Neodymium Doped Yttrium Orthovanadate (Nd:YVO4) Nd:YVO4 is the most efficient laser host crystal for diode pumping among the current commercial laser crystals, especially, for low to middle power density. This is mainly for its absorption and emission features surpassing Nd:YAG. Pumped by laser diodes, Nd:YVO4 crystal has been incorporated with high NLO coefficient crystals (LBO, BBO or KTP) to frequency-shift the output from the near infrared to green, blue or even UV. This incorporation to construct all solid state lasers is an ideal laser tool that can cover the most widespread applications of lasers, including machining, material processing, spectroscopy, wafer inspection, light displays, medical diagnostics, laser printing, and data storage, etc. It has been shown that Nd:YVO4 based diode pumped solid state lasers are rapidly occupying the markets traditionally dominated by water-cooled ion lasers and lamp-pumped lasers, especially when compact design and single-longitudinal-mode outputs are required. Nd:YVO4 s Advantages over Nd:YAG 1). As high as about five times larger absorption efficient over a wide pumping bandwidth around 808 nm (therefore, the dependency on pumping wavelength is much lower and a strong tendency to the single mode s output); 2). As large as three times larger stimulated emission cross section at the lasing wavelength of 1064nm; 3). Lower lasing threshold and higher slope efficiency; 4). As a uniaxial crystal with a large birefringence, the emission is only a linearly polarized. Capabilities With advanced technology on growing and manufacturing high optical quality Nd:YVO4 crystals, We can provide a wide variety of finished crystals, our general Nd:YVO4 production capabilities include: 1). Various Nd doping concentration from 0.1 to 3.0 atm%; 2). Dopant concentration tolerance: ±0.05% (atm% <1%), ±0.1% (atm% 1%); 3). Various size bulk and finished high quality Nd:YVO4 crystals up to Φ35x50mm 3 and Φ20x20mm 3, respectively; 5,000 pcs of Nd:YVO4 devices per month in sizes 3x3x0.5 mm to 4x4x8 mm; 4). With quick delivery; 5). With competitive price. +86 29 88173006 +86 29 88325832 http://www.chinasupply.net/optical/ mirafone@163.net 1
Nd:YVO4 Basic Properties Atomic Density 1.26 x10 20 atoms/cm 3 (Nd1.0%) Crystal Structure Zircon Tetragonal. space group D 4h -l4/amd, a=b=7.112, c=6.289 Density 4.22 g/cm 3 Mohs Hardness 4-5 (Glass-like) Thermal Expansion Coefficient (300K) α a =4.43x10-6 /K, α c =11.37x10-6 /K Thermal Conductivity Coefficient (300K) //C:5.23 W/m/K; C: 5.10W/m/K Nd:YVO4 Optical Properties Peak Absorption Wavelength Lasing Wavelength 808nm 914nm, 1064nm, 1342nm Positive uniaxial, n o =n a =n b n e =n c Crystal Class n o =1.9573, n e =2.1652 @ 1064nm n o =1.9721, n e =2.1858 @ 808nm n o =2.0210, n e =2.2560 @ 532nm Thermal Optical Coefficient (300K) dn o /dt=8.5x10-6 /K, dn e /dt=3.0x10-6 /K Stimulated Emission Cross-section 25.0x10-19 cm 2 @1064 nm Fluorescent Lifetime, Nd=1.2 atm% Nd=2.0 atm% 90 μs @ 808 nm 50 μs @ 808 nm Absorption Coefficience, Nd=1.1 atm% 31.4 cm -1 @ 808 nm Absorption Length, Nd=1.1 atm% 0.32 mm @ 808 nm Intrinsic Loss, Nd=1.1 atm% Less 0.1% cm -1 @1064 nm Gain Bandwidth 0.96nm (257GHz)@1064nm Polarized Laser Emission π polarization; parallel to optic axis (c-axis) Diode Pumped Optical to Optical efficiency > 60% Sellemeier Equation (λ in μm) n 2 o =3.77834+0.069736/(λ 2-0.04724) - 0.0108133λ 2 n 2 e =4.59905+0.110534/(λ 2-0.04813) - 0.0122676λ 2 Nd:YVO4 Laser Properties 1). One of the most attractive character of Nd:YVO4 is compared with Nd:YAG, it has 5 times larger absorption coefficient in a broader absorption bandwidth around the 808nm peak pump wavelength, which just matches the standard of high power laser diodes currently available. This means a smaller Nd:YVO4 crystal that could be used for the laser, leading to a more compact laser system. For a given output power, this also means a lower power level at which the laser diode operates, thus extending the lifetime of the expensive laser diode. The broader absorption bandwidth of Nd:YVO4 which may reaches 2.4 to 6.3 times that of Nd:YAG, is also valuable. Besides more efficient pumping, Nd:YVO4 also means a broader range of selection of diode specifications. This will be helpful to laser system makers for wider tolerance and lower cost choice. 2). Nd:YVO4 crystal has larger stimulated emission cross-sections, both at 1,064nm and 1,342nm. When a-axis cut Nd:YVO4 crystal lasing at 1,064m, it is about 4 times higher than that of Nd:YAG, while at 1,340nm the stimulated cross-section is 18 times larger, which leads to a CW operation completely outperforming Nd:YAG at 1,320nm. These make Nd:YVO4 laser be easy to maintain a strong single line emission at the two wavelengths. +86 29 88173006 +86 29 88325832 http://www.chinasupply.net/optical/ mirafone@163.net 2
3). Another important character of Nd:YVO4 lasers is, because it is an uniaxial rather than a high symmetry of cubic as Nd:YAG, what it emits is only a linearly polarized, thus avoiding undesired birefringent effects on the frequency conversion. Although the lifetime of Nd:YVO4 is about 2.7 times shorter than that of Nd:YAG, its slope efficiency can be still quite high for a proper design of laser cavity, because of its high pump quantum efficiency. The major laser properties of Nd:YVO4 vs Nd:YAG are listed in Table below, including stimulated emission cross-sections (σ), Absorption Coefficient (α) Fluorescent lifetime (τ), Absorption Length (La), threshold Power (P th ) and Pump Quantum Efficiency (ηs). Laser Properties of Nd:YVO4 vs Nd:YAG Laser Crystal Doping (atm%) σ (x10-19 cm 2 ) α(cm -1 ) τ (μs) L a (mm) P th (mw) ηs (%) Nd:YVO4(a-cut) 1.0 25 31.2 90 0.32 30 52 2.0 25 72.4 50 0.14 78 48.6 Nd:YVO4(c-cut) 1.1 7 9.2 90 231 45.5 Nd:YAG 0.85 6 7.1 230 1.41 115 38.6 Typical Results of Nd:YVO4 Diode pumped Nd:YVO4 laser output comparing with diode pumped Nd:YAG laser: Laser Crystal Size (mm 3 ) Pump Power Output (@1064nm) Nd:YVO4 3x3x1 850 mw 350 mw Nd:YVO4 3x3x5 15 W 6 W Nd:YAG 3x3x2 850 mw 34 mw Diode pumped Nd:YVO4+KTP green laser: 8W green laser was generated from a 15W LD pumped 0.5% Nd:YVO4 with intracavity KTP; 200mW green outputs are generated from 1W LD pumped 2% Nd:YVO4 lasers by using our 2x2x5mm KTP and 3x3x1mm Nd:YVO4. Marks on the crystals For general a-cut Nd:YVO4, there is a dot mark on the surface, which normal to the optical axis. And, if the coating is different on the input and output surface, there is an arrow mark on the crystal side surface, which direct from input surface to output surface. Nd:YVO4 Coatings We provide Nd:YVO4 with the following coatings: 1). Both ends AR/AR-1064/808nm, R<0.2%@1064nm, R<2%@808nm. 2). S1:HR@1064 & 532nm, HT@808 nm, R>99.8%@1064 & 532nm, T>90%@808nm, S2:AR@1064 & 532nm, R<0.2% @1064nm, R<0.5%@532nm. 3). S1:HR@1064, HT@808, R>99.8%@1064nm, T>95%@808nm, S2:AR@1064, R<0.1%@1064nm. 4). S1, S2:AR-coated, S3:gold/chrome plated. 5). Both ends AR/AR-1064nm; S3: AR-808nm. Other coatings are available upon request. +86 29 88173006 +86 29 88325832 http://www.chinasupply.net/optical/ mirafone@163.net 3
coation 1 coation 2 coation 3 coation 4 coation 5 We warranty on Nd:YVO4 Specifications Dimension Tolerance: (W±0.1mm) x (H±0.1mm) x (L+0.5/ 0.1mm) (L 2.5mm) (W±0.1mm) x (H±0.1mm) x (L+0.2/ 0.1mm) (L<2.5mm) Clear Aperture: central 90% or the diameter. Flatness: less than λ/8 @ 633nm (L 2.5mm), λ/4 @ 633nm (L<2.5mm) Transmitting Wavefront Distortion: less than λ/4 @ 633nm Chamfer: 0.2mmx45 Chip: 0.1mm Scratch/Dig Code: better than 10/5 to MIL PRF 13830B Parallelism: 10 arc seconds Perpendicularity: 5 arc minutes Angle Tolerance: 0. 5 Damage Threshold[GW/cm2]: >1.0 for 1064nm,TEM 00, 10ns, 10HZ (AR coated) Quality Warranty Period: one year under proper use. Note: To inquiry or order a finished Nd:YVO4 laser crystals, please specify the specification listed above, for common specification, we only need to know the main specification: Nd dopant concentration, sizes, surface quality and coating. For special request, please specify specification in details for evaluation and fabrication. Standard Nd:YVO4 Specifications Part No. Dimension Nd Coating (mm) (atm%) S1 FRT-NYV001 3x3x1 0.5 AR@1064nm, HT@808nm AR@1064nm FRT-NYV002 3x3x1 1.0 AR@1064nm, HT@808nm AR@1064nm FRT-NYV003 3x3x1 1.0 HR@1064nm, HT@808nm AR@1064nm S2 +86 29 88173006 +86 29 88325832 http://www.chinasupply.net/optical/ mirafone@163.net 4
FRT-NYV004 3x3x1 1.0 HR@1064nm, HT@808nm, HR@532nm AR@1064nm FRT-NYV005 3x3x3 0.5 AR@1064nm, HT@808nm AR@1064nm, HT@808nm FRT-NYV006 3x3x3 0.5 HR@1064nm, HT@808nm AR@1064nm, HT@808nm FRT-NYV007 3x3x5 0.5 AR@1064nm, HT@808nm AR@1064nm, HT@808nm FRT-NYV008 3x3x8 0.5 AR@1064nm, HT@808nm AR@1064nm, HT@808nm FRT-NYV009 3x3x12 0.5 AR@1064nm, HT@808nm AR@1064nm, HT@808nm FRT-NYV010 3x3x3 1.0 AR@1064nm, HT@808nm AR@1064nm, HT@808nm FRT-NYV011 3x3x3 1.0 HR@1064nm, HT@808nm AR@1064nm, HT@808nm FRT-NYV101 3x3x0.5 3.0 HR@1064nm, HR@532nm, HT@808nm AR@1064nm&532 nm FRT-NYV102 3x3x1 1.0 HR@1064nm, HR@532nm, HT@808nm AR@1064nm&532 nm FRT-NYV103 3x3x1 2.0 HR@1064nm, HR@532nm, HT@808nm AR@1064nm&532 nm FRT-NYV104 3x3x3 1.0 HR@1064nm, HR@532nm, HT@808nm AR@1064nm&532 nm FRT-NYV105 3x3x5 0.5 HR@1064nm, HR@532nm, HT@808nm AR@1064nm&532 nm FRT-NYV106 3x3x2 1.0 HR@1064nm, HR@532nm, HT@808nm AR@1064nm&532 nm FRT-NYV107 3x3x2 0.5 HR@1064nm, HR@532nm, HT@808nm AR@1064nm&532 nm Nd:YVO4 +KTP Cemented Series We develop a new product series (Nd:YVO4 +KTP) for very compact design of diode pumped green lasers. Nd:YVO4 and KTP crystals are cemented together which is shown below. Nd:YVO4 (Nd-3.0atm%) KTP (θ=90, φ=23.5 ) Part No. Size (mm) Coatings: S1 Size (mm) Coating: S4 FRT-NKC001 1.0x1.0x0.5 HR@1064nm 1.0x1.0x2.0 FRT-NKC002 2.0x2.0x0.5 HT@808nm 2.0x2.0x2.0 HR@1064nm FRT-NKC003 1.0x1.0x0.5 HR@1064nm 1.0x1.0x2.0 HT@532nm HR@532nm FRT-NKC004 2.0x2.0x0.5 2.0x2.0x2.0 HT@808nm Note: Coating specification: AR@1064nm, R<0.1%; HR@1064nm, R>99.8%; HR@ 532nm, R>98%, HT@808nm, T>95%. +86 29 88173006 +86 29 88325832 http://www.chinasupply.net/optical/ mirafone@163.net 5