Cobalt/Chromium/Iron/Nickel/Molybdenum/Manganese Co40/Cr20/Fe15/Ni15/Mo 7/Mn 2/C/Be Density 8.3 g cm -3 Coefficient of thermal expansion @^C 12.5 0-100 x10-6 K -1 1450-1460 C Specific heat @^C 430 20 J K -1 kg -1 Alloy Cobalt/Chromium/Iron/Nickel/Molybdenum/Mangan Mechanical Properties Electrical resistivity 95 mohmcm Modulus of elasticity 200 GPa Tensile strength 800-2200 MPa Wire CO125140 CO125150 CO125160 Diameter............... 0.25mm Temper................ Hard 810-448-720 20 m 741-218-929 50 m 147-258-301 100 m 205-485-150 200 m 432-755-849 500 m Diameter............... 0.5mm Temper................ Hard 284-250-786 10 m 026-223-494 20 m 075-280-796 50 m 465-519-447 100 m 201-368-118 200 m Diameter............... 1.0mm Temper................ Hard 060-016-033 5 m 045-234-759 10 m 514-714-463 20 m 943-835-912 50 m 241-947-748 100 m 1
Havar 1 - High-Strength Non-Magnetic Alloy Co42.5/Cr20/Ni13/Fe/W/Mo/Mn Common Brand Names : Havar 1 Mechanical Properties Density 8.3 g cm -3 Elongation at break 1 % Modulus of elasticity 200 GPa Tensile strength 1860 MPa Coefficient of thermal expansion @20-100C 9.5-11.0 x10-6 K -1 Thermal conductivity @23C 14.7 W m -1 K -1 CO010210 CO010215 CO010220 CO010230 CO010240 Thickness.............. 0.004mm Web Code Size 1pc 2pcs 5pcs Thickness.............. 0.0045mm Web Code Size 1pc 2pcs 5pcs Thickness.............. 0.005mm Web Code Size 1pc 2pcs 5pcs Thickness.............. 0.01mm 642-369-337 25 x 25 mm 296-164-191 50 x 50 mm 020-514-919 100 x 100 mm Coil Width 100mm 564-370-386 0.2 m 546-290-844 0.3 m 286-351-166 0.5 m Web Code Diameter 10 20 50 237-027-893 4 mm 628-481-989 6 mm 560-238-608 8 mm 029-831-589 10 mm 728-940-664 15 mm 117-579-886 25 mm 697-475-420 50 mm Thickness.............. 0.0125mm 184-433-699 25 x 25 mm 054-209-552 50 x 50 mm 776-197-960 100 x 100 mm 024-742-101 150 x 150 mm Coil Width 190mm 092-765-436 0.2 m Web Code Diameter 10 20 50 459-990-958 4 mm 498-865-445 6 mm 358-178-242 8 mm 772-276-908 10 mm 534-613-138 15 mm 826-648-487 25 mm 331-061-825 50 mm Alloy Havar 1 - High-Strength Non-Magnetic Alloy 2
Havar 1 - High-Strength Non-Magnetic Alloy Co42.5/Cr20/Ni13/Fe/W/Mo/Mn CO010245 CO010250 CO010270 Thickness.............. 0.020mm 377-627-805 25 x 25 mm 098-538-818 50 x 50 mm 020-164-149 100 x 100 mm Coil Width 100mm 204-773-367 0.2 m 338-530-247 0.5 m Web Code Diameter 10 20 50 035-031-916 4 mm 412-813-432 6 mm 030-724-739 8 mm 086-476-890 10 mm 040-738-809 15 mm 800-038-324 25 mm 605-717-390 50 mm Thickness.............. 0.025mm 382-725-076 25 x 25 mm 840-634-277 50 x 50 mm 079-280-739 100 x 100 mm 910-090-541 150 x 150 mm Coil Width 150mm 761-322-019 0.2 m 165-256-270 0.5 m Web Code Diameter 10 20 50 128-783-217 4 mm 097-901-391 6 mm 237-666-552 8 mm 708-322-350 10 mm 540-290-119 15 mm 536-271-591 25 mm 033-938-519 50 mm Thickness.............. 0.05mm 242-315-307 25 x 25 mm 289-422-855 50 x 50 mm 177-854-350 100 x 100 mm 231-799-677 150 x 150 mm Coil Width 150mm 974-961-734 0.2 m Web Code Diameter 10 20 50 777-510-074 4 mm 188-759-195 6 mm 594-898-148 8 mm 362-269-198 10 mm 283-639-901 15 mm 454-999-119 25 mm 874-894-227 50 mm Alloy Havar 1 - High-Strength Non-Magnetic Alloy 39
Havar 1 - High-Strength Non-Magnetic Alloy Co42.5/Cr20/Ni13/Fe/W/Mo/Mn CO010300 CO010400 CO010410 Permendur 49 1 Co49/Fe49/V 2 Thickness.............. 0.075mm 361-784-549 25 x 25 mm 223-066-765 50 x 50 mm 883-347-585 100 x 100 mm 418-440-674 150 x 150 mm Coil Width 200mm 305-081-298 0.2 m 205-682-478 0.3 m Web Code Diameter 10 20 50 893-936-192 4 mm 742-021-285 6 mm 752-654-219 8 mm 081-778-019 10 mm 222-254-962 15 mm 781-870-678 25 mm 733-828-670 50 mm Thickness.............. 0.2mm 728-586-952 25 x 25 mm 073-368-072 50 x 50 mm 171-007-951 100 x 100 mm Coil Width 100mm 375-996-329 0.2 m 999-538-364 0.5 m Thickness.............. 0.5mm 20pcs 680-512-803 25 x 25 mm 064-102-922 50 x 50 mm 012-874-915 100 x 100 mm Coil Width 212mm 609-369-922 0.2 m 654-932-650 0.3 m Common Brand Names : Permendur 49 1 Soft magnetic alloy. Uses include instrument, radar and radio transformers. Density 8.15 g cm -3 Electrical resistivity 40 mohmcm Magnetic Properties Curie temperature 940 C Coefficient of thermal expansion @20C 9.5 x10-6 K -1 Saturation flux density 2.34 T Crystallization temperature W C Alloy Havar 1 - High-Strength Non-Magnetic Alloy Mechanical Properties Elongation at break 6 % 4
Permendur 49 1 Co49/Fe49/V 2 Sheet CO153025 CO153035 CO157911 CO157940 CO157950 Thickness.............. 0.25mm 038-839-459 50 x 50 mm 854-931-883 100 x 100 mm 866-481-035 150 x 150 mm 310-135-250 180 x 500 mm Web Code Diameter 10 20 50 766-901-090 4 mm 862-630-503 6 mm 828-812-878 8 mm 601-607-228 10 mm 200-906-306 15 mm 113-296-469 25 mm 162-061-955 50 mm Thickness.............. 0.35mm 461-996-275 60 x 100 mm 531-991-756 95 x 100 mm 325-673-405 100 x 195 mm 140-201-315 195 x 200 mm Rod Diameter............... 11mm Condition............... Ground Web Code Length 1pc 2pcs 644-832-638 50 mm 701-832-906 100 mm 474-141-909 200 mm Diameter............... 25.4mm Condition............... Hot rolled (black) Web Code Length 1pc 2pcs 537-346-312 50 mm 313-098-269 100 mm Diameter............... 39mm Condition............... Hot rolled (black) Web Code Length 1pc 2pcs 889-403-911 50 mm 959-099-126 100 mm USD 989.00 Cobalt/Chromium/Tungsten/Nickel/Iron/Manganese Co50/Cr20/W 15/Ni10/Fe 3/Mn 2 Alloy Permendur 49 1 166-013-410 50 x 50 mm 046-794-998 100 x 100 mm 211-319-411 150 x 150 mm 888-280-049 300 x 300 mm Coil Width 300mm 417-321-082 0.5 m Web Code Size 1pc 2pcs 182-886-921 150 x 150 mm 674-843-463 300 x 300 mm Cobalt/Tungsten Co50/W 50 5
Cobalt/Tungsten Co50/W 50 CO106010 F 1530 C Max. Particle size....... 45micron 637-880-795 50 g 735-090-711 100 g 886-345-595 200 g 793-189-966 500 g 148-738-455 1000 g Cobalt/Silicon/Boron/Iron/Nickel Co66/Si15/B 14/Fe 4/Ni 1 Metallic glasses (glassy alloys) or amorphous metals. Uses include soft magnetic applications, brazing, coating and as reinforcing fibers. Density 7.59 g cm -3 Electrical resistivity 142 mohmcm Magnetic Properties Coercivity - as cast 0.24 A m -1 Crystallization temperature 550 C Curie temperature 205 C Maximum use temperature in air 80 C Remanence ratio - Br/Bs 0.82 Saturation flux density 0.55 T Mechanical Properties Saturation magnetostriction <1 x10-6 Hardness - Vickers 960 kgf mm -2 CO810220 CO810250 Tensile modulus Tensile strength Thickness.............. 0.018mm Coil width.............. 50.8mm Coil Width 50.8mm 681-934-903 0.5 m 488-681-723 1 m 088-866-626 2 m 093-560-149 5 m 078-465-118 10 m Thickness.............. 0.025mm Coil width.............. 25mm Coil Width 25mm 997-575-686 0.5 m 696-955-112 1 m 119-390-149 2 m 923-764-452 5 m 470-559-550 10 m 61 GPa >700 MPa Alloy Cobalt/Tungsten Cobalt/Boron/Silicon/Iron/Molybdenum/Nickel Co69/B 12/Si12/Fe 4/Mo 2/Ni 1 Density 7.80 g cm -3 Electrical resistivity 136 mohmcm Magnetic Properties Coercivity - as cast 0.8 A m -1 Crystallization temperature 520 C Curie temperature 365 C Maximum use temperature in air 80 C Remanence ratio - Br/Bs 0.83 Saturation flux density 0.70 T Mechanical Properties Saturation magnetostriction <1 x10-6 Hardness - Vickers 900 kgf mm -2 Tensile modulus Tensile strength 63 GPa >700 MPa 6
Cobalt/Boron/Silicon/Iron/Molybdenum/Nickel Co69/B 12/Si12/Fe 4/Mo 2/Ni 1 CO820250 Cobalt/Chromium Co70/Cr30 CO056010 F Thickness.............. 0.025mm Coil width.............. 50mm Coil Width 50mm 492-826-893 0.5 m 603-359-951 1 m 419-998-117 2 m 499-764-877 5 m 470-607-482 10 m 825-932-876 20 m 1470 C Max. Particle size....... 45micron 059-859-392 50 g 482-423-472 100 g 302-935-800 200 g Cobalt/Silicon/Boron/Manganese Co70/Si+B 23/Mn 5/Fe+Mo 2 Density 7.6 g cm -3 Electrical resistivity 130 mohmcm Magnetic Properties Coercivity - as cast <1 A m -1 Crystallization temperature 450 C Curie temperature 350 C Maximum use temperature in air 80-120 C Remanence ratio - Br/Bs 0.7-0.95 Saturation flux density 0.8 T Mechanical Properties Saturation magnetostriction <0.3 x10-6 Hardness - Vickers 900 kgf mm -2 CO830250 CO830400 Tensile modulus Tensile strength Thickness.............. 0.025mm Coil width.............. 25mm Coil Width 25mm 241-610-156 0.5 m 201-267-532 1 m 158-447-098 2 m 805-876-046 5 m 734-504-927 10 m 813-121-286 50 m 640-152-755 100 m Thickness.............. 0.04mm Coil width.............. 25mm Coil Width 25mm 019-091-995 0.5 m 386-495-160 1 m 311-898-337 2 m 987-289-149 5 m 411-148-983 10 m 393-621-937 50 m 150 GPa 1500-2000 MPa Alloy Cobalt/Boron/Silicon/Iron/Molybdenum/Nickel Cobalt/Silicon/Molybdenum/Iron/Boron/Niobium Co78/Si 9/Mo 5/Fe 4/B 2/Nb 2 Density 7.75 g cm -3 7
Cobalt/Silicon/Molybdenum/Iron/Boron/Niobium Co78/Si 9/Mo 5/Fe 4/B 2/Nb 2 CO840300 Cobalt/Aluminum Co79/Al21 CO036010 F Cobalt/Iron Co80/Fe20 CK226100 Thickness.............. 0.03mm Coil width.............. 20mm Coil Width 20mm 925-408-312 0.5 m 856-078-938 1 m 325-872-412 2 m 671-284-647 5 m 991-798-367 10 m 1550 C Max. Particle size....... 150micron 080-934-710 50 g 116-844-151 100 g 605-520-425 200 g 690-051-894 500 g 256-478-806 1000 g We are able to offer powders of many other alloys, compounds and intermetallics. Lump Cobalt/Chromium Co86/Cr14 CK266010 F Max. Lump size......... 5mm 615-044-559 20 g 838-174-457 50 g 453-177-631 100 g Max. Particle size....... 150micron Condition............... Atomized 048-276-635 50 g 591-784-261 100 g 081-225-315 200 g Alloy Cobalt/Silicon/Molybdenum/Iron/Boron/Niobium Cobalt/Aluminum Co90/Al10 1400 C 8
Cobalt/Aluminum Co90/Al10 CO026010 F Max. Particle size....... 150micron 171-361-653 50 g 420-208-062 100 g 526-005-865 200 g 750-725-174 500 g 840-647-438 1000 g Cobalt/Titanium Co94/Ti 6 CO086010 F 1450 C Max. Particle size....... 45micron 489-426-929 50 g 178-364-097 100 g 295-502-140 200 g 937-768-884 500 g 221-103-096 1000 g Alloy Cobalt/Aluminum 9