Designation: A 182/A 182M 07a

Designation: A 182/A 182M 07a Endorsed by Manufacturers Standardization Society of the Valve and Fittings Industry Used in USDOE-NE Standards Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service 1 This standard is issued under the fixed designation A 182/A 182M; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (e) indicates an editorial change since the last revision or reapproval. This standard has been approved for use by agencies of the Department of Defense. 1. Scope* 1.1 This specification 2 covers forged low alloy and stainless steel piping components for use in pressure systems. Included are flanges, fittings, valves, and similar parts to specified dimensions or to dimensional standards, such as the ASME specifications that are referenced in Section 2. 1.2 For bars and products machined directly from bar, refer to Specifications A 479/A 479M and A 739 for the similar grades available in those specifications. Products made to this specification are limited to a maximum weight of 10 000 lb [4540 kg]. For larger products and products for other applications, refer to Specifications A 336/A 336M and A 965/ A 965M for the similar ferritic and austenitic grades, respectively, available in those specifications. 1.3 Several grades of low alloy steels and ferritic, martensitic, austenitic, and ferritic-austenitic stainless steels are included in this specification. Selection will depend upon design and service requirements. 1.4 Supplementary requirements are provided for use when additional testing or inspection is desired. These shall apply only when specified individually by the purchaser in the order. 1.5 This specification is expressed in both inch-pound units and in SI units. However, unless the order specifies the applicable M specification designation (SI units), the material shall be furnished to inch-pound units. 1.6 The values stated in either inch-pound units or SI units are to be regarded separately as the standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification. 1 This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee A01.22 on Steel Forgings and Wrought Fittings for Piping Applications and olting Materials for Piping and Special Purpose Applications. Current edition approved Sept. 1, 2007. Published October 2007. Originally approved in 1935. Last previous edition approved in 2007 as A 182/A 182M 07. 2 For ASME oiler and Pressure Vessel Code applications see related Specification SA-182 in Section II of that Code. 2. Referenced Documents 2.1 In addition to the referenced documents listed in Specification A 961/A 961M, the following list of standards apply to this specification. 2.2 ASTM Standards: 3 A 234/A 234M Specification for Piping Fittings of Wrought Carbon Steel and Alloy Steel for Moderate and High Temperature Service A 262 Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels A 275/A 275M Practice for Magnetic Particle Examination of Steel Forgings A 336/A 336M Specification for Alloy Steel Forgings for Pressure and High-Temperature Parts A 370 Test Methods and Definitions for Mechanical Testing of Steel Products A 403/A 403M Specification for Wrought Austenitic Stainless Steel Piping Fittings A 479/A 479M Specification for Stainless Steel ars and Shapes for Use in oilers and Other Pressure Vessels A 484/A 484M Specification for General Requirements for Stainless Steel ars, illets, and Forgings A 739 Specification for Steel ars, Alloy, Hot-Wrought, for Elevated Temperature or Pressure-Containing Parts, or oth A 763 Practices for Detecting Susceptibility to Intergranular Attack in Ferritic Stainless Steels A 788/A 788M Specification for Steel Forgings, General Requirements A 961/A 961M Specification for Common Requirements for Steel Flanges, Forged Fittings, Valves, and Parts for Piping Applications A 965/A 965M Specification for Steel Forgings, Austenitic, for Pressure and High Temperature Parts E 112 Test Methods for Determining Average Grain Size 3 For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual ook of ASTM Standards volume information, refer to the standard s Document Summary page on the ASTM website. *A Summary of Changes section appears at the end of this standard. Copyright ASTM International, 100 arr Harbor Drive, PO ox C700, West Conshohocken, PA 19428-2959, United States. 1

E 165 Test Method for Liquid Penetrant Examination E 340 Test Method for Macroetching Metals and Alloys 2.3 ASME oiler and Pressure Vessel Codes: 4 Section IX Welding Qualifications SFA-5.4 Specification for Corrosion-Resisting Chromium and Chromium-Nickel Steel Covered Welding Electrodes SFA-5.5 Specification for Low-Alloy Steel Covered Arc- Welding Electrodes SFA-5.9 Specification for Corrosion-Resisting Chromium and Chromium-Nickel Steel Welding Rods and are Electrodes SFA-5.11 Specification for Nickel and Nickel-Alloy Covered Welding Electrodes 3. Ordering Information 3.1 It is the purchaser s responsibility to specify in the purchase order information necessary to purchase the needed material. In addition to the ordering information guidelines in Specification A 961/A 961M, orders should include the following information: 3.1.1 Additional requirements (see 6.2.1, Table 2 footnotes, 8.3, and 17.2), and 3.1.2 Requirement, if any, that manufacturer shall submit drawings for approval showing the shape of the rough forging before machining and the exact location of test specimen material (see 8.3.1). 4. General Requirements 4.1 Product furnished to this specification shall conform to the requirements of Specification A 961/A 961M, including any supplementary requirements that are indicated in the purchase order. Failure to comply with the general requirements of Specification A 961/A 961M constitutes nonconformance with this specification. In case of conflict between the requirements of this specification and Specification A 961/ A 961M, this specification shall prevail. 5. Manufacture 5.1 The low-alloy ferritic steels shall be made by the open-hearth, electric-furnace, or basic-oxygen process with the option of separate degassing and refining processes in each case. 5.2 The stainless steels shall be melted by one of the following processes: (a) electric-furnace (with the option of separate degassing and refining processes); (b) vacuumfurnace; or (c) one of the former followed by vacuum or electroslag-consumable remelting. Grade F XM-27Cb may be produced by electron-beam melting. 5.3 A sufficient discard shall be made to secure freedom from injurious piping and undue segregation. 5.4 The material shall be forged as close as practicable to the specified shape and size. Except for flanges of any type, forged or rolled bar may be used without additional hot 4 Available from American Society of Mechanical Engineers (ASME), ASME International Headquarters, Three Park Ave., New York, NY 10016-5990, http:// www.asme.org. working for small cylindrically shaped parts within the limits defined by Specification A 234/A 234M for low alloy steels and martensitic stainless steels and Specification A 403/ A 403M for austenitic and ferritic-austenitic stainless steels. Elbows, return bends, tees, and header tees shall not be machined directly from bar stock. 5.5 Except as provided for in 5.4, the finished product shall be a forging as defined in the Terminology section of Specification A 788. 6. Heat Treatment 5 6.1 After hot working, forgings shall be cooled to a temperature below 1000 F [538 C] prior to heat treating in accordance with the requirements of Table 1. 6.2 Low Alloy Steels and Ferritic and Martensitic Stainless Steels The low alloy steels and ferritic and martensitic stainless steels shall be heat treated in accordance with the requirements of 6.1 and Table 1. 6.2.1 Liquid Quenching When agreed to by the purchaser, liquid quenching followed by tempering shall be permitted provided the temperatures in Table 1 for each grade are utilized. 6.2.1.1 Marking Parts that are liquid quenched and tempered shall be marked QT. 6.2.2 Alternatively, Grade F 1, F 2, and F 12, Classes 1 and 2 may be given a heat treatment of 1200 F [650 C] minimum after final hot or cold forming. 6.3 Austenitic and Ferritic-Austenitic Stainless Steels The austenitic and ferritic-austenitic stainless steels shall be heat treated in accordance with the requirements of 6.1 and Table 1. 6.3.1 Alternatively, immediately following hot working, while the temperature of the forging is not less than the minimum solution annealing temperature specified in Table 1, forgings made from austenitic grades (except grades F 304H, F 309H, F 310, F 310H, F 316H, F 321, F 321H, F 347, F 347H, F 348, F 348H, F 45, and F 56) may be individually rapidly quenched in accordance with the requirements of Table 1. 6.3.2 See Supplementary Requirement S8 if a particular heat treatment method is to be employed. 6.4 Time of Heat Treatment Heat treatment of forgings may be performed before machining. 6.5 Forged or Rolled ar Forged or rolled austenitic stainless bar from which small cylindrically shaped parts are to be machined, as permitted by 5.4, and the parts machined from such bar, without heat treatment after machining, shall be furnished to the annealing requirements of Specification A 479/ A 479M or this specification, with subsequent light cold drawing and straightening permitted (see Supplementary Requirement S3 if annealing must be the final operation). 5 A solution annealing temperature above 1950 F [1065 C] may impair the resistance to intergranular corrosion after subsequent exposure to sensitizing conditions in F 321, F 321H, F 347, F 347H, F 348, and F 348H. When specified by the purchaser, a lower temperature stabilization or resolution annealing shall be used subsequent to the initial high temperature solution anneal (see Supplementary Requirement S10). 2

Grade Heat Treat Type Austenitizing/Solutioning Temperature, Minimum or Range, F [ C] A A 182/A 182M 07a TALE 1 Heat Treating Requirements Cooling Media Quenching Cool elow F [ C] Tempering Temperature, Minimum or Range, F [ C] Low Alloy Steels F 1 anneal 1650 [900] furnace cool normalize and temper 1650 [900] air cool 1150 [620] F 2 anneal 1650 [900] furnace cool normalize and temper 1650 [900] air cool 1150 [620] F 5, F 5a anneal 1750 [955] furnace cool normalize and temper 1750 [955] air cool 1250 [675] F 9 anneal 1750 [955] furnace cool normalize and temper 1750 [955] air cool 1250 [675] F 10 solution treat and quench 1900 [1040] liquid 500 [260] F 91 normalize and temper 1900-1975 [1040-1080] air cool 1350 1470 [730 800] F 92 normalize and temper 1900-1975 [1040-1080] air cool 1350 1470 [730 800] F 122 normalize and temper 1900-1975 [1040-1080] air cool 1350 1470 [730 800] F 911 normalize and temper 1900-1975 [1040-1080] air cool or liquid 1365 1435 [740-780] F 11, Class 1, 2, 3 anneal 1650 [900] furnace cool normalize and temper 1650 [900] air cool 1150 [620] F 12, Class 1, 2 anneal 1650 [900] furnace cool normalize and temper 1650 [900] air cool 1150 [620] F 21, F 3V, and F anneal 1750 [955] furnace cool 3VCb normalize and temper 1750 [955] air cool 1250 [675] F 22, Class 1, 3 anneal 1650 [900] furnace cool normalize and temper 1650 [900] air cool 1250 [675] F 22V normalize and temper or 1650 [900] air cool or liquid 1250 [675] quench and temper F 23 normalize and temper 1900-1975 [1040-1080] air cool 1350 1470 [730 800] accelerated cool F 24 normalize and temper 1800-1975 [980-1080] air cool 1350 1470 [730 800] or liquid FR anneal 1750 [955] furnace cool normalize 1750 [955] air cool normalize and temper 1750 [955] air cool 1250 [675] F 36, Class 1 normalize and temper 1650 [900] air cool 1100 [595] F 36, Class 2 normalize and temper quench and temper 1650 [900] 1650 [900] air cool accelerated air cool or liquid 1100 [595] 1100 [595] Martensitic Stainless Steels F 6a Class 1 anneal not specified furnace cool normalize and temper not specified air cool 400 [205] 1325 [725] temper not required 1325 [725] F 6a Class 2 anneal not specified furnace cool normalize and temper not specified air cool 400 [205] 1250 [675] temper not required 1250 [675] F 6a Class 3 anneal not specified furnace cool normalize and temper not specified air cool 400 [205] 1100 [595] F 6a Class 4 anneal not specified furnace cool normalize and temper not specified air cool 400 [205] 1000 [540] F 6b anneal 1750 [955] furnace cool normalize and temper 1750 [955] air cool 400 [205] 1150 [620] F 6NM normalize and temper 1850 [1010] air cool 200 [95] 1040-1120 [560-600] Ferritic Stainless Steels F XM-27 Cb anneal 1850 [1010] furnace cool F 429 anneal 1850 [1010] furnace cool F 430 anneal not specified furnace cool 3

TALE 1 Grade Heat Treat Type Austenitizing/Solutioning Temperature, Minimum or Range, F [ C] A A 182/A 182M 07a Continued Cooling Media Quenching Cool elow F [ C] Austenitic Stainless Steels F 304 solution treat and quench 1900 [1040] liquid 500 [260] F 304H solution treat and quench 1900 [1040] liquid 500 [260] F 304L solution treat and quench 1900 [1040] liquid 500 [260] F 304N solution treat and quench 1900 [1040] liquid 500 [260] F 304LN solution treat and quench 1900 [1040] liquid 500 [260] F 309H solution treat and quench 1900 [1040] liquid 500 [260] F 310 solution treat and quench 1900 [1040] liquid 500 [260] F 310H solution treat and quench 1900 [1040] liquid 500 [260] F 310MoLN solution treat and quench 1900 2010 [1050 1100] liquid 500 [260] F 316 solution treat and quench 1900 [1040] liquid 500 [260] F 316H solution treat and quench 1900 [1040] liquid 500 [260] F 316L solution treat and quench 1900 [1040] liquid 500 [260] F 316N solution treat and quench 1900 [1040] liquid 500 [260] F 316LN solution treat and quench 1900 [1040] liquid 500 [260] F 316Ti solution treat and quench 1900 [1040] liquid 500 [260] F 317 solution treat and quench 1900 [1040] liquid 500 [260] F 317L solution treat and quench 1900 [1040] liquid 500 [260] F 347 solution treat and quench 1900 [1040] liquid 500 [260] F 347H solution treat and quench 2000 [1095] liquid 500 [260] F 348 solution treat and quench 1900 [1040] liquid 500 [260] F 348H solution treat and quench 2000 [1095] liquid 500 [260] F 321 solution treat and quench 1900 [1040] liquid 500 [260] F 321H solution treat and quench 2000 [1095] liquid 500 [260] F XM-11 solution treat and quench 1900 [1040] liquid 500 [260] F XM-19 solution treat and quench 1900 [1040] liquid 500 [260] F 20 solution treat and quench 1700-1850 [925-1010] liquid 500 [260] F 44 solution treat and quench 2100 [1150] liquid 500 [260] F 45 solution treat and quench 1900 [1040] liquid 500 [260] F 46 solution treat and quench 2010-2140 [1100-1140] liquid 500 [260] F 47 solution treat and quench 1900 [1040] liquid 500 [260] F 48 solution treat and quench 1900 [1040] liquid 500 [260] F 49 solution treat and quench 2050 [1120] liquid 500 [260] F 56 solution treat and quench 2050-2160 [1120-1180] liquid 500 [260] F 58 solution treat and quench 2085 [1140] liquid 500 [260] F 62 solution treat and quench 2025 [1105] liquid 500 [260] F 63 solution treat and quench 1900 [1040] liquid 500 [260] F 64 solution treat and quench 2010-2140 [1100-1170] liquid 500 [250] F 904L solution treat and quench 1920-2100 [1050-1150] liquid 500 [260] Ferritic-Austenitic Stainless Steels F 50 solution treat and quench 1925 [1050] liquid 500 [260] F 51 solution treat and quench 1870 [1020] liquid 500 [260] F52 C liquid 500 [260] F 53 solution treat and quench 1880 [1025] liquid 500 [260] F 54 solution treat and quench 1920-2060 [1050-1125] liquid 500 [260] F 55 solution treat and quench 2010-2085 [1100-1140] liquid 500 [260] F 57 solution treat and quench 1940 [1060] liquid 175 [80] F 59 solution treat and quench 1975-2050 [1080-1120] liquid 500 [260] F 60 solution treat and quench 1870 [1020] liquid 500 [260] F 61 solution treat and quench 1920-2060 [1050-1125] liquid 500 [260] F 65 solution treat and quench 1905-2100 [1040-1150] liquid 500 [260] A Minimum unless temperature range is listed. Not applicable. C Grade F 52 shall be solution treated at 1825 to 1875 F [995 to 1025 C] 30 min/in. of thickness and water quenched. Tempering Temperature, Minimum or Range, F [ C] 7. Chemical Composition 7.1 A chemical heat analysis in accordance with Specification A 961/A 961M shall be made and conform to the chemical composition prescribed in Table 2. 7.2 Grades to which lead, selenium, or other elements are added for the purpose of rendering the material free-machining shall not be used. 7.3 Starting material produced to a specification that specifically requires the addition of any element beyond those listed in Table 2 for the applicable grade of material is not permitted. 7.4 Steel grades covered in this specification shall not contain an unspecified element, other than nitrogen in stainless steels, for the ordered grade to the extent that the steel conforms to the requirements of another grade for which that element is a specified element having a required minimum content. For this requirement, a grade is defined as an alloy described individually and identified by its own UNS designation or Grade designation and identification symbol in Table 2. 7.5 Product Analysis The purchaser may make a product analysis on products supplied to this specification in accordance with Specification A 961/A 961M. 4

8. Mechanical Properties 8.1 The material shall conform to the requirements as to mechanical properties for the grade ordered as listed in Table 3. 8.2 Mechanical test specimens shall be obtained from production forgings, or from separately forged test blanks prepared from the stock used to make the finished product. In either case, mechanical test specimens shall not be removed until after all heat treatment is complete. If repair welding is required, test specimens shall not be removed until after post-weld heat treatment is complete, except for ferritic grades when the post-weld heat treatment is conducted at least 50 F [30 C] below the actual tempering temperature. When test blanks are used, they shall receive approximately the same working as the finished product. The test blanks shall be heat treated with the finished product and shall approximate the maximum cross section of the forgings they represent. 8.3 For normalized and tempered, or quenched and tempered forgings, the central axis of the test specimen shall correspond to the 1 4 T plane or deeper position where T is the maximum heat-treated thickness of the represented forging. In addition, for quenched and tempered forgings, the mid-length of the test specimen shall be at least T from any second heat-treated surface. When the section thickness does not permit this positioning, the test specimen shall be positioned as near as possible to the prescribed location, as agreed to by the purchaser and the supplier. 8.3.1 With prior purchase approval, the test specimen for ferritic steel forgings may be taken at a depth (t) corresponding to the distance from the area of significant stress to the nearest heat-treated surface and at least twice this distance (2 t) from any second surface. However, the test depth shall not be nearer to one treated surface than 3 4 in. [19 mm] and to the second treated surface than 1 1 2 in. [38 mm]. This method of test specimen location would normally apply to contour-forged parts, or parts with thick cross-sectional areas where 1 4 T 3 T testing (see 8.3) is not practical. Sketches showing the exact test locations shall be approved by the purchaser when this method is used. 8.3.2 Metal uffers The required distances from heattreated surfaces may be obtained with metal buffers instead of integral extensions. uffer material may be carbon or low-alloy steel, and shall be joined to the forging with a partial penetration weld that seals the buffered surface. Specimens shall be located at 1 2-in. [13-mm] minimum from the buffered surface of the forging. uffers shall be removed and the welded areas subjected to magnetic particle test to ensure freedom from cracks unless the welded areas are completely removed by subsequent machining. 8.4 For annealed low alloy steels, ferritic stainless steels, and martensitic stainless steels, and also for austenitic and ferritic-austenitic stainless steels, the test specimen may be taken from any convenient location. 8.5 Tension Tests: 8.5.1 Low Alloy Steels and Ferritic and Martensitic Stainless Steels One tension test shall be made for each heat in each heat treatment charge. 8.5.1.1 When the heat-treating cycles are the same and the furnaces (either batch or continuous type) are controlled within 625 F [614 C] and equipped with recording pyrometers so that complete records of heat treatment are available, then only one tension test from each heat of each forging type (see Note 1) and section size is required, instead of one test from each heat in each heat-treatment charge. NOTE 1 Type in this case is used to describe the forging shape such as a flange, ell, tee, and the like. 8.5.2 Austenitic and Ferritic-Austenitic Stainless Steel Grades One tension test shall be made for each heat. 8.5.2.1 When heat treated in accordance with 6.1, the test blank or forging used to provide the test specimen shall be heat treated with a finished forged product. 8.5.2.2 When the alternative method in 6.3.1 is used, the test blank or forging used to provide the test specimen shall be forged and quenched under the same processing conditions as the forgings they represent. 8.5.3 Testing shall be performed in accordance with Test Methods and Definitions A 370 using the largest feasible of the round specimens. The gage length for measuring elongation shall be four times the diameter of the test section. 8.6 Hardness Tests: 8.6.1 Except when only one forging is produced, a minimum of two pieces per batch or continuous run as defined in 8.6.2 shall be hardness tested in accordance with Test Methods and Definitions A 370 to ensure that the forgings are within the hardness limits given for each grade in Table 3. The purchaser may verify that the requirement has been met by testing at any location on the forging provided such testing does not render the forging useless. 8.6.2 When the reduced number of tension tests permitted by 8.5.1.1 is applied, additional hardness tests shall be made on forgings or samples, as defined in 8.2, scattered throughout the load (see Note 2). At least eight samples shall be checked from each batch load, and at least one check per hour shall be made from a continuous run. When the furnace batch is less than eight forgings, each forging shall be checked. If any check falls outside the prescribed limits, the entire lot of forgings shall be reheat treated and the requirements of 8.5.1 shall apply. NOTE 2 The tension test required in 8.5.1 is used to determine material capability and conformance in addition to verifying the adequacy of the heat-treatment cycle. Additional hardness tests in accordance with 8.6.2 are required when 8.5.1.1 is applied to ensure the prescribed heat-treating cycle and uniformity throughout the load. 8.7 Notch Toughness Requirements Grades F 3V, F 3VCb, and F 22V. 8.7.1 Impact test specimens shall be Charpy V-notch Type, as shown in Fig. 11a of Test Methods and Definitions A 370. The usage of subsize specimens due to material limitations must have prior purchaser approval. 5

TALE 2 Chemical Requirements A Identification Symbol UNS Designation Grade Composition, % Carbon Manganese Phosphorus Sulfur Silicon Nickel Chromium Molybdenum Columbium Titanium Other Elements Low Alloy Steels F 1 K12822 carbon-molybdenum 0.28 0.60 0.90 0.045 0.045 0.15 0.35 0.44 0.65 F2 K12122 0.5 % chromium, 0.05 0.21 0.30 0.80 0.040 0.040 0.10 0.60 0.50 0.81 0.44 0.65 0.5 % molybdenum F5 C K41545 4 to 6 % chromium 0.15 0.30 0.60 0.030 0.030 0.50 0.50 4.0 6.0 0.44 0.65 F5a C K42544 4 to 6 % chromium 0.25 0.60 0.040 0.030 0.50 0.50 4.0 6.0 0.44 0.65 F 9 K90941 9 % chromium 0.15 0.30 0.60 0.030 0.030 0.50 1.00 8.0 10.0 0.90 1.10 F 10 S33100 20 nickel, 8 chromium 0.10 0.20 0.50 0.80 0.040 0.030 1.00 1.40 19.0 22.0 7.0 9.0 F 91 K90901 9 % chromium, 1 % 0.08 0.12 0.30 0.60 0.020 0.010 0.20 0.50 0.40 8.0 9.5 0.85 1.05 0.06 0.10 N 0.03 0.07 molybdenum, 0.2 % Al 0.02 D vanadium plus V 0.18 0.25 columbium and Ti 0.01 D nitrogen Zr 0.01 D F 92 K92460 9 % chromium, 1.8 % tungsten, 0.2 % vanadium plus columbium F 122 K91271 11 % chromium, 2 % tungsten, 0.2 % vanadium, plus molybdenum, columbium, copper, nickel, nitrogen, and boron F 911 K91061 9 % chromium, 1 % molybdenum, 0.2 % vanadium plus columbium and nitrogen F11 Class 1 K11597 1.25 % chromium, 0.5 % molybdenum 0.07 0.13 0.30 0.60 0.020 0.010 0.50 0.40 8.50 9.50 0.30 0.60 0.04 0.09 V 0.15 0.25 N 0.030 0.070 Al 0.02 D W 1.50 2.00 0.001 0.006 0.07 0.14 0.70 0.020 0.010 0.50 0.50 10.00 11.50 0.25 0.60 0.04 0.10 Ti 0.01 D Zr 0.01 D V 0.15 0.30 0.005 N 0.040 0.100 Al 0.02 D Cu 0.30 1.70 W 1.50 2.50 Ti 0.01 D Zr 0.01 D 0.09 0.13 0.30 0.60 0.020 0.010 0.10 0.50 0.40 8.5 9.5 0.90 1.10 0.060 0.10 W 0.90 1.10 Al 0.02 D N 0.04 0.09 V 0.18 0.25 0.0003 0.006 0.05 0.15 0.30 0.60 0.030 0.030 0.50 1.00 1.00 1.50 0.44 0.65 F11 K11572 1.25 % chromium, 0.10 0.20 0.30 0.80 0.040 0.040 0.50 1.00 1.00 1.50 0.44 0.65 Class 2 0.5 % molybdenum F11 K11572 1.25 % chromium, 0.10 0.20 0.30 0.80 0.040 0.040 0.50 1.00 1.00 1.50 0.44 0.65 Class 3 0.5 % molybdenum F12 K11562 1 % chromium, 0.05 0.15 0.30 0.60 0.045 0.045 0.50 max 0.80 1.25 0.44 0.65 Class 1 0.5 % molybdenum F12 K11564 1 % chromium, 0.10 0.20 0.30 0.80 0.040 0.040 0.10 0.60 0.80 1.25 0.44 0.65 Class 2 0.5 % molybdenum F 21 K31545 chromium-molybdenum 0.05 0.15 0.30 0.60 0.040 0.040 0.50 max 2.7 3.3 0.80 1.06 Ti 0.01 D Zr 0.01 D 6

TALE 2 Continued Identification Symbol UNS Designation Grade Composition, % Carbon Manganese Phosphorus Sulfur Silicon Nickel Chromium Molybdenum Columbium Titanium Other Elements F 3V K31830 3 % chromium, 1 % molybdenum, 0.25 % vanadium plus boron and titanium F 3VCb K31390 3 % chromium, 1 % molybdenum, 0.25 % vanadium plus boron, columbium, and titanium 0.05 0.18 0.30 0.60 0.020 0.020 0.10 2.8 3.2 0.90 1.10 0.015 0.035 V 0.20 0.30 0.001 0.003 0.10 0.15 0.30 0.60 0.020 0.010 0.10 0.25 2.7 3.3 0.90 1.10 0.015 0.070 0.015 V 0.20 0.30 Cu 0.25 Ca 0.0005 0.0150 F 22 K21590 chromium-molybdenum 0.05 0.15 0.30 0.60 0.040 0.040 0.50 2.00 2.50 0.87 1.13 Class 1 F 22 K21590 chromium-molybdenum 0.05 0.15 0.30 0.60 0.040 0.040 0.50 2.00 2.50 0.87 1.13 Class 3 F 22V K31835 2.25 % chromium, 1 % 0.11 0.15 0.30 0.60 0.015 0.010 0.10 0.25 2.00 2.50 0.90 1.10 0.07 0.030 Cu 0.20 molybdenum, 0.25 % V 0.25 0.35 vanadium 0.002 Ca 0.015 E F 23 K41650 2.25 % chromium, 1.6 % tungsten, 0.25 % vanadium, plus molybdenum, columbium, and boron F 24 K30736 2.25 % chromium, 1 % molybdenum, 0.25 % vanadium plus titanium and boron 0.04 0.10 0.10 0.60 0.030 0.010 0.50 1.90-2.60 0.05-0.30 0.02 0.08 V 0.20 0.30 0.0005 0.006 N 0.030 Al 0.030 W 1.45 1.75 0.05 0.10 0.30 0.70 0.020 0.010 0.15 0.45 2.20 2.60 0.90 1.10 0.06-0.10 V 0.20 0.30 N 0.12 Al 0.020 0.0015 0.0070 FR K22035 2 % nickel, 1 % copper 0.20 0.40 1.06 0.045 0.050 1.60 2.24 Cu 0.75 1.25 F 36 K21001 1.15 % nickel, 0.65 % copper, molybdenum, and columbium 0.10 0.17 0.80 1.20 0.030 0.025 0.25 0.50 1.00 1.30 0.30 0.25 0.50 0.015 0.045 N 0.020 Al 0.050 Cu 0.50 0.80 V 0.02 Martensitic Stainless Steels F 6a 0.15 1.00 0.040 0.030 1.00 0.50 11.5 13.5 S41000 13 % chromium 410 F F 6b S41026 13 % chromium, 0.15 1.00 0.020 0.020 1.00 1.00 2.00 11.5 13.5 0.40 0.60 Cu 0.50 0.5 % molybdenum F 6NM S41500 13 % chromium, 4 % nickel 0.05 0.50 1.00 0.030 0.030 0.60 3.5 5.5 11.5 14.0 0.50 1.00 Ferritic Stainless Steels F XM- S44627 27 chromium, 1 27Cb G molybdenum XM-27 F F 429 S42900 15 chromium 0.010 0.40 0.020 0.020 0.40 0.50 25.0 27.5 0.75 1.50 0.05 0.20 N 0.015 Cu 0.20 0.12 1.00 0.040 0.030 0.75 0.50 14.0 16.0 429 F F 430 S43000 17 chromium 0.12 1.00 0.040 0.030 0.75 0.50 16.0 18.0 430 F Austenitic Stainless Steels F 304 H S30400 18 chromium, 8 nickel 0.08 2.00 0.045 0.030 1.00 8.0 11.0 18.0 20.0 304 F 7

TALE 2 Continued Identification Symbol UNS Designation Grade Composition, % Carbon Manganese Phosphorus Sulfur Silicon Nickel Chromium Molybdenum Columbium Titanium Other Elements F 304H 0.04 0.10 2.00 0.045 0.030 1.00 8.0 11.0 18.0 20.0 S30409 18 chromium, 8 nickel 304H F F 304L H S30403 18 chromium, 8 nickel, 0.030 2.00 0.045 0.030 1.00 8.0 13.0 18.0 20.0 low carbon 304L F F 304N I S30451 18 chromium, 8 nickel, 0.08 2.00 0.045 0.030 1.00 8.0 10.5 18.0 20.0 nitrogen 304N F F 304LN I S30453 18 chromium, 8 nickel, 0.030 2.00 0.045 0.030 1.00 8.0 10.5 18.0 20.0 nitrogen 304LN F F 309H S30909 23 chromium, 13.5 0.04 0.10 2.00 0.045 0.030 1.00 12.0 15.0 22.0 24.0 nickel 309H F F 310 S31000 25 chromium, 20 nickel 0.25 2.00 0.045 0.030 1.00 19.0 22.0 24.0 26.0 310 F F 310H S31009 25 chromium, 20 nickel 0.04 0.10 2.00 0.045 0.030 1.00 19.0 22.0 24.0 26.0 310H F F 310MoLN S31050 25 chromium, 22 0.030 2.00 0.030 0.015 0.40 21.0 23.0 24.0 26.0 2.00 3.00 N 0.10 0.16 nickel, molybdenum and nitrogen, low carbon 310MoLN F F 316 H S31600 18 chromium, 8 nickel, molybdenum 316 F F 316H S31609 18 chromium, 8 nickel, molybdenum 316H F F 316L H S31603 18 chromium, 8 nickel, molybdenum, low carbon 316L F F 316N I S31651 18 chromium, 8 nickel, molybdenum and nitrogen 316N F F 316LN I S31653 18 chromium, 8 nickel, molybdenum and nitrogen 316LN F F 316Ti S31635 18 chromium, 8 nickel, molybdenum and nitrogen 316Ti F 317 S31700 19 chromium, 13 nickel, 3.5 molybdenum 317 F 0.08 2.00 0.045 0.030 1.00 10.0 14.0 16.0 18.0 2.00 3.00 0.04 0.10 2.00 0.045 0.030 1.00 10.0 14.0 16.0 18.0 2.00 3.00 0.030 2.00 0.045 0.030 1.00 10.0 15.0 16.0 18.0 2.00 3.00 0.08 2.00 0.045 0.030 1.00 11.0 14.0 16.0 18.0 2.00 3.00 0.030 2.00 0.045 0.030 1.00 11.0 14.0 16.0 18.0 2.00 3.00 0.08 2.00 0.045 0.030 1.00 10.0 14.0 16.0 18.0 2.00 3.00 J N 0.10 max 0.08 2.00 0.045 0.030 1.00 11.0 15.0 18.0 20.0 3.0 4.0 8

TALE 2 Continued Identification Symbol UNS Designation Grade Composition, % Carbon Manganese Phosphorus Sulfur Silicon Nickel Chromium Molybdenum Columbium Titanium Other Elements F 317L S31703 19 chromium, 13 nickel, 3.5 molybdenum 317L F F 321 S32100 18 chromium, 8 nickel titanium 321 F F 321H S32109 18 chromium, 8 nickel, titanium 321H F F 347 S34700 18 chromium, 8 nickel columbium 347 F F 347H S34709 18 chromium, 8 nickel, columbium 347H F F 348 S34800 18 chromium, 8 nickel columbium 348 F F 348H S34809 18 chromium, 8 nickel, columbium 348H F F XM-11 S21904 20 chromium, 6 nickel, 9 manganese XM-11 F F XM-19 S20910 22 chromium, 13 nickel, 5 manganese XM-19 F F 20 N08020 35 nickel, 20 chromium, 3.5 copper, 2.5 molybdenum F 44 S31254 20 chromium, 18 nickel, 6 molybdenum, low carbon F 45 S30815 21 chromium, 11 nickel nitrogen and cerium F 46 S30600 18 chromium, 15 nickel, 4 silicon F 47 S31725 19 chromium, 15 nickel, 4 molybdenum 317LM F F 48 S31726 19 chromium, 15 nickel, 4 molybdenum 317LMN F F 49 S34565 24 chromium, 17 nickel, 6 manganese, 5 molybdenum F 56 S33228 32 nickel, 27 chromium with columbium 0.030 2.00 0.045 0.030 1.00 11.0 15.0 18.0 20.0 3.0 4.0 0.08 2.00 0.045 0.030 1.00 9.0 12.0 17.0 19.0 K 0.04 0.10 2.00 0.045 0.030 1.00 9.0 12.0 17.0 19.0 L 0.08 2.00 0.045 0.030 1.00 9.0 13.0 17.0 20.0 M 0.04 0.10 2.00 0.045 0.030 1.00 9.0 13.0 17.0 20.0 N 0.08 2.00 0.045 0.030 1.00 9.0 13.0 17.0 20.0 M Co 0.20 Ta 0.10 0.04 0.10 2.00 0.045 0.030 1.00 9.0 13.0 17.0 20.0 N Co 0.20 Ta 0.10 0.040 8.0 10.0 0.060 0.030 1.00 5.5 7.5 19.0 21.5 N 0.15 0.40 0.06 4.0 6.0 0.040 0.030 1.00 11.5 13.5 20.5 23.5 1.50 3.00 0.10 0.30.07 2.00 0.045 0.035 1.00 32.0 38.0 19.0 21.0 2.00 3.00 8xCmin 1.00 N 0.20 0.40 V 0.10 0.30 Cu 3.0 4.0 0.020 1.00 0.030 0.010 0.80 17.5 18.5 19.5 20.5 6.0 6.5 Cu 0.50 1.00 N 0.18 0.22 0.05 0.10 0.80 0.040 0.030 1.40 2.00 10.0 12.0 20.0 22.0 N 0.14 0.20 Ce 0.03 0.08 0.018 2.00 0.020 0.020 3.7 4.3 14.0 15.5 17.0 18.5 0.20 Cu 0.50 0.030 2.00 0.045 0.030 0.75 13.0 17.5 18.0 20.0 4.0 5.0 N 0.10 0.030 2.00 0.045 0.030 0.75 13.5 17.5 17.0 20.0 4.0 5.0 N 0.10 0.20 0.030 5.0 7.0 0.030 0.010 1.00 16.0 18.0 23.0 25.0 4.0 5.0 0.10 N 0.40 0.60 0.04 0.08 1.00 0.020 0.015 0.30 31.0 33.0 26.0 28.0 0.6 1.0 Ce 0.05 0.10 Al 0.025 9

TALE 2 Continued Identification Symbol UNS Designation Grade Composition, % Carbon Manganese Phosphorus Sulfur Silicon Nickel Chromium Molybdenum Columbium Titanium Other Elements F 58 S31266 24 chromium, 20 nickel, 6 molybdenum, 2 tungsten with nitrogen F 62 N08367 21 chromium, 25 nickel, 6.5 molybdenum F 63 S32615 18 chromium, 20 nickel, 5.5 silicon F 64 S30601 17.5 chromium, 17.5 nickel, 5.3 silicon F 904L N08904 21 chromium, 26 nickel, 4.5 molybdenum 904L F 0.030 2.0 4.0 0.035 0.020 1.00 21.0 24.0 23.0 25.0 5.2 6.2 N 0.35 0.60 Cu 1.00 2.50 W 1.50 2.50 0.030 2.00 0.040 0.030 1.00 23.5 25.5 20.0 22.0 6.0 7.0 N 0.18 0.25 Cu 0.75 0.07 2.00 0.045 0.030 4.8-6.0 19.0-22.0 16.5-19.5 0.30-1.50 Cu 1.50-2.50 0.015 0.50-0.80 0.030 0.013 5.0-5.6 17.0-18.0 17.0-18.0 0.20 Cu 0.35, N 0.05 0.020 2.0 0.040 0.030 1.00 23.0 28.0 19.0 23.0 4.0 5.0 Cu 1.00 2.00 N 0.10 Ferritic-Austenitic Stainless Steels F 50 S31200 25 chromium, 6 nickel, nitrogen F 51 S31803 22 chromium, 5.5 nickel, nitrogen F 52 S32950 26 chromium, 3.5 nickel, 1.0 molybdenum F 53 S32750 25 chromium, 7 nickel, 4 molybdenum, nitrogen 2507 F F 54 S39274 25 chromium, 7 nickel, nitrogen and tungsten F 55 S32760 25 chromium, 7 nickel, 3.5 molybdenum, nitrogen and tungsten F 57 S39277 26 chromium, 7 nickel, 3.7 molybdenum F 59 S32520 25 chromium, 6.5 nickel, 4 molybdenum with nitrogen F 60 S32205 22 chromium, 5.5 nickel, 3 molybdenum, nitrogen 2205 F 0.030 2.00 0.045 0.030 1.00 5.5 6.5 24.0 26.0 1.20 2.00 N 0.14 0.20 0.030 2.00 0.030 0.020 1.00 4.5 6.5 21.0 23.0 2.5 3.5 N 0.08 0.20 0.030 2.00 0.035 0.010 0.60 3.5 5.2 26.0 29.0 1.00 2.50 N 0.15 0.35 0.030 1.20 0.035 0.020 0.80 6.0 8.0 24.0 26.0 3.0 5.0 N 0.24 0.32 Cu 0.50 0.030 1.00 0.030 0.020 0.80 6.0 8.0 24.0 26.0 2.5 3.5 N 0.24 0.32 Cu 0.20 0.80 W 1.50 2.50 0.030 1.00 0.030 0.010 1.00 6.0 8.0 24.0 26.0 3.0 4.0 N 0.20 0.30 Cu 0.50 1.00 W 0.50 1.00 O 0.025 0.80 0.025 0.002 0.80 6.5 8.0 24.0 26.0 3.0 4.0 Cu 1.20 2.00 W 0.80 1.20 N 0.23 0.33 0.030 1.50 0.035 0.020 0.80 5.5 8.0 24.0 26.0 3.0 5.0 N 0.20 0.35 Cu 0.50 3.00 0.030 2.00 0.030 0.020 1.00 4.5 6.5 22.0 23.0 3.0 3.5 N 0.14 0.20 10

TALE 2 Continued Identification Symbol UNS Designation Grade Composition, % Carbon Manganese Phosphorus Sulfur Silicon Nickel Chromium Molybdenum Columbium Titanium Other Elements F 61 S32550 26 chromium, 6 nickel, 3.5 molybdenum with nitrogen and copper 255 F F 65 S32906 29 chromium, 6.5 nickel, 2 molybdenum with nitrogen 0.040 1.50 0.040 0.030 1.00 4.5 6.5 24.0 27.0 2.9 3.9 Cu 1.50 2.50 N 0.10 0.25 0.030 0.80 1.50 0.030 0.030 0.80 5.8 7.5 28.0 30.0 1.5 2.6 Cu 0.80 N 0.30 0.40 A All values are maximum unless otherwise stated. Grade F 2 was formerly assigned to the 1 % chromium, 0.5 % molybdenum grade which is now Grade F 12. C The present grade F 5a (0.25 max carbon) previous to 1955 was assigned the identification symbol F 5. Identification symbol F 5 in 1955 was assigned to the 0.15 max carbon grade to be consistent with ASTM specifications for other products such as pipe, tubing, bolting, welding fittings, and the like. D Applies to both heat and product analyses. E For Grade F22V, rare earth metals (REM) may be added in place of calcium, subject to agreement between the producer and the purchaser. In that case the total amount of REM shall be determined and reported. F Naming system developed and applied by ASTM. G Grade F XM-27Cb shall have a nickel plus copper content of 0.50 max %. Product analysis tolerance over the maximum specified limit for carbon and nitrogen shall be 0.002 %. H Grades F 304, F 304L, F 316, and F 316L shall have a maximum nitrogen content of 0.10 %. I Grades F 304N, F 316N, F 304LN, and F 316LN shall have a nitrogen content of 0.10 to 0.16 %. J Grade F 316Ti shall have a titanium content not less than five times the carbon plus nitrogen content and not more than 0.70 %. K Grade F 321 shall have a titanium content of not less than five times the carbon content and not more than 0.70 %. L Grade F 321H shall have a titanium content of not less than four times the carbon content and not more than 0.70 %. M Grades F 347 and F 348 shall have a columbium content of not less than ten times the carbon content and not more than 1.10 %. N Grades F 347H and F 348H shall have a columbium content of not less than eight times the carbon content and not more than 1.10 %. O %Cr+3.33 %Mo+163 %N=40min. 11

TALE 3 Tensile and Hardness Requirements Grade Symbol Tensile Strength, min, ksi [MPa] Yield Strength, min, ksi [MPa] A Elongation in 2 in. [50 mm] or 4D, min, % Reduction of Area, min, % rinell Hardness Number Low Alloy Steels F 1 70 [485] 40 [275] 20 30 143 192 F 2 70 [485] 40 [275] 20 30 143 192 F 5 70 [485] 40 [275] 20 35 143 217 F 5a 90 [620] 65 [450] 22 50 187 248 F 9 85 [585] 55 [380] 20 40 179 217 F 10 80 [550] 30 [205] 30 50... F 91 85 [585] 60 [415] 20 40 248 max F 92 90 [620] 64 [440] 20 45 269 max F 122 90 [620] 58 [400] 20 40 250 max F 911 90 [620] 64 [440] 18 40 187 248 F 11 Class 1 60 [415] 30 [205] 20 45 121 174 F 11 Class 2 70 [485] 40 [275] 20 30 143 207 F 11 Class 3 75 [515] 45 [310] 20 30 156 207 F 12 Class 1 60 [415] 32 [220] 20 45 121 174 F 12 Class 2 70 [485] 40 [275] 20 30 143 207 F 21 75 [515] 45 [310] 20 30 156 207 F 3V, and F 3VCb 85 110 [585 760] 60 [415] 18 45 174 237 F 22 Class 1 60 [415] 30 [205] 20 35 170 max F 22 Class 3 75 [515] 45 [310] 20 30 156 207 F 22V 85 110 [585 780] 60 [415] 18 45 174 237 F 23 74 [510] 58 [400] 20 40 220 max F 24 85 [585] 60 [415] 20 40 248 max FR 63 [435] 46 [315] 25 38 197 max F 36, Class 1 90 [620] 64 [440] 15... 252 max F 36, Class 2 95.5 [660] 66.5 [460] 15... 252 max Martensitic Stainless Steels F 6a Class 1 70 [485] 40 [275] 18 35 143 207 F 6a Class 2 85 [585] 55 [380] 18 35 167 229 F 6a Class 3 110 [760] 85 [585] 15 35 235 302 F 6a Class 4 130 [895] 110 [760] 12 35 263 321 F 6b 110 135 [760 930] 90 [620] 16 45 235 285 F 6NM 115 [790] 90 [620] 15 45 295 max Ferritic Stainless Steels F XM-27Cb 60 [415] 35 [240] 20 45 190 max F 429 60 [415] 35 [240] 20 45 190 max F 430 60 [415] 35 [240] 20 45 190 max Austenitic Stainless Steels F 304 75 [515] 30 [205] 30 50... F 304H 75 [515] 30 [205] 30 50... F 304L 70 [485] C 25 [170] 30 50... F 304N 80 [550] 35 [240] 30 D 50 E... F 304LN 75 [515] 30 [205] 30 50... F 309H 75 [515] 30 [205] 30 50... F 310 75 [515] 30 [205] 30 50... F 310 MoLN 78 [540] 37 [255] 25 40... F 310H 75 [515] 30 [205] 30 50... F 316 75 [515] 30 [205] 30 50... F 316H 75 [515] 30 [205] 30 50... F 316L 70 [485] C 25 [170] 30 50... F 316N 80 [550] 35 [240] 30 D 50 E... F 316LN 75 [515] 30 [205] 30 50... F 316Ti 75 [515] 30 [205] 30 40... F 317 75 [515] 30 [205] 30 50... F 317L 70 [485] C 25 [170] 30 50... F 347 75 [515] 30 [205] 30 50... F 347H 75 [515] 30 [205] 30 50... F 348 75 [515] 30 [205] 30 50... F 348H 75 [515] 30 [205] 30 50... F 321 75 [515] 30 [205] 30 50... F 321H 75 [515] 30 [205] 30 50... F XM-11 90 [620] 50 [345] 45 60... F XM-19 100 [690] 55 [380] 35 55... F 20 80 [550] 35 [240] 30 50... F 44 94 [650] 44 [300] 35 50... 12

TALE 3 Continued Grade Symbol Tensile Strength, min, ksi [MPa] Yield Strength, min, ksi [MPa] A Elongation in 2 in. [50 mm] or 4D, min, % Reduction of Area, min, % rinell Hardness Number F 45 87 [600] 45 [310] 40 50... F 46 78 [540] 35 [240] 40 50... F 47 75 [525] 30 [205] 40 50... F 48 80 [550] 35 [240] 40 50... F 49 115 [795] 60 [415] 35 40... F 56 73 [500] 27 [185] 30 35... F 58 109 [750] 61 [420] 35 50... F 62 95 [655] 45 [310] 30 50... F 63 80 [550] 32 [220] 25... 192 max F 64 90 [620] 40 [275] 35 50 217 max F 904L 71 [490] 31 [215] 35...... Ferritic-Austenitic Stainless Steels F 50 100 130 65 [450] 25 50... [690 900] F 51 90 [620] 65 [450] 25 45... F 52 100 [690] 70 [485] 15...... F 53 116 [800] F 80 [550] F 15... 310 max F 54 116 [800] 80 [550] 15 30 310 max F 55 109 130 80 [550] 25 45... [750 895] F 57 118 [820] 85 [585] 25 50... F 59 112 [770] 80 [550] 25 40... F 60 95 [655] 65 [450] 25 45... F 61 109 [750] 80 [550] 25 50... F 65 109 [750] 80 [550] 25...... A Determined by the 0.2 % offset method. For ferritic steels only, the 0.5 % extension-under-load method may also be used. For sections over 5 in. [130 mm] in thickness, the minimum tensile strength shall be 70 ksi [485 MPa]. C For sections over 5 in. [130 mm] in thickness, the minimum tensile strength shall be 65 ksi [450 MPa]. D Longitudinal. The transverse elongation shall be 25 % in 2 in. or 50 mm, min. E Longitudinal. The transverse reduction of area shall be 45 % min. F For sections over 2 in. [50 mm] in thickness, the minimum tensile strength shall be 106 ksi [730 MPa]; the minimum yield strength shall be 75 ksi [515 MPa]. 8.7.2 The Charpy V-notch test specimens shall be obtained as required for tension tests in 8.2, 8.3 and 8.5. One set of three Charpy V-notch specimens shall be taken from each tensile specimen location. 8.7.3 The longitudinal axis and mid-length of impact specimen shall be located similarly to the longitudinal axis of the tension test specimens. The axis of the notch shall be normal to the nearest heat-treated surface of the forging. 8.7.4 The Charpy V-notch tests shall meet a minimum energy absorption value of 40 ft-lbf [54 J] average of three specimens. One specimen only in one set may be below 40 ft-lbf [54 J], and it shall meet a minimum value of 35 ft-lbf [48 J]. 8.7.5 The impact test temperature shall be 0 F [ 18 C]. 9. Grain Size for Austenitic Grades 9.1 All H grades and grade F 63 shall be tested for average grain size by Test Methods E112. 9.1.1 Grades F 304H, F 309H, F 310H, and F 316H shall have a grain size of ASTM No. 6 or coarser. 9.1.2 Grades F 321H, F 347H, and F 348H shall have a grain size of ASTM No. 7 or coarser. 9.1.3 Grade F 63 shall have a grain size of ASTM No. 3 or finer. 10. Corrosion Testing for Austenitic Grades 10.1 Corrosion testing is not required by this specification. 10.2 Austenitic grades shall be capable of meeting the intergranular corrosion test requirements described in Supplementary Requirement S4. 11. Retreatment 11.1 If the results of the mechanical tests do not conform to the requirements specified, the manufacturer may reheat treat the forgings and repeat the tests specified in Section 8. 12. Workmanship, Finish, and Appearance 12.1 Forgings shall conform to the requirements of Specification A 961/A 961M. 12.2 The forgings shall be free of scale, machining burrs which might hinder fit-up, and other injurious imperfections as defined herein. The forgings shall have a workmanlike finish, and machined surfaces (other than surfaces having special requirements) shall have a surface finish not to exceed 250 AA (arithmetic average) roughness height. 13. Repair by Welding 13.1 Weld repairs shall be permitted (see Supplementary Requirement S9 of Specification A 961/A 961M) at the discretion of the manufacturer with the following limitations and requirements: 13.1.1 The welding procedure and welders shall be qualified in accordance with Section IX of the ASME oiler and Pressure Vessel Code. 13.1.2 The weld metal shall be deposited using the electrodes specified in Table 4 except as otherwise provided in 13

Supplementary Requirement S5. The electrodes shall be purchased in accordance with ASME Specifications SFA-5.4, SFA-5.5, SFA-5.9, or SFA-5.11. The submerged arc process with neutral flux, the gas metal-arc process, the gas tungstenarc process, and gas shielded processes using flux-core consumables, may be used. 13.1.3 Defects shall be completely removed prior to welding by chipping or grinding to sound metal as verified by magnetic-particle inspection in accordance with Test Method A 275/A 275M for the low alloy steels and ferritic, martensitic, or ferritic-austenitic stainless steels, or by liquid-penetrant inspection in accordance with Test Method E 165 for all grades. 13.1.4 After repair welding, the welded area shall be ground smooth to the original contour and shall be completely free of defects as verified by magnetic-particle or liquid-penetrant inspection, as applicable. 13.1.5 The preheat, interpass temperature, and post-weld heat treatment requirements given in Table 4 shall be met. Austenitic stainless steel forgings may be repair-welded without the post-weld heat treatment of Table 4, provided purchaser approval is obtained prior to repair. 13.1.6 Repair by welding shall not exceed 10 % of the surface area of the forging nor 33 1 3 % of the wall thickness of the finished forging or 3 8 in. [9.5 mm], whichever is less, without prior approval of the purchaser. 13.1.7 When approval of the purchaser is obtained, the limitations set forth in 13.1.6 may be exceeded, but all other requirements of Section 13 shall apply. 13.1.8 No weld repairs are permitted for F 6a Classes 3 and 4. 13.1.9 Post-weld heat treatment times for F 36 are: for Class 1, up to 2 in. [50 mm] in thickness, 1 h per in. [25 mm], 15 minutes minimum, and over 2 in. [50 mm], 15 minutes for each additional in. of thickness or fraction thereof; for Class 2, 1 h per in. [25 mm], 1 2 h minimum. TALE 4 Repair Welding Requirements Grade Symbol Electrodes A Recommended Preheat and Interpass Temperature Range, F [ C] Low Alloy Steels Post Weld Heat-Treatment Temperature, Minimum or Range, F [ C] F 1 E 7018-A 1 200 400 [95 205] 1150 [620] F 2 E 8018-1 300 600 [150 315] 1150 [620] F 5 E 502-15 or 16 400 700 [205 370] 1250 [675] F 5a E 502-15 or 16 400 700 [205 370] 1250 [675] F 9 E 505-15 or 16 400 700 [205 370] 1250 [675] F10......... F 91 9 % Cr, 1 % Mo, VCbN 400 700 [205 370] 1350 1470 [730 800] F 92 9 % Cr, 0.5 % Mo, 1.5 % W, 400 700 [205 370] 1350 1470 [730 800] VCbNiN F 122 11 % Cr, 2 % W, MoVCbCuN 400 700 [205 370] 1350 1470 [730 800] F 911 9 % Cr, 1 % Mo, 1 % W, VCbN 400 700 [205 370] 1365 1435 [740 780] F 11, Class 1, 2, E 8018-2 300 600 [150 315] 1150 [620] and 3 F 12, Class 1 and 2 E 8018-2 300 600 [150 315] 1150 [620] F 21 E 9018-3 300 600 [150 315] 1250 [675] F 3V, and F 3VCb 3 % Cr, 1 % Mo, 1 4 % V-Ti 300 600 [150 315] 1250 [675] F 22 Class 1 E 9018-3 300 600 [150 315] 1250 [675] F 22 Class 3 E 9018-3 300 600 [150 315] 1250 [675] F 22V 2.25 % Cr, 1 % Mo, 0.25 % 300 600 [150 315] 1250 [675] V-Cb F 23 2.25 % Cr, 1.6 % W, 0.25 % 300-600 [150 315] 1350 1470 [730 800] V-Mo-Cb- F 24 2.25 % Cr, 1 % Mo, 0.25 % V 200 400 [95 205] C 1350 1470 [730 800] C F 36, Class 1 1.15 Ni, 0.65 Cu, Mo, Cb 400 700 [205 370] 1100 1200 [595 650] F 36, Class 2 1.15 Ni, 0.65 Cu, Mo, Cb 400 700 [205 370] 1000 1150 [540 620] Martensitic Stainless Steels F 6a, Class 1 E 410-15 or 16 400 700 [205 370] 1250 [675] F 6a, Class 2 E 410-15 or 16 400 700 [205 370] 1250 [675] F6b 13%Cr,1 1 2 %Ni, 1 2 % Mo 400 700 [205 370] 1150 [620] F 6NM 13 % Cr, 4 % Ni 300 700 [150 370] 1050 [565] Ferritic Stainless Steels F XM-27Cb 26 % Cr, 1 % Mo NR D NR F 429 E 430-16 400 700 [205 370] 1400 [760] F 430 E 430-16 NR 1400 [760] FR E 8018-C2 NR NR Austenitic Stainless Steels F 304 E 308-15 or 16 NR 1900 [1040] + WQ E F 304L E 308L-15 or 16 NR 1900 [1040] + WQ F 304H E 308-15 or 16 NR 1900 [1040] + WQ F 304N E 308-15 or 16 NR 1900 [1040] + WQ 14

TALE 4 Continued Grade Symbol Electrodes A Recommended Preheat and Interpass Temperature Range, F [ C] Post Weld Heat-Treatment Temperature, Minimum or Range, F [ C] F 304LN E 308L-15 or 16 NR 1900 [1040] + WQ F 309H E 309-15 or 16 F NR 1900 [1040] + WQ F 310 E 310-15 or 16 NR 1900 [1040] + WQ F 310H E 310-15 or 16 NR 1900 [1040] + WQ F 310MoLN E 310Mo-15 or 16 NR 1920 2010 [1050 1100] + WQ F 316 E 316-15 or 16 NR 1900 [1040] + WQ F 316L E 316L-15 or 16 NR 1900 [1040] + WQ F 316H E 316-15 or 16 NR 1900 [1040] + WQ F 316N E 316-15 or 16 NR 1900 [1040] + WQ F 316LN E 316L-15 or 16 NR 1900 [1040] + WQ F 316Ti E 316-15 or 16 NR 1900 [1040] + WQ F 317 E 317-15 or 16 NR 1900 [1040] + WQ F 317L E 317L-15 or 16 NR 1900 [1040] + WQ F 321 E 347-15 or 16 NR 1900 [1040] + WQ F 321H E 347-15 or 16 NR 1925 [1050] + WQ F 347 E 347-15 or 16 NR 1900 [1040] + WQ F 347H E 347-15 or 16 NR 1925 [1050] + WQ F 348 E 347-15 or 16 NR 1900 [1040] + WQ F 348H E 347-15 or 16 NR 1925 [1050] + WQ F XM-11 XM-10W NR NR F XM-19 XM-19W NR NR F 20 E/ER-320, 320LR NR 1700 1850 [925 1010] + WQ F 44 E NiCrMo-3 NR 2100 [1150] + WQ F45......... F46......... F47... G... 2100 [1150] + WQ F48... G... 2100 [1150] + WQ F49... G... 2100 [1150] + WQ F 58 E NiCrMo-10... 2100 [1150] + WQ F 62 E NiCrMo-3 NR 2025 [1105] + WQ F 904L E NiCrMo-3 NR 1920 2100 [1050 1150] + WQ Ferritic-Austenitic Stainless Steels F 50 25 % Cr, 6 % Ni, 1.7 % Mo NR NR F 51 22 % Cr, 5.5 % Ni, 3 % Mo NR NR F 52 26 % Cr, 8 % Ni, 2 % Mo NR NR F 53 25 % Cr, 7 % Ni, 4 % Mo NR NR F54 25%Cr,7%Ni,3%Mo, NR NR W F 55 25 % Cr, 7 % Ni, 3.5 % Mo NR NR F57 25%Cr,7%Ni,3%Mo,1.5% NR NR Cu, 1 % W F 59 E Ni CrMo-10 NR NR F 60 22 % Cr, 5.5 % Ni, 3 % Mo NR NR F 61 26 % Cr, 9 % Ni, 3.5 % Mo NR NR F 65 29 % Cr, 6.5 % Ni, 2 % Mo NR NR A Electrodes shall comply with ASME SFA 5.4, SFA 5.5, and corresponding ER grades of SFA-5.9 or SFA-5.11. Purchaser approval required. C Not required for not below 0.500 in. [12.7 mm]. D NR = not required. E WQ = water quench. F Filler metal shall additionally have 0.04 % minimum carbon. G Match filler metal is available. Fabricators have also used AWS A 5.14, Class ER, NiCrMo-3 and AWS A 5.11, Class E, NiCrMo-3 filler metals. 14. Inspection 14.1 Inspection provisions of Specification A 961/A 961M apply. 15. Rejection and Rehearing 15.1 The purchaser shall comply with the provisions of Specification A 961/A 961M. 16. Certification 16.1 In addition to the certification requirements of Specification A 961/A 961M, test reports shall be furnished to the purchaser or his representative. 16.2 Test reports shall include certification that all requirements of this specification have been met. The specification designation included on test reports shall include year of issue and revision letter, if any. The manufacturer shall provide the following where applicable: 16.2.1 Type heat treatment, Section 6, 16.2.2 Product analysis results, Section 8 of Specification A 961/A 961M, 16.2.3 Tensile property results, Section 8 (Table 3), report the yield strength and ultimate strength, in ksi [MPa], elongation and reduction in area, in percent, 16.2.4 Chemical analysis results, Section 7 (Table 2), 15