Power/Inductive Materials and Components
|
|
- Justin Benson
- 6 years ago
- Views:
Transcription
1 Fair-Rite Products Corp. Your Signal Solution Power/Inductive Materials and Components Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY
2
3 COMPARISON OF FAIR-RITE POWER MATERIALS units Resistivity ρ Parameters measured at Room Temperature / B < 1gauss on Lab Toroids (12-22mm diameter) unless otherwise indicated. These parameters are typical and may vary dependent upon part size and geometry. Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 1
4 Fair-Rite Products Corp. Your Signal Solution 79 MATERIAL A high frequency MnZn ferrite material for power applications up to 75 khz. This material is available as special order for customer specific applications. 79 Material Characteristics Property Unit Symbol Value Initial Permeability µ i B < 1gauss Flux Density gauss B Field Strength oersted H 5 Residual Flux Density gauss B r 17 Coercive Force oersted H c.4 Loss Factor 1-6 Frequency MHz.1 Temperature Factor of Initial Permeability (25-6ºC) 1-6 / ºC 3.4 Curie Temperature ºC T c > 225 Resistivity ohm-cm ρ 2 1 Complex Permeability vs. Frequency 3 Initial Permeability vs. Temperature µ i E+4 1.E+5 1.E+6 1.E+7 Frequency (Hz) Measured on an 18/1/6mm toroid using HP 4284A and HP 4291A Temperature (ºC) Measured on an 18/1/6mm toroid at 1kHz. Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 2
5 79 MATERIAL A high frequency MnZn ferrite material for power applications up to 75 khz. 3 Amplitude Permeability vs. Flux Density 1 Power Loss Density vs. Flux Density 25ºC kHz 3kHz 15 1ºC kHz 1kHz B (gauss) Measured on an 18/1/6mm toroid at 1kHz B (gauss) Measured on an 18/1/6mm toroid using the Clarke Hess 258 VAW at 1ºC. 2 Power Loss Density vs. Temperature 6 Flux Density vs. Temperature kHz, 4G 4 B (gauss) 1 3 1kHz, 1G 5kHz, 5G 2 5 3kHz, 5G Temperature (ºC) Temperature (ºC) Measured on an 18/1/6mm toroid using the Clarke Hess 258 VAW. Measured on an 18/1/6mm toroid at 1kHz and H=5 oersted. Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 3
6 Fair-Rite Products Corp. Your Signal Solution 97 MATERIAL A low loss MnZn ferrite material for power applications up to 4kHz. New type 97 Material is a low loss/higher frequency power material. It features minimal power loss at 1 C at moderate flux densities for operation below 4 khz. This material is available as special order for customer specific applications. 97 Material Characteristics Property Unit Symbol Value Initial Permeability µ i B < 1gauss Flux Density gauss B Field Strength oersted H 5 Residual Flux Density gauss B r 15 Coercive Force oersted H c.16 Loss Factor 1-6 Frequency MHz.1 Temperature Factor of Initial Permeability (25-6ºC) 1-6 / ºC 6.5 Curie Temperature ºC T c > 22 Resistivity ohm-cm ρ 2 1 Complex Permeability vs. Frequency 6 Initial Permeability vs. Temperature E+4 1.E+5 1.E+6 1.E+7 Frequency (Hz) Measured on an 18/1/6mm toroid using HP 4284A and HP 4291A Temperature (ºC) Measured on an 18/1/6mm toroid at 1kHz. Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 4
7 97 MATERIAL A low loss MnZn ferrite material for power applications up to 4kHz. 7 Amplitude Permeability vs. Flux Density 1 Power Loss Density vs. Flux Density 6 1ºC 5 25ºC 1 4kHz 2kHz 4 1 5kHz kHz B (gauss) Measured on an 18/1/6mm toroid at 1kHz. Power Loss Density vs. Temperature B (gauss) Measured on an 18/1/6mm toroid using the Clarke Hess 258 VAW at 1ºC. Flux Density vs. Temperature kHz, 2G 2kHz, 1G 5 4 B (gauss) kHz, 5G 1kHz, 1G Temperature (ºC) Measured on an 18/1/6mm toroid using the Clarke Hess 258 VAW Temperature (ºC) Measured on an 18/1/6mm toroid at 1kHz and H=5 oersted. Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 5
8 Fair-Rite Products Corp. Your Signal Solution 78 MATERIAL A MnZn ferrite specifically designed for power applications for frequencies up to 2kHz. Shapes available in 78 material are Toroids, Rods, U Cores, E&I Cores, Pot Cores, RM, PQ, ETD, EFD, EP, EER. 78 Material Characteristics Property Unit Symbol Value Initial Permeability µ B < 1gauss 23 Flux Density gauss B Field Strength oersted H 5 Residual Flux Density gauss B r 15 Coercive Force oersted H c.2 Loss Factor 1-6 Frequency MHz.1 Temperature Factor of Initial Permeability (25-6ºC) 1-6 / ºC 4.2 Curie Temperature ºC T c > 2 Resistivity ohm-cm ρ 2 1 Complex Permeability vs. Frequency 5 Initial Permeability vs. Temperature µ i E+4 1E+5 1E+6 1E+7 Frequency (Hz) Measured on an 18/1/6mm toroid at 1kHz Temperature( C) Measured on an 18/1/6mm toroid using HP 4284A and HP 4291A. Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 6
9 78 MATERIAL A MnZn ferrite specifically designed for power applications for frequencies up to 2kHz. 1 Amplitude Permeability vs. Flux Density 1 Power Loss Density vs. Flux Density 8 1 C 1 2kHz 1kHz 6 µ a 25 C 1 5kHz 25kHz B (Gauss) Measured on an 18/1/6mm toroid at 1kHz B (Gauss) Measured on an 18/1/6mm toroid using the Clarke Hess 258 VAW at 1ºC. 25 Power Loss Density vs. Temperature 6 Flux Density vs. Temperature kHz, 1G 4 B (gauss) kHz, 2G Temperature( C) Measured on an 18/1/6mm toroid using the Clarke Hess 258 VAW Temperature( C) Measured on an 18/1/6mm toroid at 1kHz and H=5 oersted. Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 7
10 Fair-Rite Products Corp. Your Signal Solution 98 MATERIAL A low loss MnZn ferrite material for power applications up to 2kHz. New type 98 Material is an improved version of Fair-Rite s 78 Material, this material supplies lower power loss at 1 C at moderate flux densities for operation below 2kHz. Shapes available in 98 material are Toroids, U Cores, E&I Cores, Pot Cores, RM, PQ, ETD, EFD, EP, EER. 98 Material Characteristics Property Unit Symbol Value Initial Permeability µ i B < 1gauss Flux Density gauss B Field Strength oersted H 5 Residual Flux Density gauss B r 18 Coercive Force oersted H c.17 Loss Factor 1-6 Frequency MHz.1 Temperature Factor of Initial Permeability (25-6ºC) 1-6 / ºC 5.8 Curie Temperature ºC T c > 215 Resistivity ohm-cm ρ 2 1 Complex Permeability vs. Frequency 6 Initial Permeability vs. Temperature µ i E+4 1.E+5 1.E+6 1.E+7 Frequency (Hz) Measured on an 18/1/6mm toroid using HP 4284A and HP 4291A Temperature (ºC) Measured on an 18/1/6mm toroid at 1kHz. Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 8
11 98 MATERIAL A low loss MnZn ferrite material for power applications up to 2kHz. 8 Amplitude Permeability vs. Flux Density 1 Power Loss Density vs. Flux Density 6 1ºC 1 2kHz 25ºC 1kHz 4 1 5kHz B (gauss) Measured on an 18/1/6mm toroid at 1kHz. Power Loss Density vs. Temperature B (gauss) Measured on an 18/1/6mm toroid using the Clarke Hess 258 VAW at 1ºC. Flux Density vs. Temperature kHz, 2G 4 B (gauss) kHz, 1G 2 1 1kHz, 1G Temperature (ºC) Measured on an 18/1/6mm toroid using the Clarke Hess 258 VAW Temperature (ºC) Measured on an 18/1/6mm toroid at 1kHz and H=5 oersted. Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 9
12 Fair-Rite Products Corp. Your Signal Solution 95 MATERIAL A low loss MnZn ferrite material for power applications up to 2kHz with low temperature variation. New type 95 Material is a low loss power material, which features less power loss variation over temperature (25-12 C) at moderate flux densities for operation below 2 khz. Shapes available in 95 material are Toroids, U cores, Pot Cores, RM, PQ, EFD, EP. 95 Material Characteristics Property Unit Symbol Value Initial Permeability µ i B < 1gauss Flux Density gauss B Field Strength oersted H 5 Residual Flux Density gauss B r 8 Coercive Force oersted H c.13 Loss Factor 1-6 Frequency MHz.1 Temperature Factor of Initial Permeability (25-6ºC) 1-6 / ºC 2.5 Curie Temperature ºC T cρ > 22 Resistivity ohm-cm 2 1 Complex Permeability vs. Frequency 5 Initial Permeability vs. Temperature E+4 1.E+5 1.E+6 1.E+7 Frequency (Hz) Measured on an 18/1/6mm toroid using HP 4284A and HP 4291A Temperature (ºC) Measured on an 18/1/6mm toroid at 1kHz. Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 1
13 95 MATERIAL A low loss MnZn ferrite material for power applications up to 2kHz with low temperature variation. 7 Amplitude Permeability vs. Flux Density 1 Power Loss Density vs. Flux Density 6 1ºC 2kHz 1kHz 5 1 5kHz 4 25ºC 3 25kHz B (gauss) 5 Measured on an 18/1/6mm toroid at 1kHz. Power Loss Density vs. Temperature B (gauss) Measured on an 18/1/6mm toroid using the Clarke Hess 258 VAW at 1ºC. Flux Density vs. Temperature kHz, 2G 4 B (gauss) 3 2 2kHz, 1G 2 1 1kHz, 1G Temperature (ºC) Measured on an 18/1/6mm toroid using the Clarke Hess 258 VAW at 1ºC Temperature (ºC) Measured on an 18/1/6mm toroid at 1kHz and H=5 oersted. Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 11
14 Fair-Rite Products Corp. Your Signal Solution POWER LOSS vs TEMPERATURE 25 1kHz/1g 78, 98, 95, 97, 79 Materials ºC 6 2kHz/1g 98, 95, 97, 79 (3kHz/5g) Materials ºC Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 12
15 POWER LOSS vs TEMPERATURE kHz/5g, 79 5kHz/5g Materials ºC Fair-Rite Products Corp. Phone: 888-FAIRRITE ( )/ Fax: 888-FERRITE ( )/ P.O. Box 288, One Commercial Row, Wallkill, NY ferrites@fair-rite.com 13
16 POT CORES P9/5S, P11/7S, P14/8, P18/11, P22/13, P26/16, P3/19, P36/22, P42/29 Pot cores have found application in all types of inductive devices. The core configuration provides a high degree of self-shielding. It also facilitates gapping to enhance utility for a variety of magnetic designs. Pot cores can be supplied with the center post gapped to a mechanical dimension. Pot cores can also be supplied to an A L value, these would be supplied in sets. A L value is measured at 1 khz, B < 1 gauss. Row Part Number (1) (2) (3) (4) (5) (6) (7) Dimensions Fig. Generic Size A B C D E F G H 1 P9/5S 9.15 ± ± ± min 7.5 min 3.8 ± ± min.295 min P11/7S 11.1 ± P14/8 14. ± P18/ ± P22/ ± P26/ ± P3/19 3. ± ± ± ± ± ± ± ± ± ± ± ± min.811 min 2.3 ± ± ± ± ± ± ± ± min.587 min 18.2 ± ± min.984 min 4.6 ± ± ± ± ± ± ± ± ± ± ± min.145 min 2.9 ± ± ± ± ±.2.22 Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 14
17 Row Part Number (8) (9) Dimensions Fig. Generic Size A B C D E F G H 2 P36/ ± ± ± ± min 15.9 ± ± ± min P42/ ± ± ± ± ± ± ± ± Table Continued... Row Part Number (1) (2) (3) (4) (5) (6) (7) (8) (9) Magnetic Core Parameters l/a(cm -1 ) l e(cm) A e(cm 2 ) V e(cm 3 ) A min(cm 2 ) A L(nH) ±25% 125 ±25% 14 ±25% ±25% 165 ±25% 18 ±25% ±25% 195 ±25% 21 ±25% ±25% 27 ±25% 34 ±25% ±25% 41 ±25% 5 ±25% ±25% 5 ±25% 55 ±25% ±25% 58 ±25% 75 ±25% ±25% 85 ±25% 1 ±25% ±25% 86 ±25% 112 ±25% Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 15
18 RM CORES RM4, RM5, RM6, RM8, RM1, RM12, RM14 RM (Rectangular Modulus) cores allow better shielding than E type geometries while also providing easier winding accessibility and better power dissipation than a pot core configuration. Fair-Rite s standard RM cores all have a solid center post and standard height, low profile and alternate materials are available upon request. RM cores can be supplied with the center post gapped to a mechanical dimension. RM cores can also be supplied to an A L value, these would be supplied in sets. A L value is measured at 1 khz, B < 1 gauss. Row Part Number (1) (2) (3) (4) (5) Dimensions Fig. Generic Size A B C D E F G J 1 RM ± ± ± ± ± ± min 9.6 ± min RM ± RM ± RM ± RM ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± min.236 min 8.4 min.331 min 9.8 min.386 min 12.5 min.492 min 12.5 ± ± ± ± Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 16
19 Row Part Number (6) (7) Dimensions Fig. Generic Size A B C D E F G J 1 RM ± ± ± ± ± ± min 29.2 ± min RM ± ± ± ± ± ± min.669 min ± Table Continued... Row Part Number (1) (2) (3) (4) (5) (6) (7) Magnetic Core Parameters l/a(cm -1 ) l e(cm) A e(cm 2 ) V e(cm 3 ) A min(cm 2 ) A L(nH) ±25% 12 ±25% 113 ±25% ±25% 177 ±25% 195 ±25% ±25% 247 ±25% 26 ±25% ±25% 31 ±25% 35 ±25% ±25% 43 ±25% 49 ±25% ±25% 55 ±25% 636 ±25% ±25% 62 ±25% 75 ±25% Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 17
20 PQ CORES PQ2/16, PQ2/2, PQ26/2, PQ26/25, PQ32/2, PQ32/3, PQ35/35, PQ4/4, PQ5/5 PQ cores were developed for use in power applications. The large surface area to volume of the core aids in heat dissipation. PQ cores are employed both in filter and transformer designs for switch mode power supplies. PQ cores can be supplied with the centerpost gapped to a mechanical dimension. PQ cores can also be supplied to an A L value, these would be supplied in sets. A L value is measured at 1 khz, B < 1 gauss. A Row Part Number (1) (2) (3) (4) (5) Generic Size PQ2/ ±.4.87 PQ2/2 2.5 ±.4.87 PQ26/ ± PQ26/ ± PQ32/2 32. ± Dimensions A B C D E F G 8. ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± min.472 min 12. min.472 min 15.5 min.61 min 15.5 min.61 min 19. min.748 min Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 18
21 Row Part Number (6) (7) (8) (9) Generic Size PQ32/3 32. ± PQ35/ ± PQ4/4 4. ± PQ5/5 5. ± Dimensions A B C D E F G ± ± ± ± ± ± ± ± ± ± ± ± ± ± min min 44. ± ± ± ± ± min.748 min 23.5 min.925 min 27.2 min 1.71 min 32. min 1.26 min Table Continued... Row Part Number (1) (2) (3) (4) (5) (6) (7) (8) (9) Magnetic Core Parameters l/a(cm -1 ) l e(cm) A e(cm 2 ) V e(cm 3 ) A min(cm 2 ) A L(nH) ±25% 343 ±25% 388 ±25% ±25% 292 ±25% 35 ±25% ±25% 551 ±25% 65 ±25% ±25% 467 ±25% 6 ±25% ±25% 6 ±25% 79 ±25% ±25% 45 ±25% 65 ±25% ±25% 51 ±25% 62 ±25% ±25% 43 ±25% 52 ±25% ±25% 672 ±25% 8 ±25% Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 19
22 E Cores EF12.6, EF16, E 187, EF2, EF25, EF32, E33/13, E 375, E42/15, E42/2, E55/21, E65/27 The E core geometry offers an economical design approach for inductive applications in a variety of power designs. Part number is for a single core. E cores can be supplied with the center post gapped to a mechanical dimension. E cores can also be supplied to an A L value, these would be supplied in sets. A L value is measured at 1 khz, B < 1 gauss. A Row Part Number (1) (2) (3) (4) (5) (6) (7) Generic Size EF ±.35.5 EF ± E19/5 19. ± EF2 2. ± EF ± EF ± E33/ ± Dimensions A B C D E F 6.35 ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± min.346 min 11.3 min.445 min 13.8 min.543 min 14.1 min.555 min 17.5 min.689 min 22.7 min.894 min 22.8 min.898 min 3.6 ± ± ± ± ± ± ± Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 2
23 Row Part Number (8) (9) (1) (11) (12) Generic Size E35/ ± E42/ ± E42/2 42. ± E55/ ± E65/ ± Dimensions A B C D E F ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± min 1. min 29.5 min min 29.5 min min 37.5 min min 44.2 min 1.74 min 9.4 ± ± ± ± ± Table Continued... Row Part Number (1) (2) (3) (4) (5) (6) (7) (8) (9) (1) (11) (12) Magnetic Core Parameters l/a(cm -1 ) l e(cm) A e(cm 2 ) V e(cm 3 ) A min(cm 2 ) A L(nH) ±25% 8 ±25% ±25% 1 ±25% ±25% 12 ±25% 14 ±25% ±25% 145 ±25% ±25% 19 ±25% ±25% 28 ±25% 335 ±25% ±25% 42 ±25% 5 ±25% ±25% 29 ±25% 35 ±25% ±25% 46 ±25% ±25% 52 ±25% ±25% 65 ±25% ±25% 79 ±25% Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 21
24 EFD CORES EFD1, EFD12, EFD15, EFD2, EFD25, EFD3 EFD (Economical Flat Design) cores have been designed to maximize volume in a low profile geometry. EFD cores allow maximum throughput power density with reasonably low mass for board level installation. EFD cores can be supplied with the center post gapped to a mechanical dimension. EFD cores can also be supplied to an A L value, these would be supplied in sets. A L value is measured at 1 khz, B < 1 gauss. Row Part Number (1) (2) (3) (4) (5) (6) Generic Size EFD1 1.5 ± EFD ± EFD ± EFD2 2. ± EFD ± EFD3 3. ± Dimensions A B C D E F K 5.2 ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 22
25 Table Continued... Row Part Number (1) (2) (3) (4) (5) (6) Magnetic Core Parameters l/a(cm -1 ) l e(cm) A e(cm 2 ) V e(cm 3 ) A min(cm 2 ) A L(nH) ±25% 54 ±25% 61 ±25% ±25% 73 ±25% 85 ±25% ±25% 91 ±25% 15 ±25% ±25% 12 ±25% 14 ±25% ±25% 225 ±25% 265 ±25% ±25% 215 ±25% 255 ±25% Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 23
26 PLANAR CORES EE14/7, EE18/8, EE22/11, EE32/13, EE38/16, EE43/19. EE64/21 EI 14/5, EI 18/6, EI 22/7, EI 32/1, E 64/15 ER9.5, ER11, ER14.5 Planar EE cores, and Planar EI cores, with their low profile are suitable for board level installation allowing assembly without the need for plastic coilformers and can also allow windings integrated into multi-level PCBs. Planar ER cores with their low mass and low profile are suitable for Surface Mount installations in low power filter and transformer applications. Planar EE and ER core part number is for a single core. Planar EI core part number is for a set. Planar EE, ER and EI cores can be supplied with the center post gapped to a mechanical dimension, or supplied as sets gapped for an A L value. A L value is measured at 1 khz, B < 1 gauss. Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 24
27 A Row Part Number (1) (2) (3) (4) (5) (6) (7) (8) (9) (1) (11) (12) (13) (14) (15) Dimensions Fig. Generic Size A B C D E F G 1 EE14/7 14. ± ±.1 5. ± min 1.52 min 3. ± min.414 min EE18/8 18. ± EE22/ ± EE32/ ± EE38/ ± EE43/ ± EE64/ ± EI 14/5 14. ± EI 18/6 18. ± EI 22/ ± EI 32/ ± EI 64/ ± ER ± ER ± ER ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± min.71 min 3.2 ± ± ± ± ± min.75 min 1.8 min.71 min 3.2 ± ± ± ± ± ± min.539 min 16.8 ± min.965 min 3.23 min 1.19 min 34.4 min min 53.8 ± min.414 min 13.7 min.539 min 16.8 ± min.965 min 53.8 ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± min.276 min 7.9 min.312 min n/a n/a Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 25
28 Table Continued... Row Part Number (1) (2) (3) (4) (5) (6) (7) (8) (9) (1) (11) (12) (13) (14) (15) Magnetic Core Parameters l/a(cm -1 ) l e(cm) A e(cm 2 ) V e(cm 3 ) A min(cm 2 ) A L(nH) ±25% 11 ±25% 13 ±25% ±25% 27 ±25% 33 ±25% ±25% 46 ±25% 55 ±25% ±25% 64 ±25% 76 ±25% ±25% 88 ±25% 11 ±25% ±25% 77 ±25% 87 ±25% ±25% 148 ±25% 18 ±25% ±25% 144 ±25% 16 ±25% ±25% 33 ±25% 38 ±25% ±25% 55 ±25% 62 ±25% ±25% 73 ±25% 87 ±25% ±25% 18 ±25% 222 ±25% ±25% 9 ±25% 95 ±25% ±25% 125 ±25% 135 ±25% ±25% 143 ±25% 161 ±25% Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 26
29 A Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 27
30 ETD CORES ETD29, ETD34, ETD39, ETD44, ETD49, ETD54, ETD59 ETD cores have been designed to make optimum use of a given volume of ferrite material for maximum throughput power, specifically for forward converter transformers. The structure, which includes a round center post, approaches a nearly uniform cross-sectional area throughout the core and provides a winding area that minimizes winding losses. ETD cores are used mainly in switched-mode power supplies and permit off-line designs where IEC and VDE isolation requirements must be met. ETD cores can be supplied with the center post gapped to a mechanical dimension. ETD cores can also be supplied to an A L value, these would be supplied in sets. A L value is measured at 1 khz, B < 1 gauss. Row Part Number (1) (2) (3) (4) Generic Size ETD ± ETD ± ETD ± ETD ± Dimensions A B C D E F 15.8 ± ± ± ± ± ± ± ± ± ± ± ± min.866 min 25.6 min 1.8 min 29.3 min min 32.5 min 1.28 min 9.5 ± ± ± ± Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 28
31 Row Part Number (5) (6) (7) Generic Size ETD ± ETD ± ETD59 (EER6) Dimensions A B C D E F 59.8 ± ± ± ± ± ± ± ± ± ± min min 4.5 min min 43.6 min min 16.3 ± ± ± Table Continued... Row Part Number (1) (2) (3) (4) (5) (6) (7) Magnetic Core Parameters l/a(cm -1 ) l e(cm) A e(cm 2 ) V e(cm 3 ) A min(cm 2 ) A L(nH) ±25% 22 ±25% 29 ±25% ±25% 26 ±25% 357 ±25% ±25% 3 ±25% 36 ±25% ±25% 38 ±25% 51 ±25% ±25% 4 ±25% 57 ±25% ±25% 54 ±25% 65 ±25% ±25% 695 ±25% 843 ±25% Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 29
32 EER CORES EER25.5/18, EER28/28, EER28/34, EER35/42, EER4/46, EER42/44, EER49/54 EER cores, similar to ETD cores, have been designed to make optimum use of a given volume of ferrite material for maximum throughput power. The structure, which includes a round center post, approaches a nearly uniform cross-sectional area that minimizes winding losses. EER cores can be supplied with the center post gapped to a mechanical dimension. EER cores can also be supplied to an A L value, these would be supplied in sets. A L value is measured at 1 khz, B < 1 gauss. A Row Part Number (1) (2) (3) (4) (5) Generic Size EER ± EER28/ ± EER28/ ± EER35/ ± EER4/46 4. ± Dimensions A B C D E F 9.3 ± ± ± ± ± ± ± ± ± ± ± ± ± ± ± min.78 min 21.2 min.835 min 21.2 min.835 min 25.3 min.996 min 29.5 min min 7.5 ± ± ± ± ± Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 3
33 Row Part Number (6) (7) Generic Size EER42/ ± EER49/ ± Dimensions A B C D E F 22. ± ± ± ± ± ± min 1.21 min 36.5 min min 15.2 ± ± Table Continued... Row Part Number (1) (2) (3) (4) (5) (6) (7) Magnetic Core Parameters l/a(cm -1 ) l e(cm) A e(cm 2 ) V e(cm 3 ) A min(cm 2 ) A L(nH) ±25% 18 ±25% 22 ±25% ±25% 28 ±25% 35 ±25% ±25% 271 ±25% 335 ±25% ±25% 26 ±25% 32 ±25% ±25% 36 ±25% 42 ±25% ±25% 41 ±25% 59 ±25% ±25% 535 ±25% 65 ±25% Fair-Rite Products Corp. PO Box 288, One Commerci al Row, Wallkill, NY Phone: (888) FAIR RITE / (845) Fax: (888) FERRITE / (845) Web: 31
Connector EMI Suppression Plates
1 To reduce conducted EMI, D type and other types of suppression plates are available in several sizes and pin layouts. Impedance specification applies to all holes. They are tested for impedance with
More informationBroadband Ferrite Toroidal Cores For Non-Tuned Circuits and EMI Filters
roadband Ferrite Toroidal Cores 1/8 1. 31 Material Characteristics A MnZn ferrite designed specifically for EMI suppression applications from as low as 1 Mz up to 500 Mz. This material does not have the
More informationMulti-Aperture/Binocular Ferrite Cores 1/5
Multi-Aperture/inocular Ferrite Cores 1/5 1. 43 Material Characteristics This NiZn is our most popular ferrite for suppression of conducted EMI from 20 to 250. This material is also used for inductive
More informationTSC International North Magnetics Blvd. Wadsworth IL 60083Tel (847) Fax (847)
TSC International TSC International is a manufacturer of magnetic materials for all frequencies. Our many end markets include: automotive, computer, lighting, telecommunications, instrumentation, industrial
More informationNATIONAL MAGNETICS GROUP, INC.
NATIONAL MAGNETICS GROUP, INC. MANUFACTURERS OF MAGNETIC AND ADVANCED MATERIALS AFFILIATE: TCI CERAMICS, INC. To Whom it May Concern: Enclosed please find an electronic version of our existing catalog
More informationSection Pot Cores Low Level Applications
The information contained in this section is primarily concerned with the design of linear inductors for high frequency LC tuned circuits using ferrite pot cores. Magnetics has arranged the data in this
More informationNaNOcRysTallINE VITROPERM. EMc PROducTs. advanced MaTERIals THE KEy TO PROGREss
NaNOcRysTallINE VITROPERM EMc PROducTs advanced MaTERIals THE KEy TO PROGREss VITROPERM NaNOcRysTallINE EMc PROducTs VacuuMscHMElZE GmbH & co. KG (Vac) is a leading global manufacturer of modern magnetic
More informationCSC Soft Magnetic Powder Core CSC Core Division
CSC Soft Magnetic Powder Core CSC Core Division Ⅰ. Soft Magnetic Powder Cores Ⅱ. CSC Soft Magnetic Powder Cores Ⅲ. Applications of CSC Cores Ⅳ. CSC Specialty Special shape Cores Ver. 2018. 04. I. Soft
More informationNANOCRYSTALLINE VITROPERM EMC COMPONENTS ADVANCED MATERIALS THE KEY TO PROGRESS
NANOCRYSTALLINE VITROPERM EMC COMPONENTS ADVANCED MATERIALS THE KEY TO PROGRESS VACUUMSCHMELZE NANOCRYSTALLINE VITROPERM EMC COMPONENTS VACUUMSCHMELZE GmbH & Co. KG (VAC) is one of the worldwide leading
More informationTemperature time profile this determines the grain growth, i.e. their final size in the order of some µm, and the properties of grain boundaries.
Custom Services for Magnetic Components A user guide to soft magnetic materials (part 3 of 4) Ferrites Soft magnetic ferrites are principally a ceramic material, i.e. sintered grains of non metallic (semiconducting)
More information3C95 3C97 Extreme ferrites for extreme conditions
3C95 Extreme ferrites for extreme conditions Low power loss, wide temperature for power conversion FERROXCUBE is a member of the Yageo Group, which is among the world's strongest suppliers of high quality
More informationMAGNETIC CORE DIMENSIONAL EFFECTS FLUX PROPAGATION IN FERRITES
MAGNETIC CORE DIMENSIONAL EFFECTS FLUX PROPAGATION IN FERRITES 2018-03-03 - Marcin Kącki, Marek Ryłko, Edward Herbert, John Hayes, Charles Sullivan SMA Magnetics Sp. z o.o. Content 1 2 3 4 5 6 Introduction
More informationFerrite EMI Cable Cores
Ferrite EMI Cable Cores About Laird Laird is a global technology business focused on enabling wireless communication and smart systems, and providing components and systems that protect electronics. Laird
More informationFigure 1. PART NO. A B C D (min) E (min) F L (nom) M (min)
Technical Bullet BULLETIN NO. KMC-E1 MAGNETICS KOOL Mµ E-CORES Introduction B C Kool Mµ powder cores are made of a ferrous alloy powder, which has low losses at elevated temperatures. Kool Mµ E- cores
More informationDivision of Spang & Company. Core Selection for Saturating Transformers
Division of Spang & Company Core Selection for Saturating Transformers A Division of Spang & Company Core Selection for Saturating Transformers The advent of semiconductors opened the door to a wide variety
More informationWOUND CORES STRIP WOUND CORES STRIP W
WOUND CORES STRIP WOUND CORES STRIP W x www.mag-inc.com Visit Magnetics website for a wealth of easy to access information on soft magnetic cores and materials All product specifications for Magnetics
More informationMuShield s High Permeability Magnetic Shielding per ASTM A753 Alloy Type 4
MuShield s High Permeability Magnetic Shielding per ASTM A753 Alloy Type 4 Available in coil, sheet, rod, billet, wire, and bar form, MuShield s High Permeability Magnetic Shielding is a soft magnetic
More informationDesigner and Manufacturer of electrical components and PCBAs
Designer and Manufacturer of electrical components and PCBAs Who We Are TOEC group was Founded in 1949. Began by designing and selling fax machine with Chinese language THMC was Founded in 1990. Began
More informationHOEGANAES INSULATED POWDER COMPOSITES CHARACTERISTICS AND ELECTROMAGNETIC APPLICATION GUIDELINES
HOEGANAES INSULATED POWDER COMPOSITES CHARACTERISTICS AND ELECTROMAGNETIC APPLICATION GUIDELINES HOEGANAES INSULATED POWDER COMPOSITES INTRODUCTION The molecular field theory was developed nearly years
More informationMAGNETIC COMPONENTS FOR POWER ELECTRONICS
MAGNETIC COMPONENTS FOR POWER ELECTRONICS MAGNETIC COMPONENTS FOR POWER ELECTRONICS by Alex Goldman Ferrite Technology Worldwide, US.A. SPRINGER SCIENCE+BUSINESS MEDIA, LLC ISBN 978-1-4613-5280-8 ISBN
More informationSpin Wave Line Width Hk oe (Nominal Value)
DATA SHEET Microwave Garnets Aluminum Doped Composition and Type Number Magnetization 4πMs (Gauss) Lande G-factor g-eff Line Width h Oe @ -3 db Dielectric Constant ε Dielectric Loss Tangent Tan δ = ε /ε
More informationShielded SMD Power Inductor
Features -Directly connected electrode on ferrite core -Available in magnetically shielded -Low DC resistance -Suitable for large current -Available on tape and reel for auto surface mounting Applications
More informationAPPROVED FOR PUBLIC RELEASE. CASE
Engineering Note E-530 Page 1 of 3 Digital Computer Laboratory Massachusetts Institute of Technology Cambridge, Massachusetts SUBJECT: To: Prom: MAGNETIC MATERIALS IDE HIGH-SPEED PULSE CIRCUITS (Presented
More informationNew Materials and Design Tools for Magnetic Materials Suitable for GaN and SiC Switching Frequencies
New Materials and Design Tools for Magnetic Materials Suitable for GaN and SiC Switching Frequencies APEC 2017 Industry Session ID 1100 Christopher G. Oliver Director of Technology Micrometals, Incorporated
More informationSoft Ferrite Cores Mr. Probal Mukherjee, Head, Technical, Speedofer Components Pvt. Ltd.
Soft Ferrite Cores Mr. Probal Mukherjee, Head, Technical, Speedofer Components Pvt. Ltd. Plot No: 101 & 102, Toy City, Ecotech III, Greater Noida 201306, Uttar Pradesh, India. probal@speedofer.com, +919830876431
More information26 lairdtech.com More Info: EXAMPLE APPLICATION PART NUMBER SYSTEM EXAMPLE
FERRITE EMI CABLE CORES FERRITE EMI DISKS AND PLATES Ferrite disks and plates provide a simple, cost-effective solution for radiated and inductively-coupled electromagnetic interference. After the PC board
More informationCOMPANY PROFILE A Y A G E O C O M P A N Y
COMPANY PROFILE A Y A G E O C O M P A N Y WHO WE ARE... Company profile Building on our Philips Magnetic Components heritage, FERROXCUBE can offer customers the highest level of support in the development
More informationElectronic materials and components-inductive components
Electronic materials and components-inductive components Inductive components make use of the voltage that is generated when a field changes either on the same piece of wire (self-induction) or in a nearby
More informationSMSS POWDER E-CORE and BLOCK CORE
Arnold Technical Bulletin SMSS POWDER E-CORE and BLOCK CORE INTRODUCTION Arnold s SMSS powder E-cores and Block cores are made of an alloy powder which has low losses at elevated temperature and has relatively
More informationEMC PRODUCTS. Advanced Materials The Key to Progress
EMC PRODUCTS based on NANOCRYSTALLINE VITROPERM Advanced Materials The Key to Progress The Company VACUUMSCHMELZE We are a global company with our headquarters in Hanau, Germany. We currently have approximately
More informationSoft Magnetic Powder Core
2011. 09. Changsung Corp. Soft Magnetic Powder Core 1. Toroidal Core Design 2. Special Shape Powder Core 3. Solar Inverter & Magnetic Materials 4. Q & A -CSC- 1. Toroidal Core Design 1. Soft Magnetic Materials
More informationCorporate Concept. Monthly production capacity is 80 tons for Ni-Zn Ferrite Cores and 100 tons for Mn-Zn Ferrite Cores.
Corporate Concept Yeng Tat Electronics Co., Ltd. is organized by a group of enthusiastic people who have already been engaged in the field of ferrite industry with technical and manufacturing experiences.
More informationStandard Specification for Low-Carbon Magnetic Iron 1
Designation: A 848 01 Standard Specification for Low-Carbon Magnetic Iron 1 This standard is issued under the fixed designation A 848; the number immediately following the designation indicates the year
More informationHigh Performance Amorphous and Nanocrystalline Cores
High Performance Amorphous and Nanocrystalline Cores Zhuhai King Magnetics Technology Co., Ltd. Company Profile Zhuhai King Magnetics Technology Co., Ltd. locates at Zhuhai High Technology Zone, mainly
More informationNanocrystalline magnetic materials versus ferrites in power electronics
Procedia Earth and Planetary Science 1 (2009) 1357 1361 Procedia Earth and Planetary Science www.elsevier.com/locate/procedia The 6 th International Conference on Mining Science & Technology Nanocrystalline
More informationThe International Magnetics Association
The International Magnetics Association An operating group of: The Transformer Association 1300 Sumner Avenue Cleveland, OH 44115 U.S.A. Telephone: (216) 241-7333 Facsimile: (216) 241-0105 info@transformer-assn.org
More informationInductive Absorbers for Megawatt applications. Inductive Absorbers for Megawatt applications
Presented at MAGNETEC GmbH, Langenselbold www.magnetec.de 05/2011 Dr. Fe 1/15 Content Application 1: big Wind Turbines in the MW range Application 2: big Inverters for Photovoltaic Power Plants Application
More informationUsing Magnetic Cores at High Temperatures
A Division of Spang & Company Technical Bulletin BULLETIN NO. CG-06 Using Magnetic Cores at High Temperatures All cores are not the same. Designers need to know the differences in order to make the best
More informationPFC & Output Choke Cores
Nanocrystalline AMOS AMOSENSE Nanocrystalline Nanocrystalline Common Mode Chokes Product Summary Description AMC series amorphous choke cores are made of thin iron-based amorphous alloy. This type of iron-based
More informationInduction Heating. Jean Callebaut, Laborelec. 1 Introduction Physical principles Induction Installations... 5
Induction Heating Jean Callebaut, Laborelec 1 Introduction... 2 2 Physical principles... 2 2.1 Electromagnetic induction... 2 2.2 The Joule-effect... 3 2.3 Penetration depth... 3 3 Induction Installations...
More informationApplication Information Guidelines for Designing a Concentrator for High-Current Sensing Applications with an Allegro Hall-Effect Sensor IC
Application Information Guidelines for Designing a Concentrator for High-Current Sensing Applications with an Allegro Hall-Effect Sensor IC By Cedric Gillet and Andreas Friedrich Introduction As with any
More informationFERRITE CORES AND TILES
FERRITE CORES AND TILES 1. Shape factor (Se/Le): larger the shape factor, the higher the impedance. For the case of 1 pass through the core, a snug fit, and longer core is recommended as space permits.
More informationWhy is the Ferrite Material Development for GaN so Difficult?
Why is the Ferrite Material Development for GaN so Difficult? JC Sun 04. December 2018 power electronics conference in München 1 content Introduction Bs&T Demand on ferrite material development Need for
More informationEnergy Efficiency of Amorphous Metal Based Transformers. R. Hasegawa Metglas, Inc 440 Allied Drive, SC USA
Energy Efficiency of Amorphous Metal Based Transformers R. Hasegawa Metglas, Inc 440 Allied Drive, SC 29526 USA October 2004 OVERVIEW Basics Introduction Amorphous versus crystalline magnetic material
More informationThe International Magnetics Association
The International Magnetics Association An operating group of: The Transformer Association 1300 Sumner Avenue Cleveland, OH 44115 U.S.A. Telephone: (216) 241-7333 Facsimile: (216) 241-0105 info@transformer-assn.org
More informationTDK s Environmental Technologies
TDK s Environmental Technologies Ferrite An Amazing Magnetic Material Ferrite is a magnetic material that was invented in 1930 and was initially used in radios. Today, ferrite is once again in the limelight
More informationIntroduction. Our History
Management System ISO 91:28 ISO 141:24 ISO/TS 16949:29 Introduction Our Company ACME Electronics Corporation, a subsidiary of public listed company, USI Corporation, Taiwan is one of the world s leading
More informationProducts Introduction of Composite Material for Automotive
NTN TECHNICAL REVIEW No.83(2015) [ New Product ] Products Introduction of Composite Material for Automotive Kayo SAKAI* Takahiro GOTOU** Takuya ISHII*** Eiichirou SHIMAZU* Hajime ASADA** NTN group produces
More informationVDM Magnifer 50. Material Data Sheet No August 2002 Edition
VDM Magnifer 50 Material Data Sheet No. 9002 August 2002 Edition 2 Magnifer 50 Magnifer 50 is a soft-magnetic nickel-iron alloy with about 48 % Ni. It has a saturation induction of 1.55 T and high permeability.
More informationSoft Materials and Applications
Soft Materials and Applications O. Geoffroy Grenoble Electrical Engineering (G2Elab) Materials Application Fields Transformation of Energy Actuation Recording Magnetic Properties Soft Hard Coupling properties
More informationNew Low Profile Low ESL Tantalum Multi-anode Capacitor Structure Improves Cost/Performance Ratio
New Low Profile Low ESL Tantalum Multi-anode Capacitor Structure Improves Cost/Performance Ratio T.Zedníček, L.Marek, S.Zedníček AVX Czech Republic s.r.o., Dvorakova 328, 563 01 Lanskroun, Czech Republic
More informationBonded Neo Magnetization Guide
Bonded Neo Magnetization Guide 1 Presentation Outline 1. Magnetizing Systems 2. Fixture Design 3. Construction 4. Testing 5. Design Study 2 Magnetizing Systems A typical magnetizing system consists of
More informationLamination-Based Technology For High Performance Metallic Magnetic Cores
Lamination-Based Technology For High Performance Metallic Magnetic Cores Florian Herrault and Mark G. Allen School of Electrical and Computer Engineering Georgia Institute of Technology Atlanta, GA 30332-0250
More information(TRMI) Multilayer Ferrite Chip Inductors. Token Electronics Industry Co., Ltd. Version: January 13, Web:
Version: January 13, 2017 (TRMI) Multilayer Ferrite Chip Inductors Token Electronics Industry Co., Ltd. Web: www.token.com.tw Email: rfq@token.com.tw Taiwan: No.137, Sec. 1, Zhongxing Rd., Wugu District,
More informationSP5MAT SP6MAT SP5MATB 5.25 speaker, black housing SP6MATB 6.5 speaker, black housing
MA Series 5.25 or 6.5 7/25V Commercial ABS Plastic Back Can Speakers SP5MAT SP6MAT SP5MATB 5.25 speaker, black housing SP6MATB 6.5 speaker, black housing Features ABS flame retardant back can Easy select
More informationRectangular Modulus Cores (RM Cores Soft Ferrite)
RM (Rectangular modular) cores arose due to the demand for coil formers with integrated pins that allow for efficient winding and high PCB packing densities. Clamps engaging in recesses in the core base
More informationMetal Composite Type Power Choke Coils
ETQ-PM Series Inductor Product Guide Metal Composite Type Power Choke Coils AEC-Q200 Compliant For Use In Harsh Environments Vibration Resistance of 10G ~ 30G (5Hz 2kHz) Maximum Operating Temperature of
More informationShielding and measurement of magnetic fields
Shielding and measurement of magnetic fields Workshop Solution Showcase Dr. Swen Graubner, SEKELS GmbH 06.05.2015 Berlin Basic shielding principles Influences: Alloy Geometry Ideal shielding Magnetic field
More informationCorporate Concept. Monthly production capacity is 80 tons for Ni-Zn Ferrite Cores and 100 tons for Mn-Zn Ferrite Cores.
Corporate Concept Yeng Tat Electronics Co., Ltd. is organized by a group of enthusiastic people who have already been engaged in the field of ferrite industry with technical and manufacturing experiences.
More informationSP5MAT SP6MAT SP5MATB 5.25 speaker, black housing SP6MATB 6.5 speaker, black housing
MA Series 5.25 or 6.5 7/25V Commercial ABS Plastic Back Can Speakers SP5MAT SP6MAT SP5MATB 5.25 speaker, black housing SP6MATB 6.5 speaker, black housing Features Speco Technologies Multi-Application Series
More informationTape Wound Core Specialists
Tape Wound Core Specialists ISO9001:2008 Registered Edition: June 2017 17030 Muskrat Avenue, Adelanto, California 92301 ph: 760.246.6373 fx: 760.246.6378 www.mkmagnetics.com info@mkmagnetics.com Tape
More informationCustom magnetic solutions designed for performance and reliability
Custom magnetic solutions designed for performance and reliability Power Switching Filtering Custom magnetics specialists While standard transformers and inductors meet most of today s typical electronic
More informationEddy-Current Sensors and their Applications to Force and Stress Measurement in Steel Reinforced Concrete.
Eddy-Current Sensors and their Applications to Force and Stress Measurement in Steel Reinforced Concrete. H. C. Schoenekess, W. Ricken, J.-G. Liu, W. -J. Becker Division of Electrical Engineering and Software
More informationParametric analysis of magnetic field mitigation shielding for underground power cables
Parametric analysis of magnetic field mitigation shielding for underground power cables J. C. del Pino López 1, P. Cruz Romero 1 and P. Dular 2 1 Department of Electrical Engineering, University of Seville
More informationFerrites and accessories
Ferrites and accessories EP 7 Core and accessories Series/Type: B65839, B65840 Date: September 2006 Data Sheet EPCOS AG 2006. Reproduction, publication and dissemination of this data sheet and the information
More informationMA Series 5.25 or /25V Commercial ABS Plastic Back Can Speakers
simply unique. MA Series 5.25 or 6.5 7/25V Commercial ABS Plastic Back Can Speakers SP5MAT SP6MAT 5.25 speaker 6.5 speaker Features Speco Technologies Multi-Application Series was designed to make the
More informationGlossary of Magnetic Terms
AlNiCo Permanent magnets based upon alloys containing aluminum, nickel, cobalt, iron + additions. They are very stable materials and are not sensitive to moderate temperature changes or mildly corrosive
More informationLow Impedance Ta Capacitors to Serve the Needs of the Electronics Industry
Low Impedance Ta Capacitors to Serve the Needs of the Electronics Industry Randy Hahn, and Jonathan Paulsen KEMET Electronics Corp PO Box 5928 Greenville, SC 29606 Tel: +1 864-963-6300 Fax: +1 864-228-4333
More informationELECTROMAGNETIC NOISE SUPPRESSION SHEETS
Near field EMI suppression with easy assembly. Simply attach, sandwich and wrap around Magnetic metal filler typehigh performance Soft ferritestandard P19 P20 Ferrite sheet P22 P23 17 MAGNETIC FOIL Effective
More informationINTRODUCTION:- 1.Classification of magnetic material Diamagnetic
INTRODUCTION:- Ferrites are ferromagnetic material containing predominantly oxides iron along with other oxides of barium, strontium, manganese, nickel, zinc, lithium and cadmium.ferrites are ideally suited
More informationNdFeB. Title Here. for High Temperature Motor Applications. Author Venue. Steve Constantinides. Date. with Dale Gulick
NdFeB Title Here for High Temperature Motor Applications Author Venue Steve Constantinides Date with Dale Gulick SMMA Fall Technical Conference November 3-5, 24 1 Arnold Magnetic Technologies Topics Magnet
More informationPhase error in current transformers with nanocrystalline alloys core
Phase error in current transformers with nanocrystalline alloys core Thiago C. Batista, Benedito A. Luciano 2, Raimundo C. S. Freire 2 Coordenação de pós-graduação em Engenharia Elétrica (Universidade
More informationB H. Magnetic materials
Magnetic materials In engineering applications the ferromagnets are used because of their high μ, which enable high magnetic induction to be obtained with only modest magnetic field. (Their ability to
More informationModelling the power losses in the ferromagnetic materials
Materials Science-Poland, 35(2), 2017, pp. 398-404 http://www.materialsscience.pwr.wroc.pl/ DOI: 10.1515/msp-2017-0050 Modelling the power losses in the ferromagnetic materials KALINA DETKA, KRZYSZTOF
More informationEMI Conducted and Radiated Emissions
EMI Conducted and Radiated Emissions Mark Rine Product Manager VAC Magnetics March 2016 ADVANCED MATERIALS THE KEY TO PROGRESS Abstract This presentation overviews the EMC Conducted and Radiated Emissions
More informationWCNDT Durban, South Africa April 2012
WCNDT Durban, South Africa 16 2 April 212 Innovative Flexible Eddy Current Probes for the Inspection of Complex Parts B. Marchand, JM. Decitre, O. Casula C. Ruaud 2 CONTEXT NDT using Eddy Current method:
More informationNew Low Profile Low ESL Multi-Anode Mirror Tantalum Capacitor
New Low Profile Low ESL Multi-Anode Mirror Tantalum Capacitor T.Zedníček, L.Marek, S.Zedníček AVX Czech Republic s.r.o., Dvorakova 328, 563 1 Lanskroun, Czech Republic Phone: +42 465 358 126 Fax: +42 465
More informationLOSSES IN FERRITE ROD ANTENNAS
LOSSES IN FERRITE ROD ANTENNAS The losses in ferrite rod antennas are much higher than predicted by the accepted theory. This article shows that the increased loss is due to an increase in the copper losses
More informationFerrite Cores For High Power High Power Cores
FETURES Large size ferrite cores developed for reactors and transformers used in high power units. Please contact us for machinability of non-standard special forms. MTERIL HRTERISTIS (Typical) Material
More informationZero Gauss Chambers MAGNETIC SHIELD CORPORATION. Perfection Mica Company
MAGNETIC SHIELD CORPORATION Perfection Mica Company 740 North Thomas Drive Bensenville, Illinois 60106-1643 U.S.A. FAX 630-766-2813 Phone 630-766-7800 www.magnetic-shield.com E-mail: shields@magnetic-shield.com
More informationTELCON STRIP WOUND TOROIDAL CORES
TOROIDAL CORES 1. INTRODUCTION Telcon high permeability strip wound toroidal cores are manufactured to the highest international standards, in a range of alloys and sizes developed to meet the most stringent
More informationTechniques for Detection of Surface Defects in Tubing and Pipe
FOERSTER INSTRUMENTS I N C O R P O R A T E D Techniques for Detection of Surface Defects in Tubing and Pipe By: Ronald B Peoples Foerster Instruments Inc. ASNT Level III Certificate # MM-1322 140 INDUSTRY
More information7. FERROMAGNETIC MATERIALS. aligned atomic dipoles
7. FERROMAGNETIC MATERIALS 7.1 What are ferromagnets? Earlier, in Section 6.2, we considered the following visualization of atomic dipoles in a material in a uniform applied B field: aligned atomic dipoles
More informationFERROXCUBE DATA SHEET. RM8/ILP RM, RM/I, RM/ILP cores and accessories. Supersedes data of September Sep 01
FERROXCUBE DATA SHEET RM, RM/I, RM/ILP cores and accessories Supersedes data of September 24 28 Sep 1 CORE SETS Effective core parameters SYMBOL PARAMETER VALUE UNIT Σ(I/A) core factor (C1).44 mm 1 V e
More informationSUPPLY NETWORK ANALYZER CVM-SP SERIES INSTRUCTION MANUAL ( M / 01A
SUPPLY NETWORK ANALYZER CVM-SP SERIES INSTRUCTION MANUAL ( M 981 310 / 01A ) (c) CIRCUTOR S.A. ----- CVM-SP & CVM-SP-RS485-C -------- --- Page No. 1 1.- MAIN FEATURES... 2 1.1.- Parameters measured and
More informationOverview. Benefits. Applications. Tantalum Through-Hole Capacitors Molded Radial T330 Molded Radial
Overview The KEMET T330 polar-type, radial lead, rectangular Precision Molded Tantalum (PMT) capacitors are primarily designed for applications that demand full use of the premium space available in printed
More informationFerrites and accessories
Ferrites and accessories ETD 39/20/13 Core and accessories Series/Type: B66363, B66364 Date: September 2006, December 2008 %BUB4IFFU EPCOS AG 2006. Reproduction, publication and dissemination of this data
More informationPiezoelectric Polycrystalline (PZT) Components and Wafers
Piezoelectric Polycrystalline (PZT) Components and Wafers Industry Leading Piezoelectric Polycrystalline (PZT) Component Manufacturing and Engineering CTS offers high-performance piezoelectric materials
More informationNANOPERM - Design Considerations for advanced EMI filter chokes
NANOPERM - Design Considerations for advanced EMI filter chokes May 26th 2004 PCIM, Nuremberg Fritz Rauscher MAGNETEC GmbH, Booth 525 in Hall 12 MAGNETEC GmbH www.magnetec.de 05/2004/ra 1/15 Content of
More informationLeadership in Soft Magnetic Alloys
Leadership in Soft Magnetic Alloys Carpenter Technology Corporation offers a wide selection of soft magnetic alloys to meet your material specifications. Choose from high permeability alloys, shielding
More informationQUANTITATIVE HARDENING-DEPTH-MEASUREMENTS UP TO 4 mm BY MEANS OF MICRO. Gerd Dobmann, Rolf Kern, Iris Altpeter, and Werner Theiner
QUANTITATIVE HARDENING-DEPTH-MEASUREMENTS UP TO 4 mm BY MEANS OF MICRO MAGNETIC MICROSTRUCTURE MULTIPARAMETER ANALYSIS (MA) Gerd Dobmann, Rolf Kern, Iris Altpeter, and Werner Theiner Fraunhofer-Institut
More informationSoft Magnetic Cobalt-Iron Alloys. VACOFLUX and VACODUR
Soft Magnetic Cobalt-Iron Alloys VACOFLUX and VACODUR 05/2016 Soft Magnetic Cobalt-Iron Alloys Table of Contents INTRODUCTION 3 MAGNETIC PROPERTIES 6 DC magnetic properties of strip material... 7 DC magnetic
More informationInternational Journal of Engineering Trends and Technology (IJETT) Volume 48 Number 6 June 2017
Study of Linear Array of Microstrip Hexagonal Patch Antenna Printed on LiTi Ferrite under External Magnetic Biasing N K Saxena 1, R.K. Verma 1, N. Kumar 2 and P.K.S. Pourush 1 1 Microwave Lab, Department
More informationMaterials and Device Research for Electrical System Applications at the National Energy Technology Laboratory
Sensing Material Enabled Harsh Environment Sensors Nanocrystals Intergranular Phase Magnetic Material Enabled Power Conversion Devices Materials and Device Research for Electrical System Applications at
More informationFERRITES. June Mn-Zn. Large Size Ferrite Cores for High Power. PQ series
June 2016 Mn-Zn Large Size Ferrite Cores for High Power PQ series (2/8) REMINDERS FOR USING THESE PRODUCTS Please be sure to read this manual thoroughly before using the products. The products listed on
More informationISO INTERNATIONAL STANDARD. Non-destructive testing of welds Eddy current testing of welds by complex-plane analysis
INTERNATIONAL STANDARD ISO 17643 First edition 2005-07-01 Non-destructive testing of welds Eddy current testing of welds by complex-plane analysis Contrôle non destructif des assemblages soudés Contrôle
More informationFerrites and accessories
Ferrites and accessories PQ 32/20 Cores and coil former Series/Type: Date: Version: B65879A, B65880E...April-2008,_September-2008 1,_2 Content of header bars 1 and 2 of data sheet will be automatically
More informationPOWER ELECTRONIC TRAINER Model: PET-1700
POWER ELECTRONIC TRAINER Model: PET-1700 III. MODULE BOARD 1. Size: 13.4"/.34m X 9.45"/.24m X 1.9"/.048m Approx. 2. Board frame: PS plastic extrusion, 0.118"/3mm thick. 3. Dimensions shown BELOW. I. FEATURES
More informationELECTRONIC POTTING & ENCAPSULATING COMPOUNDS
ELECTRONIC POTTING & ENCAPSULATING COMPOUNDS Epoxies Product UL Recognized Mix Ratio by Weight Mix Ratio by Volume Mixed Viscosity @ 25 C (in cps) Gel Time @25 C Glass Transition Temp. (Tg) 0155 No 1 Component
More informationFerrites and Accessories
Ferrites and Accessories Cores and coil former Series/Type: B65883A, B65884E Date: 2009-06-05 Version: 1 Content of header bars 1 and 2 of data sheet will be automatically entered in headers and footers!
More information