Jampilen Polypropylene Grades HOMOPOLYMER RANDOM COPOLYMER IMPACT COPOLYMER Injection Molding FILM (BOPP-Cast) Fiber EXTRUSION & THERMO- FORMING Injection Molding FILM (Tubular-Cast) EXTRUSION & THERMO- FORMING INJECTION MOLDING EXTRUSION & THERMO- FORMING TERPOLYMER New MFR New MFR New MFR New MFR New MFR New MFR New MFR New MFR New MFR New MFR H1850 1.2 HP522H 2 HP502H 1.8 HP432C 0.3 RP342N 10 RC1601 5 RP300D 0.6 EP302K 3.5 H1022 0.3 RP127K 5 HP500H 1.8 HP520H 2 HP550J 3.2 HP502C 0.3 RP340N 10 RP210M 6 RP270G 1.8 EP200K 3.5 H2464 0.3 RP129K 5 HP501H 2.1 HP528H 2 HP552J 3.2 H2150 0.3 RP1903 10.5 RP215M 6 RP240G 1.8 EP300K 4 EPD60R 0.35 RP128M 8 HP532J 3 HP593H 2 HP456J 3.4 H2450 0.3 RP344N 13 RP310M 8 RP210G 1.8 EP340K 4 EP300D 0.8 HP500J 3.2 HP422H 2.1 HP510L 6 HP501D 0.7 RP348R 23 RP320M 8 EP540L 6 EP310D 0.8 HP500L 6 HP421H 2.1 HP502N 12 HP502H 1.8 RP340R 25 RP316M 8 EP300L 6 EP400G 1.3 HP501M 7.5 HP529J 2.6 HP554N 12 HP456H 1.8 RP348T 48 RP325M 8 EP440L 6 EP440G 1.3 HP500M 9 HP525J 3 HP557N 12 HP640H 2 RP348U 75 RP312M 8 EP332L 7 EP302K 3.5 HP500N 12 HP524J 3 HP552N 13 HP593H 2 RCXP598 9 EP300M 7 HP500P 17 HP528J 3 HP554P 18 HP501H 2.1 RCXP599 9 EP340M 7.5 HP371P 18 HP522J 3 HP502P 16 HP540J 3.2 EP200M 8 HA840R 20 HP527J 3 HP562R 25 HA840K 3.5 EP540N 12 HP548R 23 HP425J 3.1 HP502R 25 ADXP680 3.5 EP440N 12 HP400R 25 HP421J 3.1 HP552R 25 ADXP699 3.5 EP548N 12 HP483R 27 ADXP699 3.5 HP561R 25 HP540K 3.8 BA238G3 12 HP648S 35 HP420M 8 HP462R 25 EP300N 15 HA701T 45 HP510M 9 HP561S 33 EP540P 15 HP648T 53 HP515M 9 HP562S 35 EP548P 16 HP565S 38 EP548R 21 EP440R 20 EP448S 40 EP340S 42 EP548S 44 EP448T 48 EP348U 70 EP548U 70 EP648V 100 SP151 3.5 SP179 8
Jampilen H1850 Jampilen H1850 is a very low flow homopolymer with good stiffness/toughness balance. The grade features yellowing resistance in contact with cooling water. Typical customer use is automotive expansion tanks. Injection molding Low flow Good stiffness/toughness balance Good yellowing resistance Automotive expansion tanks Under-the-hood and structural applications Melt Flow Rate (230 o C, 5kg) 1.2 g/10min ISO 1133 Density 0.902 g/cm 3 ISO 1183 Tensile Secant Modulus 1300 MPa ISO 527-1, -2 Tensile Strength at Yield (50 mm/min) 33 MPa ISO 527-1, -2 Tensile Elongation at Yield (50 mm/min) 14 % ISO 527-1, -2 Charpy impact strength (Notch A) 23 C 11 kj/m 2 ISO 179 Vicat softening point B50 85 o C ISO 306 H.D.T. B (0.45 MPa) 90 o C ISO 75B-1, -2 Others Mold shrinkage 1.6-1.8 % ----- PPCO-DS-123/01 Feb 10
Jampilen HP500H Jampilen HP500H is a polypropylene homopolymer for general injection molding applications. Besides the high stiffness and good impact strength, Jampilen HP500H offers good processability. Jampilen HP500H is suitable for a wide range of applications such as appliance components, textile bobbins, wheels, fittings, caps, closures, and household articles. Jampilen HP500H is suitable for food contact. Injection molding Good impact strength High stiffness Good processability Appliance components Textile bobbins Wheels Fittings Caps, closures Household articles Melt Flow Rate (230 o C, 2.16kg) 1.8 g/10min ASTM D1238 Flexural Modulus 1650 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 60 J/m ASTM D256 Rockwell Hardness 105 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 PPCO-DS-01/04 Feb 10
Jampilen HP501H Jampilen HP501H is a homopolymer for injection molding applications and exhibits good stiffness/impact balance at ambient temperatures. The main applications of Jampilen HP501H are caps, closures and furniture. Injection molding Thermoforming General purpose Good stiffness/impact balance Furniture Caps and Closures Melt Flow Rate (230 o C, 2.16kg) 2.1 g/10min ISO 1133 Density 0.9 g/cm 3 ISO 1183 Tensile Modulus 1450 MPa ISO 527-1, -2 Tensile Strength at Yield 33 MPa ISO 527-1, -2 Tensile Elongation at Break >50 % ISO 527-1, -2 Tensile Elongation at Yield 9 % ISO 527-1, -2 Charpy impact strength (Notch A) at 23 C 5 kj/m 2 ISO 179 Ball indentation hardness (H 358/30) 72 MPa ISO 2039-1 Vicat softening point A50 154 o C ISO 306 H.D.T. B (0.45 MPa) 85 o C ISO 75B-1, -2 PPCO-DS-84/01 Feb 10
Jampilen HP532J Jampilen HP532J is a heat and detergent resistant polypropylene homopolymer. The product is designed for injection molding items which are subject to severe environmental conditions as well as extruded tapes and raffia. Jampilen HP532J offers good processability and finished items produced by it show good balance of stiffness and impact strength. Jampilen HP532J is formulated with a very effective heat and detergent stabilisation package for both dry and wet environments. The product also shows a high resistance to solvents and chemicals. In a dry environment, items produced with Jampilen HP532J can withstand a continuous heat of 95 C for over 80.000 hours and 70 C for over 1.000.000 hours. In a wet environment, the items can resist to a continuous temperature of 95 C for over 10.000 hours and 70 C for over 130.000 hours. In a wet environment in the presence of detergents, the items can withstand 95 C for over 4.500 hours and 70 C for more than 50.000 hours. Injection molding Extrusion (raffia, tape) Good balance of stiffness and impact strength Good processability High resistance to detergent, solvents and chemicals High resistance to heat Automotive under-the-hood applications Components for small household appliances Irons, coffee machines, hair dryers and toasters Parts for dish washers, washing machines and refrigerators Chain links for conveyor belts and textile bobbins Tapes and raffia Film wrap Filament yarn Melt Flow Rate (230 o C, 2.16kg) 3.0 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 55 J/m ASTM D256 Rockwell Hardness 102 R Scale ASTM D785 Vicat softening point (10N) 156 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 1800 hours ASTM D3012 PPCO-DS-03/04 Feb 09
Jampilen HP500J Jampilen HP500J is a general purpose polypropylene homopolymer for injection molding applications and combines high stiffness and fairly good impact strength with good processability. The grade is suitable for a wide range of applications such as housewares, caps, closures, small containers, toys, parts for small appliances and components for the automotive industry. Jampilen HP500J is also used for compounding. This grade is suitable for food contact. Injection molding Compounding Good impact strength High stiffness Good processability Housewares Caps and closures Small containers Toys Parts for small appliances Components for the automotive industry Compounding Melt Flow Rate (230 o C, 2.16kg) 3.1 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 55 J/m ASTM D256 Rockwell Hardness 102 R Scale ASTM D785 Vicat softening point (10N) 156 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 PPCO-DS-02/05 Feb 10
Jampilen HP500L Jampilen HP500L is a polypropylene homopolymer for injection molding that provides good flow properties, easy processing and high stiffness. The main applications of Jampilen HP500L are housewares, small containers, crates, garden furniture, stadium seats, toys, caps and closures. Other major applications are components for appliances and parts for the automotive industry. Jampilen HP500L is suitable for food contact. Injection molding Easy processing and good moldability High stiffness Good stretchability Housewares and components for appliances Small containers Crates Garden furniture Stadium seats Toys Caps and closures Parts for the automotive industry Melt Flow Rate (230 o C, 2.16kg) 6 g/10min ASTM D1238 Flexural Modulus 1500 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 10 % ASTM D638 Izod Impact Strength (notched) at 23 o C 40 J/m ASTM D256 Rockwell Hardness 99 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 PPCO-DS-04/05 Feb 10
Jampilen HP501M Jampilen HP501M is a homopolymer polypropylene for injection molding applications that exhibits good stiffness/impact balance at ambient temperature. The main applications of Jampilen HP501M are caps and closures, housewares and furniture. Injection molding Good stiffness/impact balance Furniture Injection Molded Caps and Closures Housewares Melt Flow Rate (230 o C, 2.16kg) 7.5 g/10min ISO 1133 Density 0.9 g/cm 3 ISO 1183 Tensile Modulus (1 mm/min) 1500 MPa ISO 527-1, -2 Tensile Strenght at Yield (50 mm/min) 34 MPa ISO 527-1, -2 Tensile Elongation at Break (50 mm/min) >50 % ISO 527-1, -2 Tensile Elongation at Yield (50 mm/min) 9 % ISO 527-1, -2 Charpy impact strength (Notch A) at 23 C 3.5 kj/m 2 ISO 179 Ball indentation hardness (H 358/30) 74 MPa ISO 2039-1 Vicat softening point A50 154 o C ISO 306 H.D.T. B (0.45 MPa) 85 o C ISO 75B-1, -2 PPCO-DS-85/01 Feb 10
Jampilen HP500M Jampilen HP500M is a polypropylene homopolymer suitable for injection molding applications that due to its good flow properties offers easy processing. Articles produced from Jampilen HP500M exhibit high stiffness. Jampilen HP500M is widely used for injection molding consumer goods such as food containers, housewares, toys and garden furniture. Other major applications are components for appliances and parts for the automotive industry. Jampilen HP500M is suitable for food contact. Injection molding Good flow properties Easy processing High stiffness Housewares containers Garden furniture Toys Components for appliances Parts for the automotive industry Melt Flow Rate (230 o C, 2.16kg) 9 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 37 J/m ASTM D256 Rockwell Hardness 102 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 95 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 PPCO-DS-05/05 Feb 10
Jampilen HP500N Jampilen HP500N is a medium fluidity polypropylene homopolymer for general purpose injection molding applications. Due to its good flow properties, this grade offers easy mold filling and short cycle times. Articles produced from Jampilen HP500N exhibit good dimensional stability and high stiffness. Jampilen HP500N is widely used for injection molding consumer goods such as food containers, cool boxes, vacuum flasks, flower pots, toys, garden furniture and small appliances. In the medical sector, Jampilen HP500N is used for 3-part syringes and a wide range of health-care items. Other applications are closures, caps and crates for products. Jampilen HP500N is suitable for food contact. Injection molding Easy mold filling and short cycle times Good dimensional stability High stiffness Cool boxes, vacuum flasks, flower pots containers Garden furniture Toys 3-part syringes Closures, caps Crates Melt Flow Rate (230 o C, 2.16kg) 12 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 34 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 30 J/m ASTM D256 Rockwell Hardness 102 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 95 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 PPCO-DS-06/05 Feb 10
Jampilen HP500P Jampilen HP500P is a polypropylene homopolymer with good flow properties for injection molding and compounding applications. This grade offers medium-high fluidity, easy mold filling and short cycle times. The final items molded with Jampilen HP500P exhibit good dimensional stability and high stiffness. The product is well suited for the production of thin-walled articles and articles with long flow paths. Jampilen HP500P is also an excellent polymer base for compounding and masterbatches. Jampilen HP500P is suitable for food contact. Injection molding Compounding Easy mold filling and short cycle times Good dimensional stability High stiffness Thin-walled articles Containers Boxes Toys Household articles Closures and caps Polymer base for compounding and masterbatches Melt Flow Rate (230 o C, 2.16kg) 17 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 33 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 30 J/m ASTM D256 Rockwell Hardness 103 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 95 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 PPCO-DS-07/04 Feb 10
Jampilen HP371P Jampilen HP371P is a polypropylene homopolymer with gamma-ray stabilizing additivation featuring high fluidity and superior transparency. The product is designed for the production of three-part syringes and a wide range of medical articles. Jampilen HP371P is sterilisable both with gamma and E-beam irradiation and with ETO. Because of the high melt flow, mold filling is easy and cycle times are short leading to an excellent processability. Items produced with Jampilen HP371P feature good stiffness, high impact strength, minimum warpage and high chemical resistance and offer a really outstanding transparency. Injection molding Medium clarity Excellent processability Good stiffness Radiation and ETO sterilizable High chemical resistance Three-part syringes Medical articles and healthcare applications Labware such as needle hubs, pipette tips, test tubes, jugs, cylinders and containers High quality household articles Packaging components Melt Flow Rate (230 o C, 2.16kg) 18 g/10min ASTM D1238 Flexural Modulus 1150 MPa ASTM D790 Tensile Strength at Yield 32 MPa ASTM D638 Tensile Elongation at Yield 13 % ASTM D638 Izod Impact Strength (notched) at 23 o C 50 J/m ASTM D256 Rockwell Hardness 98 R Scale ASTM D785 Vicat softening point (10N) 151 H.D.T. (0.46 Mpa) 99 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 Optical Haze (1mm) 15 % ASTM D1003 Gloss (60 o ) 62 ---- ASTM D2457 PPCO-DS-08/04 Feb 09
Jampilen HA840R Jampilen HA840R is a special polypropylene type which features an extremely high stiffness and high gloss. It has been especially developed for the production of stiff injectionmolded articles where high rigidity is needed. Typical applications of Jampilen HA840R include food packaging containers, housewares, small appliances and technical parts. The composition of the product complies well with FDA norms and with regulations concerning food contact applications in major European countries. Injection molding High stiffness High gloss packaging containers Housewares Furniture Small appliances Technical parts Caps and clusures Melt Flow Rate (230 o C, 2.16kg) 20 g/10min ASTM D1238 Density 0.91 g/cm 3 ASTM D1505 Flexural Modulus 2350 MPa ASTM D790 Tensile Strength at Yield 41 MPa ASTM D638 Tensile Elongation at Yield 5 % ASTM D638 Izod Impact Strength (notched) at 23 o C 35 J/m ASTM D256 Rockwell Hardness 111 R Scale ASTM D785 Vicat softening point (10N) 159 H.D.T. (0.46 Mpa) 128 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 Optical Haze (1mm) 40 % ASTM D1003 Gloss (60 o ) 95 ---- ASTM D2457 PPCO-DS-09/04 Feb 10
Jampilen HP548R Jampilen HP548R is a homopolymer polypropylene for injection molding applications bearing nucleation and antistatic additivation. Jampilen HP548R exhibits good stiffness combined with good flowability. The main applications of Jampilen HP548R are caps, closures, furniture and housewares. Jampilen HP548R is suitable for food contact. Injection molding Good Flow Good stiffness Antistatic properties Nucleated Furniture Injection Molded Caps and Closures Housewares TWIM Containers Opaque containers Melt Flow Rate (230 o C, 2.16kg) 23 g/10min ISO 1133 Density 0.9 g/cm 3 ISO 1183 Tensile Modulus (1 mm/min) 1650 MPa ISO 527-1, -2 Tensile Strenght at Yield (50 mm/min) 35 MPa ISO 527-1, -2 Tensile Elongation at Break (50 mm/min) >50 % ISO 527-1, -2 Tensile Elongation at Yield (50 mm/min) 8 % ISO 527-1, -2 Charpy impact strength (Notch A) at 23 C 2.5 kj/m 2 ISO 179 Ball indentation hardness (H 358/30) 78 MPa ISO 2039-1 Vicat softening point A50 154 o C ISO 306 H.D.T. B (0.45 MPa) 95 o C ISO 75B-1, -2 PPCO-DS-86/01 Feb 10
Jampilen HP400R Jampilen HP400R is a high flow homopolymer for injection molding and compounding applications that exhibits high stiffness, outstanding processability for shorter cycle times and easy mold filling. The product is suitable for injection molding applications such as thin-walled containers and other general purpose packaging items, toys, vacuum flasks, household and kitchen articles. Jampilen HP400R also is an excellent polymer base for compounding and masterbatches. Jampilen HP400R is suitable for food contact. Injection molding Compounding Excellent processability Good stiffness Thin-walled containers Toys Vacuum flasks Household and kitchen articles Furniture Polymer base for compounding and masterbatches Melt Flow Rate (230 o C, 2.16kg) 25 g/10min ASTM D1238 Flexural Modulus 1500 MPa ASTM D790 Tensile Strength at Yield 32 MPa ASTM D638 Tensile Elongation at Yield 13 % ASTM D638 Izod Impact Strength (notched) at 23 o C 30 J/m ASTM D256 Rockwell Hardness 100 R Scale ASTM D785 Vicat softening point (10N) 152 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 PPCO-DS-10/05 Feb 10
Jampilen HP483R Jampilen HP483R is a homopolymer for injection molding with antistatic and slip agent additivation that exhibits good stiffness combined with good flowability. The main applications of Jampilen HP483R are caps, closures, furniture and TWIM. Injection molding (TWIM) Good Flow Good stiffness Antistatic properties Unspecified Slip TWIM Furniture Caps and Closures Housewares Opaque Containers Melt Flow Rate (230 o C, 2.16kg) 27 g/10min ISO 1133 Density 0.9 g/cm 3 ISO 1183 Tensile Modulus 1400 MPa ISO 527-1, -2 Tensile Strength at Yield 32 MPa ISO 527-1, -2 Tensile Elongation at Break >50 % ISO 527-1, -2 Tensile Elongation at Yield 9 % ISO 527-1, -2 Charpy impact strength (Notch A) at 23 C 2 kj/m 2 ISO 179 Ball indentation hardness (H 358/30) 68 MPa ISO 2039-1 Vicat softening point A50 151 o C ISO 306 H.D.T. B (0.45 MPa) 80 o C ISO 75B-1, -2 PPCO-DS-87/01 Feb 10
Jampilen HP648S Jampilen HP648S is a high melt flow homopolymer with a narrow molecular weight distribution. Jampilen HP648S is designed for the high speed injection molding of thin-walled items with a good transparency and optimum antistatic properties. Due to its outstanding flow properties, its very high stiffness and excellent dimensional stability, this grade can be molded at very high speeds producing thin-walled parts, even with complicated shapes, without distortion. In many of applications Jampilen HP648S can replace traditional materials such as polystyrene since the product exhibits excellent processability, low residual stress, low shrinkage and warpage on top of the advantages typical of polypropylene such as light weight, low odour transfer, high chemical resistance and a good balance of mechanical properties. Injection molding High melt flow Narrow molecular weight distribution Good transparency Very high stiffness Excellent dimensional stability Thin-walled packaging in the cosmetic and food industry Pens CD and DVD boxes Caps and closures Small appliances such as coffee machines and food processors Office accessories, disposable razors and camping articles Melt Flow Rate (230 o C, 2.16kg) 35 g/10min ASTM D1238 Flexural Modulus 1500 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 10 % ASTM D638 Izod Impact Strength (notched) at 23 o C 29 J/m ASTM D256 Rockwell Hardness 102 R Scale ASTM D785 Vicat softening point (10N) 155 H.D.T. (0.46 Mpa) 110 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 4 th Floor, No. 68 Taban St., Africa Blvd., Tehran, Iran. PPCO-DS-11/04 Feb 10
Jampilen HA701T Jampilen HA701T is very high flow polypropylene type which features an extremely high stiffness, high gloss, good transparency and improved characteristics at high temperatures. It has been especially developed for TWIM applications where high flow combined with high rigidity, high gloss and very good thermal characteristics are needed. Typical applications of Jampilen HA701T include food containers as well as any applications where high fluidity associated with high gloss and high stiffness are required. The composition of the product complies well with FDA norms and with regulations concerning food contact applications in major European countries. Injection molding Very high flow High stiffness High gloss Good transparency Improved characteristics at high temperatures Excellent dimensional stability TWIM (food containers) Melt Flow Rate (230 o C, 2.16kg) 45 g/10min ASTM D1238 Flexural Modulus 2050 MPa ASTM D790 Tensile Strength at Yield 40 MPa ASTM D638 Tensile Elongation at Yield 6 % ASTM D638 Izod Impact Strength (notched) at 23 o C 28 J/m ASTM D256 Rockwell Hardness 110 R Scale ASTM D785 Vicat softening point (10N) 157 H.D.T. (0.46 Mpa) 125 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 PPCO-DS-12/04 Feb 10
Jampilen HP648T Jampilen HP648T is a homopolymer polypropylene for injection molding applications bearing nucleation and antistatic additivation. Jampilen HP648T exhibits very good flowability and good stiffness. The main applications of Jampilen HP648T are thin walled injection molding applications especially in dairy and other food packaging products. Jampilen HP648T is suitable for food contact. Injection molding Good Flow Good stiffness Antistatic properties Nucleated Housewares TWIM Containers Dairy and other food packaging Opaque containers Melt Flow Rate (230 o C, 2.16kg) 53 g/10min ISO 1133 Density 0.9 g/cm 3 ISO 1183 Tensile Modulus (1 mm/min) 1600 MPa ISO 527-1, -2 Tensile Strenght at Yield (50 mm/min) 35 MPa ISO 527-1, -2 Tensile Elongation at Break (50 mm/min) 50 % ISO 527-1, -2 Tensile Elongation at Yield (50 mm/min) 8 % ISO 527-1, -2 Charpy impact strength (Notch A) at 23 C 2 kj/m 2 ISO 179 Ball indentation hardness (H 358/30) 80 MPa ISO 2039-1 Vicat softening point A50 154 o C ISO 306 H.D.T. B (0.45 MPa) 95 o C ISO 75B-1, -2 PPCO-DS-88/01 Feb 10
Jampilen HP522H Jampilen HP522H is a homopolymer for the production of biaxially oriented polypropylene films which is particularly suitable for metallization, both as plain film and in coextruded structures. Jampilen HP522H has been designed to provide a very stable extrusion on stenter lines and to give excellent thickness control, increased drawability and readiness to a two way orientation. This grade contains a reinforced processing stabilization but does not contain any slip or antiblocking agents and is calcium stearate free. The product features low water carry-over properties and is therefore also suitable for tubular BOPP. BOPP films produced with Jampilen HP522H feature good mechanical properties, even at low temperatures, excellent barrier against moisture, odours, oils, fats and oxygen and good optical properties. Monolayer or coextruded films made of Jampilen HP522H with a thickness ranging from 20 to 40 µm are used for the packaging of foodstuffs, cosmetics and videocassettes. Jampilen HP522H is suitable for food contact. BOPP Film High impact strength and puncture resistance Excellent barrier against moisture, odours, oils and oxygen Good optical properties packaging Packaging of cosmetics and videocassettes Lamination to other flexible films Melt Flow Rate (230 o C, 2.16kg) 2.0 g/10min ASTM D1238 Flexural Modulus 1650 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 60 J/m ASTM D256 Rockwell Hardness 105 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 500 hours ASTM D3012 Optical Haze (20µm) 0.6 % ASTM D1003 PPCO-DS-13/04 Feb 10
Jampilen HP520H Jampilen HP520H is a homopolymer designed for the production of biaxially oriented polypropylene films through a very stable extrusion on stenter and double bubble lines with excellent thickness control, increased drawability and readiness to a two way orientation. Jampilen HP520H contains a reinforced processing stabilization but does not contain any slip or antiblocking agents. BOPP films produced with this grade feature good mechanical properties, even at low temperatures, excellent barrier against moisture, odours, oils, fats and oxygen and high transparency, high gloss and good printability after corona treatment. Monolayer films made of Jampilen HP520H are used for food packaging, textiles packaging, flower wrappings and adhesive tapes. Jampilen HP520H is suitable for food contact. BOPP Film High impact strength and puncture resistance Excellent barrier against moisture, odours, oils and oxygen High transparency and gloss Good printability packaging, textiles packaging and flower wrappings Adhesive tapes Lamination to other flexible films Melt Flow Rate (230 o C, 2.16kg) 2.0 g/10min ASTM D1238 Flexural Modulus 1650 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 60 J/m ASTM D256 Rockwell Hardness 105 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 500 hours ASTM D3012 Optical Haze (20µ) 0.30 % ASTM D1003 PPCO-DS-14/04 Feb 10
Jampilen HP528H Jampilen HP528H is a homopolymer designed for the manufacture of coextruded biaxially oriented polypropylene (BOPP) films. The product is used for the core of the coextruded film structure with a low seal temperature random copolymer (Jampilen terpolymers) in the outside layers. Jampilen HP528H has been designed to provide a very stable extrusion on stenter lines and to render excellent thickness control, increased drawability and readiness to a two way orientation. The product contains a reinforced processing stabilization and a package of slip and antistatic agents but does not contain antiblocking agents. BOPP films produced with Jampilen HP528H feature good mechanical properties, high impact strength and puncture resistance, even at low temperatures. The films form an excellent barrier against moisture, odours, oils, fats and oxygen and feature high transparency, high gloss and good printability after corona treatment. Jampilen HP528H is suitable for food contact. BOPP Film High impact strength and puncture resistance Excellent barrier against moisture, odours, oils and oxidation High transparency and gloss Good printability Automatic packaging of bakery products, snacks and pasta Overwrapping of boxes and cigarette packets Melt Flow Rate (230 o C, 2.16kg) 2.0 g/10min ASTM D1238 Flexural Modulus 1650 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 60 J/m ASTM D256 Rockwell Hardness 105 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 500 hours ASTM D3012 PPCO-DS-15/04 Feb 10
Jampilen HP593H Jampilen HP593H is a new generation polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP) on high speed BOPP lines and is characterised by its very broad processing window, easy film strechability, good optical properties and stable film thickness profile. Jampilen HP593H is suitable for metallizable film, both as monolayer and in coextruded structures. Jampilen HP593H is free of any slip, antiblock agents, Irgafos 168 and Calcium Stearate. Typical applications are BOPP packaging films. Jampilen HP593H is suitable for food contact. BOPP film Thermoforming High clarity High gloss Good optical properies BOPP packaging packaging films Melt Flow Rate (230 o C, 2.16kg) 2.0 g/10min ISO 1133 Density 0.9 g/cm 3 ISO 1183 Tensile Modulus (1 mm/min) 1500 MPa ISO 527-1, -2 Tensile strength at Yield (50 mm/min) 34 MPa ISO 527-1, -2 Tensile elongation at Break (50 mm/min) 410 % ISO 527-1, -2 Tensile elongation at Yield (50 mm/min) 11 % ISO 527-1, -2 Shore hardness (Shore D) 71 ---- ISO 868 Vicat softening point A50 152 o C ISO 306 H.D.T. B (0.45 MPa) 93 o C ISO 75B-1, -2 PPCO-DS-89/01 Feb 10
Jampilen HP422H Jampilen HP422H is a modified homopolymer designed for the very high speed production of BOPP films, wherein an outstanding extrusion stability, thickness variation control, a very high drawability and readiness to a two way orientation would be achieved. The product contains a reinforced processing stabilization and features low water carry-over properties. Jampilen HP422H does not contain any slip or antistatic agent and is Calcium Stearate free. The Product is particularly suitable for metalizing film. BOPP films produced with Jampilen HP422H feature good mechanical properties, even at low temperatures, excellent barrier against moisture, odours, oils and oxygen and good transparency and gloss. Monolayer or coextruded films made of Jampilen HP422H with a thickness ranging from 20 to 40 µm are used for the packaging of foodstuffs, cosmetics and videocassettes. BOPP Film High impact strength and puncture resistance Excellent barrier against moisture, odours, oils and oxygen Good transparency and gloss packaging film Packaging of cosmetics and videocassettes Barrier film Melt Flow Rate (230 o C, 2.16kg) 2.1 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 60 J/m ASTM D256 Rockwell Hardness 102 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 92 Accelerated oven ageing in air at 150 o C 500 hours ASTM D3012 Optical Haze (20µ) 0.50 % ASTM D1003 PPCO-DS-16/05 Feb 10
Jampilen HP421H Jampilen HP421H is a modified homopolymer designed for the very high speed production of coextruded BOPP films. The product is used for the core of the coextruded film structure with a low seal temperature resin (Jampilen terpolymers) in the outside layers. Jampilen HP421H allows an outstanding extrusion stability and thickness variation control, especially on cascade lines, very high drawability and readiness to a two way orientation. The product contains a reinforced processing stabilization and a package of slip and antistatic agents but does not bear any antiblocking agents. BOPP films produced with Jampilen HP421H feature good mechanical properties, even at low temperatures, excellent barrier against moisture, odours, oils, fats and oxygen and high transparency, high gloss and good printability after corona treatment. BOPP Film High impact strength and puncture resistance Excellent barrier against moisture, odours, oils and oxygen High transparency and gloss Good printability Automatic packaging of bakery products, snacks and pasta Overwrapping of boxes and cigarette packets Textile packaging film Surface protection film Barrier film Melt Flow Rate (230 o C, 2.16kg) 2.1 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 60 J/m ASTM D256 Rockwell Hardness 102 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 92 Accelerated oven ageing in air at 150 o C 500 hours ASTM D3012 PPCO-DS-17/04 Feb 10
Jampilen HP529J Jampilen HP529J is a polypropylene homopolymer designed for the manufacture of BOPP film on stenter lines. Jampilen HP529J is approved for food contact and medical applications. BOPP Film Good processability Good mechanical properties and medical Packaging, Medical Melt Flow Rate (230 o C, 2.16kg) 2.6 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 55 J/m ASTM D256 Rockwell Hardness 102 R Scale ASTM D785 Vicat softening point (10N) 156 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 500 hours ASTM D3012 PPCO-DS-18/05 Feb 10
Jampilen HP525J Jampilen HP525J is a medium flow homopolymer with bimodal molecular weight distribution and good clarity intended for BOPP films. The product is suitable for metallizable film, both as monolayer and in coextruded structures. It contains a standard processing stabilisation but does not contain any slip, antiblocking agents and is Calcium Stearate free. Jampilen HP525J offers good optical properties, easy processing and very stable film profile. Typical applications are BOPP packaging films and Solid Phase Thermoforming sheets. Jampilen HP525J is suitable for food contact. BOPP Film Thermoforming Medium Flow Good processability Good Transparency and Gloss High quality packaging film for food Lamination to other films Metalizing Film Medical packaging Thermoformed food containers Melt Flow Rate (230 o C, 2.16kg) 3.0 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 55 J/m ASTM D256 Rockwell Hardness 105 R Scale ASTM D785 Vicat softening point (10N) 156 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 500 hours ASTM D3012 Optical Haze (20µm) 0.5 % ASTM D1003 PPCO-DS-82/02 Feb 10
Jampilen HP524J Jampilen HP524J is a medium flow homopolymer with bimodal molecular weight distribution and good clarity intended for the manufacture of BOPP films. Jampilen HP524J gives reliable and consistent processing on BOPP stenter lines, providing films having high transparency and gloss with a good balance of film properties. It contains a general purpose formulation of additives. The BOPP films obtained from this grade can be used for high quality packaging and laminates. Jampilen HP524J is suitable for food contact. BOPP Film Medium Flow Good processability Good Transparency and Gloss High quality packaging film for food Lamination to other films Medical packaging Melt Flow Rate (230 o C, 2.16kg) 3.0 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 55 J/m ASTM D256 Rockwell Hardness 105 R Scale ASTM D785 Vicat softening point (10N) 156 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 500 hours ASTM D3012 PPCO-DS-81/03 Feb 10
Jampilen HP528J Jampilen HP528J is a polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP) and contains a standard processing stabilization as well as antistatic agent, but does not contain any slip or antiblocking agents and is Calcium Stearate free. Jampilen HP528J offers good optical, easy processing and very good thickness profile of the films. Typical applications are BOPP packaging films. Jampilen HP528J is suitable for food contact. BOPP film High clarity and gloss Medium flow Good Processability BOPP Packaging Packaging Films Melt Flow Rate (230 o C, 2.16kg) 3.0 g/10min ISO 1133 Density 0.9 g/cm 3 ISO 1183 Tensile Modulus (1mm/min) 1450 MPa ISO 527-1, -2 Tensile Strength at Break (50mm/min) 23 MPa ISO 527-1, -2 Tensile Strength at Yield (50mm/min) 34 MPa ISO 527-1, -2 Tensile Elongation at Break (50mm/min) >50 % ISO 527-1, -2 Tensile Elongation at Yield (50mm/min) 11 % ISO 527-1, -2 Shore hardness (Shore D) 70 ---- ISO 868 Vicat softening point A50 156 o C ISO 306 H.D.T. B (0.45 MPa) 85 o C ISO 75B-1, -2 PPCO-DS-90/01 Feb 10
Jampilen HP522J Jampilen HP522J is a new homopolymer grade designed for the production of biaxially oriented polypropylene films (BOPP) primarily on high speed BOPP lines. This grade is characterised by its very broad processing window, easy film stretchability, good optical properties and reliable film thickness profile. Jampilen HP522J is suitable for metallization, both as monolayer and in coextruded structures. It does not contain any slip or antiblocking agents and it is Calcium Stearate free. Typical applications are BOPP packaging films and Sheet for Solid Phase Thermoforming. Jampilen HP522J is suitable for food contact. BOPP film Thermoforming High clarity High gloss Medium flow Good Processability BOPP packaging Packaging Film Thermoformed objects and containers Melt Flow Rate (230 o C, 2.16kg) 3.0 g/10min ISO 1133 Density 0.9 g/cm 3 ISO 1183 Tensile Modulus (1mm/min) 1370 MPa ISO 527-1, -2 Tensile Strength at Yield (50mm/min) 33 MPa ISO 527-1, -2 Tensile Elongation at Break (50mm/min) 550 % ISO 527-1, -2 Tensile Elongation at Yield (50mm/min) 11 % ISO 527-1, -2 Shore hardness (Shore D) 69 ---- ISO 868 Vicat softening point A50 154 o C ISO 306 H.D.T. B (0.45 MPa) 85 o C ISO 75B-1, -2 PPCO-DS-91/00 Jan 10
Jampilen HP527J Jampilen HP527J is a medium flow homopolymer with bimodal molecular weight distribution and good clarity intended for production of BOPP films. Jampilen HP527J provides reliable and consistent processing on BOPP stenter lines, rendering films having high transparency and gloss with a good balance of film properties. Besides the general purpose formulation of additives, this grade contains antistatic, antiblock and slip agents which will best contribute to its final processability and properties. The BOPP films obtained from this grade can be used for high quality packaging and laminates. Jampilen HP527J is suitable for food contact. BOPP Film Medium Flow Good Transparency and Gloss Antistatic and antiblock properties Excellent processability High quality packaging for food Lamination to other films Medical packaging Melt Flow Rate (230 o C, 2.16kg) 3.0 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 55 J/m ASTM D256 Rockwell Hardness 105 R Scale ASTM D785 Vicat softening point (10N) 156 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 500 hours ASTM D3012 merchantability, fitness for a particular purpose or suitability of this information, products or process described. PPCO-DS-122/03 Feb 10
Jampilen ADXP699 Jampilen ADXP699 is a special polypropylene type which features an extremely high stiffness, high gloss, good transparency and improved characteristics at high temperatures. In particular, it has been developed for BOPP and Cast film applications where high rigidity, outstanding transparency and very good thermal characteristics are required. Strapping made out of Jampilen ADXP699 shows extremely good creep resistance. The composition of the product complies well with FDA norms and with regulations concerning food contact applications in major European countries. BOPP and Cast Film High stiffness and rigidity High gloss Good transparency Improved characteristics at high temperatures Good creep resistance Flowers and textile packaging Sterilizable and pastorizable food packaging Printing lamination and tobacco film Strapping Melt Flow Rate (230 o C, 2.16kg) 3.5 g/10min ASTM D1238 Flexural Modulus 2000 MPa ASTM D790 Tensile Strength at Yield 39 MPa ASTM D638 Tensile Elongation at Yield 6 % ASTM D638 Izod Impact Strength (notched) at 23 o C 40 J/m ASTM D256 Rockwell Hardness 112 R Scale ASTM D785 Vicat softening point (10N) 157 H.D.T. (0.46 Mpa) 118 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 [ PPCO-DS-19/04 Feb 10
Jampilen HP420M Jampilen HP420M is a high flow polypropylene homopolymer designed for the production of biaxially oriented polypropylene film (BOPP) on tubular double bubble lines and cast film. Typical applications are BOPP packaging, laminating film and drinking straws but also packaging foodstuffs such as pasta, snacks, biscuits, bakery products and confectionery, film for packaging for flowers, books stationery, blankets, shirts, knitwear and hosiery. Jampilen HP420M is suitable for food contact. BOPP Film on tubular double bubble lines Cast Film High flow Good transparency BOPP Films Drinking Straws Packaging of foodstuffs Melt Flow Rate (230 o C, 2.16kg) 8.0 g/10min ISO 1133 Density 0.9 g/cm 3 ISO 1183 Tensile Modulus (1mm/min) 1450 MPa ISO 527-1, -2 Tensile strength at Yield (50mm/min) 35 MPa ISO 527-1, -2 Tensile elongation at Yield (50mm/min) 10 % ISO 527-1, -2 Shore hardness (Shore D) 70 ---- ISO 868 Vicat softening point A50 152 o C ISO 306 H.D.T. B (0.45 MPa) 85 o C ISO 75B-1, -2 PPCO-DS-92/01 Feb 10
Jampilen HP510M Jampilen HP510M is a homopolymer particularly suited for the extrusion of cast and water quenched blown films. Jampilen HP510M is formulated with a general purpose stabilization package and does not contain any slip or antiblocking agents. This grade exhibits excellent processability and outstanding optical properties. Jampilen HP510M renders high gloss finish in laminates and exhibits good printability after Corona treatment. Cast water quenched blown film Water quenched blown film Extrusion (Small pipes) Blow molding Excellent processability Good optical properties Excellent gloss Film for packaging food-stuffs such as pasta, snacks, biscuits, bakery products and confectionery Film for packaging of flowers, books, stationery, blankets, shirts, knitwear and hosiery Lamination with polyester, polyamide and aluminum for packaging of snacks, crisps, sweets, coffee, meat products and pre-cooked foods Small pipes and drinking straws Blow molded pigmented bottles Coextruded sheet Melt Flow Rate (230 o C, 2.16kg) 9.0 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 37 J/m ASTM D256 Rockwell Hardness 102 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 95 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 Optical Haze 1.2 % ASTM D1003 Gloss 88 ----- ASTM D2457 PPCO-DS-20/05 Feb 10
Jampilen HP515M Jampilen 515M is a polypropulene homopolymer developed for the high speed extrusion of transparent cast and blown films. It is formulated with slip and antiblocking agents. Jampilen 515M is suitable for the extrusion of low thickness films and can be used for films from 15 up to 150 µm. In comparison with standard polypropylene types for film production, Jampilen 515M allows for faster processing due to its peculiar structure and composition. Films made with Jampilen 515M show a good behavior on winding rolls and in cutting section and feature very high transparency, high gloss and good printability after corona treatment. Cast film Blown film Excellent processability High transparency and gloss Antiblock properties Shopping bags Packaging for snacks, bakery products, books, blankets, hosiery and shirts Stationery folders Twines and ropes Melt Flow Rate (230 o C, 2.16kg) 9.0 g/10min ASTM D1238 Flexural Modulus 1300 MPa ASTM D790 Tensile Strength at Yield 32 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 40 J/m ASTM D256 Rockwell Hardness 95 R Scale ASTM D785 Vicat softening point (10N) 150 H.D.T. (0.46 Mpa) 92 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 Optical Haze 1.2 % ASTM D1003 Gloss 86 ---- ASTM D2457 PPCO-DS-21/04 Feb 10
Jampilen HP502H Jampilen HP502H is a polypropylene homopolymer particularly suitable for the production of sheet for thermoforming, film yarn and monofilament. Jampilen HP502H combines excellent processability with high stiffness and is particularly suitable to produce film yarn, both with cast and tubular processes. Textile film yarns have a denier count of not more than 1100 to 1200 and are used for the production of bags, industrial fabrics and mats. Film yarn with a denier count ranging from 3000 to 28000 is used for baler twines, packaging twines and ropes. Jampilen HP502H is also well suited for the production of monofilament used for brush and broom filling and technical applications. Extrusion (Sheet, film yarn, monofilament ) Thermoforming Blow molding Injection molding Excellent processability High stiffness Sheet for thermoforming (drinking beakers, packaging for dairy products, nursery flower pots and trays for fruit, biscuits and chocolates) Bags, industrial fabrics and mats Baler twines, packaging twines and ropes Brush and broom filling and technical applications Profiles and small diameter pipes such as refills for ball pens Strapping Blow molded small containers Melt Flow Rate (230 o C, 2.16kg) 1.8 g/10min ASTM D1238 Flexural Modulus 1650 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 60 J/m ASTM D256 Rockwell Hardness 105 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 PPCO-DS-22/04 Feb 10
Jampilen HP550J Jampilen HP550J is a polypropylene homopolymer particularly suitable for the extrusion of sheet for thermoforming, film yarn and monofilament. This grade combines outstanding processability with good mechanical properties. Jampilen HP550J is designed for the production of films that can be converted into stretched tapes for weaving applications. Textile film yarns with a denier count of not more than 1100 to 1200 and are used for the production of carpet backings, bags, industrial fabrics, mats and artificial grass. Film yarn with a denier count ranging from 3000 to 28000 is used for baler twines, packaging twines and ropes. Jampilen HP550J is suitable for food contact. Extrusion (film yarn, monofilament, sheet) Thermoforming Good processability Good mechanical properties Stiff sheet for high quality thermoformings such as vending cups, packaging for dairy products and trays for fruit, biscuits and chocolates Film yarn, raffia, tapes, strapping Carpet backings, bags, industrial fabrics, mats and artificial grass Baler twines, packaging twines and ropes Brush and broom filling and technical applications Nets for various purposes Melt Flow Rate (230 o C, 2.16kg) 3.2 g/10min ASTM D1238 Flexural Modulus 1550 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 55 J/m ASTM D256 Rockwell Hardness 102 R Scale ASTM D785 Vicat softening point (10N) 156 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 PPCO-DS-23/05 Feb 10
Jampilen HP552J Jampilen HP552J is a polypropylene homopolymer for the production of film yarn and monofilament and features outstanding processability and low water carry-over properties. Jampilen HP552J is particularly suitable for the high speed extrusion of film yarn for industrial fabrics, heavy duty bags, ropes and twines. The product is also suitable for the production of water-quenched blown film and monofilament. Jampilen HP552J is suitable for food contact. Extrusion (Film yarn, monofilament) Water-quenched blown film Good processability Low water carry-over Film yarn for industrial fabrics, heavy duty bags Ropes and twines Blown film packaging Melt Flow Rate (230 o C, 2.16kg) 3.2 g/10min ASTM D 1238 Density 0.9 g/cm 3 ASTM D 1505 Flexural Modulus 1550 N/mm 2 ASTM D 790 Tensile Strength at Yield 35 N/mm 2 ASTM D 638 Tensile Elongation at Yield 12 % ASTM D 638 Izod Impact Strength (notched) at 23 o C 55 J/m ASTM D 256 Rockwell Hardness 102 R scale ASTM D 785 Vicat softening point (10N) 156 o C ASTM D 1525 H.D.T. (0.46 Mpa) 94 o C ASTM D 648 Accelerated oven ageing in air at 150 o C 360 hours ASTM D 3012 PPCO-DS-24/04 Feb 10
Jampilen HP456J Jampilen HP456J is a homopolymer, suitable for extrusion and thermoforming applications. It is formulated with a low water-carry-over additive package. Jampilen HP456J is designed for production of ropes and tapes for carpet backing. Fiber Extrusion (Raffia, Tape, Monofilament) Extrusion (Sheet) Thermoforming Good stretchability Low water carryover Raffia, tapes, strapping Artificial grass Geotextile and agriculture Melt Flow Rate (230 o C, 2.16kg) 3.4 g/10min ISO 1133 Density 0.9 g/cm 3 ISO 1183 Tensile Modulus (1mm/min) 1500 MPa ISO 527-1, -2 Tensile Strength at Yield (50mm/min) 34 MPa ISO 527-1, -2 Tensile Elongation at Break (50mm/min) >50 % ISO 527-1, -2 Tensile Elongation at Yield (50mm/min) 10 % ISO 527-1, -2 Charpy impact strength (Notch A) at 23 o C 4.0 kj/m 2 ISO 179 Vicat softening point A50 154 o C ISO 306 H.D.T. B (0.45 MPa) 97 o C ISO 75B-1, -2 PPCO-DS-93/01 Feb 10
Jampilen HP510L Jampilen HP510L is a polypropylene homopolymer with good flow properties and is particularly suitable for the extrusion of film yarn, monofilament, cast film and sheet. Jampilen HP510L combines outstanding processability with good mechanical properties. Film yarn of Jampilen HP510L is used for baler twines, packaging twines and ropes. Jampilen HP510L is well suited for the production of monofilament used for instance in brush and broom filling and technical applications. Extrusion (Film yarn, monofilament) Sheets, Cast film Good processability Good mechanical properties Baler twines, packaging twines and ropes Brush and broom filling and technical applications Coextruded film for packaging Thin sheet for stationery folders Sheet for thermoforming Straws Gunnies Melt Flow Rate (230 o C, 2.16kg) 6.5 g/10min ASTM D1238 Flexural Modulus 1500 MPa ASTM D790 Tensile Strength at Yield 35 MPa ASTM D638 Tensile Elongation at Yield 12 % ASTM D638 Izod Impact Strength (notched) at 23 o C 40 J/m ASTM D256 Rockwell Hardness 100 R Scale ASTM D785 Vicat softening point (10N) 154 H.D.T. (0.46 Mpa) 94 Accelerated oven ageing in air at 150 o C 360 hours ASTM D3012 PPCO-DS-25/04 Feb 10