Research Articles Reactive DC Magnetron Sputtering Deposition of Copper Nitride Thin Film

Similar documents
Pre-treatment of low temperature GaN buffer layer deposited on AlN Si substrate by hydride vapor phase epitaxy

Citation JOURNAL OF APPLIED PHYSICS (1995),

Citation JOURNAL OF APPLIED PHYSICS (1995),

Deposited by Sputtering of Sn and SnO 2

Microstructure, morphology and their annealing behaviors of alumina films synthesized by ion beam assisted deposition

Formation of Cupric Oxide Films on Quartz Substrates by Annealing the Copper Films

Ruthenium Oxide Films Prepared by Reactive Biased Target Sputtering

Characterization of carbon nitride thin films deposited by microwave plasma chemical vapor deposition

RightCopyright 2006 American Vacuum Soci

Growth Of TiO 2 Films By RF Magnetron Sputtering Studies On The Structural And Optical Properties

Deposition and characterization of sputtered ZnO films

Preparation and characterization of Co BaTiO 3 nano-composite films by the pulsed laser deposition

Synthesis and Characterization of DC Magnetron Sputtered ZnO Thin Films Under High Working Pressures

Excimer Laser Annealing of Hydrogen Modulation Doped a-si Film

Surface Analysis of Electrochromic Switchable Mirror Glass Based on Magnesium-Nickel Thin Film in Accelerated Degradation Test

ARTICLE IN PRESS. Materials Science in Semiconductor Processing

Characterization of Polycrystalline SiC Films Grown by HW-CVD using Silicon Tetrafluoride

Supporting Information

Solid-Phase Synthesis of Mg2Si Thin Film on Sapphire substrate

Vacuum, Ar, and O 2 annealing effects on bandgap-tunable semiconducting amorphous Cd Ga O thinfilms

Supporting Information. Selective Metallization Induced by Laser Activation: Fabricating

The Effect of Annealing Heat Treatment on Structural and Optical Properties of Ce-doped ZnO Thin Films

Investigation of molybdenum-carbon films Mo C:H deposited using an electron cyclotron resonance chemical vapor deposition system

Supporting Information. Solution-Processed 2D PbS Nanoplates with Residual Cu 2 S. Exhibiting Low Resistivity and High Infrared Responsivity

THE INFLUENCE OF NITROGEN CONTENT ON THE MECHANICAL PROPERTIES OF TiN x THIN FILMS PREPARED BY REACTIVE MAGNETRON SPUTTERING

OXYGEN SENSOR BASED ON Ga 2 O 3 FILMS OPERATING AT HIGH TEMPERATURE

Improvement of gas barrier properties by combination of polymer film and gas barrier layer

GROWTH AND CHARACTERIZATION OF NANOSTRUCTURED CdS THIN FILMS BY CHEMICAL BATH DEPOSITION TECHNIQUE

Pulsed Laser Deposition of Epitaxial Titanium Nitride on Magnesium Oxide substrate

Supplementary Figure 1 TEM of external salt byproducts. TEM image of some salt byproducts precipitated out separately from the Si network, with

DEPOSITION AND CHARACTERISTICS OF TANTALUM NITRIDE FILMS BY PLASMA ASSISTED ATOMIC LAYER DEPOSITION AS CU DIFFUSION BARRIER

Effect of melt temperature on the oxidation behavior of AZ91D magnesium alloy in 1,1,1,2-tetrafluoroethane/air atmospheres

Ceramic Processing Research

Supporting Online Material for

Supplimentary Information. Large-Scale Synthesis and Functionalization of Hexagonal Boron Nitride. Nanosheets

Deposition of TiN/CrN hard superlattices by reactive d.c. magnetron sputtering

STRUCTURAL AND ELECTRICAL PROPERTIES OF Sb 2 O 3 THIN FILMS

Amorphous Er 2 O 3 films for antireflection coatings

Vacuum Deposition of High Performance Gas Barrier Materials for Electronics Applications

STRUCTURE AND MORPHOLOGY OF INDIUM NITRIDE THIN FILMS GROWN BY PLASMA ASSISTED PLD: THE IMPACT OF NITROGEN FLOW AND SUBSTRATE TEMPERATURE

CHAPTER 4. SYNTHESIS OF ALUMINIUM SELENIDE (Al 2 Se 3 ) NANO PARTICLES, DEPOSITION AND CHARACTERIZATION

Oxidation behavior of Cu nanoclusters in hybrid thin films

High Density Plasma Etching of IrRu Thin Films as a New Electrode for FeRAM

Study of The Structural and Optical Properties of Titanium dioxide Thin Films Prepared by RF Magnetron sputtering

Applications of Successive Ionic Layer Adsorption and Reaction (SILAR) Technique for CZTS Thin Film Solar Cells

Tungsten Oxide Nanorods Array and Nanobundle Prepared by Using Chemical Vapor Deposition Technique

CEMS study on diluted magneto titanium oxide films prepared by pulsed laser deposition

Growth and Doping of SiC-Thin Films on Low-Stress, Amorphous Si 3 N 4 /Si Substrates for Robust Microelectromechanical Systems Applications

arxiv:cond-mat/ v2 [cond-mat.mtrl-sci] 29 Nov 2003

Growth of SiC thin films on graphite for oxidation-protective coating

Supplementary Information

More Thin Film X-ray Scattering and X-ray Reflectivity

Silver Diffusion Bonding and Layer Transfer of Lithium Niobate to Silicon

Anomaly of Film Porosity Dependence on Deposition Rate

EFFECT OF GROWTH TEMPERATURE ON THE CATALYST-FREE GROWTH OF LONG SILICON NANOWIRES USING RADIO FREQUENCY MAGNETRON SPUTTERING

Roman Chistyakov and Bassam Abraham Zond Inc/Zpulser LLC, Mansfield, MA

Development of Low-resistivity TiN Films using Cat Radical Sources

XPS STUDY OF DIAMOND-LIKE CARBON-BASED NANOCOMPOSITE FILMS

Polycrystalline and microcrystalline silicon

Synthesis of nanoscale CN x /TiAlN multilayered coatings by ion-beam-assisted deposition

Electron backscattered diffraction study of poly-si by Ni-mediated crystallization of amorphous silicon using a SiO 2 nanocap

Thermal stability and oxidation properties of magnetron sputtered diamond-like carbon and its nanocomposite coatings

Supporting Information. Copper inks formed using short carbon chain organic Cuprecursors

International Journal of ChemTech Research CODEN (USA): IJCRGG ISSN: Vol.7, No.3, pp ,

Growth of large single-crystalline two-dimensional boron. nitride hexagons on electropolished copper

Mechanical Properti es of ZnO:Mo Transparent Conducting Oxide Thin Film Prepared by Sputtering

An XPS and Atomic Force Microscopy Study of the Micro-Wetting Behavior of Water on Pure Chromium* 1

Available online at ScienceDirect. Materials Today: Proceedings 2 (2015 )

The growth of patterned ceramic thin films from polymer precursor solutions Göbel, Ole

Low Thermal Budget NiSi Films on SiGe Alloys

Etching Mask Properties of Diamond-Like Carbon Films

Epitaxial growth of (001) and (111) Ni films on MgO substrates

Influence of Underlayer on Crystallography and Roughness of Aluminum Nitride Thin Film Reactively Sputtered by Ion-Beam Kaufman Source

Fabrication and application of high quality diamond coated. CMP pad conditioners

High Density Iron Silicide Nanodots Formed by Ultrathin SiO 2 Film Technique

Metal-containing diamond-like carbon with self-assembled alternating nano-scaled layers

NANOSTRUCTURED TiN THIN FILMS SUITABLE FOR MEDICAL APPLICATIONS

Optical, microstructural and electrical studies on sol gel derived TiO 2 thin films

Influence of Annealing Temperature on the Properties of ITO Films Prepared by Electron Beam Evaporation and Ion-Assisted Deposition

Supporting Information

Band-gap Engineering in Sputter Deposited Amorphous/Microcrystalline Sc x Ga 1-x N

Citation for published version (APA): Borsa, D. M. (2004). Nitride-based insulating and magnetic thin films and multilayers s.n.

OUTLINE. Preparation of III Nitride thin 6/10/2010

Large-scale Spinning of Silver Nanofibers as Flexible and. Reliable Conductors

Thin-film deposition and characterization of a Sn-deficient perovskite derivative Cs 2 SnI 6

Influence of radio frequency power on structure and ionic conductivity of LiPON thin films

Electronic structure and x-ray-absorption near-edge structure of amorphous Zr-oxide and Hf-oxide thin films: A first-principles study

Ageing Resistance (12 years) of Hard and Oxidation Resistant SiBCN Coatings

Short-range order and microhardness of the compositionally complex alloy Al 8 Co 17 Cr 17 Cu 8 Fe 17 Ni 33

Fabrication and characterization of photocatalyst coatings by heat treatment in carbon powder for TiC coatings

SUPPLEMENTARY INFORMATION

Vacuum 85 (2011) 792e797. Contents lists available at ScienceDirect. Vacuum. journal homepage:

TRANSPARENT AND CONDUCTING INDIUM TIN OXIDE THIN FILMS GROWN BY PULSED LASER DEPOSITION AT LOW TEMPERATURES

This journal is The Royal Society of Chemistry S 1

Development of diamond coated tool and its performance in machining Al 11%Si alloy

ZnO thin film deposition on sapphire substrates by chemical vapor deposition

X-ray photoelectron spectroscopy of cerium and its oxides 3d states

Effect of substrate heating on elimination of pinholes in sputtering deposited SiO2 films on LiNbO3 single crystal substrates

Ferromagnetic transition in Ge 1 x Mn x Te semiconductor layers

Synthesis, Characterization and Optical Properties of ZnS Thin Films

Transcription:

468 J. Mater. Sci. Technol., Vol.23 No.4, 2007 Research Articles Reactive DC Magnetron Sputtering Deposition of Copper Nitride Thin Film Xing ao LI 1,2), Zuli LIU 1) and Kailun YAO 1,3) 1) Department of Physics, Huazhong University of Science and Technology, Wuhan 430074, China 2) School of Science, Hubei Institute for Nationalities, Enshi 445000, China 3) International Center of Material Physics, Chinese Academy of Science, Shenyang 110016, China [Manuscript received August 28, 2006, in revised form January 9, 2007] Copper nitride thin film was deposited on glass substrates by reactive DC (direct current) magnetron sputtering at a 0.5 Pa N 2 partial pressure and different substrate temperatures. The as-prepared film, characterized with X-Ray diffraction, atomic force microscopy, and X-ray photoelectron spectroscopy measurements, showed a composed structure of Cu 3 N crystallites with anti-reo 3 structure and a slight oxidation of the resulted film. The crystal structure and growth rate of Cu 3 N films were affected strongly by substrate temperature. The preferred crystalline orientation of Cu 3 N films were (111) and (200) at RT, 100 C. These peaks decayed at 200 C and 300 C only Cu (111) peak was noticed. Growth of Cu 3 N films at 100 C is the optimum substrate temperature for producing high-quality (111) Cu 3 N films. The deposition rate of Cu 3 N films estimated to be in range of 18 30 nm/min increased while the resistivity and the microhardness of Cu 3 N films decreased when the temperature of glass substrate increased. KEY WORDS: DC magnetron sputtering; Copper nitride thin film; Resistivity; Microhardness 1. Introduction Copper nitride (Cu 3 N), one kind of excellent semiconductors with many extraordinary properties, has obtained considerable attention in recent years as a new material applicable for optical storage devices and high-speed integrated circuits. For instance, its optical reflectivity in visible and infrared range is far smaller than that of pure Cu [1]. Cu 3 N is also stable at room temperature whereas it can decompose into Cu and N 2 as the temperature is over 300 C. The low decomposition temperature and discriminating optical properties of the compound compared to those of Cu are applicable for optical read-only memory disks by generating microscopic Cu-metal spots on Cu 3 N film by performing local laser heating [2]. Cu 3 N films were also used as buffer layers for depositing Cu-metal lines on Si wafers to achieve higher signal speed than existing Al-metal lines in integrated-circuit fabrication processes. The crystal structure of Cu 3 N is also interesting it has the cubic anti-reo 3 structure in which Cu atoms do not occupy the fcc close-packing sites. Therefore, another metallic atom (e.g., Pd [3], Cu [4], Li [5] ) can be inserted into the body center of the cubic unit cell, inducing significant changes in the electrical properties. Few methodology has been reported for the growth of Cu 3 N films, mainly covering RF (radio frequency) [6 10], DC (direct current) [11] sputtering, molecular beam epitaxy [12,13] and reactive pulsed laser deposition [14]. It also has been known that variations of sputtering parameters such as gas pressure, substrate temperature, and sputtering power allow alerting the structure of the deposited films. Therefore, the variations of these experimental parameters are promising to affect the crystalline structure and growth rate of deposited films on substrate. Prof., to whom correspondence should be addressed, E-mail: zlliu@hust.edu.cn. With an aim to find the optimum conditions for growing well-oriented and defect-free Cu 3 N films on glass substrates, we reported here the preparation of Cu 3 N films by reactive DC magnetron sputtering of a Cu target at different substrate temperatures and in 1.0 Pa Ar/N 2 gas mixture and at 0.5 Pa N 2 partial pressure. The investigation of the crystalline structure and growth rate of as-prepared Cu 3 N films on glass substrate was also proposed by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and atomic force microscopy (AFM). 2. Experimental Reactive DC magnetron sputtering was performed on a more function magnetron sputtering system, JZCK-III (Shenyang Juzhi Tech. Com. Shenyang, China) to prepared Cu 3 N films on glass substrates. The target was a pure Cu (99.999%) with a diameter of 50 mm and a thickness of 5 mm. The distance between substrate and target was kept at 60 mm and the DC power was 50 W during the sputtering. The base pressure of the vacuum chamber was less than 8.0 10 4 Pa before the sputtering. The flow rates of the working and the reactive gases (99.99% pure Ar and N 2 ) were adjusted by independent mass-flow controller. During the sputtering the total sputtering pressure was maintained at 1.0 Pa by setting the total gas-flow rate to be 40 sccm. The partial pressures of Ar and N 2 in the chamber were estimated to be 0.5 Pa as the respective flow rates was 20 sccm from the mass-flow controllers. Prior to deposition, the glass substrates were cleaned by ultrasonic waves in acetone and alcohol, and then dried by blowing air. Pre-sputtering was performed for 3 min before each deposition process in order to remove the oxidized surface layer of the target and also to maintain the stability of copper target during the sputtering. The crystalline properties of the obtained films were analyzed by XRD measurements with CuKα

J. Mater. Sci. Technol., Vol.23 No.4, 2007 469 in agreement with the reported results [6,7]. Theoretically the temperature of glass substrate controls the diffusion of N atoms towards Cu surface during the crystal growth, which, on the other hand, is proportional to exp( E/k B T ) according to the Arrhenius law. Here E is the activation energy, the characteristic parameter for the respective diffusion pathway and k B is the Boltzmann constant [16]. Therefore, the diffusion of Cu and N atoms is more efficient at lower substrate temperatures for producing appreciable density of Cu-N bonds necessary for the growth along the (100) direction. However, at very high substrate temperature, it is difficult to from the Cu-N bonds, and hence the Cu atoms grow in crystal alone. Fig.1 XRD spectra of Cu 3N films deposited reactive DC magnetron sputtering at 0.5 Pa N 2 partial pressure at the substrate temperature of temperature of RT (curve T 0 ), 100 C (curve T 1 ), 200 C (curve T 2 ) and 300 C (curve T 3 ) line (D/max-γA, Japan). To determine the chemical binding state and composition of the films, XPS (Kratos, XSAM800) was performed with MgKα radiation. The surface morphology of copper nitride films was characterized using atomic force microscopy (AFM, Molecular Imaging USA). The thickness of films was measured with a profilometer (DEKTAKII). The resistivities of films were measured using the fourprobe method. The microhardness measurements of films were carried out using MICROMET2104 apparatus. 3. Results and Discussion 3.1 Structure of films Figure 1 shows the XRD spectra of Cu 3 N films deposited at the substrate temperature of RT (curve T 0 ), 100 C (curve T 1 ), 200 C (curve T 2 ), and 300 C (curve T 3 ) with a fixed N 2 partial pressure of 0.5 Pa. At RT and 100 C, the XRD spectra (curve T 0 and T 1 ) show a strong (111) preferred orientation and large integrated intensity of the diffraction peak, which is corresponded to a Cu 3 N (111) reflection. The XRD spectrum also shows grains with other orientations like (200) and (210) along with those (111) at low substrate temperature. These results suggest that the deposited films are composed of Cu 3 N crystallites with the anti-reo 3 structure and preferred to be (111) peak at relatively low substrate temperature. As the temperature of the glass substrate increased to 200 C, both the peak of (100) and (211) of CuN 3 films were noticed while the (111), (200) peaks of Cu 3 N were very weak, and then totally disappeared when the temperature of the glass substrate increased to 300 C, where only Cu (111) peak was observed. These results indicate that too high temperature of the substrate was not suitable for the nitrification of Cu, in consistent with that in literature [15]. Subsequently, the temperature of glass substrates affects the crystal growth of Cu 3 N films on the glass substrate remarkably. The growth of Cu 3 N (111)-preferred film on the glass substrate is pronounced at low substrate temperature and low N 2 partial pressures, which is 3.2 Surface morphology of films The surface morphology of Cu 3 N films was studied in air by AFM in a scanning areas of 5 µm 5 µm. Figure 2 shows the AFM images taken from films deposited at the substrate temperature of RT (image T 0 ), 100 C (image T 1 ), 200 C (image T 2 ), and 300 C (image T 3 ) at a N 2 partial pressure of 0.5 Pa during the sputtering. Image T 0 shows that the Cu 3 N film has various hills, which is possible due to the small diffusivity of atoms at low substrate temperature. Image T 1 and T 2 show an unknit surface and the grain distributing uniformity. This morphology is similar to a compactness structure. However, the crystal grains size in image T 2 is bigger than that in image T 1. Moreover, the crystal structure in image T 2 is more complex than that in image T 1. Image T 3 shows an individual and uniform crystal structure, which is actually the crystal structure of Cu. These results agree with those obtained from XRD experiments. The AFM results are summarized in Table 1. From the data of the AFM images, one can see that the surface roughness of Cu 3 N films decreased from 28.4 to 5.1 nm at the temperature from RT to 100 C. However, their surface roughness then increased to 8.0 and 11.9 nm when the temperature of glass substrate increased to 200 C and 300 C, respectively. The enhancement in surface smoothness with substrate temperature from RT to 100 C (may be 150 C [17] ) can be assigned to the higher surface atom diffusion at higher substrate temperature [1], which predicted [18] theoretically smoothening film surface. When the temperature of glass substrate was 200 C or 300 C, the surface was rougher than that deposited at 100 C. This change may be due to the different crystal structures of Cu 3 N films at different substrate temperatures. Within these four samples, the smoothest Cu 3 N films were obtained when the temperature of substrate was 100 C (image T 1 ), and hence the temperature of glass substrate of 100 C is the optimum temperature for producing high-quality and (111)- preferred Cu 3 N films. 3.3 Chemical composition of films X-ray photoelectron spectroscopy (XPS) was performed with MgKα radiation to characterize the chemical binding state and composition of the films. Figure 3(a), (b), and (c) show the XPS spectra of Cu 3 N films for Cu2p, N1s, O1s, respectively. Figure 3(a) shows the peaks in the domain of 933.2 935.0 ev and of 953.0 955.0 ev as well as the peak at

470 J. Mater. Sci. Technol., Vol.23 No.4, 2007 Fig.2 AFM images of Cu3 N films deposited at 0.5 Pa N2 partial pressure and at the substrate temperature of temperature of RT (image T0 ), 100 C (image T1 ), 200 C (image T2 ), and 300 C (image T3 ) Table 1 Overview of the Cu3 N films and investigated with AFM Sample T0 T1 T2 T3 Substrate Temp./ C RT 100 200 300 Mean Height/nm 53.6 11.5 18.7 25.6 Surface roughness/nm 28.4 5.1 8.0 11.9 Thickness/nm 93.7 105.7 135.3 154.7 Fig.3 XPS spectra of Cu3 N films: (a) Cu2p, (b) N1s, (c) O1s about 944 ev. The peak at around 935.0 ev and 955.0 ev result from Cu2p3/2 and Cu2p1/2 peaks of Cu2+, respectively. The peak at 944 ev is the shakeup peak. The spin-orbit coupling energy gap of Cu2p was 20 ev. These results match those published in literature [19] and also support the concurrence of Cu1+ and Cu2+ for the Cu3 N films deposited at RT substrate temperature. Cu1+ exists in the form of Cu3 N while Cu2+ in the form of CuO. The XRD spectrum of Cu3 N films unfortunately did not show the CuO information. However, the XPS spectra of O1s in Fig.3(c) prove the idea that the Cu2+ comes from Cu atoms oxidation in the films surface. Figure 3(b) presents that the main peak of N1s is centered at about 397 ev, which results from N1s peak of Cu3 N phase[7]. For all samples, no obvious shoulder peaks appeared and the line shape remained constant with affiliation to substrate temperatures although the height and the area of the peaks for different samples have a little change. The results reveal that the nitrogen bond exists mainly in the films and the nitrogen concentrations are disparate in different samples. 3.4 Thickness and deposition rates of films The thickness of films was measured by a profil-

J. Mater. Sci. Technol., Vol.23 No.4, 2007 471 from that more matters will be formed and deposited during chemical reaction at higher substrate temperature within a certain temperature limited range. Fig.4 Deposition rates of Cu 3 N films deposited at different substrate temperatures at N 2 partial pressure of 0.5 Pa Fig.5 Resistivity of Cu 3N films deposited at different substrate temperatures and N 2 partial pressure of 0.5 Pa Fig.6 Microhardness of Cu 3N films ometer (DEKTAKII) and the deposition rates of Cu 3 N films were then calculated correspondingly using the thickness obtained and the deposition time (the sputtering process of each sample was completed for 5 min). The deposition rates of Cu 3 N films were estimated to be in the range of 18.74 30.94 nm/min. This is notably higher than the deposition rates (10 20 nm/min) of Cu 3 N films reported by Nosaka et al. [15] who employed RF magnetron sputtering for Cu 3 N film growth. Figure 4 shows the variation of the deposition rates of Cu 3 N films as a function of the substrate temperatures at a fixed N 2 partial pressure of 0.5 Pa. The deposition rates of Cu 3 N films increased almost linearly with increasing the substrate temperature, which presumably results 3.5 Resistivity of films Figure 5 is the variation of the resistivity of Cu 3 N films as a function of the temperature of the glass substrate used for the deposition of Cu 3 N films. The resistivity was obtained using a four-probe method at room temperature. The curve shows the resistivity of Cu 3 N films was in the range from 4.0 to 1.0 Ω cm, a big difference from the values (20 2 10 3 Ω cm) reported [6,11,15]. The resistivity of Cu 3 N films decreased with increasing substrate temperature. It is again noteworthy that films grown as mixtures of Cu and Cu 3 N will produce rather high electrical resistivity values. Moreover, the conduction in mixed sample might follow the Percolation Theory, (wherein two conduction processes coexist: (one), a metallic conduction process through the Cu path, and (two), the semiconductor conduction process). We tried to analyze this result qualitatively. At low N 2 partial pressure (the Ar/N 2 gas mixture at 1/2 N 2 partial pressure), the Cu 3 N films were deposited mainly by the insert of N atoms into the lattice of Cu atoms and the center of the Cu 3 N lattice contains Cu atoms. This insertion of Cu atoms into the body center of the anti-reo 3 structure was similar to WO 3, which made conductive tungsten bronzes by inserting some metal atoms into the ReO 3 structure. The inserted Cu atoms act as a donor and release free electrons as a carrier, and thus the resistivity of Cu 3 N films decreased. This is due to the released free electrons of insertion Cu atoms that was localized and scattered by crystal boundaries and crystal defects. 3.6 Microhardness of films The microhardness of the deposited films was measured using the MICROMET2104 apparatus. The microhardness of Cu 3 N films measured were 3.08 3.98 GPa. This result approximates the results in literature [20]. When the N 2 flow rate is small, the microhardness of Cu 3 N films will be a maximum value (4.25 GPa); while the N 2 flow rate increases, the microhardness of Cu 3 N films will be a constant (3.7 GPa). Figure 6 reflects that the microhardness of samples was decreased slightly as the substrate temperature increased (and the N 2 partial pressure was fixed at 0.5 Pa). The reason is that the microhardness of Cu films are lower than Cu 3 N films. These facts indicated that the substrate temperature not only affected the structures of Cu 3 N films, but also affected the combined composition and compactness of Cu 3 N films. 4. Conclusions Cu 3 N films were prepared by reactive DC magnetron sputtering of a pure Cu target on glass using a 0.5 Pa N 2 partial pressure (the Ar/N 2 gas mixture at N 2 partial pressure of 0.5 Pa) at different substrate temperatures. X-ray diffraction measurements show that the films were composed of Cu 3 N crystallites with anti-reo 3 structure (except for at substrate temperature of 300 C). The crystal growth of the Cu 3 N films was affected strongly by substrate temperature.

472 J. Mater. Sci. Technol., Vol.23 No.4, 2007 The preferred crystalline orientation of the films were (111) and (200) at RT and 100 C. The (111), (200) peaks of Cu 3 N at 200 C are very weak and decayed to almost zero when the temperature of substrate is approaching to 300 C, indicating that too high substrate temperature is not suitable for the nitrification of Cu. The film showed only Cu (111) at the substrate temperature of 300 C. The surface morphology of Cu 3 N films was studied by AFM. The smoothest film in the four samples was obtained at 100 C and this temperature was selected as the optimum substrate temperature for producing high-quality and (111)-preferred growth Cu 3 N films. Good agreement between XRD and AFM analysis was obtained in characterizing the film structures. XPS measurements revealed that the films were slightly oxidized, especially at RT substrate temperature. The substrate temperature not only affected the crystal structures and the surface morphology of the Cu 3 N films, but also affected its deposition rate, resistivity, and microhardness. The deposition rate of Cu 3 N films was evaluated in our experimental condition to be 18 30 nm/min. The deposition rate increased while the resistivity and the microhardness of Cu 3 N films decreased with increasing substrate temperatures. Acknowledgement This work was supported by the Key Program of the Education Branch of Hubei Province, China (2003A001 and D200529002). REFERENCES [1 ] T.Maruyama and T.Morishita: Appl. Phys. Lett., 1996, 69, 890. [2 ] M.Asano, K.Umeda and A.Tasaki: Jpn. J. Appl. Phys., 1990, 29, 1985. [3 ] U.Hahn and W.Weber: Phys. Rev. B, 1996, 53, 12684. [4 ] M.G.Moreno-Armenta, A.Martinez-Ruiz and N.Takeuchi: Solid State Sci., 2004, 6, 9. [5 ] F.Gulo, A.Simon, J.Kohler and R.K.Kremer: Angew. Chem. Int. Edit., 2004, 43, 2032. [6 ] D.Wang, N.Nakamine and Y.Hayashi: J. Vac. Sci. Technol. A, 1998, 16, 2084. [7 ] Z.Q.Liu, W.J.Wang, T.M.Wang, S.Chao and S.K.Zheng: Thin Solid Films, 1998, 325, 55. [8 ] G.H.Yue, P.X.Yan and J.Wang: J. Cryst. Growth, 2005, 274, 464. [9 ] J.Wang, J.T.Chen, X.M.Yuan, Z.G.Wu, B.B.Miao and P.X.Yan: J. Cryst. Growth, 2006, 286, 407. [10] X.M.Yuan, P.X.Yan and J.Z.Liu: Mater. Lett., 2006, 60, 1809. [11] L.Maya: J. Vac. Sci. Technol. A, 1993, 11, 603. [12] S.Terada, H.Tanaka and K.Kubota: J. Cryst. Growth, 1989, 94, 567. [13] D.M.Borsa and D.O.Boerma: Surf. Sci., 2004, 548(1-3), 95. [14] G.Soto, J.A.Diaz and W.Cruz: Mater. Lett., 2003, 57, 4130. [15] T.Nosaka, M.Yoshitake, A.Okamoto, S.Ogawa and Y.Nakayama: Thin Solid Films, 1999, 348, 8. [16] P.Hones, C.Zakri, P.E.Schmid, F.Levy and O.R.Shojaei: Appl. Phys. Lett., 2000, 76, 3194. [17] S.Ghosh, F.Singh, D.Choudhary, D.K.Avasthi, V.Ganesan, P.Shah and A.Guptab: Surf. Coat. Technol., 2001, 142-144, 1034. [18] W.M.Tong and R.S.Williums: Annu. Rev. Phys. Chem., 1994, 45, 401. [19] Zhiguo WU, Weiwei ZhANG, Lifeng BAI, Jun WANG and Pengxun YAN: Acta Phys. Sin., 2005, 54, 1687. (in Chinese) [20] J.F.Pierson: Vacuum, 2002, 66, 59.