All types of NOMEX are sold in 610mm and 914mm roles (type 411) and in 4mm onwards wide strips.

Transcription

1 NOMEX Aramid Paper Structure NOMEX paper is a synthetic paper, composed of short fibers (bars) and small binding fibrous particles (fibrins) from an aromatic polyamide (aramidic), a polymer which is high-temperature resistant. During the manufacturing process, longer fibers (bar) tend to go in the direction of paper which is coming out of the machine. But there is a marked difference among the mechanical properties of NOMEX paper in machine direction and in transverse direction, and these properties are always expressed for both directions. Types of NOMEX paper There are five types of NOMEX paper for sale for electrical insulation, and two types for mechanical applications. The different types of NOMEX are differenciated among themselves according to the following: Both components are mixed in a water-based coating and are shaped as a continuous sheet by means of a machine which is quite large (density 0.3), with more than medium mechanical and electrical properties. It can be used in some applications in which a soft malleable material or one with impregnation properties is needed. Densification and internal binding are achieved by heating it at high temperatures, thus producing a mechanical resistant, flexible paper, with good electrical properties up to 220ºC. Availability All types of NOMEX are sold in 610mm and 914mm roles (type 411) and in 4mm onwards wide strips. Several thicknesses of up to 0.76mm can be obtained. General Specifications NOMEX 410 has been approved by Underwriters Laboratories for continual use as electrical insulator at 22ºC. Classification of flammability test is 94V-0, which means that this is a self-extinguishing, non-dripping material, and that no test tubes from a certain batch burn for more than ten seconds after having separated them from the ignition source in the vertical flame test. No flammability of NOMEX paper has motivated its adoption in cases in which there is a great fire risk. Limit oxygen index ranges from 0.27 to 0.28.

2 The following classification authorities have approved NOMEX as class C insulating material (122ºC): Underwriters Laboratories (USA) Lloyds Register of Shipping (UK) American Bureau of Shipping (USA) U.S. Military Spec. (MIL ) and as class H material (180ºC): VDE 0530 (Federal Republic of Germany) Germanischer Lloyd (Federal Republic of Germany) Det Norske Veritas (Norway) Registro Navale Italiano (Italy) Bureau Veritas (France) As NOMEX does not melt, it can resist short exposures to temperatures higher than 300ºC, with only minimal reductions of its electrical and mechanical properties. From 400ºC onwards, NOMEX starts degrading. Intensive tests in motorette systems according to IEEE 117 have shown that NOMEX paper is compatible with resins, wire enamels and electrical varnishes of phenolic, polyester, epoxy-based, polyamidic and silicone materials. Dielectric strength of all calendering NOMEX papers is high compared to the one of many other fibrous insulating materials (e.g. asbestos paper 3/5 Kv/mm, pressboard 19/15 kv/mm), and it is more suitable to resist electrical voltage generally found in electrical appliances (approx. 2 kv/mm). Even at 250ºC, NOMEX keeps almost 95% of its value at room temperature. Dielectric strength and dissipation factor at 1 Khz are low at room temperatures, and they only slightly rise to 225ºC. NOMEX volumetric and surface resistivity exceed OHM cm at room temperature. These values drop when temperature rises, as it is shown in the following figure; however, even at 250ºC they still exceed OHM cm.

3 Electrical Properties The following chart shows the important electrical properties of the different types of NOMEX paper at 50% relative humidity. Electrical characteristics of NOMEX paper at 50% relative humidity and at 23ºC. NOMEX Pressboard Thickness (mm) Dielectric strength (10 3 v/mm) T410 T411 T Dielectric constant at Hz Dissipation factor at 10 3 Hz Volumetric resistivity (OHM Cm)

4 Thickness Yield m 2 /kg m 2 /kg m 2 /kg m 2 /kg m 2 /kg m 2 /kg m 2 /kg m 2 /kg m 2 /kg m 2 /kg m 2 /kg Nomex Mylar Nomex (Pre-preg) This ternary composite material is subjected to impregnation with modified epoxy resin and taken to B-stage polymerization which under pressure and temperature conforms a hard product. After-polymerization resin has good adhesion to copper. It is used for general insulation of slots and inter-phase rotors and stators, it can be molded under pressure and temperature to conform any type of required geometrical figure. Technical Specifications Characteristics Unit Standard Specification Total Thickness mm DIN Tolerances mm DIN Yield g/m 2 DIN Tolerance g/m Dielectric strength kv/mm ASTM Impregnated NOMEX It is composed of aramid paper (Nomex 410) impregnated on both faces with B-stage modified epoxy resin, which under pressure and temperature conforms a hard product. After-polymerization resin has good adhesion to copper, permitting the creation of class F insulations. It is suitable for insulation between field coil winding layers of rotating machines. Technical Specifications

5 Properties Unit Standard Specifications Type - - N11 N16 N22 Nomex Thickness mm IEC Impregnated mm thickness IEC Nomex Weight g/m 2 IEC Resin content g/m 2 IEC Adhesion to copper N/mm 2 - Min 7.0 Min 7.0 Min 7.0 Unit: 610mm and 910mm wide coils. Weight: 35 and 55kg respectively. Note: It is cut in rolls of customized widths. Nomex and Mylar: Trademarks of DuPont