Validity of bending tests on strip-shaped specimens to derive bending strength and stiffness properties of cross-laminated solid timber (X-lam)

Similar documents
Mechanics of stripped CLT panels with numerical validity testing

Quality control and improvement of structural timber

POTENTIAL OF CLT PRODUCED FROM NON-STRUCTURAL GRADE AUSTRALIAN PINUS RADIATA

Reinforcement of glulam beams with FRP reinforcement

Visual strength grading supported by mechanical grading. M. Frese

SHEAR PROBLEMS IN TIMBER ENGINEERING ANALYSIS AND SOLUTIONS

1. Characterize the mechanical properties of lamination timber and determine the yield of laminating grades meeting CEN standards. 2.

Modulus of elasticity local or global values

Pre-stressed FRP for the in-situ strengthening of timber structures

European Technical Assessment. ETA-18/0041 of Member of. General part

BEECH GLULAM STRENGTH CLASSES. M Frese H J Blaß. Universität Karlsruhe GERMANY

KEYWORDS: Cross-laminated timber, fire resistance, model, tests

Determination of Engineering Properties and Modeling of Wood I-Joists

GLT GIRDER LONGITUDINALLY TENSILETESTED

On The Plastic Design Of Timber Beams With A Complex Cross-Section

The influence of acetylation of Radiata pine in structural sizes on its strength properties

CLT Structural Design Sylvain Gagnon, Eng. February 8, 2011 Vancouver

SHORT NOTICES SPAN-TO-DEPTH RATIO FOR SHEAR FREE DEFORMATIONS IN STATIC BENDING OF SMALL WOOD SPECIMENS

Metal-plate connections loaded in combined bending and tension

LAMINATING LUMBER AND END JOINT PROPERTIES FOR FRP-REINFORCED GLULAM BEAMS. T G. Williamson Borjen Yeh. APA The Engineered Wood Association U.S.A.

Modeling the properties of strength graded timber material

Mechanical properties and strength grading of Norway spruce timber of different origins

April 2, 2018 PARTIES INTERESTED IN CROSS LAMINATED TIMBER PANELS USED AS COMPONENTS IN FLOOR AND ROOF DECKS

Eurocode 5 design in comparison with fire resistance tests of unprotected timber beams

twelve wood construction: materials & beams ARCHITECTURAL STRUCTURES: FORM, BEHAVIOR, AND DESIGN DR. ANNE NICHOLS SUMMER 2014 lecture

AMERICAN LUMBER STANDARD COMMITTEE, INCORPORATED POLICY FOR EVALUATION OF RECOMMENDED SPANS FOR SPAN RATED DECKING PRODUCTS

Creep behavior of cross laminated timber in service class 2

Assessment of the shear strength of glued-laminated timber in existing structures

Torque loading tests on the rolling shear strength of cross-laminated timber

Analysis of Glulam Timber Beams with Mechanically Graded (E-rated) Outer Laminations

twelve wood construction: materials & beams Wood Beam Design Wood Properties Timber National Design Specification

twelve wood construction: materials & beams Wood Beam Design Wood Properties Timber National Design Specification

twelve wood construction: materials & beams Wood Beam Design Timber Wood Properties National Design Specification

thirteen wood construction: materials & beams ELEMENTS OF ARCHITECTURAL STRUCTURES: FORM, BEHAVIOR, AND DESIGN DR. ANNE NICHOLS SPRING 2016 lecture

European Technical Assessment. ETA-12/0281 of Member of. General part

twelve wood construction: materials & beams Wood Beam Design Wood Properties Timber National Design Specification

European Technical Assessment ETA-14/0354 of

Inclined glue laminated timber beams with an end notch at the tension side

Static bending properties of structural wood-base panels: largepanel versus small-specimen tests

thirteen wood construction: materials & beams Timber Wood Beam Design Wood Properties

EXPERIMENTAL STUDY REGARDING THE BEHAVIOR OF GLUE LAMINATED BEAMS DOUBLE REINFORCED WITH RECTANGULAR METAL PIPES (RMP)

PERFORMANCE EVALUATION OF THE BENDING STRENGTH OF LARCH CROSS-LAMINATED TIMBER

LOAD BEARING CAPACITY OF TRADITIONAL ROOF STRUCTURES MODELLING OF JOINTS

Efficient Hardwood Glued-Laminated Beams

Changes to the 2005 NDS Supplement Design Values for Wood Construction

Bending Strength Classification of Some Common Nigerian Timber Species

Stress Distribution in Masonry Walls, Loaded in Plane, Simulated with Comsol.

Ken-ichi SUGIMOTO Team Leader Forestry and Forest Products Research Institute Tsukuba, JAPAN

Effects of age and moisture content on mechanical properties and twisting of Finnish round and sawn pine (Pinus sylvestris) and spruce (Picea abies)

Strength properties of glued laminated timber made from edge-glued laminae II: bending, tensile, and compressive strength of glued laminated timber

Failures in wood structures often

AITC TECHNICAL NOTE 26 DESIGN VALUES FOR STRUCTURAL GLUED LAMINATED TIMBER IN EXISTING STRUCTURES December 2007

CHEM-E0120: An Introduction to Wood Properties and Wood Products Material properties II: short-term mechanical properties

Study on Load Carrying Capacity and Stiffness of Curved Glulam Beam

Scientific Seminar Design of Steel and Timber Structures SPbU, May 21, 2015

European Technical Assessment. ETA-18/0083 of Member of. General part

Moisture Content Specific Gravity Relationships for Clear Southern Pine

Concentrated load introduction in CLT elements perpendicular to plane

X-Lam Designer for Derix Cross Laminated Timber. User manual. X-Lam Designer. User manual. Version 6.0. Page 1

Flexural behaviour of a polymeric foam/glass-fibre composite: FE modelling and experimental testing

Strength and Deformation Modification Factors of Wood Based Composites for Engineering Design

Design Methods of Elements from Cross-Laminated Timber Subjected to Flexure

Property Relationships for Tropical Hardwoods

PROPERTIES AND GRADING OF SOUTHERN PINE TIMBERS

A PRODUCT FROM KANTAFLEX (INDIA) PVT LIMITED

THE STABILITY OF A FACETTED GLASS DOME STRUCTURE

T 836 pm-95 PROVISIONAL METHOD TAPPI. Bending stiffness, four point method. 1. Scope

ULTIMATE STRENGTH PREDICTION OF DRM TIMBER BEAMS BY PLASTIC APPROACH: EXPERIMENTAL RESULTS AND DISCUSSIONS

Bonding of Carbon Fibre-reinforced Plastics with Wood

PRESTRESSED CONCRETE STRUCTURES. Amlan K. Sengupta, PhD PE Department of Civil Engineering Indian Institute of Technology Madras

A campaign by Studiengemeinschaft Holzleimbau e.v.

Radiusholz Curved Cross Laminated Timber (CLT) Elements

Declaration of performance

Initial Tests of Kevlar Prestressed Timber Beams

Other quality certification includes SINTEF (Norway) and SmartPly OSB is manufactured in accordance with the

ARE WIND-INDUCED COMPRESSION FAILURES GRADING RELEVANT? M Arnold R Steiger. Swiss Federal Laboratories for Materials Testing and Research (EMPA)

SPS 2. Special Products Standard for Machine Graded Lumber. Effective April 1, Approved by the Canadian Lumber Standards Accreditation Board

Assessment process of a new structural PUR adhesive

The Influence of Panel Lay-Up on the Characteristic Bending and Rolling Shear Strength of CLT

DEUTSCHES INSTITUT FÜR BAUTECHNIK Anstalt des öffentlichen Rechts

U.S.D.A.FOREST SERVICE RESEARCH PAPER FPL 148 DECEMBER SOME STRESS-GRADING CRITERIA AND METHODS OF GRADE SELECTION FOR DIMENSION LUMBER

American Institute of Timber Construction 7012 South Revere Parkway Suite 140 Centennial, CO Phone: 303/ Fax: 303/

TEST METHODS FOR BASIC PROPERTIES OF WOOD- BASE PANELS: PAST EXPERIENCE, TODAY S NEEDS

Investigations on longitudinal fillet welded lap joints of HSS

Duration of Load on Bolted Joints

Recent UBC research activities on CLT and Glulam

A MODULAR TIMBER CONSTRUCTION SYSTEM MADE WITH HOLLOW-BOX ELEMENTS

CONTROLLING CROSS-LAMINATED TIMBER (CLT) FLOOR VIBRATIONS: FUNDAMENTALS AND METHOD

EXPERIMENTAL INVESTIGATION ON THE LOAD- CARRYING CAPACITY OF THIN WEBS INCLUDING POST-TENSIONING TENDONS

Evaluation Listing CCMC L Nordic X-Lam

Bending strength and modulus of elasticity of BC coastal timbers

BOUNDARY CONDITIONS OF SHEAR WALLS IN MULTI-STOREY MASONRY STRUCTURES UNDER HORIZONTAL LOADINGS

INFLUENCE OF PRSTRESS LEVEL ON SHEAR BEHAVIOR OF SEGMENTAL CONCRETE BEAMS WITH EXTERNAL TENDONS

SUITABILITY: SMARTPLY OSB3 - ZERO ADDED FORMALDEHYDE

BEHAVIOUR AND DESIGN OF ANCHORS FOR LIFTING AND HANDLING IN PRECAST CONCRETE ELEMENTS

Function-integrated GFRP sandwich roof structure Experimental validation of design

GP LAM Laminated Veneer Lumber Georgia-Pacific Wood Products South LLC Revised March 20, 2015

Measurement series to verify the accuracy of Stora Enso Acoustic Prediction tool - SEAP

Murphy Laminated Veneer Lumber Murphy Engineered Wood Division Revised May 30, 2013

Moisture Gradient as Loading of Curved Timber Beams

Transcription:

The Future of Quality Control for Wood & Wood Products, 4-7 th May 21, Edinburgh Validity of bending tests on strip-shaped specimens to derive bending strength and stiffness properties of cross-laminated solid timber (X-lam) R. Steiger 1 & A. Gülzow 2 Abstract The application of cross-laminated solid timber (CLT, X-lam) used as loadbearing plates requires information on the product s strength properties; the design, however, is often governed by serviceability criterions. Hence, predicting the respective behaviour of such panels requires accurate information about their bending and shear strength as well as their elastic properties. Bending strength and stiffness of CLT have to be assessed following the procedures in EN 789. The latter requires 4-point bending tests of stripshaped specimens with a width of 3 mm, cut from the panels. By comparing results of bending tests on 1 mm and 3 mm wide strip-shaped specimens and on full panels it is shown, that neither MOR nor stiffness properties derived by testing single 1 mm wide strip-shaped specimens are appropriate to assess the respective properties of the original panels. However, with regard to stiffness properties, single 3 mm wide strips or samples of at least 5 to 6 1 mm wide strips lead to acceptable results. The analysis of the test data covers MOR, bending MOE parallel and perpendicular to the grain direction of the face layers as well as shear moduli. Rolling shear failures which frequently occurred when testing the 1 mm wide strip-shaped specimens could not be observed in destructive tests of gross CLT panels. It is concluded that tests on single strip-shaped specimens should only be used in the course of quality control of CLT (i.e. to check sufficient adhesive bond of the layers) but not to derive mechanical properties of gross panels. 1 Introduction Cross-laminated solid timber (CLT) is assembled of cross-wise oriented layers of lamellas (mostly softwood). Compared to the raw material, CLT benefits from homogenised mechanical properties. CLT is not only used as component of structural elements, but rather for load bearing plates and shear walls. In practice the design of plates loaded perpendicular to the plane is often governed by serviceability criterions like maximal deflection and vibration susceptibility. Appropriate verification of ultimate and serviceability limits of such panels is only possible when relying on accurate information about the elastic properties as well as on the strength properties of the respective CLT product. 1 Senior Scientist, rene.steiger@empa.ch Empa, Wood Laboratory, Dübendorf, Switzerland 2 Planning Engineer, guelzow@carbo-link.com Carbo-Link GmbH, Fehraltorf, Switzerland

The Future of Quality Control for Wood & Wood Products, 4-7 th May 21, Edinburgh The current European regulation EN 13986 (CEN 24b) with regard to deriving the so-called performance characteristics bending strength (MOR) and bending stiffness (MOE, G) makes reference to the standard EN 789 (CEN 24a). EN 789 requests 4-point bending tests of strip-shaped specimens with a width of 3 5 mm, cut from the CLT panels. The span has to be taken as 3 mm + 32 t, t being the nominal thickness of the CLT panel. The standard asks for only one specimen per plate and grain direction of the face layers to be tested respectively. The standard EN 13353 (CEN 23b) being relevant for the requirements on CLT allows this respective test value to be taken as the mean value of the whole panel and for using this value for all statistical calculations where the mean value and the variation of the mean values of the panels are used. It is however said that the variation within a panel and the according calculations cannot be done which means that e.g. characteristic values cannot be assigned to CLT based on the procedure described above. It is obvious that deriving mechanical properties from one single test is not reliable enough. However, in the course of production control such tests are useful to check e.g. sufficient quality of bond lines and can thus serve as a kind of red light alert. The question to what extent tests on strip-shaped specimens according to EN 789 are capable of reliably deriving MOR and bending stiffness of gross CLT panels was answered by an experimental campaign. 2 Material The study comprised of a total of 42 CLT panels with different lay-ups and geometrical dimensions as indicated in Table 1. The panels were supplied by two producers (A and B) and due to totally different ways of production the panels exhibited remarkable differences in appearance and mechanical properties although the raw material was in both cases visually strength graded Norway Spruce (Picea abies Karst.). Table 1: Geometrical properties of the investigated CLT panels Series Length 1) x Width [m] 1 2.5 x 2.5 7 2 2.5 x 2.5 11 4. x 2.5 t [mm] Lay-up [mm] Sample size 8 11 1) parallel to the grain direction of the face layers Product A and B: 1/5/1 Product A and B: 25/2/25 9 x A, 9 x B 9 x A, 9 x B Product A: 35/4/35 3 Product B: 2/7/2 3 Product A: 25/3/25 3 Product B: 15/5/15 3 Product B: 15/15/2/15/15 3 Product A: 35/4/35 3

The Future of Quality Control for Wood & Wood Products, 4-7 th May 21, Edinburgh Compared to product A, product B due to smaller sized components of the layers, lacking of grooves and due to bonding of the layers on all sides exhibits a higher degree of homogenization (Figure 1). Prior to testing in the lab, the panels as well as the strip-shaped specimens were stored in climatic chambers. The specimens reached and equilibrium moisture content of slightly below 12%. Product A Product B Lay-up 1/5/1 mm Lay-up 25/2/25 mm Figure 1: CLT products A (left) and B (right), t = 7 mm The scheme of cutting the strip-shaped specimens parallel and perpendicular to the grain direction of the face layers from the series 1 CLT panels is shown in Figure 2 left. The width of the 5 6 strips per direction in series 1 was 1 mm. In the course of test series 2 two 3 mm wide strips (one per grain direction of the face layers) were cut from each panel according to Figure 2 right. Series 1 CLT panels Series 2 CLT panels Figure 2: Scheme of cutting strip-shaped specimens from CLT panels. The arrow sign indicates the grain direction of the face layers.

The Future of Quality Control for Wood & Wood Products, 4-7 th May 21, Edinburgh 3 Method 3.1 Evaluation of elastic properties of the CLT panels To derive stiffness properties of gross CLT panels a method was applied which had recently been studied and further developed at the Swiss Federal Laboratories for Materials Testing and Research, Empa (Gülzow 28). The method is non-destructive and bases on experimental and theoretical modal analysis (Steiger et al. 28). The method was shown to be capable of deriving two MOE (E 11, E 22 ) and three shear moduli (G 12, G 13, G 23 ) of CLT panels with different geometrical dimensions and lay-ups (Gülzow et al. 28). The directions of the principal axis as used in this paper are shown in Figure 3. Figure 3: Principal axis in CLT as used in this paper 3.2 Bending tests of gross CLT panels The series 1 CLT panels were subjected to destructive bending tests, the panels being simply supported on their four edges. The tests were carried out with three different loading cases: a) 4 single loads in the centre point of the panels quadrants, b) 1 single load in the centre of the panel and c) 1 single load in the centre of one quadrant. Deformations, failure load and failure mode were recorded (Czaderski et al. 27). The MOR was calculated with the compound theory taking all layers into account (Bodig et al. 1993, Blass et al. 23). 3.3 Bending tests of strip-shaped specimens Along series 1, due to restrictions by the available testing machine the width of the specimens was only 1 mm (EN 789 would have required 3 mm!) and thus the span was reduced similarly. Specimens were subjected to 4-point bending tests with a span of 11 mm and a distance between the loading points of 3 mm (Howald et al. 26) and MOR and stiffness as well as failure mode were recorded. The reference loads to determine MOE were 1% and 4% of the assumed failure load and the deformations were measured between the loading points on the upper side of the specimens. Speed of the loading head was adjusted such that failure was reached after 3 12 seconds. In series 2 the MOE in bending and the shear modulus were evaluated according to EN 48 (CEN 23a) with the specimens having dimensions as asked by EN 789. The shear moduli G (G 13 and G 23 ) and the MOE E m (E 11 and E 22 ) were determined by the variable span method from the apparent MOE

The Future of Quality Control for Wood & Wood Products, 4-7 th May 21, Edinburgh E m,app for each test piece as indicated in EN 48. The deformations were measured for 1% and 4% of the supposed failure load and the speed of loading was such that each test cycle lasted 1 minute, which is slightly above the test duration asked by EN 48. Strips with grooves and cuts (aiming at reducing warping due to changing moisture) were tested twice with changing orientation of tension and compression side. 4 Results and discussion 4.1 MOR, MOE and failure modes of strips cut from the series 1-CLT panels Figure 4 shows a comparison of MOR recorded along bending tests of gross CLT panels (dimensions: 2.5 x 2.5 x.7 m, lay-ups 1/5/1 mm and 25/2/25 mm) and of respective values derived from strip-shaped specimens (1.2 x.1 x.7 m) cut from the panels parallel to the grain direction of the face layers (Figure 2, left). 99.99 99.9 99 Panel tests of product A (n = 12) Panel tests of product B (n = 12) Strip-shaped tests of product A (n = 7) Strip-shaped tests of product B (n = 78) 95 9 8 7 [%] 5 3 2 1 5 1.1.1 2 3 4 5 6 Bending strength f [N/mm 2 ] m 7 Figure 4: Comparison of MOR derived from tests on gross CLT panels with layups 1/5/1 mm and 25/2/25 mm and on strip-shaped specimens (width = 1 mm) cut from these panels according to Figure 2, left For both products MOR derived from tests on strip-shaped specimens is considerably lower than when performing bending tests on whole panels. Comparing the variation of results (represented by the slope of the linear regression lines) it can be seen that testing of strip-shaped specimens with a width of 1 mm is not capable to correctly account for the higher degree of homogenisation of product B, whereas this difference can clearly be seen when comparing the test results of the gross CLT panels. In the course of the strip

The Future of Quality Control for Wood & Wood Products, 4-7 th May 21, Edinburgh tests in 4-point bending shear failures occurred frequently, whereas this was not the case with the gross CLT panels. There, due to comparably lower shear stresses, bending failure on the tension side was predominant. A shear failure was noticed in one single case only. However, once punching occurred. Figure 5 shows mean, maximum and minimum values of the MOE E 11 and E 22 of 5 6 strips per panel and grain direction of the face layers. The high CoV clearly indicate a large variation of the stiffness properties within single CLT panels independent of their lay-up. When comparing the mean values of the strip test samples to the respective values derived by modal analysis of the gross CLT panels, the biggest difference is 21% for strips tested parallel to the grain direction of the face layers (E 11 ) and 14% perpendicular to it (E 22 ). No clear trend of over- or underestimating could be found. In average (mean values of all strip-shaped specimens cut from the same panel) the differences are for E 11 1% (product A) and 6% (product B) and for E 22 7% (product A) and 8% (product B). When plotting all series of the CLT panels with lay-up 1/5/1 in normal probability plots (NPP) (Figure 6) it can be seen that the mean values of the MOE of the strip tests are marginally higher than the ones derived by modal analysis of the gross panels. Comparing the slopes of the linear regression lines in the NPP, again much bigger variability of the strip test samples is obvious. Overall variations are higher in product A than in product B which can be explained by a different degree of homogenization due to the different ways of production and the quality of the raw material (see 2). This phenomenon, however, is marked more for MOE E 11 and E 22 of the gross panels than for the strip test samples. 4.2 MOE and shear moduli of strips cut from the series 2 -CLT panels Generally MOE and shear moduli could be derived with high accuracy by the variable span method (CEN 23a). However, some single values in the test series with strips oriented perpendicular to the grain direction of the face layers did not fit the trend line well, this being due to opening of layers at lamella contacts which were not glued together. When such zones in specimens tested at large span are placed in the middle of the spans, the openings take much more influence on the test results than when being put near the supports in tests with short spans. Consequently respective test results were excluded from analysis. Figure 7 shows a comparison of MOE (E 11, E 22 ) and shear moduli (G 13, G 23 ) derived by modal analysis of the gross series-2 CLT panels and by bending tests of strip-shaped specimens cut from the respective panels according to Fig. 2, right. The diagonal line in the figure indicates the ideal case, where parameters derived by modal analysis would be equal to those derived by static bending tests of the strip-shaped specimens. The results are grouped by type of product and geometrical parameters of the panel as indicated in Table 1 and in the caption of the figure. The differences independent from type of product are small to moderate. Parameter E 22 even shows a very good agreement. Some big differences are visible between values derived on gross panels and on strip-shaped specimens respectively especially regarding the MOE E 11 and the shear moduli G 13 and G 23.

The Future of Quality Control for Wood & Wood Products, 4-7 th May 21, Edinburgh E 11 - Panels of lay up 1/5/1 15 Product A Product B 2 18 16 E11 [N/mm 2 ] 1 5 E11, modal analysis, whole panel E11, strips, mean values E11, strips, maximum values E11, strips, minimum values COV. 14 12 1 8 6 4 2 A1 A2 A3 A7 A8 A9 A1 A11 A12 B13 B14 B15 CoV [%] B19 B2 B21 B22 B23 B24 Panel 1 Product A E 22 - Panels of lay up 1/5/1 Product B 35 3 25 E22 [N/mm 2 ] 5 2 15 CoV [%] E22, modal analysis, whole panel E22, strips, mean values E22, strips, maximum values E22, strips, minimum values COV 1 5 A1 A2 A3 A7 A8 A9 A1 A11 A12 B13 B14 B15 B19 B2 B21 B22 B23 B24 15 E 11 - Panels of lay up 25/2/25 18 Panel 1 E 22 - Panels of lay up 25/2/25 18 16 16 14 14 E11 [N/mm 2 ] 1 5 A4 Product A E11, modal analysis, whole panel E11, strips, mean values E11, strips, maximum values E11, strips, minimum values COV A5 A6 B16 Panel Product B B17 B18 12 1 8 6 4 2 CoV [%] E22 [N/mm 2 ] 5 A4 E22, modal analysis, whole panel E22, strips, mean values E22, strips, maximum values E22, strips, minimum values COV A5 A6 Panel B16 B17 B18 12 1 8 6 4 2 CoV [%] Figure 5: MOE E 11, E 22 derived by 4-point bending tests of 1 mm wide stripshaped specimens (5 6 specimens per series 1-CLT panel) or by modal analysis of gross panels (x-signs) together with respective coefficients of variation (CoV)

The Future of Quality Control for Wood & Wood Products, 4-7 th May 21, Edinburgh 99.99 99.9 99 E11-Product A-Panels E11-Product B-Panels E11-Product A-Strip-shaped specimnes E11-Product B-Strip-shaped specimnes [%] 95 9 8 7 5 3 2 1 5 1.1.1 99.99 99.9 99 5 1 15 MOE [N/mm 2 ] E22-Product A-Panels E22-Product B-Panels E22-Product A-Strip-shaped specimens E22-Product B-Strip-shaped specimens [%] 95 9 8 7 5 3 2 1 5 1.1.1 1 2 3 4 5 6 7 8 MOE [N/mm 2 ] Figure 6: NPP of MOE E 11 and E 22 derived by 4-point bending tests of 1 mm wide strip-shaped specimens (5 6 specimens per series 1-CLT panel) and by modal analysis of gross panels (lay-up 1/5/1 mm only) A closer look on the specimens turned out, that big differences mainly resulted from striking non-homogeneities in the used raw material. Since specimens with marked cuts and grooves were tested twice with changing orientation of the tension side in bending, it could be concluded that the test procedure did not systematically affect the data. Differences between values derived by modal analysis and by static testing, however, also result from the well-known fact that stiffness parameters derived by means of dynamic methods due to the high speed of action are approximately 6% higher than those determined on base of static experiments at comparably lower loading rate (Görlacher 1984).

The Future of Quality Control for Wood & Wood Products, 4-7 th May 21, Edinburgh E11 from static test of strip [N/mm 2 ] E 11 16 Q_.11_3L_A R_.11_3L_A 14 R_.8_3L_A Q_.11_3L_B 12 R_.8_3L_B R_.8_5L_B 1 8 6 4 2 2 4 6 8 1 12 14 16 E 11 from modal analysis [N/mm 2 ] G 13 E22 from static test of strip [N/mm 2 ] E 22 45 Q_.11_3L_A 4 R_.11_3L_A R_.8_3L_A 35 Q_.11_3L_B R_.8_3L_B 3 R_.8_5L_B 25 2 15 1 5 5 1 15 2 25 3 35 4 45 E 22 from modal analysis [N/mm 2 ] G 23 G13 from static test of strip [N/mm 2 ] 25 2 15 1 5 Q_.11_3L_A R_.11_3L_A R_.8_3L_A Q_.11_3L_B R_.8_3L_B R_.8_5L_B G23 from static test of strip [N/mm 2 ] 1 8 6 4 2 Q_.11_3L_A R_.11_3L_A R_.8_3L_A Q_.11_3L_B R_.8_3L_B R_.8_5L_B 5 1 15 2 25 G 13 from modal analysis [N/mm 2 ] 2 4 6 8 1 G 23 from modal analysis [N/mm 2 ] Figure 7: Comparison of MOE and shear moduli derived by modal analysis of the gross CLT panels and by bending tests of single strip-shaped specimens cut from the respective panel according to Fig. 2, right. (Labels: Q/R = quadric/rectangular panel 2.5 x 2.5 m / 4. x 2.5 m,.11/.8 = panel thickness [m], 3L/5L = 3/5 layers, A/B = Product) 5 Summary and conclusions Strength properties can be assigned to CLT by means of the compound theory. However, the mechanical properties (strength and stiffness) of the layers have to be known which means that the raw material has to be strength graded. Deriving stiffness properties of whole CLT panels with modal analysis is a good alternative to estimating them on base of the mechanical properties of the single layers by means of the compound theory. Especially in cases where the raw material is not strength graded or its mechanical properties are not known with sufficient precision, the modal analysis can help in assigning correct stiffness properties to CLT.

The Future of Quality Control for Wood & Wood Products, 4-7 th May 21, Edinburgh After having proven the correctness of the modal analysis method by static proof loading, the panel properties were compared to bending MOE and shear moduli derived from tests on strip-shaped specimens cut from the CLT panels. One part of the tests additionally focused on bending strength and failure modes. From the tests the following conclusions could be drawn: Bending strength and stiffness of CLT panels can vary quite strongly within one single panel. For both parameters differences in strength and stiffness of strip-shaped specimens cut from the panels of up to 1% have been found. Hence it is not possible to derive strength and stiffness properties of CLT panels from bending tests of few or single strip-shaped specimens. The accuracy of the test results when performing bending tests of stripshaped specimens according to EN 789 is increased with increasing sample size. Mean values of at least 5 6 specimens better describe the actual bending stiffness of the panels. Average differences in MOE then amount to 1% (E 11 ) and 6% (E 22 ) but can still reach 2%. The variation of the stiffness properties depends on the degree of homogenisation of the actual CLT product. The smaller the components (lamellas) are and the less the variation in mechanical properties is (due to e.g. a strength grading of the raw material), the better it can be concluded from tests on strip-shaped specimens to the bending strength and stiffness properties of the gross CLT panel. Compared to gross CLT panels, local non-homogeneities and faults (knots, pitch pockets, deviated grain, not adhesively bonded contacts, grooves, cracks) take more influence on the mechanical properties of the strip-shaped specimens. The smaller the width of such specimens is, the more their loadbearing behaviour is affected by local defects and non-homogeneities due to the quality of the raw material or due to the way of producing the panels. The distances between middle layer parts not adhesively bonded at their edges and the number of grooves, which are aimed at reducing the deformations of the CLT panel in case of changing moisture, take a big influence on the shear moduli. When deriving respective values on base of testing strip-shaped specimens this possible variation has to be taken into account by using empirical relationships. When testing strip-shaped specimens in 4-point bending, (rolling) shear failures occur quite frequently, whereas such failure modes could not be observed when testing gross CLT panels to failure in loading situations occurring in practice. There bending failure was dominating. Punching, however, should be regarded, especially with thin panels and products with grooves and layers not adhesively bonded at their edges. Single tests on strip-shaped specimens may serve as an instrument of production control especially regarding the quality of bonding. They should, however not be used to derive mechanical properties of CLT panels. In scientific studies testing of strip-shaped specimens should only be carried out on big samples. Geometrical dimensions should not be taken smaller than asked by the standards and generalization of conclusions in most cases is not possible (e.g. type of failure).

The Future of Quality Control for Wood & Wood Products, 4-7 th May 21, Edinburgh Acknowledgments The study was financially supported by the Swiss Federal Office for Professional Education and Technology OPET (Innovation Promotion Agency CTI) and by the Swiss Federal Office for the Environment FOEN (Wald- und Holzforschungsfonds WHFF). The test specimens were supplied by Pius Schuler AG, CH-6418 Rothenturm, Switzerland (www.pius-schuler.ch) and by Schilliger Holz AG, Haltikon 33, CH-643 Küssnacht (www.schilliger.ch). References Blass, H. J. & Görlacher, R. (23) "Bemessung im Holzbau: Brettsperrholz Berechnungsgrundlagen". Holzbau-Kalender, pp 58-598. Bruderverlag, Karlsruhe, Germany. Bodig, J. & Jayne, B. A. (1993) "Mechanics of wood and wood composites". Krieger Publishing Company, Malabar, Florida, USA. CEN (23a) "EN 48: Timber structures - Structural timber and glued laminated timber - Determination of some physical and mechanical properties, European Committee for Standardization. CEN (23b) "EN 13353: Solid wood panels (SWP) - Requirements, European Committee for Standardization. CEN (24a) "EN 789: Timber structures - Test methods - Determination of mechanical properties of wood based panels", European Committee for Standardization. CEN (24b) "EN 13986: Wood-based panels for use in construction - Characteristics, evaluation of conformity and marking, European Committee for Standardization. Czaderski, C., Steiger, R., Howald, M., Olia, S., Gülzow, A. & Niemz, P. (27) "Versuche und Berechnungen an allseitig gelagerten 3-schichtigen Brettsperrholzplatten". Holz als Roh- und Werkstoff, Vol 65, pp 383-42. Görlacher, R. (1984) "Ein neues Messverfahren zur Bestimmung des Elastizitätsmoduls von Holz". Holz als Roh- und Werkstoff, Vol 42, pp 219-222. Gülzow, A. (28) "Zerstörungsfreie Bestimmung der Biegesteifigkeiten von Brettsperrholzplatten". PhD Thesis Nr. 17944, ETH Zürich, Switzerland. Gülzow, A., Gsell, D. & Steiger, R. (28) "Zerstörungsfreie Bestimmung elastischer Eigenschaften quadratischer 3-schichtiger Brettsperrholzplatten mit symmetrischem Aufbau". Holz als Roh- und Werkstoff Vol 66, pp 19-37. Howald, M. & Niemz, P. (26) "Massivholzplatten für das Bauwesen Berichtsteil I/1: Berechnungsmodell für Massivholzplatten - Ermittlung mechanischer Eigenschaften anhand von Ultraschall-Messungen und Biegeversuchen an Kleinproben". Institut für Baustoffe, ETH Zürich, Switzerland. Steiger, R., Gülzow, A. & Gsell, D. (28) "Non-destructive evaluation of elastic material properties of cross-laminated timber". Proceedings of COST E53 Conference on "End user's needs for wood material and products". 29 th 3 th October 28, Delft, The Netherlands, pp 171-182.