one answer for each problem, no partial credit. (1) 1. Just one True and False question and a couple of multiple choice calculations, circle one answer for each problem, no partial credit. The next page is left blank for your use, but no partial will

More information

Engineering materials

Engineering materials 1 Engineering materials Lecture 2 Imperfections and defects Response of materials to stress 2 Crystalline Imperfections (4.4) No crystal is perfect. Imperfections affect mechanical properties, chemical

More information

Materials Science. Imperfections in Solids CHAPTER 5: IMPERFECTIONS IN SOLIDS. Types of Imperfections

Materials Science. Imperfections in Solids CHAPTER 5: IMPERFECTIONS IN SOLIDS. Types of Imperfections In the Name of God Materials Science CHAPTER 5: IMPERFECTIONS IN SOLIDS ISSUES TO ADDRESS... What are the solidification mechanisms? What types of defects arise in solids? Can the number and type of defects

More information

Chapter 5: Diffusion. Introduction

Chapter 5: Diffusion. Introduction Chapter 5: Diffusion Outline Introduction Diffusion mechanisms Steady-state diffusion Nonsteady-state diffusion Factors that influence diffusion Introduction Diffusion: the phenomenon of material transport

More information

Imperfections: Good or Bad? Structural imperfections (defects) Compositional imperfections (impurities)

Imperfections: Good or Bad? Structural imperfections (defects) Compositional imperfections (impurities) Imperfections: Good or Bad? Structural imperfections (defects) Compositional imperfections (impurities) 1 Structural Imperfections A perfect crystal has the lowest internal energy E Above absolute zero

More information

CHAPTER 4 1/1/2016. Mechanical Properties of Metals - I. Processing of Metals - Casting. Hot Rolling of Steel. Casting (Cont..)

CHAPTER 4 1/1/2016. Mechanical Properties of Metals - I. Processing of Metals - Casting. Hot Rolling of Steel. Casting (Cont..) Processing of Metals - Casting CHAPTER 4 Mechanical Properties of Metals - I Most metals are first melted in a furnace. Alloying is done if required. Large ingots are then cast. Sheets and plates are then

More information

Introduction to Engineering Materials ENGR2000 Chapter 7: Dislocations and Strengthening Mechanisms. Dr. Coates

Introduction to Engineering Materials ENGR2000 Chapter 7: Dislocations and Strengthening Mechanisms. Dr. Coates Introduction to Engineering Materials ENGR2000 Chapter 7: Dislocations and Strengthening Mechanisms Dr. Coates An edge dislocation moves in response to an applied shear stress dislocation motion 7.1 Introduction

More information

Chapter 7 Dislocations and Strengthening Mechanisms. Dr. Feras Fraige

Chapter 7 Dislocations and Strengthening Mechanisms. Dr. Feras Fraige Chapter 7 Dislocations and Strengthening Mechanisms Dr. Feras Fraige Chapter Outline Dislocations and Strengthening Mechanisms What is happening in material during plastic deformation? Dislocations and

More information

J = D C A C B x A x B + D C A C. = x A kg /m 2

J = D C A C B x A x B + D C A C. = x A kg /m 2 1. (a) Compare interstitial and vacancy atomic mechanisms for diffusion. (b) Cite two reasons why interstitial diffusion is normally more rapid than vacancy diffusion. (a) With vacancy diffusion, atomic

More information

CHAPTER 5 DIFFUSION PROBLEM SOLUTIONS

CHAPTER 5 DIFFUSION PROBLEM SOLUTIONS CHAPTER 5 DIFFUSION PROBLEM SOLUTIONS 5.5 (a) Briefly explain the concept of a driving force. (b) What is the driving force for steady-state diffusion? (a) The driving force is that which compels a reaction

More information

Dislocations & Materials Classes. Dislocation Motion. Dislocation Motion. Lectures 9 and 10

Dislocations & Materials Classes. Dislocation Motion. Dislocation Motion. Lectures 9 and 10 Lectures 9 and 10 Chapter 7: Dislocations & Strengthening Mechanisms Dislocations & Materials Classes Metals: Disl. motion easier. -non-directional bonding -close-packed directions for slip. electron cloud

More information

Why are dislocations observed primarily in metals CHAPTER 8: DEFORMATION AND STRENGTHENING MECHANISMS

Why are dislocations observed primarily in metals CHAPTER 8: DEFORMATION AND STRENGTHENING MECHANISMS Why are dislocations observed primarily in metals CHAPTER 8: and alloys? DEFORMATION AND STRENGTHENING MECHANISMS How are strength and dislocation motion related? How do we manipulate properties? Strengthening

More information

CHAPTER 6 OUTLINE. DIFFUSION and IMPERFECTIONS IN SOLIDS

CHAPTER 6 OUTLINE. DIFFUSION and IMPERFECTIONS IN SOLIDS CHAPTER 6 DIFFUSION and IMPERFECTIONS IN SOLIDS OUTLINE 1. TYPES OF DIFFUSIONS 1.1. Interdiffusion 1.2. Selfdiffusion 1.3.Diffusion mechanisms 1.4.Examples 2. TYPES OF IMPERFECTIONS 2.1.Point Defects 2.2.Line

More information

MSE 170 Midterm review

MSE 170 Midterm review MSE 170 Midterm review Exam date: 11/2/2008 Mon, lecture time Place: Here! Close book, notes and no collaborations A sheet of letter-sized paper with double-sided notes is allowed Material on the exam

More information

ES-260 Practice Final Exam Fall Name: St. No. Problems 1 to 3 were not appropriate for the current course coverage.

ES-260 Practice Final Exam Fall Name: St. No. Problems 1 to 3 were not appropriate for the current course coverage. ES-260 Practice Final Exam Fall 2014 Name: St. No. Circle correct answers All Questions worth 4 pts each. The True and False section at the end are bonus questions worth 1 point for a correct and -1 point

More information

Packing of atoms in solids

Packing of atoms in solids MME131: Lecture 6 Packing of atoms in solids A. K. M. B. Rashid Professor, Department of MME BUET, Dhaka Today s topics Atomic arrangements in solids Points, directions and planes in unit cell References:

More information

Problems. 104 CHAPTER 3 Atomic and Ionic Arrangements

Problems. 104 CHAPTER 3 Atomic and Ionic Arrangements 104 CHAPTER 3 Atomic and Ionic Arrangements Repeat distance The distance from one lattice point to the adjacent lattice point along a direction. Short-range order The regular and predictable arrangement

More information

Chapter 12 The Solid State The Structure of Metals and Alloys

Chapter 12 The Solid State The Structure of Metals and Alloys Chapter 12 The Solid State The Structure of Metals and Alloys The Solid State Crystalline solid a solid made of an ordered array of atoms, ion, or molecules Amorphous solids a solid that lacks long-range

More information

Defects and Diffusion

Defects and Diffusion Defects and Diffusion Goals for the Unit Recognize various imperfections in crystals Point imperfections Impurities Line, surface and bulk imperfections Define various diffusion mechanisms Identify factors

More information

INGE Engineering Materials. Chapter 3 (cont.)

INGE Engineering Materials. Chapter 3 (cont.) Some techniques used: Chapter 3 (cont.) This section will address the question how do we determine the crystal structure of a solid sample? Electron microscopy (by direct and indirect observations) Scanning

More information

CRYSTAL STRUCTURE TERMS

CRYSTAL STRUCTURE TERMS CRYSTAL STRUCTURE TERMS crystalline material - a material in which atoms, ions, or molecules are situated in a periodic 3-dimensional array over large atomic distances (all metals, many ceramic materials,

More information

Plastic Deformation and Strengthening Mechanisms in Crystalline Materials

Plastic Deformation and Strengthening Mechanisms in Crystalline Materials Plastic Deformation and Strengthening Mechanisms in Crystalline Materials Updated 6 October, 2011 Slip in Polycrystalline Materials and all you ll ever need to know about it in MSE250 and life (unless

More information

(a) Would you expect the element P to be a donor or an acceptor defect in Si?

(a) Would you expect the element P to be a donor or an acceptor defect in Si? MSE 200A Survey of Materials Science Fall, 2008 Problem Set No. 2 Problem 1: At high temperature Fe has the fcc structure (called austenite or γ-iron). Would you expect to find C atoms in the octahedral

More information

Energy and Packing. Materials and Packing

Energy and Packing. Materials and Packing Energy and Packing Non dense, random packing Energy typical neighbor bond length typical neighbor bond energy r Dense, regular packing Energy typical neighbor bond length typical neighbor bond energy r

More information

12/10/09. Chapter 4: Imperfections in Solids. Imperfections in Solids. Polycrystalline Materials ISSUES TO ADDRESS...

12/10/09. Chapter 4: Imperfections in Solids. Imperfections in Solids. Polycrystalline Materials ISSUES TO ADDRESS... Chapter 4: ISSUES TO ADDRESS... What are the solidification mechanisms? What types of defects arise in solids? Can the number and type of defects be varied and controlled? How do defects affect material

More information

=E Δ l l o. π d o 2 4. Δ l = 4Fl o π d o 2 E. = 0.50 mm (0.02 in.)

=E Δ l l o. π d o 2 4. Δ l = 4Fl o π d o 2 E. = 0.50 mm (0.02 in.) 6.10 (a) This portion of the problem asks that the tangent modulus be determined for the gray cast iron, the stress-strain behavior of which is shown in Figure 6.25. The slope (i.e., σ/ ε) of a tangent

More information

METALLIC CRYSTALS. tend to be densely packed. have several reasons for dense packing: have the simplest crystal structures.

METALLIC CRYSTALS. tend to be densely packed. have several reasons for dense packing: have the simplest crystal structures. METALLIC CRYSTALS tend to be densely packed. have several reasons for dense packing: -Typically, only one element is present, so all atomic radii are the same. -Metallic bonding is not directional. -Nearest

More information

Chapter 3 Structure of Crystalline Solids

Chapter 3 Structure of Crystalline Solids Chapter 3 Structure of Crystalline Solids Crystal Structures Points, Directions, and Planes Linear and Planar Densities X-ray Diffraction How do atoms assemble into solid structures? (for now, focus on

More information

Materials and their structures

Materials and their structures Materials and their structures 2.1 Introduction: The ability of materials to undergo forming by different techniques is dependent on their structure and properties. Behavior of materials depends on their

More information

Materials Science ME 274. Dr Yehia M. Youssef. Materials Science. Copyright YM Youssef, 4-Oct-10

Materials Science ME 274. Dr Yehia M. Youssef. Materials Science. Copyright YM Youssef, 4-Oct-10 ME 274 Dr Yehia M. Youssef 1 The Structure of Crystalline Solids Solid materials may be classified according to the regularity with which atoms or ions are arranged with respect to one another. A crystalline

More information

MME 2001 MATERIALS SCIENCE

MME 2001 MATERIALS SCIENCE MME 2001 MATERIALS SCIENCE 1 20.10.2015 crystal structures X tal structure Coord. # Atoms/ unit cell a=f(r) APF % SC 6 1 2R 52 BCC 8 2 4R/ 3 68 FCC 12 4 2R 2 74 HCP 12 6 2R 74 Theoretical Density, knowing

More information

CHAPTER 5: DIFFUSION IN SOLIDS

CHAPTER 5: DIFFUSION IN SOLIDS CHAPTER 5: DIFFUSION IN SOLIDS ISSUES TO ADDRESS... How does diffusion occur? Why is it an important part of processing? How can the rate of diffusion be predicted for some simple cases? How does diffusion

More information

Chapter 8. Deformation and Strengthening Mechanisms

Chapter 8. Deformation and Strengthening Mechanisms Chapter 8 Deformation and Strengthening Mechanisms Chapter 8 Deformation Deformation and Strengthening Issues to Address... Why are dislocations observed primarily in metals and alloys? How are strength

More information

IMPERFECTIONSFOR BENEFIT. Sub-topics. Point defects Linear defects dislocations Plastic deformation through dislocations motion Surface

IMPERFECTIONSFOR BENEFIT. Sub-topics. Point defects Linear defects dislocations Plastic deformation through dislocations motion Surface IMPERFECTIONSFOR BENEFIT Sub-topics 1 Point defects Linear defects dislocations Plastic deformation through dislocations motion Surface IDEAL STRENGTH Ideally, the strength of a material is the force necessary

More information

Phase Diagrams of Pure Substances Predicts the stable phase as a function of P total and T. Example: water can exist in solid, liquid and vapor

Phase Diagrams of Pure Substances Predicts the stable phase as a function of P total and T. Example: water can exist in solid, liquid and vapor PHASE DIAGRAMS Phase a chemically and structurally homogenous region of a material. Region of uniform physical and chemical characteristics. Phase boundaries separate two distinct phases. A single phase

More information

Structure of Metals 1

Structure of Metals 1 1 Structure of Metals Metals Basic Structure (Review) Property High stiffness, better toughness, good electrical conductivity, good thermal conductivity Why metals have these nice properties - structures

More information

Imperfections, Defects and Diffusion

Imperfections, Defects and Diffusion Imperfections, Defects and Diffusion Lattice Defects Week5 Material Sciences and Engineering MatE271 1 Goals for the Unit I. Recognize various imperfections in crystals (Chapter 4) - Point imperfections

More information

HOMEWORK 6. solutions

HOMEWORK 6. solutions HOMEWORK 6. SCI 1410: materials science & solid state chemistry solutions Textbook Problems: Imperfections in Solids 1. Askeland 4-67. Why is most gold or siler jewelry made out of gold or siler alloyed

More information

REVISED PAGES IMPORTANT TERMS AND CONCEPTS REFERENCES QUESTIONS AND PROBLEMS. 166 Chapter 6 / Mechanical Properties of Metals

REVISED PAGES IMPORTANT TERMS AND CONCEPTS REFERENCES QUESTIONS AND PROBLEMS. 166 Chapter 6 / Mechanical Properties of Metals 1496T_c06_131-173 11/16/05 17:06 Page 166 166 Chapter 6 / Mechanical Properties of Metals IMPORTANT TERMS AND CONCEPTS Anelasticity Design stress Ductility Elastic deformation Elastic recovery Engineering

More information

Learning Objectives. Chapter Outline. Solidification of Metals. Solidification of Metals

Learning Objectives. Chapter Outline. Solidification of Metals. Solidification of Metals Learning Objectives Study the principles of solidification as they apply to pure metals. Examine the mechanisms by which solidification occurs. - Chapter Outline Importance of Solidification Nucleation

More information

CHAPTER 3: CRYSTAL STRUCTURES & PROPERTIES

CHAPTER 3: CRYSTAL STRUCTURES & PROPERTIES CHAPTER 3: CRYSTAL STRUCTURES & PROPERTIES ISSUES TO ADDRESS... How do atoms assemble into solid structures? (for now, focus on metals) How does the density of a material depend on its structure? When

More information

Strengthening Mechanisms. Today s Topics

Strengthening Mechanisms. Today s Topics MME 131: Lecture 17 Strengthening Mechanisms Prof. A.K.M.B. Rashid Department of MME BUET, Dhaka Today s Topics Strengthening strategies: Grain strengthening Solid solution strengthening Work hardening

More information

Introduction to Engineering Materials ENGR2000 Chapter 4: Imperfections in Solids. Dr. Coates

Introduction to Engineering Materials ENGR2000 Chapter 4: Imperfections in Solids. Dr. Coates Introduction to Engineering Materials ENGR000 Chapter 4: Imperfections in Solids Dr. Coates Learning Objectives 1. Describe both vacancy and self interstitial defects. Calculate the equilibrium number

More information

Activation of deformation mechanism

Activation of deformation mechanism Activation of deformation mechanism The deformation mechanism activates when a critical amount of mechanical stress imposed to the crystal The dislocation glide through the slip systems when the required

More information

CHAPTER. The Structure of Crystalline Solids

CHAPTER. The Structure of Crystalline Solids CHAPTER 4 The Structure of Crystalline Solids 1 Chapter 4: The Structure of Crystalline Solids ISSUES TO ADDRESS... What are common crystal structures for metals and ceramics? What features of a metal

More information

9/29/2014 8:52 PM. Chapter 3. The structure of crystalline solids. Dr. Mohammad Abuhaiba, PE

9/29/2014 8:52 PM. Chapter 3. The structure of crystalline solids. Dr. Mohammad Abuhaiba, PE 1 Chapter 3 The structure of crystalline solids 2 Home Work Assignments HW 1 2, 7, 12, 17, 22, 29, 34, 39, 44, 48, 53, 58, 63 Due Sunday 12/10/2014 Quiz # 1 will be held on Monday 13/10/2014 at 11:00 am

More information

Chapter 1. The Structure of Metals. Body Centered Cubic (BCC) Structures

Chapter 1. The Structure of Metals. Body Centered Cubic (BCC) Structures Chapter 1 The Structure of Metals Body Centered Cubic (BCC) Structures Figure 1. The body-centered cubic (bcc) crystal structure: (a) hard-ball model; (b) unit cell; and (c) single crystal with many unit

More information

Chapter 2. Ans: e (<100nm size materials are called nanomaterials)

Chapter 2. Ans: e (<100nm size materials are called nanomaterials) Chapter 2 1. Materials science and engineering include (s) the study of: (a) metals (b) polymers (c) ceramics (d) composites (e) nanomaterials (f) all of the above Ans: f 2. Which one of the following

More information

MATERIALS SCIENCE-44 Which point on the stress-strain curve shown gives the ultimate stress?

MATERIALS SCIENCE-44 Which point on the stress-strain curve shown gives the ultimate stress? MATERIALS SCIENCE 43 Which of the following statements is FALSE? (A) The surface energy of a liquid tends toward a minimum. (B) The surface energy is the work required to create a unit area of additional

More information

9/28/2013 9:26 PM. Chapter 3. The structure of crystalline solids. Dr. Mohammad Abuhaiba, PE

9/28/2013 9:26 PM. Chapter 3. The structure of crystalline solids. Dr. Mohammad Abuhaiba, PE Chapter 3 The structure of crystalline solids 1 2 Why study the structure of crystalline solids? Properties of some materials are directly related to their crystal structure. Significant property differences

More information

CIVE.3100 ENGINEERING MATERIALS EXAM #2: METALS, DIFFUSION, PHASE DIAGRAMS, STRESS STRAIN DIAGRAMS, AND RULE OF MIXTURES Print Name: Section: Date:

CIVE.3100 ENGINEERING MATERIALS EXAM #2: METALS, DIFFUSION, PHASE DIAGRAMS, STRESS STRAIN DIAGRAMS, AND RULE OF MIXTURES Print Name: Section: Date: CIVE.3100 ENGINEERING MATERIALS EXAM #2: METALS, DIFFUSION, PHASE DIAGRAMS, STRESS STRAIN DIAGRAMS, AND RULE OF MIXTURES Print Name: Section: Date: You may NOT use the back of any page if additional workspace

More information

CHAPTER 3. Crystal Structures and Crystal Geometry 3-1

CHAPTER 3. Crystal Structures and Crystal Geometry 3-1 CHAPTER 3 Crystal Structures and Crystal Geometry 3-1 The Space Lattice and Unit Cells 3-2 Atoms, arranged in repetitive 3-Dimensional pattern, in long range order (LRO) give rise to crystal structure.

More information

Chapter 9: Dislocations & Strengthening Mechanisms. Why are the number of dislocations present greatest in metals?

Chapter 9: Dislocations & Strengthening Mechanisms. Why are the number of dislocations present greatest in metals? Chapter 9: Dislocations & Strengthening Mechanisms ISSUES TO ADDRESS... Why are the number of dislocations present greatest in metals? How are strength and dislocation motion related? Why does heating

More information

11/2/2018 7:57 PM. Chapter 5. Diffusion. Mohammad Suliman Abuhaiba, Ph.D., PE

11/2/2018 7:57 PM. Chapter 5. Diffusion. Mohammad Suliman Abuhaiba, Ph.D., PE Chapter 5 Diffusion 1 2 Bonus Outsource a software for heat treatment Install the software Train yourself in using the software Apply case studies on the software Present your work in front of your colleagues

More information

Preparation of Materials Lecture 6

Preparation of Materials Lecture 6 PY3090 Preparation of Materials Lecture 6 Colm Stephens School of Physics PY3090 6 iffusion iffusion Mass transport by atomic motion Mechanisms Gases & Liquids random (Brownian) motion Solids vacancy diffusion