Certified Reference Material Series for X-ray Fluorescence Analysis of Refractories JRRM (Series No.1 for Fireclay Refractories)
|
|
- Sandra Griffin
- 5 years ago
- Views:
Transcription
1 JRRM (Series No.1 for Fireclay Refractories) December 21, 2015 Constituent SiO2 Al2O3 Fe2O3 TiO2 MnO CaO MgO Na2O K2O JRRM JRRM JRRM JRRM JRRM 105a JRRM JRRM JRRM JRRM JRRM Note: The above values show the contents after igniting for one hour at
2 JRRM (Series No.2 for Fireclay Refractories) Constituent SiO2 Al2O3 Fe2O3 TiO2 MnO CaO MgO Na2O K2O P2O5 Cr2O3 ZrO2 LOI* JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRMM Note: The above values show contents after drying for two hours at (*) Indicated value
3 JRRM 201a-210 (Series No.1 for Silica Refractories) Constituent SiO2 Al2O3 Fe2O3 TiO2 MnO CaO MgO Na2O K2O JRRM 201a JRRM JRRM JRRM JRRM 205a JRRM JRRM JRRM JRRM JRRM Note: The above values show contents after igniting for one hour at
4 JRRM (Series No.1 for High Alumina Refractories) Constituent SiO2 Al2O3 Fe2O3 TiO2 MnO CaO MgO Na2O K2O B2O3* JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM Note: The above values show contents after igniting for one hour at (*) Indicated value
5 JRRM (Series No.1 for Magnesia Refractories) Constituent SiO2 Al2O3 Fe2O3 CaO MgO Indicated value TiO2 MnO Na2O K2O Cr2O3 P2O5 B2O3 JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM Note: The above values show the contents after burning for sixty minutes at
6 JRRM (Series No.1 for Chrome-Magnesia Refractories) Constituent SiO2 Al2O3 Fe2O3 TiO2 MnO CaO MgO Cr2O3 Indicated value LOI P2O5 V2O5 NiO ZnO JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRMM Note: The above values show contents after drying for two hours at
7 JRRM (Series No.1 for Zircon-Zirconia Refractories) Constituent SiO2 Al2O3 Fe2O3 TiO2 CaO MgO Na2O K2O P2O5 Cr2O3 ZrO2 HfO2 LOI* JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM Note: The above values show contents after drying for two hours at (*) Indicated value
8 JRRM (Series No.1 for Alumina-Zirconia-Silica Refractories) Constituent SiO2 Al2O3 Fe2O3 TiO2 CaO MgO Na2O K2O Cr2O3 ZrO2 HfO2 Indicated value LOI MnO P2O5 JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM Note: The above values show contents after drying for two hours at 110 5
9 JRRM (Series No.1 for Alumina-Magnesia Refractories) Constituent SiO2 Al2O3 Fe2O3 TiO2 CaO MgO Na2O K2O P2O5 Indicated value LOI MnO Cr2O3 ZrO2 JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM JRRM Note: The above values show contents after igniting for 30 minutes at
10 Certified Reference Material for Carbon Analysis of refractories JRRM (Series No.1 for Calibration of Carbon Analyzer) Certified value Approximate value C Total C Free SiC LOI Al Fe Ti Ca Mg Si Free O N JRRM 1001 (SiC 100) JRRM 1002 (C 5) JRRM 1003 (C 10) JRRM 1004 (C 20) JRRM 1005 (C 30) JRRM 1006 (C 50) JRRM 1007 (C 10-SiC 90) JRRM 1008 (C 5-SiC 30) JRRM 1009 (C 40-SiC 6) <0.001 < Note: The above values show contents after drying for two hours at 110 5
11 Certified Reference Material for Sulfur Analysis of Refractories JRRM (Series No.1 for Analyzer for Sulfur Impure Refractories) Component Chemical Symbol Sulfur S Number Certified value JRRM JRRM JRRM JRRM JRRM JRRM Note: The above values show the contents after drying for two hours at 110 5
Chris DeRosa Market Manager Metallurgical Products Washington Mills Hennepin. Ductile Iron Society Annual Meeting May 11 13, 2010 Surrey BC
Chris DeRosa Market Manager Metallurgical Products Washington Mills Hennepin Ductile Iron Slag Management in Coreless Furnaces Slag Generation and Handling Options Discussion i of Analytical l Testing
More informationCertificate of Analysis Work Order : LK [Report File No.: ]
Certificate of Analysis Work Order : LK40078 [] To: Mike Koziol COD SGS MINERALS Unit 7 3C Kelly Lake Road Sudbury ON P3E P Date: Dec 3, 204 P.O. No. Project No. No. Of Samples Date Submitted Report Comprises
More informationTable 3.1a: Results of microprobe analysis and temperature calculations, HMB diorite
Table 3.1a: Results of microprobe analysis and temperature calculations, HMB diorite Microprobe analysis of coexisting hornblende-plagioclase pairs in O/C-118a Analysis 68 70 80 76 78 79 81 Location 1
More informationX-ray Fluorescence Spectrometry X-ray Fluorescence Spectrometry (XRF) is a non-destructive, quantitative technique for determining chemical
X-ray Fluorescence Spectrometry X-ray Fluorescence Spectrometry (XRF) is a non-destructive, quantitative technique for determining chemical composition. When a primary x-ray collides with an atom in the
More informationCERTIFIED REFERENCE MATERIALS (CRM)
CERTIFIED REFERENCE MATERIALS (CRM) Sufficiently Homogenized Indian Reference Materials certified by Round robin analysis for the use of validation of methods and calibration. CSIR-National Metallurgical
More informationWhite Fused Alumina. Specifications: Best Coarse Coarse Normal part Mixed part 100%pass these mesh NO. Grain size. Fine part.
28 Charlton Street, Mt. Warrigal. NSW. 2528. Australia. Phone: 0242 956915 Mobile: 0450 695691 e mail: john.pulbrook@bigpond.com Skype: johnpulbrook1 ABN 17 949 415 002 Our products include White Fused
More informationComparison of Off-peak vs. MAN vs. Nth Point background measurements John Donovan,
Comparison of vs. vs. background measurements John Donovan, 09-03-2009 Comparison of methods The following is an attempt to compare three methods (, and ) for background determination using both a homogeneous
More informationAbstract No. 63. Applications of Borate Fusion for X-Ray Fluorescence Analysis
Abstract No. 63 Applications of Borate Fusion for X-Ray Fluorescence Analysis Author: Dr. Rainer Schramm, FLUXANA GmbH & Co. KG, Borschelstr.3, 47551 Bedburg-Hau, Germany Tel. +49 2821 99732-0, Fax +49
More informationTHE POSSIBILITY OF USING HANDHELD XRF IN CEMENT APPLICATIONS
THE POSSIBILITY OF USING HANDHELD XRF IN CEMENT APPLICATIONS Dr. Michelle Cameron, Bruker Elemental, Kennewick, WA Denver X-ray Conference 2011 ABSTRACT Handheld XRF may become a useful and cost-saving
More informationCement analysis using FP program (Fundamental Parameters)
Application note issue #5 Cement Analysis August 2017 Cement analysis using FP program (Fundamental Parameters) Cement is a blend of several minerals. It is critical to control the elemental composition
More informationFire Clay Brick. Pyrophylite Brick. Pyrophylite -SiC-C brick. Pyrophylite -SiC brick. High Alumina Brick. Alumina-SiC-C Brick.
Fire Clay Brick Pyrophylite Brick Pyrophylite -SiC-C brick Pyrophylite -SiC brick High Alumina Brick Phosphate unbuned High alumina Brick Mullite brick for dry quenching device Alumina-SiC-C Brick Silica
More informationSIMPLIFIED MATERIALS ANALYSIS VIA XRF. Ravi Yellepeddi and Didier Bonvin Thermo Fisher Scientific (Ecublens) SARL, Ecublens/Switzerland
SIMPLIFIED MATERIALS ANALYSIS VIA XRF Ravi Yellepeddi and Didier Bonvin Thermo Fisher Scientific (Ecublens) SARL, Ecublens/Switzerland SIMPLIFIED MATERIALS ANALYSIS VIA XRF Ravi Yellepeddi and Didier Bonvin
More informationTYPICAL APPLICATIONS FOR RANDOM PACKINGS
TYPICAL APPLICATIONS FOR RANDOM PACKINGS Ceramic Random Pacings [Saddles, Super Saddles, Raschig Rings, Pall Rings] Manufacture and handling of sulfuric acid Chlorine Drying Towers Nitric Acid Concentrators
More informationKarsten Agersted
Corrosionosion of refractories and ceramic materials Karsten Agersted kagn@dtu.dk Outline Introduction, materials, fundamentals and share of experience Ever fascinating corrosion in glass furnaces Corrosion
More informationN McEwan, Verref. Chromite A critical raw material for the Refractory Manufacturer
N McEwan, Verref Chromite A critical raw material for the Refractory Manufacturer Agenda: Introduction to Marico Chrome Corporation Marico Chromite deposit Refractory materials Suitability of chromite
More informationJapanese Iron and Steel Certified Reference Materials April 9, 2012
I. CRMs for Chemical Analysis Japanese Iron and Steel Certified Reference Materials April 9, 2012 I-1. Pure iron series Mass content in % C Si Mn P S Ni Cr Mo Cu Co Al As Sn B N Na X 001-6 High grade pure
More informationPumice. - Safety Data Sheet - PUMICE. tel: fax:
Pumice - Safety Data Sheet - PUMICE tel: fax: 01889 580 661 email: enquiriesspecialistaggregates.com 1 Safety Data Sheet IDENTIFICATION OF THE SUBSTANCE / MIXTURE AND OF THE COMPANY / UNDERTAKING Product
More informationBlended Cement Samples 81 & 82
Blended Cement Samples 81 & 82 Please Note: Both cements are ASTM C595 Blended Hydraulic Cements. Sample No. 81 is a Type IS(30) and Sample No. 82 is a Type IS(40). Type IS cements require the separate
More informationCERAMICS. (related only to traditional ceramics): Materials made of clays and hardened by fire
CERAMICS Original definition: (related only to traditional ceramics): Materials made of clays and hardened by fire Actual definition: Inorganic non-metallic heterogeneous materials with structure composed
More informationCorrosion of refractories and ceramic materials
Downloaded from orbit.dtu.dk on: Sep 02, 2018 Corrosion of refractories and ceramic materials Agersted, Karsten Publication date: 2012 Link back to DTU Orbit Citation (APA): Agersted, K. (2012). Corrosion
More informationUSING OF LIBYAN CALCINED CLAY AS REPLACEMENT
USING OF LIBYAN CALCINED CLAY AS REPLACEMENT CEMENT IN CONCRETE Abdelsalam.M. Akasha* Civil Engineering Department Sebha University Sebha Libya Hamza M. Addussalam** Civil Engineering Department Sebha
More informationCERTIFICATION REPORT ACIRS-A1-TR-01
CERTIFICATION REPORT ACIRS-A1-2016 Fly Ash Reference Material Date of Issue: June, 2016 Valid to: June, 2026 Report Number: ACIRS-A1-TR-01 1. Introduction This report describes the preparation and certification
More informationGlobal Cement and Raw Materials Fusion/XRF Analytical Solution
263 Global Cement and Raw Materials Fusion/XRF Analytical Solution Mathieu Bouchard, John Anzelmo, and Sebastien Rivard Corporation Scientifique Claisse, Quebec, Canada Alexander Seyfarth and Larry Arias
More informationIndustrial Reference Materials
Industrial Reference Materials Fluxana is dedicated to serve and support the X-ray fluorescence (XRF) spectroscopist. XRF is used to perform elemental analysis of a diverse range of materials, from oils
More informationPortland Cement Samples 209 & 210
Portland Cement s 209 & 210 Please Note: Portland Cement No. 209 is an C150 cement meeting both Type I and Type II specifications. Portland Cement No. 210 is an C150 cement meeting both Type I and Type
More informationEVALUATION OF BAUXITE FROM ORIN-EKITI, EKITI STATE, SOUTH-WEST NIGERIA USING CHEMICAL AND SPECTROSCOPIC METHODS OF ANALYSIS.
EVALUATION OF BAUXITE FROM ORIN-EKITI, EKITI STATE, SOUTH-WEST NIGERIA USING CHEMICAL AND SPECTROSCOPIC METHODS OF ANALYSIS. Babatunde O.A And Dayo-Olabgende.O. Department of Chemistry Nigerian Defence
More information1. Temperature Dependences of Optical Path Length in Inorganic Glasses
Reports Res. Lab. Asahi Glass Co., Ltd., 1. Temperature Dependences of Optical Path Length in Inorganic Glasses Akio Koike* and Naoki Sugimoto* Temperature dependences of optical path length (ds/dt; calculated
More informationCreating Value in Mining: How XRF Delivers Accuracy and Precision in Daily Routine
Creating Value in Mining: How XRF Delivers Accuracy and Precision in Daily Routine Presented by: Kai Behrens & Arkady Buman Bruker AXS November 19, 2012 1 Webinar: Creating Value in Mining Today s Speakers
More informationCertified Reference Materials. Minerals Industrial XRF Drift Monitors Coal ROHS/Plastics
2015 Certified Reference Materials Minerals Industrial XRF Drift Monitors Coal ROHS/Plastics Fluxana is dedicated to serve and support the X-ray fluorescence (XRF) spectroscopist. XRF is used to perform
More informationElectron Probe Micro-Analysis (EPMA)
Electron Probe Micro-Analysis (EPMA) Nilanjan Chatterjee, Ph.D. Principal Research Scientist 1 Electron Microprobe Facility Department of Earth, Atmospheric and Planetary Sciences Massachusetts Institute
More informationGTOX. a multipurpose oxide + database. GTT Users Meeting, Herzogenrath K. Hack 1, T. Jantzen 1, Elena Yazhenskhik 2, Michael Müller 2
GTOX a multipurpose oxide + database GTT Users Meeting, 28.06.2017 Herzogenrath K. Hack 1, T. Jantzen 1, Elena Yazhenskhik 2, Michael Müller 2 1, 2 IEK2-FZ Jülich Contents of presentation A bit of history
More informationNew software for Simulations of Metal-Slag Interactions. ACCESS Workshop/Users-Meeting September 25, 2007 Thermo-Calc Software, Stockholm, Sweden
Computational Thermodynamics and Kinetics New software for Simulations of Metal-Slag Interactions ACCESS Workshop/Users-Meeting September 25, 2007, Stockholm, Sweden http://www.thermocalc.com Phone: +46-8-545
More informationSteven Dutch, Natural and Applied Sciences, University of Wisconsin - Green Bay
The CIPW Norm Steven Dutch, Natural and Applied Sciences, University of Wisconsin - Green Bay Simplified by JFM (feb. 06), by removing most of the accessory minerals, and the steps needed only in rare
More informationColor in glazes and enamels 15/03/53 1
Color in glazes and enamels 15/03/53 1 Sources of color in glazes Transition metal ions The precipitation of crystal: titania and zirconia Insoluble crystal or crystals that are colored 15/03/53 2 Crystal
More informationThermodynamic database of P 2 O 5 -containing oxide system for De-P process in steelmaking
Thermodynamic database of P 2 O 5 -containing oxide system for De-P process in steelmaking *In-Ho JUNG, Pierre HUDON, Wan-Yi KIM, Marie-Aline VAN ENDE, Miftaur RAHMAN, Gabriel Garcia CURIEL, Elmira Moosavi
More information(12) Patent Application Publication (10) Pub. No.: US 2004/ A1
US 20040092379A1 (19) United States (12) Patent Application Publication (10) Pub. No.: US 2004/0092379 A1 Lewis (43) Pub. Date: (54) HIGH TEMPERATURE GLASS FIBER (30) Foreign Application Priority Data
More informationGlobal Innovation for your High Temp World
Ladle Refractories Global Innovation for your High Temp World Mission Statement Division of Fedmet Resources Corporation: We serve our clients in the high temp world by providing profitable solutions that
More informationSand Reclamation for an Aluminum Foundry
Sand Reclamation for an Aluminum Foundry (Rod Christiansen & Greg Shea) (Eck Industries) Definition Cleans the sand to a degree sufficient to allow its re-use in the foundry Molding or Core making Operations.
More informationChlorine as a geobarometer for alkaline magmas: Evidence from a systematic study of the. eruptions of Mount Somma-Vesuvius
Chlorine as a geobarometer for alkaline magmas: Evidence from a systematic study of the eruptions of Mount Somma-Vesuvius H. Balcone-Boissard 1*, G. Boudon 2, R. Cioni 3, J.D. Webster 4, G. Zdanowicz 2,5,
More informationREFRACTORY PRODUCTS. This product catalogue is compacted for electronical submission without references and illustrations for typical applications.
REFRACTORY PRODUCTS We appreciate the opportunity to present our product catalogue for refractory materials. The catalogue includes typical often used materials for different applications of industrial
More informationIf one does not want the energy consumption in the dryer to increase, then the elements mentioned above must be added in a non-water-binding form.
Consequences of using additives for reducing the firing temperature in the heavy clay ceramic industry Considerations related to energy savings and technical production aspects Hans van Wijck and Hans
More informationCoal Quality As the Boiler Sees It. Rod Hatt Chief Technical Officer Coal Combustion, Inc.
Coal Quality As the Boiler Sees It Rod Hatt Chief Technical Officer Coal Combustion, Inc. www.coalcombustion.com Short Prox Moisture total moisture in sample Ash inorganic rock like material remaining
More informationCeramic - Chemical Resistance Acids - concentrated Acids - dilute Alkalis Halogens Metals
Ceramic - Chemical Resistance Acids - concentrated Acids - dilute Alkalis Halogens Metals Fair Good Poor-Fair - Good 62/SiO2 24/B2O3 14 Fair Good Poor-Fair - - 70/SiO2 28/B2O3 2 Good Good Good Good Good
More informationModule: 5 Lecture: 24
Module: 5 Lecture: 24 CEMENT MANUFACTURE MANUFACTURE It involves the following steps 1. Mixing of raw material 2. Burning 3. Grinding 4. Storage and packaging 1. Mixing of raw material Mixing can be done
More informationCeramic - Chemical Resistance Acids - concentrated Acids - dilute Alkalis Halogens Metals
Ceramic - Chemical Resistance Acids - concentrated Acids - dilute Alkalis Halogens Metals Fair Good Poor-Fair - Good 62/SiO2 24/B2O3 14 Fair Good Poor-Fair - - 70/SiO2 28/B2O3 2 Good Good Good Good Good
More informationMagnesia-carbon refractories for the lining of gasification chambers: technical capabilities and limitations
Magnesia-carbon refractories for the lining of gasification chambers: technical capabilities and limitations M. Hampel*, P. Gehre, T. Schemmel, C.G. Aneziris 5th International Freiberg Conference on IGCC
More informationSummary of Geochemical Atlas Information
G-BASE Internet Information Summary of Geochemical Atlas Information Version 1.1 31 st March 2006 atlassummaries.pdf Page 1 of 17 Summary Atlas Information 8. Argyll 17. East Anglia 7. East Grampians 16.
More informationOF THE RED CLAY THE COMPOSITION
THE COMPOSITION OF THE RED CLAY In the volume upon Deep Sea Deposits, issued as one of the reports of the "Challenger" expedition, there are published twentyfive analyses of the "red clays."' This sediment
More informationDRAFT TANZANIA STANDARD. TBS/CDC7 (5416) P3 Lime (Quick and Hydrated) for Chemical industries Specification (Revision of TZS 586: 2001)
TBS/CDC7 (5417) P3 DRAFT TANZANIA STANDARD TBS/CDC7 (5416) P3 Lime (Quick and Hydrated) for Chemical industries Specification (Revision of TZS 586: 2001) TANZANIA BUREAU OF STANDARD Foreword This Draft
More informationProcess and quality control in the aluminum industry using ARL 9900 XRF-XRD integrated spectrometer
Lecture Transcript: LT O4/05 Process and quality control in the aluminum industry using ARL 9900 XRF-XRD integrated spectrometer Authors: R. Yellepeddi, A. Kohler and D. Bonvin Thermo Electron SA, Ecublens/Switzerland
More informationAbstract No. 72. Complexity of reception inspection for casting powders at Dillinger Steel Works
Abstract No. 72 Complexity of reception inspection for casting powders at Dillinger Steel Works Dr. Hans-Uwe Schmitz, Ingo Scher, AG der Dillinger Hüttenwerke, Dillingen, Germany The reception inspection
More informationAn application of Nanoparticles. Application of ZrO 2 as a Catalyst and a Catalyst Support
An application of Nanoparticles Application of ZrO 2 as a Catalyst and a Catalyst Support Introduction Characteristics of ZrO 2 High T m (>3000K) Low K c High resistance for corrosion Refractories, pigments,
More informationEffect of Nano-Sized Fe 2 O 3 on Microstructure and Hydration Resistance of MgO-CaO Refractories
Int. J. Nanosci. Nanotechnol., Vol. 12, No. 1, March. 2016, pp. 19-26 Effect of Nano-Sized Fe 2 O 3 on Microstructure and Hydration Resistance of MgO-CaO Refractories S. G. Kahrizsangi*, A. Nemati, A.
More informationDevelopment of Lighter and Eco-Friendly Burnt Clay Bricks Incorporating Sugarcane Bagasse Ash
Pak. J. Engg. & Appl. Sci. Vol. 21 July, 217 (p. 1 ) Development of Lighter and Eco-Friendly Burnt Bricks Incorporating Sugarcane Bagasse Ash Syed Minhaj Saleem Kazmi 1, 2*, Muhammad Junaid Munir 1, 2,
More informationCERAMIC MATERIALS I. Asst. Prof. Dr. Ayşe KALEMTAŞ
CERAMIC MATERIALS I akalemtas@mu.edu.tr, akalemtas@gmail.com, Phone: 211 19 17 Metallurgical and Materials Engineering Department Application Base Classification Advanced Ceramics Ceramic Materials Traditional
More informationREDUCING REFRACTORY COST USING NEW ASCC BRICKS FOR HOT IRON TRANSPORT
REDUCING REFRACTORY COST USING NEW ASCC BRICKS FOR HOT IRON TRANSPORT PENG, DEJIANG HE, ZHONGYANG YU, TERRY PUYANG REFRACTORY GROUP LTD. Drawings Outline Optimum Design Material Selection: Tar-Impregnated
More informationModern Steelmaking Processes 1. Charge Materials. Topics to discuss. 1. Metallics 2. Auxiliary charges 3. Oxidants 4. Fuels 5.
11 Modern Steelmaking Processes 1. Charge Materials Topics to discuss 1. Metallics 2. Auxiliary charges 3. Oxidants 4. Fuels 5. Refractories Raw Materials Principal raw materials used for steel manufacture
More informationIDENTIFICATION OF REFRACTORY MATERIAL FAILURES IN CEMENT KILNS
IDENTIFICATION OF REFRACTORY MATERIAL FAILURES IN CEMENT KILNS Peter Lugisani A dissertation submitted to the Faculty of Engineering and the Built Environment, University of the Witwatersrand, Johannesburg,
More information2018 Industrial Minerals Technology Workshop ANIONIC- CATIONIC PROCESS FOR SILICA SAND FLOTATION MINING EXTERNAL RYAN XIONG, JAMES GU AND GUOXIN WANG
ANIONIC- CATIONIC PROCESS FOR SILICA SAND 50 TH ANNIVERSARY FLOTATION MINING EXTERNAL RYAN XIONG, JAMES GU AND GUOXIN WANG WWW.ARRMAZ.COM 2017 ARRMAZ PRODUCTS, LP Outline of The Presentation ü Introduction
More informationOptimized, zero waste pyrometallurgical processing of polymetallic nodules from the German CCZ license
Optimized, zero waste pyrometallurgical processing of polymetallic nodules from the German CCZ license area David Friedmann 1, Bernd Friedrich 1, Thomas Kuhn 2 and Carsten Rühlemann 2 1 IME Process Metallurgy
More informationA Short Study to Test the Compliance of Various Pakistani Ordinary Portland Cements with ASTM Composition Standards
Pak. J. Chem. (): 1-7, 1 ISSN (Print): -5 ISSN (Online): -7X Full Paper A Short Study to Test the Compliance of Various Pakistani Ordinary Portland Cements with ASTM Composition Standards A. Shahnaz, *
More informationSuccessful Case Studies of Fluxes when Melting Metals
Successful Case Studies of Fluxes when Melting Metals September 14 th 2006 Meeting American Foundry Society North East Ohio Chapter Mr. David C. Williams ASI International Ltd Columbus Ohio Successful
More informationProcess Conditions in Oxy-fuel Combustion
Centre for Energy and Resource Technology Process Conditions in Oxy-fuel Combustion The Coal Research Forum 24 th annual meeting Nelia Jurado Hamid G Darabkhani John E Oakey Cranfield University 10 th
More informationArsenic Detections. Florida 1995 to 2008 data. As exceedance (> 10 ug/l) As detection (< 10 ug/l) (Author Unknown)
Characterization of Natural and Anthropogenic Sources of Arsenic and other Trace Metals in Florida s Florida s Aquifers J. Arthur, C. Fischler, R. Copeland, P. Hansard Florida Geological Survey October,
More informationZ E H N E G N Z G H Z O H U
FUSED ALUMINA SERIES ZHENGZHOU ONWAY IMPORT & EXPORT CO. LTD Add.: Rm 536A, Xinyuan Int l Plaza, Western Jianshe Road, Zhengzhou, Henan, China Mobile: +86-15333719138 :+86-371-86106538 Fax:+86-371-86106138
More informationComparative Reduction Behavior of Various Cement Coated Iron Ore Pellets
doi: 10.14355/me.2015.04.005 Comparative Reduction Behavior of Various Cement Coated Iron Ore Pellets M. Bahgat* 1, S. Niaz 2, S. Lakdawala 3 and H. Hanafy 4 1 Currently Lead scientist, Metal technology
More informationQualification of Micronized Kyanite and Silica Fume
Qualification of Micronized Kyanite and Silica Fume William L. Headrick Missouri Refractories Co., Inc. Formerly University of Missouri-Rolla Co-authors Dilip Jain, Kyanite Mining Corp. Musa Karakus, University
More informationMATERIAL SAFETY DATA SHEET Date Prepared September 15, 2017
MATERIAL SAFETY DATA SHEET Date Prepared September 15, 2017 1. Chemical Product and Company Information Product name: Wall Tile Company Information Emergency Contact Information +34 964 626 272 Decocer
More informationUnited States Patent (19)
United States Patent (19) Sakaguchi et al. 54) ULTRAVIOLET AND INFRARED RADIATION ABSORBING GLASS 75 Inventors: Koichi Sakaguchi; Yukihito Nagashima; Shigeki Nakagaki, all of Osaka, Japan 73 Assignee:
More informationQuality Control and traceability; the guarantee for reliable product in Cement Manufacturing
Quality Control and traceability; the guarantee for reliable product in Cement Manufacturing Maggi Loubser Test and Measurement 2013 Conference Misty Hills Conference Hotel, Muldersdrift 6-9 October 2013
More informationINTERACTION MECHANISM BETWEEN REFRACTORY AND MELTS IN IRON BATH SMELTING REDUCTION PROCESS
J o u r n a l o f J. Min. Metall. Sect. B-Metall. 46 (2) B (2010) 131-140 M i n i n g a n d M e t a l l u r g y INTERACTION MECHANISM BETWEEN REFRACTORY AND MELTS IN IRON BATH SMELTING REDUCTION PROCESS
More informationGlass as matrix for hazardous substances
On the possibility of using vitrified forts as anthropogenic analogues for assessment of long- term behaviour of vitrified waste Rolf Sjöblom, Holger Ecke 1 and Evelina Brännvall Luleå University of Technology
More informationTHE USE AND OPTIMISATION OF FERROUS FEED AT THE WHYALLA BLAST FURNACE
THE USE AND OPTIMISATION OF FERROUS FEED AT THE WHYALLA BLAST FURNACE AUSIMM Iron Ore 2015 Conference, Perth Australia 13 15 July 2015 Presented by John Tsalapatis Whyalla Location Whyalla Adelaide 2 Steelworks
More informationComparison Thermal and Hardness of CaO-MgO-Al2O3-SiO2-B2O5 Glass from Different Sources of Kaolin Minerals as Main Raw Mineral
International Journal of Current Science, Engineering & Technology Original Research Article Open Access AMCT 2017 Malaysia Special Issue ISSN : 2581-4311 Comparison Thermal and Hardness of CaO-MgO-Al2O3-SiO2-B2O5
More informationDEVELOPING A HIGH GRADE ILMENITE DEPOSIT TIO 2 WORLD SUMMIT 3-5 OCTOBER 2017 ALICANTE, SPAIN
DEVELOPING A HIGH GRADE ILMENITE DEPOSIT TIO 2 WORLD SUMMIT 3-5 OCTOBER 2017 ALICANTE, SPAIN GREENLAND: THE MISUNDERSTOOD ISLAND TOO COLD?????? TOO HARD? TOO ISOLATED???? 1 MAYBE IT S TIME TO TO THINK
More informationUse of Fly ash from KKAB, Sweden Sealing a landfill with only fly ash
Image size: 7,94 cm x 25,4 cm Use of Fly ash from KKAB, Sweden Sealing a landfill with only fly ash M.Sc.Civ.Eng Kristina Hargelius, Environmental consultant in Ramböll Sweden AB Recycled paper gives us
More informationLignite Properties and Boiler Performance
Lignite Properties and Boiler Performance Energy Generation Conference: Reducing CO 2 Intensity in Power Plants Steve Benson Presented at the Energy Generation Conference Bismarck, ND January 28, 2015
More informationOxides and Hydroxides
Descriptive Mineralogy Oxides and Hydroxides Classification of the Minerals Non-Silicates Native Elements Halides Sulfides Oxides Hydroxides Carbonates Sulfates Phosphates Silicates Orthosilicates Sorosilicates
More information4,282,035 8/1981 Nigrin /54 (viii) up to about 2% Lio, and
USOO5985.473A United States Patent (19) 11 Patent Number: 5,985,473 Knapp (45) Date of Patent: Nov. 16, 1999 54) LOW-TEMPERATURE BARIUM/LEAD-FREE 5,292,690 3/1994 Kawachi et al.... 5O1/33 GLAZE FOR ALUMINA
More informationThreshold Value of Minerals. Dr P K Jain Chief Mineral Economist Indian Bureau of Mines Nagpur
Threshold Value of Minerals Dr P K Jain Chief Mineral Economist Indian Bureau of Mines Nagpur NMP 2008 2. BASIC FEATURES Minerals being a valuable resource the extraction of mineral resources located through
More informationThe statistical analysis of compositional data: Exploratory analysis
preliminaries descriptive statistics stardisation biplot balance-dendrogram The statistical analysis of compositional data: Exploratory analysis Prof. Dr. Vera Pawlowsky-Glahn Prof. Dr. Juan José Egozcue
More informationFor personal use only
CONCENTRATES CONFIRMED AS BENCHMARK AND HIGHLY SUITABLE FOR USE IN LITHIUM-ION BATTERIES HIGHLIGHTS Independent test work demonstrates Graphmada graphite concentrates as highly suitable for lithium-ion
More informationUTILIZATION OF ALUMINIUM PROCESSING WASTE AS RAW MATERIALS IN THE MANUFACTURE OF CEMENT
UTILIZATION OF ALUMINIUM PROCESSING WASTE AS RAW MATERIALS IN THE MANUFACTURE OF CEMENT M Pareek, Digvijay Singh, D Yadav*, S K Chaturvedi* and M M Ali* Century Metal Recycling Pvt. Ltd., Palwal, Haryana
More informationAMIS0394. Certified Reference Material. Certificate of Analysis
Tel: +27 (0) 11 923 0800 Fax: +27 (0) 11 392 4715 web: www.amis.co.za 11 Gewel Street (off Hulley Road), D1 Isando Business Park, Kempton Park, 1609 P.O. Box 856, Isando, 1600, Gauteng, South Africa, a
More informationCan Fluorspar be replaced in steelmaking? Eugene Pretorius Baker Refractories
Can Fluorspar be replaced in steelmaking? By Eugene Pretorius Baker Refractories I) Introduction The use of fluorspar in steelmaking is a controversial issue. A number of studies have shown that there
More informationUNSLAKED LIME Ground Unslaked Lime
Lime Product Data Sheets UNSLAKED LIME Ground Unslaked Lime CaO G.U.S., Ground Quicklime, Calcium Oxide Typical % Available calcium as CaO 88.0 Total calcium as CaO 92.0 Total magnesium as MgO 2.2 Silica
More informationFor personal use only
Manganese Intercepted at Grenfell Project Bligh Resources Limited ACN 130 964 162 ASX: BGH ASX Release 24 December 2012 Suite 804 Level 8, 84 Pitt St Sydney New South Wales 2000 Tel: +61 2 9233 4677 Fax:
More informationAddition of ZnO to the HotVeGas Oxide database
Addition of ZnO to the HotVeGas Oxide database GTT-Workshop, 1-3. Juli 2015, Herzogenrath Klaus Hack, Tatjana Jantzen Contents of presentation Introduction Solid solution phases Ternary systems Conclusions
More informationAnalysis of glass from Seagrange, Baldoyle, Excavation No. 13E238
Analysis of glass from Seagrange, Baldoyle, Excavation No. 13E238 Sinead Middleton with Dr. Fiona Beglane and Dr. Carmel Moran Dept of Environmental Science, IT Sligo, Ash Lane, Sligo 20/05/14 1. Introduction
More informationT 619 cm-84 TENTATIVE STANDARD 1933 OFFICIAL STANDARD 1935 CORRECTED 1944 CORRECTED 1953 CLASSICAL METHOD TAPPI. Analysis of salt cake
T 619 cm-8 TENTATIVE STANDARD 19 OFFICIAL STANDARD 195 CORRECTED 19 CORRECTED 195 CLASSICAL METHOD 198 198 TAPPI The information and data contained in this document were prepared by a technical committee
More informationMine tailings valorization potential as raw materials for reaction sintered mullite based ceramics
VTT TECHNICAL RESEARCH CENTRE OF FINLAND LTD Mine tailings valorization potential as raw materials for reaction sintered mullite based ceramics Marjaana Karhu VTT Technical Research Centre of Finland Ltd
More informationCeramics for Molten Materials Containment, Transfer and Handling on the Lunar Surface
47th AIAA Aerospace Sciences Meeting Including The New Horizons Forum and Aerospace Exposition 5-8 January 2009, Orlando, Florida AIAA 2009-1657 Ceramics for Molten Materials Containment, Transfer and
More informationweight% Alt. 1 Alt. 2 CaO 32,4 33,6 SiO2 33,1 33,7 Al2O3 11,9 11,9 MgO 17,6 16,0
Slag formation The composition of slag is changed as stated in the table below Estimate B2, B3 och B4 B2: CaO/SiO 2 =32,4/33,1=0,98; 33,6/33,7=1,00 B3: (CaO+MgO)/SiO 2 =(32,4+17,6)/33,1=1,51; (33,6+16,0)/33,7=1,47
More informationWORLD IRON MARKET. World Iron market dominated by two minerals. Hematite Fe2O3 69.8% Fe Magnetite Fe3O % Fe
MAGNETITE WORLD IRON MARKET World Iron market dominated by two minerals Hematite Fe2O3 69.8% Fe Magnetite Fe3O4 72.3% Fe 60% world iron production comes from Hematite 40% from Magnetite. There are other
More informationAPPC PDH/PP PROJECT 8 CATOFIN REACTORS - JUBAIL SAUDI ARABIA ENGINEERING, DESIGN AND INSTALLATION OF REFRACTORY LINING
ctive owners. names mentioned herein may be trademarks or trade names of their respec APPC PDH/PP PROJECT 8 CATOFIN REACTORS - JUBAIL SAUDI ARABIA ENGINEERING, DESIGN AND INSTALLATION OF REFRACTORY LINING
More informationDEGRADATION THE REFRACTORIES OF ROTARY FURNACE LININGS IN THE PRODUCTION OF ZINC OXIDE
DEGRADATION THE REFRACTORIES OF ROTARY FURNACE LININGS IN THE PRODUCTION OF ZINC OXIDE Natália LUPTÁKOVÁ a, Františka PEŠLOVÁ a, Evgeniy ANISOMOV b, Adriana PAVÚČKOVÁ a, Michaela FERODOVÁ a a University
More informationModules - Pyro-Bloc Superwool AES grades
Modules PyroBloc Superwool AES grades PyroBloc Y, Y 2, M, M 2 Superwool Plus Superwool HT Color white Density, pcf (kg/m 3 ) 10, 12 (160, 192) Thickness, in1 inch (25 mm) increments 4 12 (102 305) Continuous
More informationIvoclar Vivadent AG, Bendererstrasse 2, 9494 Schaan. Principality of Liechtenstein. IPS d.sign Powder. Ceramic. Principality of Liechtenstein (FL)
Page of 5 Company Ivoclar Vivadent AG, Bendererstrasse 2, FL - 9494 Schaan Principality of Liechtenstein. Commercial product name and supplier Commercial product name / Designation Dentin, Deep Dentin,
More information