AXALTA COATING SYSTEMS Nap-Gard FBE Powder Coatings Decades of Performance. A World of Experience.
Nap-Gard FBE Powder Coatings Nap-Gard fusion bonded epoxy (FBE) powder coatings offer innovative solutions for today s epoxy-based pipe coating applications. Designed to provide superior corrosion protection, Nap-Gard FBE protects internal and external pipe surfaces of oil and gas pipelines. Nap-Gard powder coatings also provide corrosion protection for valve products used in the most demanding environments, such as in wastewater treatment facilities, and in saltwater. Nap-Gard functional coatings are also the leading choice for rebar application for concrete structures and bridges. They meet the performance standards set by AASHTO and resist cobwebbing and shatter cracking when rebar is formed. Nap-Gard powders are thermosetting, 100% solids, hazardous air pollutant (HAP) free, and are high building (8-14 mils) in just a single coat. Global leader for more than 50 years External Pipe Coating Single Layer Systems 7-2500 In buried service, coating is formulated to be capable of withstanding continuous operating temperatures of 107 C (225 F). It may also be used on the inside of steel pipes and fittings, and is NSF-61 approved for potable water services. 7-2508 - Coating is formulated to be capable of withstanding continuous operating temperatures of 107 C (225 F). It may also be used on the inside of steel pipe and fittings. 7-2514 EN Coating is formulated to provide excellent corrosion protection and improved resistance to cathodic disbondment while capable of withstanding continuous operating temperatures of 103 C (217 F). These products are certified to meet the requirements of CSA Z245.20-10, NACE RP-0394-02, and ISO 21809-1. High Tg 7-2555 - Coating is formulated for use in submerged or wet conditions where high in-service temperatures may reach up to 155 C (311 F) Complete functional coating solutions product portfolio The right choice for rebar Axalta supplies a complete offering for all pipeline applications - oil, gas and water > Single-layer FBE systems > Dual-layer FBE systems > FBE primers for multi-layer systems > Internal coatings > Girth weld coatings* > Repair materials** Dual Layer Systems 7-2610 - Abrasion resistant overcoat (ARO) provides abrasion impact resistance and aids in protecting the corrosion coating from damage during the installation or directional drilling process. 7-2504 - Coating provides water and impact resistance at high temperatures while capable of withstanding continuous operating temperatures of 130 C (265 F). 7-2502 NS - Coating provides a bonded, non-slip surface over standard FBE coatings. This coating offers additional shear slip resistance on concrete coated pipe used for negative buoyancy in offshore installations. The NS product line is a sacrificial coating and can be applied over any system. 7-2675 When used with 7-2555, the operating system tolerance increases to 180 C (356 F). The second layer provides reduced water permeability and improved chemical resistance. * Liquid coating avaliable ** Liquid and patch stick coatings avaliable
FBE Primers For Multi-Layer Systems Primers are avaliable for use in multi-layer polyethylene (PE) and polypropylene (PP) systems. In addition to corrosion resistant properties, these FBE primers are formulated to provide sufficient intercoat adhesion to the multi-layer topcoat. Internal FBE Pipe Coating Nap-Gard FBE internal pipe coating is recommended for use over Nap-Gard 7-1808 phenolic primer on the inside of steel pipe and fittings in adverse temperature and pressure service and in contact with corrosive oils, gases and water. 7-0008 - Coating offering is capable of withstanding continuous operating temperatures of up to 93 C (200 F). 7-0017- Coating is capable of withstanding continuous operating temperatures of 140 C (285 F) while providing corrosion protection in high temperature and high pressure sweet and sour gas environments. 7-0014 - Coating is designed for both external and internal buried pipeline services. In particular, it is recommended for use on the inside of steel pipe. > Meets the requirements of AWWA standards C116, C213, C550, and CSA standard Z245.20-10 > Certified to NSF-61 for drinking water system components FBE Rebar Nap-Gard functional coatings are also a leading choice for rebar application for concrete structures and bridges. These systems meet or exceed the performance standards set by ASTM and AASHTO. They are designed to resist cobwebbing and shatter cracking when rebar is formed. These FBE Rebar systems are 100% solids, HAPs free, and are high building in just a single coat. FBE Valve 7-4500 - Coatings are designed for use as a valve coating. In testing, it meets the requirements of UL 262 Gate Valve specification and FM 1120/1130, 1510 and 1511 specifications. It has been certified to NSF-61, drinking water system components (AWWA C213). Girth Weld Coating & FBE Repairs Materials Axalta offers a two-part liquid epoxy material, FBE and epoxy patch compounds for repair of Nap-Gard coated pipe or rebar and for field joint coatings of external girth welds. Select systems are formulated to offer excellent cathodic disbondment performance for temperatures up to 150 C (302 F).
Functional Coatings Applications Fusion bonded epoxy (FBE) coatings are typically applied to a hot substrate, ranging from 225 C (438 F) to 239 C (463 F) and cured with residual heat. These coatings may be applied by: > Flocking - Spraying powder onto a preheated substrate > Dipping in fluidized bed > Electrostatic spray > Gel and cure quickly to prevent running, saging or dripping at film thickness over 5 mils. Repair materials are usually 2-part liquid epoxy or patch sticks. Coating Systems for Pipelines: Onshore and Offshore Whether the application is for offshore or onshore service, Nap-Gard FBE powder coatings are designed to meet the most demanding performance requirements set by industry standards. For buried and sub-sea services this includes single or dual layer FBE systems designed for improved anti-corrosive properties, abrasion and damage resistance, and higher operating temperature pipelines in both dry and wet environments. Global Manufacturing Sites Darlington, UK Apodaca, Mexico Houston, TX Huangshan, China Cartagena, Colombia Shah Alam, Malaysia Axalta Coating Systems www.powder.axaltacs.com www.axalta.us/powder 2015 Axalta Coating Systems, LLC and all affiliates. All rights reserved.
AXALTA COATING SYSTEMS Nap-Gard 7-2500 Series FBE Powder Coatings
7-2500 Series External FBE Powder Coatings Nap-Gard 7-2500 series is a family of thermosetting epoxy powders. Designed as a corrosion protective coating, for oil and gas pipelines in underground and subsea environments. The Nap-Gard 7-2500 series is comprised of the following product numbers:. 7-2500. 7-2508FG. 7-2501. 7-2508. 7-2508LG Whether the application is for offshore or onshore service, Nap-Gard 7-2500 Series powder coatings are designed to meet the most demanding performance requirements set by industry standards. This family of products can be used as a single anti-corrosive layer or as the primer in a dual layer or multilayer system. Nap-Gard powders are thermosetting, 100% solids, hazardous air pollutant (HAP) free, and are high building (8-30 mils) in just a single coat. NapGard 7-2500 Series Applications:. Oil and Gas Pipeline. Girth Weld Coatings. Water Pipe and Valves Products in the 7-2500 Series family are typically applied to a hot substrate, ranging from 225 C (438 F) to 239 C (463 F) and cured with residual heat. These coatings can be applied by flocking, fluidized bed or electrostatic spay. In buried service, the coatings in the 7-2500 series are capable of withstanding continuous operating temperatures of 107 C (225 F). The NapGard 7-2500 series meets the requirements of: CSA Z245.20-14 NACE SP-0394 NSF/ANSI 61 for drinking water system components AWWA standards C116, C213, C550 Low VOC according to ASTM D2369-10 (2015) Standard Test Method for Volatile Content of Coatings Highlights:. Low Porosity. Excellent adhesion to steel. Good chemical resistance. Excellent flexibility. Fast Curing. Damage resistant-high impact strength and gouge resistance 100% solids More than 100,000 miles of NapGard coated pipes installed worldwide Global leader for more than 50 years in functional coatings
Typical Powder Properties Specific Gravity: Powder 1.44 ±.05 Cured Film 1.35 ±.05 Density: (CSA Z245.20-14) 1440 ± 50g/L Theoretical Coverage: 134 Ft 2 / lb/mil Thermal Characteristics: Tg2 110 ± 5 C Tg1 62 ± 5 C CSA2245.20-14 Typical Powder Qualities Product: 7-2501 7-2500 7-2508FG 7-2508 7-2508LG Typical Gel Time: (CSA Z245.20-14) @205 C (401 F) 10 ± 2 seconds 22 ± 4 seconds 8 ± 2 seconds 16 ± 3 seconds 24 ± 5 seconds Colors: Red Red Green Green Green Typical Properties of Applied Film t Test /Requirement Test Method Description Result Recommended Film Thickness Impact Resistance 1/8 X 5 X 8 steel panels Bending ASTM G14-72 CSA Z245.20-14 CSA Z245.20-14 API-RP-5L7 Elongation Modified ASTM G10-72 Hardness Cathodic Disbondment Tensile Properties Hot Water Resistance Chemical Resistance Test* ASTM D2583 ASTM D2240-74 CSA Z245.20-14: ASTM D2370-98 D882-91 CSA Z245.20-14 90 Day Immersion per CSA Z245.20-98 Average Minimum @ 25 C (77 F) 160 in. lbs @-30 C (-22 F) > 1.5 J @-30 (-22 F) 3.0 /PD @0 C (32 F) @-30 C (-22 F) Barcol Shore D 24 hours, 3.5 Vdc., 65 C, <6.5mm 28 days, 1.5 Vdc., 23 C, <8.5mm 28 days, 1.5 Vdc., 65 C, <20mm Strained C.D, no cracking Tensile Strength 75 C, 24 hours 75 C, 28 days HCl in H2O** 10% NaCl, H2SO4 in H2O ** 10% NaCl in H2O ** Distilled Water 5% NaOH in H2O ** MgCO3/CaCO3 in H2O ** ** Distilled Water * For additional information refer to Nap-Gard Products Catalog Chemical Resistance Chart Performance depends on film thickness. Consult a Nap-Gard Specialist for specific recommendations, and application guide. Typical Electircal Properties Film 350µm (14 mils) 203µm (8 mils) Pass Pass Pass Pass 4.8% 3.2% 60 Average 90 Average 1.2 mm radius 2.3 mm radius 7.2 mm radius Pass >9000 psi Rating 1-2 Rating 1-2 No Blistering No Blistering No Blistering No Blistering No Blistering No Blistering Dielectric Strength ASTM D149-97 1500 volts/mil @250µm Breakdown Voltage ASTM D149-97 20K volts @ 450µm (18 mils) Dielectric Constant ASTM D150 2.15 @ 1 MHz Volume Resistivity ASTM D257 3.3 X 10 15 ohm-cm Thermal Conductivity ASTM C177 0.19 ±0.02BTU/ (hr ft 2 ft F) Cure Schedule Guidelines The cure profile and schedule for Nap-Gard 7-2500 Series shown below, outlines the minimum time at temperature required to achieve the typical performance properties of the coating. Recommended powder application temperature range is 218 C (425 F) to 239 C (463 F) and post heating is not a normal requirement on many pipe sizes with 0.25 inch wall thickness or above. The minimum post application curing temperature (as measured on the coated pipe) and the time to quench may conform to the following cure schedule: 7-2508FG/7-2501 7-2508 7-2508 LG/ 7-2500 Application Temperature Min Time to Quench Application Temperature Min Time to Quench Application Temperature Min Time to Quench 218 C (425 F) 232 C (450 F) 239 C (463 F) 75 seconds 65 seconds 60 seconds 218 C (425 F) 232 C (450 F) 239 C (463 F) 90 seconds 70 seconds 60 seconds 218 C (425 F) 232 C (450 F) 239 C (463 F) 120 seconds 90 seconds 70 seconds Cure is by residual heat in the pipe, therefore very light wall pipe may require additional post heat to complete cure. Recommended time to quench is based on the assumption that the listed temperature is maintained without any cool down rate. Time to quench will vary with application parameters and pipe sizes. Therefore, the above information shall be used only as a guideline by the applicator to develop proper time to quench. Cure should be verified by DSC or other methods. For three layer, the optimum time for adhesive application is between 30-70% cure of the FBE. This has to be developed by the applicator based on the plant layout.
Manufacturing Sites Darlington, UK Apodaca, Mexico Houston, TX Huangshan, China Cartagena, Colombia Axalta Coating Systems www.powder.axaltacs.com www.axalta.us/powder 2015 Axalta Coating Systems, LLC and all affiliates. All rights reserved.
Nap-Gard FBE Valve Powder Coatings
Valve coatings that provide superior chemical and corrosion protection.
Nap-Gard powder coatings provide superior corrosion and chemical protection for valves used in many different environments by providing protection, durability, and strong impact resistance. Nap-Gard valve coatings are designed for projects needing high builds and excellent edge coverage, which extends the life of your valves. Nap-Gard is ideal for the following industries: Pipelines Biopharm Oil and Gas Marine and Wastewater Residential Benefits: Short flow provides exceptional edge coverage Will not sag or picture frame at high film builds Thermosetting, 100% solids Environmentally friendly Durable and flexible Higher Operating Temperatures (up to 225 F) Specifications: Certified NSF/ANSI Standard 61 Drinking Water System Components Meets the requirements of AWWA C213 C116, C213, C550 Nap-Gard Black 7-4510 Nap-Gard Blue 7-2540 Nap-Gard Multi-Purpose Green 7-0014 Nap-Gard CV Red 7-4500 For more infor on NSF certifications visit www.nsf.org Application: Nap-Gard coatings can be applied by electrostatic spray, fluidized bed or hot flocking. Depending on application, film builds can be achieved between 5-60 mils. Proper protection is required if the coating will be exposed to UV radiation Nap-Gard fusion bonded epoxies are not designed to withstand long exposure to UV radiation. If the coating is expected to be exposed to UV rays for an extended period of time, proper care must be taken to prevent degradation of the coating below the target film thickness.
Axalta Coating Systems is a leading global company focused 100% on coatings. Our goal is to provide customers with innovative, colorful, beautiful and sustainable solutions. On every surface they touch, our coatings are designed to prevent corrosion, increase productivity and enable the materials we coat to last longer. Axalta Coating Systems www.powder.axaltacs.com www.axalta.us/powder 1-800-247-3886 2016 Axalta Coating Systems, LLC and all affiliates. All rights reserved reserved.