Laser Processing on Graphite

Size: px
Start display at page:

Download "Laser Processing on Graphite"

Transcription

1 Laser Processing on Graphite MSE 503 Seminar - Fall CLA Conference Room, UT Space Institute, Tullahoma, TN , USA Deepak Rajput Graduate Research Assistant Center for Laser Applications University of Tennessee Space Institute Tullahoma, Tennessee drajput@utsi.edu Web: 1of xx

2 Outline Introduction to Graphite Problems and Possible Solutions Laser Processing Results & Discussion Summary 2 Future work 2of xx

3 Carbon: Introduction Carbon (Atomic number: 6 / 1s 2 2s 2 2p 2 ) Graphite (sp 2 ) Diamond (sp 3 ) Fullerenes (molecular form / cage-like structure) 3 3of xx

4 Allotropes of Carbon Eight allotropes a) Diamond b) Graphite c) Lonsdaleite d) C 60 e) C 540 f) C 70 g) Amorphous Carbon h) Carbon Nanotube 4 Image source: 4of xx

5 Graphite: Introduction Low specific gravity High resistance to thermal shock High thermal conductivity Low modulus of elasticity High strength (doubles at 2500 o C*) High temperature structural material 5 *Malmstrom C., et al (1951) Journal of Applied Physics 22(5) of xx

6 Graphite: Introduction Low resistance to oxidation at high temperatures Erosion by particle and gas streams Solution: Well-adhered surface protective coatings!! Adherence: (1) the ability of the coating elements to wet the surface of the carbon material (wettability). (2) the difference in the values of coefficient of thermal expansion of the coating and that of the carbon material. 6 6of xx

7 Graphite: Surface Protection 1) Wettability The ability of a material to wet the surface of carbon depends on the contact angle between the melt and the carbon material. It can be determined from the Young-Dupre equation: W a = σ ( 1+ cosθ ) W a = work of adhesion σ= surface tension of the melt θ= contact angle The smaller the contact angle, the better the wettability of the metal. 7 Image source: David Quéré (2002) Nature Materials 1, of xx

8 Graphite: Surface Protection 8 2) Thermal Expansion a) When the melt solidifies on the carbon substrate, significant internal stresses develop at the coatingsubstrate interface. b) If the interfacial stress are large enough, the interface fails and the coating delaminates. c) The reason for this failure is the weak cohesive strength of the coating surface. d) The cohesive strength of the coating depends on the difference in the values of coefficient of thermal expansion of the coating and that of the substrate. The larger the difference, the weaker the cohesive strength of the coating. 8of xx

9 Graphite: Surface Protection The ideal coating material for a carbon material: One that can wet the carbon material and Whose coefficient of thermal expansion is close to that of the carbon substrate. The coefficient of thermal expansion of a carbon material depends on the its method of preparation. Transition metals wet the carbon materials efficiently. UTSI: Semiconductor grade graphite (7.9 x 10-6 m/m o C) 9 9of xx

10 Graphite: Surface Protection Transition metals have partly-filled d orbitals. They can combine strongly with carbon. They form strong covalent bonds with carbon. Transition metals and their carbides, nitrides, oxides, and borides have been deposited on carbon materials. Non-transition metal coatings like silicon carbide, silicon oxy-carbide, boron nitride, lanthanum hexaboride, glazing coatings, and alumina have also been deposited. Methods used: chemical vapor deposition, physical vapor deposition, photochemical vapor deposition, thermal spraying, PIRAC, and metal infiltration of xx

11 Graphite: Laser Processing CLA (UTSI): the first to demonstrate laser deposition on graphite. Early attempts were to make bulk coatings to avoid dilution in the coating due to melting of the substrate. Graphite does not melt, but sublimates at room pressure. Laser fusion coatings on carbon-carbon composites. Problems with cracking. CLA process: LISI TM!! LISI TM is a registered trademark of the University of Tennessee Research Corporation. 11 LISI: Laser Induced Surface Improvement 11 of xx

12 LISI TM on Graphite 12 Prepare a precursor mixture by mixing metal particles and a binder. Spray the precursor mixture with an air spray gun on polished graphite substrates (6 mm thick). Dry for a couple of hours under a heat lamp before laser processing. Carbide forming ability among transition metals: Fe<Mn<Cr<Mo<W<V<Nb<Ta<Ti<Zr<Hf Titanium (<44 μm), zirconium (2-5 μm), niobium (<10 μm), titanium-40 wt% aluminum (-325 mesh), tantalum, W-TiC, chromium, vanadium, silicon, iron, etc. Precursor thickness: Ti (75 μm), Zr (150 μm), Nb (125 μm). Contains binder and moisture in pores. 12 of xx

13 LISI TM on Graphite 13 Two-step Processing Chamber 1,2,12,13 Overhead laser assembly; 4 Argon; 16,17 mechanical & turbo pumps 7 sample, 8 alumina rods, 9 induction heating element, 18 RF supply. 13 of xx

14 LISI TM on Graphite 14 of xx C L A 14

15 LISI TM on Graphite T = 800 o C Graphite track 15 Copper induction heating element Process variables: laser power (W), scanning speed (mm/s) focal spot size (mm), laser pass overlap (%), 15 of xx

16 LISI TM on Graphite Focal spot size (Intensity): Focal plane (Max intensity) I = P/spot area 16 Laser beam: near-gaussian, 1075±5 nm Image source: Rajput D., et al (2009) Surface & Coatings Technology, 203, of xx

17 LISI TM on Graphite D X Laser pass overlap (%) X % = x100 D 17 Overlap important to get complete melting because the beam is near-gaussian 17 of xx

18 LISI TM on Graphite: Results Scanning electron microscopy X-ray diffraction of the coating surface X-ray diffraction of the coating-graphite interface Microhardness of the coating Secondary ion mass spectrometery of the niobium coating 18 SEM was done at the VINSE, Vanderbilt University (field emission SEM) X-ray diffraction was done on a Philips X pert system with Cu Kαat Å Microhardness was done on a LECO LM 300AT under a load of 25 gf for 15 seconds (HK) SIMS was done on a Millbrook MiniSIMS: 6 kev Ga + ions 18 of xx

19 Results: Titanium XRD of the titanium coating surface (A) and its interface with the graphite substrate (B) Oxygen: LISI TM binder or traces in the chamber 19 SEM micrographs of the titanium coating HK 19 of xx

20 Results: Zirconium XRD of the zirconium coating surface (A) and its interface with the graphite substrate (B) SEM micrographs of the zirconium coating 20 Delamination and crack appear in some locations ~ 775 HK 20 of xx

21 Results: Niobium XRD of the niobium coating surface (A) and its interface with the graphite substrate (B) 21 SEM micrographs of the niobium coating HK 21 of xx

22 Proposed Mechanism Self-propagating high temperature synthesis (SHS) aided by laser heating. It is also called as combustion synthesis. Once ignited by the laser heating, the highly exothermic reaction advances as a reaction front that propagates through the powder mixture. This mechanism strongly depends on the starting particle size. In the present study, the average particle size is <25 μm. The coefficient of thermal expansion of titanium carbide is close to that of the graphite substrate than those of zirconium carbide and niobium carbide. Hence, titanium coating did not delaminate of xx

23 SIMS of the Niobium Coating 23 Chemical Image of as received Nb coating A: Potassium, B: Magnesium C: Oxygen, D: Carbon Mass Spectrum A: as received B: slightly ground 23 of xx

24 LISI TM on Graphite Mandrels Laser Powder Deposition Laser Powder Deposition of W-TiC Cermelt Rocket Nozzles on Graphite Mandrels ICALEO 2008 Temecula, CA of xx

25 LISI TM on Graphite Mandrels 0.6 mm pre-placed layer: 1500 W, 0.2 mm/s linear, 0.2 rotation/s 100 um 10 um of xx

26 Summary 26 Successfully deposited fully dense and crack-free transition metal coatings on graphite substrates. All the coating interfaces contain carbide phases. Laser assisted self-propagating high temperature synthesis (SHS) has been proposed to be the possible reason for the formation of all the coatings. SIMS analysis proved that LISI TM binder forms a thin slag layer at the top of the coating surface post laser processing. 26 of xx

27 Future Work Heat treatment Advanced characterization (oxidation analysis) Calculation of various thermodynamic quantities Publish the results in a good journal of xx

28 Questions?? (or may be suggestions) 28 of xx 28

29 Thanks!!! photos published without permission 29 of xx

Novel Refractory Cermelt Coatings on Graphite

Novel Refractory Cermelt Coatings on Graphite Novel Refractory Cermelt Coatings on Graphite Deepak Rajput, Lino Costa, Kate Lansford, William Hofmeister Center for Laser Applications University of Tennessee Space Institute 411 BH Goethert Parkway

More information

Synthesis of diamond-like carbon films with super-low friction and wear properties

Synthesis of diamond-like carbon films with super-low friction and wear properties Synthesis of diamond-like carbon films with super-low friction and wear properties MSE 676 All Things Carbon / 09-29-2009 A. Erdemir, O.L. Eryilmaz, and G. Fenske J. Vac. Sci. Technol. A 18(4), Jul/Aug

More information

Joining of C f /SiC composites with Niobium alloy

Joining of C f /SiC composites with Niobium alloy Joining of C f /SiC composites with Niobium alloy Y. Du, C. Liang, X. Zheng College of Aerospace & Materials Engineering National University of Defense Technology Changsha, 410073, P.R. China Email:yongguod@hotmail.com

More information

COOPERATIVE PATENT CLASSIFICATION

COOPERATIVE PATENT CLASSIFICATION CPC C COOPERATIVE PATENT CLASSIFICATION CHEMISTRY; METALLURGY (S omitted) METALLURGY C22 METALLURGY (of iron C21); FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS (production of

More information

LASER SURFACE ALLOYING (LSA) OF ALUMINIUM (AA 1200) WITH TiB 2 FOR HARDNESS IMPROVEMENT Paper (802)

LASER SURFACE ALLOYING (LSA) OF ALUMINIUM (AA 1200) WITH TiB 2 FOR HARDNESS IMPROVEMENT Paper (802) LASER SURFACE ALLOYING (LSA) OF ALUMINIUM (AA 200) WITH TiB 2 FOR HARDNESS IMPROVEMENT Paper (802) Abimbola Patricia Popoola *, Sisa Pityana,2 Department of Chemical and Metallurgical Engineering, Tshwane

More information

needed for the SOFC electrolyte membrane application. Few directed vapor deposition

needed for the SOFC electrolyte membrane application. Few directed vapor deposition Chapter 3 Experimental Procedure 3.1 Overview Prior to this study, DVD has not been used to create the type of dense metal oxide layers needed for the SOFC electrolyte membrane application. Few directed

More information

SIZE EFFECTS OF SIC PARTICLES ON MECHNICAL PROPERTIES OF CAST CARBON NANOFIBERS REINFORCED AZ91 MAGNESIUM COMPOSITES

SIZE EFFECTS OF SIC PARTICLES ON MECHNICAL PROPERTIES OF CAST CARBON NANOFIBERS REINFORCED AZ91 MAGNESIUM COMPOSITES THE 19 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS SIZE EFFECTS OF SIC PARTICLES ON MECHNICAL PROPERTIES OF CAST CARBON NANOFIBERS REINFORCED AZ91 MAGNESIUM COMPOSITES S.-K. Lee 1, S.-B. Lee 1*,

More information

Thermal Durability and Abradability of Plasma Sprayed Al-Si-Polyimide Seal Coatings p. 85

Thermal Durability and Abradability of Plasma Sprayed Al-Si-Polyimide Seal Coatings p. 85 Trends in Automotive Applications of Thermal Spray Technology in Japan p. 1 Production Plasma in the Automotive Industry: A European Viewpoint p. 7 The Effect of Microstructure on the Wear Behavior of

More information

Laser assisted Cold Spray

Laser assisted Cold Spray 2009-02-16 Laser assisted Cold Spray Andrew Cockburn, Matthew Bray, Rocco Lupoi Bill O Neill Innovative Manufacturing Research Centre (IMRC) Institute for Manufacturing, Department of Engineering, University

More information

DRY SLIDING WEAR PERFORMANCE OF THERMAL SPRAYED MICRO- NANO BORON CARBIDE COATING ON 410 GRADE STEEL

DRY SLIDING WEAR PERFORMANCE OF THERMAL SPRAYED MICRO- NANO BORON CARBIDE COATING ON 410 GRADE STEEL DRY SLIDING WEAR PERFORMANCE OF THERMAL SPRAYED MICRO- NANO BORON CARBIDE COATING ON 410 GRADE STEEL K. V. Sreenivas Rao, Girisha K. G. and Anil K. C. Akash R&D Center, Department of Mechanical Engineering,

More information

Water Erosion Experiment Update. T.Davenne O.Caretta S.Bennetton 5 th Dec 2013

Water Erosion Experiment Update. T.Davenne O.Caretta S.Bennetton 5 th Dec 2013 Water Erosion Experiment Update T.Davenne O.Caretta S.Bennetton 5 th Dec 2013 Motivation ISIS water cooled tungsten targets are clad with tantalum to avoid tungsten corrosion problems that occur when in

More information

ENCHANCEMENT OF MECHANICAL PROPERTIES OF CAST NANO CABONS REINFORCED A356 ALUMINIUM MATRIX COMPOSITES

ENCHANCEMENT OF MECHANICAL PROPERTIES OF CAST NANO CABONS REINFORCED A356 ALUMINIUM MATRIX COMPOSITES THE 19 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS ENCHANCEMENT OF MECHANICAL PROPERTIES OF CAST NANO CABONS REINFORCED A356 ALUMINIUM MATRIX COMPOSITES S.-B. Lee 1*, J.-W. Yi 1, B.M. Jung 1, and

More information

Multiphase Flow and Heat Transfer

Multiphase Flow and Heat Transfer Multiphase Flow and Heat Transfer Wettability Sudheer Siddapuredddy sudheer@iitp.ac.in Department of Mechanical Engineering Indian Institution of Technology Patna Multiphase Flow and Heat Transfer Wettability

More information

Laser Shock Peening of Bulk Metallic Glasses

Laser Shock Peening of Bulk Metallic Glasses Final Report Laser Shock Peening of Bulk Metallic Glasses MSE 516: Mechanical Metallurgy Spring 2008 Submitted on April 24 th, 2008 Deepak Rajput Graduate Research Assistant Center for Laser Applications

More information

Interfacial Debonding of Boron Nitride Nanoparticle Reinforced 6061 Aluminum Alloy Matrix Composites

Interfacial Debonding of Boron Nitride Nanoparticle Reinforced 6061 Aluminum Alloy Matrix Composites 2nd National Conference on Materials and Manufacturing Processes Hyderabad, Andhra Pradesh, India Interfacial Debonding of Boron Nitride Nanoparticle Reinforced 6061 Aluminum Alloy Matrix Composites 1

More information

Deposition of Diamond-like Carbon Films and Metal-DLC thin films on PCBN Substrates by RF Magnetron Sputtering Method

Deposition of Diamond-like Carbon Films and Metal-DLC thin films on PCBN Substrates by RF Magnetron Sputtering Method Deposition of Diamond-like Carbon Films and Metal-DLC thin films on PCBN Substrates by RF Magnetron Sputtering Method Authors & affiliations: Chii-Ruey Lin a,*, Chun-Hsi Su a, Chien-Kuo Chang b, Da-Hua

More information

INTRO TO THERMAL SPRAY

INTRO TO THERMAL SPRAY INTRO TO THERMAL SPRAY Thermal Spray is a process were a material heated and propelled in a gas stream on to a substrate forming splats. The splats build up to create a coating. What is Thermal Spray?

More information

Surface Characterization of Laser Polished Indirect-SLS Parts

Surface Characterization of Laser Polished Indirect-SLS Parts Surface Characterization of Laser Polished Indirect-SLS Parts Jorge A. Ramos, David L. Bourell, Joseph J. Beaman Laboratory for Freeform Fabrication The University of Texas at Austin, Austin, Texas 78712

More information

PRODUCING MULTILAYER COATINGS BY MECHANICAL ALLOYING METHOD

PRODUCING MULTILAYER COATINGS BY MECHANICAL ALLOYING METHOD PRODUCING MULTILAYER COATINGS BY MECHANICAL ALLOYING METHOD Мazhyn SKAKOV 1, Zhuldyz SAGDOLDINA 2, Marat BITENBAEV 3 1 National Nuclear Center of the Republic of Kazakhstan, Kurchatov, Kazakhstan, skakov@nnc.kz

More information

Strength of Carbon Fiber Reinforced Cu-25 at%al Alloy Junction Device*

Strength of Carbon Fiber Reinforced Cu-25 at%al Alloy Junction Device* Materials Transactions, Vol. 47, No. 7 (2006) pp. 1821 to 1825 #2006 The Japan Institute of Metals Strength of Carbon Fiber Reinforced Cu-25 at%al Alloy Junction Device* Yoshitake Nishi and Kazunori Tanaka

More information

Influence of Spraying Conditions on Properties of Zr-Based Metallic Glass Coating by Gas Tunnel Type Plasma Spraying

Influence of Spraying Conditions on Properties of Zr-Based Metallic Glass Coating by Gas Tunnel Type Plasma Spraying Influence of Spraying Conditions on Properties of Zr-Based Metallic Glass by Gas Tunnel Type Plasma Spraying KOBAYASHI Akira *, KURODA Toshio *, KIMURA Hisamichi ** and INOUE Akihisa ** Abstract Metallic

More information

Composite Materials. Metal matrix composites

Composite Materials. Metal matrix composites Composite Materials Metal matrix composites Introduction The properties that make MMCs attractive are high strength and stiffness, good wear resistance, high service temperature, tailorable coefficient

More information

Deposition and characterization of sputtered ZnO films

Deposition and characterization of sputtered ZnO films Superlattices and Microstructures 42 (2007) 89 93 www.elsevier.com/locate/superlattices Deposition and characterization of sputtered ZnO films W.L. Dang, Y.Q. Fu, J.K. Luo, A.J. Flewitt, W.I. Milne Electrical

More information

Previous Lecture. Vacuum & Plasma systems for. Dry etching

Previous Lecture. Vacuum & Plasma systems for. Dry etching Previous Lecture Vacuum & Plasma systems for Dry etching Lecture 9: Evaporation & sputtering Objectives From this evaporation lecture you will learn: Evaporator system layout & parts Vapor pressure Crucible

More information

MA-SHS of ZrC and ZrB2 in Air from The Zr/B/C Powder. the original is available online at Instructions for use

MA-SHS of ZrC and ZrB2 in Air from The Zr/B/C Powder. the original is available online at  Instructions for use Title MA-SHS of ZrC and ZrB2 in Air from The Zr/B/C Powder Author(s)Tsuchida, Takeshi; Yamamoto, Satoshi CitationEURO CERAMICS VIII, PTS 1-3: 85-88 Issue Date 2004 Doc URL http://hdl.handle.net/2115/15876

More information

Alternative Methods of Yttria Deposition For Semiconductor Applications. Rajan Bamola Paul Robinson

Alternative Methods of Yttria Deposition For Semiconductor Applications. Rajan Bamola Paul Robinson Alternative Methods of Yttria Deposition For Semiconductor Applications Rajan Bamola Paul Robinson Origin of Productivity Losses in Etch Process Aggressive corrosive/erosive plasma used for etch Corrosion/erosion

More information

Joint Technology Initiatives Collaborative Project (FCH) FCH-JU WP4 - Development of lab-scale cell components

Joint Technology Initiatives Collaborative Project (FCH) FCH-JU WP4 - Development of lab-scale cell components Joint Technology Initiatives Collaborative Project (FCH) FCH-JU-2010-1 WP4 - Development of lab-scale cell components DELIVERABLE 4.3- Prepared by: HOGANAS Document control data Document ref. : METPROCELL-WP4-

More information

Application of Fly-ash Composite in Plasma Surface Engineering

Application of Fly-ash Composite in Plasma Surface Engineering Indian Institute of Technology Kharagpur From the SelectedWorks of Ajit Behera Winter December 14, 2012 Application of Flyash Composite in Plasma Surface Engineering Ajit Behera, Indian Institute of Technology

More information

Analysis of Bending Stresses On Coating Materials by Experimental and FE Method

Analysis of Bending Stresses On Coating Materials by Experimental and FE Method Analysis of Bending Stresses On Coating Materials by Experimental and FE Method Umesh G 1, Biradar Mallikarjun 2, Dr. C.S.Ramesh 3 1 Student, IV th Semester M.Tech.(Machine Design), 2 Associate Professor,

More information

CHAPTER 4. SYNTHESIS OF ALUMINIUM SELENIDE (Al 2 Se 3 ) NANO PARTICLES, DEPOSITION AND CHARACTERIZATION

CHAPTER 4. SYNTHESIS OF ALUMINIUM SELENIDE (Al 2 Se 3 ) NANO PARTICLES, DEPOSITION AND CHARACTERIZATION 40 CHAPTER 4 SYNTHESIS OF ALUMINIUM SELENIDE (Al 2 Se 3 ) NANO PARTICLES, DEPOSITION AND CHARACTERIZATION 4.1 INTRODUCTION Aluminium selenide is the chemical compound Al 2 Se 3 and has been used as a precursor

More information

Characterization and erosion of metal-containing carbon layers

Characterization and erosion of metal-containing carbon layers Characterization and erosion of metal-containing carbon layers Martin Balden Max-Planck-Institut für Plasmaphysik, EURATOM Association, D-85748 Garching, Germany Materials Research Division (MF) Outline

More information

Ceramic Processing Research

Ceramic Processing Research Journal of Ceramic Processing Research. Vol. 11, No. 1, pp. 1~5 () J O U R N A L O F Ceramic Processing Research Preparation of Si infiltrated SiB 6 TiB 2 composites GeumChan Hwang* and Junichi Matsushita

More information

Manufacturing Processes 1 (MDP 114)

Manufacturing Processes 1 (MDP 114) Manufacturing Processes 1 (MDP 114) First Year, Mechanical Engineering Dept., Faculty of Engineering, Fayoum University Dr. Ahmed Salah Abou Taleb 1 Cutting-Tool Materials and Cutting Fluids 2 Fracture

More information

Enhancement Surface Mechanical Properties of 2024 Al-Alloys Using Pulsed Nd:YAG Laser Cladding

Enhancement Surface Mechanical Properties of 2024 Al-Alloys Using Pulsed Nd:YAG Laser Cladding Enhancement Surface Mechanical Properties of 2024 Al-Alloys Using Pulsed Nd:YAG Laser Cladding 1 1 2 Raid M.HadiP P, Mahmoad Sh. MahmoadP P and Ali H.AbdalhadiP Institute of laser for postgraduate studies,

More information

Novel Cold Spray Nanostructured Aluminum. Aberdeen Proving Ground Maryland USA 2 University of Central Florida

Novel Cold Spray Nanostructured Aluminum. Aberdeen Proving Ground Maryland USA 2 University of Central Florida Novel Cold Spray Nanostructured Aluminum Victor K. Champagne 1, Matthew Trexler 1, Yongho Sohn 2, and George E. Kim 3 1 US Army Research Laboratory Aberdeen Proving Ground Maryland 21005-5069 USA 2 University

More information

Development of a Co-Cr-Mo to Tantalum Transition using LENS for Orthopedic Applications

Development of a Co-Cr-Mo to Tantalum Transition using LENS for Orthopedic Applications Development of a Co-Cr-Mo to Tantalum Transition using LENS for Orthopedic Applications Abstract Saripella Surya Kumar, IIT Bombay Brent Stucker, Utah State University Biomedical implant material research

More information

Structure Control of Plasma Sprayed Zircon Coating by Substrate Preheating and Post Heat Treatment

Structure Control of Plasma Sprayed Zircon Coating by Substrate Preheating and Post Heat Treatment Materials Transactions, Vol. 46, No. 3 (25) pp. 669 to 674 #25 Japan Thermal Spraying Society Structure Control of Plasma Sprayed Zircon Coating by Substrate Preheating and Post Heat Treatment Masato Suzuki,

More information

X-ray residual stress measurements on plasma sprayed molybdenum coatings

X-ray residual stress measurements on plasma sprayed molybdenum coatings High Performance Structures and Materials III 351 X-ray residual stress measurements on plasma sprayed molybdenum coatings K. Hirukawa 1, K. Akita 2, S. Tobe 3, T. A. Stolarski 4 & S. Ohya 2 1 Research

More information

Application of SHS process for fabrication of copper-titanium silicon carbide composite (Cu-Ti 3

Application of SHS process for fabrication of copper-titanium silicon carbide composite (Cu-Ti 3 Journal of Physics: Conference Series PAPER OPEN ACCESS Application of SHS process for fabrication of copper-titanium silicon carbide composite (Cu-Ti 3 SiC 2 ) To cite this article: A P Amosov et al 2018

More information

Interphase Cracking in Titanium Nitride/2024 Alloy Particle- Reinforced Metal-Matrix Composites

Interphase Cracking in Titanium Nitride/2024 Alloy Particle- Reinforced Metal-Matrix Composites 3rd National Conference on Materials and Manufacturing Processes Hyderabad, Andhra Pradesh, India Interphase Cracking in Titanium Nitride/2024 Alloy Particle- Reinforced Metal-Matrix Composites 1 B. Kotiveera

More information

A Preliminary Report on Phygen s Chromium Nitride Coatings. John B. Woodford, Ph.D. and. Mohumad al-zoubi, Ph.D. Argonne National Laboratory

A Preliminary Report on Phygen s Chromium Nitride Coatings. John B. Woodford, Ph.D. and. Mohumad al-zoubi, Ph.D. Argonne National Laboratory A Preliminary Report on Phygen s Chromium Nitride Coatings by John B. Woodford, Ph.D and Mohumad al-zoubi, Ph.D Argonne National Laboratory Introduction To protect a vulnerable surface from wear or chemical

More information

Silver Diffusion Bonding and Layer Transfer of Lithium Niobate to Silicon

Silver Diffusion Bonding and Layer Transfer of Lithium Niobate to Silicon Chapter 5 Silver Diffusion Bonding and Layer Transfer of Lithium Niobate to Silicon 5.1 Introduction In this chapter, we discuss a method of metallic bonding between two deposited silver layers. A diffusion

More information

THE INFLUENCE OF NITROGEN CONTENT ON THE MECHANICAL PROPERTIES OF TiN x THIN FILMS PREPARED BY REACTIVE MAGNETRON SPUTTERING

THE INFLUENCE OF NITROGEN CONTENT ON THE MECHANICAL PROPERTIES OF TiN x THIN FILMS PREPARED BY REACTIVE MAGNETRON SPUTTERING Bulletin of the Transilvania University of Braşov Series I: Engineering Sciences Vol. 5 (54) No. 2-2012 THE INFLUENCE OF NITROGEN CONTENT ON THE MECHANICAL PROPERTIES OF TiN x THIN FILMS PREPARED BY REACTIVE

More information

2 9 & 3 0 J U N E, P A R I S - F R A N C E

2 9 & 3 0 J U N E, P A R I S - F R A N C E 2 9 & 3 0 J U N E, 2 0 1 4 P A R I S - F R A N C E HIGH-TECH MATERIALS FOR TOMORROW'S LARGE SCALE INDUSTRIAL DEVELOPMENTS: ENERGY GENERATION AND TRANSPORT, ADVANCED STRUCTURAL DESIGNS, AND DATA PROCESSING

More information

PROPERTIES OF AL-BASED ALLOYS PREPARED BY CENTRIFUGAL ATOMISATION AND HOT EXTRUSION. Filip PRŮŠA, Dalibor VOJTĚCH

PROPERTIES OF AL-BASED ALLOYS PREPARED BY CENTRIFUGAL ATOMISATION AND HOT EXTRUSION. Filip PRŮŠA, Dalibor VOJTĚCH PROPERTIES OF AL-BASED ALLOYS PREPARED BY CENTRIFUGAL ATOMISATION AND HOT EXTRUSION Filip PRŮŠA, Dalibor VOJTĚCH Institute of Chemical Technology Prague, Department of Metals and Corrosion Engineering,

More information

THE STRUCTURE AND MECHANICAL PROPERTIES OF NiCrBSi COATINGS PREPARED BY LASER BEAM CLADDING

THE STRUCTURE AND MECHANICAL PROPERTIES OF NiCrBSi COATINGS PREPARED BY LASER BEAM CLADDING Materials Engineering, Vol. 17, 2010, No. 1 11 THE STRUCTURE AND MECHANICAL PROPERTIES OF NiCrBSi COATINGS PREPARED BY LASER BEAM CLADDING Zita Iždinská 1, Ahmed Nasher 1, Karol Iždinský 2 Received 29

More information

Thermal Evaporation. Theory

Thermal Evaporation. Theory Thermal Evaporation Theory 1. Introduction Procedures for depositing films are a very important set of processes since all of the layers above the surface of the wafer must be deposited. We can classify

More information

INVESTIGATION OF HVOF THERMAL SPRAYED MICRO B4C, MICRO- 1%, 2%, 3% NANO B4C COATINGS ON DRY SLIDING WEAR PERFORMANCE OF 410 GRADE STEEL

INVESTIGATION OF HVOF THERMAL SPRAYED MICRO B4C, MICRO- 1%, 2%, 3% NANO B4C COATINGS ON DRY SLIDING WEAR PERFORMANCE OF 410 GRADE STEEL INVESTIGATION OF HVOF THERMAL SPRAYED MICRO B4C, MICRO- 1%, 2%, 3% NANO B4C COATINGS ON DRY SLIDING WEAR PERFORMANCE OF 410 GRADE STEEL Girisha K. G. 1, Anil K. C. 2, Akash 1 and K. V. Sreenivas Rao 1

More information

20th IAEA Fusion Energy Conference 1-6 November 2004 Vilamoura, Portugal. Recent Results in Plasma Facing Materials Studied at SWIP

20th IAEA Fusion Energy Conference 1-6 November 2004 Vilamoura, Portugal. Recent Results in Plasma Facing Materials Studied at SWIP INTERNATIONAL ATOMIC ENERGY AGENCY 20th IAEA Fusion Energy Conference 1-6 November 2004 Vilamoura, Portugal IAEA-CN-116 Recent Results in Plasma Facing Materials Studied at SWIP Zengyu XU 1, Xiang LIU

More information

Lecture 12. Physical Vapor Deposition: Evaporation and Sputtering Reading: Chapter 12. ECE Dr. Alan Doolittle

Lecture 12. Physical Vapor Deposition: Evaporation and Sputtering Reading: Chapter 12. ECE Dr. Alan Doolittle Lecture 12 Physical Vapor Deposition: Evaporation and Sputtering Reading: Chapter 12 Evaporation and Sputtering (Metalization) Evaporation For all devices, there is a need to go from semiconductor to metal.

More information

Polymer Interface and Adhesion

Polymer Interface and Adhesion Polymer Interface and Adhesion SOUHENG WU E. I. du Pont de Nemours &.Company Wilmington, Delaware MARCEL DEKKER, INC. New York and Basel Preface Acknowledgments 1. INTERFACIAL THERMODYNAMICS 1 1.1 Formulation

More information

PROCESS ANALYSES FOR DEVELOPING COST- EFFECTIVE PARTICULATE REINFORCED INORGANIC COMPOSITES

PROCESS ANALYSES FOR DEVELOPING COST- EFFECTIVE PARTICULATE REINFORCED INORGANIC COMPOSITES 52 Memoirs of the School of T. Engineering, Choh Nagoya University Vol.51, No.1 (1999) PROCESS ANALYSES FOR DEVELOPING COST- EFFECTIVE PARTICULATE REINFORCED INORGANIC COMPOSITES Takao CHOH Department

More information

To explore the ability of the DVD technology to create dense, pinhole-free metal oxide

To explore the ability of the DVD technology to create dense, pinhole-free metal oxide Chapter 4 Results 4.1 Strategy To explore the ability of the DVD technology to create dense, pinhole-free metal oxide layers and to develop an initial understanding of the relationship between various

More information

Comparison of Carbon Coatings Deposited by Different Techniques

Comparison of Carbon Coatings Deposited by Different Techniques Comparison of Carbon Coatings Deposited by Different Techniques V. Gorokhovsky, K.Coulter, M.Miller, R.Wei, C. Ellis, C.Engel Southwest Research Institute San Antonio, Texas Funded by SwRI: Project No.

More information

Study of the phase composition of silicide coatings, based on layered Nb-Mo structures, obtained by vacuum-arc deposition

Study of the phase composition of silicide coatings, based on layered Nb-Mo structures, obtained by vacuum-arc deposition Journal of Physics: Conference Series PPER OPEN CCESS Study of the phase composition of silicide coatings, based on layered Nb-Mo structures, obtained by vacuum-arc deposition To cite this article: Lozovan

More information

Available online at Fatigue Fatigue in AISI 4340 steel thermal spray coating by HVOF for aeronautic application

Available online at  Fatigue Fatigue in AISI 4340 steel thermal spray coating by HVOF for aeronautic application Available online at www.sciencedirect.com Procedia Procedia Engineering Engineering 2 (2010) 00 (2009) 1617 1623 000 000 Procedia Engineering www.elsevier.com/locate/procedia Fatigue 2010 Fatigue in AISI

More information

Growth and Doping of SiC-Thin Films on Low-Stress, Amorphous Si 3 N 4 /Si Substrates for Robust Microelectromechanical Systems Applications

Growth and Doping of SiC-Thin Films on Low-Stress, Amorphous Si 3 N 4 /Si Substrates for Robust Microelectromechanical Systems Applications Journal of ELECTRONIC MATERIALS, Vol. 31, No. 5, 2002 Special Issue Paper Growth and Doping of SiC-Thin Films on Low-Stress, Amorphous Si 3 N 4 /Si Substrates for Robust Microelectromechanical Systems

More information

Ti Titanium. Leading the Way in the Production of Plasma Atomized Spherical Metal Powders. Specialists in Powders for Additive Manufacturing

Ti Titanium. Leading the Way in the Production of Plasma Atomized Spherical Metal Powders. Specialists in Powders for Additive Manufacturing Leading the Way in the Production of Plasma Atomized Spherical Metal Powders Specialists in Powders for Additive Manufacturing 22 Ti 47.867 Titanium 10+ years servicing major customers AP&C: Large Scale

More information

Preparation and properties of PTFE anti-friction coating

Preparation and properties of PTFE anti-friction coating Preparation and properties of PTFE anti-friction coating Polytetrafluoroethylene (PTFE) is considered the best solid lubricant, its friction coefficient is only 0.05 within 320 temperature, even smaller

More information

Formation of Fe-base Metal Glass Coating by Gas Tunnel Type Plasma Spraying

Formation of Fe-base Metal Glass Coating by Gas Tunnel Type Plasma Spraying Formation of Fe-base Metal Glass Coating by Gas Tunnel Type Plasma Spraying KOBAYASHI Akira*, YANO Shoji**, KIMURA Hisamichi***, and INOUE Akihisa*** Abstract Metal glass has excellent functions such as

More information

Material Evaporation Application Comment MP P / Optical films, Oxide films, Electrical contacts. Doping, Electrical contacts.

Material Evaporation Application Comment MP P / Optical films, Oxide films, Electrical contacts. Doping, Electrical contacts. for vapour Aluminum (Al) -, Optical, Oxide, Electrical BN liners with lid are recommended due to the reactivity and the fact that Al creeps out. Cooling down of the cell with 1K per minute. 660 972 Antimony

More information

Effect of Heat Treatment on Interfacial Strengthening Mechanisms of Second Phase Particulate Reinforced Aluminium Alloy

Effect of Heat Treatment on Interfacial Strengthening Mechanisms of Second Phase Particulate Reinforced Aluminium Alloy 24-26.5.2005, Hradec nad Moravici Effect of Heat Treatment on Interfacial Strengthening Mechanisms of Second Phase Particulate Reinforced Aluminium Alloy S.T. Hasan Faculty of Arts, Computing, Engineering

More information

Thermal Spray Coatings in Severe Service Elaine Motyka 3/2/2017

Thermal Spray Coatings in Severe Service Elaine Motyka 3/2/2017 Thermal Spray Coatings in Severe Service Elaine Motyka 3/2/2017 In this session Basics of Thermal Spray Coatings Defining Thermal Spray Common processes Coating microstructures Properties affected by process

More information

COMPATIBILITY OF THE ALTERNATIVE SEED LAYER (ASL) PROCESS WITH MONO- Si AND POLY-Si SUBSTRATES PATTERNED BY LASER OR WET ETCHING

COMPATIBILITY OF THE ALTERNATIVE SEED LAYER (ASL) PROCESS WITH MONO- Si AND POLY-Si SUBSTRATES PATTERNED BY LASER OR WET ETCHING COMPATIBILITY OF THE ALTERNATIVE SEED LAYER (ASL) PROCESS WITH MONO- Si AND POLY-Si SUBSTRATES PATTERNED BY LASER OR WET ETCHING Lynne Michaelson 1, Anh Viet Nguyen 2, Krystal Munoz 1, Jonathan C. Wang

More information

STUDY ON HYDROXYAPATITE COATING ON BIOMATERIALS BY PLASMA SPRAY METHOD

STUDY ON HYDROXYAPATITE COATING ON BIOMATERIALS BY PLASMA SPRAY METHOD STUDY ON HYDROXYAPATITE COATING ON BIOMATERIALS BY PLASMA SPRAY METHOD Dr. Hanumantharaju H. G 1, Dr. H. K. Shivanand 2, Prashanth K. P 3, K. Suresh Kumar 4, S. P. Jagadish 5 1,2 UVCE, Department of Mechanical

More information

Cu/synthetic and impact-diamond composite heatconducting

Cu/synthetic and impact-diamond composite heatconducting Journal of Physics: Conference Series PAPER OPEN ACCESS Cu/synthetic and impact-diamond composite heatconducting substrates To cite this article: E N Galashov et al 2016 J. Phys.: Conf. Ser. 690 012043

More information

Surface & Coatings Technology

Surface & Coatings Technology Surface & Coatings Technology 291 (2016) 222 229 Contents lists available at ScienceDirect Surface & Coatings Technology journal homepage: www.elsevier.com/locate/surfcoat The effect of TiC/Al 2 O 3 composite

More information

Study of Nozzle Clogging During Cold Spray

Study of Nozzle Clogging During Cold Spray Study of Nozzle Clogging During Cold Spray Presenter: Matt Siopis UTRC Team Members: A. Nardi, A. Espinal, L. Binek, T. Landry Portions of this Research were sponsored by the Army Research Laboratories

More information

Potential of High Velocity Oxy Fuel Thermal Spraying in Turbine Shaft Repairing. Production Technology Research Institute, branch of ACECR

Potential of High Velocity Oxy Fuel Thermal Spraying in Turbine Shaft Repairing. Production Technology Research Institute, branch of ACECR Potential of High Velocity Oxy Fuel Thermal Spraying in Turbine Shaft Repairing M. Jalali Azizpour 1 S. Norouzi H.Mohammadi Majd 3 D.Sajedipour 4 E. Pipelzadeh 5 B.Aslani 6 H.Talebi 7 A.Ghamari 8 1, 3,

More information

published at the ISPC 14, Prague, CZ, August 2 nd - 6 th 1999

published at the ISPC 14, Prague, CZ, August 2 nd - 6 th 1999 published at the ISPC 14, Prague, CZ, August 2 nd - 6 th 1999 In-situ characterization of plasma chemical reactions during the deposition of Si-C (-N) coatings in a D.C. plasma jet by means of emission

More information

Material Product Data Sheet Tungsten Carbide Nickel Chromium Self-Fluxing Powders

Material Product Data Sheet Tungsten Carbide Nickel Chromium Self-Fluxing Powders Material Product Data Sheet Tungsten Carbide Nickel Chromium Self-Fluxing Powders Thermal Spray Powder Products: Metco 31C-NS, Metco 32C, Metco 34F, Metco 34FP, Metco 36C, WOKA 7701, WOKA 7702, WOKA 7703,

More information

Ag 2 S: Fabrication and Characterization Techniques

Ag 2 S: Fabrication and Characterization Techniques 2 2 S: Fabrication and Characterization Techniques This chapter describes two fabrication methods used for the growth of 2 S thin films. The specific growth parameters are presented for each method as

More information

Wettability between Porous MgAl 2 O 4 Substrates and Molten Iron

Wettability between Porous MgAl 2 O 4 Substrates and Molten Iron Materials Transactions, Vol. 50, No. 11 (2009) pp. 2552 to 2556 #2009 The Japan Institute of Metals Wettability between Porous MgAl 2 O 4 Substrates and Molten Iron Naotaka Fukami*, Ryohei Wakamatsu*,

More information

THERMAL STABILITY OF RAPIDLY SOLIDIFIED Al-Fe-X ALLOYS. Milena VODĚROVÁ, Pavel NOVÁK, Alena MICHALCOVÁ, Dalibor VOJTĚCH

THERMAL STABILITY OF RAPIDLY SOLIDIFIED Al-Fe-X ALLOYS. Milena VODĚROVÁ, Pavel NOVÁK, Alena MICHALCOVÁ, Dalibor VOJTĚCH THERMAL STABILITY OF RAPIDLY SOLIDIFIED Al-Fe-X ALLOYS Milena VODĚROVÁ, Pavel NOVÁK, Alena MICHALCOVÁ, Dalibor VOJTĚCH Department of Metals and Corrosion Engineering, Institute of Chemical Technology,

More information

Laser Fusion Coatings of Functional Parts

Laser Fusion Coatings of Functional Parts Laser Fusion Coatings of Functional Parts J.A. Ramos 1, D.L. Bourell 1, M.R. Govindaraju 2 (1) Department of Mechanical Engineering, Laboratory for Freeform Fabrication The University of Texas at Austin,

More information

Downloaded from MIL-DTL w/int. AMENDMENT 1 26 September 2014 USED IN LIEU OF. 12 May 2014 DETAIL SPECIFICATION

Downloaded from   MIL-DTL w/int. AMENDMENT 1 26 September 2014 USED IN LIEU OF. 12 May 2014 DETAIL SPECIFICATION INCH-POUND 26 September 2014 USED IN LIEU OF 12 May 2014 DETAIL SPECIFICATION ALUMINUM-BASED POWDERS FOR COLD SPRAY DEPOSITION This specification is approved for interim use by the U.S. Army Research Laboratory,

More information

Pulsed Laser Deposition of Epitaxial Titanium Nitride on Magnesium Oxide substrate

Pulsed Laser Deposition of Epitaxial Titanium Nitride on Magnesium Oxide substrate Pulsed Laser Deposition of Epitaxial Titanium Nitride on Magnesium Oxide substrate By, Preetam ANBUKARASU UTRIP 2012 (1 st Crew) Under the Guidance of, Prof. Tetsuya HASEGAWA, Solid State Chemistry Lab,

More information

CORROSION PROPERTIES OF CERMET COATINGS SPRAYED BY HIGH-VELOCITY OXYGEN-FUEL. Dragos UŢU, Iosif HULKA, Viorel-Aurel ŞERBAN, Hannelore FILIPESCU

CORROSION PROPERTIES OF CERMET COATINGS SPRAYED BY HIGH-VELOCITY OXYGEN-FUEL. Dragos UŢU, Iosif HULKA, Viorel-Aurel ŞERBAN, Hannelore FILIPESCU Abstract CORROSION PROPERTIES OF CERMET COATINGS SPRAYED BY HIGH-VELOCITY OXYGEN-FUEL Dragos UŢU, Iosif HULKA, Viorel-Aurel ŞERBAN, Hannelore FILIPESCU Politehnica University of Timisoara, Romania, dragosutu@yahoo.com,

More information

Substrate surface effect on the structure of cubic BN thin films from synchrotron-based X-ray diffraction and reflection

Substrate surface effect on the structure of cubic BN thin films from synchrotron-based X-ray diffraction and reflection Substrate surface effect on the structure of cubic BN thin films from synchrotron-based X-ray diffraction and reflection X.M. Zhang, W. Wen, X.L.Li, X.T. Zhou published on Dec 2012 PHYS 570 Instructor

More information

CHAPTER 21. Cutting-Tool Materials and Cutting Fluids. Kalpakjian Schmid Manufacturing Engineering and Technology 2001 Prentice-Hall Page 21-1

CHAPTER 21. Cutting-Tool Materials and Cutting Fluids. Kalpakjian Schmid Manufacturing Engineering and Technology 2001 Prentice-Hall Page 21-1 CHAPTER 21 Cutting-Tool Materials and Cutting Fluids Manufacturing Engineering and Technology 2001 Prentice-Hall Page 21-1 Cutting Tool Material Hardnesses Figure 21.1 The hardness of various cutting-tool

More information

INTERVIA BPP-10 Photoresist

INTERVIA BPP-10 Photoresist Technical Data Sheet INTERVIA BPP-10 Photoresist For Advanced Packaging Applications Description Regional Product Availability Advantages INTERVIA BPP-10 Photoresist is a general-purpose, multi-wavelength

More information

Microstructure-Property Relationship of AA3003/Boron Nitride Particle-Reinforced Metal Matrix Composites Cast by Bottom-Up Pouring

Microstructure-Property Relationship of AA3003/Boron Nitride Particle-Reinforced Metal Matrix Composites Cast by Bottom-Up Pouring Microstructure-Property Relationship of AA3003/Boron Nitride Particle-Reinforced Metal Matrix Composites Cast by Bottom-Up Pouring 1 Essa Zitoun and A. Chennakesava Reddy 2 1 Research Scholar, Department

More information

Surface Coating of Tungsten Carbide by Electric Exploding of Contact

Surface Coating of Tungsten Carbide by Electric Exploding of Contact Surface Coating of Tungsten Carbide by Electric Exploding of Contact Evgeny G. Grigoryev General Physics Department, Moscow Engineering Physics Institute, Kashirskoe sh. 31, Moscow, 115409, Russia Abstract.

More information

Development of New Generation Of Coatings with Strength-Ductility Relationship, Wear, Corrosion and Hydrogen Embrittlement Resistance Beyond the

Development of New Generation Of Coatings with Strength-Ductility Relationship, Wear, Corrosion and Hydrogen Embrittlement Resistance Beyond the Development of New Generation Of Coatings with Strength-Ductility Relationship, Wear, Corrosion and Hydrogen Embrittlement Resistance Beyond the Current Materials Accomplishments till date As the structural

More information

Synthesis of Multi Wall Carbon Nanotube (WCNT) over thin films of SiO 2 -Fe 2 O 3 deposited by Combustion Chemical Vapor Deposition

Synthesis of Multi Wall Carbon Nanotube (WCNT) over thin films of SiO 2 -Fe 2 O 3 deposited by Combustion Chemical Vapor Deposition Synthesis of Multi Wall Carbon Nanotube (WCNT) over thin films of SiO 2 -Fe 2 O 3 deposited by Combustion Chemical Vapor Deposition M. D. Lima*, S. S. Stein, R. Bonadiman, M. J. de Andrade, C. P. Bergmann

More information

Institute of Metallurgy and Materials Science, Polish Academy of Sciences, 25 Reyonta st., Krakow, Poland 2

Institute of Metallurgy and Materials Science, Polish Academy of Sciences, 25 Reyonta st., Krakow, Poland 2 Acta Metallurgica Slovaca, Vol. 17, 2011, No. 2, p. 77-83 77 TEM INVESTIGATION OF MATRIX - SAFFIL FIBER INTERFACES IN ALUMINIUM ALLOYS BASED COMPOSITES J. Morgiel 1, J. Kaczmar 2, M. Pomorska 1, K. Naplocha

More information

EFFECTS OF BORON CARBIDE ADDITION ON HARDNESS AND MICROSTRUCTURE OF Al-Si/B 4 C COMPOSITE. of Malaysia, 43600, Bangi Selangor, Malaysia

EFFECTS OF BORON CARBIDE ADDITION ON HARDNESS AND MICROSTRUCTURE OF Al-Si/B 4 C COMPOSITE. of Malaysia, 43600, Bangi Selangor, Malaysia EFFECTS OF BORON CARBIDE ADDITION ON HARDNESS AND MICROSTRUCTURE OF Al-Si/B 4 C COMPOSITE Anis Syukriah Ibrahim 1, Abdul Razak Daud*,1 and Yusof Abdullah 2 1 Department of Applied Physics, Faculty of Science

More information

Challenges and Future Directions of Laser Fuse Processing in Memory Repair

Challenges and Future Directions of Laser Fuse Processing in Memory Repair Challenges and Future Directions of Laser Fuse Processing in Memory Repair Bo Gu, * T. Coughlin, B. Maxwell, J. Griffiths, J. Lee, J. Cordingley, S. Johnson, E. Karagiannis, J. Ehrmann GSI Lumonics, Inc.

More information

Synthesis of nanoscale CN x /TiAlN multilayered coatings by ion-beam-assisted deposition

Synthesis of nanoscale CN x /TiAlN multilayered coatings by ion-beam-assisted deposition Synthesis of nanoscale / multilayered coatings by ion-beam-assisted deposition M. Cao, D. J. Li, a and X. Y. Deng College of Physics and Electronic Information Science, Tianjin Normal University, Tianjin

More information

Supporting Information

Supporting Information Supporting Information Large-Area, Transfer-Free, Oxide-Assisted Synthesis of Hexagonal Boron Nitride Films and Their Heterostructures with MoS2 and WS2 Sanjay Behura, Phong Nguyen, Songwei Che, Rousan

More information

Growth Of TiO 2 Films By RF Magnetron Sputtering Studies On The Structural And Optical Properties

Growth Of TiO 2 Films By RF Magnetron Sputtering Studies On The Structural And Optical Properties Journal of Multidisciplinary Engineering Science and Technology (JMEST) Growth Of TiO 2 Films By RF Magnetron Sputtering Studies On The Structural And Optical Properties Ahmed K. Abbas 1, Mohammed K. Khalaf

More information

CHAPTER 3: CRYSTAL STRUCTURES & PROPERTIES

CHAPTER 3: CRYSTAL STRUCTURES & PROPERTIES CHAPTER 3: CRYSTAL STRUCTURES & PROPERTIES ISSUES TO ADDRESS... How do atoms assemble into solid structures? (for now, focus on metals) How does the density of a material depend on its structure? When

More information

DEGRADATION THE REFRACTORIES OF ROTARY FURNACE LININGS IN THE PRODUCTION OF ZINC OXIDE

DEGRADATION THE REFRACTORIES OF ROTARY FURNACE LININGS IN THE PRODUCTION OF ZINC OXIDE DEGRADATION THE REFRACTORIES OF ROTARY FURNACE LININGS IN THE PRODUCTION OF ZINC OXIDE Natália LUPTÁKOVÁ a, Františka PEŠLOVÁ a, Evgeniy ANISOMOV b, Adriana PAVÚČKOVÁ a, Michaela FERODOVÁ a a University

More information

MECHANICAL PROPERTIES AND THERMAL STABILITY OF ALSI-X BASED ALLOYS PREPARED BY CENTRIFUGAL ATOMIZATION. Filip PRŮŠA*, Dalibor VOJTĚCH

MECHANICAL PROPERTIES AND THERMAL STABILITY OF ALSI-X BASED ALLOYS PREPARED BY CENTRIFUGAL ATOMIZATION. Filip PRŮŠA*, Dalibor VOJTĚCH MECHANICAL PROPERTIES AND THERMAL STABILITY OF ALSI-X BASED ALLOYS PREPARED BY CENTRIFUGAL ATOMIZATION Filip PRŮŠA*, Dalibor VOJTĚCH Department of Metals and Corrosion Engineering, Institute of Chemical

More information

Fabrication and thermal properties of Al 2 TiO 5 /Al 2 O 3 composites

Fabrication and thermal properties of Al 2 TiO 5 /Al 2 O 3 composites Materials Science-Poland, Vol. 28, No. 3, 2010 Fabrication and thermal properties of Al 2 TiO 5 /Al 2 O 3 composites M. LI, F. CHEN, Q. SHEN *, L. ZHANG State Key Lab of Advanced Technology for Materials

More information

Interfaces: Corrosion in Pb-alloy cooled nuclear reactors and advanced mitigation measures

Interfaces: Corrosion in Pb-alloy cooled nuclear reactors and advanced mitigation measures Interfaces: Corrosion in Pb-alloy cooled nuclear reactors and advanced mitigation measures and G. Müller KIT KIT Universität des Landes Baden-Württemberg und nationales Forschungszentrum in der Helmholtz-Gemeinschaft

More information

Amorphous Alumosilicophosphate Coatings for Niobium Alloys

Amorphous Alumosilicophosphate Coatings for Niobium Alloys Materials Science Forum Online: 2005-12-15 ISSN: 1662-9752, Vol. 502, pp 237-242 doi:10.4028/www.scientific.net/msf.502.237 2005 Trans Tech Publications, Switzerland Amorphous Alumosilicophosphate Coatings

More information

Repetition: Electrochemistry

Repetition: Electrochemistry Repetition: Electrochemistry Process types Cathodic deposition Anodic oxidation Electroless deposition Repetition: Cathodic Deposition Basic set up Potential curve - + U(x) - Me + S - + - K 300 nm + +

More information

Thermal spraying Terminology, classification

Thermal spraying Terminology, classification Provläsningsexemplar / Preview INTERNATIONAL STANDARD ISO 14917 Second edition 2017-03 Thermal spraying Terminology, classification Projection thermique Terminologie, classification Reference number ISO

More information

Microstructural Studies of Thermal Spray Coating

Microstructural Studies of Thermal Spray Coating Microstructural Studies of Thermal Spray Coating Chennupati Vijaya Kumar SSIT, Sathupally-Khammam, India Subhash Kamal, PhD Universiti Teknologi Petronas, Malaysia ABSTRACT Chromium carbide nickel chrome,

More information