NF-2000 NF-2000M08 NF-2000VUNS2 N-7S

Transcription

1 POLYCARBONATE RESIN SHEET & FILM INDUSTRIAL APPLICATIONS GENERAL GRADE Polycarbonate Sheet NF-2000 NF-2000M08 NF-2000VUNS2 N-7S Polycarbonate Film FE-2000 FE-2000M01 FE-2000M12 FE-2000N-7

2 Polycarbonate Sheet NF-2000 is a sheet made of polycarbonate resin with excellent transparency and impact resistance. Due to the excellent anti-combustibility and insulation it provides, NF-2000 is adopted for various applications including automotive parts, electric and electronic parts, signs and displays, and machinery parts. Automobile applications NF-2000 has both the heat resistance with the practical temperatures of -30 to 110 degrees C, and workability that allows for easy printing, die-cutting, and thermoforming. NF-2000 is reputed for high reliability as a material for automotive parts in the electronic age. It passed for FMVSS (Federal Motor Vehicle Safety Standards No.302) Electric, electronic applications With its light and beautiful clearness, surface appearance, excellent electrical insulation and workability, NF-2000 is widely utilized as a material suitable for electric and electronic devices or printed plates etc. Meter display parts Meter display parts Display filter Nameplates (printed) One-sided matte sheet NF-2000M08 Anti-combustible sheet NF-2000VUNS2 M08 is polycarbonate matte sheet with matte finish on one side, which prevents scratches and other damage. M08 can be adopted for printed plate applications and also be die-cut for machinery part applications. NF-2000VUNS2, with thickness 1.5mm, has the burning characteristics compliant with UL94V-2. (NF-2000, with thickness ranging from 0.5 to 1.0mm, has the burning characteristics compliant with UL94V-2.) Printed plates Diffusion board Optical data (Clear) Test Item Test Method Value () Light transmission JIS K Haze JIS K The above data are an example of actual measurement, not a guarantee for performance. Printed plates 2

3 Polycarbonate Sheet Grades of NF-2000 series Product Grade Size(mm) Thickness (mm) General sheet Clear NF Anti-combustible sheet Clear NF-2000VUNS General sheet colored NF-2000C NF-2000VC One-sided matte sheet Clear NF-2000M Standard size packing unit (sheet) Stock 1NF-2000 Thickness 1.5mm contain anti-combustible material. 2NF-2000 Thickness 1.5mm contain ultraviolet absorber. 3For the tones, see color numbers in the sample book. 4NF-2000VC Thickness 1.5mm contain anti-combustible material. Comparison of physical properties with various resin plates and inorganic glass Density Test Item Test Method ISO 1183 JIS K7112 Unit g/cm 3 NF PMMA 1.19 PVC FRP GLASS 2.50 Tensile strength Nominal strain at break Tensile modulus ISO JIS K7162 kgf/cm 2 GPa 10 4 kgf/cm Compression strength ISO 604 JIS K7181 kgf/cm Flexural strength Flexural modulus ISO 178 JIS K7171 kgf/cm 2 GPa 10 4 kgf/cm Charpy impact strength (Notched) ISO 179 JIS K7111 kj/m 2 kgfcm/cm Izod impact strength (Notched) ISO 180 JIS K7110 J/m kgfcm/cm Hardness ISO JIS K M6070 R M Shore 5080 Baccol Thermal conductivity ratio ASTM C177 JIS A W/mK 10-4 cal/cmsecc Specific heat JIS K7123 kj/kgk cal/gc Coefficient of Linear thermal expansion Heat distortion temperature ISO JIS K7139 ISO 75-1, 2 JIS K K -1 C C Continuous usage temperature Bending ratio Light transmission Flammability Oxygen index ISO 489 JIS K7142 ISO JIS K JIS K C Opaque 1.52 Above90 The physical properties in the table above are the representative values actually measured using our test method, and are not guaranteed values. All physical values except those of Iupilon Sheet (NF-2000) are taken from the literature. 3

4 Polycarbonate Sheet Anti-combustible sheet N-7S is polycarbonate sheet with heightened anti-combustibility, which is fit for use in machinery parts where insulation is required. Grades Product Size (mm) Thickness (mm) N-7S (Natural) N-7SC (Black) Standard size packing unit (sheet) Stock Basic physical properties of N-7S Test Item Test Method Condition Unit Thickness 0.5mm Thickness 0.8mm or over Density ISO 1183 JIS K7112 g/cm Tensile strength ISO JIS K Nominal strain at break ISO JIS K Flexural strength ISO 178 JIS K Flexural modulus ISO 178 JIS K7171 GPa Charpy impact strength (Notched) Heat distortion temperature ISO 179 JIS K7111 ISO 75-1, 2 JIS K kj/m 2 C Dielectric constant 1MHz Dielectric loss tangent 1MHz Dielectric breakdown strength Short-time method MVm Oxygen index JIS K Ball pressure temperature Electrical Appliance Affairs of Japan Electric Association B method C Vicat softening temperature JIS K7206 C Glow wire test IEC GWIT 1 GWFI 2 C The values in this table are representative values based on measurement, and not specified values. (1) GWIT: Glow wire ignitability test method for materials (2) GWFI: Glow wire flammability test method for materials 4

5 Polycarbonate Film General film FE-2000 is a standard type polycarbonate film with high transparency and workability as well as beautiful gloss on the surface, adopted in a wide variety of applications including printed plates and molded forms. Types and Grades General film (without masking) Thickness (m) Width (mm) 1300 Length (m) One-sided masking film (Semi-stock) Thickness (m) Width (mm) Length (m) Core - Paper tube (3 inches = inner diameter of 76.2 mm) Please contact us about the use of cut-size films. Insulation material Nameplates (printed) Matte film (Minute) (Semi-coarse) These are special films that can reduce reflection with the matte finish on their surfaces. These are adopted in printed plates, or display panels and membrane switches for automobiles, home and office appliances. Types and Grades Roll type Thickness (m) Width (mm) 1300 Length (m) Cut product (Semi-stock) Thickness (m) Size (mm) Packing Please contact us about different cut sizes Printed board Printed plate 5

6 Polycarbonate Film Basic physical properties of FE-2000FE-2000M01FE-2000M12 Category Physical properties Density Test Item Tensile strength Nominal strain at break Coefficient of Thermal expansion Second-order transition point Condition Thickness m Thickness m Test Method ISO 1183 JIS K7112 ISO JIS K ISO JIS K JIS K7140 Unit g/cm 3 cm/cm/c C FE-2000 FE-2000M01 FE-2000M Melting temperature C Thermal properties Thermal conductivity ratio JIS A cal/cmsecc Specific heat JIS K7123 kj/kgk Brittle temperature ASTM D746 C -135 Flammability Thickness m or over UL94 VTM-2 Water vapor Thickness 300m JIS Z0208 g/m 2 24h 11 Gas permeability N2 O2 Thickness 300m Thickness 300m JIS K7126 JIS K7126 cccm/cm 2 seccmhg cccm/cm 2 seccmhg CO2 Thickness 300m JIS K7126 cccm/cm 2 seccmhg Dielectric breakdown strength Thickness 60m 25C MV/m Electric properties Volume resistivity Dielectric constant 23C 23C cm Dielectric loss tangent 23C The above values are actual measurement, not a guarantee of performance. Heat stability of FE-2000FE-2000M01FE-2000M12 Shrinkage Temperature Time Thickness (m) C 120C 130C 140C Less than 1 Less than 1 150C Less than 3 Less than 1 Less than 1 According to JIS C2318 (Electric polyester film) 6

7 Polycarbonate Film Anti-combustible film FE-2000N-7 is a film-type variation of N-7S. As in the case of N-7S, anti-combustibility and insulation of FE-2000N-7 can be widely adopted in electric and electronic applications as well as machinery parts. Types and Grades Natural / Roll type Thickness (m) Width (mm) Length (m) Core - Paper tube (3 inches = inner diameter of 76.2 mm) Please contact us about specially ordered films with different thickness, width or length. Basic physical properties Test Item Condition Test Method Unit FE-2000N-7 Density ISO 1183 JIS K7112 g/cm Light transmission Thickness m ISO JIS K Haze Thickness m JIS K Tensile strength Thickness 400m ISO JIS K Nominal strain at break Thickness 400m ISO JIS K Dielectric constant Dielectric loss tangent Dielectric breakdown strength 2GHz 5GHz 10GHz 2GHz 5GHz 10GHz Thickness 200m Thickness 300m Thickness 400m Thickness 500m MV/m Tracking resistance ASTM D3638 V 175CTI Arc resistance ASTM D495 second TAR 2 60 Glow wire test Flammability Thickness m The above values are representative values based on measurement, not a guarantee of performance. (1) CTI: Comparative tracking index (2) TAR: Time of Arc resistance (3) GWIT: Glow wire ignitability test method for materials (4) GWFI: Glow wire flammability test method for materials UL94 C GWIT GWFI 4 Above960 VTM-0 (Thickness 400m) 7

8 The information in this brochure is provided in good faith and believed to be accurate. However, since the conditions of use are beyond the control of Mitsubishi Gas Chemical Company, Inc., Mitsubishi Gas Chemical Company, Inc. makes its explanation and recommendation without any warranty, explicit or implicit, including any warranty of fitness for a particular purpose. The listed properties are portrayed as general information only and are not product specifications. Mitsubishi Gas Chemical Company, Inc. disclaims any liability in connection with the use of the information in this brochure and does not warrant against infringement by reason of the use of any of its products in combination with other materials. The information presented here cannot be considered as a suggestion to use our products without taking into account existing patents, or legal provisions or regulations, whether national or local. List No. E-22 First Edition Rev.0 Lot No S