DUXONE Basecoat. All cleaned and sanded OEM finishes (not recommended on thermoplastic acrylic finishes).

Transcription

1 Description 2component productive clear to be used in clear over base system. Composition based on a special acrylic polyurethane copolymer. Products 2K HS Clear Coat Activator Slow Standard Activator Activator Extra Fast Properties Has very good flow. Has excellent mar, chemical and weather resistance. Has excellent polishability. Gives a long lasting high gloss finish. Increases productivity in air dry, low bake or IR drying. Can be used for spot, panel and overall repair. Substrates DUXONE Basecoat. All cleaned and sanded OEM finishes (not recommended on thermoplastic acrylic finishes). REF 00 GB p 15 Effective: 24 January, 2011

2 PRODUCT PREPARATION Mixing ratio Slow Standard Very fast VOC (2004/42/EC) Potlife at 20 C Spray viscosity at 20 C Spray equipment Number of coats Flash time DFT Volume Weight Volume Weight Volume Weight g/l DIN 4 FORD 4 AFNOR 4 4 hr 30 3 hr 30 2 hr s 1618 s 1719 s 552 g/l 556 g/l Fluid tip Distance Pressure Conventional guns Gravity feed mm 1520 cm 34 bar Suction feed mm 1520 cm 34 bar Pressure feed mm 1520 cm 34 bar Compliant guns (HVLP/HTE) Gravity feed mm 1015 cm According to Suction feed mm 1015 cm supplier's Pressure feed mm 1015 cm specifications 2 5 min between coats. 510 min before bake micron (2 coats) REF 00 GB p 25 Effective: 24 January, 2011

3 PRODUCT PREPARATION (con'd) Drying Dustfree Dry to handle Tapefree 40 min 6 hr O.N. IRdrying* Flash time 5 min Distance 80 cm Half power 5 min Full power C 40 min x 60 C 20 C 30 min x 60 C 25 min 1 hr 30 min 4 hr O.N. 1 hr 20 C x 60 C 3 hr 5 hr 30 min 1 hr 30 min * Guideline for short / medium wave IR equipment For professional use only! The information provided in this documentation has been carefully selected and arranged by us. It is based upon our best knowledge on the subject at the date of issuance. The Information is given for information purposes only. We are not liable for its correctness, accuracy and completeness. It is up to the user to check the information with regard to uptodateness and suitability for his intended purpose. The intellectual property in this Information, including patents, trademarks and copyrights, is protected. All rights reserved. The relevant Material Safety Data Sheet and Warnings displayed on the product label need to be observed. We may modify and/ or discontinue operation of all or portions of this Information at any time in our sole discretion, without notice and assume no responsibility to update the Information. All rules set forth in this clause shall apply accordingly for any future changes and amendments. RECOMMENDED USE Clearcoat application When the DUXONE Basecoat is completely flat, apply in 2 coats with 5 min flash between coats. Chemical resistance When fully cured, is resistant to short exposures of the chemicals as listed: sodium hydroxide battery acid sulphuric acid hydrochloric acid 25% toluene xylene phosphoric acid glycol ammonia 10% brake fluid, petrol REF 00 GB p 35 Effective: 24 January, 2011

4 RECOMMENDED USE (con'd) Equipment cleaning Use a correct solventborne gunwash. Recoatability At any time after tapefree time. After 24 hr, scuff sanding is required. Remarks is recommended for spot/panel repair only. If only necessary for minor viscosity adjustments, use DUXONE basecoat thinners (maximum 5 %). Close can of activator tightly immediately after use, as this product will react with humid air and water and lose its hardening effect. Activated material should not be returned to original can of nonactivated material. Material has to be at room temperature (1825 C) before use. Product data Package viscosity: Theoretical coverage: 90 cp m²/l at recommended DFT readytospray REF 00 GB p 45 Effective: 24 January, 2011

5 RECOMMENDED USE (con'd) Products Packages (l) Shelf life at 20 C (year) Density (kg/l) Safety Consult Safety Data Sheet prior to use. Observe the precautionary notices displayed on the container. REF 00 GB p 55 Effective: 24 January, 2011