ASTM A335 Chrome Moly Pipe By Mr. Sum Xu ASTM A335 Pipe (ASME S/A335, Chrome-Moly) is a seamless ferritic Alloy-Steel Pipe for high temperature service. Welcome to Sunny Steel Enterprise Ltd. Sunny Steel provide a wide range of steel products as Steel pipes, Seamless tube and seamless pipes, Alloy pipes, Pipe fittings, Composite steel pipe used in the industry, construction etc. You can get in touch by telephone, post, online or E-mail. Please check the help section first to see if your question may be answered there. Tel.: +8621 3378 0199 E-mail:sales@sunnysteel.com Http://www.sunnysteel.com
ASTM A335 Chrome Moly Pipe ASTM A335 Pipe (ASME S/A335, Chrome-Moly) is a seamless ferritic Alloy-Steel Pipe for high temperature service. Pipe ordered to this specification shall be suitable for bending, flanging (vans toning), and similar forming operations, and for fusion welding. Sometimes referred to as P Grade, chrome moly pipe is popular in P-Grades P5, P9, P11, P22, and P91. ASTM A335 standard is issued under the fixed designation A 335/A 335M; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. The most common use of grades P11, P22, and P91 is in the power industry and petro-chemical plants, Grades P5 and P9 are commonly used in refineries. Sunny Steel Supply stocks a full range of the following A335 pipe grades: Grades: ASTM A335 P5, P9, P11, P-22, and P91 Sizes NPS 1/4'' to NPS 24'' Wall Thickness - Schedules 40 through 160, STD, XS, XXS. Unscheduled heavy wall pipe thicknesses available up to 4 inches. It also enhances the corrosion resistance of steel, and inhibits pitting. Chromium (or chrome) is the essential constituent of stainless steel. Any steel with 12% or more Chrome is considered stainless. Chrome is virtually irreplaceable in resisting oxidation at elevated temperatures. Chrome raises the tensile, yield, and hardness at room temperatures. The composition chrome moly alloy steel pipe make it ideal for use in power plants, refineries, petro chemical plants, and oil field services where fluids and gases are transported at extremely high temperatures and pressures.
Chemical Composition: Grade Carbon Manganese Phosphorous,max Sulfur, max Silicon Molybdenum ASTM A335 P5 0.15max 0.30-0.60 0.025 0.025 0.50max 0.45-0.65 ASTM A335 P9 0.15max 0.30-0.60 0.025 0.025 0.25-1.00 0.90-1.10 ASTM A335 P11 0.05-0.15 0.30-0.60 0.025 0.025 0.50-1.00 0.44-0.65 ASTM A335 P22 0.05-0.15 0.30-0.60 0.025 0.025 0.50max 0.87-1.13 ASTM A335 P91 0.08-0.12 0.30-0.60 0.020 0.010 0.20-0.50 0.85-1.05 Zr 0.01 max V 0.18-0.25 N 0.03-0.07 Ni 0.40 max Al 0.02 max Cb 0.06-0.10 Ti 0.01 max Tensile Requirements Tensile min., psi Strength, P-5 P-9 P-11 P-22 P-91 P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC]. ksi 60 60 60 60 85 MPa 415 415 415 415 585 Yield Strength, min., psi ksi 30 30 30 30 60 MPa 205 205 205 205 415 Mechanical Properties Mechanical properties P1,P2 P12 P23 P91 P92,P11 P122 Tensile strength 380 415 510 585 620 620 Yield strength 205 220 400 415 440 400 A335 is often called chrome moly pipe because of the chemical makeup of Molybdenum (Mo) and Chromium (Cr). Molybdenum increases the strength of steel as well as the elastic limit, resistance to wear, impact qualities, and hardenability. Moly increases the resistance to softening, restrains grain growth and makes chromium steel less susceptible to embrittlement. Moly is the most effective single additive that increases high temperature creep strength. Recommended ASTM A335 alloy pipes/tubes as below:
Collect Steel pipe and fitting Resources ASTM A335 P9 alloy pipe The range of ASTM A335 P9 seamless alloy steel pipe sizes that may be examined by each method shall be subjected... ASTM A335 P11 alloy pipe ASTM A335 P11 is the part of ASTM A335, the pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding. A335 P22 alloy pipe ASTM A335 P22 is the part of ASTM A335, the pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding.
A335 P91 alloy pipe ASTM A335 P91 is the part of ASTM A335, the pipe shall be suitable for bending, flanging... ASTM A335 P92 alloy pipes ASTM A335 P92 pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding. A335 P5 High pressure pipes The range of ASTM A335 P5 pipe sizes that may be examined by each method shall be subjected to...
Heat Treatment A / N+T N+T / Q+T N+T Material & Manufacture Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below. Heat Treatment Requirements Heat Treatment Type Grade P5, P9, P11, and P22 A335 P5 (b, Full or Isothermal Annea c) l Normalizing Temperature Range F [C] Subcritical Annealing or Temp ering Temperature Range F [C] Normalize and Temper ***** 1250 [675] A335 P9 Subcritical Anneal (P5c only) Full or Isothermal Annea l ***** 1325 1375 [715-745] Normalize and Temper ***** 1250 [675] A335 P11 Full or Isothermal Annea l Normalize and Temper ***** 1200 [650] A335 P22 Full or Isothermal Annea l Normalize and Temper ***** 1250 [675] A335 P91 Normalize and Temper 1900-1975 [1040-1080] 1350-1470 [730-800] Quench and Temper 1900-1975 [1040-1080] 1350-1470 [730-800] Permissible Variation in Wall Thickness NPS [DN] Designator Tolerance, % from Specified Over Under 1/8 to 2 1/2 [6 to 65] incl., all t/d rati os 20.0% 12.5% Above 2 1/2 [65], t/d < or = 5% 22.5% 12.5% Above 2 1/2 [65], t/d > 5% 15.0% 12.5% (t = Specified Wall Thickness; D = Specified Outside Diameter)
Elongation Requirements Calculated Minimum Elongation Values Elongation in 2 in. or 50 mm, min % Wall Thickness P5, P9, P11, P22 P91 in. mm Longitudinal Transverse Longitudinal 5/16 (0.312) 8 30 20 20 9/32 (0.281) 7.2 28 19 19 1/4 (0.250) 6.4 27 18 18 7/32 (0.219) 5.6 26 17 3/16 (0.188) 4.8 24 16 5/32 (0.156) 4 22 15 7/8 (0.125) 3.2 21 14 3/32 (0.094) 2.4 20 13 1/18 (0.062) 1.6 18 12 Permissible Variations in Outside Diameter Outside Diameter at any point shall not vary from standard specified more than: NPS [DN] Designator Over Under in. mm in. mm 1/8 to 1 1/2 [6 to 40], incl. 1/64 (0.015) 0.40 1/64 (0.015) 0.40 Over 1 1/2 to 4 [40 to 100], incl. 1/32 (0.031) 0.79 1/32 (0.031) 0.79 Over 4 to 8 [100 to 200], incl. 1/16 (0.062) 1.59 1/32 (0.031) 0.79 Over 8 to 12 [200 to 300], incl. 3/32 (0.093) 2.38 1/32 (0.031) 0.79 Over 12 [300] +/- 1% of the specified outside diameter
Ordering Information Orders for material under this specification should include the following, as required, to describe the desired material adequately: Quantity Name of material Grade Manufacturer Feet, meters, or number of lengths Seamless Alloy Steel Pipe P5, P9, P11, P22, P91 Hot-finished or cold-drawn Size using one of the following: NPS and Schedule Number Outside Diameter and Nominal Wall Thickness Outside Diameter and Minimum Wall Thickness Inside Diameter and Nominal Wall Thickness Inside Diameter and Minimum Wall Thickness Length Specific or Random End Finish Mechanical Tests Specified Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested. For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe. Notes for Hardness Test: P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC]. Notes for Bend Test: For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test. Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser. The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.
Hydrostatic Test The inside diameter of the bend shall be 1 inch [25 mm]. Each length of pipe shall be Hydro tested, at option of manufacture nondestructive electric testing can be used. Referenced Documents A999/A999M Specification for General Requirements for Alloy and Stainless Steel Pipe E213 Practice for Ultrasonic Examination of Metal Pipe and Tubing E309 Practice for Eddy-Current Examination of Steel Tubular Products Using Magnetic Saturation E381 Method of Macroetch Testing Steel Bars, Billets, Blooms, and Forgings E527 Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS) E570 Practice for Flux Leakage Examination of Ferromagnetic Steel Tubular Products B36.10M Welded and Seamless Wrought Steel Pipe SAE J 1086 Practice for Numbering Metals and Alloys (UNS) SNT-TC-1A Recommended Practice for Nondestructive Personnel Qualification and Certification Read more information of seamless steel pipes European Standards for steel ASTM Standards for steel pipes JIS Seamless Pipe Tubes for Mechanical and Automobile ASTM A335 Pipe Specifications ASTM A333 Pipe Specifications ASTM A213M-09 Standard Specication How to packing the seamless pipe Tubes in small calibers for boilers and petro chemical industry Get in Touch If you are interested in our products or cooperating with us, even having a comment or a suggestion please contact us now, for more detailed information. Tel.: +8621 3378 0199 E-mail:sales@sunnysteel.com -------------- www.sunnysteel.com --------------