Stereolithography Material Properties

Transcription

1 Details Stereolithography Standard lead time: From 2 days, depending on the size of the parts and the number of components. Standard accuracy: Standard stereolithography ± 0.2% (min ± 0.2mm). Sensitive to UV-light (e.g. direct sunlight). Maximum part dimensions: Without post-finishing, dependent upon the orientation of the layers. Different finishes from high gloss to a rough texture are obtained by post-finishing. 2100x700x800mm Capacity: Materialise has over 30 stereolithography machines: 4 Next Day machines; 13 Mammoth machines; 8 SLA250 machines; 3 SLA3500 machines; 1 SLA5000 machine and 4 SLA7000 machines. Materials: Tusk Somos SolidGrey3000 / Tusk2700W NeXt NanoTool WaterClear Details Next Day Stereolithography Lead time: Accuracy: Parts ordered before 12am are shipped the same day. ± 0.2% (min ± 0.2mm) Basic finishing Maximum part dimensions: 650x650x480mm (x, y, z) Capacity: Materials: The overall Next Day capacity is sufficient to produce supported parts that fit in an envelope of 650x650x480mm (x, y, z). Our stereolithography machine park houses 4 Next Day machines. Tusk2700W Details Mammoth Stereolithography Lead time: Accuracy: Maximum part dimensions: Capacity: Materials: From 2 days, depending on the size of the parts and the number of components ± 0.2% (min ± 0.2mm) Different finishes from smooth finish up to high gloss can be obtained by post-finishing 2100x700x800mm 13 Mammoth machines Tusk Somos SolidGrey3000

2 Tusk Somos SolidGrey3000 Tensile Modulus MPa D638M Tensile Strength at yield MPa D638M Elongation at Yield % D638M 3.0 Elongation at Break % D638M Flexural Modulus MPa D790M Hardness ShoreD D Notched Izod Impact J/m D256A Water Absorption % D Tg C E a Deflection Temperature (0.46MPa) C D648-07B Deflection Temperature (1.82MPa) C D648-07B Appearance Opaque Gray Stiff Automotive body parts Machine covers concept models Robust scale models / Tusk2700W Tensile Modulus MPa D638M Tensile Strength MPa D638M Elongation at Break % D638M Flexural Modulus MPa D790M Flexural Strength MPa D790M Notched Izod Impact J/m D256A Hardness Shore D D Heat Deflection t C D648-98c at 0.46 MPa: at 1.81 MPa: Transparent or white Transparent () Strong Wind tunnel testing Water flow analysis ABS-like parts Tensile Modulus MPa D638M 2310 Tensile Strength MPa D638M 43.8 Elongation at Break % D638M 16 Flexural Modulus MPa D790M 2130 Flexural Strength MPa D790M 70.5 Notched Izod Impact J/m D256A 22 Hardness Shore D D Water Absorption % D % Tg C E Heat Deflection t C D648-98c at 0.46 MPa: 56 at 1.82 MPa: 47 Good surface quality Good thermal properties Impellers Duct work and connectors Automotive housings Dashboard assemblies

3 Tensile Modulus MPa D638M Tensile Strength MPa D638M Elongation at Break % D638M Flexural Modulus MPa D790M Flexural Strength MPa D790M Notched Izod Impact J/m D256A Hardness Shore D D Heat Deflection t at 0,46 MPa C D Flexible Automotive components Electronic housings PP-like parts Translucent NeXt Tensile Modulus MPa D638M Tensile Strength at Yield MPa D638M Tensile Strength at Break MPa D638M Elongation at Break % D638M 8-10 Flexural Modulus MPa D790M Flexural Strength MPa D790M Notched Izod Impact J/m D256A Water Absorption % D Tg C E Heat Deflection t C D648-98c at 0.46 MPa at 1.81 MPa Moisture Thermal properties Parts with high feature detail NanoTool Tensile Modulus MPa D638M Tensile Strength MPa D638M Elongation at Break % D638M Flexural Modulus MPa D790M Flexural Strength MPa D790M Notched Izod Impact J/m D256A Water Absorption % D Heat Deflection t C D648-98c at 0.46 MPa: 225 at 1.82 MPa: Off white Stiff High temperature Superior sidewall quality Brittle High temperature applications Automotive Aerospace

4 Tensile Modulus MPa D638M Tensile Strength MPa D638M Elongation at Break % D638M Flexural Modulus MPa D790M Notched Izod Impact J/m D256A Heat Deflection t C D648-98c at 0.45 MPa: 62 at 1.82 MPa: 54 Grey enclosures Replacing CNC machined parts WaterClear Tensile Modulus MPa D638M Tensile Strength at Break MPa D638M Elongation at Break % D638M 6-9 Flexural Modulus MPa D790M Flexural Strength MPa D790M Notched Izod Impact J/m D256A Water Absorption % D Tg C E Heat Deflection t C At 0.46 Mpa: At 1.82 MPa: transparant Optically clear Lower mechanical properties than Prototype parts that require fully neutral transparency

5 Name Impact strength Stiffness Humidity Heat Durability Appearance Mould Making Details Description Applications Tusk Somos SolidGrey3000 Excellent Excellent Excellent Good Good Grey Good Good Stiff Automotive body parts Machine covers concept models Robust scale models Tusk2700W Good Good Excellent Sensitive Good Optical clear with a light blue tinge or Excellent Moderate Wind tunnel testing Water flow analysis ABS-like parts Good Good Good Good Good Excellent Good Good surface quality Good thermal properties Good Moderate Moderate Moderate Good Translucent Moderate Good Flexible Excellent Good Good Good Good Grey Good Excellent NeXt Excellent Good Excellent Good Excellent Good Excellent Moisture Thermal properties Impellers Duct work and connectors Automotive housings Dashboard assemblies Automotive components Electronic housings PP-like parts enclosures Replacing CNC machined parts Parts with high feature detail NanoTool Sensitive Excellent Excellent Excellent Excellent Off white Moderate Excellent Stiff High temperature Superior sidewall quality Brittle WaterClear Good Good Moderate Sensitive Good Optical clear with neutral tinge Excellent Moderate Optically clear Lower mechanical properties than High temperature applications Automotive Aerospace Prototype parts that require fully neutral transparency faith and believed to be accurate, is provided for your guidance only. This information does not release a third party from conducting his own