A-200. Technical Information. Fluoroelastomers

Transcription

1 A-200 Technical Information Introduction Viton A-200* fluoroelastomer is an A-family gum polymer that demonstrates improved processing when compared with existing fluoroelastomers.viton A-200 is designed for use with the clean molding bisphenol curative, Viton Curative No. 50. Compared with other A-family dipolymers, Viton A-200 provides: Lower viscosity Improved mold flow Excellent extrusion characteristics Better mold release Less mold fouling Improved compression set resistance Product Description Chemical Composition Dipolymer of hexafluoropropylene and vinylidene fluoride Physical Form Free-flowing pellets Appearance Silver-gray Odor None Mooney Viscosity, ML at 121 C (250 F) 22 Specific Gravity 1.82 Storage Stability Excellent Solubility Low molecular weight esters and ketones Applications Transfer and injection molding O-rings Valve stem seals and shaft seals Parts with complicated shapes Extrusions Fuel hose and tubing Solution coating Fabric Tanks or chemical containers Safety and Handling Before handling or processing Viton A-200, read and be guided by the recommendations in the Chemours technical bulletin, Handling Precautions for Viton and Related Chemicals. Viton A-200 should be handled like other types of Viton. Keep off skin and wash well after handling. For the safe handling of other compounding ingredients, refer to the respective manufacturers literature. *Viton A-200 was formerly named VTR-5995.

2 Table 1. General Properties of Viton A-200 Compared with Viton E-45 Viton A-200 Viton E-45 Viton A Viton E MT Black (N990) High-Activity MgO 3 3 Calcium Hydroxide 6 6 Viton Curative No VPA No Mooney Scorch, MS at 121 C (250 F) Minimum, in lb Time to 1-unit rise, min M L, N m in lbf 0.5 (4) 0.7 (6) t s 2, min t c 90, min M H, N m in lbf 11.4 (96) 12.5 (108) Press Cured: 10 min at 177 C (350 F) Stress/Strain Original 100% Modulus, MPa (psi) 5.7 (820) 6.4 (930) Tensile Strength, MPa (psi) 11.1 (1,610) 11.9 (1,730) Elongation at Break, % Hardness, durometer A, pts Stress/Strain After 7 days/225 C (437 F) 100% Modulus, MPa (psi) 4.3 (620) 5.2 (750) Tensile Strength, MPa (psi) 9.7 (1,400) 10.8 (1,570) Elongation at Break, % Hardness, durometer A, pts Compression Set, Method B, O-Rings, % 22 hr at RT hr at 200 C (392 F) hr at 200 C (392 F)

3 Table 2. Hard and Soft Black Compounds in Viton A-200 Nominal Hardness (Durometer A) Viton A MT Black (N990) Viton Curative No Viton Curative No High-Activity MgO Calcium Hydroxide VPA No VPA No Mooney Scorch, MS at 121 C (250 F) Minimum, in lb pt rise, min M L, in lb t s 2, min t c 90, min M H, in lb Press Cured: 10 min at 180 C (356 F) Stress/Strain at 23 C (73 F) Original 100% Modulus, MPa (psi) 8.7 (1,240) 6.4 (930) 2.7 (390) 1.7 (250) 1.2 (170) Tensile Strength, MPa (psi) 12.9 (1,860) 12.4 (1,800) 10.6 (1.530) 7.5 (1,090) 7.7 (1,120) Elongation at Break, % Hardness, durometer A, pts Stress/Strain at 23 C (73 F) After aging 70 hr at 275 C (528 F) 100% Modulus, % change Tensile Strength, % change Elongation at Break, % change Hardness, points change Compression Set Resistance, Method B, O-Rings, % 70 hr at 0 C (32 F) hr at 23 C (73 F) hr at 200 C (392 F) hr at 232 C (450 F) Volume Swell, % ASTM #3 Oil, 70 hr at 200 C (392 F) Dexron ATF, 70 hr at 200 C (392 F) Methanol, 7 days at 23 C (73 F)

4 Table 3. Non-Black Fillers in Viton A-200 (Hardness 60 70) Control MT Black Multifex MM Viton A MT Black (N990) 25 Multifex MM 25 Nyad Celite Blanc Fixe 35 Ti-Pure R Calcium Hydroxide High-Activity MgO Viton Curative No VPA No VPA No Nyad 400 Celite 350 Blanc Fixe Ti-Pure R-960 Mooney Scorch, MS at 121 C (250 F) Minimum Rise in 30 min M L, in lb t s 2, min t c 90, min M H, in lb Press Cured: 10 min at 180 C (356 F) Stress/Strain at 23 C (73 F) Original 100% Modulus, MPa (psi) 4.7 (680) 3.7 (540) 5.1 (740) 6.8 (990) 2.8 (410) 2.9 (420) Tensile Strength, MPa (psi) 12.6 (1,830) 10.6 (1,540) 9.0 (1,300) 11.1 (1,610) 8.8 (1,280) 10.7 (1,550) Elongation at Break, % Hardness, durometer A, pts Stress/Strain at 23 C (73 F) After aging 70 hr at 275 C (528 F) 100% Modulus, % change Tensile Strength, % change Elongation at Break, % change Hardness, points change Compression Set, Method B, O-Rings, % 70 hr at 23 C (73 F) hr at 200 C (392 F) hr at 200 C (392 F) hr at 232 C (450 F) Volume Swell, % ASTM #3 Oil, 168 hr at 200 C (392 F) Methanol, 70 days at RT

5 Table 4. Curative Level in Viton A phr VC50 2 phr VC phr VC50 VC50+ VC20 VC50+ VC30 Viton A MT Black (N990) Calcium Hydroxide High-Activity MgO Viton Curative No Viton Curative No Viton Curative No VPA No VC50+ VPA No. 3 Mooney Scorch, MS at 121 C (250 F) Minimum Rise in 30 min M L, in lb t s 2, min t c 90, min M H, in lb Press Cured: 10 min at 180 C (356 F) Stress/Strain at 23 C (73 F) Original 100% Modulus, MPa (psi) 4.3 (620) 3.6 (520) 2.6 (380) 3.6 (520) 4.4 (640) 3.6 (520) Tensile Strength, MPa (psi) 11.7 (1,700) 12.1 (1,760) 10.6 (1,540) 11.7 (1,700) 11.9 (1,730) 12.6 (1,830) Elongation at Break, % Hardness, durometer A Stress/Strain at 23 C (73 F) After aging 7 days at 250 C (482 F) 100% Modulus, % change Tensile Strength, % change Elongation at Break, % change Hardness, points change Stress/Strain at 23 C (73 F) After aging 70 hr at 275 C (528 F) 100% Modulus, % change Tensile Strength, % change Elongation at Break, % change Hardness, points change Compression Set, Method B, O-Rings, % 70 hr at RT hr at 200 C (392 F) hr at 200 C (392 F) hr at 232 C (450 F)

6 Test Procedures Property Measured Compression Set Compression Set Low Temperature Compression Set, O-Rings Hardness Mooney Scorch Mooney Viscosity ODR (vulcanization characteristics measured with an oscillating disk cure meter) Property Change After Oven Heat-Aging Stress/Strain Properties 100% Modulus Tensile Strength Elongation at Break Stiffness, Torsional, Clash-Berg Temperature Retraction Volume Change in Fluids Test Procedure ASTM D3955, Method B (25% deflection) ASTM D1299, Method B (25% deflection) ASTM D1414 ASTM D2240, durometer A ASTM D1646, using the small rotor. Minimum viscosity and time to a 1-, 5-, or 10-unit rise are reported. ASTM D1646, ten pass 100 C (212 F), 121 C (250 F) ASTM D2084 ASTM D573 ASTM D412, pulled at 8.5 mm/sec (20 in/min) ASTM D1043 ASTM D1329 ASTM D471 Note: Test temperature is 24 C (75 F), except where specified otherwise. For more information, visit Viton.com The information set forth herein is furnished free of charge and based on technical data that Chemours believes to be reliable. It is intended for use by persons having technical skill, at their own discretion and risk. The handling precaution information contained herein is given with the understanding that those using it will satisfy themselves that their particular conditions of use present no health or safety hazards. Because conditions of product use are outside our control, Chemours makes no warranties, express or implied, and assumes no liability in connection with any use of this information. As with any material, evaluation of any compound under end-use conditions prior to specification is essential. Nothing herein is to be taken as a license to operate under or a recommendation to infringe any patents. NO PART OF THIS MATERIAL MAY BE REPRODUCED, STORED IN A RETRIEVAL SYSTEM OR TRANSMITTED IN ANY FORM OR BY ANY MEANS ELECTRONIC, MECHANICAL, PHOTOCOPYING, RECORDING OR OTHERWISE WITHOUT THE PRIOR WRITTEN PERMISSION OF CHEMOURS The Chemours Company FC, LLC. Viton, Ti-Pure, Chemours, the Chemours Logo, and any associated logos are trademarks or copyrights of The Chemours Company, its affiliates, or subsidiaries. Replaces: VTE-H D0710 C (9/16)