From measurements errors to a new strain gauge design for composite materials

Similar documents
Fatigue behaviour of uni-directional flax fibre/epoxy composites

Joint and column behaviour of slotted cold-formed steel studs

DCB TEST SAMPLE DESIGN FOR MICRO-MECHANICAL TESTING

Fracture Testing of Honeycomb Core Sandwich Composites Using the DCB-UBM Test

Tensile and compression properties of hybrid composites A comparative study

Chapter 7. Finite Elements Model and Results

Date: Author: Torben K. Jacobsen. 2 Unidirectional reinforcement material (1258 g/m 2 ): Id Layer Unit Stitching. 0±1 (warp)

Compression fatigue of Wind Turbine Blade composites materials and damage mechanisms

Shrinkage Properties of Cement Stabilized Gravel

Gage Series Stress Analysis Gages

Working in a broad partnership in the Kenya Miniwind Project

Systematic Analysis of the Effects of Moulding Conditions on the Properties of Shape Memory Polymers

Supplementary Figures

Microstructure, Slip Systems and Yield Stress Anisotropy in Plastic Deformation

Design of Ultra High Performance Fiber Reinforced Concrete Shells Jepsen, Michael S.; Lambertsen, Søren Heide; Damkilde, Lars

Micromechanical Time-Lapse X-ray CT Study of Fatigue Damage in Uni-Directional Fibre Composites

Residual Stress Analysis in Injection Moulded Polycarbonate Samples

Evaluation of test methods used to characterize fiber reinforced cementitious composites

Quantitative analysis of pigment dispersion taking into account the full agglomerate size distribution

Tapering of Polymer Optical Fibers for Compound Parabolic Concentrator Fiber Tip Fabrication

CORRELATION BETWEEN EXPERIMENTAL RESULTS AND FINITE ELEMENT ANALYSIS OF A MODEL COMPOSITE CONTAINING AN INTERPHASE WITH KNOWN PROPERTIES

Characterization of Mechanical Properties of SiC/Ti-6Al-4V Metal Matrix Composite (MMC) Using Finite Element Method

Biogas Production from Energy Crops and Agriculture Residues

Experimental investigation of coating degradation during simultaneous acid and erosive particle exposure

Tensile and Compressive Test on Thickness-Reduced Steel Plate Repaired by CFRP Strand Sheet and Underwater Epoxy with Bond Defects

FIBRE ORIENTATION EFFECTS ON THE TENSILE PROPERTIES OF BIAXIAL CARBON/EPOXY NCF COMPOSITES

Assignment #1 Due Date 22 September 2009; 5PM Group I: Odd questions, Group II : Even questions

Analysis of composition and microstructural uniformity of hybrid glass/carbon fibre composites

Microstructural and hardness gradients in Cu processed by high pressure surface rolling

Reduced Ductility due to Local Variation in Material Properties for 3D-printed Components

Considering the Local Anisotropy of Short Fibre Reinforced Plastics: Validation on Specimen and Component

Effects of carbon fibres on the life cycle assessment of additively manufactured injection moulding inserts for rapid prototyping

Effects of carbon fibres on the life cycle assessment of additively manufactured injection moulding inserts for rapid prototyping

Microstructural and hardness gradients in Cu processed by high pressure surface rolling

Design for Plastic Ball Grid Array Solder Joint Reliability. S.-W. R. Lee, J. H. Lau*

Hansen solubility parameters for a carbon fiber/epoxy composite

Fundamental Course in Mechanical Processing of Materials. Exercises

Flexural behaviour of a polymeric foam/glass-fibre composite: FE modelling and experimental testing

MECHANICAL BEHAVIOR OF CARBON/STEEL HYBRID FIBER- REINFORCED COMPOSITES

Effect on deformation process of adding a copper core to multifilament MgB2 superconducting wire

A computational study of biaxial sheet metal testing: effect of different cruciform shapes on strain localization

Axial Tensile Testing of Single Fibres

FEA and Experimental Studies of Adaptive Composite Materials with SMA Wires

CHAPTER 4 EXPERIMENTAL ANALYSIS FOR A 2 IN, SCHEDULE 10 PIPE

EXPERIMENTAL ANALYSIS OF HYBRID CARBON FIBER COMPOSITE SPECIMEN

Finite element prediction of curing micro-residual stress distribution in polymeric composites considering hybrid interphase region

Effects of holding pressure and process temperatures on the mechanical properties of moulded metallic parts

Reaction to fire of glass/ hemp/ furan composites

Influence of moisture absorption on properties of fiber reinforced polyamide 6 composites

Chapter 4 MECHANICAL PROPERTIES OF MATERIAL. By: Ardiyansyah Syahrom

3. TEST METHOD FOR BOND PROPERTIES OF CONTINUOUS FIBER SHEETS TO CONCRETE (JSCE-E )

Modelling of the Residual Stress State in a New Type of Residual Stress Specimen

Crack growth monitoring in composite materials using embedded optical Fiber Bragg Grating sensor

JJMIE Jordan Journal of Mechanical and Industrial Engineering

ISO INTERNATIONAL STANDARD. Fibre-reinforced polymer (FRP) reinforcement of concrete Test methods Part 1: FRP bars and grids

Characteristic values of pultruded fibre composite sections for structural design

Replica casting technique for micro Fresnel lenses characterization

Investigation of influence of tab types on tensile strength of E-glass/epoxy fiber reinforced composite materials

Function-integrated GFRP sandwich roof structure Experimental validation of design

Process Simulation of Resistance Weld Bonding and Automotive Light-weight Materials

SIZE EFFECTS ON THE TENSILE AND FLEXURAL STRENGTH OF GFRP LAMINATES

Comparisons to Tests on Reinforced Concrete Members

STRENGTHENING EFFECTS OF CONCRETE FLEXURAL MEMBERS RETROFITTED WITH HYBRID FRP COMPOSITES. Abstract. Introduction

Using ncode DesignLife for Fatigue of Composite Structures

Nonlinear Models of Reinforced and Post-tensioned Concrete Beams

Benefits of interrelationships between climate change mitigation and adaptation a case study of replanting mangrove forests in Cambodia

CHAPTER 5 FINITE ELEMENT MODELLING

CE 221: MECHANICS OF SOLIDS I CHAPTER 3: MECHANICAL PROPERTIES OF MATERIALS

The Ductility Exhaustion Method For Static Strength Assessment of Fusion Structures

MECHANICAL PROPERTIES OF TRIAXIAL BRAIDED CARBON/EPOXY COMPOSITES

MICROMECHANICS OF ELASTO-PLASTIC FIBER PULL OUT OF ELASTIC MATRIX

A comparison of brazed metal and epoxied fibre Bragg grating strain sensors under high strain regimes

Metrological investigation of nanostructured polymer surfaces replication using atomic force microscopy

Electric vehicles or use of hydrogen in the Norwegian transport sector in 2050?

CAUSES OF ELONGATION IN REINFORCED CONCRETE BEAMS SUBJECTED TO CYCLIC LOADING

Evaluation of Polymer Wear Assessment Methods

CHAPTER 7 FINITE ELEMENT ANALYSIS

Chapter 7. Mechanical properties 7.1. Introduction 7.2. Stress-strain concepts and behaviour 7.3. Mechanical behaviour of metals 7.4.

Integrated electrical-mechanical analysis - The impact of power system on wind turbine design and vice versa

Carbon-fiber Reinforced Concrete with Short Aramid-fiber Interfacial Toughening

TOOL MATERIAL EFFECTS ON PROCESS INDUCED DEFORMATION OF COMPOSITE SPAR STRUCTURES

Fabrication and Analysis of Single lap joint Glass Fiber Reinforced Polymer Composite Materials

The Roskilde Domes 2011 and 2012

Introduction to Composite Materials

A notched cross weld tensile testing method for determining true stress strain curves for weldments

Inertial response from wind turbines: the impact on structural loads

Todd F. Shupe Associate Professor School of Renewable Natural Resources Louisiana State University AgCenter Baton Rouge, LA 70803

MECHANICAL PROPERTIES. (for metals)

Thickness determination of SMC replacing Sheet metals for Automobile roof

Low Strain Rate Testing Based on Drop Weight Impact Tester

DEVELOPMENT OF TEST METHODS FOR ADHESION MEASUREMENTS OF FLEXIBLE ELASTIC MATERIALS

Reeling-induced residual stress and its effect on the fracture behavior of pipes with through thickness cracks

State-estimation of wind power system of the Danish island of Bornholm

XFEM MODELLING OF TRANSVERSE CRACKING IN FIBRE REINFORCED COMPOSITES

Multi-objective optimization of die geometry in ingot forging

Hybrid FRP-concrete-steel double-skin tubular columns: Cyclic axial compression tests

Example 8 - Hopkinson Bar

Finite Element Analysis of a High Power Resistor

Transcription:

Downloaded from orbit.dtu.dk on: Jul 25, 2018 From measurements errors to a new strain gauge design for composite materials Mikkelsen, Lars Pilgaard; Salviato, Marco; Gili, Jacopo Published in: Proceedings of the 20th International Conference on Composite Materials Publication date: 2015 Document Version Publisher's PDF, also known as Version of record Link back to DTU Orbit Citation (APA): Mikkelsen, L. P., Salviato, M., & Gili, J. (2015). From measurements errors to a new strain gauge design for composite materials. In Proceedings of the 20th International Conference on Composite Materials ICCM20 Secretariat. General rights Copyright and moral rights for the publications made accessible in the public portal are retained by the authors and/or other copyright owners and it is a condition of accessing publications that users recognise and abide by the legal requirements associated with these rights. Users may download and print one copy of any publication from the public portal for the purpose of private study or research. You may not further distribute the material or use it for any profit-making activity or commercial gain You may freely distribute the URL identifying the publication in the public portal If you believe that this document breaches copyright please contact us providing details, and we will remove access to the work immediately and investigate your claim.

20 th International Conference on Composite Materials Copenhagen, 19-24 th July 2015 FROM MEASUREMENTS ERRORS TO A NEW STRAIN GAUGE DESIGN FOR COMPOSITE MATERIALS Lars P. Mikkelsen 1a, Marco Salviato 1b and Jacopo Gili 1c 1 Department of Wind Energy, Technical University of Denmark P.O. Box 49, Frederiksborgvej 399, DK-4000 Roskilde, Denmark a Email: lapm@dtu.dk, web page: http://www.dtu.dk b Email: s131574@student.dtu.dk, web page: http://www.dtu.dk c Email: jacopo.gili@gmail.com, web page: http://www.dtu.dk Keywords: Strain gauge, Strain measurements, Composites testing, Young modulus ABSTRACT Significant over-prediction of the material stiffness in the order of 1-10% for polymer based composites has been experimentally observed and numerical determined when using strain gauges for strain measurements instead of non-contact methods such as digital image correlation or less stiff methods such as clip-on extensometers. In the present work, this has been quantified through a numerical study for three different strain gauges. In addition, a significant effect of a thin polymer coating or biaxial layer in the erroneous using strain gauges has been observed. An erroneous which can be significantly decreased using an enhanced grid design of the measuring grid. 1 INTRODUCTION Determining the material stiffness require a precise strain measurement. Due to the price and ease of using, strain gauges are often used as the deformation measurement testing composites. Strain gauges are measuring the strain in the underlying material through an electrically resistance change in a measuring grid. A resistance change which are related to a strain value through a gauge factor supplied by the strain gauge manufacture together with the specific strain gauge batch. Nevertheless, used on composite materials with a material stiffness in the range of 3-35 GPa, a uni-directional strain gauge has been found to over-predicting the material stiffness with 1-9 %, see [1]. Based on finite element studies and digital image correlation measurements, this over-predictions are identified to be caused by a strain inhomogeneity introduced by a stiffness mismatch between the measurements grid on E=180GPa and the testing material. Despite a thickness of the measurements grid on only 5 microns, the strain inhomogeneity is found to significantly influence the strain in the measurement grid. Inspired by the finite element simulations, this strain inhomogeneity in the strain gauge grid is suggested to be removed by adding a stiff material at the end of the measuring part [2]. During this, it is possible to lower the erroneous of the material stiffness determination to below 1% in the full, for the composites materials, relevant stiffness range. The improvements are only based on an alternation of the shape of the measurement grid and will therefore only cause a negligible higher manufacturing cost of the strain gauges. The improvements does not only relates to unidirectional strain gauges. As it is shown in the figure, the finite element predictions shows that using the new strain gauge design in the case of a +-45 degree strain gauges, it is possible to improve the accuracy of the experimentally shear module determination significantly. In addition to this, the improved strain gauges design is found to also to lower the dependency of the stain gauge measurements on the occurrence of low stiffness outer layer such as a resin rich layer or by applying a top ply of woven or chopped fibers. In the following, the erroneous of conventional strain gauges are numerically

Lars P. Mikkelsen, Marco Salviato and Jacopo Gilli validated. The results from the improved strain gauges design will not be presented in the proceedings paper but will be presented to ICCM20. 2 NUMERICAL MODEL A uniaxial tensile test specimen with the length of 100 mm, the width of 30 mm and a thickness of either 2, 4 or 30 mm are modelled as a linear elastic isotropic material with a material stiffness in the range of E [1; 200] GPa and a Poisson s ratio on 0.3. The uni-axial test specimen is mounted with a strain gauge on both sides but due to symmetry, only one quarter of the specimen in the width and the thickness direction is modelled, see figure 1. The strain gauge is modelled as an E=180 GPa stiff linear elastic constantan alloy grid (red part in figure 1) mounted on a 45µm thick polymer film (yellow part in figure 1). Three different gauge length, Lgrid 1.5mm, Lgrid 3.0mm or Lgrid 10mmare investigated with the corresponding grid spacing Wgap 30 m for the two first and Wgap 100 m for the last one and a corresponding wire width on Wwire 20 m, Wwire 30 m or Wwire 80 m, respectively. For all cases, the grid thickness is given by twire 5 m. The strain gauges geometry is chosen to mimic the HBM [3] strain gauges series, 1- LY11-1.5, 1-LY11-3/120 and 1-LY11-10/120, respectively but could as well be chosen to mimic one of the other strain gauges on the market. The mesh is concentrated near the strain gauges with smallest element size given by the wire width. Figure 1: Finite element model of strain gauges As the model is linear, the load level doesn t matter. Nevertheless, as the standard for testing fibre reinforced polymers [4] prescribe that the stiffness shall be taken in the range of [0.05; 0.25]% strain the specimen is elongated to an overall 0.25% strain. A physically strain gauges relate the resistance change with the strain in the substrate through a gauge factor provide by the strain gauge manufacture from a calibration on a 200 GPa stiff material. In the finite element model, the average straining of the wire in the measuring grid can be considered analog to a resistance change and the gauge factor is found relating this strain gauge wire averaging strain with the straining in the underlying substrate with a numerical gage factor found by performing the analysis for a 200 GPa substrate. Of this reason, all results found for 200 GPa has a defined error on 0%. 3 RESULTS In the following, a numerical study has been performed predicting the measurement error of the strain gauge determining the strain and thereby the material stiffness of the substrate. A positive error corresponds to an underestimate of the strain and therefore an overestimate of the material stiffness.

20 th International Conference on Composite Materials Copenhagen, 19-24 th July 2015 Figure 2: The non-uniform strain around a 3 mm strain gauge mounted on an E = 10 GPa stiff substrate. Figure 2 show the variation of the axial strain around a conventional 3 mm strain gauge mounted on a thick 10 GPa stiff substrate which e.g. could corresponds to a biaxial reinforced polymer composite. The substrate is deformed to an axial strain on 0.25% during a uniaxial elongation which corresponds to the green colour. Despite that small thickness of the constantan wire in the strain gauge grid, the higher stiffness of the wire is seen to results in a rather spread-out non-uniform strain field. The contours going from blue to red represents axial strain in the range [0.23;0.27]% while the grey and black contours corresponds to values below and above those values, respectively. Due to the thickness, the overall stiffness of the substrate is not affected by the strain gauges. Therefore, the smaller axial strain just below and in the grid must be accompanied by larger strain in the substrate material just outside the strain gauge. Figure 3: Effect of the soldering tabs (a) and of the thickness of the substrate (b) on the measurement error of the strain gauges with a 3 mm gauges section. From the two nearly coinciding curves on Figure 3a, it can be seen that the effect of the soldering tabs of a conventional strain gauges on the strain measurements of the strain gauges can be neglected. Nevertheless from Figure 3b, a small increase in the measurement error is is found mounting the strain gauges on thinner materials. It is a symmetric model so the 2, 4 and 30 mm thick specimen mounted with strain gauges on both sides corresponds to a symmetric finite element model with the thickness of 1, 2 and 15 mm, respectively. The increases in the measurements error for the thinner specimens are due to the fact that the strain gauges for the thinner case will contribute slightly to the overall stiffness

Lars P. Mikkelsen, Marco Salviato and Jacopo Gilli of the test sample. A comparison of the strain field for the 2 and 4 mm case are shown in figure 4. The contours level used are the same as the one used for the thick case in figure 2. Figure 4: Non-uniform strain around a 3 mm strain gauge mounted on an E = 10 GPa stiff substrate for the 2 and 4 mm thick substrate case. From the contour plots in figure 2 and figure 4 the reinforcement effect can be seen to concentrate around the ends of strain gauges and the size are not expected to scale the grid as also found in [1]. Therefore, the measurements error is expected to be smaller using a longer measuring grid. In figure 5, the measurements errors are found for strain gauges with a gauge length on 1.5, 3 and 10 mm, respectively. As expected, the measurement error is found degrees with increasing grid length but for all cases, there are still significant measurements error in the for glass fibre composite relevant stiffness range of E [5;45] GPa. L grid Figure 5: Predicted measurements error on the material stiffness using a 1.5, 3 and 10 mm strain gauges, respectively. Unidirectional composite materials have often a protecting biaxial or randomly oriented ply on the outer layer. In addition, the present of a resin rich layer or a gelcoat can also be present. In figure 5, the measurement error for a uni-directional glass fiber composite can be found correspond to 2% using a 3 mm strain gauges. In figure 6, the effect of the present of a softer outer layer on the strain gauges measurements is investigated.

20 th International Conference on Composite Materials Copenhagen, 19-24 th July 2015 Figure 6: Effect on the measurement error of a gelcoat or biaxial composite layer between a 3 mm strain gauges and a thick uni-directional glass fiber composite substrate with E=44GPa. Figure 6 show that increasing the layer thickness up-to approximately 1 mm will increase the overestimate of the material stiffness quite significant and e.g. increase the measurement up to above 10 % in the present of a gel-coat. Even for a thin resin rich layer on only 100 µm can be seen to increase the error with more than a factor of 2 to more than 5%. A factor needed to be taken into consideration when making precise experimental stiffness determination of compliant materials such as fiber reinforced polymer-based composites using strain gauges. 9 CONCLUSIONS A linear numerical finite element model has been used in order to validate experimental observed over-estimation of the material stiffness using strain gauges. The numerical predictions have been used to quantify this over-estimation. In addition, the effect on the erroneous of the strain gauges when a thin soft layer such as a gel-coat or a biaxial layer is present in-between the composite and the measuring strain gauges. Predictions, which show the need for well-defined testing procedures comparing experimental determined material stiffness s. ACKNOWLEDGEMENTS This research was supported by the Danish Centre for Composite Structure and Materials for Wind Turbines (DCCSM), grant no. 09-067212, from the Danish Strategic Research Council (DSF). REFERENCES [1] S. Zike and L. P. Mikkelsen, Correction of Gauge Factor for Strain Gauges Used in Polymer Composite Testing, Exp. Mech., vol. 54, no. 3, pp. 393 403, Oct. 2014. [2] L. P. Mikkelsen and S. Zike, A strain gauge, Patent Application: EP14180022.72014. [3] HBM, Strain Gauges Catalog. [Online]. Available: www.hbm.com. [4] ISO-527-4, Plastics determination of tensile properties part 4: Test conditions for isotropic and orthotripic fibre-reinforced plastic composites. 1997.