Hot-Rolled Steel Sheets and Coils

Flat Products Hot-Rolled Steel Sheets and Coils http://www.nssmc.com/ 2-6-1 Marunouchi, Chiyoda-ku, Tokyo 1-871 Japan Tel: +81-3-6867-4111 Hot-Rolled Steel Sheets and Coils U1en_2_2168f 212, 216 NIPPON STEEL & SUMITOMO METAL CORPORATION

Preface Utilizing our excellent manufacturing equipment and honored technology, supported by our rich experience and never-ceasing endeavor of development, Nippon Steel & Sumitomo Metal manufactures a wide range of Hot-Rolled Steel Sheets and Coils in accordance with Japanese Industrial Standards (JIS), the standards of other countries, and our own strict standards. Our Hot-Rolled Steel Sheets and Coils are applied to a wide range of uses such as, automobiles, electrical appliances, construction materials, containers, and steel pipes, and receive high acclaim from our customers for its excellent quality. We are committed to meet our customers requirements of quality as well as on-time delivery and offer technical consultations and services for applications of our steel products. We deeply appreciate your continued support and encouragement. Table of Contents Features... 2 Works... 3 Examples of Use... 4 Manufacturing Processes... 6 Manufacturing Equipment... 8 Products... 1 Product Size Ranges... 12 Examples of Standards... 14 Chemical Compositions and Mechanical Properties.. 14 Dimensional Tolerances... 22 Notice: While every effort has been made to ensure the accuracy of the information contained within this publication, the use of the information is at the reader s risk and no warranty is implied or expressed by Nippon Steel & Sumitomo Metal Corporation with respect to the use of the information contained herein. The information in this publication is subject to change or modification without notice. Please contact the Nippon Steel & Sumitomo Metal Corporation office for the latest information. Please refrain from unauthorized reproduction or copying of the contents of this publication. The names of our products and services shown in this publication are trademarks or registered trademarks of Nippon Steel & Sumitomo Metal Corporation, affiliated companies, or third parties granting rights to Nippon Steel & Sumitomo Metal Corporation or affiliated companies. Other productor service names shown may be trademarks or registered trademarks of their respective owners. Reference Tables... 24 Information on Usage... 2 Packaging and Labeling... 26 Ordering Information... 28 1

Features ❶ Wide Range of Product Selection Hot-Rolled Steel Sheets and Coils meeting a variety of standards ranging from mild steels to high-tensile strength steels are available. Variable sizes of cut sheets, coils, and various surface finishes such as black finish, pickled finish and shot-blasted finish can be selected in accordance with your needs. ❷ Consistent Quality Products of consistent quality are manufactured under strict quality control, utilizing excellent equipment and techniques, and drawing on our wealth of experience. ❸ Wide Variety of Sizes Size are available from 1.2 mm to 2.4 mm in thickness and from 6 mm to 218 mm in width. ❹ Technical Service for Every Need Consultation services regarding quality characteristics, applications, and processing methods of our products, and more are thoroughly provided by the technical service divisions of the headquarters and local offices. Works Yawata Works Hirohata Works Nagoya Works Kashima Works Kimitsu Works Oita Works 2 3

Examples of Use Containers Steel Racks Deck Plates Gas Cylinders Truck Frames 4 Wheels

Manufacturing Processes Limestone Iron Ore Sintering Plant Pig Iron Converter Vacuum Degassing Hot-Rolled Coil Coal Coking Plant Blast Furnace Continuous Casting Cooling Continuous Reheating Furnace Scale Breaker Finish Rolling Coiling Skin Pass Mill Pickled Coil Continuous Pickling Line Hot-Rolled Slit Coil Pickled Slit Coil Slitter Shearing Line Hot-Rolled Slit Sheet Shot Descalling Shot Blast Coil 6 7

Manufacturing Equipment Continuous Casting from the Blast Furnace Pig iron is formed by a chemical reaction of sinter and coke in the blast furnace. Then, in order to meet our customers demand for viscosity and robustness, the pig iron goes through four processes: hot metal pretreatment, converter process, secondary refining process, and continuous casting to remove excess carbons and impurities for chemical refinement in order to produce an intermediate material known as slab. Converter Hot-Rolling Hot-Rolling Hot-rolled coil is made by continuously rolling the slab, after heating the slab in the reheating furnace, by the roughing mill and finishing mill, and coiled for a easier transportation. At the hot-rolling process, strictly controlling the temperature and the roll surface is essential in producing a high productive Hot-Rolled Steel Sheets and Coils, free from surface defects and internal defects. All production line processes, starting from feeding to the reheating furnace to the completion of coiling, are controlled by a computerized system. Pickling Continuous Casting Pickling The hot-rolled coil passes through the pickling line, where surface scales (iron oxide layer) are removed from the surface of the coil to give an (attractive) surface finish to the steel. In the pickling line, surface scales are removed with hydrochloric acid, and the coil is completely washed and dried before antirust oils are applied. 8 9

Products JIS (Japanese Industrial Standards) Types Standards T.S. Types Standards T.S. Types Standards Features Examples of Use JIS G 311 Hot-Rolled Steel Sheets and Coils for General Structures SS33 33 43 SS4 4 1 SS49 49 61 SS4 4 SM4A 4 1 JIS G 312 Corrosion Resistant Rolled Steel Sheets and Coils JIS G 3116 Hot-Rolled Steel Sheets and Coils for Gas Cylinders SPA-H SG2 SG29 SG32 49 4 44 49 High-Strength Hot-Rolled Steel Sheets and Coils with Automobile Formability Dual Phase High-Strength Hot- Rolled Steel Sheets and Coils with Automobile Formability NSHA49 NSHA4 NSHA9 NSHA69 NSHA78 NSHA98 NSHA4D NSHA9D NSHA69D NSHA78D They can be used for a wide range of applications, from general forming to drawing. They are well suited for drawing because of their low yield ratio. They have also excellent fatigue strength. Automobile members, wheel rims Wheel discs SM4B 4 1 SG36 4 High-Hole Expanding High-Strength Hot-Rolled Steel Sheets and Coils with Automobile Formability NSHA37B, NSHA4B NSHA4B, NSHA9B NSHA44B, NSHA69B NSHA49B, NSHA78B They can be used for a wide range of applications, from general forming to drawing and have superior burring property (1.8 d/ d). Suspensions, links, arms SM4C 4 1 SM49A 49 61 SM49B 49 61 JIS G 3131 Hot-Rolled Mild Steel Sheets and Coils SPHC SPHD SPHE 27 27 27 High-Retained Austenite High- Strength Hot-Rolled Steel Sheets and Coils NSHA9T NSHA69T NSHA78T Exceeding the limits of conventional High-Strength Hot-Rolled Steel Sheets for automobiles, they have strength and formability comparable to highstrength cold-rolled steel sheets. Automobile structural components, suspensions, components with high performance formability of any shape JIS G 316 Hot-Rolled Steel Sheets and Coils for Welded Structures SM49C 49 61 SPHF 27 Flooring Sheets and Coils NFP NFP4 With maximum anti-slip properties, they drain quickly, and are thin-gauge and light in weight, so they can be used economically for various purposes. Steps of a car body, passageways, steps, and panels of buildings and structures SM49YA 49 61 SPHT1 27 SM49YB 49 61 SM2B 2 64 JIS G 3132 Hot-Rolled Carbon Steel Sheets and Coils for Pipes and Tubes SPHT2 SPHT3 34 41 Longitudinally Striped Steel Sheets and Coils NFPA1 NFPA2 NFPB1 They can be used as highly economical strength components resistant against bending and as exterior components for their fine design. Steps of a car body, factory floors, steel furniture, warehouse racks, steps. SM2C 2 64 SPHT4 49 Atmospheric Corrosion- Resistant Steel Sheets and Coils NAW4 NAW49 COR-TEN O They have high weatherability and can be used unpainted. They also have good wear resistance. Pillars of marine containers, rail vehicle bodies, exterior construction members SM7 7 72 SAPH31 31 Weldable High-Strength Steel Sheets and Coils WEL-TEN TM 4 WEL-TEN 9RE WEL-TEN 69RE WEL-TEN 78RE WEL-TEN 9RE They are low-carbon and low-alloy steel sheets with high strength and superior notch toughness. Also they have high weldability and demonstrate sufficient joint performance. Industrial equipment, construction machinery JIS G 3113 Hot-Rolled Steel Sheets and Coils for Automobile Structural Uses SAPH37 SAPH4 37 4 Sulfur Dew-Point Corrosion- Resistant Steel Sheets and Coils S-TEN TM 1 S-TEN 2 Developed as steels resistant against sulfuricacid dew-point corrosion, they are suitable for use in sulfuric-acid dew-point corroding environments where ordinary and stainless steels cannot normally be used. Casing and ducts of dust collectors, internal cylinders SAPH44 44 NOTE: COR-TEN is a registered trademark of United States Steel Corporation used under license by Nippon Steel & Sumitomo Metal Corporation. 1 11

Product Size Ranges As the available range of production varies depending on standards and applications, please consult us. Contact Nippon Steel & Sumitomo Metal if your choice is not available, and we will do what we can to meet your needs. 1. Hot-Rolled Coil (mill edge) 2. Pickled Coil Width (mm) 6 8 1, 1,2 1,4 1,6 1,8 2, 2,2 (mm) 2 24 (6, 2.4) (218, 2.4) Width (mm) 6 8 1, 1,2 1,4 1,6 1,8 2, 2,2 (mm) 11 1 23 9 (6, 9) (121, 9) 22 8 21 7 (118, 7) (17, 7) 2 (16, 2) (218, 2) 6 (6, 6) 19 (64, 19) 18 4 (187, 4.) (21, 4.) 17 16 1 (92, 16) (218, 17) 3 2 1 (6, 1.4) (6, 1.2) (124, 1.8) (169, 1.6) (184, 3.2) (187, 2) (213, 2.7) 14 13 12 Remarks: 1. Contact Nippon Steel & Sumitomo Metal about the varieties of steel strip (slit coil) dimensions available. 2. Contact Nippon Steel & Sumitomo Metal about the varieties of steel plates (cut sheets) available. 11 1 27 N/mm 2 class 9 8 7 6 (21, 7) 4 N/mm 2 class 49 N/mm 2 class 9 N/mm 2 class 4 (18, 4) 3 2 (6, 1.4) (12, 1.8) (188, 2) (218, 2.7) 1 (6, 1.2) 12 13

Examples of Standards Chemical Compositions and Mechanical Properties JIS G 3131 Hot-Rolled Mild Steel Sheets and Coils C Mn P S 1.2 t < 1.6 1.6 t < 2. 2. t < 2. Elongation (%) 2. t < 3.2 3.2 t < 4. 4. t Bending Angle Bending Test t < 3.2 Inner Diameter 3.2 t SPHC.12.6.4.3 27 27 29 29 29 31 31 18 Close overlap.t SPHD.1.4.3.3 27 3 32 33 3 37 39 No. rolling SPHE.8.4.3.3 27 32 34 3 37 39 41 No.3 rolling SPHF.8.3.2.2 27 37 38 39 39 4 42 JIS G 3132 Hot-Rolled Carbon Steel Sheets and Coils for Pipes and Tubes Remarks: 1. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 2. We will carry out a bending test at the customer s request. C Si Mn P S 1.2 t < 1.6 1.6 t < 2. 3. t < 6. Elongation (%) 6. t 13 Bending Angle t 3. Bending Test Inner Diameter 3. < t 13 SPHT 1.1.3 *..4.4 27 3 32 3 37 18 Close overlap.t SPHT 2.18.3.6.4.4 34 2 27 3 32 No. rolling 18 1.t 1.t SPHT 3.2.3.3.9.4.4 41 2 22 2 27 18 1.t 2.t No.3 rolling SPHT 4.3.3.3 1..4.4 49 1 18 2 22 18 1.t 2.t JIS G 311 Hot-Rolled Steel Sheets and Coils for General Structures C Mn P S Yield Point or Yield Strength t 16 SS33.. 2 33 43 Bending Test Elongation Inner Diameter Bending Angle Dimensions of Rolled Steel (mm) Elongation (%) of Rolled Steel and Coil t No. 26 of Rolled Steel and Coil < t 16 No.1A 21 Remarks: 1. *When agreed upon between the concerned parties, Si content may be specified to.4% or less. 2. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 3. We will carry out a bending test at the customer s request. 18.t No.1 SS4.. 24 4 1 SS49.. 28 49 61 SS4.3 1.6.4.4 4 4 of Rolled Steel and Coil t No. 21 of Rolled Steel and Coil < t 16 No.1A 17 of Rolled Steel and Coil t No. 19 of Rolled Steel and Coil < t 16 No.1A 1 of Rolled Steel and Coil t No. 16 of Rolled Steel and Coil < t 16 No.1A 13 18 1.t No.1 18 2.t No.1 18 2.t No.1 Remarks: 1. Alloying elements other than described above can be added to SS4 according to requirements. 2. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 3. We will carry out a bending test at the customer s request. 14 1

Examples of Standards Chemical Compositions and Mechanical Properties JIS G 316 Hot-Rolled Steel Sheets and Coils for Welded Structures Yield Point or Yield Strength Elongation (%) C Si Mn P S Steel Sheet, 16 mm max. Steel Sheet Elongation (%) SM4A.23 2.C.3.3 of Rolled Steel and Coil t No. 23 SM4B.2.3.6 1..3.3 24 4 1 of Rolled Steel and Coil < t 16 No.1A 18 SM4C.18.3.6 1..3.3 SM49A.2. 1.6.3.3 SM49B.18. 1.6.3.3 SM49C.18. 1.6.3.3 32 49 61 of Rolled Steel and Coil t No. 22 of Rolled Steel and Coil < t 16 No.1A 17 SM49YA.2. 1.6.3.3 of Rolled Steel and Coil t No. 19 36 49 61 SM49YB.2. 1.6.3.3 of Rolled Steel and Coil < t 16 No.1A 1 SM2B.2. 1.6.3.3 of Rolled Steel and Coil t No. 19 36 2 64 SM2C.2. 1.6.3.3 of Rolled Steel and Coil < t 16 No.1A 1 SM7.18. 1.7.3.3 46 7 72 of Rolled Steel and Coil t 16 No. 19 Remarks: 1. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 2. Alloying elements other than the above-mentioned ones can be added according to requirements. 3. Impact test is not performed on steel plates with a thickness of 12 mm or less. JIS G 3113 Hot-Rolled Steel Sheets and Coils for Automobile Structural Uses Bending Test P S t < 6 Yield Point 6 t < 8 8 t 14 1.6 t < 2. 2. t < 2. Elongation (%), Rolling Direction No. 2. t < 3.1 3.1 t < 4. 4. t < 6.3 6.3 t 14. Bending Angle t < 2. Inner Diameter 2. t SAPH31.4.4 (18 ) (18 ) (17 ) 31 33 34 36 38 4 41 18 Close overlap 1.t SAPH37.4.4 22 22 21 37 32 33 3 36 37 38 18.t 1.t SAPH4.4.4 2 23 23 4 31 32 34 3 36 37 18 1.t 1.t Transverse to No.3 rolling SAPH44.4.4 3 29 27 44 29 3 32 33 34 3 18 1.t 1.t High-Strength Hot-Rolled Steel Sheets and Coils with Automobile Formability NSHA49 C Si Mn P S 1. Yield Point 1.2 t < 1.6 1.6 t < 2. 2. t < 2. Elongation (%) 2. t < 3.2 3.2 t < 4. 4. t < 6.3 6.3 t 34 49 24 24 24 24 26 27 27 Remarks: 1. Values in parentheses are reference values. 2. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 3. We will carry out a bending test at the customer s request. Bending Angle Bending Test Inner Diameter 1.6 t < 3.2 3.2 t.t.t NSHA4 1.6 37 4 21 21 22 23 24 24 24 1.t 1.t NSHA9 1.7 44 9 19 19 2 21 21 22 22 Transverse to 1.t 1.t.18..3.1 JIS No. rolling 18 NSHA69 2. 69 16 17 17 17 17 18 2.t 2.t Transverse to JIS No.3 rolling NSHA78 2.2 68 78 13 14 14 1 1 2.t 2.t NSHA98 2. 8 98 1 1 11 11 Remarks: 1. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 2. Alloying elements other than the above-mentioned ones can be added according to requirements. 16 17

Examples of Standards Chemical Compositions and Mechanical Properties Dual Phase High-Strength Hot-Rolled Steel Sheets and Coils with Automobile Formability C Si Mn P S Yield Point t < 2. 2. t < 2. 2. t < 3.2 Elongation (%) 3.2 t < 4. NSHA4D.12 1. 1.8.3.2 29 4 2 26 27 28 28 NSHA9D.12 1. 2..3.2 32 9 24 2 26 27 27 NSHA69D.14 1. 2..3.2 3 69 19 2 21 22 22 NSHA78D.1 1. 3..3.2 38 78 16 17 18 19 27 4. t 6. Transverse to JIS No. rolling Remarks: 1. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 2. Alloying elements other than the abovementioned ones can be added according to requirements. High-Hole Expanding High-Strength Hot-Rolled Steel Sheets and Coils with Automobile Formability High-Retained Austenite High-Strength Hot-Rolled Steel Sheets and Coils C Si Mn P S C Si Mn P S Yield Point Yield Point 1.6 t < 2. 1.4 t < 2. 2. t < 2. Elongation (%) 2. t < 2. 2. t < 3.2 NSHA37B.1. 1..2.1 22 37 32 33 3 36 37 1 NSHA4B.1. 1..2.1 2 4 31 32 34 3 36 JIS No. rolling 1 NSHA44B.1.8 1.9.2.1 3 44 29 3 32 33 34 1 Elongation (%) 2. t < 3.2 3.2 t < 4. 3.2 t < 4. NSHA49B.16.8 2..2.1 33 49 26 26 26 28 28 NSHA4B.16 1. 2..2.1 3 4 24 24 24 26 26 Transverse to 8 NSHA9B.16 1. 2.2.2.1 44 9 21 21 21 23 23 JIS No. rolling 7 NSHA69B.16 1. 2.2.2.1 69 17 17 18 18 6 NSHA78B.16 1. 2.2.2.1 67 78 14 14 1 1 6 4. t 6. 4. t 6. NSHA9T.21 2.2 1.8.2.1 39 9 2 26 27 28 28 Transverse NSHA69T.23 2.2 2..2.1 44 69 22 23 24 2 26 to JIS No. rolling NSHA78T.2 2.2 2.2.2.1 49 78 2 21 22 23 24 Hole Expanding Test Hole Expansion Rate (%) 9 Remarks: 1. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 2. Alloying elements other than the abovementioned ones can be added according to requirements. Remarks: 1. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 2. Alloying elements other than the abovementioned ones can be added according to requirements. Flooring Sheets and Coils Bending Test Elongation (%) Yield Point (N/mm 2 Bending Angle Inner Diameter Test Specimen Rolling Direction ) Test Specimen Rolling Direction P S t.. < t 16. NFP (27 ) NFP4.. 24 4 1 21 17 t. JIS No. t. JIS No.3 18 1.t. < t 16. JIS No.1A. < t 16. JIS No.1 Remarks: 1. Values in parentheses are reference values. 2. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 18 19

Examples of Standards Chemical Compositions and Mechanical Properties Atmospheric Corrosion-Resistant Steel Sheets and Coils Elongation Yield Point Inner Diameter (N/mm 2 Bending Angle ) Elongation Test Specimen (mm) C Si Mn P S Cu Cr Ni Ti (mm) (%) Rolling Direction Bending Test Test Specimen Rolling Direction NAW4.1..2.4.4 24 4 1 NAW49.12.1.3.9.6.12.3.2..1 39 49 t. 21 JIS No. t. 18 1.t JIS No.3. < t 17 JIS No.1A. < t 18 1.t JIS No.1 t < 6. 22 JIS No. t < 6. 18 1.t JIS No.3 6. t 23 JIS No. 6. t 18 1.t JIS No.1 t. 22 JIS No. t. 18 1.t JIS No.3 COR-TEN O.12.2.7.2..7.1.3.2..3 1.2.6 3 49. < t 16 18 JIS No. 16 < t 2 21 JIS No.1A. < t 18 1.t JIS No.1 Weldable High-Strength Steel Sheets and Coils Remarks: 1. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 2. We will carry out a bending test at the customer s request. Bending Test Impact Test Tensile Elongation Yield Point Inner Diameter Strength Elongation Test Specimen Bending Angle Transverse to the C Si Mn P S Ti Ceq. (mm) (%) Rolling Direction t 16 2 JIS No. Test Specimen Transverse to the Rolling Direction (mm) 2 mm V-notch Test Specimen Test Temperature Absorbed Energy (average of the three) (J) WEL-TEN 4.2. 1.7.3.3.4 3 4 WEL-TEN 9RE.12. 2..3.2.1.4 4 9 71 WEL-TEN 69RE.14. 2..3.2.2. 9 69 83 16 < t 2 28 JIS No. 2 < t 23 JIS No.4 t 16 2 JIS No. 16 < t 2 28 JIS No. 2 < t 2 JIS No.4 t 16 17 JIS No. 16 < t 2 JIS No. 18 1.t JIS No.1 12 < t C 47 18 1.t JIS No.1 12 < t C 47 18 1.t JIS No.1 12 < t 1 C 47 WEL-TEN 78RE.16. 2..2.3.3. 62 78 93 t 9 1 JIS No. 18 1.t JIS No.1 Sulfur Dew-Point Corrosion-Resistant Steel Sheets and Coils Remarks: 1. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 2. Ceq. = C + Mn/6 + Si/24 + Ni/4 + Cr/ + Mo/4 + V/14 3. We will carry out a bending test at the customer s request. Elongation Yield Point Inner Diameter (mm) (N/mm 2 Bending Angle ) Elongation Test Specimen C Si Mn P S Cu Cr Ti Sb (%) Rolling Direction Bending Test Test Specimen Transverse to the Rolling Direction S-TEN 1.14. 1.6.2.2.2..1 t 16 24 4 4 23 JIS No. 18 1.t JIS No.1 S-TEN 2.14.1. 1.6.3.3.2.. 1..1 t 16 32 44 4 22 JIS No. 18 1.t JIS No.1 Longitudinally Stripped Steel Sheets and Coils (There are no specifications of chemical components or mechanical properties. Normal tensile strength is 27 N/mm 2 or more.) Remarks: 1. Mechanical test values do not apply to abnormal parts at both ends of steel strip (coils). 2. We will carry out a bending test at the customer s request. 3. S-TEN 1: Mn 2.[C] 2 21

Examples of Standards Dimensional Tolerances JIS G 3193 Shape, Dimensions, Weight, and Tolerance of Hot-Rolled Steel Sheets and Coils. Tolerance of Nippon Steel & Sumitomo Metal Standards Flooring Sheets and Coils (NFP series), Longitudinally Stripped Steel Sheets and Coils (NFPA series), Atmospheric Corrosion- Resistant Steel Sheets and Coils (NAW series), Weldable High-Strength Steel Sheets and Coils (WEL-TEN series), Sulfur Dew-Point Corrosion-Resistant Steel Sheets and Coils (S-TEN series). Tolerance (unit: mm) Width W < 1,6 1,6 W < 2, 2, W < 2, t < 1.2 ±.16 1.2 t < 1.6 ±.18 1.6 t < 2. ±.19 ±.23 2. t < 2. ±.2 ±.2 2. t < 3.1 ±.22 ±.29 ±.29 3.1 t < 4. ±.24 ±.34 ±.34 4. t <. ±.4 ±. ±.. t < 6.3 ±. ±.6 ±.6 6.3 t < 1. ±. ±.6 ±.6 1. t < 16. ±. ±.6 ±.6 16. t < 2. ±.6 ±.7 ±.7 Width Tolerance Width W < 16 16 W < 2 2 W < 4 4 W < 63 63 W < 1, 1, W < 1,2 1,2 W < 1,6 1,6 W t < 3.1 3.1 t < 6. 6. t < 2. 2. t t < 3.1 3.1 t < 6. 6. t < 2. 2. t t < 3.1 3.1 t < 6. 6. t < 2. 2. t t < 3.1 3.1 t < 6. 6. t < 2. 2. t t < 3.1 3.1 t < 6. 6. t < 2. 2. t t < 3.1 3.1 t < 6. 6. t < 2. 2. t t < 3.1 3.1 t < 6. 6. t < 2. 2. t t < 3.1 3.1 t < 6. 6. t < 2. 2. t As-Rolled Steel Plate + Not specified + Not specified + Not specified + Not specified + Not specified + Not specified Mill Edge Coil, or Sheet Cut from Coil { { { { ±2 ±2 ± ±2 + 2 + 3 + 3 + 4 Tolerance A Cut Edge B + + 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 2 2 Remarks: 1. As required, the above-mentioned tolerance of the (+) side or (-) side can be limited. However, in this case, the total tolerance is equal to the tolerance in the table on the left. 2. The measuring positions for steel coil thickness are as follows: in the case of a mill edged steel coil or sheet, an arbitrary point 2 mm or more from the edge is selected; for a cut edged steel plate or sheet cut from coil, an arbitrary point of 1 mm or more from the edge is selected. And for as-rolled steel plate, a measuring point inside the expected cutting line is arbitrarily selected. In the case of a cut edged steel plate, a point 1 mm or more from the edge is arbitrarily selected. NOTE: JIS G 3193 is applied to JIS G 311 (or SS 33) and to JIS G 316 (SM4A). 2. 3. 4. 2. 3. 4. 2. 3. 4. 3. 3.. 4. 4. 6. 4. 4. 6. 4. 4. 6. 4. 4. 6. (unit: mm) C ±.3 ±. ±.4 ±. ±. ±. ±. ±. Remarks: The tolerance of a mill edged strip, or sheet cut from coil, with a width less than 4 mm, is limited by adjusting at the (-) side to. In this case, the tolerance of the (+) side becomes twice the value. NOTE: Tolerance A, B, and C of the width of the cutting edge are determined by the following methods. A: normal cutting method; B: recutting or precise cutting method; C: slit method. JIS G 3113 (SAPH), 3116 (SG2, SG29), 3131 (SPHC, SPHD, SPHE, SPHF), 3132 (SPHT1, SPHT2, SPHT3) TS49N/mm 2 under High-Hole Expanding Formability Hot-Rolled Steel Sheets and Coils (NSHA37B 4B 44B) Tolerance (unit: mm) Width W < 1,2 1,2 W < 1, 1, W < 1,8 1,8 W t < 1.6 ±.14 ±.1 ±.16 1.6 t < 2. ±.16 ±.17 ±.18 ±.21 2. t < 2. ±.17 ±.19 ±.21 ±.2 2. t < 3.1 ±.19 ±.21 ±.24 ±.26 3.1 t < 4. ±.21 ±.23 ±.26 ±.27 4. t <. ±.24 ±.26 ±.28 ±.29. t < 6. ±.26 ±.28 ±.29 ±.31 6. t < 8. ±.29 ±.3 ±.31 ±.3 8. t < 1. ±.32 ±.33 ±.34 ±.4 1. t < 12. ±.3 ±.36 ±.37 ±.4 12. t 14. ±.38 ±.39 ±.4 ±. JIS G 3116 (SG32, SG36), 3132 (SPHT4), 3134 (SPFH) TS49N/mm 2 and over Dual Phase High-Strength Hot-Rolled Steel Sheets and Coils with Formability (NSHA D), High-Hole Expanding Formability Hot-Rolled Steel Sheets and Coils (NSHA49B 4B 9B 69B 78B), High-Retained Austenite, High-Strength Hot-Rolled Steel Sheets and Coils (NSHA T) Tolerance (unit: mm) Width W < 1,2 1,2 W < 1, 1, W < 1,8 1,8 W t < 1.6 ±.14 ±.1 ±.16 1.6 t < 2. ±.16 ±.19 ±.2 2. t < 2. ±.18 ±.22 ±.23 ±.2 2. t < 3.1 ±.2 ±.24 ±.26 ±.29 3.1 t < 4. ±.23 ±.26 ±.28 ±.3 4. t <. ±.26 ±.29 ±.31 ±.32. t < 6. ±.29 ±.31 ±.32 ±.34 6. t < 8. ±.32 ±.33 ±.34 ±.38 8. t < 1. ±.3 ±.36 ±.37 ±.44 1. t < 12. ±.38 ±.4 ±.41 ±.49 - High-Strength Hot-Rolled Steel Sheets and Coils with Formability (NSHA) Tolerance (unit: mm) Width W < 1,2 1,2 W < 1, 1, W < 1,8 1,8 W 2,3 1.2 t < 1.6 ±.16 ±.19 1.6 t < 2. ±.16 ±.19 ±.2 2. t < 2. ±.18 ±.22 ±.23 ±.2 2. t < 3.1 ±.2 ±.24 ±.26 ±.29 3.1 t < 4. ±.23 ±.26 ±.28 ±.3 4. t <. ±.26 ±.29 ±.31 ±.32. t < 6. ±.29 ±.31 ±.32 ±.34 6. t < 8. ±.32 ±.33 ±.34 ±.38 8. t < 1. ±.3 ±.36 ±.37 ±.44 1. t 12. ±.38 ±.4 ±.41 ±.49 Remarks: 1. measurement points conform to the standards. 2. This method does not apply to abnormal parts at both ends of a steel coil. 3. The application of thickness and width is provided in the appropriate standards. NOTE: Width tolerance refers to JIS G 3193. Remarks: 1. measurement points conform to the standards. 2. This method does not apply to abnormal parts at both ends of a steel coil. 3. The application of thickness and width is provided in the appropriate standards. NOTE: Width tolerance refers to JIS G 3193. Remarks: 1. measurement points conform to the standards. 2. This method does not apply to abnormal parts at both ends of a steel coil. 3. The application of thickness and width is provided in the appropriate standards. NOTE: Width tolerance refers to JIS G 3193. 22 23

Reference Tables Information on Usage 1. Standard Size and Weight for Hot-Rolled Steel Sheets (Unit: kg) Width x length mm 1.2 1.6 1.8 2 2.3 2.6 2.9 3 3.2 3. 4 4.. 6 7 8 9 1 11 12 13 14 1 16 17 18 19 2. Calculation Chart Example for Coil Width, Inner Diameter, Outer Diameter, and Mass Inner Diameter of Coil: 3" (762 mm) Abscissa A to Ordinate A' Abscissa B to Ordinate B' mm 914 1829 1219 2438 1219 348 1219 4877 1219 696 124 348 124 696 124 9144 124 12192 1829 696 1829 9144 1829 12192 ft 36 48 41 416 42 1 2 3 4 62 63 64 1.8 21 37.3 46.7 74.7 93.3 23.6 42 2. 84 1 26.3 46.7 8.3 93.3 117 3.2 3.7 67.1 17 134 83.9 168 22 336 34.1 6.7 7.8 121 12 94.8 19 28 379 38.1 67.6 84.6 13 169 16 211 317 423 39.4 7 87. 14 17 19 219 328 438 42 74.7 93.3 149 187 117 233 3 467 28 42 6 4.9 81.7 12 163 24 128 2 383 11 36 49 613 2. 93.3 117 187 233 146 292 438 83 3 2 7 9.1 1 131 21 262 164 328 492 66 394 91 788 6.6 117 146 233 292 182 36 47 729 438 66 87 72.2 128 16 27 321 21 41 62 82 481 722 963 78.8 14 17 28 3 219 438 67 87 2 788 1 91.9 163 24 327 48 2 1 766 121 613 919 122 1 187 233 373 467 292 83 87 1167 7 1 14 118 21 263 42 2 328 66 98 1313 788 1181 17 131 233 292 467 83 36 729 194 149 87 1313 171 144 27 321 13 642 41 82 124 164 963 1444 1926 18 28 3 6 7 438 87 1313 17 1 17 211 171 33 379 66 78 474 948 1422 189 1137 17 227 184 327 48 63 817 1 121 132 242 122 1838 241 197 3 438 7 87 47 194 1642 2189 1313 197 2627 21 373 467 747 933 83 1167 171 2334 14 21 281 223 396 496 793 991 62 1239 186 2479 1487 223 297 236 42 2 84 1 66 1313 197 262 17 2363 311 249 443 4 887 119 693 1386 28 2772 1664 249 3327 W=π/4ω7.8.97(D 2-762 2 ) W : Coil Mass (M/T) ω : Coil Width (mm).97 : Coil Occupying Area Ratio D : Outer Diameter of Coil (mm) Coil Mass (M/T) A B 4 3 2 1 2 2 1 1 Coil Mass (M/T) for Coil Width of 1, mm 1, 1, B 22.9 2.4 18.1 1.9 13.7 11.8 1. Outer Diameter of Coil (mm) 2,1 2, 1,9 1,8 1,7 1,6 1, 1,4 1,3 1,2 8.2 1,1 6.6.1 1, 3.7 2. Coil Width (mm) 914 1,219 1,24 1 2 3 A Hot-Rolled Steel Sheets and Coils are produced in a wide range of grades, each having its own unique characteristics. Selection of the right grade, therefore, is essential for the most economical production of high-quality end products. Nippon Steel & Sumitomo Metal can help customers choose the grade best suited for each application. We are also ready to cooperate with customers by offering optimal technical and production support. 1. Plating Finish Hot-rolled sheets (pickled) are coated with oil for protection against rusting. The lubricating oil used in the forming process may also remain on the surface. All traces of such oil and impurities present on the surface must be removed before beginning the plating operations. Degreasing can be achieved by various methods, including those using emulsions, alkali cleaners, etc. Of these, alkali cleaning is most widely employed because of its economy and ease of handling. The most commonly used alkali cleaners include caustic soda, carbonic soda and sodium silicate. Time, temperature, and agitation are the determining factors in degreasing. A surfactant added to the solution usually improves the degreasing effectiveness. Types of steel that contain a sizable amount of silicon can cause defective plating. Please contact us as we have steels that are compatible with plating. 2. Antirust In order to provide maximum protection against rusting and at the same time to facilitate degreasing, hot-rolled sheets are lightly and uniformly treated with an oil that is low in viscosity and easy to remove but still provides superior protection against rusting. Since the sheets are only lightly oiled, they may rust if left exposed for an unreasonably long time after unpacking. Unpacked sheets, therefore, should be used without undue delay. When production conditions make it necessary to keep the unpacked or fabricated sheets exposed for a certain period of time before painting or plating, the following precautions should be taken. a. Since humidity of or over 7 percent usually accelerates the formation of rust, sheets should be kept in an environment with less than 6 percent humidity. b. Air pollution also affects rusting. Hygroscopic substances such as hydrochloric acid gas, ammonium chloride gas and seawater salt particles accelerate rust even when humidity is 6 percent or less or temperatures are above the dew point. c. Dust and stains present on the surface tend to break the protective oil film, produce local galvanic activity with the base metal, and cause rust. 3. Welding Manufacture of satisfactory end products heavily depends upon the selection of proper welding methods and welder skills. Steel sheets may be welded by one of the following methods. The proper method should be determined on the basis of the required appearance and strength of the end products as well as economic considerations. Gas Welding For oxyacetylene welding, the highest possible grade of acetylene should be used. For this method, JIS Specification Z 321 (Gas Welding Rods for Mild Steel) rods are recommended. Submerged-Arc Welding Of the electrodes produced to JIS Specification Z 3211 (Covered Electrodes for Mild Steel), high oxygenation titania or lime titania types are recommended because of their capacity of producing excellent bead appearance and penetration. Resistance Welding a. Adequate weld strength cannot be obtained if the welded joint is not in the nugget form. b. Seam welding Seam welding may be considered a variation of continuous spot welding. Good seam welds are obtained by increasing the electrical current to 1. to 2. times and the pressure to 1.2 to 1.6 times to those of a spot welding. 4. Coils Figure (a) Figure (b) 1 D The use of coils generally has more advantage than the use of steel sheets, as means of improving yield ratio and automating line production. Coil is the material from which sheet is cut, and possesses characteristics which differs from those of a sheet. Thus effective use of coil improves productivity. Use of Coil Materials Coils may contain defective portions attributable to surface imperfections, and thus it is necessary to conduct inspection, selection and rectification. Off-gauge portions at both edges of coils are removed as a rule, but off-gauge portions at welds and their vicinities may be included, for which due attention should be paid. The material quality of coil is not different from that of sheet. d L L 24 2

Packaging and Labeling Our products are shipped bundled and packaged to prevent any possible damages possibly caused by ordinary handling practices or storage conditions prior to actual use. As the products have packaging labels affixed describing the shipped content, please see the affixed label to confirm the product after receipt. 1. Package Label Information 2. Package Label Sample Item Product Name JIS Certification Mark Standards Description Describes a specified product name. JIS is marked on the label of products authorized to designate the JIS certification mark. Code of Standards Name, Standards Number, and Standards Code. HOT ROLLED STEEL SHEETS (Pickled) SPECIFICATION SAPH44 SIZE 3.6 1 C NET MASS (THEO) 4,44KG INSPECTION NO. COIL NO. STEEL MAKING NO. PW14731 L8833-11 TP779 Dimensions The ordered size (thickness width length) is marked. For coil, "C" is marked in place of length. WORKS Net Mass Sheets The actual net or calculated mass is marked in accordance with contract terms and conditions. The actual number of sheets contained. 3. Packaging Sample Coils Marked only if two or more hoops are bundled. <As-Rolled Coil> <Pickled Coil> Inspection Number Coil Number Marked with the unit inspection number for each shipped product. Marked with the production lot unit coil number. Product End Board Outer Lateral Hoop Inner Board Outer Longitudinal Hoop Outer Packaging Paper Steel Making Number User Name Maker's Name Works Marked with the production lot unit steel making number. User's name. Nippon Steel & Sumitomo Metal Corporation (Location Name) Works Package Label Longitudinal Hoop Lateral Hoop Inner Edge Protection Package Label Product Outer Edge Protection Outer Board Inner Lateral Hoop (Inner Binding) Inner Longitudinal Hoop (Inner Binding) 26 27

Ordering Information When you order, please check the following items according to the intended use. Specifications Hot-Rolled Steel Sheets and Coils are produced in a wide range of grades satisfying both JIS and Nippon Steel & Sumitomo Metal specifications. Select the most suitable specifications by intended use, degree of fabrication, method of fabrication, and other factors. Inquire if any questions arise. If you have any questions, please contact Nippon Steel & Sumitomo Metal. Dimensions varies in increments of.1 mm as a rule. This may be reduced to increments of. mm in special cases. Width and length may be specified at increments of 1 mm. Packaging Mass Specify the packaging mass based on unloading capacity and working conditions. Cut sheets: Normally, 2 tons or more are standard. Coils: Normally available from to 2 tons. Specify the maximum weight (and the minimum weight if necessary). Coil Inside/Outside Diameters For coils, the inside diameters of 762 mm (3 inches) or 61 mm (24 inches) are standard. Specify the maximum outside diameter acceptable, if necessary. Surface Finish Specify finish: black finish (as-rolled), pickled finish, or shot blasted finish. Oiling Specify either "oiled" or unoiled. Normally, rust-prevention "oiled" products are produced. Roll Edge Finish Specify either "mill edge" or "slit edge" depending on your use condition. Slit edges are recommended, especially if the delivered product will be used as-rolled and without further processing, thus requiring edge finishing, or when strict width tolerance is required. Applications Nippon Steel & Sumitomo Metal exercises through quality control over the entire manufacturing process in order to suit the products to our customers intended use. Therefore, when placing orders we kindly request our customers to present information necessary for quality control, such as intended use and the method of fabrication. Other Some intended applications require rigorous specifications of assembly accuracy, component accuracy, and other conditions. If there are any requests of such kind, please consult with Nippon Steel & Sumitomo Metal beforehand to clarify the required specifications. 28