Comparing the Effects of Squeeze Casting on the Mechanical Properties of Selected Aluminum Alloys

Similar documents
Influence of Remelting AlSi9Cu3 Alloy with Higher Iron Content on Mechanical Properties

Introduction to Mechanical Properties, Solidification and Casting, Joining and Corrosion of Aluminium and its Alloys

EFFECTS OF COOLING MEDIA ON THE MECHANICAL PROPERTIES AND MICROSTRUCTURE OF SAND AND DIE CASTING ALUMINIUM ALLOYS

ScienceDirect. The Effect of Heat Treatment and Aging Process on Microstructure and Mechanical Properties of A356 Aluminium Alloy Sections in Casting

Correlation Between Mechanical Properties and Porosity Distribution of A356 in Gravity Die Casting and Low Pressure Die Casting

International Journal of Scientific & Engineering Research Volume 3, Issue 7, July ISSN

STUDIES ON MICROSTRUCTUREAND MECHANICAL PROPERTIES OFMODIFIED LM25 ALUMINIUM ALLOY

An establish attempt of reasons of machining splinter formation in AC47000 alloy high pressure die castings

Please refer as: Willy Handoko and Bondan T. Sofyan, Modification of Microstructure of AC4B Aluminium CastAlloys by Addition of wt. % Sr, Proc.

Effect of surface coatings of polystyrene pattern on surface morphology and mechanical properties of Al-Si eutectic casting

Evaluation of Mechanical Properties of Aluminium Metal Matrix Reinforced with Silicon

Effect of Hardness on A413 intermetallic Alloy with the influence of typical heat treatment

THE MECHANICAL PROPERTIES OF STAINLESS STEEL

A REVIEW OF PARAMETERS AFFECTING DUCTILE FRACTURE OF ALUMINUM ALLOY

The Effect of La Addition on the Microstructure and Tensile Properties of Hot-Extruded Al 15%Mg 2 Si Composite

THE EFFECT OF THERMAL AGEING ON MICROSTRUCTURE AND SOME MECHANICAL PROPERTIES OF Al/2.0% GLASS REINFORCED COMPOSITE.

Steel Properties. History of Steel

Influence of Processing Parameters in SiCp Aluminium Alloy Composite Produced by Stir Casting Method

Behavior Analysis of Aluminium Alloy with Reinforced Silicon Carbide Particles

NEW HEAT TREATMENT FOR Al HIGH PRESSURE DIE-CASTINGS

EXPERIMENTAL STUDY ON MECHANICAL PROPERTIES OF ALUMINIUM ALLOY REINFORCED WITH SILICON CARBIDE AND FLY ASH, HYBRID METAL MATRIX COMPOSITES

Modification of Al-11.1Si Alloy with Antimony through Casting Route

Evaluation of Mechanical Behaviour of Friction Stir Processing of AA6061

Department of Chemical Engineering and Materials,

MECHANICAL PROPERTIES OF ALUMINIUM 6063 ALLOY BASED GRAPHITE PARTICLES REINFORCED METAL MATRIX COMPOSITE MATERIAL

Forging Condition for Removing Porosities in the Hybrid Casting and Forging Process of 7075 Aluminum Alloy Casting

Experimental Investigation on Mechanical Behavior s of Stir Cast Aluminium 6061-SiC MMC using Taguchi Technique

Chapter 11: Applications and Processing of Metal Alloys

ME -215 ENGINEERING MATERIALS AND PROCESES

Comparing Low Pressure Permanent Mold Casting of Magnesium AZ91E and Aluminum A356

INTERNATIONAL JOURNAL OF APPLIED ENGINEERING RESEARCH, DINDIGUL Volume 1, No 4, 2011

ALUMINUM POWDER METALLURGY

Effect of melt treatment on microstructure and impact properties of Al 7Si and Al 7Si 2 5Cu cast alloys

EFFECT OF ROLLING ON HARDNESS OF ALUMINIUM METAL MATRIX COMPOSITES-AN EXPERIMENTAL STUDY

INTERDEPENDENCE BETWEEN COOLING RATE, MICROSTRUCTURE AND POROSITY IN MG ALLOY AE42

Lost foam casting(lfc)is a near-net shape forming

Journal of Reinforced Plastics and Composites OnlineFirst, published on November 20, 2008 as doi: /

The influence of remelting on the properties of AlSi6Cu4 alloy modified by antimony

Characteristics of dynamically formed oxide films on molten aluminium

CHAPTER 1 INTRODUCTION

A.S. Kiran 1, V. Desai 2, Narendranath 2 and P.G. Mukunda 1. R G g

The use of magnesium has grown dramatically in the. Section thickness-dependent tensile properties of squeeze cast magnesium alloy AM60 CHINA FOUNDRY

AL LM6 HOLLOW CYLINDER FABRICATED USING CENTRIFUGAL CASTING

Effect of Holding Time Before Solidification on Double-Oxide Film Defects and Mechanical Properties of Aluminum Alloys

The Treatment of Liquid Aluminium-Silicon Alloys

COMPUTER SIMULATION AND EXPERIMENTAL RESEARCH OF CAST PISTON POROSITY

CHAPTER INTRODUCTION

International Journal of Scientific & Engineering Research, Volume 4, Issue 6, June-2013 ISSN

Investigations on Mechanical properties of AL 8011 reinforced with micro B 4 C / Red Mud by Stir Casting Method

Effects of Alloying Additions and Cooling Rate on the Microstructures and Mechanical Properties of the Cast Al-Mg-Si Alloys

The excellent performance of austempered ductile iron

INFLUENCE OF MICROSTRUCTURE IN MECHANICAL PROPERTIES OF DIRECTIONALLY SOLIDIFIED HYPEREUTECTIC Al-15wt%Si AND Al-18wt%Si ALLOYS

Effect of Processes Parameter on Mechanical Properties in Aa2218-Fe2o3 MMCS Processed by Stir Casting

Effects Of 600 Microns Particles of Eggshell on Tensile Strength of Zinc-Aluminum (ZA27) Alloy

THE INFLUENCE OF CASTING GEOMETRY ON THE TENSILE PROPERTIES AND RESIDUAL STRESSES IN ALUMIUM CASTINGS

3. MECHANICAL PROPERTIES OF STRUCTURAL MATERIALS

Effect of The Pressure of the Squeeze Process on the Hardness and Micro Structure of Recycled Aluminum Materials

3 Department of Mechanical Engineering Technology, Universiti Tun Hussein Onn Malaysia, Batu Pahat, Malaysia,

Refining grain structure and porosity of an aluminium alloy. with intensive melt shearing

Study of the Effects of Magnesium Content on the Mechanical Properties of Aluminium 6063 Extrudates

Analysis of Mechanical and Metallurgical properties of Al-SiCp Composite by Squeeze-cum-Stir Casting

Pressure and die temperature effects on microstructure and mechanical properties of squeeze casting 2017A wrought Al alloy

Metals are generally ductile because the structure consists of close-packed layers of

MECHANICAL PROPERTIES

Effect Of Friction Stir Processing On Mechanical Properties And Microstructure Of The Cast Pure Aluminum

TENSILE AND FRACTURE BEHAVIOR OF 6061 Al-Si Cp METAL MATRIX COMPOSITES

Synthesis and Characterization of SiC Reinforced HE-30 Al Alloy Particulate MMCs

Porosity and Fatigue Performance Interactions in Aluminum Cast Alloys

Fabrication and characterisation of pure magnesium-30 vol.% SiC P particle composite

CONVENTIONAL AND SEMI-SOLID A356 ALLOY WITH ADDITION OF STRONTIUM

Fracture Analysis of a Crack Propagating in Aluminium-7% Silicon Alloy Casting

The effect of Friction Stir Processing on the fatigue life of MIG-Laser hybrid welded joints as compared to conventional FSW 6082-T6 aluminium joints

MECHANICAL PROPERTIES OF AlSi12 ALLOY WITH ALUMINIUM BRONZE

Effect of Cooling Rate and Pouring Temperature on the Hardness and Wear Resistance of Bronze SAE660

Influence of antimony on the mechanical properties and gas content of alloy AlSi6Cu4

Specification Aluminium Die-Casting Alloy, high silicon content Aluminium Die-Casting Alloy, high silicon content

Composite Materials. Metal matrix composites

Time and Strain Response of Repeated Ageing Treatments on Recycled Al-Si-Cu Alloy

EFFECTS OF STRONTIUM ON THE MICROSTRUCTURE OF AL-SI CASTING ALLOYS

INFLUENCE OF ZINC AND MAGNESIUM ADDITION ON THE FLUIDITY OF Al-Zn- Mg ALLOY

EFFECT OF SOLUTION TREATMENT TEMPERATURE ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A356 ALLOY

Semi-solid casting of pure magnesium

Simple rheocasting processes

Tensile & Fracture Behavior of Al-Si Cp Metal Matrix Composites

Water mist effect on cooling process of casting die and microstructure of AlSi9 alloy

Synthesis and Characterization of Aluminium Alloy A356 and Silicon Carbide Metal Matrix Composite

Identification and Control of Micro porosity for Al-Alloy Wheel Castings

Fundamentals of Casting

TRUE STRESS AND STRAIN

A Study on Mechanical Properties of Aluminium LM25- Si c Composites Fabricated Using Stir Casting Technique

DRY SLIDING WEAR BEHAVIOUR OF STIR CAST LM 25/ZrO 2 METAL MATRIX COMPOSITES

EVALUATION OF MECHANICAL PROPERTIES OF AL6061 METAL MATRIX COMPOSITE REINFORCED WITH FUSED ZIRCONIA ALUMINA

Heat treatment and effects of Cr and Ni in low alloy steel

BFF1113 Engineering Materials DR. NOOR MAZNI ISMAIL FACULTY OF MANUFACTURING ENGINEERING

Rajiv Suman 1, Dr. P.C.Gope 2 1 Research Scholar, Department of mechanical Engineering, College of Technology. Pantnagar (GBPUAT) Uttarakhand,INDIA

A Study on Semi Solid Squeeze Forging of High Strength Brass. K.H. Choe*, G.S.Cho*, K.W. Lee*, Y.J. Choi**, K.Y. Kim*** and M.H.

Impact Toughness of Weldments in Al Mg Si Alloys

STRUCTURE AND PROPERTIES OF ALUMINUM ALLOYS WITH ADDITIONS OF TRANSITION METALS PRODUCED VIA COUPLED RAPID SOLIDIFICATION AND HOT EXTRUSION

Sub-Liquidus Casting: Process Concept &

International Journal of ChemTech Research CODEN (USA): IJCRGG, ISSN: , ISSN(Online): Vol.10 No.

Transcription:

International Journal of Science and Engineering Investigations vol. 6, issue 63, April 217 ISSN: 2251-8843 Comparing the Effects of Squeeze Casting on the Mechanical Properties of Selected Aluminum Alloys Markson I. E. 1, Agwu O. E. 2, Ihom A. P. 3, Umana M. O. 4 1,2,3,4 Department of Mechanical and Aerospace Engineering, University of Uyo, Uyo, Nigeria ( 1 idymarks@yahoo.com, 2 o.agwu4@yahoo.com, 3 paulihom@yahoo.co.uk, 4 m.o.umana@uniuyo.edu.ng) Abstract- This study has detailed the changes in mechanical properties of selected aluminium alloys when produced using the method of squeeze casting as compared with conventional gravity castings. The alloys that were studied are: Al- 12wt.%Si, Al-12wt.%Si with sodium modifier, Al-1.3wt.%Cu- 5wt.%Si-.5wt.%Mg and Al-4.5wt.%Cu. The squeeze pressure was varied over a range of 5 MPa. The results and measurements show a marked improvement in ultimate tensile strength, ductility and hardness for samples produced by the method of squeeze casting as compared to the gravity cast samples. For instance, at 5 MPa, the ultimate tensile strength of the Al-4.5wt.%Cu alloy was found to be 6% higher than that of the same alloy produced by the conventional procedure of gravity casting. The trend was found to be similar for the other mechanical properties and alloys studied and these have been presented in the work. Further, material properties were seen to improve in all the alloys studied as cast pressure increased with the optimal pressure being in the neighbourhood of 5 MPa. Keywords- Aluminum Alloy, Squeeze Casting, Mechanical Properties I. INTRODUCTION Aluminum and its alloys are widely utilized in the transport industry largely because of their excellent strength to weight ratio. Other than this, aluminum displays a number of attractive qualities including excellent cast ability, workability and machinability as well as relatively high corrosion resistance [1]. Also, aluminum has high scrap value and the process of recycling used aluminum results in 95% energy savings compared to raw material processing [2]. Consequently, almost 4% of all aluminum used today is re-melted metal [2]. However, several mechanical properties of aluminum alloys including strength, hardness and ductility vary depending on the quality of casting. Gas porosity and microvoids are two of the defects that accompany conventional or even more advanced casting techniques [3-5]. Porosity is probably the most common defect in aluminum castings and is the result of molten alloy solidifying faster than the rate at which gas within it escapes the melt. A pore is disadvantageous for two main reasons. First, it cannot sustain external load. Second, and more importantly, it acts as a stress concentrator thereby leading to micro crack initiation and propagation [6] To address these shortcomings and thereby improve cast quality, the method of squeeze casting was developed. Squeeze casting achieves cast quality improvement by promoting molten metal solidification under applied pressure in a reuseable die. [4] Reports that components fabricated by this method a combination of permanent mold casting with die forging present with excellent surface finish and almost zero porosity. High pressure prevents development of gas bubbles in the cast thereby eliminating porosity which invariably increases the density of the casting [7,8]. The method of squeeze casting is employed in the production of combustion engine castings, casings for compressors, pistons and brake discs [9] Many researchers have reported an improvement in mechanical properties of squeeze cast aluminum alloys over the conventionally cast type. These improvements, particularly in the case of Al-Si alloys, are attributable to the shape and distribution of eutectic Si phase, the porosity and secondary dendrite arm spacing [1] [11] Studied the effect of the squeezing process on the A3 alloy and reported significant increments in ultimate tensile strength and elongation values as squeeze pressure increased. Again, the reason cited for these improvements include decreasing secondary dendrite arm spacing with increasing pressure as well as the elimination of porosities in the alloy. Optimal squeeze casting pressure range from 3 MPa to 5 MPa [11,12] Clearly then, the squeeze casting process, its effect on the mechanical properties of casts and the reasons for the observed material changes have been well researched on. Even so, there are few detailed studies on squeeze cast Al-4.5wt.%Cu alloy and fewer studies on the comparison of the properties of this alloy and other aluminum alloys cast using the same technique. The mechanical properties of four separate Al-alloys produced with the technique of squeeze casting have been compared in this study. The comparative improvement in mechanical properties for the studied alloys have, for the first time, been discussed. 41

II. MATERIAL PREPARATION The equipment and materials utilized for the study were locally sourced and produced. First off, the squeeze casting equipment was designed and produced. Then the aluminum alloys of desired composition was prepared and cast. A. Squeeze casting Equipment The squeeze cast equipment fabricated for use were made of two parts a permanent mold and a punch. The material used for the fabrication of the mold was mild steel with a cylindrical cavity of internal diameter of 48 mm, a height of 56 mm and a wall thickness of 2 mm. The purpose of the mold was to produce the required shape of casting. Consequently, the material used for the fabrication of the punch was mild steel with diameter of 46 mm. The purpose of the punch was to apply the required pressure during casting of the aluminum alloys. Plate 1 shows the fabricated squeeze casting mold and punch used for the casting of the aluminum alloys. B. Alloy Preparation The alloys were prepared with the help of liquid metallurgy. The important process parameters of the synthesized alloys were: amount of alloy, squeeze pressure, melting temperature, pouring temperature, mold temperature, mold type and size. 4 grams of aluminum alloy with varying weight percentage of alloying element (as in Table 1) were prepared by mixing of their molten charges. Aluminum and all the alloying elements were 99.9% pure. Sodium served as modifier where utilized. The crucible with the metal charged was placed inside the furnace and the melt was held at 85 C for one hour in order to attain homogeneous composition. Where modification was required, as in, sodium metal was introduced into the melt for modification of microstructure. Stirring was done by hand with the help of a metal rod for the mixing of the charge. Each melt was stirred for 3 seconds after the addition of the modifier and held for 5 minutes. Squeeze casting was carried out in a permanent mold made of mild steel pictured in Plate I. The upper die (punch) was essential for the application of requisite pressure. The mold was coated with a Boron Nitride Aerosol lubricant and then air dried. Prior to the squeeze casting, the mold was preheated to required temperature of 15 C. The temperature of the molten metal in the crucible was checked and at the required pouring temperature of 7 C, the molten aluminum silicon alloy was quickly and carefully poured from the crucible into the lower die (mold) with a 48 mm diameter and 56 mm height. The required pressure was applied on the punch for a period of 3 seconds. The pouring took between 5 and 7 seconds per mold. In pouring the metal from the crucible into the mold, the stream of metal was kept continuous and as short as possible and pouring was rapid to prevent back pressure resulting from gas entrapment. Undue agitation of the melt was avoided at all times. All precautions were taken at every other point in the foundry to avoid gas pickup and the formation and entrapment of oxides and dross. After casting, the mold was loosened and samples were taken out. For each batch cast, the first cast was allowed to cool and solidified in the shape of the mold without pressure application. Similarly a total of 48 samples were prepared with different alloy compositions and squeeze pressures of 3, 35, 4, 45 and 5 MPa were used. The prepared alloy chemical compositions are shown in Table 1. Figure 1. Fabricated Squeeze Casting Equipment C. Tensile Testing Tensile test samples were used to assess the mechanical behaviour of the alloy composition. The aluminum alloy samples were machined from each alloy composition to obtain a tensile specimen with a diameter of 5 mm and gauge length of 28 mm. Round tensile test bars were used in this investigation. The test bars were machined in accordance with the ASTM standard E8M-199. All of the test bars were subjected to mechanical property test in the as-cast condition, at room temperature on an INSTRON tensile tester. Tensile tests were carried out with a crosshead speed of 1 mm/min, which corresponds to nominal strain rate of.1 per second. During the test, the load elongation data were recorded for all test bars. The percentage elongation was both calculated from the loaded-elongation curves and measured after fracture of the test bars, by fitting the two halves of a broken test bar together and measuring the change in length over the original gage length of the bar. The yield strength at.2 percent offset was calculated from load-elongation curves recorded during the testing operation. D. Hardness Testing Tensile Hardness is defined as the resistance of a material to indentation, and it is determined by measuring the permanent depth of the indentation. More simply put, when using a fixed force (load) and a given indenter, the smaller the indentation, the harder the material. Hardness measurements can be made on a Rockwell hardness testing machine as it were in this work. First, a preliminary test force is applied to a sample using a diamond indenter. This load represents the zero or reference position that breaks through the surface to reduce the effects of surface finish. International Journal of Science and Engineering Investigations, Volume 6, Issue 63, April 217 42

Stress (MPa) Stress (MPa) TABLE I. Alloy Composition COMPOSITION OF THE ALLOYS USED IN THE STUDY Si Cu Mg Na Al Sample 1 12% Rest Sample 2 12%.1% Rest Sample 3 5% 1.3%.5% Rest Sample 4 4.5% Rest After the preload, an additional load, called the major load, is applied to reach the total required test load. This force is held for a predetermined amount of time (dwell time) to allow for elastic recovery. This major load is then released and the final position is measured against the position derived from the preload, the indentation depth variance between the preload value and major load value. This distance is converted to a hardness number. Sample used for Rockwell hardness testing in the present work was standardized with the help of a standard steel sample. Steel ball indenter of size 1/16 was chosen. A mass of 1 kg was employed as preload and applied with a steel ball indenter causing an initial penetration. Then, the dial was set to zero and a major load of 1 kg was applied. Upon removing the load the dial of the Rockwell tester gives the direct reading on Rockwell B scale. Similar processes were repeated three times for each sample to get an average value of Rockwell hardness (HRB). III. RESULTS AND DISCUSSION A. Tensile Test From the load and extension value obtained from the Instron tensile tester, corresponding engineering stress and engineering strain were calculated and plotted to get stressstrain graphs for different samples of Al-12 wt.% Si unmodified, Al-12 wt.% Si modified with.1% Na, Al- 4.5wt% Cu and Al-1.3wt% Cu 5wt% Si.5wt% Mg as shown in Figs. 2-5. Stress-strain curves describe the extent of deformation (strain) at distinct intervals of tensile or compressive stress. The curves are unique for each material and reveal many properties of the material including data to establish the modulus of elasticity a parameter which defines the resistance of a material to elastic deformation. Consequently, the shape of a stress - strain curve is important to the Materials Engineer [13]. Fig. 2 shows the stress-strain curve for Al- 12wt.%Si alloy at MPa. There are also similar graphs (in the same chart) for squeeze casting of the alloy at different pressures (ranging from 3 MPa to 5 MPa in steps of 5 MPa). 14 1 6 4 2 Figure 2. Stress-strain graph for Al-12wt.%Si unmodified for various squeeze pressures from 5 MPa 1 14 1 6 4 2 MPa 3MPa 35MPa 4MPa 45MPa 5MPa.2.4.6.8.1.2.4.6.8.1 MPa 3 MPa 35 MPa 4 MPa 45 MPa 5 MPa Figure 3. Stress-strain graph for Al-12wt.%Si Na-modified for various squeeze pressures from 5 MPa The curves clearly show that material ductility increases with casting pressure. In other words, the material undergoes more deformation (strain) before failure as squeeze pressure increases. This is evident in Fig. 3 as well where the breaking stress of the alloy is found to be farthest for the 5 MPa sample. In Fig. 3, the amount of strain possible before breakage occurs is about 23% more in the 5 MPa sample compared to the 3 MPa material. It is worthy to point out here that the material cast under gravity ( MPa) presents a stress-strain curve which flattens out as stress approaches MPa signifying that the UTS is reached at that stress value. International Journal of Science and Engineering Investigations, Volume 6, Issue 63, April 217 43

Ultimate Tensile Stength (UTS) Stress (MPa) Stress (MPa) The other curves are not as flat and enjoy further deformation at higher stress values. This represents a clear mechanical strength advantage the very essence of squeeze casting. The underlying reason for this improvement in strength has to be the absence of gas porosity and shrinkage pores in the squeeze cast alloy [14,15]. On the other hand, the piece solidified under atmospheric pressure is observed to have more pores thereby impacting negatively on alloy tensile strength. 14 1 6 4 2 Figure 4. Stress-strain graph for Al-1.3wt.%Cu-5wt.%Si-.5%Mg for various squeeze pressures from 5 MPa 1 14 1 6 4 2.2.4.6.8.1 MPa 3 MPa 35 MPa 4 MPa 45 MPa 5 MPa.2.4.6.8.1.12.14 MPa 3 MPa 35 MPa 4 MPa 45 MPa 5 MPa Figure 5. Stress-strain graph for Al-4.5wt.%Cu for various squeeze pressures from 5 MPa The curves of Fig. 4 follow the nature of those in Fig. 3. All six samples have a linear stress-strain curve up to about a stress of 4 MPa. Above that stress value, the curves lie one on top of the other as a result of the squeeze pressure. Again, for reasons of gas and shrinkage porosity absence, the highest UTS belongs to the most pressurized (5 MPa) sample [16]. Ductility is also seen to improve with increase in squeeze pressure. For the Al- 4.5wt.%Cu alloy of Fig. 5, the tensile strengths of all samples are seen to improve compared with the Al-1.3wt.%Cu- 5wt.%Si-.5wt.%Mg alloy. The increased percentage of Copper in the former creates additional strength by precipitation of CuAl 2. B. Ultimate Tensile Strength Other than the Al-1.3%Cu-5%Si-.5%Mg alloy where there is a 9% increase in UTS at a squeeze pressure of 3MPa, other samples (alloys) show no significant improvement in UTS at squeeze pressures less than 3 MPa. This is evident in the near-flat nature of the curves between and 3 MPa (Fig. 6). This result agrees with those of Raji & Khan [17]. However, beyond 3 MPa, there is a general increase in UTS for all the alloys. When squeeze pressure reached 5 MPa, the UTS of the Al-4.5wt.%Cu alloy was 162 MPa, 6% higher than the same alloy produced by gravity casting. There are increments of 23.5%, 26.4% and 31.8% in the UTS of Al- 12wt.%Si (unmodified), Al-12wt.%Si (modified) and Al- 1.3wt.%Cu-5wt.%Si-.5wt.%Mg respectively compared to their gravity-cast counterparts. At all squeeze pressures, the modified Al-12wt.%Si alloy exhibits higher UTS than the unmodified alloy. The increment in tensile strength as a consequence of Na modification agrees with Higgins [18]. Modification in the Al-Si alloy refines the eutectic phase particle shape and improves the mechanical properties (including UTS) of the cast [2]. C. Ultimate Tensile Strength It is noticed that appreciable increase in material elongation (ductility) is evident beyond a squeeze pressure of 3 MPa (Fig. 7). 17 15 14 13 11 1 2 4 6 Squeeze Presure (MPa) unmodified Na modified Al-1.3%Cu- 5%Si-.5% Mg Al-4.5% Cu Figure 6. Effect of squeeze pressure on UTS for the aluminum alloys under study International Journal of Science and Engineering Investigations, Volume 6, Issue 63, April 217 44

Rockwell Hardness Elongation% The Al-4.5%Cu alloy starts off being the least ductile of all the alloys considered. But at 5 MPa, there is a 125% increase in its elongation compared to the 3 MPa value. The other alloys enjoy increments in ductility but not as much. The reason is probably that the presence of metallic Cu in the Al- 4.5%Cu alloy improves the metallic properties (including ductility) of the alloy. It is well known that the mechanical properties of an alloy consisting of a ductile phase and a hard brittle phase depend on the distribution of the brittle phase in the microstructure. If the brittle phase is present as a grain boundary envelope, the alloy tends to be brittle [19]. However, the brittleness of the alloy is reduced somewhat if the brittle phase is in the form of discontinuous particles at grain boundaries [2]. 4 3 2 1 Figure 7. Effect of squeeze pressure on elongation of samples of the aluminum alloys under study 95 9 85 75 7 65 2 4 6 Squeeze Presure (MPa) 1 2 3 4 5 6 Squeeze Presure (MPa) unmodified Na modified Al-1.3%Cu- 5%Si-.5Mg Al-4.5%Cu unmodified Na modified Al-1.3%Cu-5%Si-.5% Mg Al-4.5%Cu Figure 8. Effect of squeeze pressure on the hardness of samples of the aluminum alloys under study D. Hardness Test As it were with previous mechanical properties studied, hardness of alloys is seen to show positive increase as casting squeeze pressure increases (Fig. 8). Overall, hardness increases from a range of 69 75 HRB to about 83 92 HRB. The greatest increment occurred in the modified alloy. The hardness test results agree with earlier work carried out by [2]. The applied pressure in the process of squeeze casting serves to suppress the nucleation of gas pores. Besides that, [2] further noticed a decrease in secondary dendrite arm spacing as squeeze pressure increases all contributing to improvement in material hardness. IV. CONCLUSION An investigation has been carried out on the mechanical properties of squeeze cast aluminum alloys of different compositions. These properties of a squeeze cast aluminum alloy were compared with those of the gravity cast aluminum alloys. Improvements in three key mechanical properties of the alloys was noticed. There is a considerable increment in material strength as casting pressure increases. Beyond 3 MPa, there is a general increase in strength for all the alloys. For instance, at 5 MPa, the UTS of the Al-4.5wt.%Cu alloy was found to be 6% higher than that of the same alloy produced by conventional gravity casting. The trend is similar for the other alloys studied. There are increments of 23.5%, 26.4% and 31.8% in the UTS of Al-12wt.%Si (unmodified), Al-12wt.%Si (modified) and Al- 1.3wt.%Cu-5wt.%Si-.5wt.%Mg respectively compared to their gravity-cast counterparts. Also, material ductility and hardness was seen to improve as casting pressure increased. For example, the Al-4.5wt.%Cu cast under a pressure of 5 MPa experiences a 125% increase in its elongation compared to the 3MPa value. Further, alloys tend to become harder as casting pressure increases. The hardness of samples was found to increase from a range of 69 75 HRB to about 83 92 HRB, the biggest improvement occurring in the modified Al-12wt.%Si alloy. REFERENCES [1] Okorafor O. E. (27), Foundry Technology, M. C. Computer Press, Nnewi, Nigeria. [2] Obiekea K., Aku S. Y and Yawas D. S. (212). Influence of Pressure on the Mechanical Properties and Grain Refinement of Die Cast Aluminum A135 Alloy. Advances in Applied Science Research, 3 (6), pp. 3663 3673. [3] Kurz W, Fisher D. J. (1989) Fundamentals of Solidification, 3rd ed., Trans. Tech. Publ., Switzerland. [4] Ghomashchi M. R., Vikrov A. (2). Squeeze Casting: An Overview, Journal of Materials Processing Technology, 11:1-9. [5] Anson J. P. and Gruzleski J. E. (2). Effect of Hydrogen content on relative shrinkage and gas microporosity in Al-7%Si casting. AFS Transactions, pp. 135 141. [6] Haizhi, Y. (23). An overview of the development of Al-Si-Alloy Based Material for Engine Applications. Journal of Materials Engineering and Performance, 12(3), pp. 288 297. International Journal of Science and Engineering Investigations, Volume 6, Issue 63, April 217 45

[7] Chaterje B. and Das A. A. (1973). The British Foundryman, volume 14, p. 118 [8] Zyska A., Konopka Z., Lagiewka M. (27). The solidification of squeeze cast AlCu4Ti alloy. Archives of Foundry Engineering, 7(4), pp. 193 196. [9] Zyska A., Konopka Z., Lagiewka M. and Nadolski M. (211). The influence of modification and squeeze casting on properties of AlSi11 alloy castings. Archives of Foundry Engineering, 11(2), pp. 153 156. [1] Dispinar D., Campbell J. (27). J. Mater. Process. Technol., 182, p. 955. Doi:1.116/j.matprotec.26.8.21 [11] Murat, L. H., (212). Effect of casting parameters on the Microstructure and Mechanical Properties of Squeeze Cast A3 Aluminum die cast Alloy. Kovove Materials Journal. Vol. 5, pp. 243 25. [12] Ozer G., Guler K. A. and Murat H. L. (212). Effects of squeeze pressure on microstructure, porosity and hardness of an in-situ Mg2Si/Al-Si-Cu composite. Materials Testing, 54. [13] Brown R. (1999). 'Foseco Non-Ferrous Foundryman s Handbook', 11th edn; Butterworth-Heinemann, Oxford. [14] Choong D. L. (28). Variability in the Tensile Properties of Squeezecast Al Si CuAlloy A488: 296 32. [15] Mrowka-Nowotnik G. and Sieniawski J. (211). Microstructure and Mechanical Properties of C355. Cast Aluminum Alloy. International Scientific Journal of Archives of Materials Science and Engineering 47(2): 85-94. [16] Surappa, M. K., Blank, E. W., and Jaquet, J. C.(1986). "Effect of Macro- Porosity on the Strength and Ductility of Cast Al-7Si-.3Mg Alloy," Scripta Metallurgica, 2:1281-1286. [17] Raji A. and Khan R. H. (26). Comparative Analysis of Al.8%Si Alloy Produced by Squeeze Casting and Chill Casting. Journal of Material Science and Engineering 121(3): 11-16. [18] Higgins, R. A. (1983). Properties of Engineering Materials, Hodder and Stoughton Educational, Bungay, Suffolk. Pp. 56-223. [19] Rana R. S., Rajesh P. and Das S. (212). Reviews of the Influences of Alloying Elements on the Microstructure and Mechanical Properties of Aluminum Alloys and Aluminum Alloy Composites. International Journal of Scientific and Research Publications 2(6):1-7. [2] Masoumi, M. and Henry, H. (211). Influence of Applied Pressure on Microstructure and Tensile Properties of Squeeze cast Magnesium Mg- Al-Ca Alloy. Material Science and Engineering A, Vol. 528, pp. 3589 3593. International Journal of Science and Engineering Investigations, Volume 6, Issue 63, April 217 46