Simulation of galvanic corrosion of magnesium coupled to a steel fastener in NaCl solution
|
|
- Lynn Day
- 5 years ago
- Views:
Transcription
1 468 Jia, Atrens, Song and Muster Materials and Corrosion 2005, 56, No. 7 Simulation of galvanic corrosion of magnesium coupled to a steel fastener in NaCl solution J. X. Jia, A. Atrens*, G. Song and T. H. Muster The galvanic corrosion of magnesium alloy AZ91D coupled to a steel fastener was studied using a boundary element method (BEM) model and experimental measurements. The BEM model used the measured polarization curves as boundary conditions. The experimental program involved measuring the total corrosion rate as a function of distance from the interface of the magnesium in the form of a sheet containing a mild steel circular insert (5 to 30 mm in diameter). The measured total corrosion rate was interpreted as due to galvanic corrosion plus self corrosion. For a typical case, the self corrosion was estimated typically to be 230 mm/y for an area surrounding the interface and to a distance of about 1 cm from the interface. Scanning Kelvin Probe Force Microscopy (SKPFM) revealed microgalvanic cells with potential differences of approximately 100 mv across the AZ91D surface. These microgalvanic cells may influence the relative contributions of galvanic and self corrosion to the total corrosion of AZ91D. 1 Introduction The galvanic corrosion of magnesium alloys is a major concern in the application of magnesium in the automotive industry. Magnesium is the most active structural metal and thus would suffer serious galvanic corrosion when in contact with a different metal [1, 2]. More specifically, the galvanic corrosion of magnesium caused by fasteners is of the most concern in automotive applications. Many types of fasteners have been developed and several evaluations of the various fastener systems in terms of mass loss of magnesium have been reported by Hawke and Ruden [3], Skar [4] and Gao et al. [5]. Skar [4] showed that 6000 series aluminum alloy fasteners caused negligible galvanic corrosion of magnesium in salt spray test conditions. However, for many applications steel fasteners are desired due to their inherent mechanical properties. The use of steel fasteners with an aluminium plated coating has been shown to have poor compatibility with magnesium [5]. Hawke and Ruden [3] found steel fasteners with zinc or tin-zinc alloy coatings to have an effective compatibility with magnesium in salt water exposure. In addition to characterizing galvanic corrosion by mass loss, the maximum depth of corrosion is also an important characteristic, which can be evaluated by an examination of the cross section corrosion penetration [5]. In neutral or alkaline salt solutions, the corrosion of magnesium alloys is characterized by pitting [6]. Stable corrosion pits have been observed to initiate at flaws adjacent to a fraction of * A. Atrens, J. X. Jia, G. Song, CRC for Cast Metals Manufacturing (CAST), Division of Materials, School of Engineering, The University of Queensland, St Lucia, QLD 4072 (Australia) T. H. Muster, Corrosion Science and Surface Design, CSIRO Manufacturing and Infrastructure Technology, Graham Road, Highett, Victoria, 3190 (Australia) DOI: /maco the intermetallic particles as a result of the breakdown of passivity. The pitting corrosion could occur in combination with the galvanic corrosion, and can be initiated by the galvanic corrosion. The total corrosion in the area of galvanic corrosion can be considered to be made up of the following two components: (1) galvanic corrosion and (2) self corrosion [3-5]. In this approach the galvanic corrosion is defined as that part of the corrosion which is directly caused by the coupling of the magnesium to a steel fastener. The self corrosion is defined as the extra corrosion. Both the galvanic corrosion and the self corrosion may take the form of more or less general corrosion, or the form of localized corrosion or pitting corrosion. The total corrosion is often measured by mass loss of the test sample. The galvanic corrosion of specimens can be measured using various electrochemical methods as in our prior work [7 9], and can be modelled using numerical methods such as Boundary Element Methods as used in our prior work [7 11]. Astley [12, 13], Fu [14], Adey [15] and Kasper [16] have indicated that numerical methods are promising for the prediction of galvanic corrosion and more specifically, galvanic current distributions. With the development of computer technology, a boundary element based program, BEASY, has become widely used in galvanic corrosion studies since the early 1980s [17]. Our previous study showed the BEASY program to provide promising correlations with experimental data [7, 10]. In the present study the BEASY program was used to calculate the galvanic current distribution on magnesium alloy AZ91D surfaces. Based on our prior work [7 11], the expectation was that the BEASYprogram could provide a good prediction of the galvanic current distribution. In addition, the total corrosion was measured experimentally as a function of distance from the magnesium-steel interface. AZ91D has a two-phase microstructure, consisting of a matrix of a grains and b-phase Mg 17 Al 12 intermetallics [1, 2]. As a result, the localized potential differences resulting from the heterogeneous composition of the surface will influence both galvanic and self corrosion processes. In an effort to further understand the total corrosion and the galvanic corrosion caused by a steel fastener in 5% NaCl solution, information on the magnitude of localized potential differences was ob- F 2005 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
2 Materials and Corrosion 2005, 56, No. 7 Simulation of galvanic corrosion of magnesium 469 tained by performing Scanning Kelvin Probe Force Microscopy (SPKFM) over the surface of AZ91D specimens. 2 Experimental approach 2.1 Galvanic corrosion assembly HPDC AZ91D and mild steel were the test materials. Each galvanic assembly consisted of an 11 cm 12 cm plate of AZ91D containing a mild steel circular insert in the center of the plate. The diameters of the mild steel inserts were 5 mm, 10 mm and 30 mm. The steel was insulated from the AZ91D by a thin layer of Teflon and molded in resin. The AZ91D plate and steel electrode were electrically connected by a wire and formed a galvanic couple. 2.2 Electrolytes 5% NaCl solution was used because it represents a severe corrosive environment. Also, previous studies have shown reasonable agreement between the BEM calculation and the experimental measurement using this electrolyte [7, 10]. That is, the galvanic current is stable and there is little corrosion product interference, which makes it easier to distinguish the effect of geometry. The 5% NaCl solution was made with analytical grade reagents and deionized water. The conductivity of the 5% NaCl solution, as measured using a platinic conductivity cell, was determined to be S cm. 2.3 Corrosion assessment After 48 hours of immersion test in a solution of 5% NaCl to a depth of 10 mm, the corrosion product was removed from the surface of each specimen. The corrosion morphology was recorded. Each specimen was sectioned into 8 pie-shaped pieces. The corroded area on each cross section was measured in 1 mm sections using an optical microscope and Leica Qwin image analysis software. The average corrosion rate for each sample was calculated by integrating the damage depth along the length of each cross section. 2.4 Polarization curve measurement Fig. 1(a) presented the experimental arrangement for polarization curves measurement. Further detail on this technique can be found in previous studies [7, 10]. Both potentiodynamic and galvanostatic polarization curves were measured. The potentiodynamic curves provide an estimate of the current density values for the subsequent measurement of the galvanostatic polarization curves. For each applied constant current, the potential was measured as a function of time. The galvanostatic polarization curves were obtained by plotting the potential versus current density at 5 to 10 minutes for the 5% NaCl solution, when steady state had been attained. A 1287 electrochemical interface was used to measure the polarization curves. A REF201 Ag/AgCl reference electrode was used. To eliminate the influence of solution resistance on the measured polarization curve, the solution resistance was measured using a 1255B Frequency Response Analyzer. The polarization curves were corrected for potential drop caused by the solution resistance. The solution resistance corrected galvanostatic polarization curves for AZ91D and steel 4150 in 5% NaCl solution, were obtained by plotting current density versus potential. Fig. 1(b) provides a typical polarization curve. 2.5 AFM and SKPFM measurements Fig. 1. (a). Schematic arrangement for measuring polarization curves; (b) Galvanostatic polarization curve measurements (data points) in 5% NaCl solution. Curves represent typical potentiodynamic polarization curves, at a scan rate of 2 mv/s Atomic Force Microscopy (AFM) and Scanning Kelvin Probe Force Microscopy (SKPFM) investigations were performed on a Digital Instruments Nanoscope III Multimode instrument with an Extender TM electronics module. Contact potential differences were captured using a Lift-Mode TM height of 100 nm. To achieve acceptable tracking of the surface topography when using lift mode, a considerable contact force of up to 80 nn was applied between tip and sample, and scan rates as low as 0.4 Hz were used. Further operational details have been published elsewhere [18 21]. All contact potential differences presented in this study were scaled relative to the potential of a Pt-coated silicon cantilever tip (NT-MDT), and for ease of presentation, contact potential differences were plane-fitted and plotted with the most negative potential being the most noble. For SKPFM analysis, six AZ91 samples with dimensions of 10 mm 10 mm 1 mm were cut from larger AZ91 blocks. The thin slices were polished using a sequence of diamond pastes (15 lm, 3 lm and 1 lm) and OP-S (Struers) oxide polish. After the final polish the samples were rinsed with deionised water, analytical grade ethanol and dried using high purity argon. Individual samples were then immersed in 5% NaCl solution for one minute, rinsed with deionised water and dried using high purity argon.
3 470 Jia, Atrens, Song and Muster Materials and Corrosion 2005, 56, No. 7 Fig. 2. Schematic of the mesh for the BEM model 3 BEM model Three-dimensional BEM models were generated in the BEASY environment to represent the real specimens immersed in 10 mm 5% NaCl solution. The mesh sizes were defined by the minimum 0.1 cm to maximum 0.7 cm for all the three models. These dimensions were found to be fine enough to give reliable and reproducible galvanic current gradients. The tolerance of the potential was set as 0.01 mv. Fig. 2 illustrates the mesh for the galvanic specimen with f ¼ 30 mm steel insert. 4 Results and discussion 4.1 Overiew Figs. 3a, 4a and 5a illustrate the physical appearance of the AZ91D plate after 48 hours immersion in 5% NaCl solution. The samples exhibited an unevenly distributed corrosion due to the galvanic couple with steel. Corrosion damage was deeper at the AZ91D-steel interface, and included pitting further away from the interface. Corrosion damage to AZ91D was concentrated around the steel and was largely confined to within about 1 to 2 cm radial distance from the interface. The radial extent of the corrosion was similar in all these cases. There were some pits distributed randomly out on the remaining surface of the AZ91D. However, most of the remaining area was free from corrosion and retained its original appearance. This indicated that the effective distance of galvanic corrosion was limited to a distance of 1 to 2 cm. Most of the remaining area seemed to be protected as a cathode. A similar finding was also reported by Hawke [22], who derived an effective insulating space of about 5 mm for magnesium coupled with cast iron. Figs. 3 to 5 compare the overview of the physical appearance of the corrosion with the area of galvanic corrosion as simulated by the BEM model. This comparison shows that the computer model provided reasonable predictions of the effective galvanic corrosion area for each of the three different sizes of steel cathodes in 5% NaCl solution. Fig. 3. Comparison of the galvanic corrosion area for the BEM model and the immersion test for 30 mm diameter steel cathode. a) experimental immersion test and b) the BEM model. The extent of the galvanic corrosion for the BEM model was estimated by the point where the galvanic current becomes essentially zero 4.2 Distribution of corrosion Figs. 6 to 14 illustrate the typical distribution of total corrosion and provide a comparison between the total corrosion rate on the corroded area for each small cross section, and the galvanic current derived from the BEM modeling calculation for AZ91D coupled with 5 mm, 10 mm and 30 mm diameter steel inserts. The total corrosion rate for each small cross section was calculated from the corresponding measured corroded area. This total corrosion rate includes galvanic and self corrosion, both of which may be in the form of pitting corrosion and general corrosion. Analysis of the cross sectional damage indicated that the corrosion of AZ91D included unevenly distributed pitting corrosion. The maximum corrosion depth occurred close to but not always immediately adjacent to the magnesium-steel interface as shown in Figs. 6, 7, 9, 10, 12 and 13. A similar finding was also reported by Ault [18]. The maximum depth occurred within about 1 mm away from the interface. The depth distribution of the galvanic pitting corrosion was quite randomly scattered on the surface and there was no obvious relationship between the depth and the pit location within a 2 cm distance. Figs. 8 and 11 provide a comparison of the BEM model predicted galvanic corrosion and the experimental measurement of the total corrosion for AZ91D coupled with 5 mm and 10 mm steel inserts, respectively. Both the BEM model and the experimental measurements indicate maximum corrosion
4 Materials and Corrosion 2005, 56, No. 7 Simulation of galvanic corrosion of magnesium 471 Fig. 4. Comparison of the galvanic corrosion area for BEM model and the immersion test for 10 mm diameter steel cathode. a) experimental immersion test and b) the BEM model. The extent of the galvanic corrosion for the BEM model was estimated by the point where the galvanic current becomes essentially zero at the magnesium-steel interface, and both indicated a decrease in corrosion rate with increasing distance from the interface. The experimental measurements indicate a corrosion rate significantly higher than the galvanic corrosion rate, and this is interpreted as self corrosion of magnesium. This self corrosion was estimated by subtracting the galvanic corrosion (as predicted by the BEM model) from the total measured corrosion in Figs. 8 and 11. The value as estimated was 10 ma/ cm 2 at the magnesium-steel interface and similar values were estimated at a distance of 1 cm from the interface. This self corrosion corresponds to a penetration rate of 230 mm/y. Fig. 14 provides similar comparison for magnesium coupled to a 30 mm steel insert. In this case, there was reasonable agreement. 4.3 SKPFM investigation Figs. 15 and 16 present the potential distribution on the surface of the magnesium alloy derived from SKPFM measurements. The average contact potential difference between the Pt tip and polished AZ91D was 1590 mv. This value decreased slightly to 1560 mv following a one minute exposure to 5% NaCl. Comparison of the potential maps and the microstructure led to the following interpretation. In the potential Fig. 5. Comparison of the galvanic corrosion area for the BEM model and the immersion test for 5 mm diameter steel cathode. a) experimental immersion test and b) the BEM model. The extent of the galvanic corrosion for the BEM model was estimated by the point where the galvanic current becomes essentially zero maps the darker regions (corresponding to the b phase) exhibited a decreased contact potential difference in comparison to the surrounding matrix (a phase). For polished samples the contact potential difference between the a and b phases was as much as 145 mv with contact potential difference values of 1705 mv and 1560 mv for a and b phases, respectively. After exposure to 5% NaCl for one minute the difference in potential difference between a and b phases decreased to approximately 90 mv, with typical contact potential difference values of 1640 mv and 1550 mv for the a and b phases, respectively. The relationship between contact potential difference and electrochemical potentials has been explored previously by Schmutz and Frankel [20, 21]. They showed that a linear relationship existed between SKPFM measured contact potential difference values (which were measured in air) and the corrosion potential measured in NaCl aqueous solution. Therefore, contact potential difference measurements provide a platform in which to investigate local galvanic interactions on metallic surfaces. The current study indicates that the b phase has increased nobility in comparison to the a phase. Similar conclusions have been reported by Song, Atrens, and Dargusch [23]. This suggests that micro-galvanic cells may be formed between the b phase and a phase. The galvanic corrosion or pitting can be initiated and developed at the flaws next to the b phase particles and can cause accelerated corrosion of the a phase. The size, distribution and potential differences of the micro-galvanic cells associated with the b phase
5 472 Jia, Atrens, Song and Muster Materials and Corrosion 2005, 56, No. 7 Fig. 6. Image of corrosion on Mg surface coupled with 5 mm diameter steel insert (side 1) Fig. 7. Image of corrosion on Mg surface coupled with 5 mm diameter steel insert (side 2) Fig. 11. Comparison of corrosion current density between the BEM model and the experiments for Mg coupled with 10 mm diameter steel insert Fig. 12. Image of corrosion on Mg surface coupled with 30 mm diameter steel insert (side 2) Fig. 8. Comparison of corrosion current density between the BEM model and the experiments for Mg coupled with 5 mm diameter steel insert Fig. 13. Image of corrosion on Mg surface coupled with 30 mm diameter steel insert (side 1) Fig. 9. Image of corrosion on Mg surface coupled with 10 mm diameter steel insert (side 1) Fig. 10. Image of corrosion on Mg surface coupled with 10 mm diameter steel insert (side 2) Fig. 14. Comparison of corrosion current density between the BEM model and the experiments for Mg coupled with 30 mm diameter steel insert
6 Materials and Corrosion 2005, 56, No. 7 Simulation of galvanic corrosion of magnesium 473 Fig. 15. A representative contact potential difference map for the SKPFM of magnesium alloy AZ91D after immersion in 5% NaCl for one minute Fig. 16. (a), (b) and (c) show cross sections of the potential along sections representing the surface of AZ91D, as per Fig. 15
7 474 Jia, Atrens, Song and Muster Materials and Corrosion 2005, 56, No. 7 particles may influence self corrosion rates, may also influence galvanic corrosion rates and ultimately determine the relative contributions to the total corrosion rate. The corrosion rate could be higher if the micro-galvanic corrosion rate is high for some locations which can be far away from the steel as illustrated in Fig. 9. This effect is not taken into account in the BEM model. 5 Conclusion Both the BEM model and the experimental measurements of the galvanic corrosion of AZ91D coupled to steel predicted a similar distribution of the current density: a maximum at the interface and decreasing rapidly to zero within 1 to 2 cm from the interface. The total corrosion was interpreted as being due to galvanic corrosion plus self corrosion. The self corrosion was evaluated on the basis that the BEM model provides a good evaluation of the galvanic corrosion. On this basis, the self corrosion rate was evaluated to be typically 230 mm/y for the area surrounding the interface and to a distance of about 1 cm from the interface. Self corrosion rates may be controlled by localized microgalvanic corrosion processes. SKPFM confirmed the presence of microgalvanic cells on the surface of AZ91D, which appear to have potential differences in the order of 100 mv between phases in the alloy. 6 References [1] G. Song, A. Atrens, Advanced Engineering Materials 2003, 5, 837. [2] G. L. Song, A. Atrens, Advanced Engineering Materials 1999, 1, 11. [3] D. Hawke, T. Ruden, Society of Automotive Engineers, [Special Publication] SP, 1995, SP-1096, [4] J. I. Skar, Materials and Corrosion 1999, 50, 2. [5] G. Gao et al. in: The 2nd Israeli International Conference on Magnesium Science & Technology 2000, Dead Sea, Israel. [6] E. Ghali, Magnesium Alloys, 2000, 350 3, 261. [7] J. X. Jia, G. Song, A. Atrens, Materials and Corrosion 2005, 56, 259. [8] J. X. Jia, G. Song, A. Atrens, G. Chandler, D. H. StJohn, in: The First International Light Metals Technology Conference 2003, Brisbane, Australia, [9] J. X. Jia, G. Song, A. Atrens, D. H. St.John, J. Baynham, G. Chandler, Materials and Corrosion 2004, 55, 845. [10] J. X. Jia, G. Song, A. Atrens, Corrosion Science, submitted for publication. [11] J. X. Jia, G. Song, A. Atrens, D. H. StJohn, in: 13th Asian- Pacific Corrosion Control Conference, 2003, Osaka, Japan. Japan Society of Corrosion Engineering, 34. [12] D. J. Astley, Chem. Ind. (London) 1977, 13, Suppl., Seawater Cool. Chem. Plant, 4. [13] D. J. Astley, ASTM Spec. Tech. Publ. 1988, 978 (Galvanic Corros.), [14] J. W. Fu, ASTM Spec. Tech. Publ., 1988, 978 (Galvanic Corros.), [15] R. A. Adey, S. M. Niku, ASTM Spec. Tech. Publ., 1988, 978 (Galvanic Corros.), [16] R. G. Kasper, E. M. Valeriote, Galvanic Corrosion, ed. H. P. Hack. 1988, Philadelphia, American Society for Testing and Material. [17] H. P. Hack, Corros. Rev., 1997, 15, 195. [18] P. Campestrini et al., Surface and Coatings Technology 2004, 176, 365. [19] V. Guillaumin, P. Schmutz, G. S. Frankel, Journal of the Electrochemical Society 2001, 148, B163. [20] P. Schmutz, G. S. Frankel, Journal of the Electrochemical Society 1998, 145, [21] P. Schmutz, G. S. Frankel, Journal of the Electrochemical Society 1998, 145, [22] D. L. Hawke, in: 14th International DieCasting Congress and Exposition Toronto, Ontario, Canada. [23] G. Song, A. Atrens, M. Dargusch, Corros. Sci. 1999, 41, 249. (Received: December 13, 2004) W 3855
The Etching of Aluminium Alloy 2024-T3 in a Non-chromate Fe(III)-HF- HNO 3 Deoxidiser: an Atomic Force and Scanning Kelvin Microscopy Study.
Proceedings of the 9 th International Conference on luminium lloys (2004) 1243 Edited by J.F. Nie,.J. Morton and.c. Muddle Institute of Materials Engineering ustralasia Ltd The Etching of luminium lloy
The influence of Mg 17 Al 12 phase volume fraction on the corrosion behaviour of AZ91 magnesium alloy. Andrzej Kiełbus* and Grzegorz Moskal
196 Int. J. Microstructure and Materials Properties, Vol. 4, No. 2, 2009 The influence of Mg 17 Al 12 phase volume fraction on the corrosion behaviour of AZ91 magnesium alloy Andrzej Kiełbus* and Grzegorz
THE INFLUENCE OF ANODISING PARAMETERS ON THE CORROSION PERFORMANCE OF ANODISED COATINGS ON MAGNESIUM ALLOY AZ91D
THE INFLUENCE OF ANODISING PARAMETERS ON THE CORROSION PERFORMANCE OF ANODISED COATINGS ON MAGNESIUM ALLOY AZ91D Zhiming Shi, Guangling Song, and Andrej Atrens (CRC for Cast Metals Manufacturing (CAST),
Investigation of Stress Corrosion Cracking Behaviors of an AZ91 Magnesium Alloy in 0.1 kmol/m 3 Na 2 SO 4 Solution Using Slow Strain Rate Test
Materials Transactions, Vol. 49, No. 5 (2008) pp. 1052 to 1056 Special Issue on Platform Science and Technology for Advanced Magnesium Alloys, IV #2008 The Japan Institute of Metals Investigation of Stress
Laboratory Experiments in Corrosion Engineering II
Lecture - 40 Laboratory Experiments in Corrosion Engineering II Keywords: Polarization Experiments, Pitting Potentials, Microbial Corrosion. A. Electrochemical tests in a given environment Polarization
Simulation of corrosion damage, stress concentration, and fatigue crack growth
28 th ICAF Symposium Helsinki, 3 5 June 2015 Simulation of corrosion damage, stress concentration, and fatigue crack growth Sharon Mellings 1, John Baynham 1, Andres Peratta 1 1 CM BEASY, Ashurst Lodge,
Using predicted corrosion damage to determine stress concentration, fracture and crack growth
Paper No. 7800 Using predicted corrosion damage to determine stress concentration, fracture and crack growth Sharon Mellings, Andres Peratta, John Baynham, Tim Froome CM BEASY Ltd Ashurst Lodge Southampton,
A Scanning Probe Investigation of Inter-Granular Corrosion in Sensitised Stainless Steel Nuclear Fuel Cladding
A Scanning Probe Investigation of Inter-Granular Corrosion in Sensitised Stainless Steel Nuclear Fuel Cladding Ronald Clark (Final year PhD.) Professor Geraint Williams (Swansea University) Dr. Steve Walters
Galvanic corrosion evaluation of 6061 aluminum coupled to CVD coated stainless steel Elizabeth Sikora and Barbara Shaw 6/9/2016
SHAW AND ASSOCIATES CONSULTING Galvanic corrosion evaluation of 6061 aluminum coupled to CVD coated stainless steel Elizabeth Sikora and Barbara Shaw 6/9/2016 Evaluation of galvanic corrosion of aluminum
Corrosion behavior of Al Si Cu (Sn, Zn) brazing filler metals
Materials Characterization 47 (2001) 401 409 Corrosion behavior of Al Si Cu (Sn, Zn) brazing filler metals S.S. Wang, M.D. Cheng, L.C. Tsao, T.H. Chuang* Institute of Materials Science and Engineering,
Effect of Anodizing Potential on the Surface Morphology and Corrosion Property of AZ31 Magnesium Alloy
Materials Transactions, Vol. 51, No. 6 (21) pp. 119 to 1113 #21 The Japan Institute of Metals Effect of Anodizing Potential on the Surface Morphology and Corrosion Property of AZ31 Magnesium Alloy S. A.
Chapter 16 Corrosion and Degradation of Materials
Chapter 16 Corrosion and Degradation of Materials Concept Check 16.1 Question: Would you expect iron to corrode in water of high purity? Why or why not? Answer: Iron would not corrode in water of high
Improved corrosion resistance of AZ91D magnesium alloy by an aluminium-alloyed coating
Surface & Coatings Technology 200 (2006) 2834 2840 www.elsevier.com/locate/surfcoat Improved corrosion resistance of AZ91D magnesium alloy by an aluminium-alloyed Liqun Zhu a, Guangling Song b, a Department
Kinetic Characteristics of Different Materials used for Bolting Applications
Kinetic Characteristics of Different Materials used for Bolting Applications Report Kinetic Characteristics of Different Materials used for Bolting Applications Overview One of the most common problems
Microstructure and Corrosion Properties of the Plasma-MIG Welded AA5754 Automotive Alloy
Journal of Minerals and Materials Characterization and Engineering, 2015, 3, 318-325 Published Online July 2015 in SciRes. http://www.scirp.org/journal/jmmce http://dx.doi.org/10.4236/jmmce.2015.34034
CHEMICAL SPECIFICATIONS OF ZINC AND ZINC ALUMINUM ALLOYS: TABLE 1 TABLE 1
TECHNICAL BULLETIN CORROSION RESISTANCE OF ZINC And Zinc Alloys CHEMICAL SPECIFICATIONS OF ZINC AND ZINC ALUMINUM ALLOYS: TABLE 1 PROPERTIES OF ZINC ALLOYS The Mechanical and physical properties of the
Improvement of corrosion resistance of HVOF thermal sprayed coatings by gas shroud
Improvement of corrosion resistance of HVOF thermal sprayed coatings by gas shroud Jin Kawakita, Takeshi Fukushima, Seiji Kuroda, and Toshiaki Kodama National Research Institute for Materials Science Abstract
Studies on the in uence of chloride ion and ph on the corrosion and electrochemical behaviour of AZ91D magnesium alloy
Journal of Applied Electrochemistry 30: 865±874, 2000. 865 Ó 2000 Kluwer Academic Publishers. Printed in the Netherlands. Studies on the in uence of chloride ion and ph on the corrosion and electrochemical
BOUNDARY ELEMENT METHOD PREDICTIONS OF THE INFLUENCE OF THE ELECTROLYTE ON THE GALVANIC CORROSION OF AZ91D COUPLED TO STEEL
BOUNDARY ELEMENT METHOD PREDICTIONS OF THE INFLUENCE OF THE ELECTROLYTE ON THE GALVANIC CORROSION OF AZ91D COUPLED TO STEEL Jimmy X. Jia, Guangling Song, Andrej Atrens CRC for Cast Metals Manufacturing
Corrosion of. magnesium alloys. Edited by. Guang-Ling Song WOODHEAD PUBLISHING. pppvr- Oxford Cambridge Philadelphia New Delhi
Corrosion of magnesium alloys Edited by Guang-Ling Song WOODHEAD PUBLISHING pppvr- Oxford Cambridge Philadelphia New Delhi Contents Contributor contact details xiii Preface xvii Part I Fundamentals 1 Corrosion
Erosion corrosion of mild steel in hot caustic. Part II: The evect of acid cleaning
Corrosion Science 48 (2006) 2660 2675 www.elsevier.com/locate/corsci Erosion corrosion of mild steel in hot caustic. Part II: The evect of acid cleaning Rihan Omar Rihan, Srdjan NeniT The Department of
Effect of Contact between Electrode and Interconnect on Performance of SOFC Stacks
DOI: 10.1002/fuce.201000176 Effect of Contact between Electrode and Interconnect on Performance of SOFC Stacks W. B. Guan 1, H. J. Zhai 1, L. Jin 1,T.S.Li 1, and W. G. Wang 1 * 1 Ningbo Institute of Material
Influence of Al Content on the Atmospheric Corrosion Behaviour of Magnesium-Aluminum Alloys
J. Mater. Sci. Technol., Vol.25 No.2, 2009 225 Influence of Al Content on the Atmospheric Corrosion Behaviour of Magnesium-Aluminum Alloys Ruiling Jia 1,3), Chuanwei Yan 2) and Fuhui Wang 1,2) 1) College
The Viability of Mg Alloy with Nano/Sub-micron Structure as a new Material for Practical Applications
The Viability of Mg Alloy with Nano/Sub-micron Structure as a new Material for Practical Applications E. Aghion and A. Arnon Department of Materials Engineering, Ben-Gurion University of the Negev, Beer-Sheva,
Integrated AFM and SECM for in situ studies of localized corrosion of Al alloys
Electrochimica Acta 52 (2007) 7697 7705 Integrated AFM and SECM for in situ studies of localized corrosion of Al alloys A. Davoodi a,j.pan a,, C. Leygraf a, S. Norgren b a Division of Corrosion Science,
Olympus LEXT offers new capabilities in the study of corrosion
KIMAB Olympus LEXT offers new capabilities in the study of corrosion Studying the material world Corrosion is a big problem! From metal and concrete to polymers and electronics, different forms of decay
CORROSION BEHAVIOR OF LASER SURFACE MELTED 2014 ALUMINIUM ALLOY IN T6 AND T451 TEMPERS. P.H. Chong*, Z. Liu, P. Skeldon and G. E.
CORROSION BEHAVIOR OF LASER SURFACE MELTED 2014 ALUMINIUM ALLOY IN T6 AND T451 TEMPERS P.H. Chong*, Z. Liu, P. Skeldon and G. E. Thompson Corrosion and Protection Centre, University of Manchester Institute
Corrosion Rate Measurement on C-Steel
Measurements of corrosion rate on Carbon-steel using Electrochemical (potentiodynamic Polarization, EIS etc.) technique. Corrosion Rate Measurement on C-Steel Abdullah Al Ashraf 1. Introduction: The degradation
Available online at ScienceDirect. Physics Procedia 50 (2013 )
Available online at www.sciencedirect.com ScienceDirect Physics Procedia 50 (2013 ) 421 426 International Federation for Heat Treatment and Surface Engineering 20th Congress Beijing, China, 23-25 October
Crack Initiation and Crack Propagation of Pre-corroded Ni-16Cr Alloy in 4.5%NaCl Aqueous Solution
IOSR Journal of Engineering (IOSRJEN) e-issn: 2250-3021, p-issn: 2278-8719 Vol. 3, Issue 8 (August. 2013), V2 PP 11-15 Crack Initiation and Crack Propagation of Pre-corroded Ni-16Cr Alloy in 4.5%NaCl Aqueous
Electrochemical corrosion behavior of Ni-containing hypoeutectic Al-Si alloy
J. Electrochem. Sci. Eng. X(Y) (2015) 173-179; doi: 10.5599/jese.174 Original scientific paper Open Access : : ISSN 1847-9286 www.jese-online.org Electrochemical corrosion behavior of Ni-containing hypoeutectic
SCC Initiation for X80 Pipeline Steel Under AC Application in High ph Solution
2017 2nd International Seminar on Applied Physics, Optoelectronics and Photonics (APOP 2017) ISBN: 978-1-60595-522-3 SCC Initiation for X80 Pipeline Steel Under AC Application in High ph Solution Min ZHU,
CORROSION PROTECTION OF MRI230D MAGNESIUM ALLOY BY THE PLASMA ELECTROLYTIC OXIDATION
CORROSION PROTECTION OF MRI230D MAGNESIUM ALLOY BY THE PLASMA ELECTROLYTIC OXIDATION Barbara Kazanski Traubin, Alex Lugovskoy *, Michael Zinigrad Department of Chemical Engineering, Ariel University, Ariel
INFLUENCE OF MANGANESE, ZIRCONIUM AND IRON ON THE CORROSION OF MAGNESIUM
INFLUENCE OF MANGANESE, ZIRCONIUM AND IRON ON THE CORROSION OF MAGNESIUM D.S. Gandel 1,2, N. Birbilis 1,2, M.A. Easton 1,2, M.A. Gibson 1,3 1 CAST Co-operative Research Centre, 2 Department of Materials
Some Corrosion Characteristics of Aged Aluminum Alloy 6061 in Neutral and Alkaline Solutions
Some Corrosion Characteristics of Aged Aluminum Alloy 6061 in Neutral and Alkaline Solutions K.El-Menshawy 1, A.A.El-Sayed 1, M.E.El-Bedawy 1, H. A.Ahmed 2 and S.M.El-Raghy 2 1- Metallurgy Department,
Cathodic Protection Anodes
Cathodic Protection Anodes Page no. 1 Mixed Metal Oxide Anodes (MMO) 3 Sacrificial Anodes 3 Silicon Anodes 4 Ribbon Anodes Mixed Metal Oxide Anodes (MMO) Mixed Metal Oxide Anodes are electrically conductive
Materials of Engineering ENGR 151 CORROSION ELECTRICAL PROPERTIES
Materials of Engineering ENGR 151 CORROSION ELECTRICAL PROPERTIES more anodic (active) more cathodic (inert) GALVANIC SERIES Ranking of the reactivity of metals/alloys in seawater Platinum Gold Graphite
The effect of protective coatings on galvanic corrosion for bolted components
The effect of protective coatings on galvanic corrosion for bolted components K.S. Yeung Ford Motor Company, MI, USA Abstract The increasing demands for better fuel-efficiency have led the automobile industry
Corrosion and Protection of Metal in the Seawater Desalination
IOP Conference Series: Earth and Environmental Science PAPER OPEN ACCESS Corrosion and Protection of Metal in the Seawater Desalination To cite this article: Xiangyu Hou et al 018 IOP Conf. Ser.: Earth
Effects of Galvanic Corrosion on Au-Sn Plated Contacts in Electronic Cable Interconnect
Effects of Galvanic Corrosion on Au-Sn Plated Contacts in Electronic Cable Interconnect J.H. Lau, B.Y. Kuu, W.K. Koh, Hui-Hong J.K. Li JSB Tech Pte Ltd, 20 Science Park II, Singapore 117674 August 2011
Effect of Additional Cu and Mg in Al-Mn-Si Alloy on Intergranular Corrosion Susceptibility After Heat-treatment at 473K.
Proceedings of the 2th International Conference on Aluminium Alloys, September 5-9, 200, Yokohama, Japan 200 The Japan Institute of Light Metals pp. 53-58 53 Effect of Additional and Mg in Al-Mn-Si Alloy
Tutorial Corrosion II. Electrochemical characterization with EC-Lab techniques
Tutorial Corrosion II Electrochemical characterization with EC-Lab techniques 1 OUTLINE 1. Introduction 2. Types of corrosion a) Uniform corrosion b) Localized corrosion 3. Corrosion experiment 4. EC-Lab
Available online at ScienceDirect. Procedia Engineering 184 (2017 )
Available online at www.sciencedirect.com ScienceDirect Procedia Engineering 184 (2017 ) 418 422 Advances in Material & Processing Technologies Conference Development of Al-Zn-Cu Alloy for Low Voltage
A Study of Corrosion and Pitting Initiation of AA2024-T3 Using Atomic Force Microscopy
Journal of the Electrochemical Society, Vol. 149, No. 6, 2002, pp. B239-B247. ISSN: 0013-4651 DOI: 10.1149/1.1471546 http://www.electrochem.org/ http://www.ecsdl.org/getpdf/servlet/getpdfservlet?filetype=pdf&id=jesoan00014900000600b239000001&idty
Heat Transfer Simulation to Determine the Impact of Al-5Mg Arc Sprayed Coating onto 7075 T6 Al Alloy Fatigue Performance
11 th International LS-DYNA Users Conference Simulation (5) Heat Transfer Simulation to Determine the Impact of Al-5Mg Arc Sprayed Coating onto 7075 T6 Al Alloy Fatigue Performance G. D Amours, B. Arsenault,
Supporting Information
Copyright WILEY-VCH Verlag GmbH & Co. KGaA, 69469 Weinheim, Germany, 2013. Supporting Information for Adv. Funct. Mater., DOI: 10.1002/adfm.201302405 Self-Assembly Mechanism of Spiky Magnetoplasmonic Supraparticles
CORROSION RESISTANCE OF PLASMA NITRIDED AND NITROCARBURIZED AISI 316L AUSTENITIC STAINLESS STEEL
CORROSION RESISTANCE OF PLASMA NITRIDED AND NITROCARBURIZED AISI 316L AUSTENITIC STAINLESS STEEL F.A.P. Fernandes 1*, J. Gallego 2, G.E. Totten 3, C.A. Picon 2, L.C. Casteletti 1 1 Department of Materials
Transactions on Engineering Sciences vol 13, 1996 WIT Press, ISSN
Improvement in corrosion resistance of CrN coating steel with multi-stage deposition method and its corrosion fatigue strength M. Sonobe, K. Shiozawa, K. Motobayashi Department of Mechanical Systems Engineering,
Institute for Diagnostic Imaging Research
Institute for Diagnostic Imaging Research (Repair applications of the LPCS process) Roman Gr. Maev, Emil Strumban, Volf Leshchinskiy, and Dmitry Dzhurinskiy CSAT 2014, Worcester, MA Low Pressure Cold Spray
Aluminium Alloy Corrosion of Aircraft Structures
Aluminium Alloy Corrosion of Aircraft Structures WITpress WIT Press publishes leading books in Science and Technology. Visit our website for the current list of titles. www.witpress.com WITeLibrary Home
Surface Treatments and Coatings (Lightweight Materials)
Surface Treatments and Coatings (Lightweight Materials) Surender Maddela Ph.D., Lightweight Materials Processing, GM Research and Development Center, Warren, MI- USA Materials Research Center, Missouri
Corrosion of Metals. Industrial Metallurgists, LLC Northbrook, IL Copyright 2013 Industrial Metallurgists, LLC
Corrosion of Metals Industrial Metallurgists, LLC Northbrook, IL 60062 847.528.3467 www.imetllc.com Copyright 2013 Industrial Metallurgists, LLC Course structure Learning modules 1. Introduction to corrosion
A Study of Performance of Aluminium Anode by Addition of Zinc in Sea Water
A Study of Performance of Aluminium Anode by Addition of Zinc in Sea Water G.M.Pradeep 1, R.M.Ravindran 2, A.Gokulram 3, R.Rajesh 4, B.YogeshEswaran 5, L. Samson Joshua 6 1 Assistant professor, Dept of
Galvanic Corrosion Prevention Guide for Water Cooling Systems
WATER COOLED DEVICES Galvanic Corrosion Prevention Guide for Water Cooling Systems November 2017 White Paper Created by Helen E. Kane, Advanced Energy Industries, Inc. Water Cooled Devices Abstract This
Validation of a Galvanic Corrosion Model for AA2024 and CFRP with Localised Coating Damage
Validation of a Galvanic Corrosion Model for AA2024 and CFRP with Localised Coating Damage Siva PALANI 1, Theo HACK 2, Andres PERATTA 3, Robert ADEY 4, John BAYNHAM 5, Hubertus LOHNER 6 1 EADS, Germany,
Corrosion Damage Monitoring of Stainless Steel by Acoustic Emission
Corrosion Damage Monitoring of Stainless Steel by Acoustic Emission Kaige Wu A, Seung-mi Lee B, Won-Sik Lee C, Dong-Pyo Hong D and Jai-Won Byeon A Abstract In this work, the acoustic emission signals of
THE RELATIONSHIP BETWEEN SURFACE TREATMENTS AND CORROSION RESISTANCE OF HOT-DIP GALVANIZED STEEL. Amirreza Bakhtiari
Association of Metallurgical Engineers of Serbia AMES Scientific paper UDC: 620.197.2:669.141; 620.193 THE RELATIONSHIP BETWEEN SURFACE TREATMENTS AND CORROSION RESISTANCE OF HOT-DIP GALVANIZED STEEL Amirreza
M.N.Singh, D.K.Basu, A.K.Bhattmishra and S. K.Narang CORROSION RESISTANT ELECRODEPOSITED ZINC COATING FROM ZINC DROSS
..:: CORCON 2UU2 ::.. SPEAKERS (Basic Corrosion) 04 TECHNICAL A SPEAKERS A ABOUT NA( M.N.Singh, D.K.Basu, A.K.Bhattmishra and S. K.Narang M. N. Singh, D. K. Basu, A. K. Bhattmishra and S. K. Narang National
Accepted Manuscript. Corrosion mechanism and evaluation of anodized magnesium alloys. Guang-Ling Song, Zhiming Shi
Accepted Manuscript Corrosion mechanism and evaluation of anodized magnesium alloys Guang-Ling Song, Zhiming Shi PII: S0010-938X(14)00168-1 DOI: http://dx.doi.org/10.1016/j.corsci.2014.04.008 Reference:
Corrosion Behaviour of aluminium alloys used in heat-exchangers Joana Catarina Videira Madeira. 1. Introduction to Aluminium Science and Technology
Corrosion Behaviour of aluminium alloys used in heat-exchangers Joana Catarina Videira Madeira 1. Introduction to Aluminium Science and Technology Although many metals can alloy with aluminium, only few
Transactions on Modelling and Simulation vol 8, 1994 WIT Press, ISSN X
Invited paper Analysis of stray current corrosion problems using the boundary element method J. Trevelyan* & H.P. Hack& ^ Computational Mechanics, Inc., Billerica, Massachusetts, USA ^ Naval Surface Warfare
Electrochemical Considerations
17-1 CHAPTER 17 CORROSION AND DEGRADATION OF MATERIALS PROBLEM SOLUTIONS Electrochemical Considerations 17.1 (a) Oxidation is the process by which an atom gives up an electron (or electrons) to become
Corrosion Resistance Improvement of Galvanised Steel by Doped Silane Pre-Treatments
2015 2 nd International Conference on Material Engineering and Application (ICMEA 2015) ISBN: 978-1-60595-323-6 Corrosion Resistance Improvement of Galvanised Steel by Doped Silane Pre-Treatments J.F.
ROLES OF PASSIVATION AND GALVANIC EFFECTS IN LOCALIZED CO 2 CORROSION OF MILD STEEL
Paper No. 08332 ROLES OF PASSIVATION AND GALVANIC EFFECTS IN LOCALIZED CO 2 CORROSION OF MILD STEEL Jiabin Han, Yang Yang, Srdjan Nesic and Bruce N Brown Institute for Corrosion and Multiphase Technology,
Effects of thickness of Al thermal spray coating for STS 304
Effects of thickness of Al thermal spray coating for STS 304 Min-Su HAN 1, Yong-Bin WOO 1, Seok-Cheol KO 2, Young-Jae JEONG 3, Seok-Ki JANG 1, Seong-Jong KIM 1 1. Division of Marine Engineering, Mokpo
Correlation between Neutral Salt Spray (NSS) Test and Potentiostat Dynamic Test for Corrosion on Zinc Plated Steel
Correlation between Neutral Salt Spray (NSS) Test and Potentiostat Dynamic Test for Corrosion on Zinc Plated Steel Prithiviraj D [1], Rajendran R [2], Venugopal [3] Department of Mechanical Engineering,
Improvement of anticorrosion and adhesion to magnesium alloy by phosphate coating formed at room temperature
Improvement of anticorrosion and adhesion to magnesium alloy by phosphate coating formed at room temperature NIU Li-yuan( ), LIN Ji-xing( ), LI Yong( ), SHI Zi-mu( ), XU Lin-chao( ) Advanced Material Research
COMPOSITION, STRUCTURE AND SOME CORROSION PROPERTIES OF AS-RECEIVED NdFeB MAGNETIC MATERIAL AND PROTECTIVE ZnAl COATING
COMPOSITION, STRUCTURE AND SOME CORROSION PROPERTIES OF AS-RECEIVED NdFeB MAGNETIC MATERIAL AND PROTECTIVE ZnAl COATING Stanislav LASEK, Miroslav KURSA, Kateřina KONEČNÁ VŠB-TU Ostrava, 17. listopadu 15/2172,
Roles of Alloying Elements on the Corrosion Behavior of Amorphous W Zr (15 33)Cr Alloys in 1 M NaOH Solution
Roles of Alloying Elements on the Corrosion Behavior of Amorphous W Zr (15 33)Cr Alloys in 1 M NaOH Solution Raju Ram Kumal and Jagadeesh Bhattarai * Central Department of Chemistry, Tribhuvan University,
Corrosion Behavior of Cu Zr Ti Nb Bulk Glassy Alloys
Materials Transactions, Vol. 44, No. 4 (3 pp. 749 to 753 #3 The Japan Institute of Metals Corrosion Behavior of Cu Bulk Glassy Alloys Chunling Qin 1; *, Katsuhiko Asami 1, Tao Zhang 1, Wei Zhang 2 and
Regional Cathodic Protection Design of a Natural Gas Distribution Station
CORROSION SCIENCE AND TECHNOLOGY, Vol.16, No.5(2017), pp.235~240 pissn: 1598-6462 / eissn: 2288-6524 [Research Paper] DOI: https://doi.org/10.14773/cst.2017.16.5.235 Regional Cathodic Protection Design
Sealing of Hard Chrome Plating
Sealing of Hard Chrome Plating Background Hard chrome coating is used to protect steel components from corrosion in salt and acid medium. It is extensively applied on steel cylinders, gears, used in many
Effect of Oxidizer on the Galvanic Behavior of Cu/Ta Coupling during Chemical Mechanical Polishing
Journal of The Electrochemical Society, 153 6 B193-B198 2006 0013-4651/2006/153 6 /B193/6/$20.00 The Electrochemical Society Effect of Oxidizer on the Galvanic Behavior of Cu/Ta Coupling during Chemical
Effect of Modified AA5356 Filler on Corrosion Behavior of AA6061 Alloy GTA Welds
Vol.2, Issue.6, Nov-Dec. 2012 pp-4429-4433 ISSN: 2249-6645 Effect of Modified AA5356 Filler on Corrosion Behavior of AA6061 Alloy GTA Welds 1 N. Ramanaiah 2 B. Balakrishna, 3 K. Prasad Rao 1 Professor
Influence of Silicon on Intergranular Corrosion for Aluminum Alloy*
UACJ Technical Reports, Vol.1 21 pp. 8-16 論 文 Influence of Silicon on Intergranular Corrosion for Aluminum Alloy* Yoshiyuki Oya** and Yoichi Kojima** An alternative fluorocarbon refrigerant of a heat exchanger
Surface Engineering Challenges of Dissimilar Materials Joints
Surface Engineering Challenges of Dissimilar Materials Joints Michele Curioni & LATEST2 team Corrosion And Protection Centre School of Materials The University of Manchester M13 9PL, Manchester, UK Microstructure
An Investigation on Metallic Bipolar Plate Corrosion in Simulated Anode and Cathode Environments of PEM Fuel Cells using Potential-pH Diagrams
Int. J. Electrochem. Sci., 1(2006)447-455 www.electrochemsci.org An Investigation on Metallic Bipolar Plate Corrosion in Simulated Anode and Cathode Environments of PEM Fuel Cells using Potential-pH Diagrams
Mat E 272 Lecture 26: Oxidation and Corrosion
Mat E 272 Lecture 26: Oxidation and Corrosion December 11, 2001 Introduction: Environmental degradation of materials is one of the most costly failure modes, accounting for over 5 percent of the total
Grain Refiner Fade in Aluminium Castings
Proceedings of the 9 th International Conference on Aluminium Alloys (2004) Edited by J.F. Nie, A.J. Morton and B.C. Muddle Institute of Materials Engineering Australasia Ltd 705 Grain Refiner Fade in
Frictional Coefficients of the Passive Titanium Surfaces Evaluated with In-situ and Ex-situ Nano-scratching Tests
Volume 6 Paper C097 Frictional Coefficients of the Passive Titanium Surfaces Evaluated with In-situ and Ex-situ Nano-scratching Tests M. Seo, Y. Kurata and M. Chiba Graduate School of Engineering, Hokkaido
AL LM6 HOLLOW CYLINDER FABRICATED USING CENTRIFUGAL CASTING
AL LM6 HOLLOW CYLINDER FABRICATED USING CENTRIFUGAL CASTING Saifulnizan Jamian 1, Safwan Yutiman 2 and Haffidzudin Hehsan 3 1 Crashworthiness and Collisions Research Group, Universiti Tun Hussein Onn Malaysia,
Re-alkalisation technology applied to corrosion damaged concrete
Concrete Repair, Rehabilitation and Retrofitting II Alexander et al (eds) 2009 Taylor & Francis Group, London, ISBN 978-0-415-46850-3 Re-alkalisation technology applied to corrosion damaged concrete G.K.
Corrosion Control and Cathodic Protection Data Sheet
Data Sheet CORROSION CONTROL Corrosion control is the application of engineering principles and procedures to minimise corrosion to an acceptable level by the most economical method. It is rarely practical
HYDROGEN ABSORPTION INTO ALPHA TITANIUM ALLOYS
16th International Corrosion Congress September 19-24, 25, Beijing, China HYDROGEN ABSORPTION INTO ALPHA TITANIUM ALLOYS Li Yan, J. J. Noël, Z. Qin, D. W. Shoesmith*, Department of Chemistry, University
ACCELERATED CORROSION TESTING OF GALVANIC COUPLES. James F. Dante, Josh Averett, Fritz Friedersdorf, and Christy Vestal
ACCELERATED CORROSION TESTING OF GALVANIC COUPLES James F. Dante, Josh Averett, Fritz Friedersdorf, and Christy Vestal Luna Innovations 706 Forest St. Suite A Charlottesville, VA 22903 dantej@lunainnovations.com
Observations of Corrosion Fatigue Crack Initiation Processes in Metals by Means of AFM
Materials Science Research International, Special Technical Publication 1, pp.11-16 (21) General Paper Observations of Corrosion Fatigue Crack Initiation Processes in Metals by Means of AFM Yoshikazu NAKAI,
Metallurgical Influences on Anodising Qualities
Brighter ideas with aluminum Metallurgical Influences on Anodising Qualities ESTAL Congress 21./22.09.2009 Dr. mont. Andreas Tesch Content 1. Who is Novelis? 2. General Influences on the anodising result
a: potential difference before direct current is applied b: potential difference after the application of current
CATHODIC PROTECTION Cathodic protection is a proven corrosion control method for protection of underground and undersea metallic structures, such as oil and gas pipelines, cables, utility lines and structural
Effect of Annealing Process on the Corrosion Resistance of Aluminium 7075-T6 Alloy
Effect of Annealing Process on the Corrosion Resistance of Aluminium 7075-T6 Alloy Palkar Aman Manohar 1, Ghanshyam Das 2, Nitesh Kumar Sinha 3, Rohit Kumar Mishra 4 1,3,4M.Tech, Department of Materials
ROLE OF INTERMETALLIC COMPOUND ON CORROSION OF ALUMINIUM/STEEL TRANSITION JOINT USED IN NAVAL APPLICATIONS
ROLE OF INTERMETALLIC COMPOUND ON CORROSION OF ALUMINIUM/STEEL TRANSITION JOINT USED IN NAVAL APPLICATIONS Nattarat Kengkla and Napachat Tareelap* Division of Materials Technology, School of Energy, Environment
Keysight Technologies Combining Atomic Force Microscopy with Scanning Electrochemical Microscopy. Application Note
Keysight Technologies Combining Atomic Force Microscopy with Scanning Electrochemical Microscopy Application Note Introduction Scanning probe microscopy (SPM) techniques have found a broad range of applications
MMFX 2 (ASTM A 1035, GRADE 100) STEEL REBAR CORROSION PERFORMANCE TESTING IN ACCORDANCE WITH AASHTO MP 18M/MP MMFX Technologies Corporation
MMFX 2 (ASTM A 1035, GRADE 100) STEEL REBAR CORROSION PERFORMANCE TESTING IN ACCORDANCE WITH AASHTO MP 18M/MP 18-09 Prepared for: MMFX Technologies Corporation August 3, 2011 TCG # 11072 Report Prepared
2. Wet Corrosion: Characteristics, Prevention and Corrosion Rate
2. Wet Corrosion: Characteristics, Prevention and Corrosion Rate Mighty ships upon the ocean suffer from severe corrosion. Even those that stay at dockside are rapidly becoming oxide Alas, that piling
Arch. Metall. Mater., Vol. 61 (2016), No 1, p
Arch. Metall. Mater., Vol. 61 (2016), No 1, p. 289 294 DOI: 10.1515/amm-2016-0055 R. MICHALIK*,#, A. TOMASZEWSKA* An influence of ageing on the structure, corrosion resistance and hardness of high aluminum
3 Department of Mechanical Engineering Technology, Universiti Tun Hussein Onn Malaysia, Batu Pahat, Malaysia,
AL LM6 HOLLOW CYLINDER FABRICATED USING CENTRIFUGAL CASTING Saifulnizan Jamian 1, Safwan Yutiman 2 and Haffidzudin Hehsan 3 1 Department of Engineering Mechanics, Universiti Tun Hussein Onn Malaysia, Batu
The Effect of Preparation and Cleaning Techniques on Electrochemical Testing of Aluminium Anodes
The Effect of Preparation and Cleaning Techniques on Electrochemical Testing of Aluminium Anodes B Linde and R Northey Cathodic Diecasting, Australia SUMMARY: When comparing the preparation and cleaning
EFFECT OF LOCAL PLASTIC STRETCH OM TOTAL FATIGUE LIFE EVALUATION
EFFECT OF LOCAL PLASTIC STRETCH OM TOTAL FATIGUE LIFE EVALUATION Abstract G. S. Wang Aeronautics Division, The Swedish Defence Research Agency SE-17290 Stockholm, Sweden wgs@foi.se This paper shows that
Investigation of the oxidation process at the coppersolder interface with atomic force microscopy
Investigation of the oxidation process at the coppersolder interface with atomic force microscopy Attila Bonyár, Tamás Hurtony Department of Electronics Technology Budapest University of Technology and
Light Bases & Light Fixtures
Light Bases & Light Fixtures Keeping Them Together Clamping Force/Preload Force Torque Bolt Specifications Corrosion Galling 18-8 Disadvantages EB-83 bolts 2 Clamping Force = Preload Force 3 Fastener acts
Localized Corrosion of a 7075 Aluminum Alloy Exposed to KCl
Localized Corrosion of a 7075 Aluminum Alloy Exposed to KCl Christopher F. Mallinson Department of Mechanical Engineering Sciences The Surface Analysis Laboratory Monday, 20 April 2015 1 Outline Introduction