PROTECTIVE COATINGS FOR INDUSTRY Flooring Coating Systems
Contents Page Portfolio Overview Product Data Sheets Standard System Sheets Case Studies
Tikkurila Floor Coating Systems Tikkurila s flooring portfolio offers a wide range of products suitable for everything from light duty cosmetics applications to that of specialist self-leveling and trowelled screeds for the most hardwearing floor and steel decking requirements. In addition to providing High Performance Industrial Coatings, we also offer a free technical service to assist in site surveys and prepare bespoke specifications for each project. Dust Binding Varnishes & Sealers Ensi Urethane Oil For protection and dust-binding of concrete surfaces. Colour: clear Temafloor 220W A two-component, solvent free epoxy varnish. Suitable for dust binding and for priming of damp concrete surfaces. Temafloor 400 A two-component, solvent-free epoxy varnish. Used as a binder for Temafloor 4000 grinding screed and epoxy concrete. Waterborne Paints & Varnishes Fontedur FL Matt. A two-component, full-matt water-borne polyurethane top varnish. Suitable to be used a top varnish for Temafloor epoxy and polyurethane floors Fontecoat FL100 A two component, water borne epoxy paint. For painting of new, old and earlier painted concrete surfaces Betalux Akva Water-based polyurethane-acrylate. Suitable also for previously alkyd and epoxy paint or varnish-treated floors for maintenance painting. Solvent-borne Paints & Coatings Temafloor PU A solvent free, two-component polyurethane coating. For new and old concrete and asphalt floors exposed to mechanical and chemical stress. Available in grey. Temafloor P300 A two-component, solvent free, self-levelling epoxy coating. For new and old concrete floors exposed to heavy mechanical stress. Betalux Temacoat RM40 Solvent-borne one component top coat. Suitable also for previously alkyd and epoxy paint or varnish-treated floors for maintenance painting. A two component, resin modified epoxy paint. Flooring Screeds Temafloor 3000 A solvent free epoxy resin screed. The screed is prepared by adding sand to Temafloor P 300 epoxy coating mixture Temafloor 4000 ESD Solvent free Temafloor 4000 ESD grinding screed is prepared by adding conductive sand mixture to Temafloor 401 epoxy varnish mixture.
Product Data Sheets
PRODUCT DATA SHEET 18.02.2009 1 (2) Ensi DESCRIPTION PRODUCT FEATURES RECOMMENDED USES Urethane oil. For protection and dust-binding of concrete surfaces. Suitable for concrete floors and walls in industry, store and cellar spaces. TECHNICAL DATA Features Colour Range Gloss groups Coverage Application method Drying time at 23 C and 50% relative air humidity Solids volume Density Withstands well abrasion and washing. Resistant against petrol, spirits and lubrication oils and grease. Resistant against vegetable and animal grease and weak solutions of acids and alkali. Clear. Gloss Coverage on concrete floors is on the average: Porous concrete surfaces: 3-6 m 2 /l Tight concrete surfaces: 10-15 m 2 /l Practical coverage depends on the porosity of the substrate and on the application method. By brush or roller. Dust dry after Touch dry after 2 hours 6 hours Dries also in low temperature, over + 5 ºC. 30 ± 2 % volume 0.8 kg / l Product code 005 0433
PRODUCT DATA SHEET 18.02.2009 2 (2) Ensi APPLICATION DETAILS Application conditions Preparation The relative humidity of the concrete should not exceed 97 %. The temperature of the ambient air, surface or coating should not fall below + 5 ºC during application or drying. Relative humidity of air should not exceed 80 %. New concrete: Remove laitance by power grinding or hydrochloric acid etching. Choose the method best suited for the premises. After cleaning remove dust carefully with a vacuum cleaner. Hydrochloric acid etching is carried out with diluted hydrochloric acid (1 part concentrated hydrochloric acid, 4 parts water). Rinse with plenty of water. Dry the floor. Priming Treatment EU VOC 2004/ 42/EC-limit value Old concrete: Remove all grease, oil, chemicals and other impurities by MAALIPESU detergent. Clean out pot-holes removing all loose friable material. Open cracks with e.g. an abrasive tool. Remove loose material and dust. Prime using 10-20 % thinned ENSI urethane oil. Pour ENSI onto the floor and apply evenly. Application by brush or roller. The second treatment can be carried out after 12-24 hours after priming if necessary. Note! Apply ENSI thinly so that after drying it has completely absorbed into the concrete. VOC 2004/42/EC (cat A/h) 750 g/l (2007), 750 g/l (2010) Ensi: max. VOC < 750 g/l HEALTH AND SAFETY CLASSIFICATION Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy. The above information, based on laboratory tests and practical experience, has been proved valid at the date marked on the product data sheet. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As a manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes. Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com -
PRODUCT DATA SHEET 02.12.2010 1 (3) Temafloor 220W Primer DESCRIPTION PRODUCT FEATURES RECOMMENDED USES A two component solvent free epoxy varnish. For impregnating and priming of new and old concrete floors prior to laying Temafloor coatings and screeds. Suitable for dust binding and for priming of damp concrete (relative humidity of the concrete over 97 %) surfaces. Can also be used to accelerate the hardening of new concrete. Concrete floors. TECHNICAL DATA Features Colour Range Gloss groups Coverage Good resistance against abrasion, oil and grease. Yellowish. Full-gloss Thinner 1029 and 1031 Coverage on concrete floors is on the average 6-10 m 2 /l. Practical coverage depends on the porosity and evenness of the substrate and on the application method. Mixing ratio Base 2 parts by volume 008 4360 Hardener 1 part by volume 008 4370 Pot-life (+23 C) Drying time at 23 C and 50% relative air humidity Approx. 30 minutes after mixing, on substrate. Dust dry after 6 hours Recoatable after 9 hours - 3 days Fully cured after 7 days At lower temperature the drying will last longer. Solids volume approx. 100 volume % Density Product code 008 4360 1.1 kg / litre (mixture)
PRODUCT DATA SHEET 02.12.2010 2 (3) Temafloor 220W Primer APPLICATION DETAILS Application conditions Preparation Priming Patching Mixing of components The temperature of the ambient air, surface or coating should not fall below + 15 ºC during application or drying. Relative humidity of air should not exceed 80 %. New concrete: Remove laitance by power grinding, vacuum grit blasting or hydrochloric acid etching. Choose the method best suited for the premises. After grinding remove dust carefully with a vacuum cleaner. Hydrochloric acid etching is carried out with diluted hydrochloric acid (1 part concentrated hydrochloric acid, 4 parts water). Rinse with plenty of water. Dry the floor. Old concrete: Remove all grease, oil, chemicals and other impurities by MAALIPESU detergent. Remove old peeling paint layer by grinding or vacuum grit blasting. Clean out pot-holes removing all loose friable material. Open cracks with e.g. an abrasive tool. Remove loose material and dust. Curing of the concrete by using TEMAFLOOR 220: As soon as it is possible to walk on the new concrete surface, apply the varnish. Remove the varnish and laitance by power grinding or grit blasting before final coating. Prime using 30-50 % thinned Temafloor 220W Primer epoxy varnish. Pour the varnish onto the floor and apply as much as is needed to impregnate the concrete surface. If necessary, repeat priming after about 9 hours to get a non-porous surface. Patch pot-holes and cracks with a mixture of unthinned Temafloor 200W Primer epoxy varnish and dry, clean sand. Mixing ratio e.g. 1 part by volume of varnish mixture and 1-2 parts by volume of sand of grain size 0.1-0.6 mm. If the topcoat will be applied as a thin layer, grind the patched areas before overcoating. Mix the correct proportions of base and hardener thoroughly (approx. 2 minutes) by using an industrial hand drill with a paddle. Cleaning of tools Thinner 1029 (or Thinner 1031). EU VOC 2004/ 42/EC-limit value VOC 2004/42/EC (cat A/j) 500 g/l (2010) Temafloor 220W Primer: max. VOC < 500 g/l HEALTH AND SAFETY CLASSIFICATION Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj. -
PRODUCT DATA SHEET 02.12.2010 3 (3) Temafloor 220W Primer CE The European harmonized productstandard EN 13813 defines the requirements for Screed materials and floor screeds, including synthetic resin screeds. This product is tested and CE-labelled in accordance with the tables ZA.1.5 and ZA.3.3 in the appendix ZA.3. Tikkurila Oyj P.O.Box 53 FI-01301 Vantaa 11 EN 13813 SR-B2,0 Primer Reaction to fire Efl 1) Release of corrosive substances Water permeability Abrasion resistance SR NPD NPD Bond strength B2,0 Impact resistance Sound insulation Sound absorption Thermal resistance Chemical resistance NPD NPD NPD NPD NPD 1) In accordance with the Commission decision 2010/85/EC The above information, based on laboratory tests and practical experience, has been proved valid at the date marked on the product data sheet. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As a manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes. Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com
PRODUCT DATA SHEET 23.12.2010 1 (3) Temafloor 400 DESCRIPTION PRODUCT FEATURES RECOMMENDED USES A two component solvent free epoxy varnish. Used as a binder for Temafloor 4000 grinding screed and epoxy concrete. Suitable for dust binding and priming of new and old concrete floors under Temafloor coatings. Filled with sand also suitable for patching of concrete floors. Concrete floors. TECHNICAL DATA Features Colour Range Gloss groups Coverage Fire classification according to standard EN 13501 is BFL-s1. Sunlight will affect on the shade and the gloss of the varnish in the long run. Full-gloss Thinner 1029 Coverage on concrete floors is on the average: Primer 5-8 m 2 /l Topcoat 6-10 m 2 /l Practical coverage depends on the porosity and evenness of the substrate and on the application method. Mixing ratio Base 3 parts by volume 008 4403 Hardener 1 part by volume 008 4404 Application method Pot-life (+23 C) Drying time at 23 C and 50% relative air humidity Special feature Pour the varnish mixture onto the floor, spread with a rubber trowel and level with a roller. Approx. 30 minutes after mixing, on substrate. Dust dry after 6 hours Recoatable after 16-24 hours Fully cured 7 days Solids volume approx. 100 volume % Density Product code 008 4403 1.1 kg / litre (mixture) Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com
PRODUCT DATA SHEET 23.12.2010 2 (3) Temafloor 400 APPLICATION DETAILS Application conditions Preparation Priming Patching Overcoating Mixing of components Cleaning of tools Thinner 1029. EU VOC 2004/ 42/EC-limit value The relative humidity of the concrete should not exceed 97 %. The temperature of the ambient air, surface or coating should not fall below + 15 ºC during application or drying. Relative humidity of air should not exceed 80 %. New concrete: Remove laitance by power grinding, vacuum grit blasting or hydrochloric acid etching. Choose the method best suited for the premises. After grinding remove dust carefully with a vacuum cleaner. Hydrochloric acid etching is carried out with diluted hydrochloric acid (1 part concentrated hydrochloric acid, 4 parts water). Rinse with plenty of water. Dry the floor. Old concrete: Remove all grease, oil, chemicals and other impurities by MAALIPESU detergent. Remove old peeling paint layer by grinding or vacuum grit blasting. Choose the method best suited for the premises. Clean out pot-holes removing all loose friable material. Open cracks with e.g. an abrasive tool. Remove loose material and dust. Prime using about 30 % thinned Temafloor 400 epoxy varnish. Pour the varnish onto the floor and apply as much as is needed to impregnate the concrete surface. If necessary, repeat the priming to get a non-porous surface. Subsequent treatment can be carried out after 2 hours using "wet-on-wet" technique. Patch pot-holes and cracks with a mixture of unthinned Temafloor 400 epoxy varnish and dry, clean sand. Mixing ratio e.g. 1 part by volume of epoxy mixture and 1-2 parts by volume of sand of grain size 0.5-1.2 mm. Overcoating should be done within 16-24 hrs after priming. If the primed surface is not overcoated within 24 hrs, it should be abraded. Use unthinned Temafloor 400 varnish for the topcoat. Pour the varnish mixture onto the floor, spread with a rubber trowel and level with a roller. Mix the correct proportions of base and hardener thoroughly (approx. 2 minutes) by using a low speed hand drill with a paddle. The amount of mixture depends on the area to be coated and on the pot life of the mixture. Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface, weaken the properties of the coating and risk the success of the application. VOC 2004/42/EC (cat A/j) 500 g/l (2010) Temafloor 400: max. VOC < 500 g/l HEALTH AND SAFETY CLASSIFICATION Product safety data sheet Thinner safety data sheet Hardener safety data sheet Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj. TEMAFLOOR 400 [GB-ENG] THINNER 1029 [GB-ENG] TEMAFLOOR 400 HARDENER [GB-ENG] -
PRODUCT DATA SHEET 23.12.2010 3 (3) Temafloor 400 CE The European harmonized productstandard EN 13813 defines the requirements for Screed materials and floor screeds, including synthetic resin screeds. This product is tested and CE-labelled in accordance with the tables ZA.1.5 and ZA.3.3 in the appendix ZA.3. Reaction to fire Release of corrosive substances Water permeability - Abrasion resistance Tikkurila Oyj P.O.Box 53 FI-01301 Vantaa 11 EN 13813 SR-B2,0 Primer/Screed/Sealer Bfl SR NPD Bond strength B2,0 Impact resistance Sound insulation Sound absorption Thermal resistance IR4 NPD NPD NPD Chemical resistance CR 1, 2, 5, 6b, 7...8, 10...12, 14 (Class 2) The above information, based on laboratory tests and practical experience, has been proved valid at the date marked on the product data sheet. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As a manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes. Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com
PRODUCT DATA SHEET 20.11.2006 1 (2) Fontedur FL Matt DESCRIPTION PRODUCT FEATURES RECOMMENDED USES A two-component, waterborne polyurethane top varnish. Suitable to be used as a top varnish for TEMAFLOOR epoxy and polyurethene floors. Floors. TECHNICAL DATA Gloss groups Coverage Thinner Matt Not defined. Practical coverage depends on the evenness of the substrate. Water Mixing ratio Base 10 parts by volume 008 4910 Hardener 1 part by volume 008 4911 Application method Pot-life (+23 C) Drying time at 23 C and 50% relative air humidity Trowel. 5 hours. Dust dry after 40 min Fully cured after about 1 d Solids volume 40 ± 2 volume % Density At lower temperatures the curing process will last longer. 1,1 kg / l Product code 008 4910
PRODUCT DATA SHEET 20.11.2006 2 (2) Fontedur FL Matt APPLICATION DETAILS Application conditions Preparation Overcoating Mixing of components Cleaning of tools EU VOC 2004/ 42/EC-limit value The temperature of the ambient air, surface or coating should not fall below + 10 ºC during application or drying. Relative humidity of air should not exceed 90 %. Remove dust and loose particles from the floor. Remove all grease, oil and other impurities by detergent washing. Overcoating may be carried out not earlier than 16 hrs after priming. If the primed surface is not overcoated within 24 hrs, it should be abraded. Pour the coating mixture onto the floor and spread it with a trowel. Mix the correct proportions of base and hardener thoroughly before use. Mix the correct proportions of base and hardener thoroughly (approx. 3-5 minutes) by using a low speed hand drill with a paddle. Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface, weaken the properties of the coating and risk the success of the application. Water. VOC 2004/42/EC (cat A/j) 140 g/l (2007), 140 g/l (2010) Fontedur FL Matt: max. VOC < 140 g/l HEALTH AND SAFETY CLASSIFICATION Product safety data sheet Hardener safety data sheet Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy. FONTEDUR FL MATT [GB-ENG] FONTEDUR FL MATT HARDENER [GB-ENG] The above information, based on laboratory tests and practical experience, has been proved valid at the date marked on the product data sheet. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As a manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes. Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com -
PRODUCT DATA SHEET 20.11.2006 1 (2) Fontedur FL Matt DESCRIPTION PRODUCT FEATURES RECOMMENDED USES A two-component, waterborne polyurethane top varnish. Suitable to be used as a top varnish for TEMAFLOOR epoxy and polyurethene floors. Floors. TECHNICAL DATA Gloss groups Coverage Thinner Matt Not defined. Practical coverage depends on the evenness of the substrate. Water Mixing ratio Base 10 parts by volume 008 4910 Hardener 1 part by volume 008 4911 Application method Pot-life (+23 C) Drying time at 23 C and 50% relative air humidity Trowel. 5 hours. Dust dry after 40 min Fully cured after about 1 d Solids volume 40 ± 2 volume % Density At lower temperatures the curing process will last longer. 1,1 kg / l Product code 008 4910
PRODUCT DATA SHEET 20.11.2006 2 (2) Fontedur FL Matt APPLICATION DETAILS Application conditions Preparation Overcoating Mixing of components Cleaning of tools EU VOC 2004/ 42/EC-limit value The temperature of the ambient air, surface or coating should not fall below + 10 ºC during application or drying. Relative humidity of air should not exceed 90 %. Remove dust and loose particles from the floor. Remove all grease, oil and other impurities by detergent washing. Overcoating may be carried out not earlier than 16 hrs after priming. If the primed surface is not overcoated within 24 hrs, it should be abraded. Pour the coating mixture onto the floor and spread it with a trowel. Mix the correct proportions of base and hardener thoroughly before use. Mix the correct proportions of base and hardener thoroughly (approx. 3-5 minutes) by using a low speed hand drill with a paddle. Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface, weaken the properties of the coating and risk the success of the application. Water. VOC 2004/42/EC (cat A/j) 140 g/l (2007), 140 g/l (2010) Fontedur FL Matt: max. VOC < 140 g/l HEALTH AND SAFETY CLASSIFICATION Product safety data sheet Hardener safety data sheet Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy. FONTEDUR FL MATT [GB-ENG] FONTEDUR FL MATT HARDENER [GB-ENG] The above information, based on laboratory tests and practical experience, has been proved valid at the date marked on the product data sheet. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As a manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes. Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com -
Betolux Akva Floor Paint 25.02.2008 DESCRIPTION PRODUCT FEATURES Water-borne polyurethane-acrylate paint. Concrete and wooden floors and stairs in dry residential. Suitable also for renovation of floor surfaces previously painted with alkyd or epoxy paint, or treated with epoxy varnish. RECOMMENDED USES Concrete and wooden floors and stairs in dry residential, commercial and storage buildings exposed to light mechanical and chemical stress. Suitable also for renovation of floor surfaces previously painted with alkyd or epoxy paint, or treated with epoxy varnish. TECHNICAL DATA APPLICATION CONDITIONS Base paints: A, C and F Colour Range: Tikkurila Floor Paints Colour Card Colour Cards: Floor Paints Colour Card Gloss grade: Semi-gloss Building material emission class: M1 Coverage: 5-7 m 2 /l Can sizes: 0,9 l, 2,7 l, 9 l, 18 l Thinner: Water Application method: Brush or roller Drying time at 23 C and 50% relative air humidity: Dust dry after approx. 15 min. Ready to use the next day. Completely cured and reaches final durability approximately in 2 weeks Chemical resistance: Resists White Spirit and Denaturized Spirit. Does not resist strong solvents e.g. Thinner. Solids volume: n. 35 % Density: n. 1,1-1,2 kg/l, ISO 2811 Storage: Protect from frost. Product code: 412_6001/3 The surface of the concrete must be dry and at least 4 weeks old. Relative humidity of the concrete must be below 97%. During painting work and drying the temperature of the air, surface and paint must be at least 10ºC, and the relative humidity of the air below 80 %. PREPARATION New unpainted surfaces: Concrete floors: Remove laitance with a grinding machine. Remove sanding dust. Wooden floors: Remove dirt, dust, grease and oil. Treat knots with Tikkurila Knotting Lacquer. Previously painted surfaces: Wash down previously painted surfaces with Maalipesu (Cleaning Agent) and rinse carefully with water. After drying: remove old, loose paint. Sand the surfaces carefully. Remove sanding dust. manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes.
PAINTING Stir Betolux Akva well before use. Concrete floors: Prime new concrete floors with Betolux Akva Pohjuste (Primer) or once with Betolux Akva thinned 10% with water. Finish new and previously painted concrete floors with non-diluted Betolux Akva 2-3 times. Use shortpile roller or synthetic brush on small surfaces Wooden floors: Prime new wooden floors once with Betolux Akva thinned with 10% water. Finish new and previously painted floors 2-3 times with non-diluted Betolux Akva. Apply with a synthetic brush. NB The paint dries quickly, so plan the painting work ahead to avoid overlaps. Paint floor boards in longitudinal direction, only a few at a time. Any required changes must be made on dry paintwork. CLEANING INSTRUCTIONS MAINTENANCE INSTRUCTIONS EU VOC 2004/42/EC-limit value HEALTH AND SAFETY CLASSIFICATION ENVIRONMENTAL PROTECTION AND WASTE DISPOSAL TRANSPORT Clean tools with water or Tikkurila Pensselipesu (Tool Cleaner). The painted surface reaches its ultimate abrasion and chemical resistance approx. 2 weeks from the surface treatment, during that time avoid cleanup. Clean the surface with a brush, a mop or a rag. Clean soiled surfaces with cleaning supplies using neutral (ph 6-8) detergent. (cat A/i) max.140 g/l (2010). The product is not classified as dangerous. A Material Safety Data Sheet is available on request. Empty cans should be recycled or disposed of in accordance with local regulations. Liquid waste should be destroyed according to the local regulations. VAK/ADR - The above information, based on laboratory tests and practical experience, has been proved valid at the date marked on the product data sheet. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As a manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes.
PRODUCT DATA SHEET 03.04.2009 1 (4) Temafloor PU DESCRIPTION PRODUCT FEATURES RECOMMENDED USES A solvent free, two-component polyurethane coating. For new and old concrete and asphalt floors exposed to mechanical and chemical stress. Concrete floors in industrial and storage facilities, repair shops; e.g. process or paper machine units and corridors. TECHNICAL DATA Features Colour Range Gloss groups Coverage Good resistance to abrasion. Withstands water, oils, greases, chemicals and dilute solutions of non-oxidizing acids, alkali and salt solutions. Resists only temporary splashes of oxidizing acids and bleaching chemicals. Withstands + 80 ºC dry heat and + 60 ºC in immersion. Does not resist abrupt changes of temperature. Good impact resistance. Self-levelling, to be applied with serrated or steel trowel. Fire classification: BFL-s1 according to EN 13501-1. TVT 0229. Sunlight will affect on the shade and the gloss of the coating in the long run. Full-gloss Practical coverage depends on the porosity and evenness of the substrate and on the application method. Film thickness 0.3 mm coverage approx. 3 m 2 /litre Film thickness 0.5 mm coverage approx. 2 m 2 /litre Mixing ratio Application method Pot-life (+23 C) Drying time at 23 C and 50% relative air humidity Solids volume Density Product code For coating: 1 mm layer: 1 litre ready for use screed / m 2 2 mm layer: 2 litres ready for use screed / m 2 Base 4 parts by volume 534 serie Hardener 1 part by volume 008 4011 Serrated or steel trowel. 20-30 minutes on substrate, abt. 15 minutes in the mixing container. Dust dry after Light trucking after Fully cured after 6 hours 24 hours 7 days At lower temperatures the curing process will last longer. Approx. 100 % volume 1,4 kg / litre (mixture) 534-series
PRODUCT DATA SHEET 03.04.2009 2 (4) Temafloor PU APPLICATION DETAILS Application conditions Preparation Priming Patching Diluting Coating Mixing of components Cleaning of tools Thinner 1061. EU VOC 2004/ 42/EC-limit value The relative humidity of the concrete should not exceed 97 %. The temperature of the ambient air, surface or coating should not fall below + 15 ºC during application or drying. Relative humidity of air should not exceed 70 %. New concrete: Remove laitance by power grinding, vacuum grit blasting or hydrochloric acid etching. Choose the method best suited for the premises. After grinding remove dust carefully with a vacuum cleaner. Hydrochloric acid etching is carried out with diluted hydrochloric acid (1 part concentrated hydrochloric acid, 4 parts water). Rinse with plenty of water. Dry the floor. Old concrete: Remove all grease, oil, chemicals and other impurities by detergent washing. Remove old peeling paint layer by grinding, milling or vacuum grit blasting. Choose the method best suited for the premises. Clean out pot-holes removing all loose friable material. Open cracks with e.g. an abrasive tool. Remove loose material and dust. Prime using 30-50 % with Thinner 1029 thinned TEMAFLOOR 400 epoxy varnish. Pour the varnish onto the floor and apply as much as is needed to impregnate the concrete surface. If necessary, repeat priming to get a non-porous surface. Subsequent treatment can be carried out after 2 hours using "wet-on-wet" technique. A porous priming coat will result in holes and air bubbles in the finished screed. Scatter sand of grain size Ø 0,1-0,6 mm on the fresh primer coat to ensure the screed adhesion and prohibit gliding of the screed. Remove loose sand with vacuum cleaner before coating with TEMAFLOOR PU. Asphalt floors should be primed by applying TEMAFLOOR PU with a suitable steel trowel. Patch pot-holes and cracks with unthinned TEMAFLOOR 400 epoxy varnish and dry, clean sand. Mixing ratio e.g. 1 part by volume of epoxy mixture and 1-2 parts by volume of sand of grain size 0.1-0.6 mm. Grind the patched areas before overcoating. Do not thin TEMAFLOOR PU polyurethane coating. Overcoating may be carried out not earlier than 16 hrs and not later than 24 hrs after priming and patching. If the primed surface is not overcoated within 24 hrs, it should be abraded. Pour the coating mixture onto the floor and spread it with a serrated steel trowel or an adjustable trowel. Control that the thickness of layer is correct by observing coating consumption and by measuring the film thickness. Recommended thickness of a layer is 1.0-2.0 mm. Level the screed with a spiked roller approx. 10-20 min after application. Spiked roller helps removing air bubbles from the coating. Note! Add the remaining mixture to the next batch of the screed, do not scrape it out of the container onto the floor. Mix the correct proportions of base and hardener thoroughly (approx. 2 minutes) by using a low speed hand drill with a paddle. The amount of mixture depends on the area to be coated and on the pot life of the mixture. Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface, weaken the properties of the coating and risk the success of the application. VOC 2004/42/EC (cat A/j) 550 g/l (2007), 500 g/l (2010) Temafloor PU: max. VOC < 500 g/l HEALTH AND SAFETY CLASSIFICATION Product safety data sheet Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy. TEMAFLOOR PU [GB-ENG]
PRODUCT DATA SHEET 03.04.2009 3 (4) Temafloor PU Hardener safety data sheet TEMAFLOOR PU HARDENER -
PRODUCT DATA SHEET 03.04.2009 4 (4) Temafloor PU CE The European harmonized productstandard EN 13813 defines the requirements for Screed materials and floor screeds, including synthetic resin screeds. This product is tested and CE-labelled in accordance with the tables ZA.1.5 and ZA.3.3 in the appendix ZA.3. Reaction to fire Release of corrosive substances Water permeability Abrasion resistance Tikkurila Oyj P.O.Box 53 FI-01301 Vantaa 11 EN 13813 SR-B2,0 Coating/Screed Bfl SR NPD NPD Bond strength B2,0 Impact resistance Sound insulation Sound absorption Thermal resistance IR10 NPD NPD NPD Chemical resistance CR 2, 5, 5a, 10...12,14 (Class 2) The above information, based on laboratory tests and practical experience, has been proved valid at the date marked on the product data sheet. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As a manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes. Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com
PRODUCT DATA SHEET 05.08.2011 1 (3) Temafloor P 300 DESCRIPTION PRODUCT FEATURES RECOMMENDED USES A two component, solvent free epoxy coating. For new and old concrete floors exposed to heavy mechanical and chemical stress. Concrete floors in industrial and storage facilities, repair shops; e.g. process or paper machine units and corridors. TECHNICAL DATA Features Colour Range Colour Cards Gloss groups Coverage Good resistance to abrasion. Withstands water, oils, greases, chemicals and dilute solutions of non-oxidizing acids, alkali and salt solutions. Resists only temporary splashes of oxidizing acids and bleaching chemicals. A separate chemical resistance table available. Withstands + 70 ºC dry heat and + 60 ºC in immersion. Does not resist abrupt, great or repeated changes of temperature. Self-levelling. Temafloor Flex hardener makes the paint surface flexible and thus more resistant to moving or cracking of concrete. Fire classification: BFL-s1 according to EN 13501-1. Sunlight will affect on the shade and the gloss of the coating in the long run. TEMASPEED tinting. Shade of TEMASPEED tinted product may differ from shade of inplant tinted product. Full-gloss Coverage on concrete floors is on the average: Film thickness 0.3 mm coverage approx. 3 m 2 /litre Film thickness 0.5 mm coverage approx. 2 m 2 /litre Mixing ratio Practical coverage depends on the porosity and evenness of the substrate and on the application method. Base 10 parts by volume 167-serie Hardener 3,3 part by volume 930 5147 or Application method Pot-life (+23 C) Drying time at 23 C and 50% relative air humidity Special feature Paint 2 parts by volume 167-serie Flex hardener 1 part by volume 930 5002 Pour the coating mixture onto the floor and spread it with a serrated steel trowel or a trowel. Level with a roller. 20-30 minutes on substrate, approx. 15 minutes in the mixing container. Dust dry after 6 hours Light trucking after 16 hours Fully cured after 7 days At lower temperature the curing process will last longer. With Temafloor Flex hardener the curing times are a little longer than with standard hardener. Solids volume Approx. 100 volume % Density Product code 1.4 kg / litre (mixture) 167-serie
PRODUCT DATA SHEET 05.08.2011 2 (3) Temafloor P 300 APPLICATION DETAILS Application conditions Preparation Priming The relative humidity of the concrete should not exceed 97 %. The temperature of the ambient air, surface or coating should not fall below + 15 ºC during application or drying. Relative humidity of air should not exceed 80 %. New concrete: Remove laitance by power grinding, vacuum grit blasting or hydrochloric acid etching. Choose the method best suited for the premises. After grinding remove dust carefully with a vacuum cleaner. Hydrochloric acid etching is carried out with diluted hydrochloric acid (1 part concentrated hydrochloric acid, 4 parts water). Rinse with plenty of water. Dry the floor. Old concrete: Remove all grease, oil, chemicals and other impurities by MAALIPESU detergent. Remove old peeling paint layer by grinding or vacuum grit blasting. Choose the method best suited for the premises. Clean out pot-holes removing all loose friable material. Open cracks with e.g. an abrasive tool. Remove loose material and dust. Prime using 30-50 % with Thinner 1029 (or 1031) thinned Temafloor 200 Primer or 400 epoxy varnish. Pour the varnish mixture onto the floor and apply as much as is needed to impregnate the concrete surface. If necessary, repeat priming to get a nonporous surface. Subsequent treatment can be carried out after 2 hours using "wet-onwet" technique. A porous priming coat will result in holes and air bubbles in the finished screed. Patching Patch pot-holes and cracks with Colofill putty or a mixture of unthinned Temafloor 200 Primer epoxy varnish or Temafloor P 300 epoxy coating and dry, clean sand. Mixing ratio e.g. 1 part by volume of epoxy mixture and 1-2 parts by volume of sand of grain size 0.1-0.6 mm. Grind the patched areas before overcoating. Diluting Coating Mixing of components Do not thin Temafloor P 300 epoxy coating. Overcoating may be carried out not earlier than 6 hrs and not later than 24 hrs after priming and patching. If the primed surface is not overcoated within 24 hrs, it should be abraded. Pour the coating mixture onto the floor and spread it with a serrated steel trowel or a trowel. Level with a roller. Recommended film thickness is 0.3-0.5 mm. Mix the correct proportions of base and hardener thoroughly (approx. 2 minutes) by using a low speed hand drill with a paddle. The amount of mixture depends on the area to be coated and on the pot life of the mixture. Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface, weaken the properties of the coating and risk the success of the application. Cleaning of tools Thinner 1029 or 1031. EU VOC 2004/ 42/EC-limit value VOC 2004/42/EC (cat A/j) 500 g/l (2010) Temafloor P300: max. VOC < 500 g/l HEALTH AND SAFETY CLASSIFICATION Product safety data sheet Thinner safety data sheet Hardener safety data sheet Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj. TEMAFLOOR P300 and 3000 [GB-ENG] THINNER 1029 [GB-ENG] TEMAFLOOR 100-200-P300 hardener [GB-ENG] The above information, based on laboratory tests and practical experience, has been proved valid at the date marked on the product data sheet. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As a manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes. -
PRODUCT DATA SHEET 05.08.2011 3 (3) Temafloor P 300 Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com
PRODUCT DATA SHEET 19.01.2009 (Previous date 26.02.2008) 1 (2) Betolux - Floor Paint Betolux - Floor Paint DESCRIPTION PRODUCT FEATURES RECOMMENDED USES TECHNICAL DATA Urethane alkyd paint. Interior concrete and wooden floors. Also suitable for repainting floors previously painted with alkyd or epoxy paints, or treated with epoxy varnish. Concrete and wooden floors and stairs in residential, commercial and storage premises. Suitable for interior concrete and wooden floors subjected to light mechanical and chemical stress. 7 11 Base paints Colour Range Gloss grade Coverage Can sizes A and C Tikkurila Floor Paint colour card and most of the shades on the Tikkurila Symphony colour card. Gloss Concrete floors 7-9 m 2 /l. Metal and wooden surfaces 9-11 m 2 /l. 0,9 l, 2,7 l, 9 l and 18 l Thinner White Spirit 1050 Application method Drying time at 23 C and 50% relative air humidity Brush, roller or spray. Wash resistance Good, SFS 3755 Chemical resistance Dust dry after 3-4 hours, recoatable after approx. 24 hours. Dries completely and reaches final durability in approx. 1 month. Resistant to fats, white spirits and denatured alcohol. Non-resistant to strong solvents, e.g. thinners. Heat resistance 120 ºC, light shades may undergo some yellowing at high temperatures, SFS 3757 Solids volume Approx. 50 % Density n. 1,0-1,2 kg/l, ISO 2811 Product code 270_6001/3 Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com
PRODUCT DATA SHEET 19.01.2009 (Previous date 26.02.2008) 2 (2) Betolux - Floor Paint APPLICATION DETAILS Application conditions Preparation The surface to be painted must be dry and at least 4 weeks old, with concrete relative humidity less than 97%, the air temperature at least + 5 º C, and relative air humidity less than 80 %. Unpainted surfaces: Concrete floors: Remove cement glue with a grinding machine. Remove sanding dust. Wooden floors: Remove all dirt, oil, dust and grease. Painting Treatment Cleaning of tools Maintenance instructions Maintenance treatment EU VOC 2004/42/ EC-limit value Previously painted surfaces: Wash down previously painted surfaces with Maalipesu (Cleaning Agent), rinse thoroughly with water and allow to dry. Remove old, flaking paint. Sand the surfaces carefully and remove sanding dust. First application: Stir the paint thoroughly before use. Apply two coats by brush, roller or spraying, dilute the first coat by 20-30% with White Spirit 1050. Apply the second coat at least 24 hrs later with undiluted or slightly diluted paint. Non-slip treatment: To increase grip on painted surfaces, Non-Slip Agent can be added to Betolux in the ratio of 0.33 l powder to 10 litres of undiluted paint. Mixing by hand is sufficient. Apply two final topcoats of non-slip paint. Apply non-slip paint to the entire floor area or parts of it marked off with tape: It is also suitable for stair step edges. White Spirit 1050 or Tikkurila Pensselipesu (Tool Cleaner) The painted surface will dry completely and reach its final durability and chemical resistance in approx. 1 month. Avoid cleaning during this period. Clean the surface with a brush, mop or duster, removing dirt with a neutral (ph 6-8) detergent. Maintenance application: Maintain surfaces previously painted with Betolux floor paint with Betolux or Betolux Akva floor paints. See also Pretreatment: Previously painted surfaces. cat (A/i) 500 g/l (2010) Betolux contains VOC max 500 g/l HEALTH AND SAFETY CLASSIFICATION ENVIRONMENTAL PROTECTION AND WASTE DISPOSAL TRANSPORT VAK/ADR - Contains: Naphtha, hydrotreated heavy (aliphatic hydrocarbon solvent) FLAMMABLE. Use only in well-ventilated areas. Do not breathe vapour/spray. If swallowed, seek medical advice immediately and show this container or label. Keep out of the reach of children. Contains ethylmethylketoxime and cobalt compound. May produce an allergic reaction. A Material Safety Data Sheet is available on request. Material Safety Data Sheet - Betolux Floor Paint Empty cans should be recycled or disposed of in accordance with local regulations. Liquid waste should be destroyed according to the local regulations. dco141008/mli130109/ars190109//270- The above information, based on laboratory tests and practical experience, has been proved valid at the date marked on the product data sheet. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As a manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes. Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com
PRODUCT DATA SHEET 01.03.2010 1 (4) Temacoat RM 40 DESCRIPTION PRODUCT FEATURES RECOMMENDED USES A two component, resin modified epoxy paint. Used as a primer or finish for interior and exterior steel, aluminium, zinc and concrete surfaces exposed to mechanical and/or chemical stress - also for underground and underwater structures. Also suitable as a single coat system. Used as a vapour barrier coating for concrete surfaces. VTT s (Technical Research Centre of Finland) report available. (When tested paint name was Reacolor). Recommended for building frameworks, tubular bridges, conveyors, ship hulls and other steelwork and equipment. TECHNICAL DATA Features Colour Cards Gloss groups Coverage Thinner 1031 Mixing ratio Application method Excellent resistance to abrasion, chemicals and water immersion. RAL, NCS, SSG, BS, MONICOLOR NOVA and SYMPHONY colour cards. TEMASPEED tinting. Semi-gloss Recommended film thicknesses dry wet Theoretical coverage 80 µm 125 µm 8.1 m 2 /l 125 µm 195 µm 5.2 m 2 /l Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated. Base 4 parts by volume 161-series Hardener 1 part by volume 008 5600 or 008 5605 (fast) By airless spray or brush. Pot-life (+23 C) 8 hours with Hardener 008 5600 4 hours with Hardener 008 5605 Drying times DFT 100 µm + 5 ºC Dust dry, after with Hardener 008 5600 Touch dry, after Recoatable, min. after Recoatable, surfaces to be submerged, min. after Recoatable with polyurethane with Hardener 008 5605 with Hardener 008 5600 with Hardener 008 5605 with Hardener 008 5600 with Hardener 008 5605 with Hardener 008 5600 with Hardener 008 5605 with Hardener 008 5600 with Hardener 008 5605 + 10 ºC + 23 ºC + 35 ºC 8 h 4 h 2 h 1 h 5 h 2½ h 1½ h ¾ h 16 h 14 h 7 h 4 h 10 h 8 h 5 h 3 h 16 h 10 h 4 h 2 h 10 h 6 h 3 h 1½ h 2 d 36 h 16 h 8 h 1½ d 18 h 12 h 6 h 2 d 48 h 24 h 12 h 1½ d 24 h 16 h 8 h Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com
PRODUCT DATA SHEET 01.03.2010 2 (4) Temacoat RM 40 paints, min. after Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation. Solids volume 65 ± 2 volume % (ISO 3233) 77 ± 2 weight % Density Product code 1.2-1.3 kg / l (mixed). 161-series
PRODUCT DATA SHEET 01.03.2010 3 (4) Temacoat RM 40 APPLICATION DETAILS Application conditions All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below +10ºC during application and drying. Relative humidity should not exceed 80%. The surface temperature of the steel should remain at least 3ºC above the dew point. Preparation Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4) Priming Finishing Painting Cleaning of tools Thinner 1031. EU VOC 2004/ 42/EC-limit value Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion. Zinc surfaces: Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with PANSSARIPESU detergent. Hot dip galvanized surfaces are recommended to be painted with a mist coat (paint thinned 25-30 %) before the actual priming. Aluminium surfaces: Sweep blast clean with none-metallic abrasives to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with MAALIPESU detergent. Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4) Concrete surfaces: The surface must dry and at least 4 weeks old. The relative humidity of the concrete should not exceed 97%. Remove any splashes and unevennesses by grinding. Remove laitance and form oil from concrete castings by sanding or blast cleaning. Any cracks, crevices and voids must be repaired with a mixture of Temafloor 200 and fine dry quartz sand. Application: 2-3 x Temacoat RM 40 Temacoat RM 40, Temacoat GPL-S Primer, Temacoat GF Primer, Temacoat PM Primer, Temacoat GPL-S MIO, Temacoat SPA, Temabond, Temasil 90, Temazinc 77, Temazinc 88 and Temazinc 99. Temacoat RM 40, Temadur, Temathane and Temacryl EA. By airless spray or brush. At spray application the paint can be thinned 0-20%. Airless spray nozzle tip 0.015" - 0.021" and nozzle pressure 120-180 bar. Spray angle shall be chosen according to the shape of the object. At brush application the paint should be thinned according to the circumstancies. The Volatile Organic Compounds amount is 310 g/litre of paint mixture. VOC content of the paint mixture (thinned 30 % by) volume is 456 g/l. Only for industrial and professional use. HEALTH AND SAFETY CLASSIFICATION Product safety data sheet Thinner safety data sheet Hardener safety data sheet Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj. TEMACOAT RM 40 [GB-ENG] THINNER 1031 [GB-ENG] HARDENER 008 5600 [GB-ENG]
PRODUCT DATA SHEET 01.03.2010 4 (4) Temacoat RM 40 The above information, based on laboratory tests and practical experience, has been proved valid at the date marked on the product data sheet. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As a manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes. Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com -
PRODUCT DATA SHEET 05.08.2011 1 (4) Temafloor 3000 DESCRIPTION PRODUCT FEATURES RECOMMENDED USES A solvent free epoxy resin screed. The screed is prepared by adding sand to Temafloor P 300 epoxy coating mixture. For new and old concrete floors exposed to heavy mechanical and chemical stress in industrial facilities. Warehouses and repair shops; e.g. process or paper machine units, corridors and other floors subjected to high point loadings. TECHNICAL DATA Features Colour Range Colour Cards Excellent resistance to abrasion. Withstands water, oils, greases, chemicals and diluted solutions of non-oxidizing acids, alkali and salt solutions. Resists only temporary splashes of oxidizing acids and bleaching chemicals. Separate chemical resistance table available. Withstands + 70 ºC dry heat and + 60 ºC in immersion. Does not resist abrupt, great or repeated changes of temperature. Self-levelling. Can be used for floors with a max. slope of 5 %. Temafloor Flex hardener makes the paint surface flexible and thus more resistant to moving or cracking of concrete and improves the impact resistance. Fire classification: BFL-s1 according to EN 13501-1. Sunlight will affect on the shade and the gloss of the coating in the long run. TEMASPEED tinting. Shade of TEMASPEED tinted product may differ from shade of inplant tinted product. Gloss groups Full-gloss Coverage For a flat substrate: 1 mm layer: 1 litre ready for use screed / m 2 2 mm layer: 2 litres ready for use screed / m 2 4 mm layer: 4 litres ready for use screed / m 2 Mixing ratio Practical coverage depends on the evenness of the substrate. Temafloor P 300 mixture: Base 10 parts by volume 167-s. Hardener 3,3 part by volume 930 5147 Application method Pot-life (+23 C) Drying time at 23 C and 50% relative air humidity Temafloor P 300 Flex mixture: Base 2 parts by volume 167-s. Flex Hardener 1 part by volume 930 5002 Screed film thickness 1.5-3.0 mm 1 part by vol. Temafloor P 300 mixture 1 part by vol. sand grain size Ø 0.1-0.6 mm Screed film thickness3.0-4.0 mm 1 part by vol. Temafloor P 300 mixture 1 part by vol. sand grain size Ø 0.1-0.6 mm ½ part by vol. sand grain size Ø 1.0-2.0 mm 25 litres of Temafloor P 300 filled with sand using the above mixing ratios give approx. 36 and 44 litres of Temafloor 3000 epoxy screed ready for use. Reduce the amount of sand, if the temperature of screed, sand and ambient air is below 20 ºC. Adjustable or steel trowel or spiked roller. 20-30 minutes on substrate, approx. 15 minutes in the mixing container. Dust dry after 6 hours Light trucking after 24 hours Fully cured after 7 days At lower temperature the curing process will last longer. With Temafloor Flex hardener the curing times are a little longer than with standard hardener. Special feature Fire classification: BFL-s1 according to EN 13501-1 Solids volume Approx. 100 volume % Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com
PRODUCT DATA SHEET 05.08.2011 2 (4) Temafloor 3000 Density Product code 1.8-2.0 kg / litre (mixture), depending on the grain size and amount of sand. 167-series
PRODUCT DATA SHEET 05.08.2011 3 (4) Temafloor 3000 APPLICATION DETAILS Application conditions Preparation Priming Patching Diluting Screeding Joint sealing Mixing of components The relative humidity of the concrete should not exceed 97 %. The temperature of the ambient air, surface or coating should not fall below + 15 ºC during application or drying. Relative humidity of air should not exceed 80 %. New concrete: Remove laitance by power grinding, vacuum grit blasting or hydrochloric acid etching. Choose the method best suited for the premises. After grinding remove dust carefully with a vacuum cleaner. Hydrochloric acid etching is carried out with diluted hydrochloric acid (1 part concentrated hydrochloric acid, 4 parts water). Rinse with plenty of water. Dry the floor. Old concrete: Remove all grease, oil, chemicals and other impurities by MAALIPESU detergent. Remove old peeling paint layer by grinding, milling or vacuum grit blasting. Choose the method best suited for the premises. Clean out pot-holes removing all loose friable material. Open cracks with e.g. an abrasive tool. Remove loose material and dust. Prime using 30-50 % with Thinner 1029 (or 1031) thinned Temafloor 200 Primer or 400 epoxy varnish. Pour the varnish onto the floor and apply as much as is needed to impregnate the concrete surface. If necessary, repeat priming to get a non-porous surface. Subsequent treatment can be carried out after 2 hours using "wet-on-wet" technique. A porous priming coat will result in holes and air bubbles in the finished screed. Patch pot-holes and cracks with a mixture of unthinned Temafloor 200 Primer epoxy varnish or Temafloor P 300 epoxy coating and dry, clean sand. Mixing ratio e.g. 1 part by volume of epoxy mixture and 1-2 parts by volume of sand of grain size 0.1-0.6 mm. Do not thin Temafloor 3000 epoxy screed. The screed may be applied not earlier than 6 h (23 ºC) and not later than 24 h after priming and patching. If the primed surface is not overcoated within 24 hrs, it should be abraded. Pour the screed mixture onto the floor and spread it with an adjustable or a serrated trowel. When using a flat-bladed steel trowel, control that the thickness of layer is correct by observing screed consumption and by measuring the film thickness. Level the screed with a spiked roller approx. 10-15 min after application. Spiked roller helps removing air bubbles from the coating. Note! Add the remaining mixture to the next batch of the screed, do not scrape it out of the container onto the floor. When you apply screed on large areas, place working joints in line with pillars, expansion joints, gullies etc. Make working joints and trimmings by using a wide masking tape. Apply the screed on the masking tape and remove after levelling with a spiked roller. When continuing application mask the edge of the already hardened layer of screed and remove the tape after application and levelling with a spiked roller.when you apply screed on large areas, place working joints in line with pillars, expansion joints, gullies etc. Make working joints and trimmings by using a wide masking tape. Apply the screed on the masking tape and remove after levelling with a spiked roller. When continuing application mask the edge of the already hardened layer of screed and remove the tape after application and levelling with a spiked roller. Mix the correct proportions of base and hardener thoroughly (approx. 2 minutes) by using a hand drill with a paddle. Add filler to the mixture mixing carefully at the same time. Use dry, clean natural or quarz sand as a filler. The amount of mixture depends on the area to be coated and on the pot life of the mixture. Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface, weaken the properties of the screed and risk the success of the application. Cleaning of tools Thinner 1029 or 1031. EU VOC 2004/ 42/EC-limit value VOC 2004/42/EC (cat A/j) 500 g/l (2010) Temafloor 3000: max. VOC < 500 g/l HEALTH AND SAFETY CLASSIFICATION
PRODUCT DATA SHEET 05.08.2011 4 (4) Temafloor 3000 Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj. The above information, based on laboratory tests and practical experience, has been proved valid at the date marked on the product data sheet. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As a manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes. Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com -
PRODUCT DATA SHEET 22.04.2010 1 (2) Temafloor 4000 ESD DESCRIPTION PRODUCT FEATURES RECOMMENDED USES Solvent free Temafloor 4000 ESD grinding screed is prepared by adding conductive sand mixture to Temafloor 401 epoxy varnish mixture. Forms electrically conductive coating when used with Temafloor 310 ESD primer. Meets the requirements for conductive floor coatings according to IEC-EN 61340-5-1. High impact and good chemical resistance. Prevents electrostatic discharge damages and recommended in places where electric discharge is not desirable e.g. in electronic industry, production and storing of explosive materials, place with higher risks of ignition. TECHNICAL DATA Features Colour Range Gloss groups Coverage Withstands heavy wear. Resistance to chemicals is given case by case. Withstands +110ºC dry heat and +60ºC in immersion. Non-slip. The colour of the screed is determined by the sand used. Full-gloss For a flat substrate: 3mm layer: 3 litres ready for use screed / m 2 4mm layer: 4 litres ready for use screed / m 2 Mixing ratio Application method Pot-life (+23 C) Drying time at 23 C and 50% relative air humidity Practical coverage depends on the evenness of the substrate. Temafloor 401 mixture Base 2 parts by volume 008 4002 Hardener 1 part by volume 008 4012 Screed film thickness 3-4mm 1 part by volume Temafloor 401 mixture 4 parts by volume (6 parts by weight) of conductive sand mixture: 30% conductive sand 70% coloured sand By adjustable trowel, serrated trowel, float, levelling trowel and screed box. 20-30 minutes on substrate, 10-15 minutes in the mixing container. Dust dry after 6 hours Light trucking afte 24 hours Recoatable 16-24 hours Fully cured 7 vrk:n kuluttua Solids volume approx. 100%. Density Product code 008 4002 At lower temperature the curing process will last longer. 1.8-2.0kg / l (mixture), depending on the grain size and the amount of sand. Recommended grain size 0.5-1.2mm. Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com
PRODUCT DATA SHEET 22.04.2010 2 (2) Temafloor 4000 ESD APPLICATION DETAILS Application conditions Preparation Priming Diluting Screeding Overcoating Mixing of components Cleaning of tools Thinner 1029. EU VOC 2004/ 42/EC-limit value The relative humidity of the concrete should not exceed 97%. The temperature of the ambient air, surface or coating should not fall below +15ºC during either application or drying. Relative humidity of air should not exceed 80%. New concrete Remove laitance by power grinding, vacuum grit blasting or hydrochloric acid etching. Choose the method best suited for the premises. After grinding remove dust carefully with a vacuum cleaner. Hydrochloric acid etching is carried out with diluted hydrochloric acid (1 part concentrated hydrochloric acid, 4 parts water). Rinse with plenty of water. Dry the floor. Old concrete Remove all grease, oil, chemicals and other impurities by MAALIPESU detergent. Remove old peeling paint layer by grinding, milling or vacuum grit blasting. Choose the method best suited for the premises. Clean out pot-holes removing all loose friable material. Open cracks with e.g. an abrasive tool. Remove loose material and dust. Prime using Temafloor 310 ESD primer thinned 20-30% with Thinner 1029 according to the product data sheet. Scatter conductive sand on the fresh primer coat to ensure the screed adhesion and prevent gliding of the screed. Do not thin Temafloor 4000 ESD grinding screed. Pour the screed mixture onto the floor. If a thin layer is required, apply by an adjustable trowel to the desired screed thickness. Thick layers are applied by a screed box or by a straight-edge and suitable laths to gauge the required thickness. Knead the screeded surface by hands or use a suitable lightweight floating machine. Overcoating can be carried out after 16-24 hours using Temafloor 401 epoxy varnish thinned 20-30% with Thinner 1029. If the surface is not overcoated within 24 hrs, it should be abraded. Pour the varnish mixture onto the floor, spread with a rubber trowel and level with a roller. Mix the correct proportions of base and hardener thoroughly (approx. 2 minutes) by using a hand drill with a paddle, concrete mixer or power mixer. Add conductive sand mixture to the varnish mixture by mixing carefully at the same time. Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface, weaken the properties of the screed and risk the success of the application. VOC 2004/42/EC (cat A/j) 500 g/l (2010) Temafloor 4000 ESD: max. VOC < 500 g/l HEALTH AND SAFETY CLASSIFICATION Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj. The above information, based on laboratory tests and practical experience, has been proved valid at the date marked on the product data sheet. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As a manufacturer we cannot be responsible for any damages caused by using the product against our instructions or for inappropriate purposes. Tikkurila Oyj P.O. Box 53 Kuninkaalantie 1 FI-01301 Vantaa Finland Tel. +358 9 857 71 Fax. +358 9 8577 6900 VAT FI01970674 Business Identity Code 0197067-4 Registered Office Vantaa e-mail: info@tikkurila.com www.tikkurila.com -
Standard System Sheets
Standard System Sheet Prepared Floor (Blasted) Project summary only to be read in conjunction with attached observations and method statement Project : Environment: Internal Aircraft Hangar Approvals: - Date: Prepared By: Preparation Summary - Remove old peeling paint layer by diamond grinding / vacuum grit blasting / mechanical abrasion. Choose the method best suited to the premises and substrate. Concrete must be abraded to form a distinct absorbent key - Clean out pot holes and cavities removing all loose and friable material - Open cracks with an abrasive tool - Remove all loose material and dust - Ensure substrate is dry clean and stable before application of Temafloor P300 Solvent Free Epoxy Coating System Summary No of coats Product Colour DFT Theo Spread Volume Thinner Rate Solids 1 x Primer coat thinned TEMAFLOOR 400 SOLVENT FREE EPOXY CLEAR 100µ 10 m 2 /L 100% 1031 30% CLEAR PRIMER 1 x Primer coat if TEMAFLOOR 400 SOLVENT FREE EPOXY CLEAR 100µ 10 m 2 /L 100% 1031 required thinned 30% CLEAR PRIMER 1 x Full Coat TEMAFLOOR P300 SOLVENT FREE EPOXY COATING TBC 300µ 3 m 2 /L 100% 1031 Notes: Ensure all potholes and cracks are filled with Tikkurila Colofill putty or suitable equivalent Certain finish colours may require two topcoats to ensure opacity. Spread rates are approximate practical but can vary according to actual thicknesses achieved and wastage etc. Ensure coatings are well ventilated during curing and sufficiently cured before overcoating. Drying times are specified in Tikkurila TDS Dry film thicknesses must be in accordance with ISO19840 If an anti slip surface is required 2 coats will be necessary. Broadcast anti slip aggregate into 1 st full coat to required degree of anti slip. When dry brush of surplus and apply finish. When priming a wet look finish must be achieved prior to application of P300 finishing coats (follow advice in priming section of (TDS) TIKKURILA INDUSTRIAL UK VALTTI UNIT B3 SOUTH GYLE CRESCENT LANE EDINBURGH EH12 9EG TEL: +44 (0)131 334 4999 FAX: +44 (0)131 334 3987 EMAIL: enquiries@valtti.co.uk www.valtti.co.uk
Standard System Sheet- Previously Painted Project summary only to be read in conjunction with attached observations and method statement Project : Environment: Internal Approvals: N/A Date: Prepared By: Preparation Summary - Degrease/clean overall using a suitable water soluble detergent (Tikkurila cleaning agent) - Remove old peeling paint layer by grinding, scraping, vacuum grit blasting/mechanical abrasion. Choose the method best suited to the premises and substrate. All remaining sound paint must be abraded to form a distinct key - Clean out pot holes and cavities removing all loose and friable material - Open cracks with an abrasive tool - Remove all loose material and dust - Ensure substrate is dry clean and stable before application of Temafloor P300 Solvent Free Epoxy Coating System Summary No of coats Product Colour DFT Theo Spread Volume Thinner Rate Solids Patch Prime Patch TEMAFLOOR 400 SOLVENT FREE EPOXY CLEAR 100µ 10 m 2 /L 100% 1031 prime all filled and exposed bare/porous areas CLEAR PRIMER 1 x Full Coat TEMAFLOOR P300 SOLVENT FREE EPOXY COATING Grey tbc 300µ 3 m 2 /L 100% 1031 Notes: Ensure all potholes and cracks are filled with Tikkurila Colofill putty or suitable equivalent Certain finish colours may require two topcoats to ensure opacity. Spread rates are approximate practical but can vary according to actual thicknesses achieved and wastage etc. Ensure coatings are well ventilated during curing and sufficiently cured before overcoating. Drying times are specified in Tikkurila TDS Dry film thicknesses must be in accordance with ISO19840 If an anti slip surface is required 2 coats will be necessary. Broadcast anti slip aggregate into 1 st full coat to required degree of anti slip. When dry brush of surplus and apply finish. TIKKURILA INDUSTRIAL UK VALTTI UNIT B3 SOUTH GYLE CRESCENT LANE EDINBURGH EH12 9EG TEL: +44 (0)131 334 4999 FAX: +44 (0)131 334 3987 EMAIL: enquiries@valtti.co.uk www.valtti.co.uk
Case Study Information Project Name Arriva Bus Garage 3 of 8 Project Date 2011 Site Location Liverpool Category New Build Client Arriva Clients Agent - Specifier Tim Haythorthwaite Fabricator - Proj. No - Applicator Quest Industrial Services Ltd Sq Mts (known) 1950m 2 (Estimated) - Tonnes (Known) - (Estimated) - Tikkurila Pers Tim Haythornthwaite Press Release - Substrate New concrete block Surface Prep Dust free autoblasting Product Product Code DFT Colour Temafloor 400 -µ Clear Temafloor P300 300µ M323 (red) M168 (black) Yellow Green TIKKURILA INDUSTRIAL UK VALTTI UNIT B3 SOUTH GYLE CRESCENT LANE EDINBURGH EH12 9EG TEL: +44 (0)131 334 4999 FAX: +44 (0)131 334 3987 EMAIL: enquiries@valtti.co.uk www.valtti.co.uk
Images (2) Case Study Information TIKKURILA INDUSTRIAL UK VALTTI UNIT B3 SOUTH GYLE CRESCENT LANE EDINBURGH EH12 9EG TEL: +44 (0)131 334 4999 FAX: +44 (0)131 334 3987 EMAIL: enquiries@valtti.co.uk www.valtti.co.uk
Case Study Information Project Name RWE N Power Fiddlers Ferry Power Station Project Date July 2012 Site Location Yorkshire Category Client Clients Agent Specifier Tim Haythornthwaite Fabricator Proj. No Applicator Sq Mts (known) 3000 Sq. Mts (Estimated) - Tonnes (Known) (Estimated) - Tikkurila Pers Tim Haythornthwaite Press Release Substrate Surface Prep Blasted Product Product Code DFT Colour Temafloor 400 - Temafloor P300 300µm TIKKURILA INDUSTRIAL UK VALTTI UNIT B3 SOUTH GYLE CRESCENT LANE EDINBURGH EH12 9EG TEL: +44 (0)131 334 4999 FAX: +44 (0)131 334 3987 EMAIL: enquiries@valtti.co.uk