series PRODUCT INFORMATION Hazy/Matte/White Opaque Film Description Performance Benefits

Transcription

1 CI series Hazy/Matte/White Opaque Film Description ASTROLL CI series are PET (Polyethylene terephthalate) based hazy/matte/white opaque polyester film designed for various application such as package, label, insulation, & solar cell back sheet, etc. Performance ASTROLL CI series can be treated with coating materials in order to adhesion promotion. This type of coating is treated inside/outside of the film. The available thickness ranges from 12 μm to 250 μm (48 to 1000 gauge). According to the customer s needs, ASTROLL CI series have various optical properties such as haze, transmittance & gloss. Benefits ASTROLL CI series have the advantages of below Good dimensional stability Good adhesive strength at high temperature & high humidity Good electrical resistance Good adhesion to various materials by coating treatment : Ink, metal, silicone, PVA, & PE direct lamination NPI1

2 Application Slightly hazy Insulation Industrial Lamination Hazy Insulation Solar cell back sheet (PV module) Matte Label Book cover Transcription White opaque Label Magnetic card Printing White board Solar cell back sheet (PV module) Warning Take care of rolls: heavy rolls can pressed down your body & equipments. Do not step on the scrap films: sometimes plain/coated film may very slippery. NPI2

3 Haze () FORMATION Schematic of ASTROLL CIseries 1. Detailed type of ASTROLL CI Series plain type CI 9XXSeries Type Slightly Hazy Hazy Milky White White Matte Thickness (um) 25 ~ ~ 250 (25 ~ 250) 12 ~ 188 Haze () 5 ~ ~ ~ ~ 85 Properties Transmittance () 10 (100 μm ) Break down Voltage (kv) 15 ± 5 Opacity () 80 (100 μm ) Gloss () 18 ± 2 Application Electrical Insulation Industrial Lamination Electrical Insulation Back Sheet (PV module) Electrical Insulation Industrial Lamination Labels, Card Printing Back Sheet (PV module) Labels Book cover Item CI910 CI911 CI920 CI921 CI930 CI931 CI940 CI941 CI990 CI Haze of ASTROLL CI Series as Function of thickness CI940 (White Opaque) CI920 CI320 Thickness ( μm ) CI900 NPI3

4 : CI900 Thickness um 19 (FB3) 23 (FB3) 36 (FB3) Yield mm 2 /kg TD TD TD ASTM D2305 TD (150, 30min) μk Haze ASTM D1003 Normal laboratory condition : 24, 45RH NPI4

5 : CI900 Thickness um 50 (FB1) 75 (FB1) 100 (FB1) Yield mm 2 /kg TD TD TD ASTM D2305 TD (150, 30min) μk Haze ASTM D1003 Normal laboratory condition : 24, 45RH NPI5

6 : CI900 Thickness um 125 (FB1) 190 (FB1) 250±7.0 Yield mm 2 /kg (FB1,K3) TD TD TD ASTM D2305 TD (150, 30min) μk Haze ASTM D1003 Normal laboratory condition : 24, 45RH NPI6

7 : CI920 Thickness um 36 (FB3) 75 (FB1) 100 (FB1) Yield mm 2 /kg TD TD TD ASTM D2305 TD (150, 30min) μk Haze ASTM D1003 Normal laboratory condition : 24, 45RH NPI7

8 : CI920 Thickness um 125 (FB1) 188 (FB1) 190 (FB1) Yield mm 2 /kg TD TD TD ASTM D2305 TD (150, 30min) μk Haze ASTM D1003 Normal laboratory condition : 24, 45RH NPI8

9 : CI920 Thickness um 250±4.0 Yield mm 2 /kg (FB1,K3) 18.0 TD TD TD ASTM D2305 TD 0.3 (150, 30min) 0.35 μk 0.38 Haze ASTM D1003 Normal laboratory condition : 24, 45RH NPI9

10 : CI930 Thickness um 125 (FB1) 188 (FB1) 250 (FB1) Yield mm 2 /kg TD TD TD ASTM D2305 TD (150, 30min) μk Haze ASTM D1003 Normal laboratory condition : 24, 45RH NPI10