Carboset PL-958 Acrylic Copolymer Emulsion TECHNICAL DATA SHEET

Transcription

1 Acrylic Copolymer Emulsion TECHNICAL DATA SHEET General Description Carboset PL-958 is an acrylic copolymer emulsion designed for clear or pigmented temporary peelable coating applications. Carboset PL-958 resin offers very good solvent resistance as well as high tensile strength. Carboset PL-958 resin may not require coalescing aids at ambient temperatures which allows the formulator to produce temporary coatings with extremely low VOC's. Carboset PL-958 resin may be applied to a wide variety of metal, plastic, and painted substrates for a temporary protective coating which peels easily and leaves no residue after removal. Carboset PL-958 resin is composed of ingredients which meet the current requirements of FDA for food contact use when used in accordance with the regulation. (See Page 2 for details.) Performance Features Clear films Excellent release No residue Solvent resistant High tensile strength Extremely low VOC coatings possible Suggested Uses Spray booth coatings Paint maskant Sign maskants Release coatings for temporary paper labels Factory-applied temporary protective coatings Field-applied temporary protective coatings Typical Physical Properties* Appearance Milky White Emulsion Total Solids by Weight, % 47.0 Total Solids by Volume, % 43.4 Density, pounds/gallon 8.9 Density, Specific Gravity 1.07 Brookfield Viscosity, 25 C, RVT #2 Spindle, 20 rpm, cps 65 ph 8.0 Minimum Film Forming Temperature <3 C Surface Tension, dynes/cm 32 Volatiles Water/Ammonia Mechanical Stability, 30 minutes, Waring Blender Pass Freeze/Thaw Stability Protect from freezing *Property values represent typical results only and are not to be considered specifications. June 4, 2007 The information contained herein is believed to be reliable, but no representations, guarantees or warranties of any kind are made as to its accuracy, suitability for particular applications or the results to be obtained. The information is based on laboratory work with small-scale equipment and does not necessarily indicate end product performance. Because of the variations in methods, conditions and equipment used commercially in processing these materials, no warranties or guarantees are made as to the suitability of the products for the applications disclosed. Full-scale testing and end product performance are the responsibility of the user. Lubrizol Advanced Materials, Inc. shall not be liable for and the customer assumes all risk and liability of any use or handling of any material beyond Lubrizol Advanced Materials, Inc.'s direct control. The SELLER MAKES NO WARRANTIES, EXPRESS OR IMPLIED, INCLUDING, BUT NOT LIMITED TO, THE IMPLIED WARRANTIES OF MERCHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE. Nothing contained herein is to be considered as permission, recommendation, nor as an inducement to practice any patented invention without permission of the patent owner. Lubrizol Advanced Materials, Inc Brecksville Road Cleveland, OH The Lubrizol Corporation

2 Page 2 Typical Performance Data White Peelable Coating (PL B) Cure: Air Dry Peel Strength: 10 days air dry, oz./linear inch, 180 peel Set-to-Touch: 35 minutes CRS 1-2 Hot-dipped (72 F, 50% R.H., 6 mils wet) Peak Tensile: 2100 psi Glass 0-1 Galvanized 1-2 Peak Elongation: 960% Lexan (ML4291) 4-6 Electro 2-3 galvanized ABS (Cycolac 5-8 Zinc phosphate 1-2 AR31596) Noryl (PX ) 0-1 Tin plate 0-1 Polypropylene 0-1 Aluminum 0 Tensile and Elongation Test Results Peelable Coating Dry Film Thickness Tensile psi Elongation % Clear Film 3 mil Carboset PL-958 resin White Coating 3 mil Black Coating 3 mil (PL A) Low Cost White Coating (PL A) 3 mil FDA Status Carboset PL-958 resin is composed of ingredients which meet the current requirements of the FDA for food contact use when used in accordance with the following sections and limitations of the 21CFR: , , ,4, and NOTES: Reference FDA Regualtion 2 4 The final food contact article and the polymer "Adhesives" must meet the extraction requirements of (b) "Resinous and Polymeric Coatings" The final food contact article must meet the extraction requirements of (c) "Components of Paper and Paperboard in Contact with Aqueous and Fatty Foods: "Components of Paper and Paperboard in Contact with Dry Food"

3 Page 3 WHITE PEELABLE COATING Model Formula PL B Charge to letdown tank Carboset PL-958 resin Acrylic Emulsion In a separate tank, high speed the following ingredients to a 7.0 Hegman Add materials in order with agitation Water BYK Dispersant Triton CF Surfactant Tego Defoamer Tri-Pure R Pigment Use as needed to adjust for grind viscosity Water Transfer grind dispersion to letdown with agitation Add the remaining with agitation TSPP ph Buffer Carbopol EP-1 resin Thickener Triethanolamine Amine Raybo Flash Rust Inhibitor Water Total Solids By Weight, % 46.4 Total Solids by Volume, % 42.9 Weight per Gallon, lbs 9.04 VOC, grams/liter 31 pounds/gallon 0.26 Pigment Weight, % 2.15 Pigment Volume, % 0.57 Pigment Volume Concentration 1.33 Viscosity, Ford #4, Seconds ph

4 Page 4 BLACK PEELABLE COATING Model Formula PL B Add materials in order with agitation Carboset PL-958 resin Acrylic Emulsion Add premix Carbopol EP-1 resin Thickener Triethanolamine Amine Colonyl Black Pigment Dispersion Tego Defoamer Raybo Flash Rust Inhibitor Water Total Solids By Weight, % 45.4 Total Solids by Volume, % 43.2 Weight per Gallon, lbs 8.93 VOC, grams/liter 30 pounds/gallon 0.25 Pigment Weight, % 0.80 Pigment Volume, % 0.49 Pigment Volume Concentration 1.12 Pigment/Binder Ratio Viscosity, Ford #4, Seconds ph

5 Page 5 LOW COST WHITE PEELABLE COATING Model Formula PL B Charge to letdown tank Carboset PL-958 resin Acrylic Emulsion In a separate tank, high speed the following ingredients to a 7.0 Hegman Add materials in order with agitation Water Strodex PK Dispersant Tego Defoamer Omyacarb Filler Pigment Tri-Pure R Pigment Transfer grind paste with agitation Add the remaining with agitation Mix next two items until TSPP is dissolved TSSP ph Buffer Water Dispersant Tego Defoamer Carbopol EP-1 resin Thickener Add triethanol amine slowly Triethanolamine Amine Raybo Flash Rust Inhibitor Water Total Solids By Weight, % 52.4 Total Solids by Volume, % 44.6 Weight per Gallon, lbs 9.78 VOC, grams/liter 25 pounds/gallon 0.21 Pigment Weight, % Pigment Volume, % 6.67 Pigment Volume Concentration Pigment/Binder Ratio 0.43 Viscosity, Ford #4, Seconds ph

6 Page 6 LOW TEMPERATURE WHITE PEELABLE COATING Model Formula PL A Add in order indicated Water BYK Dispersant Triton CF Surfactant Tego Defoamer Tri-Pure R Pigment Use as needed to adjust grind viscosity Water Disperse to 6.5 Hegman Add dispersion to Carboset PL-958 with agitation Carboset PL-958 resin Acrylic Emulsion Triethyl Citrate C Plasticizer TSPP ph Buffer Carbopol EP-1 resin Thickener Triethanolamine Amine Raybo Flash Rust Inhibitor Water Total Solids By Weight, % 47.6 Total Solids by Volume, % 44.1 Weight per Gallon, lbs 9.05 VOC, grams/liter 26 pounds/gallon 0.22 pounds/solid pount Viscosity, Ford #4, Seconds ph Note: The addition of Triethyl Citrate C-2 plasticizer significantly enhances low temperature film flexibility and cohesive strength for improved peel characteristics at temperatures as low as 0 F.

7 Page 7 Suggestions DEFOAMERS In order to reduce foam during manufacture and application, it is usually necessary to use a defoamer. The following commercial defoamers have been found to be effective with Carboset PL-958 resin: Tego 825 Tego 1488 Foam Burst 338 Bubblebreaker 748 DeeFo XGM-14-I* Tego Chemie Tego Chemie Ross Chemical, Inc. Witco, Inc. Ultra Additives, Inc. *We have found this defoamer, XGM-14-I, to be very effective with Carboset PL-958 resin for defoaming during manufacturing and during airless spray applications -- even at high film builds. Suggested usage levels range from 0.25 to 2.0 pounds per 100 gallons formula. DISPERSANTS/SURFACTANTS Several dispersants and surfactants have been found to be effective in dispersing various pigments in Carboset PL-958 resin, and in helping to wet out various substrates with the formulated coating: BYK 158 Triton CF-10 FLASH RUST INHIBITION Byk-Chemie Union Carbide Application to some metal substrates may induce flash rusting under certain temperature/humidity conditions. The following is a suitable inhibitor: Raybo 60 OTHER RAW MATERIALS Raybo, Inc. THICKENERS The addition of thickeners often helps structure peelable coatings made with Carboset PL-958 resin to reduce or eliminate sag and permit application to vertical surfaces. Several thickeners have been found to be effective: Ti-Pure R902 Tetrasodium Pyrophosphate Colonyl Black Strodex PK-90 Triethyl Citrate C-2 DuPont Pigments Morton Thiokol Hoechst Dexter Moreflex Inc. Carbopol EP-1 resin HECQP-4400 Lubrizol Union Carbide FREEZE/THAW RESISTANCE The freeze/thaw resistance of the formulated product can be greatly improved with additions of 1-5% sodium chloride. Higher ph also contributes to freeze/thaw stability.