A Low Temperature Brittle Fracture Investigation of Gray Iron and Nodular Iron on Machinery Casings
|
|
- Hubert McDaniel
- 6 years ago
- Views:
Transcription
1 75-GT-80 Copyright 1975 by ASME $3.00 PER COPY author(s). $1.00 TO ASME MEMBERS The Society shall not be responsible for statements or opinions advanced in papers or in discussion at meetings of the Society or of its Divisions or Sections, or printed in its publications. Discussion is printeo only if the paper is published in an ASME journal or Proceedings. Released for general publication upon presentation. Full credit should be given to ASME, the Technical Division, and the A Low Temperature Brittle Fracture Investigation of Gray Iron and Nodular Iron on Machinery Casings R. EISENSTADT Professor of Mechanical Engineering, Union College, Schenectady, N.Y. Mom. ASME G. H. ROULSTON Design Engineer, KARL, General Electric Co., Schenectady, N.Y. The resistance to brittle fracture of two iron alloys commonly used in machinery components is investigated. The Stress Intensity Factor (KI) is calculated using the principles of Fracture Mechanics, and is compared to available fracture toughness data in the form of Charpy Energies, and Plane Strain Fracture Toughness (Kl c). Also presented are appropriate correlations to relate Charpy Energy and Kl c. The critical flaw size (i.e., the flaw size necessary for brittle fracture) is also calculated and is presented in a generalized form which is applicable for various materials. The results of the investigation are evaluated, and the value of examining both Charpy and Kl c data, particularly for irons, is discussed. Contributed by the Gas Turbine Division of The American Society of Mechanical Engineers for presentation at the Gas Turbine Conference & Products Show, Houston, Texas, March 2-6, Manuscript received at ASME Headquarters December 2, Copies will be available until December 1, THE AMERICAN SOCIETY OF MECHANICAL ENGINEERS, UNITED ENGINEERING CENTER, 345 EAST 47th STREET, NEW YORK, N.Y
2 1 A Low Temperature Brittle Fracture Investigation of Gray Iron and Nodular Iron on Machinery Casings R. EISENSTADT G. H. ROULSTON INTRODUCTION Applications in Artic Environments have led to increased probability for brittle fracture failures. High operating stress in the presence of flaws, combined with temperatures as low as -50 F (-46 C) can create the conditions which lead to brittle fracture. It is the purpose of this investigation to examine this phenomenon for two materials commonly used in machinery components, nodular or ductile iron, and gray cast iron. One method of approach will use the principles of fracture mechanics to determine the Stress Intensity Factor (KI) for a given flaw size and compare this to available. fracture toughness data for the material. A second approach will use the available fracture toughness data to calculate a critical flaw size necessary for brittle fracture. This may then be compared to the maximum flaw size which is considered acceptable, CALCULATION OF THE STRESS INTENSITY FACTOR K I In order to calculate K I, it is necessary to have an estimate of the expected flaw size and shape, as well as an estimate of the nominal stresses encountered during operation. The type of flaw which will be considered here will be a buried or internal flaw, rather than a surface flaw. This is a common type of flaw for machinery applications, and of more concern than a surface flaw since it is more difficult to detect. Reference ( 1 ) 1 gives the following equation for a buried flaw under a stress normal to the flaw cross section. KI a Qa (1) where Q is a flaw shape parameter defined by the curves shown in Fig. 1, FLAW SIZE AND SHAPE Fig, 2 shows a cross section of a nodular iron casing containing flaws, The flaws shown in this figure are spongy shrink areas and are typical of both nodular and gray iron components, Flaws as large as 1/2 in. x 5 in. (12.7 x 127 mm) have been found in nodular iron casings, while in gray iron casings flaws 3/4 in. x 3 in, (19.0 x 76.0 mm) in cross section have been observed. The spongy shrink areas are groups of small flaws separated by ligaments of material, It is likely that early in the life of the component, these ligaments will fail, forming one large flaw, These shrink areas can best be modeled as elliptical flaws, (see Fig. 2) due 1 Underlined numbers in parentheses designate References at end of paper. NOMENCLATURE a = half minor diameter of flaw-(in,)-(mm) a c = critical minor diameter of flaw-(in.)- (mm) C = half major diameter of flaw-(in,)-(mm) KI = stress intensity factor-ksi (in,) 1/2 1/2 ) -(MPa(m) KI = plane strain fracture toughness, (slow cloading)-ksi (in.) 1/ 2 -(MPa(m) 1 / 2 ) = applied stress-(psi or ksi) - (MPa) Q = flaw shape parameter (dimensionless) f = ratio of applied stress to yield strength (dimensionless) KId = plane strain fracture toughness dynamic loading ksi (in.) 1 / 2 -(MPa(m) 1 / 2 ) a ys = yield stress - ksi - (MPa) 'max = maximum stress - ksi - (MPa) 2
3 0.5 E i 2a INTERNAL FLAT! a2c RATIO 0.2 r6- y 5=.8 6s O ^y 3.G Fig, 1 Flaw shape parameter curves r to their shape and the numerous solutions available for a buried elliptical flaw. Fig, 2 Examples of spongy shrink areas OPERATING STRESSES Nominal operating stresses for nodular iron components appear to be higher thaii for gray iron components. In the case of the nodular iron casings, stresses, excluding thermal stresses, normal to the shrink areas are as large as 11,000 psi, (75,1 MPa). Stresses in the gray iron casings are limited to 3000 psi, (20.7 MPa), tension and 4500 psi, (31.1 MPa), in bending, While the bending stresses do not strictly apply to the model chosen (i.e., a uniform stress field normal to the flaw) the bending stress limit of 4500 psi, (31.1 MPa), will be used here as a conservative estimate of expected operating stresses, PHYSICAL AND MECHANICAL PROPERTIES The mechanical properties of both gray and nodular iron vary considerably depending upon the chemical composition of the particular alloy. The chemical composition of a nodular iron and a gray iron for which both mechanical properties and fracture toughness properties have been obtained is shown in Table 1 rreference (2)a STRESS INTENSITY FACTOR If it is assumed that the spongy shrink areas are buried elliptical cracks, then a value of Q in equation (1) may be obtained from Fig. 1. Flange and casing defects in nodular iron casings have been known to have elliptically spongy shaped defects as large as 1/2 in., (12.7 mm), minor diameter by 5 in,, (127 mm), major diameter. For this size flaw, a = 1/4 in., (6.4 mm), 2c = 5.0 in., (127 mm), and a/2c = 0.05, Assuming a stress level of 11 ksi, (75,1 MPa), and a yield strength for this material at the temperature of concern (-50 F), (-46 C) of 54.5 ksi, (375 MPa),a /vys = 0.20, then Fig. 1 shows that Q = 1.0. Substituting into equation (1) yields: K I = 11 ksi1 25 = 9.75 ksi in (ID i M Pa rm ') For the flaws in gray iron similar to that shown in Fig, 2 where the minor diameter = 0.75 in., (19.0 mm), and the major diameter = 2,5 in., (63.5 mm), a = in., (8.5 mm), 2c = 2.5 in., (63.5 mm), and,,a/2c = 0.150, At a stress level of 4500 psi, (31.1 MPa), with ays = 37,300 psi, (256 MPa),c /Qys = Fig. 1 shows that Q u 1.18, and equation (1) yields: K I = 4.5 ksi ^g75 = 4.9 ksi in MPaFr- TOUGHNESS DATA Most toughness data available for these materials is in the form of Charpy impact data, (3-7) with some limited Plane Strain Fracture 3
4 Table 1 Chemical Compositions Percent Material C Mn P S Si Ni Cr Mg Nodular Iron 3.1 0, Gray Iron , Table 2 shows the mechanical properties of interest for these two alloys at room temperature, and at -50 F (-46 C). Table 2 Mechanical Properties Material Room Temperature - 50 F (-46 C) Nodular Iron Yield = 46,300 psi, (319 MPa) Ultimate = 59,000 psi, (406 MPa) Yield = Ultimate = 54,500 psi, (375 MPa) Gray Iron Yield = Ultimate = 35,000 psi, Yield = Ultimate = 37,300 psi, (256 MPa) (2)41 MPa) Toughness data (KI c ) from [Reference (2)3. Since Charpy data is so commonly used as toughness criteria, it is worthwhile to examine the Charpy data and compare it with the available K I data. c Fig. 3, (2), shows Charpy energies obtained at various temperatures for the nodular and gray iron discussed in this paper. As is apparent from this figure Charpy energies at lower temperatures are extremely small, and in the case of gray iron, do not increase appreciable at higher temperatures. For this reason, a conversion of these Charpy values into fracture toughness values is of questionable value. However, in many cases this is the only method available to the design engineer and, therefore, will be investigated here. Fig. 4 shows two relationships between rrpy data and K Ic which were obtained from ferences (8) and (9)3. Both correlations are for steels and must be extrapolated to the lower Charpy values of irons. Fig, 3 shows that at -50 F (-46 C) nodular iron has a Charpy energy of 2 ft lb (2.7 J), while gray iron has approximately l.ft lb (1.4 J). Via Fig. 4 this yields values of KI of 10 ksi in., (11 MPa j '' ), and 5 ksi-in.,?5.5 MPa^ m ), respectively, or very nearly equal to the calculated Stress Intensity Factor for both materials. This would indicate that with the assumed flaw size and stresses, at -50 F (-46 C) either material could be susceptable to brittle fracture. However, fracture toughness data for both materials would indicate otherwise. Fracture toughness tests were performed on both nodular and gray iron using a three point bend bar (Reference (2)1. The tests were conducted at -320 F (-196 C) in order to obtain Plane Strain conditions for the size test bar used. The results show that nodular iron has a KI c of 21.6 ksi in., (23.8 MPa ), while gray iron has a KI c of 24.2 ksi in., (26.6 MPa[). Thus the fracture toughness tests indicate that nodular iron has approximately twice the toughness needed for these applications, and that gray iron has nearly five times the necessary toughness. Fracture toughness tests on 11 grey cast irons (10) resulted in values of K I varying from 11.3 to 18.5 ksi (in.) 1/2 ( MPa m ), It is most important therefore to evaluate this quantity for the particular grey iron and heat treatment involved, Many materials are strain rate sensitive and toughness values should be obtained that simulate the most rapid loading rate expected, These impact fracture toughness values sometimes using the symbol KId are a more useful index that K I obtained under very slow loading conditions. c Reference (1) contains data of this kind for nodular irons at low temperatures and shows that KId (11) may be considerably lower than K I c CRITICAL FLAW SIZE Another way to examine this situation is 4
5 J 3 0 KJ N ^ 2 I^ J 1 N ' cd IKI. IROJ :iiiiiizit7 0.^ REF, 8 li. w si REF, 9 r0 N 20 N ^ U NODULAR IRON TEMPERATURE -'C 9' &-8 13G C _. -tn LlI'arw ENMRGY JDi_ILES 2^ _ - -firs CHARPY ENLRGY - FT, LB. Fig, 4 Charpy energy versus Klc 34 I 0 Mfr 4. B TEMPERATURE - `F Fig, 3 Charpy energy versus temperature for the irons in Tables 1 and 2 to determine the flaw size necessary to produce brittle fracture, given the fracture toughness and operating stress. When solved for a c, equation (1) reduces to the following: more than sufficient toughness for the intended applications. For either case, the flaw shapes encountered were relatively long and thin, with Q being close to 1.0. Fig. 1 shows that for a /uys less than 0.5, Q is approximately 1.0 for any long thin flaw (a/2c <0.1), Thus for small values of Q/Qys, it is conservative to assume that Q = 1.0, If Q max in equation (3) is expressed as a fraction of yield strength (i.e., u max = f (a ys ), then for f ' 0.5 equation (3) becomes: _ I ax 2 (3) acn m 1 /K I \2(EL) a c \f a ^) For nodular iron where Q = 1.0, K I = 21,6 ksi ;ft., (23.8 MPA J), and umax = 11 k si (75.1 MPa), equation (3) yields: a = n () 2 = 1.23(31.'3mm) This size flaw would be approximately equivalent to a 2.5 in. x 25 in., (63.5 mm x 635 mm), spongy shrink area, This is a large flaw which could be easily detected during an inspection. For gray iron where Q = 1.18, KI c = 24.2 ksi(, (26.6 MPa J), and max = 4.5 ksi, (31.1 MPa), equation (3) yields: a c = n 4.5) = (29q mm) This is an extremely large flaw and could not occur in a machinery component. The magnitude of these flaws sizes is another way of showing that both materials have Thus the critical flaw size can be expressed in terms of f and the ratio, KI c/sys. It should be remembered that equation (4) applies to an internal flaw and for values of 0/C 0.5, Fig. 5 is a plot of equation (4) for various values of KI c/ays, both of which are material properties. Expressed in this general form, Fig. 5 may be used for a variety of materials (depending upon the ratio of K Ic / ys ), and may be used conservatively for any elliptical flaw provided r/tys is less than approximately 0.5. This is often the case since the majority of brittle fracture problems occur at stress levels considerably below the yield strength. For nodular iron, KI /rys = 21,6/54.5 = 0.40, while for gray iron ki c / ys = 24.2/37.3 = These values are shown in Fig. 5 for flaws sizes up to 2.5 in., (63.5 mm). An excellent reference for the graphical solution of such problems can be found in the paper ( 12 ), H. D., Greenberg, and W. G. Clark "A Fracture Mechanics Approach to the Development of Realistic Standards for Heavy Walled Steel 5
6 Castings." These solve the previously mentioned analytical expressions graphically and yield rapid results for scoping the brittle fracture susceptibility of a structure. I a DISCUSSION It is interesting to note that the Charpy impact data and other physical properties for both gray and nodular iron do yield fracture toughness values less than the KI c determined in the fracture toughness tests ( ). Thus, from interpretation of the Charpy data alone, it would be concluded that brittle fracture was a distinct possibility for both materials for machinery applications. The actual fracture toughness is, however, more than adequate for the applications. One explanation of this discrepency between toughness predictions could be the scatter of the Charpy data, particularly in the lower ranges. An absolute error of 2 ft lb (2.7 J) for a Charpy test is not uncommon. In addition a certain amount of the Charpy energy (approximately 0.5 ft lb, (1,4 J) is transformed into kinetic energy as the specimen fails. When these sources of error are combined for lower range Charpy values a percentage error of 200 to 300 percent can result. Fig. 4 shows that such an uncertainity in Charpy values will produce similar changes in KI c. In fact, the uncertainity is enough to account for the discrepancy in fracture toughness agreement noted here, Another possible explanation of the discrepancy could be the strain rate effect caused by the difference in loading rates between the Charpy tests and the KI tests. The loading rate for the KI c tests was such that all specimens failed in from 1 to 1.5 min, while the loading rate for the Charpy tests is such that failure is nearly instantaneous. Reference ( 1 ) confirms that some nodular irons will give good ductility in relatively slow strain rate tension tests, yet will fail in a brittle manner on impact. The value of examining both K Ic data and Charpy data is apparent. For machinery applications, or other applications where no impact type of loading is anticipated, the use of Charpy data alone as a toughness criteria could lead to an over conservative design, or use of material with unnecessarily excessive toughness. Likewise for applications where impact loading is anticipated, interpretation of only KI c data as toughness criteria could lead to the use of a material with insufficient toughness. 1, 0. DL , ,1 t = ^ax/jys Fig,5 Generalized critical flaw curves ACKNOWLEDGMENT The authors wish to acknowledge the support of the Gas Turbine Department of the General Electric Co., Schenectady, New York for this work and in particular Mr. D. E. Brandt of the same department for his advice and help on this paper. REFERENCES 1 "Progress in Measuring Fracture Toughness and Using Fracture Mechanics," Materials and Research Standards, March 1964, p Brandt, D. E., "Crack Growth and Fracture Characterization of Ductile Iron, Gray Iron, and 0.25 Percent Carbon Cast Steel," General Electric Report 71-GTD-17, Gilbert, G. N. J., "Ductile and Brittle Failure in Ferritic Nodular Irons," Symposium of Metallic Materials at Low Temperatures, ASTM STP-158, 1953, pp Sandoz, G. A., Bishop, H. F., and Pellini, W. S., "Notch Ductile High Strength Nodular Irons," Transactions of the ASM, Vol. 48, 1956, p Gilbert, G. N. J., "Low Temperature Properties of Cast Irons," Symposium of Metallic Materials at Low Temperatures, ASTM-STP-158, 1953, p Pellini, W. S., Sandoz, G., and Bishop, H. F., "Notch Ductility of Nodular Iron," Transactions of ASM, Vol. 46, 1954, p Mogford, I. L., Brown, J. L., and Hull, D., "Fracture of Nodular Cast Iron," 6
7 Journal of the Iron and Steel Institute, July 1967, 8 Pellini, W. S., "Advances in Fracture Toughness Characterization Procedures and in Quantitative Interpretations to Fracture Safe Design of Structural Steels," NRL Report 6713, 9 Barsom, J. M., and Rolfe, S. T., "Correlation Between Klc and Charpy V Notch Test Results in Transition Temperature Range," Presented at the ASTM Meeting, June 1969, U. S. Steel Paper, Fig, 14, 10 Grover, A. G., and Pollard, G., "Brittle Failure of Grey Cast Irons," International Conference on Fracture, 2nd,, Proceedings Brighton England, April Bishop, H. F,, Sandoz, G., Howells and Pellini, "Notch Ductility of Commercial Malleable Iron," NRL Report 4713, March Greenberg, H, D,, and Clark, W. G., "A Fracture Mechanics Approach to the Development of Realistic Standards for Heavy Walled Steel Casting," Metals Engineering Quat., August Pellini, W. S., Sandoz, G. A,, and Bishop, H. F., "Drop Weight Test Measures Notch Ductility," Iron Age, July 8, 1954, 14 Pellini and Loss, "Integration of Metallurgical and Fracture Mechanics Concepts of Transition Temperature Factors Relating to Fracture Safe Design for Structural Steels," NRL Report 6900, April 1969, 15 Vanick, J. S., "Low Temperature Toughness of Flake and Spherodal Graphite Cast Iron Symposium on Metallic Materials at Low Temperature," ASTM-STP-158, 1958, pp
True Stress and True Strain
True Stress and True Strain For engineering stress ( ) and engineering strain ( ), the original (gauge) dimensions of specimen are employed. However, length and cross-sectional area change in plastic region.
More informationMolybdenum. Standard Specification for Pressure Vessel Plates, Alloy Steel, Chromium- Designation: A 387/A 387M 03
Designation: A 387/A 387M 03 Used in USDOE-NE Standards Standard Specification for Pressure Vessel Plates, Alloy Steel, Chromium- Molybdenum 1 This standard is issued under the fixed designation A 387/A
More informationPLANE STRAIN CRACK TOUGHNESS TESTING OF HIGH STRENGTH METALLIC MATERIALS
PLANE STRAIN CRACK TOUGHNESS TESTING OF HIGH STRENGTH METALLIC MATERIALS by William F. Brcwn, Jr., and John E. Srawiey ASTM SPECIAL TECHNICAL PUBLICAT'ON NO. 410 List price $5.50; 30 per cent discount
More informationQuiz 1 - Mechanical Properties and Testing Chapters 6 and 8 Callister
Quiz 1 - Mechanical Properties and Testing Chapters 6 and 8 Callister You need to be able to: Name the properties determined in a tensile test including UTS,.2% offset yield strength, Elastic Modulus,
More informationME -215 ENGINEERING MATERIALS AND PROCESES
ME -215 ENGINEERING MATERIALS AND PROCESES Instructor: Office: MEC325, Tel.: 973-642-7455 E-mail: samardzi@njit.edu PROPERTIES OF MATERIALS Chapter 3 Materials Properties STRUCTURE PERFORMANCE PROCESSING
More informationIntroduction to Engineering Materials ENGR2000 Chapter 8: Failure. Dr. Coates
Introduction to Engineering Materials ENGR2000 Chapter 8: Failure Dr. Coates Canopy fracture related to corrosion of the Al alloy used as a skin material. 8.2 Fundamentals of Fracture Fracture is the separation
More informationMat E 272 Lecture 19: Cast Irons
Mat E 272 Lecture 19: Cast Irons November 8, 2001 Introduction: One reason steels and cast iron alloys find such wide-ranging applications and dominate industrial metal production is because of how they
More informationREVISED PAGES IMPORTANT TERMS AND CONCEPTS REFERENCES QUESTIONS AND PROBLEMS. 166 Chapter 6 / Mechanical Properties of Metals
1496T_c06_131-173 11/16/05 17:06 Page 166 166 Chapter 6 / Mechanical Properties of Metals IMPORTANT TERMS AND CONCEPTS Anelasticity Design stress Ductility Elastic deformation Elastic recovery Engineering
More informationSchedule of Accreditation issued by United Kingdom Accreditation Service 2 Pine Trees, Chertsey Lane, Staines-upon-Thames, TW18 3HR, UK
2 Pine Trees, Chertsey Lane, Staines-upon-Thames, TW18 3HR, UK 19 Wildmere Road Banbury Oxfordshire OX16 3JU Contact: Mr J Guntrip Tel: +44 (0)1295 261211 Fax: +44 (0)1295 263096 E-Mail: qualityuk@wmtr.com
More informationPractice Problems Set # 3 MECH 321 Winter 2018
Question 1 Copper-rich copper beryllium alloys are precipitation hardenable. After consulting the portion of the phase diagram given below, answer the following questions: (a) Specify the range of compositions
More informationStructural Vessel Repairs Using Automated Weld Overlays
Structural Vessel Repairs Using Automated Weld Overlays Mahmod Samman, Ph.D., P.E. mms@hes.us.com Houston Engineering Solutions, LLC Eric Williams George Gemmel ewilliams@cimsltd.com ggemmell@cimsltd.com
More informationFerrous Alloys. Metal Alloys. Ferrous. Non ferrous. Grey iron. Carbon Low Alloy High Alloy. Nodular iron White iron Malleable iron Alloy cast irons
Metal Alloys Most engineering metallic materials are alloys. Metals are alloyed to enhance their properties, such as strength, hardness or corrosion resistance, and to create new properties, such as shape
More information41003 STAINLESS STEEL
41003 STAINLESS STEEL D ATA S H E E T Formable and Weldable in Heavy Sections Refined Grain Structure Leads to Good Toughness Ferritic as Annealed Low Cost AK Steel 41003 is an economical ferritic stainless
More information4.4 Single Load Path Structure
4.4 Single Load Path Structure For a single load path structure, the only means to protect the safety is to prevent the damage growth from degrading the strength of the structure to less than the design
More informationATI ATI 2205 Alloy (UNS S31803 and S32205) Duplex Stainless Steel. Technical Data Sheet
Alloy (UNS S31803 and S32205) Duplex Stainless Steel GENERAL PROPERTIES alloy (UNS S31803 and/or S32205) is a nitrogenenhanced duplex stainless steel alloy. The nitrogen serves to significantly improve
More informationAND IMPACT PROPERTIES RESEARCH PROJECT AT CASE WESTERN RESERVE UNIVERSITY
THE EFFECT OF INTERNAL SHRINKAGE DISCONTINUITIES ON THE FATIGUE AND IMPACT PROPERTIES OF CAST STEEL SECTIONS RESEARCH PROJECT AT CASE WESTERN RESERVE UNIVERSITY Sponsored by STEEL FOUNDRY RESEARCH FOUNDATION
More informationEvaluation of Crashworthiness for SAE Materials under Ductile to Brittle Transition Temperature (DBTT)
Evaluation of Crashworthiness for SAE Materials under Ductile to Brittle Transition Temperature (DBTT) Amol Bhanage *1, Nilesh Satonkar # 2, Pratap Deshmukh # 3, Rupesh Sundge # 4 * Mechanical Engineering,
More informationAnalysis of High-Collapse Grade P110 Coupling Failures
Analysis of High-Collapse Grade P110 Coupling Failures Michael G. Burns, P. E., Stress Engineering Services, Inc., Houston, Texas USA W. M. Buehler, Stork Testing and Metallurgical Consulting, Inc., Houston,
More informationMACHINES DESIGN SSC-JE STAFF SELECTION COMMISSION MECHANICAL ENGINEERING STUDY MATERIAL MACHINES DESIGN
1 SSC-JE STAFF SELECTION COMMISSION MECHANICAL ENGINEERING STUDY MATERIAL C O N T E N T 2 1. MACHINE DESIGN 03-21 2. FLEXIBLE MECHANICAL ELEMENTS. 22-34 3. JOURNAL BEARINGS... 35-65 4. CLUTCH AND BRAKES.
More informationFatigue Strength of Ferritic Ductile Cast Iron Hardened by Super Rapid Induction Heating and Quenching
Materials Transactions, Vol. 45, No. 9 (4) pp. 293 to 2935 #4 The Japan Institute of Metals EXPRESS REGULAR ARTICLE Fatigue Strength of Ferritic Ductile Cast Iron Hardened by Super Rapid Induction Heating
More informationChances and limits of High silicon ductile iron. Metal Casting Conference South Africa 2017
Chances and limits of High silicon ductile iron Dr.-Ing. Claudia Dommaschk TU Bergakademie Freiberg, Foundry Department Metal Casting Conference South Africa 2017 TU Bergakademie Freiberg Foundry Department
More informationJoint ICTP/IAEA Workshop on Irradiation-induced Embrittlement of Pressure Vessel Steels November 2009
2067-1 Joint ICTP/IAEA Workshop on Irradiation-induced Embrittlement of Pressure Vessel Steels 23-27 November 2009 Surveillance Programs for Monitoring the Integrity of the Reactor Pressure Vessel (RPV)
More informationVM12-SHC Technical-Datasheet
VM12-SHC Technical-Datasheet p.2 / Vallourec / VM12-SHC Technical-Datasheet Innovation by nature Specializing in the most complex applications, Vallourec relies on its 6 R&D centers around the world and
More information1) Fracture, ductile and brittle fracture 2) Fracture mechanics
Module-08 Failure 1) Fracture, ductile and brittle fracture 2) Fracture mechanics Contents 3) Impact fracture, ductile-to-brittle transition 4) Fatigue, crack initiation and propagation, crack propagation
More informationINVESTIGATIONS ON THE DYNAMIC FRACTURE TOUGHNESS OF HEAVY-SECTION DUCTILE CAST IRON FOR TRANSPORT AND STORAGE CASKS
INVESTIGATIONS ON THE DYNAMIC FRACTURE TOUGHNESS OF HEAVY-SECTION DUCTILE CAST IRON FOR TRANSPORT AND STORAGE CASKS Karsten Müller, Wolfram Baer and Peter Wossidlo, Department of Materials Engineering,
More informationStandard Specification for Seamless and Welded Steel Pipe for Low-Temperature Service 1
Designation: A 333/A 333M 04a Standard Specification for Seamless and Welded Steel Pipe for Low-Temperature Service This standard is issued under the fixed designation A 333/A 333M; the number immediately
More informationA Review of Suitability for PWHT Exemption Requirements in the Aspect of Residual Stresses and Microstructures
Transactions, SMiRT-23 Division IX, Paper ID 612 (inc. assigned division number from I to X) A Review of Suitability for PWHT Exemption Requirements in the Aspect of Residual Stresses and Microstructures
More informationSPECIFICATION FOR PRESSURE VESSEL PLATES, CARBON STEEL, FOR MODERATE- AND LOWER-TEMPERATURE SERVICE
Technical Literature: ASME SA-516 [ASTM A516] Company Website: www.metalspiping.com SA-516/SA-516M Carbon & Low Alloy Steels From Hebei Metals Industrial Limited SPECIFICATION FOR PRESSURE VESSEL PLATES,
More informationWith Dura-Bar you will be able to:
Dura-Bar Stock List Dura-Bar is an engineered iron designed to meet our customers most critical requirements. It is manufactured to strict process controls that provide world-class quality and uncompromising
More informationLOW CYCLE FATIGUE AND FATIGUE GROWTH BEHAVIORS OF ALLOY IN7 18. J. 2. Xie. Institute of Aeronautical Materials Beijing , P. R. China.
LOW CYCLE FATIGUE AND FATIGUE CRACK GROWTH BEHAVIORS OF ALLOY IN7 18 J. 2. Xie Institute of Aeronautical Materials Beijing 100095, P. R. China Abstract The low cycle fatigue (LCF) behavior and fatigue
More informationStandard Specification for Piping Fittings of Wrought Carbon Steel and Alloy Steel for Low-Temperature Service 1
Designation: A 420/A 420M 07 Standard Specification for Piping Fittings of Wrought Carbon Steel and Alloy Steel for Low-Temperature Service This standard is issued under the fixed designation A 420/A 420M;
More informationMATERIALS SCIENCE-44 Which point on the stress-strain curve shown gives the ultimate stress?
MATERIALS SCIENCE 43 Which of the following statements is FALSE? (A) The surface energy of a liquid tends toward a minimum. (B) The surface energy is the work required to create a unit area of additional
More informationJ = D C A C B x A x B + D C A C. = x A kg /m 2
1. (a) Compare interstitial and vacancy atomic mechanisms for diffusion. (b) Cite two reasons why interstitial diffusion is normally more rapid than vacancy diffusion. (a) With vacancy diffusion, atomic
More information3. MECHANICAL PROPERTIES OF STRUCTURAL MATERIALS
3. MECHANICAL PROPERTIES OF STRUCTURAL MATERIALS Igor Kokcharov 3.1 TENSION TEST The tension test is the most widely used mechanical test. Principal mechanical properties are obtained from the test. There
More informationFracture and Fatigue Control in Steel Structures
Fracture and Fatigue Control in Steel Structures S. T. ROLFE CONSIDERABLE effort has been devoted to the prevention of brittle. fracture* in manufactured structures such as aircraft and pressure vessels,
More informationMarc King. Hiler Industries LaPorte, IN
Carbidic Ductile Iron Marc King Metallurgist Hiler Industries LaPorte, IN Why would anybody in their right mind want to add carbides to ductile iron? Ductile Iron is a great engineering material: Great
More informationCast Steel Propellers W27. (May 2000) (Rev.1 May 2004)
(May 2000) (Rev.1 May 2004) Cast Steel Propellers 1. Scope 1.1 These unified requirements are applicable to the manufacture of cast steel propellers, blades and bosses. 1.2 Where the use of alternative
More informationElectron Beam Melted (EBM) Co-Cr-Mo Alloy for Orthopaedic Implant Applications Abstract Introduction The Electron Beam Melting Process
Electron Beam Melted (EBM) Co-Cr-Mo Alloy for Orthopaedic Implant Applications R.S. Kircher, A.M. Christensen, K.W. Wurth Medical Modeling, Inc., Golden, CO 80401 Abstract The Electron Beam Melting (EBM)
More informationE-BRITE E-BRITE. Technical Data Sheet. Stainless Steel: Superferritic GENERAL PROPERTIES PLANAR SOLID OXIDE FUEL CELLS CHEMICAL COMPOSITION
E-BRITE Stainless Steel: Superferritic (UNS 44627, ASTM Type XM-27) GENERAL PROPERTIES E-BRITE alloy is a high purity ferritic stainless steel which combines excellent resistance to corrosion and oxidation
More informationStandard Specification for Stainless Chromium-Nickel Steel-Clad Plate 1
Enclosed is a computer file in PDF format containing one or more ASTM Standards. The documents contained in this e-mail are complimentary, prepublication copies of the final edited documents. These documents
More informationMechanical Properties of Metals. Goals of this unit
Mechanical Properties of Metals Instructor: Joshua U. Otaigbe Iowa State University Goals of this unit Quick survey of important metal systems Detailed coverage of basic mechanical properties, especially
More informationTechnical Reference on Hydrogen Compatibility of Materials
Technical Reference on Hydrogen Compatibility of Materials High-Alloy Ferritic Steels: (code 1500) Prepared by: C. San Marchi, Sandia National Laboratories and J.A. Zelinski, Defense Nuclear Facilities
More informationANALYSIS OF HETEROGENEOUS NUCLEATION IN DUCTILE IRON
ANALYSIS OF HETEROGENEOUS NUCLEATION IN DUCTILE IRON TMS 1, Simon N. Lekakh 2 1 TMS (The Minerals, Metals & Materials Society); 184 Thorn Hill Rd.; Warrendale, PA 15086-7514, USA 2 Missouri University
More informationCasing Failure Prevention East Texas Gas Producer s Assoc. 9 March 2010
Casing Failure Prevention East Texas Gas Producer s Assoc. 9 March 2010 The Ideal Casing String For as long as needed, it will: Safely carry all applied loads, Until the next string is set and be free
More informationThe strength of a material depends on its ability to sustain a load without undue deformation or failure.
TENSION TEST The strength of a material depends on its ability to sustain a load without undue deformation or failure. This strength is inherent in the material itself and must be determined by experiment.
More informationPROPERTIES OF FREE MACHINING ALUMINIUM ALLOYS AT ELEVATED TEMPERATURES. Ji í Faltus, Petr Homola, Peter Sláma
PROPERTIES OF FREE MACHINING ALUMINIUM ALLOYS AT ELEVATED TEMPERATURES Ji í Faltus, Petr Homola, Peter Sláma VÚK Panenské B e any a.s., Panenské B e any 50, 250 70 Odolena Voda E-mail: faltus@vukpb.cz
More informationIMF Ingot Metallurgy Forum
IMF Ingot Metallurgy Forum 19 th Annual Ingot Metallurgy Symposium September 27, 2006 THE RAMM MOLDS by Horacio Lima 1 TABLE CONTENTS: PAGE 3. HTCI- GRAY IRON MOLD BY RAMM 4. TAILORED DUCTILE IRON MOLDS
More informationPOLITECNICO DI TORINO Repository ISTITUZIONALE
POLITECNICO DI TORINO Repository ISTITUZIONALE Relationships between tensile and fracture mechanics properties and fatigue properties of large plastic mold steel Original Relationships between tensile
More informationMaterial Orientation Toughness Assessment (MOTA) for the Purpose of Mitigating Branch Technical Position (BTP) 5-3 Uncertainties
Westinghouse Non-Proprietary Class 3 2015 Westinghouse Electric Company LLC All Rights Reserved Global Expertise One Voice Material Orientation Toughness Assessment (MOTA) for the Purpose of Mitigating
More informationDATA SHEET ZERON 100 UNS S32760 THE GLOBAL LEADER IN SPECIALTY ALLOYS ALLOYS AND PROCESSING
DATA SHEET ZERON 100 UNS S32760 THE GLOBAL LEADER IN SPECIALTY ALLOYS ALLOYS AND PROCESSING ZERON 100 Data Sheet Contents Specifications, Chemical Composition, Applications and Features...2 Performance
More informationImpact 7 Steel. A Durable, Dependable Steel Solution For Harsh Environments. Technical Data. Alloy Description. Alloy Type. Typical Applications
Impact 7 Steel Technical Data A Durable, Dependable Steel Solution For Harsh Environments Alloy Description As a world leader in steel manufacturing, TimkenSteel specializes in providing custom steel solutions
More informationFailure Analysis of the US 422 Girder Fracture
Lehigh University Lehigh Preserve ATLSS Reports Civil and Environmental Engineering 10-1-2004 Failure Analysis of the US 422 Girder Fracture Eric J. Kaufmann Robert J. Connor John W. Fisher Follow this
More informationApplications Potential
P R O D U C T D A T A B U L L E T I N STAINLESS 301STEEL UNS S30100 High Strength and Good Ductility When Cold Worked Excellent Corrosion Resistance Readily Welded Readily Formed and Drawn Economical Oxidation
More informationProperties in Shear. Figure 7c. Figure 7b. Figure 7a
Properties in Shear Shear stress plays important role in failure of ductile materials as they resist to normal stress by undergoing large plastic deformations, but actually fail by rupturing under shear
More informationChapter 11: Applications and Processing of Metal Alloys
Chapter 11: Applications and Processing of Metal Alloys ISSUES TO ADDRESS... How are metal alloys classified and what are their common applications? What are some of the common fabrication techniques for
More informationThe American Institute
Cynthia J. Lanz Cynthia J. Lanz is Director of Specifications at the American Institute of Steel Construction (AISC) in Chicago. The American Institute of Steel Construction (AISC) will welcome the new
More informationStress Corrosion Cracking in a Dissimilar Metal Butt Weld in a 2 inch Nozzle. Master of Engineering in Mechanical Engineering
Stress Corrosion Cracking in a Dissimilar Metal Butt Weld in a 2 inch Nozzle by Thomas E. Demers An Engineering Project Submitted to the Graduate Faculty of Rensselaer Polytechnic Institute in Fulfillment
More informationCREEP AND FATIGUE CRACK GROWTH IN SEVERAL CAST SUPERALLOYS
CREEP AND FATIGUE CRACK GROWTH IN SEVERAL CAST SUPERALLOYS P. Shahinian and K. Sadananda Material Science & Technology Division Naval Research Laboratory Washington, DC 20375 Summary Crack growth behavior
More informationAnnex to the Accreditation Certificate D-PL according to DIN EN ISO/IEC 17025:2005
Deutsche Akkreditierungsstelle GmbH Annex to the Accreditation Certificate D-PL-11299-01-00 according to DIN EN ISO/IEC 17025:2005 Period of validity: 17.10.2016 to 16.10.2021 Holder of certificate: Salzgitter
More informationIt is our intent to always maintain the highest level of quality metals obtainable from our mill sources.
This stock catalog contains the sizes, weights and descriptions of all standard Steel, Brass, Bronze and Dura-Bar Cast Iron items that are available from stock for immediate delivery. However, new items
More informationInternational Journal of Scientific & Engineering Research, Volume 6, Issue 3, March-2015 ISSN
1530 Component Crack Analysis of high pressure die casting aluminum alloy (Alsi9cu ) Satish kumar Manocha Designation Dy. Manager Department - R&D Name of industries Rico auto industries ABSTRACT: Crack
More informationSubway Cars. Applications Potential
301 STAINLESS STEEL P R O D U C T D ATA B U L L E T I N Aircraft Structural Parts Roof Drainage Cooking Utensils Automotive Trim Subway Cars Applications Potential Type 301 is an austenitic chromium-nickel
More informationATI 2205 ATI Technical Data Sheet. Duplex Stainless Steel GENERAL PROPERTIES. (UNS S31803 and S32205)
ATI 2205 Duplex Stainless Steel (UNS S31803 and S32205) GENERAL PROPERTIES ATI 2205 alloy (UNS S31803 and/or S32205) is a nitrogen-enhanced duplex stainless steel alloy. The nitrogen serves to significantly
More informationExercises on Fracture Mechanics
Exercises on Fracture Mechanics Jan Zuidema and Michael Janssen These exercises are made available free of charge. Details of the accompanying textbook Fracture Mechanics are available at http://www.sponpress.com
More informationNew Generation High Strength High Damage Tolerance 7085 Thick Alloy Product with Low Quench Sensitivity
Proceedings of the 9 th International Conference on Aluminium Alloys (2004) Edited by J.F. Nie, A.J. Morton and B.C. Muddle Institute of Materials Engineering Australasia Ltd 969 New Generation High Strength
More informationReinforced Concrete Design. A Fundamental Approach - Fifth Edition
CHAPTER REINFORCED CONCRETE Reinforced Concrete Design A Fundamental Approach - Fifth Edition Fifth Edition REINFORCED CONCRETE A. J. Clark School of Engineering Department of Civil and Environmental Engineering
More informationApplied Fracture Mechanics
TALAT Lecture 403 Applied Fracture Mechanics 49 pages and 40 figures Advanced Level prepared by Dimitris Kosteas, Technische Universität München Objectives: Teach the principles and concepts of fracture
More informationCHROMESHIELD 22 STAINLESS STEEL
CHROMESHIELD 22 STAINLESS STEEL P R O D U C T D ATA B U L L E T I N Appliances Food Service Equipment Architectural Welded Components Tubing Cookware Applications Potential CHROMESHIELD 22 Stainless Steel
More information12 SR STAINLESS STEEL. More Oxidation Resistant Than Type 409. More Creep Resistant Than Type 409. Applications Potential
12 SR STAINLESS STEEL P R O D U C T D ATA B U L L E T I N More Oxidation Resistant Than Type 409 More Creep Resistant Than Type 409 Applications Potential AK Steel 12 SR Stainless Steel was developed specifically
More informationCRACK GROWTH IN THE PRESENCE OF LIMITED CREEP DEFORMATION
1 CRACK GROWTH IN THE PRESENCE OF LIMITED CREEP DEFORMATION O. Kwon*, K M Nikbin*, G. A. Webster*, K.V. Jata + * Department of Mechanical Engineering Imperial College London SW7 2BX UK Email: k.nikbin@ic.ac.uk
More informationAPPLIED ENGINEERING PRINCIPLES MANUAL
NAVSEA Training Manual APPLIED ENGINEERING PRINCIPLES MANUAL NAVAL SEA SYSTEMS COMMAND NAVY DEPARTMENT WASHINGTON, D.C. NAVSEA Training Manual APPLIED ENGINEERING PRINCIPLES MANUAL NAVAL SEA SYSTEMS COMMAND
More informationMECHANICAL CHARACTERISTICS OF 9% Ni STEEL WELDED JOINT FOR LNG STORAGE TANK AT CRYOGENIC
Advanced Materials Development and Performance (AMDP2011) International Journal of Modern Physics: Conference Series Vol. 6 (2012) 355-360 World Scientific Publishing Company DOI: 10.1142/S2010194512003431
More informationInstitutional repository of Jönköping University
Institutional repository of Jönköping University http://www.publ.hj.se/diva This is an author produced version of a paper published in Metallurgical and Materials Transactions A. This paper has been peer-reviewed
More informationCHAPTER 3 OUTLINE PROPERTIES OF MATERIALS PART 1
CHAPTER 3 PROPERTIES OF MATERIALS PART 1 30 July 2007 1 OUTLINE 3.1 Mechanical Properties 3.1.1 Definition 3.1.2 Factors Affecting Mechanical Properties 3.1.3 Kinds of Mechanical Properties 3.1.4 Stress
More informationsample initial height
EXPERIMENT 2 NOTCHED BAR IMPACT TESTING OF MATERIALS Background Materials sometimes display brittleness which precludes their use in a given design. Brittleness is characterized by fracturing with low
More informationIntroduction: Ferrous alloys - Review. Outline. Introduction: Ferrous alloys
Introduction: Ferrous alloys - Review Outline Introduction - Review - Ferritic SS - Austinitic SS - Matensitic SS - Precipitation Hardenable SS Cast Irons - Gray CI - Ductile CI - White CI - Malleable
More informationFatigue of metals. Subjects of interest
Fatigue of metals Chapter 12 Subjects of interest Objectives / Introduction Stress cycles The S-N curve Cyclic stress-strain curve Low cycle fatigue Structural features of fatigue Fatigue crack propagation
More informationThe use of magnesium has grown dramatically in the. Section thickness-dependent tensile properties of squeeze cast magnesium alloy AM60 CHINA FOUNDRY
CHINA FOUNDRY Vol.9 No.2 Section thickness-dependent tensile properties of squeeze cast magnesium alloy AM60 *Xuezhi Zhang, Meng Wang, Zhizhong Sun, and Henry Hu (Department of Mechanical, Automotive and
More informationQQ-A-250F September 25, 1978 SUPERSEDING QQ-A-250E October 19, 1970 (See 6.3) FEDERAL SPECIFICATION
September 25, 1978 SUPERSEDING QQ-A-250E October 19, 1970 (See 6.3) FEDERAL SPECIFICATION ALUMINUM AND ALUMINUM ALLOY PLATE AND SHEET: GENERAL SPECIFICATION FOR This specification was approved by the commissioner,
More informationMechanical behavior of crystalline materials - Stress Types and Tensile Behaviour
Mechanical behavior of crystalline materials - Stress Types and Tensile Behaviour 3.1 Introduction Engineering materials are often found to posses good mechanical properties so then they are suitable for
More information441 STAINLESS STEEL. Good High-Temperature Oxidation Resistance. Applications Potential
441 STAINLESS STEEL P R O D U C T D ATA B U L L E T I N Equiaxed Microstructure Good High-Temperature Strength Good High-Temperature Oxidation Resistance Applications Potential AK Steel 441 is used in
More informationAPPLICATIONS OF Fe-C PHASE DIAGRAM
APPLICATIONS OF Fe-C PHASE DIAGRAM KEY POINTS OF Fe-C Diagram Phases: Liquid Fe-Tmin=1148C @ 4.3%C 1394 C
More informationDURABILITY AND OPTIMIZATION OF CONNECTING RODS
DURABILITY AND OPTIMIZATION OF CONNECTING RODS Adila Afzal and Pravardhan Shenoy Graduate Research Assistants and Ali Fatemi, Professor The University of Toledo Funded by: OVERALL OBJECTIVES Evaluate and
More informationMP 35N MECHANICAL-PROPERTY DATA. un -F 7~E F Work Strengthened and Aged Bar. Issued by
1T4 MECHANICAL-PROPERTY DATA MP 35N Work Strengthened and Aged Bar Issued by Air Force Materials Laboratory Air Force Systems Command Wright-Patterson Air Force Bose, Ohio Sept.ber, 1970 Prepared by Tiwi
More informationSECTION 1043 FENCE MATERIAL
SECTION 1043 FENCE MATERIAL 1043.1 Scope. This specification covers the material required in the construction of chainlink fence and woven wire fence. 1043.2 Basis of Acceptance. The basis of acceptance
More informationTensile Testing. Objectives
Laboratory 3 Tensile Testing Objectives Students are required to understand the principle of a uniaxial tensile testing and gain their practices on operating the tensile testing machine to achieve the
More informationSTUDY OF SENT SPECIMENS WITH A TILTED NOTCH TO EVALUATE DUCTILE TEARING IN SPIRAL WELDED PIPELINE APPLICATIONS
STUDY OF SENT SPECIMENS WITH A TILTED NOTCH TO EVALUATE DUCTILE TEARING IN SPIRAL WELDED PIPELINE APPLICATIONS M. Deprez, F. Keereman, K. Van Minnebruggen, S. Hertelé, W. De Waele Ghent University, Laboratory
More informationStainless Steel & Stainless Steel Fasteners Chemical, Physical and Mechanical Properties
Stainless Steel & Stainless Steel Fasteners Chemical, Physical and Mechanical Properties Stainless steel describes a family of steels highly resistant to tarnishing and rusting that contain at least two
More informationStandard Specification for Seamless Brass Tube [Metric] 1
Designation: B 135M 00 e1 METRI Standard Specification for Seamless Brass Tube [Metric] 1 This standard is issued under the fixed designation B 135M; the number immediately following the designation indicates
More informationIN-SITU NONDESTRUCTIVE MEASUREMENTS OF KEY MECHANICAL PROPERTIES OF OIL AND GAS PIPELINES
PVP-Vol. 429, Residual Stress Measurement and General Nondestructive Evaluation ASME 2001 IN-SITU NONDESTRUCTIVE MEASUREMENTS OF KEY MECHANICAL PROPERTIES OF OIL AND GAS PIPELINES Fahmy M. Haggag Advanced
More informationBond Characteristics of ASTM A1035 Steel Reinforcing Bars
ACI STRUCTURAL JOURNAL Title no. 106-S51 TECHNICAL PAPER Bond Characteristics of ASTM A1035 Steel Reinforcing Bars by Hatem M. Seliem, Amr Hosny, Sami Rizkalla, Paul Zia, Michael Briggs, Shelby Miller,
More informationISO/TR TECHNICAL REPORT. Designation system for cast irons and pig irons. Système de désignation pour la fonte et la fonte brute
TECHNICAL REPORT ISO/TR 15931 First edition 2004-08-15 Designation system for cast irons and pig irons Système de désignation pour la fonte et la fonte brute Reference number ISO/TR 15931:2004(E) ISO 2004
More informationOMAE Fracture Control Offshore Pipelines - Advantages of using direct calculations in fracture assessments of pipelines
Proceedings of OMAE2005 24th International Conference on Offshore Mechanics and Arctic Engineering (OMAE 2005) June 12-16, 2005, Halkidiki, Greece OMAE 2005-67521 Fracture Control Offshore Pipelines -
More information21 Fracture and Fatigue Revision
21 Fracture and Fatigue Revision EG2101 / EG2401 March 2015 Dr Rob Thornton Lecturer in Mechanics of Materials www.le.ac.uk Fracture concepts Fracture: Initiation and propagation of cracks within a material
More informationHeat treatment and effects of Cr and Ni in low alloy steel
Bull. Mater. Sci., Vol. 34, No. 7, December 2011, pp. 1439 1445. Indian Academy of Sciences. Heat treatment and effects of Cr and Ni in low alloy steel MOHAMMAD ABDUR RAZZAK Materials and Metallurgical
More informationThis is the author s version of a work that was submitted/accepted for publication in the following source:
This is the author s version of a work that was submitted/accepted for publication in the following source: Yan, C. & Mai, Y. W. (1997) Effect of constraint on ductile crack growth and ductile-brittle
More informationChapter Outline: Failure
Chapter Outline: Failure How do Materials Break? Ductile vs. brittle fracture Principles of fracture mechanics Stress concentration Impact fracture testing Fatigue (cyclic stresses) Cyclic stresses, the
More informationIMPACT. Chemical composition For the chemical composition of the ladle analysis the following limits are applicable (in %):
IMPACT Wear resistant steel Material data sheet, edition April 2016 1 DILLIDUR IMPACT is a wear resistant steel with a nominal hardness of 340 HBW in delivery condition. DILLIDUR IMPACT is not a constructional
More informationWhat Are Metal Standards and Why Are They Important?
What Are Metal Standards and Why Are They Important? Table of Content Metallurgy101...3 Pure Metals...3 Component Metals...4 Characteristics of Metal Standards...5 Metal Standards and Testing Standards...6
More informationMAE 322 Machine Design Lecture 5 Fatigue. Dr. Hodge Jenkins Mercer University
MAE 322 Machine Design Lecture 5 Fatigue Dr. Hodge Jenkins Mercer University Introduction to Fatigue in Metals Cyclic loading produces stresses that are variable, repeated, alternating, or fluctuating
More information