eta 5 Un-alloyed Date: 2003-06-19 Revision: 18 eta 5 is an acid-rutile iron powder electrode with 160% recovery, intended for the welding of general construction steels in the horizontal and horizontal-vertical positions. The electrode is designed to give a fast burn-off rate enabling the user to make extended run lengths and thereby produce small fillet welds at high deposition rates. It is particularly recommended for plate where the surface has been treated with primer or contaminated by rust, mill scale, paint etc. Both the weld appearance and transition with the base material are exceptionally smooth and consistent, making eta 5 a suitable choice when demands on fatigue resistance of the joint are high. 123RTY Acid-rutile D +/-, A O> 65 160% 100-120, 2h 0,07 2 0 0,40 0,70 0,9 1,10 0 r lassification: EN 499-95 E 42 2 RA 73 AW A5.1-91 E 7027 GL 3Y K Force DN 3 Inspecta LR 3m, 3Ym TÜ MR 3 UDT E 42 2 RA 73 RINA E 52 2 B 3, 3Y DB Kennblatt Nr. 10.042.06 AB 3 ore wire: < 0.015 % < 0.015 % N < 0.008 % u pecified Yield strength, Re: 420 Nmm² 480 N/mm² Tensile trength, Rm: 510-560 N/mm² 540 N/mm² Elongation, A5 22% 24% Impact energy, : -20 47 J -20 70 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 3,25 450 72013200 110-170 32 0,73 22 1,9 77 4,00 450 72014000 150-240 35 0,71 15 2,9 78 4,50 600 72014560 170-250 31 0,72 9 3,0 134 4,50 700 72014570 170-250 31 0,72 7 3,0 158 5,00 450 72015000 200-360 37 0,71 9 4,8 75 5,00 600 72015060 200-340 37 0,72 7 4,9 100 5,00 700 72015070 200-330 37 0,73 6 5,0 118 4,5 450 72014500 170-270 34 0,69 12 3,1 90
eta 6 Un-alloyed Date: 2003-06-19 Revision: 18 eta 6 is an acid-rutile iron powder electrode with 170% recovery, intended for the welding of general construction steels in the flat and horizontal-vertical positions. The electrode burns with a very forceful arc and is designed to give a fast burn-off rate enabling small fillet welds to be produced at high travel speeds. The powerful arc force enables plate treated with primer or contaminated by rust, water, mill scale, paint etc. to be welded successfully. Weld bead appearance and transition with the base material are clean and smooth. eta 6 has excellent fracture toughness at temperatures down to 20 and is ideal for shipyard use. 123RTY Acid-rutile D +/-, A O 65 lassification: EN 499-95 E 42 2 RA 73 AW A5.1-91 E 7027 DN 3 LR 3m, 3Ym UDT E 42 2 RA 73 ore wire: < 0.015 % < 0.015 % N < 0.008 % 170% 120, 2h 0,07 2 0 0,40 0,75 1,0 1,25 0 0 0 r u pecified Yield strength, Re: > 420 N/mm² 490 N/mm² Tensile trength, Rm: 510-560N/mm² 540 N/mm² Elongation, A5 22% 24% Impact energy, : -20 47 J -20 60 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 3,25 450 72033200 110-160 25 0,72 22 1,7 88 4,00 450 72034000 150-235 34 0,72 15 3,1 74 5,00 450 72035000 200-350 39 0,7 9 5 72 5,00 700 72035070 200-340 39 0,7 6 5 117 6,00 450 72036000 270-430 36 0,71 7 5,5 89 6,00 700 72036070 270-410 36 0,71 4 5,4 144
eta 10 Un-alloyed Date: 2003-06-19 Revision: 18 eta 10 is rutile-coated iron powder electrode with 135% recovery intended for welding medium thick sections in general construction steels. The electrode design has been optimised to produce fillet welds with a good mitre profile and throat thickness in the 3.5-4.0 mm range. eta 10 produces a finely rippled bead surface, minimum spatter and a self-detaching slag. 123RTY Rutile D +/-, A O 65 135% 100-120, 2h 0,07 0 0,40 0,7 0 0,40 0,6 0 0 r lassification: EN 499-95 E 42 0 RR 53 AW A5.1-91 E 7024 GL 2Y MR 2 AB 2 B 2, 2Y DN 2 UDT E 42 0 RR 53 LR 2m, 2Ym L RINA E 42 2 K Inspecta Force ore wire: < 0.015 % < 0.015 % N < 0.008 % u pecified Yield strength, Re: 420 N/mm² 470 N/mm² Tensile trength, Rm: 510-610 N/mm² 570 N/mm² Elongation, A5 22% 24% Impact energy, : 0 47 J 0 50 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 350 72022500 90-125 28 0,7 45 1,6 46 3,25 450 72023200 130-160 39 0,73 23 2,2 61 4,00 450 72024000 140-220 30 0,65 17 2,6 73 4,50 600 72024560 5,00 450 72025000 190-310 31 0,66 11 3,7 78 5,00 700 72025070 190-260 31 0,64 7 3,3 140
eta 11 Un-alloyed Date: 2003-06-19 Revision: 14 eta 11 is a rutile-coated iron powder electrode with 190% recovery designed for high productivity welding in heavier section mild steel. The electrode is particularly suitable for high speed fillet welding in the downhand and horizontal-vertical positions as well as downhand butt welds. Excellent mitre profile fillets are produced having a smooth transition with the base material. The electrode runs with a smooth stable arc leaving a finely rippled bead surface with self-detaching slag and minimum spatter. It operates equally well on primer-treated material. eta 11 is specially designed to give very low fume emission. 12ERTY Rutile A O> 50, D +/- 190% 100-120, 2h 0,08 0 0,40 0,6 0 0,70 0,9 1,15 5 0 r lassification: EN 499-95 E 42 0 RR 74 AW A5.1-91 E 7024 Force MOD (Navy) M<25 mm DN 2 GL 2Y LR 2m, 2Ym L RINA E 51 2 K B 2 Inspecta AB 2 UDT E 42 0 RR 74 MR 2 ore wire: < 0.015 % < 0.015 % N < 0.008 % u pecified Yield strength, Re: 420 N/mm² 500 N/mm² Tensile trength, Rm: 510-610 N/mm² 580 N/mm² Elongation, A5 22% 24% Impact energy, : 0 47 J 0 50 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 3,25 450 72043200 130-170 28 0,72 20 2,5 67 4,00 450 72044000 150-260 31 0,73 13 3,3 76 4,50 450 72044500 170-335 34 0,73 11 5,3 60 4,50 600 72044560 170-250 30 0,73 8 4,2 101 4,50 700 72044570 170-240 31 0,72 7 4,3 117 5,00 450 72045000 200-390 35 0,72 8 6,7 61 5,00 600 72045060 200-300 34 0,72 7 5,3 104 5,00 700 72045070 200-290 33 0,72 5 5,4 119 5,60 700 72045670 230-340 32 0,74 4 6,2 128 6,00 450 72046000 300-450 35 0,72 6 7,7 71
eta 11 Un-alloyed Date: 2001-01-22 Revision: 10 eta 11 is a grade 3 rutile-coated iron powder electrode with 175% recovery. It is designed for high productivity welding in heavier section structural steels requiring good impact strength down to 20. The electrode is optimised for high speed fillet welding in the horisontal-vertical position and tolerates relatively thick shop primer. Excellent mitre profile fillets are produced having a smooth transition with the base material. 12ERTY Rutile D +, A O>50 175% 100-120, 2h 0,06 0,08 0,30 0,4 0,60 0 1,1 1,20 5 0 5 r lassification: EN 499-95 E 42 2 RR 74 AW A5.1.91 E 7024 LR 3m, 3Ym GL 3Y DN 3 RINA E 42 2 ore wire: < 0.015% < 0.015% N < 0.008% 0 u pecified Yield strength, Re: 420 N/mm² 530 N/mm² Tensile trength, Rm: 510 N/mm² 570 N/mm² Elongation, A5 22% 23% Impact energy, : -20 47 J -20 55 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 3,20 450 72003200 120-150 30 4,00 450 72004000 130-230 33 0,71 14 2,9 84 4,50 450 72004500 140-250 36 0,73 11 3,1 99 4,50 600 72004560 140-250 36 4,50 700 72004570 140-240 36 5,00 450 72005000 170-310 37 0,72 9 4,2 93
eta 16 Un-alloyed Date: 2003-06-19 Revision: 14 eta 16 is a rutile-coated iron powder electrode with 160% recovery intended for horizontal and fillet welding of heavier section construction steels. The electrode has been specially designed to achieve the highest possible productivity when depositing fillet welds with a throat thickness in the 3.0-4.0 mm range. Fillet welds can be made in primer-treated material without porosity or fusion problems along the top edge. As with the other high recovery in Elga's programme, eta 16 has excellent slag detachability and very low fume emission. 12ERTY Rutile D +/-, A O>50 lassification: EN 499-95 E 42 0 RR 73 AW A5.1-91 E 7024 DN 2 AB 2 GL 2Y L Force LR 2m, 2Ym UDT E 42 0 RR 73 B 2Y MR 2 K 160% 100-120, 2h 0,07 0 0,30 0,70 0,60 0,7 0,95 0 r ore wire: < 0.015% < 0.015% N < 0.008% u pecified Yield strength, Re: 420 N/mm² 470 N/mm² Tensile trength, Rm: 510-610 N/mm² 560 N/mm² Elongation, A5 22% 24% Impact energy, : 0 47 J 0 50 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 3,25 450 72053200 130-160 28 0,72 21 2,2 72 4,00 450 72054000 150-235 31 0,71 14 3 78 4,50 600 72054560 5,00 450 72055000 200-320 31 0,71 9 4,1 86 6,00 450 72056000 290-420 36 0,72 6 6,3 84
eta 20 Un-alloyed Date: 1999-11-15 Revision: 16 eta 20 is a basic-rutile low hydrogen iron powder electrode with 150% recovery intended for welding of heavier section construction steels. The electrode is particularly suitable for welding of standing fillets enabling the user to make extended run lengths and thereby achieve small fillet welds at high deposition rates. Excellent mitre profile fillets are produced having a smooth transition with the base material. The electrode runs with a stable arc leaving a finely rippled bead surface with self-detaching slag and minimum spatter. It operates equally well on primer-treated material without porosity or fusion line problems along the top edge. lassification: EN 499-95 E 42 3 RB 53 H10 AW A5.1-91 E 7028 LR DN L Force 3m, 3Ym, H10 3YH5 123RTY Basic-rutile D +/-, A O> 65 Hydrogen content / 100 g < 10 ml 150% 300, 2h 0 0,4 0,70 0,9 1,1 1,50 0 0 5 r ore wire: < 0.015 % < 0.015 % N < 0.008 % u pecified Yield strength, Re: 420 N/mm² 480 N/mm² Tensile trength, Rm: 510-640 N/mm² 550 N/mm² Elongation, A5 22% 27% Impact energy, : -30 47 J -40 28 J -30 70 J -40 40 J Article Diam.mm Length mm roduct code urrent A oltage /kg /electrode 3,25 450 72083200 150-180 28 0,60 27 1,6 81 4,00 450 72084000 220-250 31 0,60 18 2,3 72 5,00 450 72085000 270-300 32 0,60 12 3,6 80
eta 21 Un-alloyed Date: 2003-06-19 Revision: 19 eta 21 is a zircon-basic low hydrogen iron powder electrode with 170% recovery, intended for welding heavier sections in construction and ship steels. It is designed for fast and easy welding in the horizontal position and operates well on both A and D. eta 21 can be used on primer-treated material without porosity or other problems and gives good mechanical properties. 12ERTY Zircon-basic D +/-, A O> 70 Hydrogen content / 100 g < 5 ml 170% 300-350, 2h 0,06 0,09 0 0,4 0,60 1,1 1,25 1,4 0 0 r lassification: EN 499-95 E 42 4 B 73 H5 AW A5.1-91 E 7028 UDT L LR Inspecta AB DN Force K GL ore wire: < 0.015 % < 0.015 % N < 0.008 % WHT 600 2 h E 42 2 B 73 H10 3m, 3Ym, H5 3, 3Y 3YH5 3Y H10 u pecified WHT Yield strength, Re: 420 N/mm² 460 N/mm² 430 Tensile trength, Rm: 500-610 N/mm² 560 N/mm² 530 Elongation, A5 22% 24% 30% Impact energy, : -40 47J -20 150 J -40 70 J -20 160 J -40 110J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 3,25 450 72063200 100-190 24 0,72 21 2,8 56 4,00 450 72064000 170-240 30 0,72 14 3 80 4,50 450 72064500 190-290 31 5,00 450 72065000 225-355 33 0,71 9 4,6 78 6,00 450 72066000 300-430 35 0,72 7 7,2 72
eta 22 Un-alloyed Date: 2003-06-19 Revision: 17 eta 22 is a zircon-basic low hydrogen iron powder electrode with 240% recovery. It is designed for high productivity welding of heavy section mild steel and higher strength steels in the downhand position. Deposition rates with eta 22 are comparable with those for submerged arc welding. The electrode operates on A/D but A is preferable. eta 22 produces a with very good mechanical properties. 1WERTY Zircon-basic D +/-, A O> 65 Hydrogen content / 100 g < 10 ml 240% 350-400, 2h 0,09 0,30 0,70 0,75 1,0 1,25 0 0 r lassification: EN 499-95 E 42 3 B 74 H10 AW A5.1-91 E 7028 L K Inspecta MR AB B UDT DN Force GL LR ore wire: < 0.015 % < 0.015 % N < 0.008 % 4Y 42 HHH 3, 3Y 3, 3Y, HH E 42 3 B 74 H10 3Y, H5 3Y H5 3m, 3Ym H5 u pecified Yield strength, Re: 420 N/mm² 450 N/mm² Tensile trength, Rm: 510-610 N/mm² 560 N/mm² Elongation, A5 22% 26% Impact energy, : -20 47J -40 27J -20 110 J -40 60J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 4,00 450 72074000 190-240 33 0,74 11,0 4,9 62 4,50 450 72074500 220-320 34 0,75 9,0 5,8 63 5,00 450 72075000 240-360 34 0,76 6,0 8,0 72 5,00 600 72075060 240-340 34 0,75 5,0 7,5 91 6,00 450 72076000 300-470 39 0,75 4,0 1 73 6,00 600 72076060 300-450 39 0,75 3,0 10,3 94
31 Un-alloyed Date: 2003-06-19 Revision: 20 31 is a medium-coated rutile electrode suitable for shipbuilding and structural steels as well as general purpose fabrication in mild and medium carbon steels. It has particularly good operability in both downhand and positional welding. The coating of the electrode is of higher basicity than most other rutile types and provides weld deposits of high metallurgical, Grade 3, quality. Rutile D +/-, A O 50 For root passes: D - 95% 80-90, 2h 0 0 0,40 1,0 5 5 0 r lassification: EN 499-95 E 38 2 R 12 AW A5.1-91 E 6013 UDT E 38 2 R 12 B 3 DN 3 MOD (Navy) M < 25 mm, B & BX< 12 mm LR 3m, 3Ym ore wire: < 0.015 % < 0.015 % N < 0.008 % u pecified Yield strength, Re: 380 N/mm² 450 N/mm² Tensile trength, Rm: 470-550 N/mm² 530 N/mm² Elongation, A5 22% 24% Impact energy, : -20 47 J -20 50 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 350 71312500 70-100 18 0,62 88 0,9 45 3,25 350 71313235 90-120 19 0,69 48 1,3 40 3,25 450 71313200 90-120 19 0,69 36 1,3 53 4,00 450 71314000 130-180 20 0,71 25 1,7 61 5,00 450 71315000 160-240 25 0,73 23 2,1 76
39 Un-alloyed Date: 2003-06-19 Revision: 15 39 is a rutile-acid coated electrode specially designed for welding the root and first pass in mild steel pipe with wall thickness 4-10 mm. It has a forceful, penetrating arc and mixed-mode droplet transfer. It is an A/D electrode, with (-) polarity preferred and is suitable for all positions except vertical down. For both root and first pass the electrode should be weaved, with a slight dwell at the joint edges. Rutile D -, A O> 65 95% 80-90, 2h 0 2 0 0 0 0,6 1,1 0 0 0 r 0,3 lassification: EN 499-95 E 42 2 RB 12 AW A5.1-91 E 6013 UDT E 38 2 RB 12 DB Kennblatt Nr. 10.042.02 TÜ ore wire: < 0.015 % < 0.015 % N < 0.008 % u 0,3 pecified Yield strength, Re: 380 N/mm² 390 N/mm² Tensile trength, Rm: 470-550 N/mm² 520 N/mm² Elongation, A5 24% 25% Impact energy, : -20 47 J 0 65 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 350 71392500 90-110 25 0,60 87 46 3,25 350 71393200 130-155 24 0,6 49 1,1 59 4,00 350 71394000 160-200 24 65 30 1,5 71
40 Un-alloyed Date: 2003-06-19 Revision: 19 40 is a thicker-coated, all positional rutile-cellulosic electrode suitable for general purpose applications in mild steel. It is particularly recommended for vertical up and overhead applications, but can also be used in the vertical down position. The electrode welds with a smooth, low spatter arc to produce a finely rippled bead surface and good slag detachability. ombined with good striking/restriking and tolerance to large gaps, the electrode is very easy to use and recommended for all-round fabrication work. 123456 Rutile-cellulosic D +/-, A O 50 For root passes: D - 95% 80-90, 2h 0,09 0 0,3 0,6 0,7 1,0 5 5 0 r lassification: EN 499-95 E 42 0 R 11 AW A5.1-91 E 6013 K UDT E 42 0 R 11 Force DN 2 LR 2m, 2Ym ore wire: < 0.015 % < 0.015 % N < 0.008 % u pecified Yield strength, Rp0.2%: Tensile trength, Rm: 510-640N/mm² 580 N/mm² Elongation, A5 22% 24% Impact energy, : 0 47 J 0 50J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,00 300 71402000 40-80 22 0,6 156 0,4 53 2,50 350 71402500 60-90 22 7 90 0,7 61 3,25 350 71403200 90-150 23 8 55 1,3 54 4,00 350 71404000 130-190 24 7 36 1,6 62 4,00 450 71404045 130-180 24 9 27 1,6 80 5,00 450 71405000 180-225 25 0,6 18 1,6 80
41 Un-alloyed Date: 2003-06-19 Revision: 9 41 is a rutile-cellulosic electrode ideal for both shop and site fabrication. The design of 41 combines good weldability in both vertical up and vertical down position. The arc force is strong and the arc stability is excellent, so the electrode can be used to advantage on rusty and dirty plates. The viscous slag pool facilitates bridging gaps and the electrode is recommended for situations where the joint fit up is poor, for example, in maintenance and repair welding. The bead surface is smooth, the slag removal and restriking properties are good. 123456 Rutile-cellulosic D - (+), A O 50 For root passes: D - lassification: EN 499-95 E 38 AR 11 AW A5.91 E 6012 95% 80-90, 2h 0,08 0 0 0,30 0,40 0,3 0,4 0 5 0 pecified Yield strength, Re: 380 N/mm² 450 N/mm² Tensile trength, Rm: 480-550 N/mm² 500 N/mm² Elongation, A5 22% 23% Impact energy, : 20 47 J 20 50 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 350 71412500 65-90 25 0,67 85 0,7 52 3,25 350 71413200 110-135 25 0,69 49 1,1 57 4,00 350 71414000 120-190 25 0,68 25 1,4 88
42 Un-alloyed Date: 2003-06-19 Revision: 9 42 is a medium-coated rutile electrode with an extremely soft arc. The electrode operates with a very stable arc with an absolutely minimum of spatter. 42 is ideal for butt and fillet welding of sheet metal work. The bead surface is finely rippled and the transition to the base material is smooth. The slag is self-detaching and the excellent restriking properties make it ideal for tack welding. 42 can be used on hobby welding equipment. 42 is recommended mainly for welding in the horisontal position. It is not suitable for root passes, but can be used for fill and capping in the vertical up position. Rutile D - (+), A O 45 For root passes: D - lassification: EN 499-95 E 42 0 R12 AW A5.91 E 6013 95% 80-90, 2h 0,06 0 5 0,4 0 0,30 0,4 0,60 5 5 0 r u pecified Yield strength, Re: 420 N/mm² 435 N/mm² Tensile trength, Rm: 510-560 N/mm² 520 N/mm² Elongation, A5 22% 22% Impact energy, : 0 47J 0 50J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 350 71422500 60-90 25 0,63 83 0,6 64 3,25 350 71423200 90-140 25 0,63 50 1,0 68
43 Un-alloyed Date: 2003-06-19 Revision: 15 43 is a medium-coated rutile electrode intended for welding light to medium sections in mild steel. The electrode operates with a very smooth arc and is suitable for all positions except vertical down. It is easy to strike and re-strike and produces a self-detaching slag leaving a finely rippled bead appearance. With its excellent bead surface and smooth transition with the base material 43 is ideal for butt and fillet welding of sheet metal work. Rutile D +/-, A O 50 For root passes: D - 95% 80-90, 2h 0,07 1 0,30 0,4 0,60 0,30 0,75 5 5 0 r lassification: EN 499-95 E 42 0 R 12 AW A5.1-91 E 6013 LR 2m K B 2 Force DN 2 UDT E 42 0 R 12 Inspecta AB 2 ore wire: < 0.015 % < 0.015 % N < 0.008 % u pecified Yield strength, Re: 420 N/mm² 480 N/mm² Tensile trength, Rm: 510-560 N/mm² 550 N/mm² Elongation, A5 22% 24% Impact energy, : 0 47 J 0 50 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 1,60 300 71431600 25-60 22 233 27 2,00 300 71432000 40-80 22 0,6 142 0,6 34 2,50 350 71432500 55-100 23 0,62 81 50 3,25 450 71433200 75-140 23 0,67 36 1,2 72 3,25 350 71433235 75-140 23 0,67 48 1,2 54 4,00 450 71434000 110-190 25 0,64 26 1,7 81 4,00 350 71434035 110-190 25 0,64 33 1,7 60 5,00 450 71435000 140-265 29 0,65 16 2,7 77 6,00 450 71436000 220-350 30 0,65 11 3,9 90
44 Un-alloyed Date: 2003-06-19 Revision: 19 44 is a thinner-coated, all positional, rutile-cellulosic electrode for general purpose fabrication in mild steel, but with exceptionally good vertical down operability. It can be welded in all positions without the need to alter the current setting and is particularly suitable for working conditions with restricted space or difficult access. The electrode is easy to use where joint fit-up is poor or outside corner joints are to be welded. Excellent strike and restriking characteristics make it ideal for tack-welding. 44 is highly tolerant to plate contaminated by rust, mill scale, paint, dirt etc., making it suitable for repair and maintenance work as well as shipyard applications. 123456 Rutile-cellulosic D +/-, A O 50 For root passes: D - lassification: EN 499-95 E 38 0 R 11 AW A5.1-91 E 6013 DN 2 GL 2Y UDT E 38 0 R 11 Inspecta LR 2m, 2Ym K TÜ Force DB Kennblatt Nr. 10.042.04 AB 2 95% 80-90, 2h ore wire: < 0.015 % < 0.015 % N < 0.008 % 0,07 0 0 0,3 0,40 0,30 0,75 5 5 0 r u pecified Yield strength, Re: 380 N/mm² 460 N/mm² Tensile trength, Rm: 470-550 N/mm² 530 N/mm² Elongation, A5 22% 24% Impact energy, : 0 47 J 0 60 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,00 300 71442000 40-80 21 0,67 153 0,7 30 2,50 350 71442500 70-100 22 0,69 80 46 3,25 350 71443200 90-150 23 0,69 49 1,3 51 4,00 350 71444000 120-190 23 0,7 34 1,6 61 5,00 350 71445000 180-240 24 0,7 20 2 76
45 Un-alloyed Date: 2003-06-19 Revision: 17 45 is a multi-purpose rutile-cellulosic coated electrode suitable for a wide application range in mild steel. The electrode is fully positional, including vertical down and welds with a crisp, steady arc to produce a smooth bead surface with good slag detachability. It is relatively insensitive to rust, dirt and surface coatings. Together with its ability to bridge gaps, the general versatility of 45 makes it ideal for both shop and site fabrication. Applications: 123456 Rutile-cellulosic D +/-, A O 50 For root passes: D - lassification: EN 499-95 E 42 0 R 11 AW A5.1-91 E 6013 UDT E 42 0 R 11 B 2Y LR 2m, 2Ym Inspecta AB 2 DN 2 GL 2Y Force L K MR 2 MOD (Navy) M 25 mm 90% 80-90, 2h 0,07 0 0,30 0,4 0,70 0,30 0,75 5 5 0 r ore wire. < 0.015 % < 0.015 % N < 0.008 % u pecified Yield strength, Re: 420 N/mm² 470 N/mm² Tensile trength, Rm: 510-560 N/mm² 550 N/mm² Elongation, A5 22% 24% Impact energy, : 0 47 J 0 50 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,00 300 71452000 40-80 24 0,7 139 0,4 40 2,50 350 71452500 70-100 25 0,7 78 48 3,25 350 71453200 90-145 25 0,7 48 1,2 49 3,25 450 71453245 90-135 25 0,7 37 1,2 65 4,00 350 71454000 120-195 25 0,7 33 1,7 58 4,00 450 71454045 120-180 25 0,7 25 1,8 77 5,00 350 71455000 180-270 26 0,75 21 2,3 64
46 Un-alloyed Date: 2003-06-19 Revision: 17 46 is a heavy coated rutile electrode intended for fast downhand welding of general construction steels. The electrode design has been optimised to produce fillet welds with a mitre profile and smooth blend-in at the bead edges. 46 is a touch welding electrode and extremely easy to use, producing a finely rippled bead appearance, self-detaching slag and minimal spatter. Excellent arc stability at low currents makes the electrode particularly suitable for sheet metal fabrication. 12ERTY Rutile D -, A O 50 For root passes: D - 95% 80-90, 2 h 0,08 0 0 0,4 0 0,30 0,70 5 5 0 r lassification: EN 499-95 E 42 0 RR 13 AW A5.1-91 E 6013 TÜ Force UDT E 42 0 RR 13 DN 2 DB Kennblatt Nr. 80.042.01 LR 2m, 2Ym ore wire: < 0.015 % < 0.015 % N < 0.008 u pecified Yield strength, Re: 420 N/mm² 460 N/mm² Tensile trength, Rm: 510-560 N/mm² 550 N/mm² Elongation, A5 22% 22% Impact energy, : 0 47 J 0 50 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,00 300 71462000 50-70 23 1 156 0,6 34 2,50 350 71462500 65-100 23 8 82 50 3,25 450 71463200 90-150 25 5 38 1,2 82 3,25 350 71463235 90-150 25 5 45 1 62 4,00 450 71464000 130-200 26 7 25 1,5 88 4,00 350 71464035 130-200 26 7 33 1,3 66 5,00 450 71465000 200-280 27 8 16 1,8 110
47 Un-alloyed Date: 2003-10-16 Revision: 18 47 is a basic-coated, 105% recovery electrode intended for general welding applications in those cases where a ''7016'' type is preferred. 47 has very good positional operability and excellent resistance to porosity in plate coated with primer or contaminated by mill scale and rust. uitable for shipbuilding, storage tanks and general construction purposes. Basic; D +/-, A O 60 For root passes: D - Hydrogen content / 100 g < 5 ml; 105% 350-400, 2h 0,06 0,09 0,30 0,70 0,75 1,0 1,25 5 0,005 5 r lassification: EN 499-95 E 46 4 B 12 H5 AW A5.1-91 E 7016-1 B L DN GL LR UDT AB Force ore wire: < 0.015 % < 0.015 % N < 0.008 %; WHT 620 1 h 3, 3 Y HH 3Y H5 3Y H5 3m, 3Ym H5 E 46 4 B 12 H5 4YQ420 u pecified WHT Yield strength, Re: 460 N/mm² 490 N/mm² 420 N/mm² Tensile trength, Rm: 500-640 N/mm² 570 N/mm² 515 N/mm² Elongation, A5 22% 26% 31% Impact energy, : -40 47 J -46 70 J -40 150 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 350 71472533 60-90 24 0,64 80 0,9 50 3,25 350 71473233 80-160 26 0,66 44 1,2 65 3,25 450 71473245 80-145 23 0,66 32 1,2 81 4,00 350 71474033 110-210 25 0,66 29 1,7 70 4,00 450 71474045 110-200 24 0,67 22 1,7 86 5,00 450 71475045 155-290 25 0,70 14 2,4 96
47D Un-alloyed Date: 2003-06-19 Revision: 16 47D is a basic double coated low hydrogen A/D electrode for welding mild and medium tensile steels in all positions except vertical down. It has an exceptionally stable arc making it particularly suitable for root passes. The electrode can be used on small welding transformers with a low O and operates with minimal spatter to deposit smooth weld beads featuring easy slag detachability and excellent mitre fillet profile. 47D is very easy to strike and combines good metallurgical quality with extreme ease of use, making it ideal for general repair and maintenance applications. Basic D +, A O 55 Hydrogen content / 100 g < 10 ml 98% 350-400, 2h 0,07 0 5 0,7 0,75 0,60 0,9 1,60 5 5 0 r 0,30 0,30 lassification: EN 499-95 E 42 2 B 12 H10 AW A5.1-91 E 7016 DB Kennblatt Nr. 10.042.05 LR 3m, 3Ym UDT E 42 2 B 12 H10 Force TÜ ore wire: < 0.015 % < 0.020% N < 0.010 % Approvals are valid for dim. 4.0 mm. WHT 600 1 h 0,30 u 0 0,08 pecified WHT Yield strength, Re: 420 N/mm² 465 N/mm² 400 N/mm² Tensile trength, Rm: 510-610 N/mm² 550N/mm² 510 N/mm² Elongation, A5 22% 26% 31% Impact energy, : -20 47 J -20 60 J -20 100 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,00 300 71492000 45-65 20 0,61 155 0,6 52 2,50 350 71492500 60-90 25 0,65 77 53 3,25 450 71493200 80-140 25 0,67 36 1,3 66 3,25 350 71493235 80-140 25 0,67 45 1,3 52 4,00 450 71494000 130-200 25 0,69 22 1,7 76 4,00 350 71494035 130-200 25 0,69 30 1,7 60
47 Un-alloyed Date: 1999-11-15 Revision: 18 47 is a basic, thin-coated low hydrogen electrode intended for mild and higher strength steels. The excellent positional welding characteristics together with the thin coating make this electrode ideal for full penetration root runs in general and pipe welding in particular. 47 has superior notch toughness down to -50, and is suitable for high integrity applications such as offshore fabrication. Basic D +/-, A O 65 For root passes: D - Hydrogen content / 100 g < 5 ml 105% 350-400, 2h 0,06 0,09 0,30 0,6 0,90 0 1,1 1,30 5 0 0,005 5 r lassification: EN 499-95 E 46 4 B 12 H5 AW A5.1-91 E 7016-1H8 B 639-86 E 51 5 6 B[2 4 H] DIN 1913-84 E 51 55 B10 NF A81-309 E 51 55 B 24 H Force L ore wire: < 0.015 % < 0.015 % N < 0.008 % u Al pecified Yield strength, Re: 460 N/mm² 550 N/mm² Tensile trength, Rm: 530-660 N/mm² 620 N/mm² Elongation, A5 22% 26% Impact energy, : -40 47 J -46 27 J -40 150J -46 70 J Article Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 350 71472500 60-90 22 0,64 82 0,9 50 3,25 450 71473200 80-140 22 0,66 38 1,4 69 3,25 350 71473232 80-150 22 0,66 50 1,4 52 4,00 450 71474000 140-200 24 0,63 26 1,7 96 5,00 450 71475000 160-250 26
48M Un-alloyed Date: 2003-05-05 Revision: 8 48M is a basic coated low hydrogen D+ electrode designed for welding mild and higher strength steels. It is particularly suitable for heavily restrained sections and also steels with higher impurity levels. The electrode operates with a very smooth and stable arc and shows no tendency to ''freeze'', even on low current. Root passes can be welded with D-. 48M has very good fracture toughness at temperatures down to -50. Basic D + (-) Hydrogen content / 100 g < 4 ml 120% 350-400, 2h 0,09 0,40 0,75 1,10 1,4 1,60 5 0 0 0 r lassification: EN 499-95 E 42 5 B 42 H5 AW A5.1-91 E 7018-1 H4 GL DN K UDT RINA ore wire: < 0.015% < 0.015% N < 0.008% 3 Y 42 H5 4 Y 42 H5 E 42 4 B 42 H5 3Y H5 u pecified Yield strength, Re: 420-500 N/mm² 480 N/mm² Tensile trength, Rm: 510-660 N/mm² 560 N/mm² Elongation, A5 24% 28% Impact energy, : -40 47 J -46 27 J -40 80 J -46 70 J -50 60 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,00 300 71552000 40-80 23 0,64 112 0,7 43 2,50 350 71552500 70-110 23 0,69 62 0,9 58 3,25 350 71553235 80-145 24 0,71 39 1,3 64 3,25 450 71553200 80-145 24 0,71 30 1,3 85 4,00 350 71554035 120-210 24 0,73 26 1,8 68 4,00 450 71554000 120-210 25 0,73 20 1,8 90 5,00 450 71555000 200-285 25 0,75 13 2,7 93
48 Un-alloyed Date: 2003-06-19 Revision: 10 48 is a basic-coated, low hydrogen, carbon manganese electrode specially designed for pipewelding. The all-positional A/D electrode is exceptionally easy to use. 48 has an extremely stable arc which enables it to be manipulated in the most difficult welding positions without any risk of arc extinction due to freezing. Root beads are even and slightly convex, providing a smooth blend-in with the base material. Operating characteristics are not sensitive to variations in the root gap or edge misalignment. Fill and capping passes fuse flush with the joint edges, minimising the risk of edge defects when using either the stringer bead or weaving technique. The flat-to slightly convex bead profile results in the need for only a bare minimum of grinding and therefore considerable reduction in the associated problems of dust and noise pollution. 48 combines the special operability needs of the pipe welder with the general requirement for improved productivity. Basic D +/-, A O> 70 Hydrogen content / 100 g 5 ml 105% 350, 2h 0,06 0,08 5 0,60 0,75 0,90 1,20 1,60 5 0 0 5 r lassification: EN 499-95 E 46 2 B 12 H5 AW A5.1-91 E 7018-H8 UDT AB LR L GL K Force TÜ MR DN B Inspecta ore wire: < 0.015% < 0 015% N < 0.008% E 42 2 B 12 H5 3, 3Y 3m, 3Ym, H5 3Y H5 3Y 40 HHH 3Y H5 3 Y HH u pecified Yield strength, Re: 460 N/mm² 530 N/mm² Tensile trength, Rm: 530-650 N/mm² 620 N/mm² Elongation, A5 22 % 25 % Impact energy, : -20 47 J -30 28 J -20 80 J -30 70 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,00 300 71592000 45-65 20 0,61 155 0,6 52 2,50 350 71592500 60-85 22 0,62 80 0,6 65 3,25 450 71593200 70-130 23 0,75 30 1,1 88 3,25 350 71593235 70-130 23 0,75 42 1 66 4,00 450 71594000 120-190 24 0,73 23 1,7 84 4,00 350 71594035 120-190 23 0,75 28 1,7 75
48 Un-alloyed Date: 2003-06-19 Revision: 1 48 is a basic-coated, low hydrogen, general purpose electrode for use on D+ only, for which the outstanding all-round operability has been optimised. The smooth, soft arc, easy slag control, all-positional welding, low spatter and excellent slag release provide maximum welder-appeal. 48 combines the good running characteristics required for general fabrication work with the exacting operability needs for pipe welding, where the fine spray transfer provides precise weld pool control and ensures an exceptionally regular and smooth root bead. Basic D + (-) Hydrogen content / 100 g < 4 ml 120% 350-440, 2h 0,09 0,40 0,60 0,75 u 1,10 1,40 1,60 5 0 0 r lassification: EN 499-95 E 42 4 B 42 H5 AW A5.1-91 E 7018-1H4 B 3 3Y HH TÜ Inspecta RINA E 52 3 HHH AB 3, 3Y DB Kennblatt Nr 10.042.01 DN 3YH5 MR 3Y 40 HHH LR 3m, 3Ym, H5 IEL E 44L 4 B20 R12 K20 K UDT E 42 3 B 42 H5 Force GL 3Y H5 ore wire: < 0.015 % < 0.015 % N< 0.008 % WHT 600 1 h pecified WHT Yield strength, Re: 420 N/mm² 530 N/mm² 490 Tensile trength, Rm: 510-640 N/mm² 600 N/mm² 510 Elongation, A5 22% 26% 29% Impact energy, : -40 47 J -46 27 J -40 60 J -46 40 J -20 130 J 2,50 350 71482520E 80-110 23 0,71 60 1 54 3,25 450 71483220E 110-155 24 0,72 28 1,6 76 4,00 450 71484020E 140-205 25 0,74 19 2,1 82 5,00 450 71485020E 200-285 25 0,75 13 2,9 91
50 Un-alloyed Date: 2000-08-18 Revision: 1 50 is an acid-rutile electrode producing a with very low -content it is designed specially for the fabrication and repair of hot-dip zink galvanesing baths. The low content is necessary to give a god resistance to corrosion by molten Zn at the bath operating temperature of 450-500. 1234TY A>70, D- lassification: EN 499-95 E 38 0 RA 13 100% 10h 0,08 0 0,07 0,6 0,7 5 5 pecified Yield strength, Re: >380 N/mm2 420 N/mm2 Tensile trength, Rm: >470 N/mm2 500 N/mm2 Elongation, A5 >20 % 25 % Impact energy, : 0>47J -10 65J Article Diam.mm Length mm roduct code urrent A oltage /kg /electrode 4,00 450 71504000 140-190 25 0,7 26 1,9 74 5,00 450 71505000 190-240 25 0,7 17 2,4 87
51 Un-alloyed Date: 2003-06-19 Revision: 25 51 is a basic-coated low hydrogen A/D electrode designed for welding mild and higher strength steels. It combines strength and toughness and is particularly suitable for heavily restrained sections where there can be risk of cracking due to weld stresses. With its excellent general operability and good positional welding characteristics 51 is often used for pipe welding. It operates without difficulties on both primer-treated and rusty material. The electrode produces a finely rippled bead surface and smooth transition with the base material. This together with the exceptionally good slag detachability, even in root runs, gives 51 superior radiographic quality. Basic D - (+), A O 70 For root passes: D - Hydrogen content / 100 g < 5 ml 120% 350-400, 2h 0,09 0,30 0,75 1,10 1,35 1,60 0 5 r lassification: EN 499-95 E 46 4 B 32 H5 AW A5.1-91 E 7018-1H8 Force, K TÜ Inspecta, UDT GL 3YHH DB Kennbl. Nr 10.042.03 MR 3Y 40 HHH LR 3m, 3Ym, H5 RINA E 52 3HH L B 3, 3Y HH DN 3YH5 AB 3, 3Y MOD (Navy) M 25 mm, B & BX 12 mm 7151-2400, special variant for rootruns. ore wire: < 0.015 % < 0.015 % N < 0.008 % WHT 600 1 h u Al pecified WHT Yield strength, Re: 460 N/mm² 560 N/mm² 520 N/mm² Tensile trength, Rm: 530-650 N/mm² 600 N/mm² 600 N/mm² Elongation, A5 22% 25% 26% Impact energy, : -46 27 J -40 47 J -46 30 J -40 60 J -40 60 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,00 300 71512000 50-90 23 0,74 104 0,6 45 2,50 350 71512500 70-110 23 0,68 60 1,0 55 3,25 450 71513200 110-150 24 0,68 30 1,3 82 3,25 350 71513235 110-150 24 0,68 38 1,3 64 4,00 450 71514000 140-200 24 0,72 19 1,8 94 4,00 350 71514035 140-200 24 0,72 25 1,8 74 4,50 450 71514500 170-230 24 0,73 14 2,1 99 5,00 450 71515000 200-270 24 0,72 13 2,6 100 6,00 450 71516000 220-350 24 0,76 9 3,6 97
54 Un-alloyed Date: 2003-06-19 Revision: 16 54 is a basic A/D electrode specially designed for vertical down welding of ordinary and higher strength steels. The vertical down technique is characterized by high welding speeds and low heat input, giving enhanced productivity combined with low stress and deformation. 54 produces a clean bead profile with minimum spatter and gives very good mechanical properties. QWER5Y Basic A O 65, (D +) Hydrogen content / 100 g < 10 ml 110% 350-400, 2h 0,06 0 0,40 0 0,70 0,9 1,15 5 0 5 r lassification: EN 499-95 E 46 2 B 35 H10 AW A5.1-91 E 7048 RINA K Inspecta LR AB DN GL Force B UDT MR ore wire: < 0.015 % < 0.015 % N < 0.008 % E 52 3HH 3m, 3Ym H5 3, 3Y 3YH5 3 Y HH 3, 3Y HH E 46 4 B 35 H10 3Y 40 HHH u Al pecified Yield strength, Re: 460 N/mm² 530 N/mm² Tensile trength, Rm: 530-650 N/mm² 590 N/mm² Elongation, A5 22% 25% Impact energy, : -20 47-40 27-20 90 J -40 40 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 3,25 450 71543200 110-150 23 0,78 32 1,7 59 4,00 450 71544000 150-200 24 0,76 22 2,1 73 4,50 450 71544500 175-235 24 0,76 18 2,7 72 5,00 450 71545000 200-280 25 0,75 14 2,9 81 5,60 450 71545600 240-300 25 0,75 11 3,1 93
eta 24 Low-alloyed Date: 2003-06-19 Revision: 18 eta 24 is a zircon-basic low hydrogen electrode with 160% recovery, producing a nominal 0.9 %. It is intended for welding fillets and butt joints in the horizontal-vertical and flat positions, combining high deposition rates with very good fracture toughness at temperatures down to -60. eta 24 has excellent TOD values and is particularly suitable for offshore construction. 123RTY Zircon-basic D +/-, A O 70 Hydrogen content / 100 g < 5 ml 160% 300-350, 2h 0,09 0,30 0,3 0,60 0,90 1,1 1,35 0 5 r 0,7 1,0 lassification: EN 499-95 E 46 5 1 B 53 H5 AW A5.5-96 ~E7018-G Inspecta UDT K Force DN AB LR L E 50 6 1 B 33 H5 4Y 42 H5 4Y 40 H5 4Y 40m H5 TOD -10 > 0.25 mm (t: 90 mm, 2G) AW: No designation for high recovery. ore wire: < 0.012 % < 0.012 % N < 0.060 % Approvals are valid for dim.< 5.0 mm. u pecified Yield strength, Re: 460 N/mm² 510 N/mm² Tensile trength, Rm: 530-650 N/mm² 600 N/mm² Elongation, A5 22% 25% Impact energy, : -50 47 J -50 70 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 3,25 450 72093200 100-190 26 0,72 32 1,3 82 4,00 450 72094000 170-240 29 0,74 14 3,0 80 5,00 450 72095000 225-355 33 0,71 10 4,6 78 6,00 450 72096000 300-430 35 0,72 6 7,2 72
eta 110 Low-alloyed Date: 2003-06-19 Revision: 16 eta 110 is a zircon-basic low hydrogen electrode with 160% recovery, specially designed for welding quenched and tempered steels with a yield strength of 700 N/mm2, e.g. Weldox 700, HY 100, N-A-XTRA 70, TI, uprafort 700, TE 690, etc. The gives very high strength properties with good fracture toughness at temperatures down to -60. eta 110 is intended for high productivity welding, producing a mitre fillet profile with smooth blend-in with the base plate. The combination of very high strength, good toughness and fast deposition rate makes this electrode particularly suitable for offshore and mobile cranes, jack-up rigs, submarine hulls and earth moving equipment. 123RTY Zircon-basic D +/-, A O 70 Hydrogen content / 100 g < 5 ml 160% 350-400, 2h 0,09 5 0,4 0,60 1,10 1,2 1,60 5 0 5 0 r 2,2 2,6 2,8 lassification: EN 757-97 ~E 69 5 2 B 73 H5 AW A5.5-96 ~E 11018-G UDT DN AW: no designation for high recovery. AW: slight deviation in yield strength. AW: slight deviation in, and. EN: slight deviation in and. ore Wire: < 2 % < 2 % N < 0,060 % WHT 640 1 h EY 69 76 2 B H5 4Y 69 H5 0,30 0,60 u pecified WHT Yield strength, Rp0.2%: 690 N/mm² 720 N/mm² Tensile trength, Rm: 760-960 Nmm ² 700 N/mm² 780 N/mm² 760 N/mm² Elongation, A5 20% 20% 22% Impact energy, : -40 69J -40 75J -20 50J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 4,00 450 72114000 170-240 28 0,74 14 3 81 4,50 450 72114500 190-280 29 0,75 11 3,7 81 5,00 450 72115000 225-355 30 0,74 9 4,9 78
eta H400 Low-alloyed Date: 2000-09-26 Revision: 1 Hardsurfacing for moderate abrasion. The is tough and produces a crack free deposit. The electrode is a basic high recovery type. Applications: Hard surfacing of un- and lowalloyed steels, especially designed for surfacing and welding of the cap layers of welded joints in base material Hardox 400 12ERTY Basic lassification: peciall type no standards None Hardness in the fist layer on unalloyed 400-450 Hv Hydrogen content / 100 g < 5 ml/100 g 160 % 250-350, 2 h 5 5 0,6 3,7 4,0 4,3 r 1,4 1,6 1,8 0,6 0,6 pecified Article Diam.mm Length mm roduct code urrent A oltage /kg /electrode 3,2 450 72403200 120-160 26 0,70 23 1,7 92 4,0 450 72404000 160-210 27 0,71 14 2,3 100 5,0 450 72405000 200-260 31 0,71 10 2,9 120
48K Low-alloyed Date: 2003-10-28 Revision: 17 48K is a basic-coated low hydrogen electrode producing a 2.5 % weld metal. The all-positional electrode is designed for applications demanding high yield strength and excellent fracture toughness at temperatures down to -60, both in the as welded and stress relieved condition, and is suitable for offshore fabrication and LG work. 48K is TOD tested Basic D +/-, A O 70 Hydrogen content / 100 g < 5 ml 120% 350-400, 2h 0,09 0,30 0,60 0,70 1,25 5 0,005 5 r 2,0 2,4 2,6 lassification: EN 499-95 E 46 6 2 B 32 H5 AW A5.5-96 E8018-1 Inspecta Force LR AB UDT B DN MR ore wire: < 0.012 % < 0.012 % N < 0.060 % 3m, 5Y40m H5 3, 3Y E 46 6 2 B 32 H5 U.. -60 5Y H5 5Y 42 HHH u pecified Yield strength, Re: 460 N/mm² 530 N/mm² Tensile trength, Rm: 550-650 N/mm² 620 N/mm² Elongation, A5 22% 25% Impact energy, : -60 47 J -60 90 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 350 71582500 80-110 24 0,64 63 0,9 64 3,25 450 71583200 110-150 25 0,67 33 1,3 84 4,00 450 71584000 140-200 27 0,7 22 1,9 88 5,00 450 71585000 200-270 27 0,71 13 2,6 95
62MR Low-alloyed Date: 2002-12-05 Revision: 22 62MR is a basic-coated low hydrogen electrode producing a nominal 0.9%, designed to give excellent fracture toughness at temperatures down to -60. It is an A/D electrode with optimised welder-appeal, especially in the vertical up position, producing a finely rippled bead surface and good slag detachability. zes up to 3,25x350 mm have a thin coating ideally suited for root pass welding and joints with restricted access. 62MR conforms to NAE requirements for oil and gas production equipment in sour service and has excellent TOD values, making it highly suitable for offshore applications. Basic D +/-, A O 70, For root passes: D - Hydrogen content / 100 g < 5 ml 110-120% 350-400, 2h 0,06 0,08 0 0,3 0 1,05 1,3 1,60 5 0,005 5 r 0,9 1,0 lassification: EN 499-95 ~E 46 5 1 B 32 H5 AW A5.5-96 E7018-G MR 5Y 42 HHH B 3Y HHH LR 3m, 5Y 40 H5 UDT ~E 46 6 1 B 32 H5 Force K 3212-H10 AB E 51 75 H10 2 DN 5Y 46 H5 Inspecta L WHT: 600, 1h (WHT: 620, 2h: -20 150J, -46 70J, -60 40J) TOD -10 > 0.25 mm art no. 7162-2000, -2500, -3235: thin coating. art no. 7162-3200, -4000, -5000: thick coating. ore wire: <0.012%, <0.012%, N<0.060% EN: slight deviation in u pecified WHT Yield strength, Re: 460 N/mm² 530 N/mm² 500 N/mm² Tensile trength, Rm: 530-650 N/mm² 610 N/mm² 580N/mm² Elongation, A5 23% 25% 23% Impact energy, : -50 47J -60 60J -50 70J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,00 350 71622000 40-80 23 0,64 123 0,6 43 2,50 350 71622500 60-110 22 0,73 71 54 3,25 450 71623200 80-150 24 0,73 28 1,4 82 3,25 350 71623235 80-155 23 0,73 43 1,3 54 4,00 450 71624000 140-200 24 0,72 19 1,9 89 5,00 450 71625000 200-270 24 0,72 13 2,6 100
64MR Low-alloyed Date: 2002-12-05 Revision: 11 Basic D +/-, A O 70, For root passes: D - Hydrogen content / 100 g < 5 ml 120% 350, 1h lassification: AW A5.5-96 E 8018-3 NOTE! Not in the Elga programme, but can be made on order. ore wire: < 0.012 % < 0.012 % N < 0.060 % 0.05 0.12 0,30 0,4 0.80 0,4 1,0 1.25 0 0.030 0 0.030 r 0.1 0.8 1,0 1.1 0.017 0.35 u 0.2 0.05 0.05 pecified Yield strength, Re: 470-550 N/mm² 540 N/mm² Tensile trength, Rm: > 550 N/mm² 580 N/mm² Elongation, A5 > 24% 25% Impact energy, : -40 27 J -60 70 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,5 350 7164-2500 60-110 22 0,73 70 54 3,25 350 7164-3235 80-155 24 0,73 35 1,4 62 3,25 450 7164-3200 80-155 24 0,73 29 1,4 82 4 450 7164-4000 140-210 24 0,72 20 1,9 89 5 450 7164-5000 200-270 24 0,72 14 2,6 100
65MR Low-alloyed Date: 2002-12-05 Revision: 13 65MR is a basic-coated low hydrogen electrode producing a nominal 0.9% with molybdenum addition, designed for welding steels with a minimum yield strength of 450 N/mm2 e.g. B 7191-450 EM, B 4360-55E/F and similar materials, used in offshore fabrication etc. 65MR gives a minimum yield strength of 560 N/mm2, minimum tensile strength of 610 N/mm2 and has excellent fracture toughness down to -60. It is an A/D, all-positional electrode producing a finely rippled bead surface and good slag detachability. Electrode sizes up to 3,25x350 mm have a thin coating ideally suited for root pass welding and joints with restricted access. Basic D +/-, A O 70, For root passes: D - Hydrogen content / 100 g 5 ml 110-120% 350-400, 2h 0,06 0,08 0 0,4 0 1,40 1,6 1,70 5 0,005 5 r 0,7 1,0 lassification: EN 499-95 E 50 6 1 B 32 H5 AW A5.5-96 8018-G DN UDT LR 5Y 46 H5 ~EY 55 77 1 B H5 5Y 46 H5 WHT 600, 1h art no. 7165-2500 and 7165-3235: thin coating. art no. 7165-3200,7165-4000 and 7165-5000: thick coating < 2% < 2% N < 0,060% 5 u pecified WHT Yield strength, Re: 500 N/mm² 610 N/mm² 590 N/mm² Tensile trength, Rm: 560-720 N/mm² 650 N/mm² 630 N/mm² Elongation, A5 19% 22% 19% Impact energy, : -60 47 J -60 60 J -40 60 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 350 71652500 60-110 22 0,71 71 56 3,25 450 71653200 80-150 24 0,68 31 1,5 75 3,25 350 71653235 80-155 23 0,74 42 1,4 51 4,00 450 71654000 140-200 24 0,72 20 1,9 85 5,00 450 71655000 200-270 24 0,73 13 2,6 101
70 Low-alloyed Date: 2001-01-22 Revision: 2 Basic A, D+ Hydrogen content / 100 g < 5 120 % 350-400, 2h 0,06 0,09 0,30 0,4 0,60 0,70 0,9 1,00 5 0 0,005 5 r 1,0 1,2 lassification: EN 757-97 E 55 4 1 B 32 H5 AW A5.5-96 E 9018-G AB DN Force LR K UDT EN:slight deviatoin in 3Y,Q460 3YH5 3Ym,H5 EY 55 75 1 B H5 0,40 0,60 u pecified Yield strength, Re: >550 N/mm2 570 N/mm2 Tensile trength, Rm: > 620 N/mm2 640 N/mm2 Elongation, A5 > 22 % 24 % Impact energy, : -40 >47J -40 95J Article Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,5 350 71703500 70-110 22 0,68 69 63 3,5 450 71703200 110-140 22 0,73 31 1,3 87 4,0 450 71704000 150-190 22 0,73 22 1,8 90 5,0 450 71705000 170-250 23 0,77 15 2,5 100
81R Low-alloyed Date: 2001-01-22 Revision: 15 81R is a basic-coated, low hydrogen electrode which deposits a 0.5% type. It is primarily intended for welding similar composition steels, used where creep rupture strength and ductility at service temperatures up to 550 are required e.g. DIN 15 3, B 3059 Grade 243 and ATM A335 Grade 1. The content confers some resistance to hydrogen attack in chemical process plant applications. 81R is also suitable for ordinary - steels when higher tensile strength is required. reheat and interpass temperature of 100-150 is recommended. ost-weld heat treat at 620. Basic D + Hydrogen content / 100 g < 5 ml 100% 400, 1-2h 0,07 0 0 0,4 0,60 0,75 5 0,90 5 5 0,40 0,65 lassification: EN 1599-94 E B 12 H5 AW A5.5-96 E 7015-A1 B 2493-85 E B DIN 8575-84 E B20+ NF A81-345-79 E B20 BH UDT E B20+ Inspecta TÜ L WHT:620, 1h (TÜ) WHT:650, 15h, (TÜ) Re: 285 N/mm2 (TÜ) Rm: ² 480-600 N/mm2, (TÜ) A5: 22% (TÜ) : 20 47 J operating temperature: 550 reheat and interpass temp. between 100-150 is recommended. pecified WHT Yield strength, Rp0.2%: 390 N/mm² 420 N/mm² 390 N/mm² Tensile trength, Rm: 480 N/mm² 550N/mm² 480 N/mm² Elongation, A5 25% 27% 25% Impact energy, : 20 47 J 20 90 J 20 47 J Article Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 300 71812500 65-95 21 0,63 85 0,7 57 3,25 350 71813200 95-130 23 0,67 44 1,1 70 4,00 350 71814000 120-165 23 0,71 29 1,5 75
83R Low-alloyed Date: 2002-04-19 Revision: 17 83R is a basic-coated, low hydrogen electrode which deposits a low carbon 1.25% r/ 0.5%. It is intended for welding creep resisting steels of similar composition, used in power generation plant operating at temperatures up to 570, e.g. DIN 13 r 44, G-17 r 55, B 3604 Grades 620 and 621 etc. Also suitable for use in the chemical and petrochemical industries where resistance to hydrogen attack, corrosion from sulphur bearing crude oil and stress corrosion cracking in sour environments is required. reheat and interpass temperature of 150-200 is recommended. ost-weld heat treat at 690. Basic D + Hydrogen content / 100 g < 5 ml 100% 350-400, 2h 0 0,3 0,60 0,40 0,7 0,90 5 5 r 1,0 1,2 1,4 0,45 0,65 lassification: EN 1599-94 E r 1 B 12 H5 AW A5.5-96 E 8015-B2L B 2493-85 E 1 r LBH DIN 8575-84 E r 1B20+ NF A81-345 E 1 r B 20 BH TÜ L Inspecta UDT E r 1B20+ WHT: 690, 1h. operating temperature: 570 ore wire: < 0.015 % < 0.015 % N < 0.010 % pecified WHT Yield strength, Rp0.2%: 460 N/mm² 470 N/mm² 460N/mm² Tensile trength, Rm: 550 N/mm² 600 N/mm² 550 N/mm² Elongation, A5 22% 25% 22% Impact energy, : 20 47 J 20 90 J 20 47 J roduct data Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 300 71832500 65-95 21 0,63 84 0,7 56 3,25 350 71833200 90-130 23 0,67 43 1,1 69 4,00 350 71834000 125-165 23 0,71 28 1,5 75
84R Low-alloyed Date: 2001-01-22 Revision: 15 84R is a basic-coated, low hydrogen electrode which deposits a low carbon 2.25% r/1.0%. It is intended for welding creep resisting steels of similar composition, used in steam generation plant operating at temperatures up to 600, e.g. DIN 10 r 9 10, G-18 r 9 10, G-17 r 5 11, B 3604 Grade 622 etc. Also suitable for use in the chemical and petrochemical industries where resistance to hydrogen attack, corrosion from sulphur bearing crude oil and stress corrosion cracking in sour environments is required. reheat and interpass temperature of 200-250 is recommended. ost-weld heat treat at 700. Basic D + Hydrogen content / 100 g < 5 ml 100% 350-400, 2h 0,04 0 0,3 0,45 0 0,7 0,90 5 5 r 2,0 2,3 2,5 0,90 1,0 1,20 lassification: EN 1599-94 E r 2 B 12 H5 AW A5.5-96 E 9015-B3L B 2493-85 E 2 r LBH DIN 8575-84 E r 2 B20+ NF A81-345 E 2 r B 20 BH Inspecta UDT E r 2 B20+ L TÜ WHT: 700, 1h. operating temperature: 600 reheat and interpass temp. between 200-250 is recommended. ore wire: < 0.015 % < 0.015 % N < 0.010 % pecified WHT Yield strength, Rp0.2%: 390 N/mm² 540 N/mm² 540 N/mm² Tensile trength, Rm: 620 N/mm² 680 N/mm² 620 N/mm² Elongation, A5 18% 20% 18% Impact energy, : 20 47 J 20 70J 20 47 J Article Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 300 71842500 65-95 23 0,63 83 0,7 55 3,25 350 71843200 90-130 23 0,67 42 1,1 71 4,00 350 71844000 125-165 23 0,71 28 1,5 74 5,00 450 71845000 180-270 25
85R Low-alloyed Date: 2001-01-22 Revision: 14 85R is a basic-coated, low hydrogen electrode depositing a low carbon 5% r/0.5%. It is intended for welding creep resisting steels of matching composition, used widely in chemical and petrochemical plant because of their excellent resistance to hydrogen attack and corrosion by high sulphur crude oils at service temperatures up to 650, e.g. DIN 12 r 19 5, B 3604 Grades HF 625 and F 625, ATM A155 Grade 5r etc. To avoid hydrogen cracking, preheat and interpass temperature of 250-300 must be carefully controlled. Maintain preheat for some after completion of welding. ost-weld heat treat at 840. Basic D + Hydrogen content / 100 g < 5 ml 100% 400, 1-2h 0,04 0,07 0 0,4 0 0 1,0 5 0 2 5 r 4,0 5,0 6,0 0,45 5 0,65 lassification: EN 1599-94 E r 5 B 12 H5 AW A5.5-96 E 502-15 B 2493-85 E 5 r B DIN 8575-84 E r 5 B20+ NF A81-345 E 5 r B20 BH UDT E r 5 B20+ L WHT: 840, 2h (TÜ) WHT: R at 750, 15h (TÜ) Re: 390 N/mm2 (TÜ) Rm: 590 N/mm2 (TÜ) A5: 18% (TÜ) : 20 47 J operating temperature: 650 reheat and interpass temp. between 250-300 is recommended. pecified WHT Yield strength, Rp0.2%: 400 N/mm² 460 N/mm² 400N/mm² Tensile trength, Rm: 590 N/mm² 650 N/mm² 590 N/mm² Elongation, A5 18% 20% 18% Impact energy, : 20 47 20 70 J 20 47 J Article Diam.mm Length mm roduct code urrent A oltage /kg /electrode 2,50 300 71852500 65-90 21 0,63 83 0,7 54 3,25 350 71853200 90-135 22 0,67 42 1,1 70 4,00 350 71854000 120-160 23 0,71 27 1,5 73