MICROSTRUCTURE AND MECHANICAL PROPERTIES COMPARISON OF 316L PARTS PRODUCED BY DIFFERENT ADDITIVE MANUFACTURING PROCESSES

Similar documents
Electron Beam Melted (EBM) Co-Cr-Mo Alloy for Orthopaedic Implant Applications Abstract Introduction The Electron Beam Melting Process

POROSITY DEVELOPMENT AND CRACKING BEHAVIOR OF Al-Zn-Mg-Cu ALLOYS FABRICATED BY SELECTIVE LASER MELTING

EFFECT OF SCANNING METHODS IN THE SELECTIVE LASER MELTING OF 316L/TiC NANOCOMPOSITIES

Mechanical property evaluation of Ti-6Al-4V parts made using Electron Beam Melting

Producing Metal Parts

DEVELOPMENT OF A MARAGING STEEL POWDER FOR ADDITIVE MANUFACTURING. Simon Hoeges GKN Sinter Metals Engineering GmbH Radevormwald, Germany

Y. Zhou, X. Zhou, Q. Teng, Q.S. Wei, Y.S. Shi

Solidification Morphology Analysis of SLM of Cu Powder

Crack Prevention in NiCr-Alloys when Processed by AM (L-PB) William Jarosinski March 8, 2017

Microstructural Investigation of Direct Metal Deposition of H13 Steel on High Strength Copper Substrate

Estimation of Dilution and Carbon Content of Laser Cladding on Stellite 6 Coatings Deposited on an AISI 316L Stainless Steel Substrate

Development of Novel EBSM System for High-Tech Material. Additive Manufacturing Research

Effect of Scan Pattern on the Microstructural Evolution of Inconel 625 during Selective Laser Melting

Injection Moulding and Heat Treatment of Ni-Cr-Si-B Alloy Powder

Material data sheet. EOS StainlessSteel 316L. Description

Material data sheet. EOS NickelAlloy HX. Description, application

CHARACTERIZATION OF THIN WALLED Ti-6Al-4V COMPONENTS PRODUCED VIA ELECTRON BEAM MELTING

Surface Characterization of Laser Polished Indirect-SLS Parts

The University of Texas at El Paso, El Paso, TX USA 2 W. M. Keck Center for 3-D Innovation

The effect of ER4043 and ER5356 filler metal on welded Al 7075 by metal inert gas welding

Direct Metal Laser Re-Melting (DMLR) of 316L Stainless Steel Powder Part 1: Analysis of Thin Wall Structures

Effect of Zn content on microstructure, mechanical properties and fracture behavior of Mg-Mn alloy

Effects of Powder Variation on the Microstructure and Tensile Strength of Ti6Al4V Parts Fabricated by Selective Laser Melting

Effects of holding pressure and process temperatures on the mechanical properties of moulded metallic parts

SINTERABILITY OF HIGH-SPEED STEELS M2, M3/2 AND T15

Uddeholm AM Corrax. Uddeholm AM Corrax

CHAPTER 2 - OBJECTIVES

CHROMESHIELD 22 STAINLESS STEEL

related to the welding of aluminium are due to its high thermal conductivity, high

Microstructure of Friction Stir Welded 6061 Aluminum Alloy

EOS StainlessSteel 17-4PH

Effects of Processing Parameters on the Mechanical Properties of CMSX-4 Additively Fabricated through Scanning Laser Epitaxy (SLE)

Microstructure and Strength Properties of Austenitic and Ferritic Stainless Steels When Brazed with Ni-Cr-P Amorphous Brazing Foils

Machinability Enhancement of PM Stainless Steels Using Easy-Machinable Stainless Steel Powder. Bo Hu, Roland T. Warzel III, Sydney Luk

THE STRUCTURE AND MECHANICAL PROPERTIES OF NiCrBSi COATINGS PREPARED BY LASER BEAM CLADDING

QUANTITATIVE MICROSTRUCTURE ANALYSIS OF DISPERSION STRENGTHENED Al-Al 4 C 3 MATERIAL BY EBSD TECHNIQUE

RAPID PATTERN BASED POWDER SINTERING TECHNIQUE AND RELATED SHRINKAGE CONTROL

Localized Corrosion of a 7075 Aluminum Alloy Exposed to KCl

Material data sheet - FlexLine

A R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume Issue 2 DOI: /amm

Results are presented in Table 1. The tube was fabricated from a Type 347 and no unusual conditions were noted.

Dynamic mechanical properties of AMmanufactured

Effect of Ti on Charpy Fracture Energy and Other Mechanical Properties of ASTM A 710 Grade B Cu-Precipitation-Strengthened Steel

Tensile Strength and Pseudo-elasticity of YAG Laser Spot Melted Ti-Ni Shape Memory Alloy Wires

Effect of Precipitation Hardening on Microstructural Characteristics of 15-5 Ph Steel

REVIEW ON POWDER-BASED ELECTRON BEAM ADDITIVE MANUFACTURING TECHNOLOGY. The University of Alabama Tuscaloosa, AL 35487

Structure and properties of the gradient tool materials of unalloyed steel matrix reinforced with HS6-5-2 high-speed steel

Microstructure Study of Diffusion Bonding of Centrifuged Structural Steel-Bronze

STRESS CORROSION CRACKING OF STAINLESS STEELS IN HIGH PRESSURE ALKALINE ELECTROLYSERS

SEGREGATION BEHAVIOR OF PHOSPHORUS AND ITS EFFECT ON MICROSTRUCTURE AND MECHANICAL PROPERTIES IN ALLOY SYSTEM Ni-Cr-Fe-Mo-Nb-Ti-Al*

Discover the variety of Metal Powders

LASER SURFACE MELTING OF 17-4 PH PRECIPITATION-HARDENABLE STAINLESS STEEL Paper 1203

Arch. Metall. Mater. 62 (2017), 2B,

The Microstructure and Mechanical Properties of Inconel 718 Fine Grain Ring Forging

Laser assisted Cold Spray

EFFECT OF DEFECTS ON FATIGUE TESTS OF AS-BUILT TI-6AL-4V PARTS FABRICATED BY SELECTIVE LASER MELTING

Keywords: Copper, laser additive manufacturing, process parameters, composition, thermal conductivity

MECHANICAL PROPERTIES OF PURE TITANIUM MODELS PROCESSED BY SELECTIVE LASER MELTING

The Many Facets and Complexities of 316L and the Effect on Properties

Microstructures and Properties of Recycled Composites Particle Reinforced Iron Matrix Functionally Graded Materials Fabricated by Centrifugal Casting

Precipitation of Laves phase Fe 2 Mo type in HSLA steel with copper addition and high content of molybdenum

EFFECT OF POST SINTERING THERMAL TREATMENTS ON DIMENSIONAL PRECISION AND MECHANICAL PROPERTIES IN SINTER-HARDENING PM STEELS

AM CORRAX. Uddeholm AM Corrax

Characterization of Titanium Alloy Friction Stir Butt-Welds TIMET 54M, ATI 425 and BOATI Standard Grain

Influence of Process Parameters in the Direct Metal Deposition of H13 Tool Steel on Copper Alloy Substrate

Evaluation of Direct Diode Laser Deposited Stainless Steel 316L on 4340 Steel Substrate for Aircraft Landing Gear Application

In the past a few years, TiAl-based intermetallics have been

CORROSION BEHAVIOR OF AUSTENITIC AND FERRITIC STEELS IN SUPERCRITICAL WATER

Printing Metals and Light Absorbing Ceramics, using the DLP method

AGING BEHAVIOR IN CO-CR-MO-C ALLOYS

OPERATOR BURDEN IN METAL ADDITIVE MANUFACTURING. A.M. Elliott, L. J. Love

I. Hajiannia 1 *, M. Shamanian 2, M. Kasiri 3 1,3

Heat treatment and effects of Cr and Ni in low alloy steel

PROPERTIES AND MICROSTRUCTURES OF SINTERED STAINLESS STEEL PREPARED FROM 304L AND 410L POWDERS

Development of creep-resistant magnesium casting alloys for high temperature automotive applications

Thermal ageing of nickel-base Alloy 690 TT

Characteristics of centrifugally cast GX25CrNiSi18-9 steel

MICROSTRUCTURAL CHARACTERIZATION OF AGE 625 ALLOY. G. F. Vander Voort, J. W. Bowman and R. B. Frank

Microstructure and properties of NiCrBSiC overlay coatings deposited by the plasma scanning process

GRAIN GROWTH MODELING FOR ADDITIVE MANUFACTURING OF NICKEL BASED SUPERALLOYS

Study on Effect of Welding Speed on Micro Structure and Mechanical Properties of Pulsed Current Micro Plasma Arc Welded Inconel 625 Sheets

Characterization of Coatings on Grey Cast Iron Fabricated by Hot-dipping in Pure Al, AlSi11 and AlTi5 Alloys

Material data sheet. EOS NickelAlloy IN625. Description, application

Characterization of Microstructure and Mechanical Properties of Direct Metal Laser Sintered 15-5 PH1 Stainless Steel Powders and Components

Stainless Steel & Stainless Steel Fasteners Chemical, Physical and Mechanical Properties

CORROSION PROPERTIES OF CERMET COATINGS SPRAYED BY HIGH-VELOCITY OXYGEN-FUEL. Dragos UŢU, Iosif HULKA, Viorel-Aurel ŞERBAN, Hannelore FILIPESCU

Effect of Molybdenum Content on Mechanical Properties of Sintered PM Steels. Candido Ruas, Sylvain St-Laurent Quebec Metal Powders Limited

CHALLENGES AND OPPORTUNITIES FOR ADDITIVE MANUFACTURING IN THE AUTOMOTIVE INDUSTRY. Paul J. Wolcott Ph.D. Body SMT Innovation

Material data sheet. EOS MaragingSteel MS1. Description

Material data sheet. EOS NickelAlloy IN625. Description

STUDIES ON MICROSTRUCTUREAND MECHANICAL PROPERTIES OFMODIFIED LM25 ALUMINIUM ALLOY

- HSS-Blade (EOS art.-no ) - 90 µm mesh for powder sieving recommended (EOS art.-no ) - Argon atmosphere

Characterization of microstructures and mechanical properties of Inconel 617/310 stainless steel dissimilar welds

Surface formation in direct chill (DC) casting of 6082 aluminium alloys

DIRECT SELECTIVE LASER SINTERING OF TOOL STEEL POWDERS TO HIGH DENSITY: PART B THE EFFECT ON MICROSTRUCTURAL EVOLUTION

VACUUM SINTERING AND SINTER-HARDENING OF Mo AND Ni LOW ALLOYED STEEL

Metallic Additive Manufacturing Process and Materials Development at the University of Sheffield

Investigation of direct metal laser sintering process Slavko Dolinšek

Transcription:

Solid Freeform Fabrication 2017: Proceedings of the 28th Annual International Solid Freeform Fabrication Symposium An Additive Manufacturing Conference MICROSTRUCTURE AND MECHANICAL PROPERTIES COMPARISON OF 316L PARTS PRODUCED BY DIFFERENT ADDITIVE MANUFACTURING PROCESSES Mihaela Nastac, Rick Lucas Andrew Klein ExOne, Irwin, PA Abstract 316L stainless steel alloy is well known for its corrosion resistance and combination of strength and ductility. By using direct metal additive manufacturing, 316L parts can be produced with volumes and complexity that were previously unachievable. Three of the major metal additive manufacturing technologies binder jetting, electron beam melting, and selective laser melting produce SS316L parts, but with different material properties and microstructures. This paper will examine the microstructure and mechanical properties differences between parts produced by the three methods and discuss recent advances to improve microstructure and mechanical performance of metallic alloy parts produced by additive manufacturing. Introduction A detailed comparison of three different additive manufacturing (AM) technologies in terms of microstructure and mechanical properties of a 316L stainless steel alloy is presented in this study. The selected AM technologies are: (1) Binder Jetting Additive Manufacturing (BJ), (2) Electron Beam Melting (or EBM) and (3) Direct Metal Laser Sintering (DMLS). These main technologies are widely used to fabricate parts for various commercial applications related to energy, automobile, and aerospace industries. The BJ technology, which was developed by Exone, was employed to produce the samples, which were then evaluated for microstructure and mechanical properties in this study. The EBM Samples were supplied by Oak Ridge NL, while the DMLS samples were produced by Proto labs. Experimental Procedure for BJ Process Both the EBM and the DMLS technologies are presented in the literature [1-3]. BJ technology is described in the following paragraphs. BJ technology is an additive manufacturing process capable of printing relatively large parts. The process consists of selectively depositing a liquid binder to join powder particles forming a voxel as shown in Fig. 1a. Figure 1b illustrates the deposition of the liquid binder during the printing process. 332

(a) (b) Figure 1. The formation of voxels in the BJ process (a) and the printer head dispending the liquid binder during the printing process (b). As the print-head passes over a layer of powder, binder is deposited onto the powder. The job-box lowers and a subsequent layer of powder is spread; the print-head passes again, depositing binder onto the second layer of powder. The part develops through the layering of powder and binder, until a near-net shape object is achieved. While other additive manufacturing techniques, produce parts with thermallyinduced residual stresses and distortions due to large thermal gradients, BJ does not employ heat during the build process, therefore the parts are virtually stress free at the end of the printed cycle. During the printing process, the parts are supported by the loose powder in the job box, therefore eliminating the need for a build plate. After the part is printed, it undergoes a curing and sintering cycle to become the finished part. The samples used in this study were created using this approach. An Innovent ExOne powder bed binder jet printer was used to produce 316L stainless steel samples with the following printing parameters: layer height of 50 μm, recoat speed of 150 mm/s, oscillator speed of 2200 rpm, roller rotation speed of 250 rpm, roller traverse speed of 8 mm/s, and drying speed of 7 mm/s. The 316L powder chemical composition provided by the manufacturer is given in Table 1. The water based binder used in this study is made of ethylene glycol monobutyl ether (CAS # 111-76-2) and ethylene glycol (CAS #107-21-1) [4]. Table 1. Chemical composition of 316L alloy Element Cr Ni Mo Mn Si P C S Fe Chemical composition [wt. %] 16.0-18.0 10.0-14.0 2.0-3.0 Max 2 Max 1 Max 0.04 Max 0.03 Max 0.03 balance In order to perform a microstructural analysis of the processed samples, sections were cut from the specimens, mounted, ground and polished. After surface preparations, the samples were etched with a Glyceregia solution and then optical microscopy (OM) micrographs were taken. Microstructural characterizations and compositional analyses were also conducted using Scanning Electron Microscopy (SEM) equipped with Energy Dispersive X-ray Spectroscopy. Experimental Results and Discussion Microstructure characterizations of the 316L stainless steel sample produced via BJ process were performed on the etched surface using OM and SEM. The chemical composition of the precipitates was determined by an Energy Dispersive X-Ray Spectroscopy (EDS) detector (OmegaMax Express SEM/EDS). The OM micrographs, taken on the polished surface (Figure 2 333

(a) and (b)), reveal a largely compact material with few fine pores, which are randomly distributed. The microstructure of the etched sample is shown in Fig. 3 (a), (b) and (c). The specimen consists of an equiaxed grain structure, with a grain size ranging from 30µm to 60µm. The precipitates are primarily observed at the grain boundaries. Few precipitates are also found inside the grains. The EDS elemental analysis for different areas of the sample are consistent with the SS316L austenite matrix as well as with some precipitates with a higher amount of Carbon and Oxygen, as it can be observed from Fig. 5 (b) and Table 2, location #7. Figure 2. OM micrographs (50x) of the 316L polished sample showing porosity distribution. (a) (b) (c) Figure 3. OM micrographs of the 316L sample in as etched condition (Glyceregia etchant): a) 100x; b) 200x; c) 500x. 334

Figure 4. SEM image of the 316L BJ etched sample. (a): EDS elemental analysis 1 (b): EDS Elemental analysis 7 Figure 5. 316L BJ; EDS elemental spectrum analysis (a) location 1 (b) location 7. Table 2. Compositional analysis (in wt. %) of the 7 points selected on the 316L BJ sample, as shown in Fig. 4 Typical mechanical properties of the as sintered 316L BJ components are shown in Table 3. The values meet and exceed the requirements included in the B-883-15, Standard Specification for Metal Injection Molded Materials: MIM-316L (as sintered) [5]. 335

Material Table 3. Typical mechanical properties for 316L B Ultimate Yield Elongation at Hardness, strength, Strength, Break, % HRB MPa MPa Density, g/cm³ 316L 517 214 43 66 7.7 Comparison of microstructure and mechanical properties of BJ, EBM, and DMLS Samples The mechanical properties of the processed samples are influenced by the size, shape and distribution of the pores, as well as by the size and shape of the grains. Typical values for the mechanical properties of the 316L alloy produced by the BJ, EBM, and DMLS processes, as well as the B883 Standard Specification for Metal Injection Molded Materials, are shown in Table 4. Additive Manufacturing Process Ultimate strength, MPa Table 4: 316L mechanical properties [1, 5, 6]. Yield Elongation at Strength, Break, % MPa Hardness, HRB Density, g/cm³ BJ 517 214 43 66 7.7 EBM [1] 509 ± 3 253 ± 3 59 ± 3 DMLS [5] 482 172 30 77 MIM [6] 450 140 40 67 7.6 The optical micrographs of the EBM 316L stainless steel sample are shown in Figure 6 (a) and (b). The mounted specimen was polished and then etched. The as polished surface reveals a largely compact material with few relative large pores as well as fine pores, randomly distributed. The microstructure of the etched sample shown in Fig. 7 (a) and (b) reveals tiered microstructures, including columnar grain structure, with a grain size in the range of 300-400µm. Fig. 8 shows the point locations of the EDS elemental analysis and Fig. 9 (a); (b), the EDS elemental analysis spectrum for locations #4 and #7. The complete compositional analysis (in wt. %) of the points are shown in Table 5. The chemical composition of the points indicates consistency with the SS316L matrix, as well as some Carbon and Oxygen rich areas (Table 5, reading #6 and #7). 336

Figure 6. OM micrographs (50x) of the 316L EBM sample in as polished condition. (a) (b) Figure 7. OM micrographs of the 316L EBM sample etched with the Glyceregia etchant: (a) 100x; (b) 200x. Figure 8. SEM image of the 316L EBM etched sample. 337

(a): EDS elemental analysis 4 (b): EDS elemental analysis 7 Figure 9: 316L EBM sample: EDS elemental spectrum analysis: (a) location 4 (b) location 7. Table 5. Compositional analysis (in wt. %), for the 7 points selected on the EBM 316L sample, as shown in Fig. 8. The OM micrographs of the DMLS 316L are shown in Fig. 10 (a) and (b) in as polished condition, and in Fig. 11 (a) and (b) in as etched condition. Generally, the OM micrographs show a similar tiered microstructure as the EBM sample, with a similar columnar grain structure. The grain size is in the range of 80µm to 150µm. A few larger pores as well as fine pores exist inside the specimen. Figure 10. OM micrographs (50x) of 316L DMLS sample in as polished condition. 338

(a) (b) Figure 11. 316L DMLS sample in as etched condition (Glyceregia etchant); optical microscopy, (a) 100x; (b) 200x. Figure 12. SEM image of the 316L DMLS etched sample. (a): EDS elemental analysis 1 (b): EDS elemental analysis 2 Figure 13: 316L DMLS sample: EDS elemental spectrum analysis: (a) location 1 (b) location 2 339

Fig. 12 shows the point locations of the EDS elemental analysis and Fig. 13 (a) and (b), the EDS elemental analysis spectrum for locations #1 and #2. The complete compositional analysis (in wt. %) of the points are shown in Table 6. Table 6. Compositional analysis (in wt. %), of the 7 points selected on the 316L DMLS sample, as shown in Fig. 12 Conclusions Microstructure characterization and analysis of the 316L stainless steel alloy produced by 3 different AM processes was performed in this study. The data showed that while the EBM and DMLS processes are conducive to comparable columnar grain microstructures, the BJ process is generating a relatively fine equiaxed grain microstructure, as illustrated in Fig. 14. The size and the shape of the grains are essential factors in defining the mechanical properties of the components. An equiaxed grain structure is known to produce isotropic properties and therefore, regardless of the built direction, the components are displaying similar mechanical properties in X, Y and Z directions. Another advantage of the BJ process as related to the 316L alloy is the lack of chemical segregation at the grain boundary, since the process does not involve melting and solidification. This is another key factor that together with an isotropic microstructure will lead to uniform and improved mechanical properties of the final BJ product. (a) (b) (c) Figure 14. OM micrographs of the 316L samples in etched condition (Glyceregia etchant): (a) BJ 50x; (b) EBM 50x; (c) DMLS 50x; 340

Acknowledgement The authors would like to acknowledge the producers of the EBAM (Oak Ridge NL) and the SLM (Proto-labs) samples as well as Janusz Plucinski for his valuable help with the SEM images and the EDS elemental analysis. References [1] Y. Zhong, L.E. Rannar, L. Liu, A. Koptyug, S. Wikman, J. Olsen, D. Cui, Z. Shen, Additive manufacturing of 316L stainless steel by electron beam melting for nuclear fusion applications, Journal of Nuclear Materials, vol. 486, 2017, pp. 234-245. [2] E. Fitzgerald, W. Everhart, The Effect of Location on the Structure and Mechanical Properties of Selective Laser Melted 316L Stainless Steel;, Solid Freeform Fabrication 2016: Proceedings of the 26th Annual International Solid Freeform Fabrication Symposium An Additive Manufacturing Conference, 2016, pp. 1-10. [3] L.E. Murr, E. Martinez, S.M. Gaytan, D.A. Ramirez, B.I. Machado, P.W. Shindo, J.L. Martinez, F. Medina, J. Wooten, D. Ciscel, U. Ackelid, and R.B. Wicker, Microstructural Architecture, Microstructures and Mechanical Properties for a Nickel-Base Superalloy Fabricated by Electron Beam Melting, Metallurgical and Materials Transactions A, vol. 42A, 2011, pp. 3491-3508, DOI: 10.1007/s11661-011-0748-2. [4] A. Mostafaei, E. L. Stevens, E. T. Hughes, S. D. Biery, C. Hilla, M. Chmielus, Powder bed binder jet printed alloy 625: Densification, microstructure and mechanical properties, Materials and Design, vol. 108, 2016, pp. 126 135. [5] Direct Metal laser Sintering Stainless Steel 315L, Product Specification, ProtoLabs, website: https://www.stratasysdirect.com/wp-content/themes/stratasysdirect/files/materialdatasheets/direct_metal_laser_sintering/dmls-stainless-steel-316l-material-specifications.pdf [6] ASTM B883 Standard Specification for Metal Injection Molded Materials: https://www.astm.org/standards/b883.htm 341