19 th World Conference on Non-Destructive Testing 16 Detection of Sensitization for 6 Alloy and Austenitic Stainless Steel by Magnetic Field Sensor Hiroaki KIKUCHI 1, Hiroki YANAGIWARA 1, Hideki TAKAHASHI 1, Takaki SUMIMOTO 1, Takeshi MURAKAMI 1 1 Iwate University, Faculty of Engineering, 4-3-5 Ueda, Morioka, Japan Contact e-mail: hkiku@iwate-u.ac.jp Abstract. The Ni base alloy and austenitic stainless steel show usually paramagnetic property, whereas they transform into ferromagnetic along grain boundaries where sensitization occurs; this indicates a potential of non-destructive evaluation using magnetic measurement for sensitization. Here, as a feasibility study for application of non-destructive evaluation for sensitization using magnetic measurement, heat treated Ni base alloy and austenitic stainless steel were scanned by a magnetic field sensor and the changes in magnetization were obtained non-destructively. When the specimens were magnetized with the direction perpendicular to their surface before measurement, behaviour of changes in the magnetic flux density perpendicular to the surface are consistent with the results of magnetization obtained by the Vibrating Sample Magnetometer. The change in the flux density near the surface of specimen is related to the degree of chromium carbides progressing sensitization. The obtained results suggest that scanning with magnetic field sensor is effective to assess sensitization due to heat treatment for Ni base alloy and austenitic stainless steel. 1. Introduction The Ni base alloy and austenitic stainless steel are widely used for steam generators tubing because of its high strength and high corrosion resistance. However sensitization occurs along grain boundaries during long-term heat treatment, which degrades the corrosion resistance of the materials and generates stress corrosion cracking (SCC). The SCC induces tubing failures in steam generators. The sensitization mechanism has been thoroughly investigated [1-8], and the eddy current testing detects micro cracks caused by sensitization in practical use [9, 1]. However, it is preferable to detect suspicious sensitized areas prior to the formation of cracks for keeping the integrity of the tubes. The Ni base alloy and austenitic stainless steel show typically paramagnetic characteristics, while they transform into ferromagnetic phase along grain boundaries where sensitization occurs. Thus non-destructive evaluation (NDE) using magnetic measurement for sensitization can be possible. Several fundamental studies have been performed about these phenomena [11-13] and we also confirmed by a Vibrating Sample Magnetometer (VSM) that the alloys and steels showed ferromagnetic properties during heat treatment [14, 15]; however, the measurement using VSM is not NDE technique. Here, as a feasibility study of NDE application using magnetic measurement for sensitization, Inconel 6, Ni base alloy, and SUS34, austenitic stainless steel, were heat treated and scanned by a magnetic License: http://creativecommons.org/licenses/by/3./ 1 More info about this article: http://ndt.net/?id=19687
field sensor and the changes in magnetization were examined non-destructively. The behaviours of the flux density near the surface of specimen depend on the combination of magnetizing direction, sensing direction and scanning direction. On the basis of obtaining results, a possibility of non-destructive evaluation (NDE) for sensitization is discussed.. Sensitization and Magnetization Generally, Ni base alloy and austenitic stainless steel include chromium to enhance corrosion resistance. Sensitization is a phenomenon that chromium concentration decreases along grain boundaries and the chromium depletion zone is formed, consequently, corrosion resistance becomes weaker. The chromium depletion generates by the formation of chromium rich carbide: the carbon absorbs chromium when it forms carbide. When chromium concentration decreases to less than 1%, the Curie temperature of 6 alloy rises above the room temperature. On the other hand, the martensitic transition temperature of SUS34 shifts to the higher temperature, although typical temperature is very row temperature. These temperature shifts are attributed to the transformation into ferromagnetic phase in those materials. The carbides become coarser with absorbing chromium elements from the vicinity of grain boundaries, while chromium in the matrix diffuses to the chromium depletion zone; this causes the recovery of chromium concentration in the chromium depletion zone and the magnetization decreases for 6 alloy with longer heat treatment. Since the formation of martensitic phase contributes to the transformation into ferromagnetic for SUS34, the magnetization is kept higher during heat treatment. 3. Experimental Procedure 3.1 Preparation of Sample The Inconel 6 alloy manufactured by the Nilaco Co. (Japan) and SUS34 stainless steel were used here. The chemical compositions of the samples are listed in Table 1. The three types of SUS34, have different carbon content, were prepared and named as H, S and L, respectively. The as-received alloy and steel were cut out to plate specimens using an electro-discharge machining, and those plates have 5 mm width, 1 mm length and 1 mm thickness. The specimens were heat treated in vacuum (less than 1-3 Pa) at 873 K with 1 to 4 hours for 6 alloy, at 973K with 1 to 33 hours for SUS34, respectively, followed by air-cooling. After heat treatment, the specimens were polished by an electrochemical polishing to remove an oxide layer of the specimen surface. Table 1. Chemical compositions of (a) Inconel 6 and (b) SUS34. (a) Inconel 6 Ni Cr Fe Mn Si C 76 15.5 7.8.5.. (b) SUS34 Ni Cr P S Mn Si C H 8. 18.7.3.1 1.63.48.88 S 9. 18.5.3.1 1.63.51.56 L 1. 18.4.5.1 1.65.51.7
Fig. 1. Measurement setup. Magnetization, M (Gauss) 1 5-5 h 3h 1h 5h 1h h 4h Magnetization, M (Gauss) 15 1 5-5 -1 h 8h 3h 85h 135h 3h 33h -1 - -15-1 -5 5 1 15-15 - -15-1 -5 5 1 15 Magnetic Field, H (koe) Magnetic field, H (koe) (a) Inconel alloy 6 heat treated at 873K (b) SUS34H heat treated at 973K Fig. Magnetization curves for specimens with heat treatment. 3. Measurements A magnetic field sensor scanned over the specimens after magnetization to investigate an applicability of the technique for a practical application. A hall senor (Arepoc HHP-S series), was adopted to detect surface magnetic flux density, which reflects the amount of magnetization inside a specimen, and to evaluate the degree of chromium depletion of specimens. Fig. 1 shows the measurement setup to scan a hall sensor over a specimen. The active area of hall sensor has dimensions of µm x µm and detects the component of magnetic flux density perpendicular to the surface of the specimen. The origin is the center of the specimen and width, longitudinal and perpendicular directions are defined as the x-, y- and z- directions, respectively. Before measurement, the specimens were magnetized with the particular direction using VSM and the sensor scanned along with x- or y- direction. The combination of magnetizing and scanning direction is summarized in Table. 4. Experimental Results and Discussion Fig. shows the magnetization curves for 6 alloy and SUS34H measured by VSM with maximum applied field of koe (1.6 MA/m), when specimens were heat treated. These curves were evaluated at room temperature. The magnetization curves show paramagnetic property for both materials before heat treatment ( h). The susceptibilities are 4.9x1-3 and.8x1-3 for 6 alloy and SUS34H, respectively. The magnetization curves become nonlinear with increasing heat treatment time; the maximum magnetization increases up to hours heat treatment and then decreases for 6 alloy, whereas it increases monotonically up to 33 hours for SUS34H. For SUS34S&L, the apparent changes in magnetization were not observed during heat treatment. Fig. 3 shows the images of ferromagnetic phase distribution obtained by a magnetic 3
Table. Combination of magnetization direction and scanning direction. magnetizing scanning (a) x x y = (b) x y x = (c) y x y = (d) y y x = (e) z x y = (f) z y x = (a) before heat treatment (b) 1 hours Fig. 3. MFM images for Inconel 6 before and after heat treatment of 1 hours at 873K. force microscopy (MFM) for 6 alloy. No ferromagnetic area appears on the image of the specimen before heat treatment ( h), while the image for 1 hours heat treatment shows clear ferromagnetic phases which correspond to grain boundaries. MFM measurement may be a strong tool for evaluation of chromium depletion zone, i.e., sensitization, however, it is not applicable to the practical use. Although a transformation into magnetism occurs in quite local area, it is reflected on the averaging magnetic properties of the specimens as shown in the magnetization curves obtained by VSM measurement. Therefore, a magnetic field sensor is an expedient tool for evaluating magnetic properties of heat treated specimens. Fig. 4 (a) (f) show the magnetic flux density distribution obtained by scanning the sensor over the surface of the specimen for Inconel 6 alloy before and after heat treatment with the combination of magnetization direction and scanning direction in Table. The magnetic flux density distribution is almost zero for the specimens before heat treatment in the case of all combinations. This is consistent with the fact that the specimen is paramagnetic. In the case of (a) and (d), i.e., the scanning direction is parallel to the magnetizing direction, the intensity of magnetic flux density shows peaks only near the edges and becomes nearly zero at the centre of the specimen. This is because magnetic pole exists at the edge of the specimen. In the case of (b) and (c), the scanning direction is perpendicular to the magnetizing direction and the coordinates of the perpendicular axis to the scanning axis is zero; the magnetic flux density is zero and has no distribution. The scanning directions are parallel to in-plane where the magnetization exists in the cases of (a) (d). When the specimens were magnetized with the direction perpendicular to their surface before measurement, i.e. cases (e) and (f), the magnetic flux density is almost constant above the specimen, though it has slight distribution near edges of specimens. From the results mentioned above, it is suitable to magnetize specimen perpendicular to its surface. Fig. 5 shows the results of scanning the sensor over the surface of the specimen magnetized perpendicular to the surface of specimens (z-direction) with heat treatments. The scanning direction is parallel to the longitudinal direction (y-direction). Fig. 6 plots the changes in the magnetic flux density obtained from the results in Fig. 5 against the heat treatment time for Inconel 6 and SUS34H. As a reference, the saturation magnetization 4
(a) x-direction (b) y-direction (c) x-direction (d) y-direction (e) x-direction (f) y-direction Fig. 4. Distribution of magnetic flux density on surface of Inconel 6 alloy with heat treatment. obtained from the VSM measurement is also plotted. The saturation magnetization is obtained by the subtraction of paramagnetic component from maximum magnetization. The behaviors of changes in the magnetic flux density detected by hall sensor are consistent with the results of magnetization obtained by the VSM. For example, the magnetic flux density increases with elapsing heat treatment time up to hours and then decreases, followed by disappearance of ferromagnetic properties for Inconel 6. On the other hand, the magnetic flux density increases monotonically with heat treatment time for SUS34H, and both saturation magnetization and leakage magnetic flux density is constant before and after heat treatment with 33 hours. Consequently, the combination mentioned above is optimized for the detection of sensitization using a magnetic field sensor. In a practical use, steam generator tubing usually does not include the edge parts, therefore we can expect the uniform distribution of magnetic flux density reflecting the degree of transformation into 5
Magnetic flux density (G) 1.5 1.5 h 3h 1h 5h 1h h 4h -.5-1 -5 5 1-1 -5 5 1 Position y (mm) Position y (mm) (a) Inconel 6, 873K (b) SUS34 H, 973K Fig. 5. Distribution of magnetic flux density on surface of specimens with heat treatment. Magnetic flux density (G) 8 6 4 h 3h 8h 135h 33h 3 3 1 1 Saturation magnetization M s (G) 5 15 1 5 M s Hall sensor.5 1.5 1.5 Magnetic flux density (G) 1 1 1 1.1 1 1 1 1 Heat treatment time (h) Heat treatment time (h) (a) Inconel 6, 873K (b) SUS34, 973K Fig. 6. Relations between saturation magnetization, leakage magnetic flux density and heat treatment time. Saturation magnetization M s (G) 8 6 4 M s H S L Hall sensor H S L 8 6 4 Magnetic flux density (G) ferromagnetic phase. 5. Conclusion A hall sensor scanned over the specimens and successfully detected the change in magnetic flux density on the surface of the specimen. The changes in the magnetic flux density are consistent with the saturation magnetization evaluated by the VSM. This change is related to the degree of chromium depletion. Thus, a potential of magnetic NDE for sensitization due to heat treatment of Inconel 6 alloy and SUS34 was revealed. Acknowledgement This research was partially supported by a Grant-in-Aid for Scientific Research (B), Grant No. 36416, from Japan Society for the Promotion of Science and carried out in part at the International Research Center for Nuclear Materials Science, Institute for Materials Research, Tohoku University. References [1] M. Kowaka, H. Nagano, T. Kubo, Y. Okada, M. Yagi, O. Takaba, T. Yonezawa, K. Arioka, Effect of Heat Treatment on The Susceptibility to Stress Corrosion Cracking of Alloy 6, Nuclear Technologies, Vol. 55, pp. 394-44, 1981. 6
[] J. J. Kai, C. H. Tsai, G. P. Yu, The IGSCC sensitization, and microstructure study of Alloys 6 and 69, Nuclear Engineering and Design, Vol. 144, pp. 449-457, 1993. [3] J. J. Kai, C. H. Tsai, T. A. Huang, M. N. Liu, The Effects of Heat Treatment on the Sensitization and SCC Behavior of INCONEL 6 Alloy, Metallurgical Trans., Vol. A, pp. 177-188, 1989. [4] W. E. Mayo, Predicting IGSCC/IGA susceptibility of Ni-Cr-Fe alloys by modelling of grain boundary chromium depletion, Mater. Sci. Eng. Vol. A3, pp. 19-139, 1997. [5] J. D. Wang, D. Gan, Effect of grain boundary Carbides on the Mechanical Properties of Inconel 6, Mater. Chem. Phys., Vol. 7, pp. 1418, 1. [6] W. van Gestel, Girth weld failure in 13Cr sweet wet gas flow lines, CORROSION/4, paper no. 4141, 4. [7] T. Akiyama, T. Terasaki, Prediction of Sensitization and Low Temperature Sensitization (LTS) to the Intergranular Corrosion of Austenitic Stainless Steel, J. Jpn. Inst. Metal. Mater., Vol 5, pp. 37-335, 1988. [8] S. M. Bruemmer, L. A. Charlot, Development of grain boundary chromium depletion in type 34 and 316 stainless steels, Scripta Metallurgica, Vol., pp. 119-14, 1986. [9] H. Shaikh, N. Sivaibharasi, B. Sasi, T. Anita, R. Amirthalingam, B.P.C. Rao, T. Jayakumar, H. S. Khatak, Baldev Raj, Use of eddy current testing method in detection and evaluation of sensitisation and intergranular corrosion in austenitic stainless steels, Corrosion Sci., Vol. 48, pp. 146148, 6. [1] R. Oikawa, T. Uchimoto, T. Takagi, R. Urayama, Y. Nemoto, S. Takaya, S. Keyakida, Evaluation of susceptibility to stress corrosion cracking based on non-linear eddy current method, Int. J. Appl. Electromagn. Mech., Vol. 33, pp. 133-138, 1. [11] Y. Okada, K. Yoshikawa, T. Yukitoshi, Measurement of Sensitization Behavior in Ni-Based Alloy 6 by means of Magnetic Property, J. Jpn. Inst. Metals, Vol. 45, pp. 496-5, 1981. [1] S. Takahashi, Y. Sato, Y. Kamada, T. Abe, Study of chromium depletion by magnetic method in Ni-based alloys, J. Magn. Magn. Mater., Vol. 69, pp. 139-149, 4. [13] Y. Kamada, T. Mikami, S. Takahashi, H. Kikuchi, S. Kobayashi and K. Ara, Compositional dependence of magnetic properties on thermally sensitized austenitic stainless steels, J. Magn. Magn. Mater., Vol. 31, pp. 856-858, 7. [14] H. Kikuchi, H. Takahashi, H. Yanagiwara, T. Murakami Relationship between ferromagnetic properties and grain size of Inconel alloy 6, J. Magn. Magn. Mater., Vol. 381, pp. 56-64, 15. [15] H. Yanagiwara, T. Murakami, H. Kikuchi, Relationship between sensitization and magnetic characteristics in SUS34 stainless steel, Int. J. Appl. Electromagn. Mech., in press. 7