is an acrylic copolymer emulsion designed for air dry and forced dry industrial coatings. can be formulated into economical coatings that exhibit an excellent balance of properties on metal, plastic and wood substrates. Delivery form: 42 % solids in water. Product characteristics Type - Acrylic emulsion Total solids, by volume, % - 40 % Weight per gallon 25 C - 8.64 lbs. as supplied Freeze/thaw stability - Keep from freezing Thermal stability - Satisfactory 52 C, one month Mechanical stability - Satisfactory Film properties/key Benefits - Block & Print Resistance - Adhesion to Plastics & Metals - Low VOC Demand - Very Fast Solvent Release - Rapid Hardness Development Recommendations for end-use - Suggested Markets: - General Metal & Plastic Coatings - DIY Flooring Product specifications Property Range Unit GAP Appearance Opaque liquid 0059 Total solids w/w 41 43 % 0025 ph 7.5 8.5 0016 Visc. Brookfield 25 C 10-500 mpa.s 0020 Sediment 1-1 max. 0.20 % 0005 Sediment straight max. 0.10 % Other product data Property Value Unit GAP MFFT 26 C 0011 Free monomer max. 2000 ppm 0118 VOC (theoretical) none % Acid value (on solid) ± 45 mgkoh/g 0095 Preservative(s): BIT (casno. 2634-33-5) 0.028 % 0222 Test methods Test methods (GAP) referred to in the table(s) are available on request. Storage guidelines The resin should be stored indoors in original, unopened, undamaged container in a dry place at storage temperature between 5-40 C. Exposure to direct sunlight should be avoided. Shelf life Under above mentioned storage conditions, the shelf life of the resin will be 12 months ex work. Page 1 of 11 Material safety A Material Safety Data Sheet for this product is available on request.
Page 2 of 11
Formulating Information Formulation Description WB-5024 WB-4213 WB-2103 Gray Concrete Sealer Brushing Lacquer Low VOC Red Oxide Primer Market Decorative Architectural Clears Industrial Metal Additional Resin NeoRez R-9649 None None Solids, Wt. % 50 33 47 VOC, g/l 191 246 149 Additive Selection Component Type Supplier Solvents DPnP DPnB EB PNB DPM Dow Chemical Lyondell Chemical Coalescing Requirements: The addition of coalescing solvents to is required in order to form a good film. Usually 18-22% co-solvent, on resin solids is common for adequate film formation. Flow Agents BYK 345 BYK Chemie Triton CF-10 Dow Chemical Surfynol 104DPM Air Products Defoamers Nalco 2301 Nalco Chemical Co. Page 3 of 11 Byk 024 Byk Chemie Foamaster 111 Foamaster W-220 Cognis Corporation Patco 519 Patco 520 Birko Corp, Patco Additives Dispersants Tamol 165A Rohm & Haas BYK 156 Byk Chemie
Formulating Information Continued Component Type Supplier Thickeners Acrysol RM 825 Acrysol TT-615 Acrysol RM-2020 DSX-1514 Rohm & Haas Cognis Corporation Neutralizing Agent AMP 95 Angus Chemical Biocide Proxel GXL Arch Chemical Resin Compatibility, Industrial Formulations * Blends weight % on resin solids % / % secondary resin 25/75 50/50 75/25 NeoCryl A-601 Hazy Hazy Hazy NeoCryl A-612 Hazy (1) Hazy (1) Hazy (1) NeoCryl A-614 Hazy Hazy Hazy NeoCryl A-622 Clear Clear Clear NeoCryl A-633 Clear Clear Clear NeoCryl A-639 Clear Clear Clear NeoCryl A-655 Clear Clear Clear NeoCryl A-6037 Hazy (1) Hazy (1) Clear NeoRez R-940 Clear Hazy Slight Hazy (1) NeoRez R-9409 Clear Clear Slight Hazy NeoRez R-960 Hazy Slight Hazy Slight Hazy NeoRez R-962 Hazy Hazy Hazy (1) NeoRez R-967 Hazy Hazy Hazy (1) Gritty Film * Formulation WB-2004, Clear Gloss Lacquer for Metal Page 4 of 11
Resin Compatibility, Clear Wood Brushing Lacquer Formulating Information Continued Blends weight % on resin solids % / % secondary resin 30/70 70/30 NeoRez R-9637 Very Slight Haze Clear NeoRez R-9679 Very Slight Haze Slight Haze NeoRez R-9403 Clear Clear NeoPac TM R-9009 Slight Haze Slight Haze NeoPac TM E-106 Clear Clear Storage Precaution is known to react with the zinc in some grades of galvanized steel. The result can be a build-up of gel on the bulk tank inner walls and/or absolute solidification in the valves/plumbing. Stainless steel is the recommended storage material for. If your current storage system is galvanized steel, a one (1) week standing jar test with the specific grade (type) of galvanized to be used will be a reasonable indicator. Drying Notes Film Formation Clear Lacquer Drying Stage Set to touch Dry to touch Through dry Time 30 minutes 45 minutes 2 hrs. 30 minutes 3 mil wet draw down on Leneta 7B, 70 o F & 50% RH Page 5 of 11
Drying Notes Continued Recoat Time For Architectural Clears on wood substrates, three to four hours is recommended between coats for quickest development of final film properties in a multi-coat application. General Physical Performance Clear Films Durability: General Test Conditions Results Imprint Resistance Glass, baked @ 140 o F for 1 hour & 1 lb. for 4 hours @ 140 o F 3.5 Rating 1-5, 5 = Best Yellowness Index QUV aged, A bulbs, 1 week ASTM 313 2.0 (4 on scale of 1-5, 5 = colourless) König Hardness Development Time König Osc 24 hours 45 48 hours 66 1 week 89 3 mil wet films, glass, dried at room temperature Page 6 of 11
Performance Properties of Formulation WB-2005 Gloss White Lacquer Durability: Industrial Metal Test Conditions Results Gloss 60 87 Hardness Pencil B König 59 Sward 28 Flexibility Conical Mandrel Passes Impact Resistance Direct, in-lbs. 40 Reverse, in-lbs. 4 Test, Adhesion Conditions Results Plastics Nylon 6,6 Noryl N 190 Noryl 1222 Noryl GTX-910 Noryl FN-215 Styron 6075 Styron 484 ABS KJW Metals B-1000 QD Brass Hot Dipped Galvanized Steel x Aluminum Page 7 of 11
Durability: Industrial Metal Continued Performance Properties of Formulation, WB-2005 Continued Salt Spray Resistance (B1000 panels, 1.0-1.2 DFT, 168 hours) Description Face Scribe Results Rusting Trace, 9 Blistering Few, #6,8 Undercutting 1/16" Rust Bleed V. Slight Blistering MD, #4,6 Humidity Resistance B1000 panels 1.0-1.2 DFT 168 hours Rusting V. Slight, #7 Blistering Dense, #8 Block Resistance 165 o F / 7 min. bake 140 o F / 2 psi / 1 hour block Hot Print Resistance 140 o F / 2 psi / 2 hours Page 8 of 11
NeoCryl A-6069 ph/viscosity Curve 1000 Viscosity, cps 100 Page 9 of 11 10 8 8.1 8.2 8.3 8.4 8.5 8.6 8.7 ph
Durability: Clear Wood Lacquers Resistance Properties 3 coats brush applied, maple, air dry 7 days Household Chemical Resistance & NeoPac TM E-106 70/30* & NeoPac TM E-106 30/70* Water 10 9 10 50% Ethanol 6 8 9 70% IPA 5 7 7 Fantastic 6 7 8 Formula 409 5 7 8 Windex 8 8 8 Mustard 6 6 7 Shoe Polish 2 2 1 Rating 1-10, 10 = Best Rating is average of 1hr. on and 1hr. off Black Heel Mark Resistance BHMR 1 3 3 Rating 1-5, 5 = Best * weight % on resin solids Page 10 of 11
Raw Material Suppliers Material Supplier Butyl Cellosolve Butyl Carbitol DPnB DPnP Triton CF-10 Acrysol TT-615 Acrysol RM-825 Patcote 519 Patcote 520 Dow Chemical www.dow.com Rohm & Haas Company www.rohmhaas.com Birko Corp., Patco Additives www.birkocorp.com Nalco 2301 Foamaster 111 Foamaster W-220 PNB DPM BYK 345 BYK 024 BYK 156 Surfynol 104DPM AMP 95 Proxel GXL Nalco Chemical Company www.nalco.com Cognis Corporation www.cognis.com Lyondell Chemical www.lyondell.com BYK Chemie www.byk.com. Air Products www.airproducts.com Angus Chemical www.dow.com/angus Arch Chemical www.archchemicals.com Page 11 of 11