Effect of Silicon Carbide on Reactions between Molten Steel and Fused Magnesia Silicon Carbide Composite Refractory
|
|
- Eleanor Nelson
- 6 years ago
- Views:
Transcription
1 Effect of Silicon Carbide on Reactions between Molten Steel and Fused Magnesia Silicon Carbide Composite Refractory Interactions between MgO SiC composite and liquid steel resulted in decomposition of SiC particles by the molten steel that damaged the integrity of the composite. Yaowu Wei, Nan Li and Changming Ke Interactions between refractories and liquid steel have attracted attention with the development of clean steelmaking. 1 3 Low-carbon (LC) steel and ultra-low-carbon (ULC) steel require low carbon content. However, carbon-containing refractories are a source of carbon to the molten steel. Steelmakers prefer to use low-carbon-content refractories as steelmaking vessel linings. However, their service life remains a concern. SiC is considered a component substitute for graphite, which is widely used in steelmaking refractories. A study by Li and Chi 4 emphasizes SiC as substitute for ordinary carbon materials in mold fluxes for continuous casting of ULC steel. The results show that the carbon pickup Fig. 1 Schematic of the experimental arrangement. for ULC steel is weak (10% compared with traditional carbon-containing material). Carbon pickup of interstitial-free steel from MgO SiC composites has been reported. 5 Results show that aluminum powder decreases SiC oxidation and accelerates deoxidization in the steel. This accelerates the process of carbon pickup of steel from the SiC. SiC possesses many interesting properties, such as high thermal conductivity, good wetting resistance to slag and liquid steel, and low recarburization compared with carbon. Therefore, attention has been directed to the research and manufacture of MgO SiC composites. Because of their high-temperature properties, MgO SiC composites can be used as a component under high-temperature conditions. The eutectic point of the MgO 2MgO system is 1860 C. Studies of interactions between refractories and molten steel reveal that the refractory influences the properties of the steel. 6,7 The study on the route of steel penetration into refractories also is important. This study has investigated the reaction between molten steel and MgO SiC composites. 9201
2 Table 1 Chemical Composition of Raw Materials Fused MgO SiC powder Component (mass%) (mass%) MgO CaO Fe SiC 97.9 LOI Fig.2 Illustration of one piece of MgO SiC composite after the experiment. The Experiment Fused MgO aggregates, MgO fine powder and SiC fine powder were used in this study (Table 1). The SiC content in the composites was 7 mass%. The chemical composition of interstitial free (IF) steel was determined (Table 2). The raw materials were mixed with phenol formaldehyde resin (4 mass% added). The mixtures were fabricated using cold isostatic pressing at 200 MPa. The fabricated refractory crucible was heated at 230 C for 24 h. IF steel specimens (110 mm diameter 75 mm length) were embedded in the crucibles and covered with mold flux (Table 3). MgO-based ramming materials filled the interspace between the crucible and furnace induction coil (Fig. 1). The MgO SiC crucible that contained IF steel and flux was heated at 1600 C for 3 h in the induction furnace. A fast-heating process was adopted in this study. It took only 2 h to heat from room temperature to 1600 C. Table 2 Chemical Composition of IF Steel Component Composition (mass%) Oxygen Carbon Silicon 0.03 Manganese 0.12 Titanium Sulfur Aluminum Nitrogen Table 3 Chemical Composition of Mold Flux Component Composition (mass%) MgO Al CaO 40.2 Fe CaF The boundary between molten steel and composite was investigated using X-ray diffractometry (XRD) analysis and electron probe microanalysis (EPMA) with energy-dispersive spectroscopy (EDS) analysis. The original layer of the composite also was studied. Composite Corroded by Liquid Steel The MgO SiC crucible was cut into several pieces after the experiment. The MgO SiC composite obviously was corroded by the liquid steel (Fig. 2). Scanning electron microscopy and EDAS analyses of the reaction layer between the MgO SiC composite and steel were conducted (Fig. 3). The results showed that steel did penetrate into the composite (white dots in Fig. 3(A)). Moreover, the reaction layer was composed of MgO particles (point 2 in Fig. 3(B)), MgO CaO oxide mixture (point 4) and Fe Si mixture (point 1). A MgO particle that contained a small amount of Al 2 also was observed (point 3). The silicon content of the steel in the matrix was much higher than that of the IF steel sample. Therefore, the silicon in the Fe Si mixture might have come from SiC in the composite. No SiC particles were found in the reaction layer. The SiC content in the reaction layer was small. Therefore, SiC might have transferred to the other constituent; e.g., SiC decomposed into the steel. The hot face of the composite was investigated using XRD analysis. MgO, 2MgSiO 4 and CaMgSiO 4 existed in the hot face of the composite (Fig. 4). The original layer of the MgO SiC composite was studied 9202
3 after it was heated. SiC particles existed in that layer (Fig. 5). Interface Reactions When SiC particles come in contact with molten steel, SiC directly dissolves into the steel: SiC(s) = [C] + [Si] G 1 = T J/mol (1) The [Si] and [C] later react with [O] in the steel melt: [C] + [O] = CO(g) G 2 = T J/mol (2) [Si] + 2[O] = G 3 = T J/mol (3) Therefore, when the SiC dissolves into the steel, interspace remains for further steel penetration. This study shows that significant porosity exists in the reaction layer (Fig. 2). Some is removed from the liquid steel and some reacts with MgO CaO in the composite matrix. CaO and might also result from impurities in the fused MgO powder. One of the CaO MgO oxide mixture formations is described as MgO(s) + CaO(s) + SiO2(s) CaMgSiO 4 (s) (4) When the heating time is increased, more CaO MgO oxide forms in the matrix. At the same time, the aluminum content oxidizes and then reacts with MgO to form a nonstoichiometric spinel: MgO(s) + Al 2 (s) MgO Al 2 (s) G 5 = T J/mol (5) MgO CaO oxides observed at room temperature might be liquid oxide mixtures at high temperature. 8 It also has been reported that MgO CaO oxides, such as CaMgSiO 4, decompose to MgO and liquid phase at temperatures <1492 C. 9 Once the liquid forms in the matrix of a MgO SiC composite, it flows into the interparticle pores and subsequently (A) (B) penetrates the particle boundaries in the compact. Finally, the particles are surrounded by the liquid phase. The impurity Al 2 dissolves into the oxide mixture under high temperatures, but only in a small amount. The low-melting-phase CaO MgO oxides become the passageway for steel penetration. Molten steel corrodes the MgO aggregates along the crystal boundary, and MgO particles enter into molten steel once it is surrounded by steel melt. Fig. 3 SEM and EDAS analysis of the composite steel reaction layer (hot face is on the left hand) at (A) low magnification and (B) higher magnification showing various specific particles. Iron Silicon Magnesium Calcium Oxygen Aluminum Point (mass%) (at.%) (mass%) (at.%) (mass%) (at.%) (mass%) (at.%) (mass%) (at.%) (mass%) (at.%)
4 Counts 2θ (deg) Fig. 4 XRD analysis of reaction layer between molten steel and composite. Fig. 5 Original layer of MgO SiC composite. Some SiC particles in the composites might oxidize during heating, and, then, film forms around the particle surface. 10 2MgO forms on the boundary between MgO and SiC particles, and its amount increases in the matrix with heating temperature and time. Refractory Integrity Damaged The molten steel damaged the integrity of MgO SiC composites under high temperature. SiC particles can be directly dissolved into molten steel. The interspace that remains after SiC decomposition acts as the route for steel penetration. MgO particles become isolated and dissolve into the molten steel. that forms around the SiC surface reacts with CaO and MgO to form a low-melting-point phase, such as CaMgSiO 4, that also damages the integrity of MgO SiC composites. About the Authors Yaowu Wei is Associate Professor at Hubei Province Key Lab of Refractories and Ceramics, Wuhan University of Science and Technology, Wuhan, People s Republic of China. His research focuses on refractories for clean steelmaking. The interactions between refractories and molten melt are a main subject in his study. Nan Li is Professor and Director for Ph.D. studies at Hubei Province Key Lab of Refractories and Ceramics. His research focuses on refractories used for metallurgical industry. He is a Chinese commissioner of UNITECR. Changming Ke is Professor at Hubei Province Key Lab of Refractories and Ceramics. His research focuses on refractories and refractories recycling. Correspondence regarding this article should be addressed to Yaowu Wei via at yaowuwei@hotmail.com or wangyure@public.wh.hb.cn. 9204
5 References 1 N. Li, Interactions between Refractories and Steel and Its Influence on the Property of Steel; pp Metallurgical Industrial Publishing, G.Z. Ruan and N. Li, Carbon Pickup of Interstitial Free Steel from Al 2 C Refractories, Ironmaking Steelmaking, 31 [4] (2004). 3 P. He, R. Chen, G.F. Fang, et al., Study of Carbon Pickup of IF Steel Caused by Carbon-Containing Refractories, Naihuo Cailiao, 39 [4] (2005). 4 N. Li and J. Chi, Study on SiC as the Substitute of the Mold Fluxes in Continuous Casting of ULC Steel, Journal of Shanguan University (Natural Science), 19 [3] (1988). 5 Y. Wei, N. Li, et al., Behavior of Al Powder on the Carburization of MgO SiC Material to Molten Steel, Naihuo Cailiao, 40 [5] (2006). 6 J. Potschke, K. Beimdiek and M. Ollig, Reaction between MgO C Bricks and Steel Melts ; pp in UNITE- CR 99 Proceedings. Edited by J. Kramss, German Refractory Association, Berlin, H. Soulard, J. Lehmann and M. Boher, Interaction Mechanism between MgO C and Al-Killed Steels; see Ref. 6, pp N. Li, L.H. Li and Y.W. Wei, Effect of Microsilica in MgO-Based Castables on Oxygen Content of Interstitial Free Steel, Br. Ceram. Trans., 103, (2003). 9 G. Yu Guocheng, Theory of Basic Refractories; p Shanghai Technology Publishing, Shanghai, Z. Chen, Chemical Thermodynamics of Refractories; p Metallurgical Industrial Publishing, Beijing,
EFFECT OF THE Si POWDER ADDITIONS ON THE PROPERTIES OF SiC COMPOSITES
Original papers EFFECT OF THE Si POWDER ADDITIONS ON THE PROPERTIES OF SiC COMPOSITES # GUOZHI RUAN, MINGQIANG YIN, ZHIHUI ZHANG, GUOGANG XU College of Materials Science and Engineering, Shandong University
More informationFormation of Mg 2 C 3 phase in N220 nanocarbon containing low carbon MgO-C composition
Bull. Mater. Sci., Vol. 40, No. 5, September 2017, pp. 939 943 DOI 10.1007/s12034-017-1429-6 Indian Academy of Sciences Formation of Mg 2 C 3 phase in N220 nanocarbon containing low carbon MgO-C composition
More informationFabrication and thermal properties of Al 2 TiO 5 /Al 2 O 3 composites
Materials Science-Poland, Vol. 28, No. 3, 2010 Fabrication and thermal properties of Al 2 TiO 5 /Al 2 O 3 composites M. LI, F. CHEN, Q. SHEN *, L. ZHANG State Key Lab of Advanced Technology for Materials
More informationLightweight cordierite mullite refractories with low coefficients of thermal conductivity and high mechanical properties
Bull. Mater. Sci., Vol. 38, No. 2, April 2015, pp. 409 415. c Indian Academy of Sciences. Lightweight cordierite mullite refractories with low coefficients of thermal conductivity and high mechanical properties
More informationEffect of Nano-Sized Fe 2 O 3 on Microstructure and Hydration Resistance of MgO-CaO Refractories
Int. J. Nanosci. Nanotechnol., Vol. 12, No. 1, March. 2016, pp. 19-26 Effect of Nano-Sized Fe 2 O 3 on Microstructure and Hydration Resistance of MgO-CaO Refractories S. G. Kahrizsangi*, A. Nemati, A.
More informationCeramic Processing Research
Journal of Ceramic Processing Research. Vol. 17, No. 4, pp. 313~317 (2016) J O U R N A L O F Ceramic Processing Research Lightweight corundum-mullite refractories: II, Effects of porous aggregates on the
More informationMagnesia-carbon refractories for the lining of gasification chambers: technical capabilities and limitations
Magnesia-carbon refractories for the lining of gasification chambers: technical capabilities and limitations M. Hampel*, P. Gehre, T. Schemmel, C.G. Aneziris 5th International Freiberg Conference on IGCC
More informationCorrosion of Nozzle Refractories by Liquid Inclusion in High Oxygen Steels
, pp. 1281 1288 Corrosion of Nozzle Refractories by Liquid Inclusion in High Oxygen Steels Mun-Kyu CHO 1) and In-Ho JUNG 2) 1) Research Institute of Industrial Science and Technology, Pohang, Republic
More informationCorrosion behavior of silicon nitride bonding silicon carbide in molten magnesium and AZ91 magnesium alloy
Materials Science and Engineering A 45 (2006) 29 296 Corrosion behavior of silicon nitride bonding silicon carbide in molten magnesium and AZ9 magnesium alloy Hukui Chen, Jianrui Liu, Weidong Huang State
More informationMgO modification of slag from stainless steelmaking
ERIKSSON, J and BJÖRKMAN, B. MgO modification of slag from stainless steelmaking. VII International Conference on Molten Slags Fluxes and Salts, The South African Institute of Mining and Metallurgy, 2004.
More informationINTERACTION MECHANISM BETWEEN REFRACTORY AND MELTS IN IRON BATH SMELTING REDUCTION PROCESS
J o u r n a l o f J. Min. Metall. Sect. B-Metall. 46 (2) B (2010) 131-140 M i n i n g a n d M e t a l l u r g y INTERACTION MECHANISM BETWEEN REFRACTORY AND MELTS IN IRON BATH SMELTING REDUCTION PROCESS
More informationGel-Bonded Alumina Silicon Carbide Carbon-Based Blast-Furnace Trough Castable
Gel-Bonded Alumina Silicon Carbide Carbon-Based Blast-Furnace Trough Castable Incorporation of an organic fiber improved the densification, strength, corrosion and penetration properties, under dried and
More informationEffect of B 2 O 3 on Melting Temperature, Viscosity and Desulfurization Capacity of CaO based Refining Flux
, pp. 702 706 Effect of B 2 O 3 on Melting Temperature, Viscosity and Desulfurization Capacity of CaO based Refining Flux Hongming WANG, 1) Tingwang ZHANG, 1) Hua ZHU, 1,2) Guirong LI, 1) Yongqi YAN 1)
More informationThe generic requirements from blast furnace refractories are summarised below:
BLAST FURNACE In the blast furnace iron ore is melted and reduced by coke and limestone. The materials are charged from the furnace top to form layers. Hot blast blown from furnace bottom burns coke and
More informationStudy on reduction behavior of molybdenum trioxide in molten steel
Indian Journal of Engineering & Materials Sciences Vol. 22, August 2015, pp. 460-464 Study on reduction behavior of molybdenum trioxide in molten steel Hangyu Zhu*, Jianli Li, Zhengliang Xue & Wei Wang
More informationDEGRADATION THE REFRACTORIES OF ROTARY FURNACE LININGS IN THE PRODUCTION OF ZINC OXIDE
DEGRADATION THE REFRACTORIES OF ROTARY FURNACE LININGS IN THE PRODUCTION OF ZINC OXIDE Natália LUPTÁKOVÁ a, Františka PEŠLOVÁ a, Evgeniy ANISOMOV b, Adriana PAVÚČKOVÁ a, Michaela FERODOVÁ a a University
More informationTrial of capillary refining by porous CaO with molten slag
Trial of capillary refining by porous CaO with molten slag Toshihiro TANAKA, Masanori SUZUKI Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University, 2-1 Suita,
More informationSiC/Aluminum Composites Fabricated by in situ Processing using Reactive Infiltration Aid
Proceedings of the 12th International Conference on Aluminium Alloys, September 5-9, 2010, Yokohama, Japan 2010 2010 The Japan Institute of Light Metals pp. 1886-1890 1886 /Aluminum Composites Fabricated
More informationThe excellent performance of austempered ductile iron
Design and control of chemical compositions for high-performance austempered ductile iron *Gong Wenbang 1, Chen Guodong 1, Luo Li 1, Hao Jing 2 and Zhang Zhonghe 3 (1. Wuhan Textile University, Wuhan 430073,
More informationFabrication of Ni-Al Intermetallic Compounds on the Al Casting alloy by SHS Process
Fabrication of Ni-Al Intermetallic Compounds on the Al Casting alloy by SHS Process G.S. Cho *, K.R. Lee*, K.H. Choe*, K.W. Lee* and A. Ikenaga** *Advanced Material R/D Center, KITECH, 994-32 Dongchun-dong,
More informationREDUCING REFRACTORY COST USING NEW ASCC BRICKS FOR HOT IRON TRANSPORT
REDUCING REFRACTORY COST USING NEW ASCC BRICKS FOR HOT IRON TRANSPORT PENG, DEJIANG HE, ZHONGYANG YU, TERRY PUYANG REFRACTORY GROUP LTD. Drawings Outline Optimum Design Material Selection: Tar-Impregnated
More informationCharacterization of Sintered Ceramic Tiles Produced from Steel Slag
Journal of Minerals and Materials Characterization and Engineering, 2012, 11, 863-868 Published Online September 2012 (http://www.scirp.org/journal/jmmce) Characterization of Sintered Ceramic Tiles Produced
More informationSecondary Steelmaking 1 Synthetic slag practice, injection ladle metallurgy, deoxidation
17 Secondary Steelmaking 1 Synthetic slag practice, injection ladle metallurgy, deoxidation Topics to discuss... Secondary steelmaking Synthetic slag practice Injection ladle metallurgy Deoxidation Secondary
More informationPROTECTING REFRACTORIES AGAINST CORUNDUM GROWTH IN ALUMINUM TREATMENT FURNACES. C. Allaire and M. Guermazi
PROTECTING REFRACTORIES AGAINST CORUNDUM GROWTH IN ALUMINUM TREATMENT FURNACES C. Allaire and M. Guermazi CIREP-CRNF, Dept. of Eng. Physics & Materials Engng., Ecole Polytechnique (CRIQ campus), 8475 Christophe
More informationTHEORY AND APPLICATION OF MAGNESIA RAMMING MATERIAL IN FERROALLOY REFINING FURNACES
THEORY AND APPLICATION OF MAGNESIA RAMMING MATERIAL IN FERROALLOY REFINING FURNACES S. Wang 1, Y. Jin 2 and G. Li 2 1 Jilin Ferroalloy Company Limited, No.21 Heping Street, Jilin, 132062, China. E-mail:
More informationRECYCLING PRACTICES OF SPENT MgO-C REFRACTORIES
Journal of Minerals & Materials Characterization & Engineering, Vol. 1, No.2, pp69-78, 2002 Printed in the USA. All rights reserved RECYCLING PRACTICES OF SPENT MgO-C REFRACTORIES Kyei-Sing Kwong and James
More informationEFFECTS OF LIGHTWEIGHT MULLITE-SILICA RICH GLASS COMPOSITE AGGREGATES ON PROPERTIES OF CASTABLES
Original papers EFFECTS OF LIGHTWEIGHT MULLITE-SILICA RICH GLASS COMPOSITE AGGREGATES ON PROPERTIES OF CASTABLES YUANYUAN LI, # NAN LI, WEN YAN The Key State Laboratory Breeding Base of Refractories and
More informationCan Fluorspar be replaced in steelmaking? Eugene Pretorius Baker Refractories
Can Fluorspar be replaced in steelmaking? By Eugene Pretorius Baker Refractories I) Introduction The use of fluorspar in steelmaking is a controversial issue. A number of studies have shown that there
More informationMolten Metal-Slag-Refractory Reactions During Converting Process
International Journal of Engineering & Technology IJET-IJENS Vol: 10 No: 03 52 Molten Metal-Slag-Refractory Reactions During Converting Process Hady Efendy 1, Mochamad Safarudin 1, Haeryip Sihombing. 2
More informationCorrosion Mechanism of Commercial MgO C Refractories in Contact with Different Gas Atmospheres
, pp. 760 767 Corrosion Mechanism of Commercial MgO C Refractories in Contact with Different Gas Atmospheres Sune JANSSON, 1) Voicu BRABIE 2) and Pär JÖNSSON 3) 1) Arvika Gjuteri AB, SE-671 82 Arvika,
More informationc c T/ 130(J"C 1. INTRODUCTION 2. Investigation of SENs after Service TEM to investigate attack morphology, phase
1. INTRODUCTION A Mechanism of Slagline Wear of Graphite-Bonded Zirconia Submerged Nozzle during Continuous Casting of Steel Jooh-Hyuk Hong, Jae-Yoon Ko', Jong-Sun Park", Sung-Man Kim Dept. of Metallurgical
More informationTrial on the Applicaton of Capillary Phenomenon of Solid CaO to Desulfurization of Liquid Fe
Title Author(s) Citation Trial on the Applicaton of Capillary Phenomenon of Solid CaO to Desulfurization of Liquid Fe Tanaka, Toshihiro; Ogiso, Yumi; Ueda, Mitsuru; Lee, Joonho ISIJ INternational. 50(8)
More informationEVALUATION OF MECHANICAL PROPERTIES OF AL6061 METAL MATRIX COMPOSITE REINFORCED WITH FUSED ZIRCONIA ALUMINA
EVALUATION OF MECHANICAL PROPERTIES OF AL6061 METAL MATRIX COMPOSITE REINFORCED WITH FUSED ZIRCONIA ALUMINA *P.V.Rajesh, **S.Roseline, *** V.Paramasivam *P.G Scholar: Department of Mechanical Engineering,
More informationraw sinter mix ignition hood direction of strand wind main electrostatic wind boxes wind legs gas flow Fig. 1 Schematic of a typical sinter plant
Does the handling of iron present a potential health hazard from the release of respirable crystalline silica? IP TWG position paper to support the Iron Sinter REACH dossier 1. INTRODUCTION Sintering is
More informationThermodynamic determination of low melting area in CaO-Al 2 O 3 -SiO 2 -MgO-MnO system inclusion and its control in spring steel
Thermodynamic determination of low melting area in CaO-Al 2 O 3 -SiO 2 -MgO-MnO system inclusion and its control in spring steel Bo ZHANG 1),2), Fuming WANG 1),2) and Changrong LI 3) 1) School of Metallurgical
More informationDevelopment of Carbon Blocks for Blast Furnace Hearths
Technical Report UDC 669. 162. 212. 6 Development of Carbon Blocks for Blast Furnace Hearths Michio NITTA* Akio ISHII Hitoshi NAKAMURA Abstract Carbon blocks have been used as refractory for blast furnace
More informationPart III: Slag Practices and Oxygen/Carbon Injection when Melting Direct Reduced Iron
Use of DRI in EAF s Gregory L. Dressel Dressel Technologies Pawleys Island, SC Part III: Slag Practices and Oxygen/Carbon Injection when Melting Direct Reduced Iron Introduction When melting DRI or HBI
More informationEFFECT OF FERROSILICON, SILICON AND ALUMINUM ANTIOXIDANTS ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF MAGNESIA-GRAPHITE REFRACTORY
Feature Article... EFFECT OF FERROSILICON, SILICON AND ALUMINUM ANTIOXIDANTS ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF MAGNESIA-GRAPHITE REFRACTORY Z. A. Nemati 1, S. K. Sadrnezhaad 1, H. R. Ahmadi
More informationDEVELOPMENT AND CHARACTERIZATION OF ALUMINA/ALUMINUM CO-CONTINUOUS COMPOSITE BY REACTIVE MELT INFILTRATION TECHNIQUE
Journal of Quality and Technology Management Volume VIII, Issue I, June 2012, Page 71 82 DEVELOPMENT AND CHARACTERIZATION OF ALUMINA/ALUMINUM CO-CONTINUOUS COMPOSITE BY REACTIVE MELT INFILTRATION TECHNIQUE
More informationAustenitic stainless steel, as a corrosion-resistant material,
Study on wear resistant cast B-containing 1Cr18Ni9Ti stainless steel *Kuang Jiacai 1, Jiang Zhiqiang 2, 3, Zhang Shiyin 1, Ye Chang 1, and Liu Qicheng 1 (1. Department of Material Science and Engineering,
More informationForm of Al Ti Oxide Produced by Al Ti Deoxidation Reaction at 1873 and 1473 K
Form of Al Ti Oxide Produced by Al Ti Deoxidation Reaction at 1873 and 1473 K Hiroyuki Matsuura Lecturer Department of Advanced Materials Science, Graduate School of Frontier Sciences, The University of
More informationFAYALITE SLAG MODIFIED STAINLESS STEEL AOD SLAG
FAYALITE SLAG MODIFIED STAINLESS STEEL AOD SLAG Shuigen HUANG, Muxing GUO, Peter Tom JONES, Bart BLANPAIN Department of Metallurgy and Materials Engineering, KU Leuven, 3001 Heverlee, Belgium shuigen.huang@mtm.kuleuven.be,
More informationThe Function of Ca(OH) 2 and Na 2 CO 3 as Additive on the Reduction of High-Phosphorus Oolitic Hematite-coal Mixed Pellets
, pp. 427 433 The Function of Ca(OH) 2 and Na 2 CO 3 as Additive on the Reduction of High-Phosphorus Oolitic Hematite-coal Mixed Pellets Wen YU, Tichang SUN,* Jue KOU, Yuxia WEI, Chengyan XU and Zhenzhen
More informationEffects of slag chemistry and temperature on wetting and penetration of refractories by slags
TRAN, T., XIE, D. and CHENG, Y.B. Effects on slag chemistry and temperature on wetting and penetration of refractories by slags. VII International Conference on Molten Slags Fluxes and Salts, The South
More informationQualification of Micronized Kyanite and Silica Fume
Qualification of Micronized Kyanite and Silica Fume William L. Headrick Missouri Refractories Co., Inc. Formerly University of Missouri-Rolla Co-authors Dilip Jain, Kyanite Mining Corp. Musa Karakus, University
More informationCeramic Processing Research
Journal of Ceramic Processing Research. Vol. 11, No. 1, pp. 56~60 (2010) J O U R N A L O F Ceramic Processing Research Investigation of properties of boehmitic sol coated graphite added alumina-low cement
More informationLecture 17 Alternative Charge Materials in EAF
Lecture 17 Alternative Charge Materials in EAF Contents: Introduction Types of metallic charge materials Carbon content in DRI Charging methods Key words: Sponge iron, DRI, electric arc furnace, UHP furnaces
More informationEXPERIMENTAL INVESTIGATION OF PHASE EQUILIBRIA OF SUBSYSTEMS IN THE MnO-SiO 2 -Al 2 O 3 -MnS SYSTEM
EXPERIMENTAL INVESTIGATION OF PHASE EQUILIBRIA OF SUBSYSTEMS IN THE MnO-SiO 2 -Al 2 O 3 -MnS SYSTEM Dae-Hee Woo, Henri Gaye & Hae-Geon Lee Pohang University of Science and Technology, Korea Youn-Bae Kang
More informationPyrometallurgy of iron is still the most important pyrometallurgical process economically.
1 Pyrometallurgy of iron is still the most important pyrometallurgical process economically. Prehistorically, iron was prepared by simply heating it with charcoal in a fired clay pot. Coke is coal that
More informationFormation of MgO Al 2 O 3 Inclusions in High Strength Alloyed Structural Steel Refined by CaO SiO 2 Al 2 O 3 MgO Slag
, pp. 885 890 Formation of MgO Al 2 O 3 Inclusions in High Strength Alloyed Structural Steel Refined by CaO SiO 2 Al 2 O 3 MgO Slag Min JIANG, Xinhua WANG, Bin CHEN and Wanjun WANG School of Metallurgical
More informationThe Effect of La Addition on the Microstructure and Tensile Properties of Hot-Extruded Al 15%Mg 2 Si Composite
The Effect of La Addition on the Microstructure and Tensile Properties of Hot-Extruded Al 15%Mg 2 Si Composite Paper Presenter: S.H. Allameh 1 A. Akhlaghi 2, M. Noghani 3, M. Emamy 4. 1,4- School of Metallurgy
More informationResearch on High Performance Fe 3 Si-Si 3 N 4 -SiC Composite Used for Blast Furnace
The Open Materials Science Journal, 2012, 6, 1-5 1 Open Access Research on High Performance Fe 3 Si-Si 3 N 4 -SiC Composite Used for Blast Furnace Yong Li, Xiaoyan Zhu, Yawei Zhai, Jiaping Wang, Wendong
More informationStudy on the enameling properties of cold-rolled sheet steels contained different alloyed elements
Study on the enameling properties of cold-rolled sheet steels contained different alloyed elements SUN Quanshe, XU Chun 2 ) R & D Center, Baoshan Iron and Steel Co. Ltd., Shanghai 29, China 2) School of
More informationThe formation of an inner slag layer during the dissolution of MgO particles in ladle slag
The formation of an inner slag layer during the dissolution of MgO particles in ladle slag Deyong Wang, Maofa Jiang, Xiaobing Li, Tongsheng Zhang and Chengjun Liu Dept. Ferrous Metallurgy, School of Materials
More informationREFRACTORIES IN HEATING UNITS
Refractories and Industrial Ceramics Vol. 54, No. 2, July, 2013 REFRACTORIES IN HEATING UNITS ANALYSIS OF THE EFFECT OF PERICLASE-CARBON REFRACTORY QUALITY ON CONVERTER LINING LIFE É. A. Visloguzova, 1
More informationTechnical Paper. C. Wöhrmeyer* 1 ; J.M. Auvray 1 ; B. Li 1 ; H. Fryda 1 ; M. Szepizdyn 1 ; D. Pörzgen 2 ; N. Li 3 ; W. Yan 3.
Page : 1/9 Novel Calcium Magnesium Aluminate Bonded Castables For Steel And Foundry Ladles C. Wöhrmeyer* 1 ; J.M. Auvray 1 ; B. Li 1 ; H. Fryda 1 ; M. Szepizdyn 1 ; D. Pörzgen 2 ; N. Li 3 ; W. Yan 3. 1
More informationBriquette Smelting in Electric Arc Furnace to Recycle Wastes from Stainless Steel Production
Briquette Smelting in Electric Arc Furnace to Recycle Wastes from Stainless Steel Production Qi-xing YANG 1 2 2, Dong-feng HE 2 3 1 Abstract: Wastes from stainless steel production were briquetted together
More informationPROCESS ANALYSES FOR DEVELOPING COST- EFFECTIVE PARTICULATE REINFORCED INORGANIC COMPOSITES
52 Memoirs of the School of T. Engineering, Choh Nagoya University Vol.51, No.1 (1999) PROCESS ANALYSES FOR DEVELOPING COST- EFFECTIVE PARTICULATE REINFORCED INORGANIC COMPOSITES Takao CHOH Department
More informationSTUDY ON SLAG RESISTANCE OF REFRACTORIES IN SUBMERGED ARC FURNACES MELTING FERRONICKEL
STUDY ON SLAG RESISTANCE OF REFRACTORIES IN SUBMERGED ARC FURNACES MELTING FERRONICKEL Dong HU 1 Pei-Xiao LIU 2 Shao-Jun CHU 1 1 School of Metallurgical and Ecological Engineering, University of Science
More informationMECHANICAL PROPERTIES AND THERMAL STABILITY OF ALSI-X BASED ALLOYS PREPARED BY CENTRIFUGAL ATOMIZATION. Filip PRŮŠA*, Dalibor VOJTĚCH
MECHANICAL PROPERTIES AND THERMAL STABILITY OF ALSI-X BASED ALLOYS PREPARED BY CENTRIFUGAL ATOMIZATION Filip PRŮŠA*, Dalibor VOJTĚCH Department of Metals and Corrosion Engineering, Institute of Chemical
More informationMg-Al alloys, such as AZ91 and AM60 alloys, have been
Effect of Cu addition on microstructure and properties of Mg-10Zn-5Al-0.1Sb high zinc magnesium alloy *You Zhiyong, Zhang Yuhua, Cheng Weili, Zhang Jinshan and Wei Yinghui ( College of Materials Science
More informationHigh Efficiency Hot Metal Desulfurization by Enhancing Flux Dispersion in Mechanical Stirring Process
JFE TECHNICAL REPORT No. 22 (Mar. 207) High Efficiency Hot Metal Desulfurization by Enhancing Flux Dispersion in Mechanical Stirring Process NAKAI Yoshie * MATSUI Akitoshi *2 KIKUCHI Naoki *3 Abstract:
More informationLecture 25: Principles of degassing
Lecture 25: Principles of degassing Contents Introduction Principles Side reactions General considerations Fluid flow in degassing Material balance in de gassing Key words: Degassing, gases in steel, ladle
More informationMechanism of Dissolution of Burnt Lime into Molten Slags Containing Iron Oxide.
Mechanism of Dissolution of Burnt Lime into Molten Slags Containing Iron Oxide. Hiroyuki Sunayama *, Masayasu Kawahara* Toshiyuki Kozuka *, Toshiharu Mitsuo* * Y oshimasa Mizukami*** * Department of Materials
More informationSlag formation during high temperature interactions between refractories containing SiO 2 and iron melts with oxygen
Slag formation during high temperature interactions between refractories containing SiO 2 and iron melts with oxygen E. Kapilashrami* 1, V. Sahajwalla 2 and S. Seetharaman 1 Refractory metal interactions
More informationInfluence of milling time on the performance of ceramic ball grinding media prepared from refractory waste
Materials Science-Poland, Vol. 25, No. 1, 2007 Influence of milling time on the performance of ceramic ball grinding media prepared from refractory waste L.Y. ZHONG 1, 2, 3, B. L. WU 2,3, L. M. ZHANG 1*,
More informationStudy On Application Of Alumina In High-Purity Andalusite Based Refractory
Journal of Minerals & Materials Characterization & Engineering, Vol. 3, No.2, pp 81-89, 2004 jmmce.org Printed in the USA. All rights reserved Study On Application Of Alumina In High-Purity Andalusite
More informationInstitute of Industrial Science (IIS) and Okabe Lab.
Institute of Industrial Science (IIS) and Okabe Lab. Ryosuke Matsuoka Graduate School of Engineering, The University of Tokyo 1 Institute of Industrial Science (IIS) http://www.iis.u-tokyo.ac.jp/ 2 About
More informationLecture 14 Modern trends in BOF steelmaking
Lecture 14 Modern trends in BOF steelmaking Contents: Post combustion Technology of post combustion Potential post combustion issues Slag splashing What is required for slag splashing Liquidus temperature
More informationKey Laboratory of Special Functional Materials Technology of Ministry of Education, Wuhan University of Technology, Wuhan, , China 2
21 st International Conference on Composite Materials Xi an, 20-25 th August 2017 PREPARATION AND PROPERTIES OF ZIRCONIA FIBRE REINFORCED BORON PHENOLIC RESIN FOR CERAMIC AND HIGH TEMPERATURE COMPOSITES
More informationEffect of melt temperature on the oxidation behavior of AZ91D magnesium alloy in 1,1,1,2-tetrafluoroethane/air atmospheres
available at www.sciencedirect.com www.elsevier.com/locate/matchar Effect of melt temperature on the oxidation behavior of AZ91D magnesium alloy in 1,1,1,2-tetrafluoroethane/air atmospheres Hukui Chen
More informationCLEANLINESS OF CONVENTIONALLY DEOXIDIZED AND CALCIUM TREATED LOW CARBON STEEL
STEEL FOUNDERS' SOCIETY OF AMERICA TECHNICAL SERVICE REPORT #108 CLEANLINESS OF CONVENTIONALLY DEOXIDIZED AND CALCIUM TREATED LOW CARBON STEEL Published by the STEEL FOUNDERS' SOCIETY OF AMERICA Malcolm
More informationSynthesis of Chromite for Subsequent Carburization by Methane-Hydrogen Gas Mixture
Synthesis of Chromite for Subsequent Carburization by Methane-Hydrogen Gas Mixture Vincent Canaguier, Ingeborg-Helene Svenum and Leiv Kolbeinsen Abstract The syntheses of stoichiometric iron chromite and
More informationDISSOLUTION BEHAVIOR OF FLUORINE IN AOD SLAG FROM THE PRODUCTION OF STAINLESS STEEL AFTER TREATMENT FOR VOLUME STABILIZATION
DISSOLUTION BEHAVIOR OF FLUORINE IN AOD SLAG FROM THE PRODUCTION OF STAINLESS STEEL AFTER TREATMENT FOR VOLUME STABILIZATION Qixing Yang 1, Fredrik Engström 1, Jianli Li 2, Anjun Xu 2 and Bo Björkman 1
More informationCHARACTERISATION OF INTERMETALLIC INCLUSIONS OBTAINED BY DISSOLUTION OF IRON ALLOYING ADDITIVES IN MOLTEN ALUMINIUM. Varužan Kevorkijan *
Association of Metallurgical Engineers of Serbia AMES Scientific paper UDC: 669.13'71 CHARACTERISATION OF INTERMETALLIC INCLUSIONS OBTAINED BY DISSOLUTION OF IRON ALLOYING ADDITIVES IN MOLTEN ALUMINIUM
More informationThe effect of additives on Al 2 O 3 SiO 2 SiC C ramming monolithic refractories
MAHT 090263 The effect of additives on Al 2 O 3 SiO 2 SiC C ramming monolithic refractories E. Karamian, A. Monshi and S.M. Siadati* Department of Materials Engineering, Isfahan University of Technology
More informationWear of magnesia-chrome refractory bricks as a function of matte temperature
Wear of magnesia-chrome refractory bricks as a function of matte temperature by M. Lange*, A.M. Garbers-Craig*, and R. Cromarty* Paper written on project work carried out in partial fulfilment of B. Eng.
More informationSynthesis of -SiAlON-AlN-Polytypoid Ceramics from Aluminum Dross
Materials Transactions, Vol. 51, No. 5 (2010) pp. 844 to 848 Special Issue on Growth of Ecomaterials as a Key to Eco-Society IV #2010 The Japan Institute of Metals Synthesis of -SiAlON-AlN-Polytypoid Ceramics
More informationHaseeb Ullah Khan Jatoi Department of Chemical Engineering UET Lahore
Haseeb Ullah Khan Jatoi Department of Chemical Engineering UET Lahore Greek word Keramikos which means Burnt Stuff indicating that desired properties of these materials are normally achieved through a
More informationMICROSTRUCTURE OF LONG TERM MARINE IMMERGED ANTI-WASHOUT CONCRETE
MICROSTRUCTURE OF LONG TERM MARINE IMMERGED ANTI-WASHOUT CONCRETE Shaowei Yang and Hengjing Ba School of Civil Engineering, Harbin Institute of Technology, Harbin, China Abstract In this contribution,
More informationMICROSTRUCTURE AND PROPERTIES OF COLLOIDAL SILICA BONDED MAGNESITE CASTABLE REFRACTORIES
Iranian Journal of Materials Science & Engineering Vol. 8, Number 1, Winter 211 MICROSTRUCTURE AND PROPERTIES OF COLLOIDAL SILICA BONDED MAGNESITE CASTABLE REFRACTORIES N. Hamedani Golshan, H. Sarpoolaky*
More informationInfluence of Steel Grade on Oxidation Rate of Molten Steel in Tundish
, pp. 831 840 Influence of Steel Grade on Oxidation Rate of Molten Steel in Tundish Katsuhiro SASAI and Akihiro MATSUZAWA Oita R & D Laboratories, Nippon Steel Corporation, 1 Oaza-Nishinosu, Oita, Oita-ken,
More informationWettability between Porous MgAl 2 O 4 Substrates and Molten Iron
Materials Transactions, Vol. 50, No. 11 (2009) pp. 2552 to 2556 #2009 The Japan Institute of Metals Wettability between Porous MgAl 2 O 4 Substrates and Molten Iron Naotaka Fukami*, Ryohei Wakamatsu*,
More informationPhosphorous Problem. AkMB Rashid Professor, Department of MME BUET, Dhaka
09 Phosphorous Problem AkMB Rashid Professor, Department of MME BUET, Dhaka Today s Topics Behaviour of phosphorous in metal and slag Oxidation of phosphorous Effect of temperature Effect of metal and
More informationUsing Slag in Manufacturing Masonry Bricks and Paving Units
Using Slag in Manufacturing Masonry Bricks and Paving Units Yasser Korany 1 and Salah El-Haggar 2 Steel production involves reducing the iron ore, after being sintered or belletized, in a blast furnace
More informationOxidation of Iron, Silicon and Manganese
08 Oxidation of Iron, Silicon and Manganese AkMB Rashid Professor, Department of MME BUET, Dhaka Today s Topics Oxidation of iron Oxidation and reduction of silicon Oxidation and reduction of manganese
More informationREDUCTION OF CHROMITE FINES IN SOLID STATE USING A MIXTURE OF GASES CONTAINING NATURAL GAS, HYDROGEN AND NITROGEN
REDUCTION OF CHROMITE FINES IN SOLID STATE USING A MIXTURE OF GASES CONTAINING NATURAL GAS, HYDROGEN AND NITROGEN C. N. Harman Director (Technical), Facor Alloys Ltd., Shreeramnagar-535 101(A.P.), India;
More informationMechanisms of Pig-iron Making from Magnetite Ore Pellets Containing Coal at Low Temperature
, pp. 1316 1323 Mechanisms of Pig-iron Making from Magnetite Ore Pellets Containing Coal at Low Temperature Kazuhiro NAGATA, Rie KOJIMA, 1) Taichi MURAKAMI, Masahiro SUSA 1) and Hiroyuki FUKUYAMA Department
More informationTECHNICAL SERVICE REPORT #119 ANALYSIS OF A SCAB DEFECT FROM A WCC CASTING
STEEL FOUNDERS' SOCIETY OF AMERICA TECHNICAL SERVICE REPORT #119 ANALYSIS OF A SCAB DEFECT FROM A WCC CASTING Published by the STEEL FOUNDERS' SOCIETY OF AMERICA Malcolm Blair Technical and Research Director
More informationResearch Article Conversion of Mill Scale Waste into Valuable Products via Carbothermic Reduction
Metallurgy Volume 215, Article ID 92628, 9 pages http://dx.doi.org/1.1155/215/92628 Research Article Conversion of Mill Scale Waste into Valuable Products via Carbothermic Reduction Mamdouh Eissa, Azza
More informationMicrostructures and Properties of Recycled Composites Particle Reinforced Iron Matrix Functionally Graded Materials Fabricated by Centrifugal Casting
Engineering, 00,, 360-366 doi:0.436/eng.00.504 Published Online May 00 (http://www.scirp.org/journal/eng) Microstructures and Properties of Recycled Composites Particle Reinforced Iron Matrix Functionally
More informationPREPARATION AND PROPERTIES OF Cr 2 N-Al 2 O 3 NANOCOMPOSITES
PREPARATION AND PROPERTIES OF Cr 2 N-Al 2 O 3 NANOCOMPOSITES Lian Gao 1 and Yaogang Li 2 1 State Key Lab of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese
More informationIMPROVING THERMO-MECHANICAL PROPERTIES OF TABULAR ALUMINA CASTABLES VIA USING NANO STRUCTURED COLLOIDAL SILICA
254 Nanomaterials: Applications and Properties (NAP-2011). Vol. 2, Part II IMPROVING THERMO-MECHANICAL PROPERTIES OF TABULAR ALUMINA CASTABLES VIA USING NANO STRUCTURED COLLOIDAL SILICA Alireza Souri *,
More informationEffects in Ductile Iron
Summary of Element Effects in Ductile Iron Rick Gundlach Element Materials Technology Wixom Insert Company Logo Here DIS Annual Meeting, June 7, 2012 Muskegon, Michigan Types of Alloying Elements Substitutional
More informationMSE 351 Engineering Ceramics I
Kwame Nkrumah University of Science & Technology, Kumasi, Ghana MSE 351 Engineering Ceramics I Ing. Anthony Andrews (PhD) Department of Materials Engineering Faculty of Mechanical and Chemical Engineering
More informationLow Carbon Steels, Collected in the Refining Treatment and Continuous Casting Stages
Vol. Materials 7, No. Research, 4, 2004Vol. 7, No. 4, 517-521, Study of 2004. the Nature of Non-Metallic Inclusions in Samples of Aluminum and Silicon Killed 2004 517 Study of the Nature of Non-Metallic
More informationSlag formation during high-temperature interactions between SiO 2 -containing refractories and iron melts with oxygen
KAPILASHRAMI, E., SAHAJWALLA, V., and SEETHARAMAN, S. Slag formation during high-temperature interactions between SiO 2 -containing refractories and iron melts with oxygen. VII International Conference
More informationMINERALOGICAL STUDY AND PROPERTIES OF MAGNESIA REFRACTORIES DERIVED FROM EVIAN MAGNESITE
ελτίο της Ελληνικής Γεωλογικής Εταιρίας τοµ. XXXVI, 2004 Πρακτικά 10 ου ιεθνούς Συνεδρίου, Θεσ/νίκη Απρίλιος 2004 Bulletin of the Geological Society of Greece vol. XXXVI, 2004 Proceedings of the 10 th
More informationMost castables and gun mixes. Better Refractories through NANOTECHNOLOGY
SPECIAL FOCUS REFRACTORIES A robot applies the colloidal silica bonded shotcrete material to a blast furnace. Better Refractories through NANOTECHNOLOGY by Michael Anderson, Senior Research Engineer, Magneco/
More informationEffects of Reducing Time on Metallization Degree of Carbothermic Reduction of Tall Pellets Bed
ISIJ International, Vol. 56 (2016), ISIJ No. International, 1 Vol. 56 (2016), No. 1, pp. 88 93 Effects of Reducing Time on Metallization Degree of Carbothermic Reduction of Tall Pellets Bed Xin JIANG,
More information