Welding Solutions for Advanced High-Strength Steels Menachem Kimchi 1
|
|
- Chad Cameron
- 6 years ago
- Views:
Transcription
1 Welding Solutions for Advanced High-Strength Steels Menachem Kimchi 1 A. Peer 1, Y. Lu 1, W. Zhang 1, C. Ji 2, Y. Park 2, T. Abke 3, S. Malcom 3 1 The Ohio State University, 2 Dong-Eui University, 3 Honda R&D Americas, Inc. Sponsored Work by: Honda R&D Americas, Inc. & WorldAutoSteel GDIS2017
2 Global Formability Diagram for Today s AHSS Grades 3
3 4 Issues in RSW of AHSS Hot Stamped Boron Steel Case Study 1: Coating Effects Parameter Optimization Technique Case Study 2: Failure Behavior Outline Initial Development of Criterion for Crash Simulation
4 Failure Modes on Resistance Spot Welds in AHSS Destructive inspection Chisel test Peel test Modes of failure Implied cooling rates (1000s of o C/s) Martensite formation FB PIF FIF 5
5 In AHSS applications, the acceptable strength can be achieved with PP or IF failure Button pulled without evidence of interfacial fracture Interfacial fracture with button pull Fracture Behaviors of RSW Partial thickness fracture with button pull Interfacial fracture with partial thickness fracture Partial thickness fracture with no button pull Full interfacial Fracture Interfacial fracture with button pull and partial thickness fracture No fusion 6
6 Presence of tensile stress Liquid Metal Embrittlement (LME) in AHSS Presence of liquid metals(low melting alloy from coating) Susceptible Microstructure(Austenite in TRIP,TWIP Steels) 7
7 Possible Solutions to Improve Failure Mode in AHSS Long weld time Pre/post pulsing Down sloping Short hold time Weld and temper Pulsation (0.87 mm, 980 MPa) 8 Dilution (AHSS to Mild Steel, HSLA) Increased minimum weld size
8 Case Study 1 Hot Stamped Boron Steel Coating Effects Parameter Optimization Technique C. Ji, M. Kimchi, Y. Kim and Y. Park, "The application of pulsed current in resistance spot welding of zn-coated hot-stamped boron steels," in Advances in Resistance Welding, Miami, FL,
9 Previous Research of Hot-Stamped Boron Steel Al-Si coated Hot stamped boron steel High speed Camera 10
10 Analysis of Hot-Stamped Boron Steel Coating Layer (Zn) 11
11 Pulsed Current Approach Based on Coating layer behavior & Contact area during Initial welding time Heat Generation Pattern & Nugget formation Nugget growth and Expulsion behavior 12
12 Welding Current (ka) Welding Current (ka) Heat generation pattern of 1 st Pulse 1 st Pulse Welding Time(Cy) Welding Time(Cy) 13
13 1 st Pulse Coating melting behavior & nugget formation of 1 st pulse 14
14 4 ka, 3 cycle 1 st Pulse - Results 8 ka, 1 cycle Molten Coating layer Molten B.M 15
15 Welding Current (ka) Welding Current (ka) 2 nd Pulse Comparison of heat generation pattern by 2 nd pulse 4kA 25cy 5.5kA 10cy 2m m 2m m Welding Time(Cy) Welding Time(Cy) 16
16 2 nd Pulse Comparison of nugget diameter and contact diameter by 2 nd a pulse b 17
17 Diameter (mm) 2 nd Pulse - Results Comparison of nugget diameter and contact diameter by 2 nd pulse 8 a b a b Welding time (cycle)
18 3 rd Pulse 19
19 Welding Current (ka) Button Diameter (mm) 3 rd Pulse Optimized welding conditions using three pulsed current steps kA-1Cy ka 2Cy 5.5kA- 12Cy 2Cy ka 15Cy Welding Time(Cy) Weld Current (ka) 20
20 Welding Current (ka) Optimized Conditions 8kA-1Cy 5.5kA- 12Cy ka 15Cy Welding Time(Cy) 21
21 Hot Stamped Boron Steel Failure Behavior Case Study 2 Initial Development of Criterion for Crash Simulation Andrea Peer, Ying Lu, Tim Abke, Menachem Kimchi, and Wei Zhang "Deformation Behaviors of Subcritical Heat Affected Zone of Ultra-high Strength Steel Resistance Spot Welds." in 9th International Seminar & Conference on Advances in Resistance Spot Welding. Miami, (3 2016). Paper No. 12 Ying Lu, Andrea Peer, Tim Abke, Menachem Kimchi, and Wei Zhang "Heat-Affected Zone Microstructure and Local Constitutive Behaviors of Resistance Spot Welded Hot-Stamped Steel." in Sheet Metal Welding Conference XVII. Livonia, ( ). 22
22 UHSS Performance Testing Approach Objective: Develop an understanding of the deformation and failure behavior of resistance spot welds of ultra-high strength steels 23
23 Metallographic Characterization The spot weld microstructure is highly inhomogeneous 24
24 Temperature Profile Martensitic Microstructure Base Metal Weld Nugget Coarse Grain HAZ Fine Grain HAZ Unique Microstructure Subcritical HAZ 25
25 Hardness Profile A ring of softened material surrounds the weld nugget Subcritical Heat Affected Zone (SCHAZ) 0.7 mm Usibor BM & WM: > 500 HV SCHAZ: ~300 HV 26
26 Ncorr Post-Processing Extended Stress Strain Curve Constitutive Behavior Development Example of SCHAZ tensile test. Virtual extensometer of 2 mm used to extract data. 27 YS (MPa) UTS (MPa) Base Metal CGHAZ SCHAZ
27 Single-Sided Wedge Testing Observe the localized deformation with the aid of DIC 28
28 Weld Size Results Interfacial Weld Metal WM/CGHAZ SCHAZ 4 t minimum nugget diameter 29 5 t minimum nugget diameter No interfacial failure when weld diameter > 5.8 mm No defined trend for non-if failure mode
29 Incorporating softened SCHAZ properties is essential to predict the localized deformation FEA Comparison Wedge Test FEA simulation with SCHAZ flow FEA Small simulation Weld with SCHAZ Large Weld flow DIC results 30 No strain localization without incorporating SCHAZ flow stress Effect of nugget size on local deformation Small weld (5.5 mm): Concentrated on notch Large weld (7.00 mm): Concentrated on SCHAZ
30 As-welded Lap Shear Difficult to observe localized deformation Failure in Hot Stamped Boron Steel Microstructurespecific properties needed to simulate actual failure behavior 31
31 Three common problems associated with welding AHSS: Narrow Current Range: Summary By implementing the proper welding schedule, the weldability window can be broadened. More complex welding schedules can allow for more control over heat generation and current density, thus minimizing the possibility of expulsion to grow the nugget further. Hardness Values: The increased hardness values seen in AHSS weld nuggets can induce interfacial failure. Acceptable strengths can be achieved with interfacial failure. Nonhomogeneous Microstructures: The nonhomogeneous microstructures seen in AHSS welds cannot be universally classified as a beneficial or detrimental effect of welding. Solutions need to be made on a case by case study and cannot be blanketed over all advanced high-strength steels. Different solutions will need to be taken for different grades as well as different stack-up configurations and sheet thicknesses. 32
32 For More Information Menachem Kimchi The Ohio State University Andrea Peer The Ohio State University
33 Base Metal Characterization Unaffected Base Metal: Fully martensitic microstructure with fine martensite laths Hot stamping heat treatment prior to welding Heated above the austenitization temperature (Ac3) Austenite completely transformed into martensite, which is supersaturated in carbon 34
34 Weld Metal Characterization Solidified Weld Metal: Fully martensitic microstructure with fine martensite laths Molten weld nugget solidifies rapidly during welding Austenite completely transformed into martensite, which is supersaturated in carbon 35
35 CGHAZ Characterization Coarse-Grained Heat Affected Zone: Fully martensitic microstructure with fine martensite laths Heated above the austenitization temperature (Ac3) for an extended period of time Large austenite grains completely transform into martensite 36
36 SCHAZ Characterization Subcritical Heat Affected Zone: Ferrite grains and cementite precipitates Ferrite Cementit e Cementite precipitates decorate along the prior austenite grain boundaries and along the inter-lath regions of martensite Over-tempering of martensite decomposition of metastable martensite into ferrite and cementite. Heated to peak temperatures below 37
37 INPUT Y. Adonyi. Heat-Affected Zone Characterization by Physical Simulations, Welding Journal, Microstructure Simulation SCHAZ span < 1 mm CGHAZ span < 0.6 mm Very difficult to measure local mechanical properties of this region Gleeble Simulation: Creates a bulk homogeneous SCHAZ microstructure to extract mechanical property data Heating Rate Holding Time Holding Temperature Cooling Rate CGHAZ SCHAZ
38 Weld Size Study Objective: Determine effect of weld size on failure mode. 39 Weld Sizes: Below Min ka Small ka Medium ka Large ka Near Exp ka
39 Interfacial Failure Weld Metal SCHAZ Peak Load Failure Peak Load End of Test Peak Load End of Test
40 Cooling Rate (C o /s) Key Challenges with AHSS - Joining Selection of Joining Technique Body-in-White Joining Processes Resistance spot Projection welding GMAW MIG brazing Laser welding (TWB) Mechanical fastening Magnetic pulse welding Deformation resistance welding IF AKDQ M1400 TRIP 600 DP 980 DP 600 TRIP 800 DP 780 GMAW LBW RMSW RSW Sheet Thickness (mm)
41 Cooling Rate (C o /s) Key Challenges with AHSS - Joining Selection of Joining Technique Body-in-White Joining Processes Resistance spot Projection welding GMAW MIG brazing Laser welding (TWB) Mechanical fastening Magnetic pulse welding Deformation resistance welding IF AKDQ M1400 TRIP 600 DP 980 DP 600 TRIP 800 DP 780 GMAW LBW RMSW RSW Sheet Thickness (mm)
42
Performance Testing and Modeling of Ultra- High Strength Steel and Complex Stack-Up Resistance Spot Welds
Performance Testing and Modeling of Ultra- High Strength Steel and Complex Stack-Up Resistance Spot Welds THESIS Presented in Partial Fulfillment of the Requirements for the Degree Master of Science in
More informationCross Tension Strength Improvement for AHSS Using Post-Weld Heat Treatment
Cross Tension Strength Improvement for AHSS Using Post-Weld Heat Treatment Stephen Kelley (Lead Engineer) Hassan Ghassemi-Armaki (Senior Research Engineer) ArcelorMittal Global R&D E. Chicago May 11, 2016
More informationResistance Spot Welding of Coated High Strength Dual Phase Steels
Resistance Spot Welding of Coated High Strength Dual Phase Steels Murali D. Tumuluru United States Steel Corporation Research and Technology Center Monroeville, Pa Topics Introduction Dual Phase Steels
More informationINFLUENCES OF SECONDARY PULSE ON RESISTANCE SPOT WELDING OF HOT FORMING STEELS. Jeff Hou
2014 International Symposium on Advances in Resistance Welding, Atlanta INFLUENCES OF SECONDARY PULSE ON RESISTANCE SPOT WELDING OF HOT FORMING STEELS Jeff Hou D.Saha, S. Nayak, N.Zhou, A.Gerlich (UofWaterloo)
More informationGuidelines for the Manufacture of Advanced High-Strength Steel Vehicle Applications. Dr. Chris Lahaije, Sascha Sikora Aachen,
Guidelines for the Manufacture of Advanced High-Strength Steel Vehicle Applications Dr. Chris Lahaije, Sascha Sikora Aachen, 2014-09-24 09 24 WorldAutoSteel A t Automotive ti Group G off the th World W
More informationC Mn Si P S Mo Cr
ANALYSIS OF WELDABILITY OF DUAL-PHASE STEEL SHEETS USED IN CAR BODY PRODUCTION LUBOS KASCAK, EMIL SPISAK, RENE KUBIK Technical University of Kosice, Faculty of Mechanical Engineering, Institute of Technology
More informationWeldability and Performance of GMAW Joints of Advanced High- Strength Steels (AHSS)
Weldability and Performance of GMAW Joints of Advanced High- Strength Steels (AHSS) Zhili Feng *, John Chang **, Cindy Jiang *** and Min Kuo **** * Oak Ridge National Laboratory ** Ford Motor Company ***
More informationInfluence of Electrode and Welding Parameters During Resistance Spot Welding of Hot- Stamped Ultra-High Strength Steel Sheets.
International Symposium on Advances in Resistance Welding April 28-30, 2014 / Atlanta Influence of Electrode and Welding Parameters During Resistance Spot Welding of Hot- Stamped Ultra-High Strength Steel
More informationWeldability of AHSS. Dr. Sree Harsha Lalam, CWEng. Mittal Steel Company. w w w. a u t o s t e e l. o r g
Weldability of AHSS Dr. Sree Harsha Lalam, CWEng. Mittal Steel Company Overview AHS Steels & Weld Joint Spot welding Spot Welding Window Effect of Coating AC vs. Mid-Frequency DC Weldmetal Hardness Mechanical
More informationTECHNIQUES FOR IMPROVING THE WELDABILITY OF TRIP STEEL USING RESISTANCE SPOT WELDING. G Shi and S A Westgate TWI Ltd, Cambridge, United Kingdom
TECHNIQUES FOR IMPROVING THE WELDABILITY OF TRIP STEEL USING RESISTANCE SPOT WELDING G Shi and S A Westgate TWI Ltd, Cambridge, United Kingdom ABSTRACT High strength steels (UTS >6N/mm 2 ) are increasingly
More informationResistance Spot Welding and In-Process Heat Treatment of Hot Stamped Boron Steel
Resistance Spot Welding and In-Process Heat Treatment of Hot Stamped Boron Steel by Jeff Shao-Chun Hou A thesis presented to the University of Waterloo in fulfillment of the thesis requirement for the
More informationMicrostructure Evolution and Properties of Resistance Spot Welding of Press-hardened Steels
Microstructure Evolution and Properties of Resistance Spot Welding of Press-hardened Steels H. L. Yi & H. L. Cai Northeastern University State Key Lab of Rolling and Automation Background PHS: Press-hardening
More informationAHS Steels for Automotive Parts
20-21June 2013 BITEC, Bangkok -Thailand AHS Steels for Automotive Parts Asst. Prof. Vitoon Uthaisangsuk, Dr.-Ing. Department of Mechanical Engineering, Faculty of Engineering King Mongkut s University
More informationRobust Schedules for Spot Welding Zinc Coated Advanced High Strength Automotive Steels
Robust Schedules for Spot Welding Zinc Coated Advanced High Strength Automotive Steels Gajendra Tawade (Ryerson University) Gary Boudreau (Dofasco Inc. Canada) 1 Outline Objective Introduction Experimental
More informationWeldability Evaluation and Microstructure Analysis of Resistance Spot Welded High Manganese Steel in Automotive Application
Weldability Evaluation and Microstructure Analysis of Resistance Spot Welded High Manganese Steel in Automotive Application Dulal Chandra Saha, Chul Young Choi, Sangho Han, Kwang Geun Chin, Ildong Choi
More informationImproving Electrode Life for RSW of Coated Advanced High Strength Steel
Improving Electrode Life for RSW of Coated Advanced High Strength Steel D. Huh, Z. Jiao, Y. Zhou Centre for Advanced Materials Joining, University of Waterloo, 200 University Ave. W, Waterloo, ON N2L 3G1,
More informationDynamic Considerations in Prediction of Fracture of Ultra High-Strength Steel During Crash
Dynamic Considerations in Prediction of Fracture of Ultra High-Strength Steel During Crash Presenter: Michael Worswick, uwaterloo GDIS2018 Co-Authors A. Abedini, M. Nemcko, T. Rahmaan, N. Pathak, C. O
More informationSteels for cold stamping -Fortiform
Automotive Worldwide Steels for cold stamping -Fortiform Extract from the product catalogue -European edition Note: Information contained in this catalogue is subject to change. Please contact our sales
More informationLASER BEAM WELDING OF QUENCHED AND TEMPERED ASTM A 517 GR.B STEEL
LASER BEAM WELDING OF QUENCHED AND TEMPERED ASTM A 517 GR.B STEEL S. Missori*, G.Costanza*, E. Tata*, A. Sili** *University of Roma-Tor Vergata, ** University of Messina ABSTRACT Quenched and tempered
More informationWeldability and Liquation Cracking Characteristics on Resistance-Spot-Welded High-Mn Austenitic Steel
Weldability and Liquation Cracking Characteristics on Resistance-Spot-Welded High-Mn Austenitic Steel Dulal Chandra Saha,Yeong-Do Park Department of Advanced Materials Engineering, Graduate School of Engineering,
More informationIntroduction. 1. Development of microstructure controlled Hi- Ten
Improvement of fuel economy, crash worthiness and passenger safety are gaining increasing attention in the automobile industry. Kobe Steel has developed and has continued to produce a variety of high strength
More informationEffects of GMAW conditions on the tensile properties of hot rolled Complex Phase 780 steel. Carlos Cardenas Luis Hernandez Jaime Taha-Tijerina
Effects of GMAW conditions on the tensile properties of hot rolled Complex Phase 780 steel Carlos Cardenas Luis Hernandez Jaime Taha-Tijerina OUTLINE 1. Introduction 2. Material Description 3. Experimental
More informationUnderstanding Resistance Spot Welding of Advanced High-Strength Steels
Understanding Resistance Spot Welding of Advanced High-Strength Steels BY V. H. LÓPEZ-CORTÉZ AND F. A. REYES-VALDÉS Experiments were conducted to better understand weldability issues when joining martensitic-type
More informationSteels for hot stamping
Automotive Worldwide Steels for hot stamping Extract from the product catalogue -European edition Note: Information contained in this catalogue is subject to change. Please contact our sales team whenever
More informationExpulsion Reduction in Resistance Spot Welding by Controlling of welding Current Waveform
Available online at www.sciencedirect.com Procedia Engineering 10 (2011) 2775 2781 International conference on the mechanical behavior of materials Expulsion Reduction in Resistance Spot Welding by Controlling
More informationCharacteristics of 1180MPa Grade Cold-rolled Steel Sheets with Excellent Formability
Characteristics of 1180MPa Grade Cold-rolled Steel Sheets with Excellent Formability Tadao MURATA *1, Sae HAMAMOTO *1, Yukihiro UTSUMI *1, Takayuki YAMANO *2, Dr. Yuichi FUTAMURA *3, Takayuki KIMURA *4
More informationEvaluation of weldability for resistance spot welded single-lap joint between GA780DP and hot-stamped 22MnB5 steel sheets
Journal of Mechanical Science and Technology 25 (6) (2011) 1543~1550 www.springerlink.com/content/1738-494x DOI 10.1007/s12206-011-0408-x Evaluation of weldability for resistance spot welded single-lap
More informationIntroduction. 1. Concept of microstructure control
A series of 590-980MPa grade hot-dip galvannealed steel sheets has been developed in order to improve the formability of automotive body frame parts, such as lower pillars. These are either DP or TRIP-aided
More informationSteels for hot stamping -Usibor and Ductibor
Automotive Worldwide Steels for hot stamping -Usibor and Ductibor Extract from the product catalogue -European edition Note: Information contained in this catalogue is subject to change. Please contact
More informationThermo-mechanical forming analysis and mapping of material properties in hot stamped component with tailored material properties
Thermo-mechanical forming analysis and mapping of material properties in hot stamped component with tailored material properties Greger Bergman, Daniel Berglund and Kenneth Isaksson 2014-08-21 Copyright
More informationQuasi Static Spot Weld Strength of Advanced High Strength Sheet Steels
Quasi Static Spot Weld Strength of Advanced High Strength Sheet Steels This study highlights the spot weld strength in tension shear and cross tension loading modes, and HAZ strength as a function of base
More informationTable 1 El. Steel Category TS grade MPa MPa 980MPa GA980Y 724 1,022 Developed steel Galvannealed 780MPa GA780Y MPa CR980Y 690 1,030
With growing awareness of global environmental issues, automobile manufacturers are striving to reduce automotive weight and thus decrease exhaust emissions. Concurrently, automakers are pursuing higher
More informationAnalysis of Spot Weld Growth on Mild and Stainless Steel
SUPPLEMENT TO THE WELDING JOURNAL, AUGUST 2011 Sponsored by the American Welding Society and the Welding Research Council Analysis of Spot Weld Growth on Mild and Stainless Steel Nugget growth by varying
More informationRELATIONSHIPS BETWEEN MICROSTRUCTURE AND MECHANICAL PROPERTIES OF AUTOMOTIVE SHEET STEELS
RELATIONSHIPS BETWEEN MICROSTRUCTURE AND MECHANICAL PROPERTIES OF AUTOMOTIVE SHEET STEELS Adam Grajcar SILESIAN UNIVERSITY OF TECHNOLOGY Faculty of Mechanical Engineering SILESIAN UNIVERSITY OF TECHNOLOGY
More informationVirtual Prototyping of Lightweight Designs Made with Cold and Hot Formed Tailored Solutions
2 nd World Congress on Integrated Computational Materials Engineering Edited by: Mei Li, Carelyn Campbell, Katsuyo Thornton, Elizabeth Holm, and Peter Gumbsch TMS (The Minerals, Metals & Materials Society),
More informationEffects of Ar and He on Microstructures and Properties of Laser Welded 800MPa TRIP Steel
Effects of Ar and He on Microstructures and Properties of Laser Welded 800MPa TRIP Steel Wen-Quan Wang 1,, Shu-Cheng Dong 1, Fan Jiang 1, and Ming Cao 1 1 School of Material Science and Engineering, Jilin
More informationw w w. a u t o s t e e l. o r g
Great Designs in Steel is Sponsored by: ArcelorMittal Dofasco, ArcelorMittal USA, Nucor Corporation, Severstal North America, Inc. and United States Steel Corporation A Comparative Study of Joint Efficiency
More informationLaser welding of modern automotive high strength steels
Laser welding of modern automotive high strength steels Hardy Mohrbacher Niobium Products Company GmbH, Steinstrasse 28, D-40210 Düsseldorf, Germany Abstract: The paper demonstrates the correlation between
More informationLaser welding of Al-Si coated hot stamping steel
Available online at www.sciencedirect.com Procedia Engineering 10 (2011) 2226 2231 ICM11 Laser welding of Al-Si coated hot stamping steel C. Kim a*, M. J. Kang a, Y. D. Park b a Korea Institute of Industrial
More informationCost Savings for Rocker Reinforcement through Material Conversion
Cost Savings for Rocker Reinforcement through Material Conversion J. Cheriyan R. Bhatnagar & Dr. S.H. Lalam. Outline Project Objective Martensitic Steel Overview Spot Weld Verification Summary Project
More informationA Comparative Study of Joint Efficiency for AHSS
A Comparative Study of Joint Efficiency for AHSS John Bohr A/SP Joining Technologies Team MISSION STATEMENT The Auto/Steel Partnership (A/SP) leverages the resources of the automotive, steel and related
More informationMECHANICAL PROPERTIES OF ALUMINUM WELDS FOR AUTOMOTIVE STRUCTURAL APPLICATIONS
MECHANICAL PROPERTIES OF ALUMINUM WELDS FOR AUTOMOTIVE STRUCTURAL APPLICATIONS Jennifer Hyde Supervisor: Dr. McDermid MATLS 701 Seminar Feb 17, 2012 Outline 2 Motivation Background/Literature Review Project
More informationResistance Welding. Simulation Software
Saving Time and Money with Resistance Welding Simulation Software Software takes into account various strengths and limitations of welding processes and materials to predict optimum welding conditions
More informationEffect of Welding Current on the Mechanical Response of Resistance Spot Welds of Unequal Thickness Steel Sheets in Tensile-Shear Loading Condition
Effect of Welding Current on the Mechanical Response of Resistance Spot Welds of Unequal Thickness Steel Sheets in Tensile-Shear Loading Condition M. Pouranvari Materials and Metallurgical Engineering
More informationTempering of hot-formed steel using induction heating. Master of Science Thesis OLOF HEDEGÄRD MARTIN ÅSLUND
Tempering of hot-formed steel using induction heating Master of Science Thesis OLOF HEDEGÄRD MARTIN ÅSLUND Department of Materials and Manufacturing Technology CHALMERS UNIVERSITY OF TECHNOLOGY Gothenburg,
More informationMechanical Attachment of Fasteners to UHSS Materials
Mechanical Attachment of Fasteners to UHSS Materials Rob Edwards PROFIL System Incorporated Agenda Mechanical Attachment of Fasteners to UHSS Materials 1. Mechanical Fastener Basics 2. Evolution: Market
More informationManufacturing (Bending-Unbending-Stretching) Effects on AHSS Fracture Strain
Manufacturing (Bending-Unbending-Stretching) Effects on AHSS Fracture Strain Hong Zhu ArcelorMittal Global R & D - East Chicago Crush Distance (mm) Background 300 250 200 150 100 50 300 600 900 1200 1500
More informationJoining as an Enabling Technology for Mainstream Vehicle Lightweighting
Joining as an Enabling Technology for Mainstream Vehicle Lightweighting March 17, 2015 Jerry E. Gould LIFT: Technology Pillar Leader, Joining and Assembly EWI: Technology Leader, Resistance and Solid State
More informationEffects of Welding Schedules on Resistance Spot Welding of DP600 Steel
, pp. 2375 2379 Effects of Welding Schedules on Resistance Spot Welding of DP600 Steel Xiaodong WAN, 1) * Yuanxun WANG 1,2) and Peng ZHANG 1) 1) Department of Mechanics, Huazhong University of Science
More informationA TOUGHNESS STUDY OF THE WELD HEAT AFFECTED ZONE OF A MODIFIED 9Cr-1Mo STEEL
ICF100358OR A TOUGHNESS STUDY OF THE WELD HEAT AFFECTED ZONE OF A MODIFIED 9Cr-1Mo STEEL A. Moitra, K. Laha, P.R. Sreenivasan and S. L. Mannan Materials Development Group Indira Gandhi Centre for Atomic
More informationEffects of Welding Procedures on Resistance Projection Welding of Nuts to Sheets
ISIJ International, Advance Publication by J-STAGE ISIJ International, ISIJ International, J-Stage Advanced Advance ISIJ Publication International, Publication, ISIJ International, by DOI: J-STAGE, Advance
More informationParameter optimization of dissimilar resistance spot welding on ultra-high strength hot-stamped steel and mild steel by numerical simulation
Available online at www.amse.org.cn Acta Metall. Sin.(Engl. Lett.)Vol.25 No.6 pp487-498 December 2012 Parameter optimization of dissimilar resistance spot welding on ultra-high strength hot-stamped steel
More informationSteel Sheets for Highly Productive Hot Stamping
Steel Sheets for Highly Productive Hot Stamping Sae HAMAMOTO *1, Hiroyuki OMORI *1, Tatsuya ASAI *1, Naoki MIZUTA *2, Noriyuki JIMBO *2, Takayuki YAMANO *2 *1 Sheet Products Development Dept., Research
More informationMicrostructure and Mechanical Properties of Resistance Spot Welded Advanced High Strength Steels
Materials Transactions, Vol. 49, No. 7 (2008) pp. 1629 to 1637 #2008 The Japan Institute of Metals Microstructure and Mechanical Properties of Resistance Spot Welded Advanced High Strength Steels M. I.
More informationInvestigation of Resistance Spot Weld Failure in Tailored Hot Stamped Assemblies
Investigation of Resistance Spot Weld Failure in Tailored Hot Stamped Assemblies by Cameron O Keeffe A thesis presented to the University Of Waterloo in fulfillment of the thesis requirement for the degree
More informationResistance Spot Welding Characteristic of Ferrite-Martensite DP600 Dual Phase Advanced High Strength Steel-Part III: Mechanical Properties
World Applied Sciences Journal 15 (11): 1521-1526, 2011 ISSN 1818-4952 IDOSI Publications, 2011 Resistance Spot Welding Characteristic of Ferrite-Martensite DP600 Dual Phase Advanced High Strength Steel-Part
More informationCHAPTER 1 AN INTRODUCTION TO THE WELDABILITY OF 3CR12
CHAPTER 1 AN INTRODUCTION TO THE WELDABILITY OF 3CR12 1. INTRODUCTION The main purpose of this first chapter is to outline three aspects of the weldability of a 12 percent chromium steel, 3CR12, on which
More informationMechanical joining as an alternative method to resistance spot welding and riveting
Mechanical joining as an alternative method to resistance spot welding and riveting Ľuboš Kaščák Department of Computer Support of Technology Technical University of Košice Košice, Slovakia lubos.kascak@tuke.sk
More informationExperimental Study of Tensile Test in Resistance Spot Welding Process
1228 Experimental Study of Tensile Test in Resistance Spot Welding Process Abstract Resistance spot welding (RSW) is a widely used joining process for fabricating sheet metal assemblies in automobile industry.in
More informationContent MS-W. Areas of application. Product information for martensitic-phase steels
Steel MS-W Product information for martensitic-phase steels Issue: December 2016, version 0 Overview of steel grades 50 Hot-rolled steel flat products Recommended applications Content 01 Areas of application
More informationResistance Spot Welding of AA5052 Sheet Metal of Dissimilar Thickness
IOP Conference Series: Materials Science and Engineering PAPER OPEN ACCESS Resistance Spot Welding of AA5052 Sheet Metal of Dissimilar Thickness To cite this article: N A Mat Din et al 2016 IOP Conf. Ser.:
More informationApplication of Forced Freeze during Flash-Butt Welding for Coil Joining of Advanced High Strength Steels (AHSS)
Application of Forced Freeze during Flash-Butt Welding for Coil Joining of Advanced High Strength Steels (AHSS) Michael Prokop * and Jerry E. Gould ** * Taylor-Winfield Technologies ** EWI Abstract Recent
More informationAdvances in steel and Al alloy materials High strength (HSS) & Advanced high strength steel (AHSS)
Advances in steel and Al alloy materials High strength (HSS) & Advanced high strength steel (AHSS) Low strength steel HSS UHSS Development of new steel grade materials that can withstand more strength
More informationAHSS Coating Issues and Concerns. Introduction
AHSS Coating Issues and Concerns Gary Dallin GalvInfo Center Introduction Compared to HSS, AHSS grades use higher amounts of alloys such as Mn, Si, Mo, and C - many of which have a higher affinity for
More informationAWS D8.7M:2005 An American National Standard. Recommended Practices for Automotive Weld Quality Resistance Spot Welding
An American National Standard Recommended Practices for Automotive Weld Quality Resistance Spot Welding Key Words Resistance spot welding, weld quality, destructive test, nondestructive test AWS D8.7M:2005
More informationMechanical Performance of Resistance Spot Welding Joint of Dissimilar High Strength Steels Shang-gong ZHOU, Kai-wei LIU, Mian WANG and Jiang-wei REN *
2016 International Conference on Advanced Materials Science and Technology (AMST 2016) ISBN: 978-1-60595-397-7 Mechanical Performance of Resistance Spot Welding Joint of Dissimilar High Strength Steels
More informationWELDING RESEARCH Predicting Resistance Spot Weld Failure Modes in Shear Tension Tests of Advanced High-Strength Automotive Steels
Predicting Resistance Spot Weld Failure Modes in Shear Tension Tests of Advanced High-Strength Automotive Steels To judge the quality of resistance spot welds in advanced high-strength steels, the load-bearing
More informationWidening the Welding Lobe of Advanced High Strength Steels in the Resistance Spot Welding Process
Strength Steels in the Resistance Spot Welding Process Nigel Scotchmer Huys Industries Limited nscotchmer@huysindustries.com Abstract The intention of this project was to examine the resistance spot welding
More informationULSAB-Advanced Vehicle Concepts ULSAB-AVC
ULSAB-Advanced Vehicle Concepts ULSAB-AVC Jody Shaw Technical Industry Manager United States Steel Corporation February 19, 2003 Great Designs in Steel ULSAB-AVC U.S. Partnership for a New Generation of
More informationMechanisms for Boron Effect on Microstructure and Creep Strength of Ferritic Power Plant Steels
Mechanisms for Boron Effect on Microstructure and Creep Strength of Ferritic Power Plant Steels - Boron Metallurgy of Ferritic Power Plant Steels - Fujio Abe, M Tabuchi and S Tsukamoto National Institute
More informationInfluence of welding current in resistance spot welding on the properties of Zn coated steel DX51D
Songklanakarin J. Sci. Technol. 38 (3), 237-242, May - Jun. 2016 http://www.sjst.psu.ac.th Original Article Influence of welding current in resistance spot welding on the properties of Zn coated steel
More informationAnalysis of Fracture Mode of Galvanized Low Carbon Steel Resistance Spot Welds
Analysis of Fracture Mode of Galvanized Low Carbon Steel Resistance Spot Welds M. Pouranvari Materials and Metallurgical Engineering Department, Dezful Branch, Islamic Azad University, Dezful, Iran mpouranvari@yahoo.com
More informationEffect of the plasma arc welding procedure on mechanical properties of DP700 steel
Available online at www.sciencedirect.com Procedia Materials Science 1 (2012 ) 50 57 11 th International Congress on Metallurgy & Materials SAM/CONAMET 2011. Effect of the plasma arc welding procedure
More informationJoining of Dissimilar Automotive Materials
Joining of Dissimilar Automotive Materials P.K. Mallick William E. Stirton Professor of Mechanical Engineering Director, Center for Lighweighting Automotive Materials and Processing University of Michigan-Dearborn
More informationAdhesively Bonded Steel Structures
Adhesively Bonded Steel Structures by Man-Shin Tan Nozhan Sharifian Diploma work No. 52/2011 at Department of Materials and Manufacturing Technology CHALMERS UNIVERSITY OF TECHNOLOGY Göteborg, Sweden Diploma
More informationTHE INFLUENCE OF THERMAL LOAD ON PROPERTIES OF HETEROGENEOUS JOINTS BETWEEN STEEL AND ALUMINIUM ALLOY A. FRANC 1, J. TESAŘ 2
CO 2 /Km [g] THE INFLUENCE OF THERMAL LOAD ON PROPERTIES OF HETEROGENEOUS JOINTS BETWEEN STEEL AND ALUMINIUM ALLOY A. FRANC 1, J. TESAŘ 2 1 Faculty of Mechanical Engineering, University of West Bohemia,
More informationDevelopment of bimodal grain structures in microalloyed steels:
Development of bimodal grain structures in microalloyed steels: Niobium and titanium are added to high strength low alloy (HSLA) steels to provide grain boundary pinning precipitates to help produce the
More informationAN IMPROVEMENT OF CLOSED DIE FORGING OF HIGH STRENGTH STEEL PRODUCTS AND A STUDY OF ITS WELDING SUITABILITY
AN IMPROVEMENT OF CLOSED DIE FORGING OF HIGH STRENGTH STEEL PRODUCTS AND A STUDY OF ITS WELDING SUITABILITY Ing. Khodr Ibrahim, West Bohemia University, Univerzitni 8, 306 14 Pilsen Czech Republic ABSTRACT
More informationFULL SET OF INNOVATIVE TOOLS FOR THE PREDICTION OF LASER WELDED BLANK FORMABILITY IN SIMULATION
FULL SET OF INNOVATIVE TOOLS FOR THE PREDICTION OF LASER WELDED BLANK FORMABILITY IN SIMULATION Daniel Duque Múnera (a) ArcelorMittal Noble International Sadok Gaied (a)(c), Fabrice Pinard (b), Francis
More informationGAS METAL ARC WELDING OF ADVANCED HIGH STRENGTH STEEL DEVELOPMENTS FOR OPTIMIZED WELD CONTROL AND IMPROVED WELD QUALITY
GAS METAL ARC WELDING OF ADVANCED HIGH STRENGTH STEEL DEVELOPMENTS FOR OPTIMIZED WELD CONTROL AND IMPROVED WELD QUALITY Adrian N. A. Elliott Advanced Body Construction Manufacturing & Processes Department
More informationWELDABILITY EVALUATION OF API 5L X52 STEEL AND HEAT-AFFECTED ZONE (HAZ) SIMULATION USING GLEEBLE
WELDABILITY EVALUATION OF API 5L X52 STEEL AND HEAT-AFFECTED ZONE (HAZ) SIMULATION USING GLEEBLE *Ashish Kumar Mechanical department ITS Engineering College Gr. Noida *Corresponding author: ashuatcoer@gmail.com
More informationAn Efficient Methodology for Fracture Characterization and Prediction of DP980 Steels for Crash Application GDIS2018
An Efficient Methodology for Fracture Characterization and Prediction of DP980 Steels for Crash Application University of Waterloo: Cliff Butcher Honda Research America: Jim Dykeman, Skye Malcolm GDIS2018
More informationStudy on Microstructure and Mechanical Properties of Titanium-bearing High-strength Hot-rolled Steels for Enamelling
Study on Microstructure and Mechanical Properties of Titanium-bearing High-strength Hot-rolled Steels for Enamelling Quanshe Sun (1), Faliang Jv (2), Weizhong Jiang (3) (1) R & D Center, Baoshan Iron and
More informationTechnical Transfer Dispatch #6
ULSAB-AVC Consortium Appendix III Rev d 6 June 2001 Technical Transfer Dispatch #6 ULSAB-AVC Body Structure Materials May 2001 FOREWORD 1.0 Introduction 2.0 Materials Selected for the ULSAB-AVC Body Structure
More informationlow susceptibility to delayed fracture. High strength steels are known to be prone to delayed fracture.
Stricter requirements are imposed on collision safety by newly revised regulations such as Federal Motor Vehicle Safety Standard (FMVSS) No.214 and Insurance Institute for Highway Safety (IIHS) 1). To
More informationDYNAMIC MATERIAL PROPERTIES OF THE HEAT-AFFECTED ZONE (HAZ) IN RESISTANCE SPOT WELDING
International Journal of Modern Physics B Vol. 22, Nos. 31 & 32 (28) 58 586 World Scientific Publishing Company DYNAMIC MATERIAL PROPERTIES OF THE HEAT-AFFECTED ZONE (HAZ) IN RESISTANCE SPOT WELDING JI-WOONG
More informationValidating NEXMET AHSS as a Lightweight Steel Solution
Validating NEXMET AHSS as a Lightweight Steel Solution Scott Stevens AK Steel Corporation GDIS2018 Agenda Recap of NEXMET 1000 & 1200 AHSS Qualification & Characterization Applications under development
More informationExperimental and numerical analysis of resistance spot welded joints on DP600 sheets
Experimental and numerical analysis of resistance spot welded joints on DP600 sheets Z. Bézi, B. Baptiszta, S. Szávai Research Fellow, Bay Zoltán Nonprofit Ltd. for Applied Research, Department of Structural
More informationBasic Welding Metallurgy of Structural Steels Explained in Everyday Terms.
Basic Welding Metallurgy of Structural Steels Explained in Everyday Terms. Prepared by J. Manning September 27, 2017 Modern controlled rolled carbon manganese or micro alloyed steels derive their strength
More informationSteels for Cold Formed Parts without Heat Treatment
Steels for Cold Formed Parts without Heat Treatment Sidenor Cold Forging Pre-Treated Steels Conventional Process Hot Rolling 2 Spheroidizing Annealing Cold Heading Quenching & Tempering Straightening Fastener
More informationSecond Pulse Current in Resistance Spot Welded TRIP Steel Effects on the Microstructure and Mechanical Behavior
Second Pulse Current in Resistance Spot Welded TRIP Steel Effects on the Microstructure and Mechanical Behavior The second pulse current improved mechanical properties when the fusion zone microstructure
More informationMartensitic Steel Sheets of 1300 and 1500MPa Grades
Martensitic Steel Sheets of 1300 and 1500MPa Grades Yukihiro UTSUMI *1, Atsuhiro SHIRAKI *1, Sae HAMAMOTO *1, Junichiro KINUGASA *2 *1 Sheet Products Development Dept., Research & Development Lab., Iron
More informationMicrostructures and Properties of Ultra-high Strength Steel by Laser Welding
, pp. 1126 1131 Microstructures and Properties of Ultra-high Strength Steel by Laser Welding Zhengwei GU, 1) Sibin YU, 1) Lijun HAN, 2) Jia MENG, 1) Hong XU 1) and Zhenglin ZHANG 1) 1) Department of Materials
More informationROLLING OF ADVANCED HIGH STRENGTH STEELS FOR AUTOMOTIVE INDUSTRY. Michał DZIEDZIC, Stanisław TURCZYN
ROLLING OF ADVANCED HIGH STRENGTH STEELS FOR AUTOMOTIVE INDUSTRY Michał DZIEDZIC, Stanisław TURCZYN Abstract Akademia Górniczo-Hutnicza, al. Mickiewicza 30, 30-059 Kraków, Poland dziedzic@metal.agh.edu.pl,
More informationMTLS 4L04 Steel Section. Lecture 6
MTLS 4L04 Steel Section Lecture 6 Tempering of Martensite To get around the problem of the brittleness of the Martensite, Martensite is heat treated at elevated temperatures (200-700 C) to precipitate
More informationCase Study: Design of Bainitic Steels
Materials Science & Metallurgy Part II Course C9, Alloys, H. K. D. H. Bhadeshia Case Study: Design of Bainitic Steels Bainite Summarised Bainite is a non lamellar aggregate of carbides and plate shaped
More informationContent. CP-W and CP-K. Areas of application. Product information for complex-phase steels
Steel CP-W and CP-K Product information for complex-phase steels Issue: January 2017, version 2 Overview of steel grades 50 Hot-rolled flat products Cold-rolled/hot-dip coated flat products Recommended
More informationAn Experimental Investigation on Spot Weld Growth on Dissimilar Joints of 304L Austenitic Stainless Steel and Medium Carbon Steel (Part 1)
International Journal of Advances in Applied Sciences (IJAAS) Vol. 2, No. 1, March 2013, pp. 25~32 ISSN: 2252-8814 25 An Experimental Investigation on Spot Weld Growth on Dissimilar Joints of 304L Austenitic
More informationA Comparison of AC to Inverter DC Resistance Spot Welding and the Effects On Dual-Phase 600
A Comparison of AC to Inverter DC Resistance Spot Welding and the Effects On Dual-Phase 600 ABSTRACT Dual-phase 600 is a mixture of ferrite matrix and martensitic islands distributed at grain boundaries
More informationTHE HOT FORMING OF GALVANIZED STEELS
THE HOT FORMING OF GALVANIZED STEELS Karl M. Radlmayr, voestalpine Metal Forming GmbH Reiner Kelsch, Andreas Sommer, voestalpine Automotive Components Schwäbisch Gmünd GmbH & Co. KG Christian Rouet, voestalpine
More information