BOPP-FILMS TECHNICAL DATA SHEETS

Transcription

1 BOPP-FILMS TECHNICAL DATA SHEETS

2 TRANSPARENT FILMS HGPL Heat sealable transparent film with standard coefficient of friction....4 HGHL Heat sealable transparent film with low coefficient of friction...6 HGFL Heat sealable transparent film with high coefficient of friction for special purposes...8 PGR Transparent release film HGSL Heat sealable transparent film for hot climate HGHW Heat sealable transparent with a wide temperature sealing range PGP Non heat sealable for printing and lamination METALLIZED FILMS HMPL.M Metallized heat sealable film for general purposes HMPLB.M Metallized heat sealable film with improved barrier properties HOHMLB.M Metallized white pearlised heat sealable film with improved barrier properties HMIL.M Metallized heat sealable for printing and lamination P.M Metallized non heat sealable film for the production of decorative packaging.. 26 HMPLA.M Metallized heat sealable with low sealing threshold PMP.M Metallized non heat sealable both side treated HMHW.M Metallized heat sealable with a wide range of welding NON-FOOD FILMS PGA Transparent non heat sealable film for general purposes and production of adhesive tapes PGD Transparent non heat sealable film for general purposes and decorative packaging PGT Transparent non heat sealable for general purposes and decorative overwrapping PWA White none heat sealable opaque for general purposes and production of adhesive tapes MATT FILMS MGS One side matt non heat sealable film MGD Both side matt non heat sealable film MGPL Matt heat sealable film with low seal initiation temperature MGR Matte release film OPAQUE FILMS HOHL Heat sealable white-pearlised film with low seal initiation temperature HWHL White heat sealable film with low seal-initiation temperature HOHW White Pearlised film with wide heatsealing range HOHG White Pearlised film both side corona treated with a standard coefficient of friction HWHW White heat sealable film with low seal intention temperature HOHC Heat sealable white-pearlised with high yield LABEL FILMS LGBA Transparent film for labels LOBA White Pearlised film for full-wrap label LOBB White Pearlised film for full-wrap label with improved gloss LOBC White Pearlised film for full-wrap label with high yield LOHM.M White pearlised metallized film for bottle labeling LOMB Matt White Pearlised microporous film LGBL Transparent for self-adhesive labels LWBL Solid white for self-adhesive labels SOI White-pearlised for self-adhesive labels SOIL White-pearlised for inmould labels TOBACCO FILMS TSHL Heat shrinkable non treated-film for «rigid» carton pack overwrapping TSHD Heat shrinkable non treated film for «rigid» carton pack overwrapping for ultra high speed machines TSHT Heat shrinkable treated film «rigid» carton pack overwrapping... 86

3 STORAGE AND HANDLING Rolls should be stored In their original wrapping on pallets in dry closed sun protected place minimum 1 meter from heating units. Storage conditions should eliminate any risk of wrapping deterioration. If stored in unheated area Biaxplen films should be placed at room temperature and humidity at least for 48 hours before converting. It is recommended to corona pre treat fi lm before printing Guaranteed storage life is 6 months from the date of production. SURFACE TREATMENT DIMENSIONS Application For tobacco films For all packaging films Max outer diameter, mm Core diameter, mm Width, mm Tolerance Order weight ± 10* 120 ± 0, < 2000 kg ± > 2000 kg ± ± 3 mm 780 > 5000 kg ± ± 2 mm >10000 kg ± 2 Metallized film surface energy Is affected by temperature and storage life. Biaxplen guarantees surface treatment level of metallized films higher than 36 dynes within 15 days after metallization. In order to minimize the deterioration of surface energy it is recommended to store film below 30 C and to convert it asap. Should film be used for specific application, it is advisable to measure surface energy in order to prove if it suits. Standard roll- outside corona treated web. Metallized film is advised to be primer covered before printing. Metallized film can be laminated with a number of materials. Information given in Techical data sheets is based on typical values checked in standard production. Techical data sheet has not to be considered a product specification. * 500 kg It s highly recommended that the film should be used according to the application recommended by the Producer.

4 Transparent films Biaxplen HGPL DESCRIPTION: Heat sealable transparent BOPP film with a standard coefficient of friction and low heat sealing threshold for packaging machines. For high quality rotogravure and flexographic printing and lamination. B Treated modified heat sealable copolymer skin layer C Transparent oriented polypropylene core layer D Heat sealable, non treated skin layer with low seal intention temperature and standard coefficient of friction MAIN PROPERTIES: A wide range of heat sealing; contains slip-antistatic and antiblocking additives; excellent optical properties; good physical and mechanical properties; intended for contact with food; standard coefficient of friction; without coatings and primers. APPLICATION: High quality solvent based rotogravure and flexographic printing; solvent based and solvent free lamination with polyurethane adhesives; manufacture of flexible packaging for food products; for vertical VFFS and horizontal HFFS packaging machines; production of decorative packaging for flowers, gift wrap and etc.; for cold seal glue frame coating onto UT film side (if necessary). 4

5 Thickness, ± 5 Properties Methods Unit HGPL mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68 Yield, ± 5 m 2 /kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89 Tensile strength, not less Elongation at break, not more Kinetic coefficient of friction UT/UT GOST ISO 8295 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less N/mm 2, TD MPa GOST ISO 527 D TD D ,3 5 4 GOST ISO TD D UT/UT GOST ISO 527 Haze, not more GOST ISO Gloss at 45, not less T ISO 2813 D 882, F 88 D 1003 D 2457 N/15 mm 2,0 2,2 2,3 2,5 2,8 2,5 3,0 3,2 85 Heat sealing range at 1 bar, 1 sec.* UT/UT C Treatment level, not less T ISO 8296 D 2578 Dyne/cm, mn/m ,10-0,15 Machine, longitudinal direction T Treated side of the film TD Transverse direction UT Untreated side of the film GOST Russian Federation standards * Typical value

6 Transparent films Biaxplen HGHL DESCRIPTION: Heat sealable transparent BOPP film with low coefficient of friction and low heat sealing threshold for high-speed packaging machines. For high quality rotogravure and flexographic printing and lamination. B Treated modified heat sealable copolymer skin layer C Transparent oriented polypropylene core layer D Heat sealable, non treated skin layer with low seal intention temperature and low coefficient of friction MAIN PROPERTIES: A wide range of heat sealing; contains slip-antistatic and antiblocking additives; excellent optical properties; good mechanical properties; intended for contact with food; both side low coefficient of friction; without coatings and primers. APPLICATION: High quality solvent based rotogravure and flexographic printing; solvent based and solvent free lamination with polyurethane adhesives; manufacture of flexible packaging for food products; for high-speed vertical VFFS and horizontal HFFS packaging machines. 6

7 Thickness, ± 5 Properties Methods Unit HGHL mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68 Yield, ± 5 m 2 /kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89 Tensile strength, not less Elongation at break, not more Kinetic coefficient of friction Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less N/mm 2, TD MPa GOST ISO 527 D TD UT/UT +0,05 GOST ISO ,2 Т/Т D ,1 5 4 GOST ISO TD D UT/UT GOST ISO 527 Haze, not more GOST ISO Gloss at 45, not less T ISO 2813 D 882, F 88 D 1003 D 2457 N/15 mm 2,0 2,2 2,3 2,5 2,8 2,5 3,0 3,2 85 Heat sealing range at 1 bar, 1 sec.* UT/UT C Treatment level, not less T ISO 8296 D 2578 Dyne/cm, mn/m 38 Machine, longitudinal direction T Treated side of the film TD Transverse direction UT Untreated side of the film GOST Russian Federation standards * Typical value

8 Transparent films Biaxplen HGFL DESCRIPTION: Heat-sealing transparent BOPP film with a low threshold of welding, with high coefficient of friction for a special purposes, for high quality rotogravure and flexographic printing and lamination. B Treated modified heat sealable copolymer skin layer C Transparent oriented polypropylene core layer D Heat sealable, non treated skin layer with low seal intention temperature and high coefficient of friction MAIN PROPERTIES: A wide range of heat sealing; contains antistatic and antiblocking additives; excellent optical properties; good mechanical properties; intended for contact with food; high coefficient of friction stable in time; without coatings and primers. 8 APPLICATION: High quality solvent based rotogravure and flexographic printing; solvent based and solvent free lamination with polyurethane adhesives; manufacture of flexible packaging for food products; for vertical VFFS and horizontal HFFS packaging machines; laminating with PE and CPP films with a high content of slipping additives; to reduce the impact of slip additives transition from PE or CPP film to the BOPP film side, which leads to a significant coefficient of friction reduction. The high coefficient of friction of the HGFL film, provides a certain margin in this case; for a case in which the bondage process of packed products is present, for example, in pasta packaging; to save the packed packages in a single group without sliding over each other (if necessary); in the other cases, when slip reduction on BOPP side of the flexible packaging is necessary; for cold seal glue frame coating onto UT film side (if necessary).

9 Thickness, ± 5 Properties Methods Unit HGFL mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68 Yield, ± 5 m 2 /kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89 Tensile strength, not less Elongation at break, not more Kinetic coefficient of friction Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less N/mm 2, TD MPa GOST ISO 527 D TD UT/UT GOST ISO 8295 D , GOST ISO TD D UT/UT GOST ISO 527 Haze, not more GOST ISO Gloss at 45, not less T ISO 2813 D 882, F 88 D 1003 D 2457 N/15 mm 2,0 2,2 2,3 2,5 2,8 2,5 3,0 3,2 85 Heat sealing range at 1 bar, 1 sec.* UT/UT C Treatment level, not less T ISO 8296 D 2578 Dyne/cm, mn/m ,20-0,05 Machine, longitudinal direction T Treated side of the film TD Transverse direction UT Untreated side of the film GOST Russian Federation standards * Typical value

10 Transparent films Biaxplen PGR DESCRIPTION: Transparent release BOPP film for high quality rotogravure and flexographic printing and lamination; for the production of flexible packaging with frame cold seal glue. B Treated modified copolymer skin layer C Transparent oriented polypropylene core layer D Non heat sealable, untreated release skin layer with low coefficient of friction MAIN PROPERTIES: UT side has a release properties to the latex cold seal glue; high optical: transparency and gloss and high physical and mechanical properties; low coefficient of friction, including hot surfaces, specially for HFFS machines; contains antistatic, slip-antiblocking and release additives; intended for contact with food; chemically resistant to oils, fats and chemicals. APPLICATION: High quality rotogravure and flexographic solvent printing; solvent or solventless polyurethane laminating adhesives; for the production of flexible packaging (typically duplex) with frame cold seal glue. 10

11 Properties Methods Unit PGR Thickness, ± 5 mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 13,65 18,20 22,75 27,30 31,85 Yield, ± 5 m 2 /kg 73,26 54,95 43,96 36,63 31, Tensile strength, not less N/mm 2, MPa TD 250 GOST ISO 527 D Elongation at break, not more TD 70 Kinetic coefficient of friction UT/UT GOST ISO 8295 D ,25 +0,10-0,15 Thermal shrinkage at 120 C, 5 min, not more 5 4 GOST ISO D1204 TD 2 2 Haze, not more GOST ISO D Gloss at 45, not less UT ISO 2813 D Treatment level, not less T ISO 8296 D 2578 Dyne/cm, mn/m 38 Machine, longitudinal direction T Treated side of the film TD Transverse direction UT Untreated side of the film GOST Russian Federation standards * Typical value

12 Transparent films Biaxplen HGSL DESCRIPTION: Heat sealable transparent BOPP film for hot climate with a standard coefficient of friction and low heat sealing threshold for packaging machines. For high quality rotogravure and flexographic printing and lamination. B Treated modified heat sealable copolymer skin layer C Transparent oriented polypropylene core layer D Heat sealable, non treated skin layer with low seal intention temperature and standard coefficient of friction MAIN PROPERTIES: A wide range of heat sealing; contains low speed migratory slip-antistatic additives; less slippery surface in comparison with HGPL film; contains an antiblock additives; stable optical properties; good physical and mechanical properties; intended for contact with food; standard coefficient of friction; without coatings and primers. APPLICATION: High quality solvent based rotogravure and flexographic printing; solvent based and solvent free lamination with polyurethane adhesives; manufacture of flexible packaging for food products; for vertical VFFS packaging machines as film in laminate, turned to pulling belts; for horizontal HFFS packaging machines as internal film in laminate (turned to the product); production of decorative packaging for flowers, gift wrap and etc.; for cold seal glue frame coating onto UT film side (if necessary). 12

13 Thickness, ± 5 Properties Methods Unit HGSL mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68 Yield, ± 5 m 2 /kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89 Tensile strength, not less Elongation at break, not more Kinetic coefficient of friction UT/UT GOST ISO 8295 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less N/mm 2, TD MPa GOST ISO 527 D TD D , GOST ISO TD D UT/UT GOST ISO 527 Haze, not more GOST ISO Gloss at 45, not less T ISO 2813 D 882, F 88 D 1003 D 2457 N/15 mm 2,0 2,2 2,3 2,5 2,8 2,3 2,8 3,0 85 Heat sealing range at 1 bar, 1 sec.* UT/UT C Treatment level, not less T ISO 8296 D 2578 Dyne/cm, mn/m ,10-0,15 Machine, longitudinal direction T Treated side of the film TD Transverse direction UT Untreated side of the film GOST Russian Federation standards * Typical value

14 Transparent films Biaxplen HGHW DESCRIPTION: Transparent heat sealable BOPP film with a wide temperature sealing range and low coefficient of friction for high speed packaging machines for high quality rotogravure and flexographic printing. B Treated modified heat sealable copolymer skin layer C Transparent oriented polypropylene core layer D Heat sealable, non treated skin layer with very low seal intention temperature and standard coefficient of friction MAIN PROPERTIES: A very wide range of heat sealing; sufficiently low coefficient of friction, including the heated surfaces for high-speed packaging machines; contains slip-antistatic and antiblocking additives; excellent optical properties; good mechanical properties; intended for contact with food; permanent coefficient of friction, even after printing and lamination; without coatings and primers. APPLICATION: High quality solvent based rotogravure and flexographic printing; solvent based and solvent free lamination with polyurethane adhesives; manufacture of flexible packaging for food products; for high speed vertical VFFS and horizontal HFFS packaging machines; for heatsealing by UT / UT (fin seam) and UT / T (overlap) film sides;. for applications requiring temperature decrease or increase the speed of heat sealing; not for corona treatment of UT side and not for cold seal coating of UT side. 14

15 Thickness, ± 5 Properties Methods Unit HGHW mkm Density * g/cm 3 0,91 Weight, ± 5 g/m 2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68 Yield, ± 5 m 2 /kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89 Tensile strength, not less Elongation at break, not more Kinetic coefficient of friction Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1bar, 1 sec, not less N/mm 2, TD MPa GOST ISO 527 D TD UT / UT + 0,10 GOST ISO ,25 Т / Т D , GOST ISO TD D UT / T GOST ISO 527 Haze, not more GOST ISO Gloss at 45, not less T ISO 2813 Heat sealing range at 1bar, 1sec.* Treatment level, not less T ISO 8296 D 882, F 88 D 1003 D 2457 N/15mm 2,0 2,2 2,3 2,5 2,8 2,5 3 3,2 85 UT/ UT C T / T * D 2578 Dyne/ cm, mn/m Machine, longitudinal direction T Treated side of the film GOST Russian Federation standards TD Transverse direction UT Untreated side of the film * Typical value 36

16 Transparent films Biaxplen PGP DESCRIPTION: Transparent non heat sealable BOPP film for printing and lamination B Glossy, flame treated, none heat sealable polypropylene skin layer C Transparent biaxially oriented polypropylene D Glossy, none treated, none heat sealable polypropylene skin layer MAIN PROPERTIES: Film with high transparency and gloss; high and long time surface tension; high adhesion of printing and lamination; good sliding UT side for all known surfaces; good physical and mechanical properties; contains slip-antistatic and antiblocking additives; intended for contact with food; without coatings and primers. APPLICATION: As front film of the film in the production of flexible packaging with outstanding brilliance; the production of packaging for horizontal HFFS and VFFS vertical packaging machines; high quality solvent based rotogravure and flexographic printing; solvent based and solvent free lamination with polyurethane adhesives; in cases in which the exception of heat sealability is required for front side of flexible packaging; the production of packaging for hand or machine wrap boxes and gifts; not for use in original form (without lamination) in the production of packets of any kind. 16

17 Thickness, ± 5 Properties Methods Unit PGP mkm Density * g/cm 3 0,91 Weight, ± 5 g/m 2 18,2 22,75 27,30 31,85 36,40 43,68 Yield, ± 5 m 2 /kg 54,95 43,96 36,63 31,40 27,47 22,89 Tensile strength, not less Elongation at break, not more Kinetic coefficient of friction UT / UT GOST ISO 8295 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1bar, 1 sec, not less N/mm 2, 140 TD MPa 250 GOST ISO 527 D TD 70 D ,3 4 GOST ISO TD D UT/UT GOST ISO 527 Haze, not more GOST ISO Gloss at 45, not less T ISO 2813 D 882, F 88 D 1003 D 2457 N/15mm Non heat sealable 2 90 Heat sealing range at 1bar, 1sec.* UT / UT C Non heat sealable Treatment level, not less T ISO 8296 D 2578 Dyne/cm, mn/m ,1-0,1 Machine, longitudinal direction T Treated side of the film TD Transverse direction UT Untreated side of the film GOST Russian Federation standards * Typical value

18 Metallized films Biaxplen HMPL.M DESCRIPTION: Metallized heat sealable BOPP film with a low sealing intention temperature and standard coefficient of friction for printing and lamination. B Aluminum layer C Treated modified copolymer layer for aluminum adhesion D Transparent oriented polypropylene core layer E Heat sealable non treated, skin layer with standard coefficient of friction F MAIN PROPERTIES: Good adhesion of the aluminum layer; excellent optical and barrier properties of the metallized films; low threshold for welding, high adhesion of aluminum, good mechanical properties; stable standard coefficient of friction; contains slip-antiblock additives; intended for contact with food; without coatings and primers; UT side is allowed to accept activation inline on the printing press or laminator (if necessary). APPLICATION: High quality rotogravure and flexographic solvent based printing; for lamination with solvent based or solventless polyurethane adhesives; manufacture of flexible packaging for food products; packaging for vertical VFFS and horizontal HFFS packaging machines; for production of fully wrapped labels for bottles; UT side can be coated by frame cold seal glue. 18

19 Thickness, ± 5 Properties Methods Unit HMPL.M mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 Yield, ± 5 m 2 /kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 Tensile strength, not less Elongation at break, not more N/mm 2, MPa TD GOST ISO 527 D TD Kinetic coefficient of friction UT/UT GOST ISO 8295 D ,3 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less UT/UT GOST ISO GOST ISO D1204 TD 3 2 D 882, F 88 N/15 mm 2,0 2,2 2,3 2,5 2,8 Heat sealing range at 1 bar, 1 sec.* UT/UT С Optical density, not less 1,8 Treatment level, not less** T ISO 8296 D 2578 Dyne/cm, mn/m ,15-0,15 Machine, longitudinal direction T Metallized side TD Transverse direction UT Untreated, non metallized film side GOST Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 15 days from the date of manufacture indicated on roll label

20 Metallized films Biaxplen HMPLB.M DESCRIPTION: Metallized heatsealable BOPP film with low sealing threshold and standard coefficient of friction, with barrier properties, for printing and lamination. B Aluminum layer with increased thickness C Treated modified layer for high adhesion to aluminum D Transparent oriented polypropylene core layer E Heat sealable, non treated skin layer with standard coefficient of friction MAIN PROPERTIES: More thick coating of aluminium is firmly bound to the film high barrier properties to oxygen and water vapor; low threshold for heat sealing, high adhesion of aluminum, good mechanical properties; permanent standard coefficient of friction; contains no migratory antiblock and slip additives; intended for contact with food; without coating or primer. APPLICATION: High quality rotogravure and flexographic solvent based printing; for lamination with solvent based or solventless polyurethane adhesives; manufacture of flexible packaging for the food with long shelf life: cakes, sunflower seeds, candies, chips and the like; for vertical VFFS and horizontal HFFS packaging machines; for cold seal glue frame coating onto UT film side (if necessary). 20

21 Thickness, ± 5 Properties Methods Unit HMPLB.M mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 16,38 18,20 27,30 31,85 36,40 Yield, ± 5 m 2 /kg 61,05 54,95 36,63 31,40 27,47 Tensile strength, not less Elongation at break, not more N/mm 2, MPa TD GOST ISO 527 D TD Kinetic coefficient of friction UT/UT GOST ISO 8295 D ,3 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less UT/UT GOST ISO GOST ISO D1204 TD 3 2 D 882, F 88 N/15 mm 2,0 2,3 Heat sealing range at 1 bar, 1 sec.* UT/UT С Optical density, not less 2,3 Treatment level, not less** T ISO 8296 D 2578 Dyne/cm, mn/m 36 Water vapour transmission rate at 38 C, 90 rel.humidity, 24 h, not more F 1249 g/m 2 /24 h 1,0 Oxygen transmission rate at 23 С, 24 h, not more D 3985 cm 3 /m 2 /24 h ,10-0,10 Machine, longitudinal direction T Metallized side TD Transverse direction UT Untreated, non metallized film side GOST Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 30 days from the date of manufacture indicated on roll label

22 Metallized films Biaxplen HOHMLB.M DESCRIPTION: Metallized white pearl microporous heatsealable BOPP film with increased barrier properties for printing and laminations for production of flexible packaging for products with long shelf life. B Aluminum layer with increased thickness C Treated modified layer for high adhesion to aluminum D Oriented polypropylene tie layer E White Pearl cavitated core layer of orinted polypropylene F Oriented polypropylene tie layer G White pearl heat sealable, non treated skin layer with standard coefficient of friction MAIN PROPERTIES: Metallized side with high adhesion to the film; low threshold for heat welding, increased barrier properties and stable coefficient of friction; contains mineral fillers as calcium carbonate and titanium dioxide; good protection from UV and sunlight; intended for contact with food; pearl side (UT) easily takes an activation, at 200 m/min corona power 4 KW is enough for proper printing or lamination; without coating or primer. APPLICATION: High quality rotogravure and flexographic solvent based printing; for both side printing or in center of triplex lamination; for lamination with solvent based or solventless polyurethane adhesives; production of flexible packaging with frame cold glue; manufacture of flexible packaging for products with high shelf life; manufacture of lid for trays with food, typically in center of triplex; production of flexible packaging for the bouillon cubes. 22

23 Thickness, ± 5 Properties Methods Unit HOHMLB.M mkm Density* g/cm 3 0,7 Weight, ± 5 g/m 2 21,0 24,5 28,0 Yield, ± 5 m 2 /kg 47,6 40,8 35,7 Tensile strength, not less Elongation at break, not more 70 N/mm 2, MPa TD 140 GOST ISO 527 D TD 60 Kinetic coefficient of friction UT/UT GOST ISO 8295 D ,4 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less UT/UT GOST ISO GOST ISO D1204 TD 2 D 882, F 88 N/15 mm 2,5 Heat sealing range at 1 bar, 1 sec* UT/UT С Optical density, not less 2,5 Treatment level, not less** T ISO 8296 D 2578 Dyne/cm, mn/m 36 Water vapour transmission rate at 38 C, 90 rel. humidity, 24 h, not more F 1249 g/m 2 /24 h 1 Oxygen transmission rate at 23 С, 24 h, not more D 3985 cm 3 /m 2 /24 h 90 +0,1-0,1 Machine, longitudinal direction T Metallized side TD Transverse direction UT White pearl side, untreated side GOST Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 15 days from the date of manufacture indicated on roll label

24 Metallized films Biaxplen HMIL.M DESCRIPTION: Metallized heat sealable BOPP film with a low sealing intention temperature, long time surface tension shelf life and standard coefficient of friction for printing and lamination. B Aluminum layer C Treated modified copolymer layer for aluminum adhesion D Transparent oriented polypropylene core layer E Heat sealable non treated, skin layer with standard coefficient of friction F MAIN PROPERTIES: Excellent adhesion of the aluminum layer; long time surface tension shelf life; good optical and barrier properties of the metallized films; low threshold for welding, high adhesion of aluminum, good mechanical properties; stable standard coefficient of friction; contains slip-antiblock additives; intended for contact with food; without coatings and primers; UT side is allowed to accept activation inline on the printing press or laminator (if necessary). APPLICATION: High quality rotogravure and flexographic solvent based printing; for lamination with solvent based or solventless polyurethane adhesives; manufacture of flexible packaging for food products; packaging for vertical VFFS and horizontal HFFS packaging machines; for production of fully wrapped labels for bottles; UT side can be coated by frame cold seal glue. 24

25 Thickness, ± 5 Properties Methods Unit HMIL.M mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 Yield, ± 5 m 2 /kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 Tensile strength, not less Elongation at break, not more N/mm 2, MPa TD GOST ISO 527 D TD Kinetic coefficient of friction UT/UT GOST ISO 8295 D ,3 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less UT/UT GOST ISO GOST ISO D1204 TD 3 2 D 882, F 88 N/15 mm 2,0 2,2 2,3 2,5 2,8 Heat sealing range at 1 bar, 1 sec.* UT/UT С Optical density, not less 1,8 Treatment level, not less** T ISO 8296 D 2578 Water vapour transmission rate at 38 C, 90 rel. humidity, 24 h* Oxygen transmission rate at 23 С, 0 rel.humidity 24 h* Dyne/cm, mn/m F 1249 g/m 2 /24 h 1 D 3985 cm 3 /m 2 /24 h ,15-0,15 Machine, longitudinal direction T Metallized side TD Transverse direction UT Untreated, non metallized film side GOST Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 30 days from the date of manufacture indicated on roll label

26 Metallized films Biaxplen P.M DESCRIPTION: None heat sealable metallized BOPP film for the production of decorative packaging. With increased coefficient of friction. for printing and lamination and for decorative packaging. B Aluminum layer C Treated modified copolymer layer for aluminum adhesion D Transparent oriented polypropylene core layer E Non heat sealable skin layer with high coefficient of friction, without treatment (by default) MAIN PROPERTIES: Standard barrier properties of metallized films; contains antiblock additives; mechanical properties are good; high adhesion of the aluminum layer; intended for contact with food; without coating or primer. APPLICATION: High quality rotogravure and flexographic solvent based printing; for lamination with solvent based or solventless polyurethane adhesives; production of decorative packaging for flowers, gift wrap and etc.; heat sealing by string is possible; lamination with films, paper and cardboard; in case of both side corona treatment: - lamination as middle of triplex or both side printing; - cold seal glue coating onto non metalized film side. 26

27 Thickness, ± 5 Properties Methods Unit P.M mkm Density * g/cm 3 0,91 Weight, ± 5 g/m 2 18,2 22,8 27,3 31,9 36,4 Yield, ± 5 m 2 /kg 54,9 44,0 36,6 31,4 27,5 Tensile strength, not less Elongation at break, not more 140 N/mm 2, MPa TD 280 GOST ISO 527 D TD 70 Kinetic coefficient of friction UT / UT GOST ISO 8295 D ,3 Thermal shrinkage at 120 C, 5 min, not more 4 GOST ISO D1204 TD 2 Treatment level, not less ** T ISO 8296 D 2578 Dyne/cm, mn/m Optical density, not less 1,8 36 / 36 *** + 0,1-0,1 Machine, longitudinal direction T Metallized side TD Transverse direction UT Untreated, non metallized film side GOST Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 30 days from the date of manufacture indicated on roll label *** When the order is placed for both side corona treatment Shelf life of activation for non metallized film side is 6 months

28 Metallized films Biaxplen HMPLA.M DESCRIPTION: Metallized heatsealable BOPP film with low sealing threshold and standard coefficient of friction, with barrier properties for printing and lamination with glue or hot melt. B Aluminum layer with increased thickness (T) C Treated modified layer for aluminum coating, with increased heat resistance D Transparent oriented polypropylene core layer E Heat sealable, non treated skin layer with standard coefficient of friction (UT) MAIN PROPERTIES: Thick coating of aluminium; increased heat resistance for metallized layer; long time surface tension shelf life; high barrier properties to oxygen and water vapor; increased stiffness; low threshold for heat sealing, high adhesion of aluminum, good mechanical properties; permanent standard coefficient of friction; contains no migratory antiblock and slip additives; intended for contact with food; without coating or primer. APPLICATION: High quality rotogravure and flexographic solvent based printing; hot melt lanination; for lamination with solvent based or solventless polyurethane adhesives; manufacture of flexible packaging for the food with long shelf life: cakes, sunflower seeds, candies, chips and the like; for vertical VFFS and horizontal HFFS packaging machines; for cold seal glue frame coating onto UT film side (if necessary). 28

29 Thickness, ± 5 Properties Methods Unit HMPLA.M mkm Density * g/cm 3 0,91 Weight, ± 5 g/m 2 16,38 18,20 27,30 31,85 36,40 Yield, ± 5 m 2 /kg 61,05 54,95 36,63 31,40 27,47 Tensile strength, not less Elongation at break, not more N/mm 2, MPa TD GOST ISO 527 D TD Kinetic coefficient of friction UT / UT GOST ISO 8295 D ,3 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1bar, 1 sec, not less 5 4 GOST ISO D1204 TD 3 2 UT/UT GOST ISO 527 D 882, F 88 N/15mm 2,0 2,3 Heat sealing range at 1bar, 1sec.* UT / UT С Optical density, not less 2,5 Treatment level, not less ** T ISO 8296 D 2578 Dyne/cm, mn/m Water vapour transmission rate at 38 C, 90 rel.humidity, 24h, not more F 1249 g/m 2 /24h 0,1 Oxygen transmission rate at 23 С, 24h, not more D 3985 cm 3 /m 2 /24h ,10-0,10 Machine, longitudinal direction T Metallized side TD Transverse direction UT Untreated, non metallized film side GOST Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 90 days from the date of manufacture indicated on roll label

30 Metallized films Biaxplen PMP.M DESCRIPTION: Metallized non heat sealable both side treated BOPP film with standard coefficient of friction for both side printing and lamination B Aluminum layer C Treated modified copolymer layer for aluminum adhesion D Transparent oriented polypropylene core layer E Treated non heat sealable skin layer with standard coefficient of friction MAIN PROPERTIES: Both sides (T, UT) activated film; standard barrier properties of metallized films; standard coefficient of friction; mechanical properties and aluminum adhesian are good; contains no migratory antiblock and slip additives; intended for contact with food; without coating or primer. APPLICATION: Rotogravure and flexographic solvent based one or both side printing; for both side lamination with solvent based or solventless polyurethane adhesives; lamination with films, paper and cardboard, as well as in the center of the triplex in flexible packaging; for the production of labels with both side printed design; 30

31 Thickness, ± 5 Properties Methods Unit PMP.M mkm Density * g/cm 3 0,91 Weight, ± 5 g/m 2 18,2 22,8 27,3 31,9 36,4 Yield, ± 5 m 2 /kg 54,9 44,0 36,6 31,4 27,5 Tensile strength, not less Elongation at break, not more 140 N/mm 2, MPa TD 250 GOST ISO 527 D TD 70 Kinetic coefficient of friction UT / UT GOST ISO 8295 D ,3 Heat sealing strength at 130 C, 1bar, 1 sec, not less Thermal shrinkage at 120 C, 5 min, not more UT / UT GOST ISO 527 D 882, F 88 N/15mm 4 GOST ISO D1204 TD 2 Treatment level, not less ** T Dyne/cm, 36 ISO 8296 D 2578 Treatment level, not less *** UT mn/m 38 Optical density, not less 2,2 Heat sealing range at 1bar, 1sec.* UT / UT С Water vapour transmission rate at 38 C, 90 rel.humidity, 24h, not more F 1249 g/m 2 /24h 1 Oxygen transmission rate at 23 C, 24h, not more D 3985 cm 3 /m 2 /24h 100-0,1 + 0,1 Machine, longitudinal direction T Metallized side TD Transverse direction UT Non metallized film side GOST Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 15 days from the date of manufacture indicated on roll label *** Activation shelf-life for UT activated side is at least for 6 months

32 Metallized films Biaxplen HMHW.M DESCRIPTION: Metallized BOPP heat sealable film with a very wide range of welding and a standard coefficient of friction for high speed packaging machines. for high quality rotogravure and flexographic printing. B Ò C Aluminum layer D Treated modified copolymer layer for aluminum adhesion E Transparent oriented polypropylene core layer F Heat sealable, non treated skin layer with very low seal intention temperature and standard coefficient of friction MAIN PROPERTIES: Good adhesion of the aluminum layer; good optical and barrier properties; a very wide range of heat sealing; sufficiently low coefficient of friction, including the heated surfaces for high-speed packaging machines; contains slip-antiblock additives; intended for contact with food; without coatings and primers. APPLICATION: High quality rotogravure and flexographic solvent based printing; for lamination with solvent based or solventless polyurethane adhesives; manufacture of flexible packaging for food products; for high speed vertical VFFS and horizontal HFFS packaging machines; for applications requiring temperature decrease or increase the speed of heat sealing; in some cases, instead of using packaging with frame glue cold welding; not for corona treatment of UT side; not for cold seal coating for UT side. 32

33 Thickness, ± 5 Properties Methods Unit HMHW.M mkm Density * g/cm 3 0,91 Weight, ± 5 g/m 2 13,65 18,20 22,75 27,30 31,85 36,40 Yield, ± 5 m 2 /kg 73,26 54,95 43,96 36,63 31,40 27,47 Tensile strength, not less Elongation at break, not more Kinetic coefficient of friction UT / UT GOST ISO 8295 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1bar, 1 sec, not less N/mm 2, TD MPa GOST ISO 527 D TD D , GOST ISO TD D UT / UT GOST ISO 527 D 882, F 88 N/15mm 2,0 2,3 2,5 2,8 Heat sealing range at 1bar, 1sec.* UT / UT С Optical density, not less 1,8 Treatment level, not less ** T ISO 8296 Water vapour transmission rate at 38 C, 90 rel.humidity, 24h * Oxygen transmission rate at 23 C, 0 rel.humidity 24h * D 2578 F 1249 D 3985 Dyne/cm, mn/m g/m 2 /24h 1 cm 3 / m 2 /24h Machine, longitudinal direction T Metallized side TD Transverse direction UT Untreated, non metallized film side GOST Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 15 days from the date of manufacture indicated on roll label

34 Non-food films Biaxplen PGA DESCRIPTION: Transparent BOPP film for general purposes for the production of adhesive tapes. B Glossy, treated, none heat sealable skin layer C Transparent biaxially oriented polypropylene D Glossy, non treated (by default), none heat sealable skin layer MAIN PROPERTIES: Contains antiblocking additives; very high optical properties: transparency and gloss; high mechanical properties; good flatness of the film; intended for contact with food (if necessary); low thermo shrinkage to save print sizes in glue drying process; without coatings and primers. APPLICATION: High quality solvent based rotogravure and flexographic printing; production of adhesive tapes (skotch) with hot melt and water based adhesives; solvent based and solvent free lamination with polyurethane adhesives (if necessary). 34

35 Thickness, ± 5 Properties Methods Unit PGA mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 18,20 20,93 22,75 23,66 25,48 29,12 36,40 Yield, ± 5 m 2 /kg 54,95 47,78 43,96 42,27 39,25 34,34 27,47 Tensile strength, not less Elongation at break, not more N/mm 2, MPa TD 250 GOST ISO 527 D TD 70 Kinetic coefficient of friction UT/UT GOST ISO 8295 D ,5 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less UT/UT GOST ISO GOST ISO D1204 TD 2 D 882, F 88 N/15 mm Non heat sealable Haze, not more GOST ISO D Gloss at 45, not less T ISO 2813 D Heat sealing range at 1 bar, 1 sec.* UT/UT C None heat sealable Treatment level, not less T ISO 8296 D 2578 Dyne/cm, mn/m 38**/44 *** + 0,1-0,1 Machine, longitudinal direction T Treated side of the film TD Transverse direction UT Untreated side of the film GOST Russian Federation standards * Typical value ** In case of corona treatment *** In case of flame treatment

36 Non-food films Biaxplen PGD DESCRIPTION: Transparent non heat sealable BOPP film for general purposes and decorative packaging. B Glossy, treated, none heat sealable polypropylene skin layer C Transparent biaxially oriented polypropylene D Glossy, none treated, none heat sealable polypropylene skin layer MAIN PROPERTIES: Contains slip-antistatic and antiblocking additives; very high optical properties: transparency and gloss; good physical and mechanical properties; intended for contact with food; without coatings and primers. APPLICATION: High quality solvent based rotogravure and flexographic printing; production of decorative packaging for flowers, gift wrap and etc.; solvent based and solvent free lamination with polyurethane adhesives (if necessary); in cases in which the exception of heat sealability is required. 36

37 Thickness, ± 5 Properties Methods Unit PGD mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 18,2 22,75 27,30 31,85 36,40 43,68 Yield, ± 5 m 2 /kg 54,95 43,96 36,63 31,40 27,47 22,89 Tensile strength, not less Elongation at break, not more 140 N/mm 2, MPa TD 250 GOST ISO 527 D TD 70 Kinetic coefficient of friction UT/UT GOST ISO 8295 D ,45 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less UT/UT GOST ISO GOST ISO D1204 TD 2 D 882, F 88 N/15 mm Non heat sealable Haze, not more GOST ISO D Gloss at 45, not less T ISO 2813 D Heat sealing range at 1 bar, 1 sec.* UT/UT C Non heat sealable Treatment level, not less T ISO 8296 D 2578 Dyne/cm, mn/m ,1-0,1 Machine, longitudinal direction T Treated side of the film TD Transverse direction UT Untreated side of the film GOST Russian Federation standards * Typical value

38 Non-food films Biaxplen PGT DESCRIPTION: Transparent non heat sealable BOPP film for textile packaging, general purposes and decorative overwrapping with high antistatic properties. B Corona treated, copolymer skin layer C Transparent biaxially oriented polypropylene with antistatic D Glossy, none treated, none heat sealable polypropylene skin layer MAIN PROPERTIES: Contains efficient antistatic and antiblocking additives; corona treated film; very high optical properties: transparency and gloss; good physical and mechanical properties; high antistatic properties; intended for contact with food; without coatings and primers. APPLICATION: High quality solvent based rotogravure and flexographic printing; for textiles packaging, production of decorative and flowers packagings, gift wrapping and etc.; for heat sealing by hot wire or knife (sealing and cutting simultaneously); solvent based and solvent free lamination with polyurethane adhesives (if necessary); in cases in which the exception of heat sealability and/or stickiness is required at the increased temperatures. 38

39 Thickness, ± 5 Properties Methods Unit PGT mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 18,20 22,75 25,48 27,30 31,85 36,40 Yield, ± 5 m 2 /kg 54,95 43,96 39,25 36,63 31,40 27,47 Tensile strength, not less Elongation at break, not more 140 N/mm 2, MPa TD 250 GOST ISO 527 D TD 70 Kinetic coefficient of friction UT/UT GOST ISO 8295 D ,4 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less UT/UT GOST ISO GOST ISO D1204 TD 2 D 882, F 88 N/15 mm Non heat sealable Haze, not more GOST ISO D Gloss at 45, not less T ISO 2813 D Heat sealing range at 1 bar, 1 sec.* UT/UT C Non heat sealable Treatment level, not less T ISO 8296 D 2578 Dyne/cm, mn/m ,1-0,1 Machine, longitudinal direction T Treated side of the film TD Transverse direction UT Untreated side of the film GOST Russian Federation standards * Typical value

40 Non-food films Biaxplen PWA DESCRIPTION: White none heat sealable opaque BOPP film for general purposes and production of adhesive tapes. B Glossy, treated, none heat sealable skin layer C Solid white opaque oriented polypropylene core layer D Glossy, non treated (by default), none heat sealable skin layer MAIN PROPERTIES: White appearance; high opacity; good mechanical properties; high protection from UV light; contains antiblocking and mineral filler as titanium dioxide; does not contain migratory additives; intended for contact with food (if necessary); without coatings and primers. APPLICATION: High quality solvent based rotogravure and flexographic printing; production of adhesive tapes (sktoch) with hot melt and water based adhesives; decorative wrapping or other packaging with protection from UV light; white appearance allows to exclude white inks from printing or/and exclude white adhesives; solvent based and solvent free lamination with polyurethane adhesives (if necessary). 40

41 Thickness, ± 5 Properties Methods Unit PWA mkm Density* g/cm 3 0,96 Weight, ± 5 g/m 2 22,08 24,00 26,88 30,72 Yield, ± 5 m 2 /kg 45,29 41,67 37,20 32,55 Tensile strength, not less Elongation at break, not more N/mm 2, MPa TD GOST ISO 527 D TD 70 Coefficient of friction, kinetic UT/UT GOST ISO 8295 D ,5 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 С, 1 bar, 1 sec UT/UT GOST ISO GOST ISO D1204 TD 2 F 88; D882 N/15 mm None heat sealable Light transmission, not more GOST ISO D Gloss at 45, not less T ISO 2813 D Heat sealing range at 1 bar, 1 sec* UT/UT C None heat sealable Treatment level, not less T ISO 8296 D 2578 Dyne/cm, mn/m 38 **/42 *** + 0,1-0,1 Machine, longitudinal direction T Treated side of the film TD Transverse direction UT Untreated side of the film GOST Russian Federation standards * Typical value ** In case of corona treatment *** In case of flame treatment

42 Matt films Biaxplen MGS DESCRIPTION: One side matt BOPP film for general purposes, for high quality rotogravure and flexographic printing and lamination for flexible packaging and labels. B Matt not treated side C Transparent oriented polypropylene core layer D Treated modified heat sealable copolymer skin layer MAIN PROPERTIES: Matte appearance; contains slip-antistatic and anti-blocking additives; good ink adhesion; good mechanical properties; low coefficient of friction; intended for contact with food; without coatings and primers. APPLICATION: High quality solvent based rotogravure and flexographic printing; solvent based and solvent free lamination with polyurethane adhesives; manufacture of flexible packaging for food products; for vertical VFFS and horizontal HFFS packaging machines; for production of decorative packaging for flowers, gift wrap and etc.; for production of fully wrapped labels for bottles; to make the flexible packaging or labels matte (paper like) appearance. 42

43 Thickness, ± 5 Properties Methods Unit MGS mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 13,65 18,2 31,85 Yield, ± 5 m 2 /kg 73,26 54,95 31,40 Tensile strength, not less Elongation at break, not more 125 N/mm 2, MPa TD 240 GOST ISO 527 D TD 80 Kinetic coefficient of friction UT/UT GOST ISO 8295 D ,25 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less UT/UT GOST ISO GOST ISO D1204 TD 2 D 882, F 88 +0,15-0,15 N/15 mm 2,0 2,3 2,5 Haze, not less GOST ISO D Gloss at 45, not more T ISO 2813 D Heat sealing range at 1 bar, 1 sec.* UT/UT C Treatment level, not less T ISO 8296 D 2578 Dyne/cm, mn/m 38 Machine, longitudinal direction T Treated glossy side of the film TD Transverse direction UT Untreated matt side of the film GOST Russian Federation standards * Typical value

44 Matt films Biaxplen MGD DESCRIPTION: Both side matt film for general purposes, for flexographic printing, for decorative packaging. B Matt not treated side C Transparent oriented polypropylene core layer D Matt treated side E MAIN PROPERTIES: Both side matte appearance; contains slip-antistatic additives; good mechanical properties; standard coefficient of friction; intended for contact with food; without coatings and primers. APPLICATION: Solvent based flexographic printing; for production of decorative packaging for flowers, gift wrap and etc.; heat sealing by string is possible; to make the flexible packaging or labels matte (paper like) appearance. 44

45 Thickness, ± 5 Properties Methods Unit MGD mkm Density* g/cm 3 0,91 Weight, ± 5 g/m 2 18,2 27,3 31,85 Yield, ± 5 m 2 /kg 54,95 36,63 31,40 Tensile strength, not less Elongation at break, not more 125 N/mm 2, MPa TD 240 GOST ISO 527 D TD 80 Kinetic coefficient of friction UT/UT GOST ISO 8295 D ,35 Thermal shrinkage at 120 C, 5 min, not more Heat sealing strength at 130 C, 1 bar, 1 sec, not less UT/UT GOST ISO GOST ISO D1204 TD 2 D 882, F 88 +0,10-0,15 N/15 mm 2,3 2,4 2,5 Haze, not less GOST ISO D Gloss at 45, not more T ISO 2813 D Heat sealing range at 1 bar, 1 sec.* UT/UT C Treatment level, not less T ISO 8296 D 2578 Dyne/cm, mn/m 38 Machine, longitudinal direction T Treated matt side of the film TD Transverse direction UT Untreated matt side of the film GOST Russian Federation standards * Typical value